WO2000034146A1 - Contenant alimentaire comprenant des particules d'oxyde de titane et procede de preparation associe - Google Patents

Contenant alimentaire comprenant des particules d'oxyde de titane et procede de preparation associe Download PDF

Info

Publication number
WO2000034146A1
WO2000034146A1 PCT/JP1999/006878 JP9906878W WO0034146A1 WO 2000034146 A1 WO2000034146 A1 WO 2000034146A1 JP 9906878 W JP9906878 W JP 9906878W WO 0034146 A1 WO0034146 A1 WO 0034146A1
Authority
WO
WIPO (PCT)
Prior art keywords
titanium oxide
oxide particles
food container
binder
container
Prior art date
Application number
PCT/JP1999/006878
Other languages
English (en)
Japanese (ja)
Inventor
Masahiro Ohmori
Takashi Ohkubo
Masayuki Sanbayashi
Original Assignee
Showa Denko K.K.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from JP28611499A external-priority patent/JP2000229618A/ja
Application filed by Showa Denko K.K. filed Critical Showa Denko K.K.
Publication of WO2000034146A1 publication Critical patent/WO2000034146A1/fr

Abstract

Ce contenant alimentaire possède des particules d'oxyde de titane sur sa surface, il est moins susceptible de se tacher, est facile à nettoyer même lorsqu'il est taché, et est solide à long terme. La très grande transparence d'un film d'oxyde de titane, que l'on ne peut attendre d'un revêtement de résine, permet de conserver telle quelle l'apparence du matériau du contenant, par exemple un brillant métallique et une impression de propreté donnés par un contenant réalisé dans un métal tel qu'un acier inoxydable. Dans le cas d'un contenant alimentaire en verre, le film d'oxyde de titane permet d'augmenter la résistance du contenant, ce qui autorise une diminution de l'épaisseur de celui-ci et donc abaisse le poids du contenant.
PCT/JP1999/006878 1998-12-09 1999-12-08 Contenant alimentaire comprenant des particules d'oxyde de titane et procede de preparation associe WO2000034146A1 (fr)

Applications Claiming Priority (8)

Application Number Priority Date Filing Date Title
JP10/350406 1998-12-09
JP35040698 1998-12-09
US13623199P 1999-05-26 1999-05-26
US60/136,231 1999-05-26
JP28611499A JP2000229618A (ja) 1998-12-09 1999-10-06 酸化チタン粒子を用いた食品容器およびその製造方法
JP11/286114 1999-10-06
US16675699P 1999-11-22 1999-11-22
US60/166,756 1999-11-22

Publications (1)

Publication Number Publication Date
WO2000034146A1 true WO2000034146A1 (fr) 2000-06-15

Family

ID=27479395

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP1999/006878 WO2000034146A1 (fr) 1998-12-09 1999-12-08 Contenant alimentaire comprenant des particules d'oxyde de titane et procede de preparation associe

Country Status (1)

Country Link
WO (1) WO2000034146A1 (fr)

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2002053285A1 (fr) * 2000-12-28 2002-07-11 Showa Denko K.K. Poudre a fonction optique et son utilisation
US7060643B2 (en) 2000-12-28 2006-06-13 Showa Denko Kabushiki Kaisha Photo-functional powder and applications thereof

Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH07232080A (ja) * 1993-12-28 1995-09-05 Toto Ltd 光触媒機能を有する多機能材及びその製造方法
JPH07275137A (ja) * 1994-04-06 1995-10-24 Kato Kikai Seisakusho:Kk 飲食および料理用器具
JPH10287810A (ja) * 1997-04-11 1998-10-27 Sumitomo Chem Co Ltd 電子レンジ部品

Patent Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH07232080A (ja) * 1993-12-28 1995-09-05 Toto Ltd 光触媒機能を有する多機能材及びその製造方法
JPH07275137A (ja) * 1994-04-06 1995-10-24 Kato Kikai Seisakusho:Kk 飲食および料理用器具
JPH10287810A (ja) * 1997-04-11 1998-10-27 Sumitomo Chem Co Ltd 電子レンジ部品

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2002053285A1 (fr) * 2000-12-28 2002-07-11 Showa Denko K.K. Poudre a fonction optique et son utilisation
US7060643B2 (en) 2000-12-28 2006-06-13 Showa Denko Kabushiki Kaisha Photo-functional powder and applications thereof
US7169728B2 (en) 2000-12-28 2007-01-30 Showa Denko Kabushiki Kaisha Photo-functional powder and applications thereof

Similar Documents

Publication Publication Date Title
US9458539B2 (en) Metal surfaces compromising a thin glass- or ceramic type protective layer having high chemical resistance and improved non-stick properties
US7311944B2 (en) Aluminum phosphate coatings
US8101280B2 (en) Alkali-resistant coating on light metal surfaces
ES2338140T3 (es) Procedimiento para la preparacion de particulas de tio2 fotocatalicamente activas y de sustratos con una capa de tio2 fotocatalitica.
WO1999058451A1 (fr) Sel d'oxyde de titane, film mince et procedes de production de ces derniers
CN100535052C (zh) 含光催化剂的有机硅树脂组合物和具有该组合物的固化膜的涂敷制品
JP4296431B2 (ja) バイオフィルム阻害コーティングを有する支持体
WO2000018504A1 (fr) Article photocatalyseur, article protege contre l'encrassement et le voilement, et procede de production d'un article protege contre l'encrassement et le voilement
JPH09310039A (ja) 光触媒コーティング剤
US7029768B1 (en) Food container using titanium oxide particle and production method thereof
JP5118068B2 (ja) 光触媒薄膜、光触媒薄膜の形成方法及び光触媒薄膜被覆製品
JP3961097B2 (ja) ブラインドのスラット製造方法
WO2000034146A1 (fr) Contenant alimentaire comprenant des particules d'oxyde de titane et procede de preparation associe
JP3759651B2 (ja) 光触媒表面を有する樹脂または樹脂被覆材料およびその製造方法
JPH11513359A (ja) 表面に不粘着性および非湿潤性を与える系
JP2000229618A (ja) 酸化チタン粒子を用いた食品容器およびその製造方法
JPH09328336A (ja) 光触媒活性を有する被膜とそれを形成する組成物
CN1701102A (zh) 亲水性膜、其制造方法及亲水性膜形成用涂料
JP4131534B2 (ja) ステンレス鋼製器物
JP2001040294A (ja) 吸湿性コーティング組成物
JP2007217739A (ja) 撥水性被膜の成膜方法
JP2003299606A (ja) 食器洗い乾燥機
WO2001095309A1 (fr) Barriere transparente auto-nettoyante de protection contre le bruit, et son procede de fabrication
CN1167760C (zh) 用于形成光催化透明亲水涂层的二氧化钛纳米涂料及其制备方法
JP4132468B2 (ja) 耐錆性、耐食性および密着性に優れた容器用金属板

Legal Events

Date Code Title Description
AK Designated states

Kind code of ref document: A1

Designated state(s): CA CN KR US

AL Designated countries for regional patents

Kind code of ref document: A1

Designated state(s): AT BE CH CY DE DK ES FI FR GB GR IE IT LU MC NL PT SE

121 Ep: the epo has been informed by wipo that ep was designated in this application
DFPE Request for preliminary examination filed prior to expiration of 19th month from priority date (pct application filed before 20040101)
122 Ep: pct application non-entry in european phase