Classifications

• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
  • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
  • B01J20/00—Solid sorbent compositions or filter aid compositions; Sorbents for chromatography; Processes for preparing, regenerating or reactivating thereof
  • B01J20/28—Solid sorbent compositions or filter aid compositions; Sorbents for chromatography; Processes for preparing, regenerating or reactivating thereof characterised by their form or physical properties
  • B01J20/28014—Solid sorbent compositions or filter aid compositions; Sorbents for chromatography; Processes for preparing, regenerating or reactivating thereof characterised by their form or physical properties characterised by their form
  • B01J20/28042—Shaped bodies; Monolithic structures
  • B01J20/28045—Honeycomb or cellular structures; Solid foams or sponges
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
  • B01D—SEPARATION
  • B01D53/00—Separation of gases or vapours; Recovering vapours of volatile solvents from gases; Chemical or biological purification of waste gases, e.g. engine exhaust gases, smoke, fumes, flue gases, aerosols
  • B01D53/02—Separation of gases or vapours; Recovering vapours of volatile solvents from gases; Chemical or biological purification of waste gases, e.g. engine exhaust gases, smoke, fumes, flue gases, aerosols by adsorption, e.g. preparative gas chromatography
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
  • B01D—SEPARATION
  • B01D53/00—Separation of gases or vapours; Recovering vapours of volatile solvents from gases; Chemical or biological purification of waste gases, e.g. engine exhaust gases, smoke, fumes, flue gases, aerosols
  • B01D53/34—Chemical or biological purification of waste gases
  • B01D53/74—General processes for purification of waste gases; Apparatus or devices specially adapted therefor
  • B01D53/86—Catalytic processes
  • B01D53/88—Handling or mounting catalysts
  • B01D53/885—Devices in general for catalytic purification of waste gases
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
  • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
  • B01J20/00—Solid sorbent compositions or filter aid compositions; Sorbents for chromatography; Processes for preparing, regenerating or reactivating thereof
  • B01J20/02—Solid sorbent compositions or filter aid compositions; Sorbents for chromatography; Processes for preparing, regenerating or reactivating thereof comprising inorganic material
  • B01J20/06—Solid sorbent compositions or filter aid compositions; Sorbents for chromatography; Processes for preparing, regenerating or reactivating thereof comprising inorganic material comprising oxides or hydroxides of metals not provided for in group B01J20/04
  • B01J20/08—Solid sorbent compositions or filter aid compositions; Sorbents for chromatography; Processes for preparing, regenerating or reactivating thereof comprising inorganic material comprising oxides or hydroxides of metals not provided for in group B01J20/04 comprising aluminium oxide or hydroxide; comprising bauxite
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
  • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
  • B01J20/00—Solid sorbent compositions or filter aid compositions; Sorbents for chromatography; Processes for preparing, regenerating or reactivating thereof
  • B01J20/02—Solid sorbent compositions or filter aid compositions; Sorbents for chromatography; Processes for preparing, regenerating or reactivating thereof comprising inorganic material
  • B01J20/10—Solid sorbent compositions or filter aid compositions; Sorbents for chromatography; Processes for preparing, regenerating or reactivating thereof comprising inorganic material comprising silica or silicate
  • B01J20/16—Alumino-silicates
  • B01J20/18—Synthetic zeolitic molecular sieves
  • B01J20/183—Physical conditioning without chemical treatment, e.g. drying, granulating, coating, irradiation
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
  • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
  • B01J20/00—Solid sorbent compositions or filter aid compositions; Sorbents for chromatography; Processes for preparing, regenerating or reactivating thereof
  • B01J20/02—Solid sorbent compositions or filter aid compositions; Sorbents for chromatography; Processes for preparing, regenerating or reactivating thereof comprising inorganic material
  • B01J20/10—Solid sorbent compositions or filter aid compositions; Sorbents for chromatography; Processes for preparing, regenerating or reactivating thereof comprising inorganic material comprising silica or silicate
  • B01J20/16—Alumino-silicates
  • B01J20/18—Synthetic zeolitic molecular sieves
  • B01J20/186—Chemical treatments in view of modifying the properties of the sieve, e.g. increasing the stability or the activity, also decreasing the activity
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
  • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
  • B01J20/00—Solid sorbent compositions or filter aid compositions; Sorbents for chromatography; Processes for preparing, regenerating or reactivating thereof
  • B01J20/28—Solid sorbent compositions or filter aid compositions; Sorbents for chromatography; Processes for preparing, regenerating or reactivating thereof characterised by their form or physical properties
  • B01J20/28002—Solid sorbent compositions or filter aid compositions; Sorbents for chromatography; Processes for preparing, regenerating or reactivating thereof characterised by their form or physical properties characterised by their physical properties
  • B01J20/28011—Other properties, e.g. density, crush strength
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
  • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
  • B01J20/00—Solid sorbent compositions or filter aid compositions; Sorbents for chromatography; Processes for preparing, regenerating or reactivating thereof
  • B01J20/28—Solid sorbent compositions or filter aid compositions; Sorbents for chromatography; Processes for preparing, regenerating or reactivating thereof characterised by their form or physical properties
  • B01J20/28014—Solid sorbent compositions or filter aid compositions; Sorbents for chromatography; Processes for preparing, regenerating or reactivating thereof characterised by their form or physical properties characterised by their form
  • B01J20/28042—Shaped bodies; Monolithic structures
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
  • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
  • B01J20/00—Solid sorbent compositions or filter aid compositions; Sorbents for chromatography; Processes for preparing, regenerating or reactivating thereof
  • B01J20/28—Solid sorbent compositions or filter aid compositions; Sorbents for chromatography; Processes for preparing, regenerating or reactivating thereof characterised by their form or physical properties
  • B01J20/28054—Solid sorbent compositions or filter aid compositions; Sorbents for chromatography; Processes for preparing, regenerating or reactivating thereof characterised by their form or physical properties characterised by their surface properties or porosity
  • B01J20/28057—Surface area, e.g. B.E.T specific surface area
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
  • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
  • B01J20/00—Solid sorbent compositions or filter aid compositions; Sorbents for chromatography; Processes for preparing, regenerating or reactivating thereof
  • B01J20/28—Solid sorbent compositions or filter aid compositions; Sorbents for chromatography; Processes for preparing, regenerating or reactivating thereof characterised by their form or physical properties
  • B01J20/28054—Solid sorbent compositions or filter aid compositions; Sorbents for chromatography; Processes for preparing, regenerating or reactivating thereof characterised by their form or physical properties characterised by their surface properties or porosity
  • B01J20/28057—Surface area, e.g. B.E.T specific surface area
  • B01J20/28061—Surface area, e.g. B.E.T specific surface area being in the range 100-500 m2/g
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
  • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
  • B01J29/00—Catalysts comprising molecular sieves
  • B01J29/04—Catalysts comprising molecular sieves having base-exchange properties, e.g. crystalline zeolites
  • B01J29/06—Crystalline aluminosilicate zeolites; Isomorphous compounds thereof
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
  • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
  • B01J29/00—Catalysts comprising molecular sieves
  • B01J29/04—Catalysts comprising molecular sieves having base-exchange properties, e.g. crystalline zeolites
  • B01J29/06—Crystalline aluminosilicate zeolites; Isomorphous compounds thereof
  • B01J29/40—Crystalline aluminosilicate zeolites; Isomorphous compounds thereof of the pentasil type, e.g. types ZSM-5, ZSM-8 or ZSM-11, as exemplified by patent documents US3702886, GB1334243 and US3709979, respectively
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
  • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
  • B01J35/00—Catalysts, in general, characterised by their form or physical properties
  • B01J35/30—Catalysts, in general, characterised by their form or physical properties characterised by their physical properties
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
  • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
  • B01J35/00—Catalysts, in general, characterised by their form or physical properties
  • B01J35/50—Catalysts, in general, characterised by their form or physical properties characterised by their shape or configuration
  • B01J35/56—Foraminous structures having flow-through passages or channels, e.g. grids or three-dimensional [3D] monoliths
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
  • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
  • B01J35/00—Catalysts, in general, characterised by their form or physical properties
  • B01J35/60—Catalysts, in general, characterised by their form or physical properties characterised by their surface properties or porosity
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
  • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
  • B01J35/00—Catalysts, in general, characterised by their form or physical properties
  • B01J35/60—Catalysts, in general, characterised by their form or physical properties characterised by their surface properties or porosity
  • B01J35/64—Pore diameter
  • B01J35/651—50-500 nm
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
  • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
  • B01J37/00—Processes, in general, for preparing catalysts; Processes, in general, for activation of catalysts
  • B01J37/0009—Use of binding agents; Moulding; Pressing; Powdering; Granulating; Addition of materials ameliorating the mechanical properties of the product catalyst
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
  • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
  • B01J37/00—Processes, in general, for preparing catalysts; Processes, in general, for activation of catalysts
  • B01J37/0009—Use of binding agents; Moulding; Pressing; Powdering; Granulating; Addition of materials ameliorating the mechanical properties of the product catalyst
  • B01J37/0018—Addition of a binding agent or of material, later completely removed among others as result of heat treatment, leaching or washing,(e.g. forming of pores; protective layer, desintegrating by heat)
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
  • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
  • B01J37/00—Processes, in general, for preparing catalysts; Processes, in general, for activation of catalysts
  • B01J37/08—Heat treatment
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
  • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
  • B01J2220/00—Aspects relating to sorbent materials
  • B01J2220/40—Aspects relating to the composition of sorbent or filter aid materials
  • B01J2220/42—Materials comprising a mixture of inorganic materials
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
  • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
  • B01J35/00—Catalysts, in general, characterised by their form or physical properties
  • B01J35/60—Catalysts, in general, characterised by their form or physical properties characterised by their surface properties or porosity
  • B01J35/61—Surface area
  • B01J35/615—100-500 m2/g

Definitions

• the present invention relates to a improved zeolite/silica/alumina material and a method for making such material.
• a zeolite/silica/alumina composite material exhibiting a high strength and a high surface area.
• a catalytic converter is installed on an automobile to purify the exhaust gas stream.
• the catalytic converter removes unburned gasoline, carbon monoxide and nitrogen oxides simultaneously in the exhaust stream.
• a conventional catalytic converter consists of a multi-channel ceramic honeycomb and includes a high surface area material that is, along with the actual catalytic material
• the monolithic ceramic honeycomb provides a strong substrate for the catalyst, in addition to meeting mechanical and thermal requirements. However, acting as an inert structure, the catalyst substrate does not participate in the chemical reactions for removal of unburned hydrocarbons, carbon monoxide and nitrogen oxides.
• US Patent No. Re. 34,804 discloses the formation of extruded zeolite honeycomb bodies that include a permanent binder silicone resin component.
• An improved method for making the zeolite body is disclosed in U.S. Pat. No 5,492,883 (Wu) wherein the zeolite material is mixed with an aqueous silicone resin emulsion and, a temporary binder, such as methylcellulose, and the mixture is extruded to form a green honeycomb body, which is thereafter dried and sintered.
• Another improved method for making a zeolite body is disclosed in U.S. Pat. No.
• Wu, Lynn and Lachman references are not inert and are capable of use as a catalyst material, they each require the application of a precious metal washcoat in order to function as a three-way catalyst capable of the conversion of hydrocarbons, nitrogen oxides and carbon monoxide into their nontoxic gaseous counterparts.
• zeolite based materials to be used as monolithic honeycombs at increased temperatures (>300°C) the zeolite material should exhibit the following combination of properties, not currently possessed by conventional zeolite bodies: high strength, high surface area, high thermal stability (i.e. high thermal shock resistance) and a low coefficient of thermal expansion.
• the object of the present invention is to solve the above problems of the prior art and to provide high strength, high surface area zeolite material exhibiting a high thermal stability and low thermal expansion.
• the invention is directed at a zeolite based material for use as a catalyst substrate, adsorber or catalyst carrier comprising a zeolite having a silica alumina ratio of greater at least 300 and a surface area of 250m " /g and no greater than about 20 parts, by weight, of a silica binder.
• the properties this zeolite based material exhibits includes the following: (1) a modulus of rupture of at least 1500 psi; (2) a surface area of at least lOOmJg; (3) a coefficient of thermal expansion of less than about +/-10 ppm/°C; and, (4) a thermal shock resistance of at least 850°C.
• the zeolite-based material includes a third component, specifically gamma alumina having a specific surface area of greater than 100 m 2 /g.
• This invention also relates to a method for producing an extruded honeycomb monolith having the aforementioned high strength and surface area properties, comprising mixing into a substantially homogeneous body the following components: (1) a zeolite having a silica/alumina ratio of at least 300 to 1 and a surface area of at least 250 m 2 /g; (2) no greater than 20 parts, by weight, of a silica binder derived from using a resin/solvent mixture having a ratio ranging between from 2/1 to 4/1; (3) a temporary binder; and, (4) water.
• the method involves extruding the mixture to form a green honeycomb structure, and then drying the structure for a time sufficient to form a crack-free dry structure. Once the extruded body is dried, the method next involves heating the dried honeycomb structure in a nitrogen atmosphere, to a first temperature of at least 500°C, cooling to ambient, and thereafter, heating, in air, to a second temperature of at least 850°C to form a sintered structure.
• the product of the present invention is a zeolite body for use as an adsorber or catalyst carrier, specifically a zeolite-based material wherein the zeolite exhibits a silica/alumina ratio of at least more than 300 and a surface area of at least 250 m 2 /g.
• the zeolite based bodies, according to the invention characteristically contain between about 30 to 90 parts, by weight, zeolite and at least
• silica binder 20 parts, by weight, silica binder.
• zeolites typically comprise large particles on the order of several microns and exhibit a regular array of accessible micropores, a combination that provides the high surface attribute of zeolites; a feature that is retained by zeolites after sintering.
• catalyst support and adsorber applications require substantial overall surface areas of at least 20m7g, preferably greater than lOOrrf/g, and most preferably greater than 150-200 m 2 /g.
• the inventive zeolite based body is capable of being extruded into a high cell density, thin walled monolithic body, e.g., a honeycomb structure exhibiting at least 400 cells/in " , exhibiting surface areas of at least 200 m"/g, with surface areas in excess of 250 m7g being readily attainable.
• the zeolite component is desirably a high silica-containing zeolite exhibiting a SiO 2 /Al 2 O 3 molar ratio of at least 300.
• the presence of a zeolite having the requisite high silica/alumina ratio provides for a zeolite-based material having both a thermal stability at those high temperatures typically experienced in the exhaust environment, and the expected ability to adsorb and desorb hydrocarbons.
• the high silica content of the zeolite provides the composite with the ability to maintain its structure at high temperatures.
• the presence of a low alumina content in the zeolite ensures that the zeolite will not experience the type of moisture problems typically associated with zeolites having high alumina content; high alumina zeolites typically de-aluminate in the presence of moisture at high temperatures. Furthermore, the zeolites crystalline silica phase is maintained at high temperatures and is responsible for the negative CTE characteristic that compensates to reduce the overall thermal expansion of the composite body.
• the inventive material provides for a zeolite adsorber material that allows the automotive exhaust system designer a certain degree of flexibility in exhaust system design; adsorber material having increased thermal stability. Suitable zeolites include any silica-based zeolite having the requisite very high silica/alumina ratio.
• Useful high silica/alumina ratio-containing zeolites for the practice of the invention can be found among the zeolites selected from the following: mordenite, ultrastabilized Y (USY), ZSM-5, ZSM-8, ZSM-11, ZSM-12, Hyper Y, beta- zeolites, H-ferrierite, H-rissatite, faujasite, X zeolite, type L zeolite, mazzite, EMC-2, and combinations of these, preferably silicalite, and any of the natural zeolites including erionite, clinoptilolite, chanazite and phillipsite.
• One commercially available zeolite having the requisite high silica property is CBV 3002 available from the PQ Corporation.
• this zeolite body In addition to a high surface area, other features of this zeolite body that make it suitable for use as an adsorber material include its relatively low thermal expansion and high thermal stability; less than 10ppm °C, preferably 5 ppm/°C, and thermal stability up to at least 1000°C, respectively. Furthermore, catalyst support applications and filter/adsorber applications preferably require a flexural strength in excess of 1500 psi.
• the zeolite body of the instant invention exhibits flexural and crushing strengths that exceed this value and are on the order of greater than about 1500 psi, with MOR's in excess of 3500 psi being attainable.
• a second embodiment of the inventive zeolite body comprises the inclusion of a third component, a gamma alumina having a surface area of greater than 100 m2/g.
• the gamma alumina component having the high surface area also contributes to result in an overall zeolite-based body that is well within the surface area requirements of many catalyst support applications.
• the zeolite/silica/alumina bodies, according to the invention characteristically contain between about 85 to 90 parts, by weight, zeolite and 10-15 parts, by weight, silica binder, and up to 50, parts, by weight, alumina.
• the presence of silica prevents the incorporation of PGM catalysts into the extruded zeolite substrate, due to silica's known PGM incompatibility, the presence of alumina in this embodiment provides the zeolite-based composite structure the support material function for non-PGM catalysts. Specifically the gamma alumina provides the necessary sites to enable binding of transition metal oxide catalyst to the structure, such that the composite will have enhanced catalytic activity and lifetimes over zeolite-only structures, when used in the certain harsh environments typically associated with high temperature, such as seen in chemical processing applications.
• the alumina, whereby the transition metal oxides are typically sited is porous enough and exhibits a high enough surface area porous structure so as to inhibit sintering of the metal oxides present and to provide for the accessibility of the transition metal oxides to the reactant stream.
• Gamma alumina suitable for use in the formation of this composite include those aluminas that after calcining provide the requisite gamma alumina phase and exhibit a sufficiently high surface area suitable for functioning as the catalytic support material.
• a suitable commercially available gamma alumina having the requisite high surface area characteristic is GL-25 supplied by LaRoche Industries.
• the zeolite body should include a stabilized high surface area alumina.
• the stabilized alumina should include an amount of stabilizing agent selected from the group consisting of lanthanum oxide (La 2 O 3 ) or it equivalents, including barium oxide, strontium oxide and yttrium oxide.
• stabilizing agents are known for stabilizing the specific surface area of the alumina, which in its pure form is typically unstable at high temperatures. Specifically, the stabilizing agents inhibit the phase transformation of alumina at high temperatures, thereby increasing the high temperature stability of the alumina.
• the stabilizing agents are typically included in the alumina as a pre-dopant prior to the batching of the composite, and more preferably they are added to the composite after firing via an impregnation process.
• a preferred stabilizing agent for the alumina is lanthanum oxide (La 2 O 3 ), which is included by impregnation into the gamma alumina component of the composite.
• Lanthanum impregnation is such that the composite includes lanthanum oxide in the weight range of 0.5-20, parts, by weight, with respect to the alumina component amount. If lanthanum is added in an amount less than such range, then the beneficial effect of increase in activity due to the lanthanum addition is not observed.
• porosity as measured by total porosity, of the zeolite/alumina composite should be sufficient to permit access to the transition metal oxide catalyst through the walls.
• porosity as measured by average pore size, should be sufficient to allow the support to function effectively as an adsorber.
• the inventive zeolite structures may exhibit a total porosity of about at least about 30%, along with sub micron average pore sizes.
• the inventive high silica/alumina zeolite material can be used as a catalyst substrate, specifically, as a replacement for cordierite.
• the inventive zeolite can be used as a catalyst substrate in those applications where it performs the additional function of adsorbing hydrocarbon during the cold-start stage (e.g., Bag I and T emissions).
• the zeolite honeycomb substrate is washcoated with a conventional three-way catalyst, and catalyst system performs in the same manner as a regular cordierite supported three-way catalyst system.
• Suitable catalytic materials for supporting on the high silica/alumina zeolite substrate include platinum, palladium, rhodium and iridium.
• the zeolite substrate is comprised of a zeolite material that exhibits high thermal stability under automotive exhaust conditions.
• Suitable zeolites include those selected from the following materials: mordenite, ultrastabilized Y (USY), ZSM-5, ZSM-8, ZSM- 11 , ZSM- 12, all exhibiting a silica/alumina ratio of 300 and above.
• the zeolite substrate is washcoated with an oxidation catalyst; suitable oxidation catalysts including platinum, palladium rhodium or iridium.
• the washcoated zeolite catalyst functions as a hydrocarbon trap for reducing hydrocarbon emissions during the cold-start stage.
• Zeolite material choices for the substrate include the following: beta-zeolite, USY and ZSM-5 and mordenite, all exhibiting the requisite high silica/alumina ratio of 300 or above. These large pore zeolites exhibit a large capacity for the adsorption of hydrocarbon, while at the same time exhibiting requisite thermal stability to survive the harsh environment in an automotive exhaust stream.
• the general method of producing porous sintered substrates is by mixing batch materials, blending the mixture, forming a green body, and subsequently sintering the green body to a hard porous structure.
• various lubricants such as zinc stearate and sodium stearate, and organic binders are added to the batch during the mixing step to provide viscosity control and strength prior to firing and porosity to the after fired structure.
• a particularly preferred method for producing the composite of the invention described herein, an extruded honeycomb monolith having a high surface area comprises mixing into a substantially homogeneous body certain raw materials capable of forming the aforementioned composite.
• the raw materials that will form a composite include a zeolite raw material that exhibits a silica/alumina ratio of at least 300 to 1 and a surface area of at least 250 m 2 /g, a silica binder exhibiting a resin/solvent ratio of between 2/1 to 4/1 and, optionally, a gamma alumina component exhibits a specific surface area of greater than 100 mJg.
• the batch mixture should include a temporary organic binder and water.
• the preferred method of forming the body includes extruding the body to form a green honeycomb structure. Once formed into a honeycomb body the extruded green body is then dried by heating the structure for a time period sufficient to form a crack-free dry structure.
• the drying step is accomplished in a number of different ways.
• One embodiment involves placing the structure in an oven at a temperature in the range of 50 to 100°C, preferably, at a temperature in the range of 90 to 100°C for periods of up to 4 days.
• the drying step is accomplished by placing the green structure in a relative humidity controlled oven (e.g., 90% relative humidity) for similar time periods and temperatures as for the aforementioned standard oven-drying embodiment.
• the drying step is accomplished by placing the green structure in a dielectric oven for a period of time sufficient to form a crack-free, self-supporting structure, preferably, a period of no greater than 60 minutes, more preferably for a period of 5 to 30 minutes.
• Sintering of the dried honeycomb structure involves heating or sintering the honeycomb for a time period sufficient to form a sintered structure having a high surface area.
• the sintering comprises heating the honeycomb in a nitrogen atmosphere, at a rate 10-25°C/hr, to a first temperature of at least 500°C, preferably this temperature is then maintained for period of up to 10 hours, more preferably 4 hours.
• the honeycomb is cooled to ambient temperature. Once ambient temperature is attained, the honeycomb is heated, in air, to a second temperature of at least 850°C, preferably 1100°C.
• This second air-heating step, to at least 850°C may involve two distinct heating steps: (1) a first heating step, at a rate of between 10-25°C/hr to 500°C, whereupon the temperature is held for period of time; and, (2) and a second heating step from 500°C to at least 850°C, at a rate of about 50°C/hr, whereupon the temperature is again held for a period of time.
• the temperature-holds are preferably maintained for period of up to 10 hours, and more preferably 4 hours.
• the pre-treatment nitrogen heating step is thought to result in sintered structures exhibiting an increased MOR over those bodies not subject to this pre-treatment step. While not intending to be limited by theory it is thought that the nitrogen pre-treatment produces a gradual slow burnout of the organic binder that does not disrupt the microstructure of the zeolite bodies, thus allowing for easier densification of the zeolite body at the later achieved higher firing temperatures.
• the purpose of the organic binder is to provide plasticity during forming, and some green strength after drying.
• Organic binder according to the present invention refers to cellulose ether type binders and/or their derivatives, some of which are thermally gellable.
• Some typical organic binders according to the present invention are methylcellulose, hydroxybutylcellulose, hydrobutyl methylcellulose, hydroxyethylcellulose, hydroxymethylcellulose, hydroxypropylcellulose, hydroxypropyl methylcellulose, hydroxyethyl methylcellulose, sodium carboxy methylcellulose, and mixtures thereof.
• Methylcellulose and/or methylcellulose derivatives are typically used in the practice of the present invention.
• Methylcellulose, hydroxypropyl methylcellulose, and combinations thereof are especially preferred.
• Preferred sources of cellulose ethers and or derivatives thereof are Methocel A4M, F4M, and F240M from Dow Chemical Co.
• Methocel A4M is a methylcellulose binder having a gel temperature of 50-55°C and gel strength of 5000 g/cm 2 (based on 2% solution at 65°C).
• Methocel F4M and F240M are hydroxypropyl methylcellulose.
• the zeolite raw material comprised a ZSM-5 zeolite having an SiO 2 /A12O 3 ratio of 300 (CBV-3002 from PQ Corporation) and a silica binder comprising an amount of a concentrated silicone resin (6-2230 resin from Dow Corning) dissolved in a dibasic ester solution with the resin/solvent ratio reported in the Table; in each example the amount of resin resulted in the amount of silica permanent binder reported in the fired composition.
• the mixed batch was transferred to a muller and an amount of water, in as reported in Table I, was added to the batch and the batch was uniformly plasticized; the water listed as a superaddition weight percent based on the fired composition.
• Honeycomb bodies with a wall thickness of about 8 mil and exhibiting 400 cells/in 2 and rods suitable for testing MOR, exhibiting a diameter of 0.3125 in. were formed by extrusion through a ram extruder.
• Each of the two examples, green extruded honeycombs and the rods were dried in the following manner: RT to 95°C in a humidity oven (95-100% relative humidity) for a period of 4 days. After drying, the extruded honeycombs and rods were pre-fired in an N 2 atmosphere at a rate of between 15-25°C/hr. to 500°C, where temperature was held for a period of 4 hours.
• the honeycombs were cooled to room temperature and then heated in air, at a rate of between 15-25°C/hr, to a temperature of 500°C, where again the temperature was held for a period of 4 hours. Following this hold, the firing involved heating the honeycombs, at a rate of between 25-50°C/hr, to a final temperature of 1100°C, where the honeycombs were held for a final period of 4 hours.
• the composition of the fired body is reported in Table I.
• the resultant rods were used for characterization of mechanical properties such as MOR, CTE, and E-modulus.
• the porosity and mean pore size data was measured for the honeycombs and was generated utilizing a conventional mercury intrusion porosimetry technique. All of these physical properties for the canes and honeycomb are detailed listed in TABLE I.
• EXAMPLES 3-7 Each example involved thoroughly mixing together in a Littleford mixer a batch mixture as provided Table I.
• the zeolite raw material comprised a ZSM-5 zeolite having an SiO 2 /A12O 3 of 300 (CBV-3002 from PQ Corporation), the gamma alumina raw material comprised GL-25 supplied from LaRoche Industries (surface area of 260 m ⁇ /g), and the methylcellulose temporary binder comprised Methocel A4M from the Dow Chemical Co.
• the batch mixture additionally comprised an amount of a concentrated silicone resin (6-2230 resin from Dow Corning) dissolved in a dibasic ester solution having the resin/solvent ratio reported in the Table; in each example the amount of resin resulted in the amount of silica permanent binder reported in the fired composition.
• a concentrated silicone resin 6-2230 resin from Dow Corning
• a dibasic ester solution having the resin/solvent ratio reported in the Table; in each example the amount of resin resulted in the amount of silica permanent binder reported in the fired composition.
• the mixed batch then was transferred to a muller and amount of water, as reported in Table I, was added to the batch and the batch was uniformly plasticized; note that each of the weight percents listed in Table 1 for the water, oleic and acetic acids are superaddition weight percents based on the final fired composition.
• Honeycomb bodies with a wall thickness of about 8 mil and exhibiting 400 cells/in 2 and rods suitable for testing MOR, exhibiting a diameter of 0.3125 in. were formed by extrusion through a ram extruder.
• the green extruded honeycombs and rods of Examples 3-5 and 7 were dried in manner similar to that for Examples 1 and 2.
• Example 6 was dried in a dielectric oven for a period of 20 minutes. After drying, the extruded honeycomb and rod green bodies were fired in a manner similar to that utilized for Examples 1 and 2 with the exception that the temperature was not held at 500°C, following the second ramp-up, in air. The final fired composition, physical and mechanical properties of the extruded zeolite/silica/alumina bodies are shown in TABLE I.
• inventive samples 1 and 2 exhibit the requisite combination of properties. Specifically, the inventive samples 1 and 2 exhibit the following combination of properties: (1) a surface area of not less than 235 m 2 /g; (2) an MOR of at least 1520 psi;
• inventive samples 3-6 containing a gamma alumina ranging from 10 to 50 parts, by weight, exhibit the requisite combination of properties.
• inventive samples 3-6 exhibit the following combination of properties: (1) a surface area of not less than 170 m 2 /g; (2) an MOR of at least 2270 psi; (3) a CTE less than 2 ppm/°C; and, (4) a calculated thermal shock resistance of at least 1510°C.
• zeolite/silica body comprising 10 parts, by weight silica
• TABLE I reveals that this sample has a less than desirable MOR of 483 psi.

Landscapes

• Chemical & Material Sciences (AREA)
• Chemical Kinetics & Catalysis (AREA)
• Organic Chemistry (AREA)
• Engineering & Computer Science (AREA)
• Analytical Chemistry (AREA)
• Materials Engineering (AREA)
• Inorganic Chemistry (AREA)
• General Chemical & Material Sciences (AREA)
• Environmental & Geological Engineering (AREA)
• Oil, Petroleum & Natural Gas (AREA)
• Crystallography & Structural Chemistry (AREA)
• Biomedical Technology (AREA)
• Health & Medical Sciences (AREA)
• Physics & Mathematics (AREA)
• Thermal Sciences (AREA)
• Catalysts (AREA)
• Exhaust Gas After Treatment (AREA)
• Solid-Sorbent Or Filter-Aiding Compositions (AREA)
• Silicates, Zeolites, And Molecular Sieves (AREA)

Priority Applications (4)

Applications Claiming Priority (2)

Publications (1)

Family

ID=22632725

Family Applications (1)

Country Status (7)

Cited By (11)

Families Citing this family (17)

Citations (3)

Family Cites Families (19)

• 2000
  • 2000-12-07 DE DE60023743T patent/DE60023743T2/de not_active Expired - Lifetime
  • 2000-12-07 WO PCT/US2000/033157 patent/WO2001049409A1/en not_active Ceased
  • 2000-12-07 KR KR1020027008512A patent/KR20020080357A/ko not_active Withdrawn
  • 2000-12-07 EP EP00982494A patent/EP1242182B1/en not_active Expired - Lifetime
  • 2000-12-07 JP JP2001549767A patent/JP4771639B2/ja not_active Expired - Fee Related
  • 2000-12-07 CN CNB008179271A patent/CN1153619C/zh not_active Expired - Lifetime
  • 2000-12-12 US US09/735,225 patent/US6548439B2/en not_active Expired - Lifetime

Patent Citations (3)

Non-Patent Citations (1)

Also Published As

Similar Documents

Legal Events