WO2004054803A1 - Verfahren zur herstellung von flexodruckformen mittels lasergravur unter verwendung von fotopolymeren flexodruckelementen und fotopolymerisierbares flexodruckelement - Google Patents
Verfahren zur herstellung von flexodruckformen mittels lasergravur unter verwendung von fotopolymeren flexodruckelementen und fotopolymerisierbares flexodruckelement Download PDFInfo
- Publication number
- WO2004054803A1 WO2004054803A1 PCT/EP2003/013743 EP0313743W WO2004054803A1 WO 2004054803 A1 WO2004054803 A1 WO 2004054803A1 EP 0313743 W EP0313743 W EP 0313743W WO 2004054803 A1 WO2004054803 A1 WO 2004054803A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- relief
- forming layer
- protective element
- layer
- flexographic printing
- Prior art date
Abstract
Description
Claims