WO2001030519A1 - PROCEDE DE MOULAGE DE PRECISION PAR PRESSION D'UN ALLIAGE DE Mg, DISPOSITIF DE MOULAGE CORRESPONDANT ET MOULAGE EN ALLIAGE DE Mg PRODUIT CONFORMEMENT AUDIT PROCEDE - Google Patents

PROCEDE DE MOULAGE DE PRECISION PAR PRESSION D'UN ALLIAGE DE Mg, DISPOSITIF DE MOULAGE CORRESPONDANT ET MOULAGE EN ALLIAGE DE Mg PRODUIT CONFORMEMENT AUDIT PROCEDE Download PDF

Info

Publication number
WO2001030519A1
WO2001030519A1 PCT/JP2000/007227 JP0007227W WO0130519A1 WO 2001030519 A1 WO2001030519 A1 WO 2001030519A1 JP 0007227 W JP0007227 W JP 0007227W WO 0130519 A1 WO0130519 A1 WO 0130519A1
Authority
WO
WIPO (PCT)
Prior art keywords
mold
alloy
movable
precision pressure
product
Prior art date
Application number
PCT/JP2000/007227
Other languages
English (en)
Japanese (ja)
Inventor
Manabu Matsumoto
Shigefumi Matsumoto
Original Assignee
Matsumoto Seisakusho Co., Ltd.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Matsumoto Seisakusho Co., Ltd. filed Critical Matsumoto Seisakusho Co., Ltd.
Priority to AU79475/00A priority Critical patent/AU7947500A/en
Publication of WO2001030519A1 publication Critical patent/WO2001030519A1/fr

Abstract

L'invention concerne un procédé de moulage de précision par pression d'un alliage de Mg, le dispositif de moulage correspondant et un moulage en alliage de Mg produit conformément audit procédé, lequel procédé permet d'éliminer les défauts classiques, inhérents à la technique, se produisant lors de la coulée sous pression d'un alliage de Mg, à savoir qu'il est difficile de couler des pièces compactes à paroi mince exemptes de friasses ou de cavités de surface et que lesdites parties sont coulées avec une proportion de défectuosités très élevée. Dans le cas de pièces à paroi épaisse, il est possible d'obtenir par compression des moulages présentant un nombre réduit de friasses et de cavités de surface, une résistance accrue et une rugosité de surface réduite. L'invention concerne également un procédé de production d'un moulage en alliage de Mg, consistant à cramper un premier moule en utilisant la force de crampage du moule d'une machine à mouler, et ce sous basse pression, jusqu'à obtenir une épaisseur de 0,1 % à 20 % environ plus importante que l'épaisseur du produit ; à verser un métal en fusion d'alliage de Mg dans une cavité, et à cramper un second moule, une ou plusieurs fois, sous haute pression, de manière à comprimer ou à forger les parties d'un produit.
PCT/JP2000/007227 1999-10-22 2000-10-18 PROCEDE DE MOULAGE DE PRECISION PAR PRESSION D'UN ALLIAGE DE Mg, DISPOSITIF DE MOULAGE CORRESPONDANT ET MOULAGE EN ALLIAGE DE Mg PRODUIT CONFORMEMENT AUDIT PROCEDE WO2001030519A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
AU79475/00A AU7947500A (en) 1999-10-22 2000-10-18 Mg alloy precision pressure molding method and molding device therefor and mg alloy molding produced thereby

Applications Claiming Priority (6)

Application Number Priority Date Filing Date Title
JP33837899 1999-10-22
JP11/338378 1999-10-22
JP2000/171143 2000-06-07
JP2000171143 2000-06-07
JP2000/295680 2000-09-28
JP2000295680A JP2002059252A (ja) 1999-10-22 2000-09-28 Ｍｇ合金精密圧力成形法及びその成形装置並びにそれにより作製されたＭｇ合金成形品

Publications (1)

Publication Number Publication Date
WO2001030519A1 true WO2001030519A1 (fr) 2001-05-03

Family

ID=27340877

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2000/007227 WO2001030519A1 (fr) 1999-10-22 2000-10-18 PROCEDE DE MOULAGE DE PRECISION PAR PRESSION D'UN ALLIAGE DE Mg, DISPOSITIF DE MOULAGE CORRESPONDANT ET MOULAGE EN ALLIAGE DE Mg PRODUIT CONFORMEMENT AUDIT PROCEDE

Country Status (4)

Country Link
JP (1) JP2002059252A (fr)
AU (1) AU7947500A (fr)
TW (1) TW527239B (fr)
WO (1) WO2001030519A1 (fr)

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN1327993C (zh) * 2005-08-02 2007-07-25 陆如辉 镁合金齿轮箱压铸模具
US8828158B2 (en) 2007-06-28 2014-09-09 Sumitomo Electric Industries, Ltd. Magnesium alloy sheet
CN110722125A (zh) * 2019-11-27 2020-01-24 深圳市昊翔压铸制品有限公司 一种铸锻一体压铸方法

Families Citing this family (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
KR100985310B1 (ko) * 2004-06-30 2010-10-04 스미토모덴키고교가부시키가이샤 마그네슘 합금재의 제조방법
JP2006297433A (ja) * 2005-04-19 2006-11-02 Kyocera Chemical Corp マグネシウム合金の成形方法およびマグネシウム合金用成形金型
NO20063703L (no) * 2006-08-18 2008-02-19 Magontec Gmbh Magnesium stopeprosess og legeringssammensetning
JP5556108B2 (ja) * 2009-09-25 2014-07-23 トヨタ自動車株式会社 半溶融金属の鋳造方法、及び半溶融金属の鋳造装置
JP5713709B2 (ja) * 2011-01-31 2015-05-07 クロダイト工業株式会社 鋳鉄鋳造方法
CN105014045B (zh) * 2015-08-05 2017-03-01 中北大学 一种镁合金异形零件的复合挤压铸造方法
CN105108112A (zh) * 2015-09-06 2015-12-02 无锡贺邦金属制品有限公司 一种金属压铸工艺
JP6544270B2 (ja) * 2016-03-02 2019-07-17 株式会社デンソー 鋳造装置および鋳造製品の製造方法

Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH02299758A (ja) * 1989-05-15 1990-12-12 Kobe Steel Ltd マグネシウム用ホットチャンバ型ダイカスト機
JPH079106A (ja) * 1993-06-25 1995-01-13 Olympus Optical Co Ltd 圧力鋳造方法
JPH10263781A (ja) * 1997-03-24 1998-10-06 Asahi Tec Corp Ｍｇ合金用ダイカスト鋳造装置
JPH11156513A (ja) * 1997-11-28 1999-06-15 Asahi Tec Corp 金属部材の鋳造方法及びこの方法に用いる鋳造用金型

Patent Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH02299758A (ja) * 1989-05-15 1990-12-12 Kobe Steel Ltd マグネシウム用ホットチャンバ型ダイカスト機
JPH079106A (ja) * 1993-06-25 1995-01-13 Olympus Optical Co Ltd 圧力鋳造方法
JPH10263781A (ja) * 1997-03-24 1998-10-06 Asahi Tec Corp Ｍｇ合金用ダイカスト鋳造装置
JPH11156513A (ja) * 1997-11-28 1999-06-15 Asahi Tec Corp 金属部材の鋳造方法及びこの方法に用いる鋳造用金型

Cited By (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN1327993C (zh) * 2005-08-02 2007-07-25 陆如辉 镁合金齿轮箱压铸模具
US8828158B2 (en) 2007-06-28 2014-09-09 Sumitomo Electric Industries, Ltd. Magnesium alloy sheet
US9499887B2 (en) 2007-06-28 2016-11-22 Sumitomo Electric Industries, Ltd. Magnesium alloy sheet
CN110722125A (zh) * 2019-11-27 2020-01-24 深圳市昊翔压铸制品有限公司 一种铸锻一体压铸方法

Also Published As

Publication number Publication date
AU7947500A (en) 2001-05-08
TW527239B (en) 2003-04-11
JP2002059252A (ja) 2002-02-26

Similar Documents

Publication Publication Date Title
Li et al. Recent research and advances in extrusion forming of magnesium alloys: A review
WO2015035894A1 (fr) Procédé de fabrication de section pour lisse d'aile d'avion
US5979535A (en) Methods for semi-melting injection molding
WO2001030519A1 (fr) PROCEDE DE MOULAGE DE PRECISION PAR PRESSION D'UN ALLIAGE DE Mg, DISPOSITIF DE MOULAGE CORRESPONDANT ET MOULAGE EN ALLIAGE DE Mg PRODUIT CONFORMEMENT AUDIT PROCEDE
US20170326630A1 (en) Die casting machine
WO2018196263A1 (fr) Procédé et appareil de refoulement destinés à une billette comportant un rapport hauteur/diamètre ultra-élevé
CN100998997A (zh) 供货态铝合金超塑挤压成型的工艺方法
EP0904875B1 (fr) Procédé de moulage par injection d'un aliage en métal léger
CN110315018B (zh) 高效率消除坯料内部孔洞型缺陷的超高温软芯锻造方法
US4990310A (en) Creep-resistant die cast zinc alloys
CN109128078B (zh) 一种铝合金压铸坯锭的等温半固态组织浆料制备方法
GB2056338A (en) Die-casting method and apparatus
CN115415504A (zh) 一种高强韧铝合金的铸造设备及工艺方法
CN109127756A (zh) 一种高强度镁合金的挤压模具及镁合金挤压方法
CN109136703A (zh) 一种zk60镁合金及其制备方法
CN109175058A (zh) 一种板材半固态气压触变成形方法
CN109926564B (zh) 一种ZCuSn10P1合金半固态浆料的制浆成型一体化装置和方法
KR100268359B1 (ko) 우수한 인장강도를 갖는 아연계합금 및 다이케스팅 주조물
Xue et al. Study on processing and structure property of Al-Cu-Mg-Zn alloy cup-shaped part produced by radial-backward extrusion
Azpilgain et al. Servomechanical press: A new press concept for semisolid forging
KR100756422B1 (ko) 용탕압출법에 의한 금속선재의 제조방법 및 이를 위한 장치
Sharma A Research Paper on Squeeze Casting
KR20240145266A (ko) 다이캐스팅 차체부품의 내부결함 제어방법
CN118720085A (zh) 汽车铸锻复合工艺方法
JPH0288735A (ja) 延性と耐摩耗性を兼ね備えた複合材料、その製造方法およびその用途

Legal Events

Date Code Title Description
AK Designated states

Kind code of ref document: A1

Designated state(s): AE AG AL AM AT AU AZ BA BB BG BR BY BZ CA CH CN CR CU CZ DE DK DM DZ EE ES FI GB GD GE GH GM HR HU ID IL IN IS KE KG KP KR KZ LC LK LR LS LT LU LV MA MD MG MK MN MW MX MZ NO NZ PL PT RO RU SD SE SG SI SK SL TJ TM TR TT TZ UA UG US UZ VN YU ZA ZW

AL Designated countries for regional patents

Kind code of ref document: A1

Designated state(s): GH GM KE LS MW MZ SD SL SZ TZ UG ZW AM AZ BY KG KZ MD RU TJ TM AT BE CH CY DE DK ES FI FR GB GR IE IT LU MC NL PT SE BF BJ CF CG CI CM GA GN GW ML MR NE SN TD TG

121 Ep: the epo has been informed by wipo that ep was designated in this application
DFPE Request for preliminary examination filed prior to expiration of 19th month from priority date (pct application filed before 20040101)
REG Reference to national code

Ref country code: DE

Ref legal event code: 8642

122 Ep: pct application non-entry in european phase