Classifications

• • C—CHEMISTRY; METALLURGY
  • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
  • C09D—COATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
  • C09D151/00—Coating compositions based on graft polymers in which the grafted component is obtained by reactions only involving carbon-to-carbon unsaturated bonds; Coating compositions based on derivatives of such polymers
  • C09D151/08—Coating compositions based on graft polymers in which the grafted component is obtained by reactions only involving carbon-to-carbon unsaturated bonds; Coating compositions based on derivatives of such polymers grafted on to macromolecular compounds obtained otherwise than by reactions only involving carbon-to-carbon unsaturated bonds
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
  • C08F283/00—Macromolecular compounds obtained by polymerising monomers on to polymers provided for in subclass C08G
  • C08F283/10—Macromolecular compounds obtained by polymerising monomers on to polymers provided for in subclass C08G on to polymers containing more than one epoxy radical per molecule
• • C—CHEMISTRY; METALLURGY
  • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
  • C09D—COATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
  • C09D133/00—Coating compositions based on homopolymers or copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and at least one being terminated by only one carboxyl radical, or of salts, anhydrides, esters, amides, imides, or nitriles thereof; Coating compositions based on derivatives of such polymers
  • C09D133/04—Homopolymers or copolymers of esters
  • C09D133/06—Homopolymers or copolymers of esters of esters containing only carbon, hydrogen and oxygen, the oxygen atom being present only as part of the carboxyl radical
  • C09D133/062—Copolymers with monomers not covered by C09D133/06
  • C09D133/068—Copolymers with monomers not covered by C09D133/06 containing glycidyl groups
• • C—CHEMISTRY; METALLURGY
  • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
  • C09D—COATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
  • C09D4/00—Coating compositions, e.g. paints, varnishes or lacquers, based on organic non-macromolecular compounds having at least one polymerisable carbon-to-carbon unsaturated bond ; Coating compositions, based on monomers of macromolecular compounds of groups C09D183/00 - C09D183/16
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
  • C08L2312/00—Crosslinking
• • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
  • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
  • Y10S—TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
  • Y10S525/00—Synthetic resins or natural rubbers -- part of the class 520 series
  • Y10S525/937—Utility as body contact e.g. implant, contact lens or I.U.D.
• • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
  • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
  • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
  • Y10T428/00—Stock material or miscellaneous articles
  • Y10T428/31504—Composite [nonstructural laminate]
• • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
  • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
  • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
  • Y10T428/00—Stock material or miscellaneous articles
  • Y10T428/31504—Composite [nonstructural laminate]
  • Y10T428/31507—Of polycarbonate
• • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
  • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
  • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
  • Y10T428/00—Stock material or miscellaneous articles
  • Y10T428/31504—Composite [nonstructural laminate]
  • Y10T428/31511—Of epoxy ether
• • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
  • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
  • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
  • Y10T428/00—Stock material or miscellaneous articles
  • Y10T428/31504—Composite [nonstructural laminate]
  • Y10T428/31533—Of polythioether
• • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
  • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
  • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
  • Y10T428/00—Stock material or miscellaneous articles
  • Y10T428/31504—Composite [nonstructural laminate]
  • Y10T428/31551—Of polyamidoester [polyurethane, polyisocyanate, polycarbamate, etc.]

Definitions

• the present invention relates to primer coating compositions exhibiting very good adhesion properties on a large variety of substrates, in particular plastic substrates such as ophthalmic lenses made of organic glasses, and which also impart good impact resistance properties to the thus coated substrates.
• the present invention also concerns substrates coated with these primer coating compositions as well as a method for making such coated substrates
• Japanese patent IP 7-35902 discloses coating polyurethane lenses (MR6) with, successively, an epoxy/acrylate primer composition, an anti- abrasive silicone based coating and an anti-re lecting multiplayer coating.
• the resulting final lenses show good impact and abrasion resistances, good resistance to weathering, a good visual appearance, some colorability and a good adhesion between the layers.
• the epoxy/acrylate composition comprises acryl esters with OH groups, in particular of the bisphenol-A type.
• Japanese patent JP 6-271788 discloses a primer coating composition comprising a mixture of a monomer bearing 1 to 3 acrylate functionalities and one or more hydroxy groups, a mono- or polyepoxy monomer and an initiator. A silicone based anti-abrasion coating and a multilayer anti-reflecting coating are then successively formed on the primer coating.
• the substrate is made of mineral glass. The coated substrate shows good impact and abrasion resistances, good resistance to weathering, a good visual appearance, as well as a good adhesion between the layers.
• the substrate is a lens made of CR39 ® from PPG.
• the coated lenses have good performances with regard to impact resistance and adhesion.
• these primer coatings have not proven to be successfully applicable on a large variety of organic substrates in particular (meth)acrylic or polycarbonate based substrates.
• a primer coating composition which will provide improved impact resistance properties as well as good adhesion to a large variety of substrates, in particular organic glass substrates, and also to anti- abrasion coatings.
• a still further object of the invention is to provide an impact-resistant primer coating composition having low sensitivity to humidity.
• the impact-resistant primer coating composition according to the invention comprises :
• the acrylate monomer can be any acrylate monomer or mixtures thereof which exhibit a non-hydrophilic character.
• non-hydrophilic character there is meant an acrylate monomer free of any hydrophilic group such as OH.
• the at least one non-hydrophilic acrylate monomer is a mixture of (a)at least one acrylate monomer selected from the group consisting of mono and difunctional acrylate monomers and (b) at least one acrylate monomer selected from the group consisting of tri to hexaacrylate monomers.
• acrylate monomers that can be used in the primer coating composition of the invention, there can be cited :
• - mono- and polyacrylic esters of mono- or polyhydric alkanols in particular Cj - C ⁇ 2 alkanols, such as methyl, ethyl, propyl, butyl, hexyl and pentaerythrityl mono- and polyacrylates
• - mono- and polyacrylic esters of mono- or polyhydric cycloalkanols such as cyclobutyl, cyclopentyl, cyclohexyl, cycloheptyl and isobornyl mono- and polyacrylates ;
• - diacrylic esters of alkylene glycols and poly(alkylene) glycols in particular ethylene and propylene glycol and poly(ethylene) and (propylene) glycols such as ethylene or propylene glycol diacrylate, diethylene or dipropylene glycol diacrylate, triethylene or tripropylene glycol diacrylate, tetraethyleneglycol diacrylate and poly(ethylene) glycol diacrylate having up to 600 ethoxy units, such as polyethylene (200) diacrylate, polyethylene (400) diacrylate and polyethylene (600) diacrylate ; and - mono- and polyacrylic esters of mono- or polyhydric arylalkyl alcohols such as phenoxyethylacrylate.
• ethylene and propylene glycol and poly(ethylene) and (propylene) glycols such as ethylene or propylene glycol diacrylate, diethylene or dipropylene glycol diacrylate, triethylene or tripropylene glycol diacrylate, te
• the acrylate monomer derives from a polyol all the hydroxy groups of the polyol are esterified with acrylic acid in order to obtain a non-hydrophilic acrylate monomer.
• the amount of acrylate monomer in the primer composition ranges from 10 to 50% by weight, preferably 20 to 35% by weight based on the total weight of acrylate and epoxy monomers present in the composition.
• the epoxy monomer of the present primer composition can be any epoxy compound having one or more epoxy groups, in particular two, three or more epoxy groups.
• Preferred epoxy monomers are glycidyl ethers of polyhydric alkanols such as di- or triglycidyl ethers of alkane diols and triols.
• the amount of epoxy monomer in the primer composition ranges from 50 to 90% by weight, preferably 70 to 85% by weight based on the total weight of acrylate and epoxy monomers present in the composition.
• the photoactivable cationic catalyst of the primer composition can be any known photoactivable cationic catalyst, in particular UV activable cationic catalysts.
• photoactivable cationic catalysts there may be cited aromatic onium salts and iron arene salt complexes such as UVI 6990, UVI 6974..
• the amount of cationic catalyst present in the composition usually ranges from 0.01 to 5% by weight, preferably from 1 to 3% by weight, based on the total weight of the epoxy monomers present in the composition.
• the primer coating composition of the invention can be applied onto a large variety of plastic substrates, in particular transparent plastic materials commonly used for forming ophthalmic lenses.
• plastic materials there can be cited carbonate, (meth)acrylic, thio(meth)acrylic, (diethyleneglycol bisallylcarbonate), urethane, thiourethane, homopolymers and copolymers and mixtures thereof.
• the primer coating composition comprises at least one penta or hexaacrylate monomer.
• the primer coating composition comprises at least one mono or diacrylate monomer, which generally represents up to 10% by weight of the total weight of the acrylate monomers.
• the primer coating composition of the invention can be applied on the plastic material substrate using any well known direct coating method such as dip coating, flow coating and spin coating.
• the primer coating composition also preferably includes at least one photoinitiator for radical polymerisation of the monomers.
• These radical photoinitiators are well known in the art and include, for example Irgacure ® 500 from CIBA SPECIALTY CHEMICAL and Darocur ® 1173, Irgacure ® 819, Irgacure ® 184, benzophenone and acetophenone compounds.
• the amount of radical photoinitiator usually ranges from 1 to 10% by weight, preferably from 2 to 7% by weight based on the total weight of the acrylic monomers present in the composition.
• the primer coating composition can also be applied to the substrate using a transfer method such as the so-called "in mold coating (IMC)".
• IMC in mold coating
• this IMC method comprises providing a two-part mold, forming on at least one optical surface of the mold a layer of the primer coating composition according to the invention, optionally fully or partially curing the primer coating layer, assembling the mold parts, filling the molding cavity with a substrate precursor liquid curable monomer composition, curing the substrate composition and the primer coating layer if not already fully cured, and disassembling of the mold parts to recover the coated substrate. Then, preferably, the concentration of cationic catalyst is increased to between 8 to 14% by weight of the total epoxy concentration.
• Curing of the primer coating composition and of the substrate composition typically comprises photocuring, preferably UV-curing.
• the primer composition may also contain one or more photoinitiator for radical polymerisation
• the primer coating composition is preferably free of such photoinitiator which is then preferably included in the liquid polymerizable composition comprising the (meth)acrylic monomer used for forming the substrate. Then, preferably, the concentration of cationic catalyst is increased to between 8 to 14% by weight of the total epoxy concentrations.
• the primer coating composition of the invention can be cured using any well known photopolymerization process, and in particular UV photopolymerization.
• the thickness of the cured primer coating preferably ranges from 0.5 to 7 micrometers ( ⁇ m), more preferably from 1 to 6 micrometers and even better from 2 to 5 micrometers.
• the substrate coated with the primer coating can be overcoated with classical properties enhancing coatings such as anti-abrasion coating, anti- reflecting coating and top coat.
• an anti-abrasion coating can be applied onto the impact- resistant primer coating of the invention.
• Anti-abrasion coatings are well known in the art.
• Preferred anti-abrasion coatings are those made by curing a precursor composition including epoxyalkoxysilanes or a hydrolyzate thereof, silica and a curing catalyst. Examples of such compositions are disclosed in US-4,211,823 ; US-5,015,523 ; and WO-94/10230.
• the most preferred anti-abrasion coating compositions are those comprising as the main constituents an epoxyalkoxysilane such as, for example, ⁇ -glycidoxypropyltrimethoxysilane (GLYMO) and optionally a dialkyldialkoxysilane such as, for example, dimethyldiethoxysilane (DMDES), colloidal silica and a catalyst amount of a curing catalyst such as aluminium acetylacetonate or a hydrolyzate thereof, the remaining of the composition being essentially comprised of solvents typically used for formulating these compositions.
• GLYMO ⁇ -glycidoxypropyltrimethoxysilane
• DMDES dimethyldiethoxysilane
• colloidal silica such as aluminium acetylacetonate or a hydrolyzate thereof
• anti-abrasion coating compositions can be applied onto the primer coating using a direct coating method or a transfer method as described above.
• Anti-reflecting coatings and their methods of making are well known in the art.
• the anti-reflecting coating can be any layer or stack of layers which improves the anti-reflecting properties of the finished optical article.
• the anti-reflecting coating may preferably consist of a mono- or multilayer film of dielectric materials such as SiO, Si0 2 , Si 3 N , Ti0 2 , Zr0 2 , A1 2 0 3 , MgF 2 or Ta 2 ⁇ 5, or mixtures thereof.
• the anti-reflecting coating can be applied in particular by vacuum deposition according to one of the following techniques : l)-by evaporation, optionally ion-beam assisted ;
• the anti-reflecting coating is a multilayer film comprising three or more dielectric material layers of alternatively high and low refractive indexes.
• anti-reflecting coating can be done directly on the already coated substrate or through a transfer method such as the IMC method.
• the top coat typically a hydrophobic top coat, which in the finished optical article constitutes the outermost coating on the optical substrate, is intended for improving the dirty mark resistance of the finished optical article.
• hydrophobic top coats are well known in the art and are usually made of silicones or fluorosilicones. They can be deposited using any classical deposition process, but preferably using thermal evaporation technique. They can be applied on the coated substrate using a direct or a transfer method.
• Primer coating compositions 1 to 6 were prepared by mixing the ingredients as indicated in table I below.
• Coating Preparation (Composition 3) : 12.47 parts of pentaerythritol pentaacrylate was added to a clean dry light resistant glass bottle. Next, 11.96 parts of tripropyleneglycol diacrylate was added. 17.29 parts of 1,4-butanediol diglycidyl ether and 34.23 parts of trimethylolpropane triglycidyl ether were then added. To this mixture, 7.11 parts of each n-propanol, Dowanol-PM, and Arcosolv PnP were added and the bottle was closed. The mixture was gently shaken to form a homogeneous solution.
• FC-430 surfactant it is necessary to place the closed bottle in an ultrasonic water bath for approximately 20 minutes to eliminate bubbles prior to use.
• the particular order of addition of the acrylates and epoxies is not important.
• compositions 1, 2, 4, 5 and 6 are prepared in the same way as that of composition 3.
• the acrylates and/or the epoxies are added and mixed followed by the solvent mixture, photoinitiators, and finally the surfactant mixture if called for.
• Dowanol PM l-methoxy-2-propanol and 2-methoxy-l-propanol solvent commercialised by DOW CHEMICAL.
• Arcosolv PnP solvent commercialised by DOW CHEMICAL comprising a mixture of l-propoxy-2-propanol, 2-propoxy-l-propanol, propyleneglycol, diethyleneglycol and dipropylglycolmonopropylether.
• HIT 32.M colloidal stannic-titanium-zirconium oxide in methanol from
• FC-430 surfactant commercialised by 3M.
• the primer coating composition is applied to either the concave or the convex side of a finished or a surfaced semi- finished piano lens having a diameter of 70 mm and a center thickness of 2.0 mm for Mean index material and CR-39 ® and a center thickness of 1.5 mm for polycarbonate and Thin & Lite ® .
• the primer is applied at a flow rate of ⁇ 0.5 ml / second by spin coating.
• the coating is applied at a centrifugal speed of 600 rpm for 8 seconds followed by a final spin speed of 1400 rpm for a period of 10 seconds to apply a uniform film at a thickness of between 1 and 10 microns, preferably between 2 and 5 microns.
• the coating is then cured (polymerized) using UV radiation.
• a Fusion H-bulb was used at a distance of 12 cm from the lens. Typical energies necessary for cure are listed below :
• PC polycarbonate
• the above substrates coated with the primer coating compositions were coated with an organosilane abrasion-resistant coating composition.
• This coating composition identified as hard coating n°l is prepared as described in US patent 4.211.823 and is a mixture of GLYMO hydrolyzed in HC1 0.1N and colloidal silica (with a ratio
• This organosilane hard coating composition n°l is applied by dip or spin at a coating thickness of 2 microns.
• the coated lens is then cured for a period o 15 minutes at 80°C up to a tack free state.
• the coating is then further cured for a period of 3 hours at 100°C.
• N/A not able to measure.
• tinted substrates were coated as described above with primer coating composition n°4 and the above described anti-abrasion organosilane coating composition. Dry adhesion and adhesion after 30 minutes in boiling water of the resulting coated substrates were measured. The results and the nature of the tinted substrates are given in table VI below:
• SF-surfaced Semi-finished - surfaced lens - Mean index substrate (SF-surfaced) : Semi-finished - surfaced lens
• the primer coating compositions according to the invention exhibit good adhesion on a large variety of thermoplastic and thermosetting plastic materials and also provide good inter- coating adhesion to classical organopolysiloxane anti-abrasion coatings. Further, adhesion of the primer coatings of the invention to the substrate does not require prior surface modification of the substrate.
• Hard coating 2 The front part of a polycarbonate two-part mold already coated with a hydrophobic top coat and an AR coating was coated with an anti-abrasion coating composition (hard coating 2).
• Hard coating application speed was set at 600 rpm for 8 seconds and spin off speed at 1200 rpm for 10 seconds.
• Hard coating is UV cured by Fusion system H bulb at (5 feet per minute) 1.524 m/minute and followed by 30 seconds IR cure at 725F for 30 seconds, using LESCO IR curing unit. Coated mold was allowed to cool to room temperature and Impact Primer Coating composition of table VI below was applied at the same speed and timing as mentioned above.
• Impact primer coating was cured by UV light, using Fusion SYSTEM H bulb with belt speed of (5 feet per minute) 1.524 m/minute.
• the coated plastic mold was assembled, filed with a liquid optical substrate composition and polymerized within 20 minutes. Upon disassembly of the mold, all of the coatings transferred to the finished lens.
• the impact primer coating, substrate and hard coating compositions are given in tables VII, VHI and IX below :
• Irgacure 1850 mixture (50/50 by weight) of :
• Glymo ⁇ -glycidoxypropyltrimethoxysilane Colloidal silica : Sun Colloid MA-ST from NISSAN Company Tyzor DC :
• the hydrophobic top coat and anti-reflecting coating were deposited on the optical surface of the front part of the mold as follows :
• the hydrophobic top coat and anti-reflecting treatments are accomplished in a standard box coater using well known vacuum evaporation practices.
• a) The mold is loaded into the standard box coater such as a Balzers BAK760 and the chamber is pumped to a high vacuum level.
• Hydrophobic top coat, fluorosilazane (Shin Etsu KP801M) is deposited onto the optical surface of the first part of the mold using a thermal evaporation technique, to a thickness in the range of 2-15 nm.
• the dielectric multilayer anti-reflecting (AR) coating consisting of a stack of high- and low-index materials is then deposited, in reverse of the normal order.
• the first layer is a layer of Si0 2 having a physical thickness of 80-110 nm
• the second layer is a layer of Zr0 2 having a thickness of about 100 nm
• the third layer is a Si0 2 layer having a thickness of about 30 nm
• the fourth layer is a Zr0 2 having a thickness of about 55 nm.
• a thin layer of Si0 2 having a physical thickness of 1-50 nm, is deposited. This layer is to promote adhesion between the oxide antireflecting stack and the subsequent hard-coating which will be deposited on the coated mold at a later time.
• Tc Thickness at center : 1.34 mm
• NxlO blows is described in patent application WO99/49097 (ESSLLOR).
• the given value is the number of cycles that an anti-reflection treated lens can bear before the appearance of a defect.
• Bayer abrasion resistance was determined by measuring the percent haze of a coated and uncoated lens, before and after testing on an oscillating sand abrader as in ASTM F 735-81.
• the ratio of the uncoated lens haze (final-initial) is a measure of the performance of the coating, with a higher ratio meaning a higher abrasion resistance.
• Steel wool scratch resistance was determined by hand with a steel wool 0 0 0 grade.
• Dry adhesion was measured by cutting through the coating a series of 10 lines, spaced 1 mm apart, with a razor, followed by a second series of 10 lines, spaced 1 mm apart, at right angles to the first series, forming a Crosshatch pattern. After blowing off the Crosshatch pattern with an air stream too remove any dust formed during scribing, clear cellophane tape was then applied over the Crosshatch pattern, pressed down firmly, and then rapidly pulled away from coating in a direction perpendicular to the coating surface. Application and removal of fresh tape was then repeated two additional times. The lens was then submitted to tinting to determine the percentage adhesion, with tinted areas signifying adhesion failures. Adhesion after 30 minutes in boiling water was effected as indicated for the dry adhesion but after having immersed the test samples in boiling water for 30 minutes.
• Coating passes adhesion tests when percentage adhesion is more than 95%.
• Impact energy was measured using a proprietary system but can be measured by using the protocole of FDA drop ball test with increasing weights for the ball up to the breaking of the lens or the appearance of a visual crack, generally having the shape of a star, where the ball impacted. The corresponding energy is then measured.

Landscapes

• Chemical & Material Sciences (AREA)
• Organic Chemistry (AREA)
• Life Sciences & Earth Sciences (AREA)
• Engineering & Computer Science (AREA)
• Materials Engineering (AREA)
• Wood Science & Technology (AREA)
• Chemical Kinetics & Catalysis (AREA)
• Health & Medical Sciences (AREA)
• Medicinal Chemistry (AREA)
• Polymers & Plastics (AREA)
• Paints Or Removers (AREA)
• Surface Treatment Of Optical Elements (AREA)
• Materials For Medical Uses (AREA)
• Laminated Bodies (AREA)
• Coating Of Shaped Articles Made Of Macromolecular Substances (AREA)

Priority Applications (3)

Applications Claiming Priority (2)

Publications (2)

Family

ID=23133363

Family Applications (1)

Country Status (6)

Cited By (2)

Families Citing this family (12)

Citations (3)

Family Cites Families (15)

• 2002
  • 2002-05-27 WO PCT/EP2002/005794 patent/WO2002096966A1/en not_active Ceased
  • 2002-05-27 EP EP02745321A patent/EP1401901B1/en not_active Expired - Lifetime
  • 2002-05-27 DE DE60221527T patent/DE60221527T2/de not_active Expired - Lifetime
  • 2002-05-27 AT AT02745321T patent/ATE368692T1/de not_active IP Right Cessation
  • 2002-05-27 JP JP2003500145A patent/JP3834034B2/ja not_active Expired - Fee Related
  • 2002-05-29 US US10/157,177 patent/US7067565B2/en not_active Expired - Lifetime

Patent Citations (3)