WO2003095204A1 - Systeme de conduction thermique perfectionne et stratifies fabriques au moyen de celui-ci - Google Patents

Systeme de conduction thermique perfectionne et stratifies fabriques au moyen de celui-ci Download PDF

Info

Publication number
WO2003095204A1
WO2003095204A1 PCT/KR2003/000549 KR0300549W WO03095204A1 WO 2003095204 A1 WO2003095204 A1 WO 2003095204A1 KR 0300549 W KR0300549 W KR 0300549W WO 03095204 A1 WO03095204 A1 WO 03095204A1
Authority
WO
WIPO (PCT)
Prior art keywords
heat
separator
laminates
unit
conducting
Prior art date
Application number
PCT/KR2003/000549
Other languages
English (en)
Inventor
Myung Chul Chu
W. Jaewoo Shim
Original Assignee
Css Technologies Co., Ltd.
Anico Corporation
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Css Technologies Co., Ltd., Anico Corporation filed Critical Css Technologies Co., Ltd.
Priority to AU2003215944A priority Critical patent/AU2003215944A1/en
Priority claimed from KR1020030017643A external-priority patent/KR100575546B1/ko
Publication of WO2003095204A1 publication Critical patent/WO2003095204A1/fr

Abstract

L'invention concerne un système de conduction thermique perfectionné pouvant réduire au minimum un changement de température entre les stratifiés formés, pendant un processus de refroidissement. Certains stratifiés placés entre les plateaux supérieur et inférieur sont formés dans un environnement chauffé et pressurisé. On utilise un séparateur contenant une couche de conduction de chaleur et une unité de conduction thermique latérale en contact avec un côté du séparateur, conçu pour assurer une conduction supplémentaire de chaleur jusqu'aux plateaux. Ainsi, le problème inhérent au processus de refroidissement classique est résolu et les avantages de ce processus sont conservés.
PCT/KR2003/000549 2002-03-22 2003-03-21 Systeme de conduction thermique perfectionne et stratifies fabriques au moyen de celui-ci WO2003095204A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
AU2003215944A AU2003215944A1 (en) 2002-03-22 2003-03-21 An improved thermal conducting system and laminates produced thereform

Applications Claiming Priority (4)

Application Number Priority Date Filing Date Title
KR20020015645 2002-03-22
KR10-2002-0015645 2002-03-22
KR1020030017643A KR100575546B1 (ko) 2002-03-22 2003-03-21 개선된 열 전달 시스템 및 이에 의해 제조된 라미네이트
KR10-2003-0017643 2003-03-21

Publications (1)

Publication Number Publication Date
WO2003095204A1 true WO2003095204A1 (fr) 2003-11-20

Family

ID=29422499

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/KR2003/000549 WO2003095204A1 (fr) 2002-03-22 2003-03-21 Systeme de conduction thermique perfectionne et stratifies fabriques au moyen de celui-ci

Country Status (2)

Country Link
AU (1) AU2003215944A1 (fr)
WO (1) WO2003095204A1 (fr)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2009064344A1 (fr) 2007-11-09 2009-05-22 The Nordam Group, Inc. Fabrication de panneau double

Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5615470A (en) * 1992-05-05 1997-04-01 Cedal S.R.L. Process for producing plastic laminates with metal laminae
US5647940A (en) * 1993-03-18 1997-07-15 Cedal S.R.L. Process for automatically connecting a source of electric current and a pile of packages to make plastic laminates with endothermic heating

Patent Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5615470A (en) * 1992-05-05 1997-04-01 Cedal S.R.L. Process for producing plastic laminates with metal laminae
US5647940A (en) * 1993-03-18 1997-07-15 Cedal S.R.L. Process for automatically connecting a source of electric current and a pile of packages to make plastic laminates with endothermic heating

Cited By (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2009064344A1 (fr) 2007-11-09 2009-05-22 The Nordam Group, Inc. Fabrication de panneau double
EP2219867A1 (fr) * 2007-11-09 2010-08-25 THE NORDAM GROUP, Inc. Fabrication de panneau double
EP2219867A4 (fr) * 2007-11-09 2011-12-14 Nordam Group Inc Fabrication de panneau double
USRE45682E1 (en) 2007-11-09 2015-09-29 The Nordam Group, Inc. Dual panel fabrication

Also Published As

Publication number Publication date
AU2003215944A1 (en) 2003-11-11
AU2003215944A8 (en) 2003-11-11

Similar Documents

Publication Publication Date Title
CN101553094B (zh) 具埋藏式金属导通柱的线路板制作方法
KR100203540B1 (ko) 회로부품 및 회로부품의 제조방법
US20060014403A1 (en) Connecting structure of circuit board and method for manufacturing the same
EP0645952A1 (fr) Procédé de fabrication d'un circuit multicouche
US20050205291A1 (en) Flexible substrate having interlaminar junctions, and process for producing the same
EP2157842A1 (fr) Carte de câblage stratifiée et son procédé de fabrication
US8476534B2 (en) Multilayer printed board and method for manufacturing the same
TWI667946B (zh) 軟式電路板基材及其製作方法
CN103929896A (zh) 一种内埋芯片的印制电路板制造方法
EP1491078B1 (fr) Boitier de circuit integre a couches multiples
JP2007221068A (ja) フラッシュプリント配線板およびその製造方法ならびにフラッシュプリント配線板からなる多層プリント配線板。
TWI603450B (zh) Multilayer electronic structure with improved dielectric thickness control
WO2003095204A1 (fr) Systeme de conduction thermique perfectionne et stratifies fabriques au moyen de celui-ci
JP2005050885A (ja) 配線基板及びその製造方法
JP2001068856A (ja) 絶縁樹脂シート及びその製造方法
JPH08153971A (ja) 多層プリント配線基板及びその製造方法
JP4720767B2 (ja) フレキシブル基板およびその製造方法
KR100575546B1 (ko) 개선된 열 전달 시스템 및 이에 의해 제조된 라미네이트
JPH08264939A (ja) 印刷配線板の製造方法
US6174591B1 (en) Separators with direct heating medium and method for manufacturing thermally curable laminates thereof
JP3923224B2 (ja) 多層プリント配線板及びその製造方法
JP4429712B2 (ja) 基板前駆体の製造方法
JP4274861B2 (ja) 多層基板およびその製造方法
EP0543331B1 (fr) Plaquette de circuits multicouche de polyimide et son procédé de fabrication
JP2004342978A (ja) マルチワイヤ配線板の製造方法

Legal Events

Date Code Title Description
AK Designated states

Kind code of ref document: A1

Designated state(s): AE AG AL AM AT AU AZ BA BB BG BR BY BZ CA CH CN CO CR CU CZ DE DK DM DZ EC EE ES FI GB GD GE GH GM HR HU ID IL IN IS JP KE KG KP KZ LC LK LR LS LT LU LV MA MD MG MK MN MW MX MZ NI NO NZ OM PH PL PT RO RU SC SD SE SG SK SL TJ TM TN TR TT TZ UA UG US UZ VC VN YU ZA ZM ZW

AL Designated countries for regional patents

Kind code of ref document: A1

Designated state(s): GH GM KE LS MW MZ SD SL SZ TZ UG ZM ZW AM AZ BY KG KZ MD RU TJ TM AT BE BG CH CY CZ DE DK EE ES FI FR GB GR HU IE IT LU MC NL PT RO SE SI SK TR BF BJ CF CG CI CM GA GN GQ GW ML MR NE SN TD TG

121 Ep: the epo has been informed by wipo that ep was designated in this application
122 Ep: pct application non-entry in european phase
NENP Non-entry into the national phase

Ref country code: JP

WWW Wipo information: withdrawn in national office

Country of ref document: JP