Classifications

• • H—ELECTRICITY
  • H01—ELECTRIC ELEMENTS
  • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
  • H01M8/00—Fuel cells; Manufacture thereof
  • H01M8/02—Details
  • H01M8/0202—Collectors; Separators, e.g. bipolar separators; Interconnectors
  • H01M8/0204—Non-porous and characterised by the material
  • H01M8/0223—Composites
  • H01M8/0228—Composites in the form of layered or coated products
• • H—ELECTRICITY
  • H01—ELECTRIC ELEMENTS
  • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
  • H01M8/00—Fuel cells; Manufacture thereof
  • H01M8/02—Details
  • H01M8/0202—Collectors; Separators, e.g. bipolar separators; Interconnectors
  • H01M8/0247—Collectors; Separators, e.g. bipolar separators; Interconnectors characterised by the form
• • H—ELECTRICITY
  • H01—ELECTRIC ELEMENTS
  • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
  • H01M8/00—Fuel cells; Manufacture thereof
  • H01M8/02—Details
  • H01M8/0202—Collectors; Separators, e.g. bipolar separators; Interconnectors
  • H01M8/0247—Collectors; Separators, e.g. bipolar separators; Interconnectors characterised by the form
  • H01M8/0254—Collectors; Separators, e.g. bipolar separators; Interconnectors characterised by the form corrugated or undulated
• • H—ELECTRICITY
  • H01—ELECTRIC ELEMENTS
  • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
  • H01M8/00—Fuel cells; Manufacture thereof
  • H01M8/02—Details
  • H01M8/0271—Sealing or supporting means around electrodes, matrices or membranes
• • H—ELECTRICITY
  • H01—ELECTRIC ELEMENTS
  • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
  • H01M8/00—Fuel cells; Manufacture thereof
  • H01M8/24—Grouping of fuel cells, e.g. stacking of fuel cells
  • H01M8/241—Grouping of fuel cells, e.g. stacking of fuel cells with solid or matrix-supported electrolytes
  • H01M8/242—Grouping of fuel cells, e.g. stacking of fuel cells with solid or matrix-supported electrolytes comprising framed electrodes or intermediary frame-like gaskets
• • H—ELECTRICITY
  • H01—ELECTRIC ELEMENTS
  • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
  • H01M8/00—Fuel cells; Manufacture thereof
  • H01M8/24—Grouping of fuel cells, e.g. stacking of fuel cells
  • H01M8/241—Grouping of fuel cells, e.g. stacking of fuel cells with solid or matrix-supported electrolytes
  • H01M8/2425—High-temperature cells with solid electrolytes
  • H01M8/2428—Grouping by arranging unit cells on a surface of any form, e.g. planar or tubular
• • H—ELECTRICITY
  • H01—ELECTRIC ELEMENTS
  • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
  • H01M8/00—Fuel cells; Manufacture thereof
  • H01M8/24—Grouping of fuel cells, e.g. stacking of fuel cells
  • H01M8/241—Grouping of fuel cells, e.g. stacking of fuel cells with solid or matrix-supported electrolytes
  • H01M8/2425—High-temperature cells with solid electrolytes
  • H01M8/2432—Grouping of unit cells of planar configuration
• • H—ELECTRICITY
  • H01—ELECTRIC ELEMENTS
  • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
  • H01M8/00—Fuel cells; Manufacture thereof
  • H01M8/24—Grouping of fuel cells, e.g. stacking of fuel cells
  • H01M8/2465—Details of groupings of fuel cells
• • H—ELECTRICITY
  • H01—ELECTRIC ELEMENTS
  • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
  • H01M8/00—Fuel cells; Manufacture thereof
  • H01M8/24—Grouping of fuel cells, e.g. stacking of fuel cells
  • H01M8/2465—Details of groupings of fuel cells
  • H01M8/2483—Details of groupings of fuel cells characterised by internal manifolds
• • H—ELECTRICITY
  • H01—ELECTRIC ELEMENTS
  • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
  • H01M8/00—Fuel cells; Manufacture thereof
  • H01M8/10—Fuel cells with solid electrolytes
  • H01M8/12—Fuel cells with solid electrolytes operating at high temperature, e.g. with stabilised ZrO2 electrolyte
  • H01M2008/1293—Fuel cells with solid oxide electrolytes
• • H—ELECTRICITY
  • H01—ELECTRIC ELEMENTS
  • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
  • H01M2300/00—Electrolytes
  • H01M2300/0017—Non-aqueous electrolytes
  • H01M2300/0065—Solid electrolytes
  • H01M2300/0068—Solid electrolytes inorganic
  • H01M2300/0071—Oxides
  • H01M2300/0074—Ion conductive at high temperature
• • H—ELECTRICITY
  • H01—ELECTRIC ELEMENTS
  • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
  • H01M8/00—Fuel cells; Manufacture thereof
  • H01M8/02—Details
  • H01M8/0202—Collectors; Separators, e.g. bipolar separators; Interconnectors
  • H01M8/0204—Non-porous and characterised by the material
  • H01M8/0206—Metals or alloys
• • H—ELECTRICITY
  • H01—ELECTRIC ELEMENTS
  • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
  • H01M8/00—Fuel cells; Manufacture thereof
  • H01M8/02—Details
  • H01M8/0202—Collectors; Separators, e.g. bipolar separators; Interconnectors
  • H01M8/0204—Non-porous and characterised by the material
  • H01M8/0223—Composites
  • H01M8/0226—Composites in the form of mixtures
• • H—ELECTRICITY
  • H01—ELECTRIC ELEMENTS
  • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
  • H01M8/00—Fuel cells; Manufacture thereof
  • H01M8/24—Grouping of fuel cells, e.g. stacking of fuel cells
  • H01M8/2465—Details of groupings of fuel cells
  • H01M8/247—Arrangements for tightening a stack, for accommodation of a stack in a tank or for assembling different tanks
• • H—ELECTRICITY
  • H01—ELECTRIC ELEMENTS
  • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
  • H01M8/00—Fuel cells; Manufacture thereof
  • H01M8/24—Grouping of fuel cells, e.g. stacking of fuel cells
  • H01M8/249—Grouping of fuel cells, e.g. stacking of fuel cells comprising two or more groupings of fuel cells, e.g. modular assemblies
• • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
  • Y02—TECHNOLOGIES OR APPLICATIONS FOR MITIGATION OR ADAPTATION AGAINST CLIMATE CHANGE
  • Y02E—REDUCTION OF GREENHOUSE GAS [GHG] EMISSIONS, RELATED TO ENERGY GENERATION, TRANSMISSION OR DISTRIBUTION
  • Y02E60/00—Enabling technologies; Technologies with a potential or indirect contribution to GHG emissions mitigation
  • Y02E60/30—Hydrogen technology
  • Y02E60/50—Fuel cells

Definitions

• the present invention relates to a fuel cell assembly comprising a stack of a plurality of planar fuel cells, and is particularly concerned with such a fuel cell assembly in which the compressive load on each fuel cell is independent of its position in the stack.
• the invention also extends to a single fuel cell assembly.
• a fuel cell assembly comprising a stack of a plurality of planar fuel cells requires interconnect means between each pair of adjacent fuel cells to transfer electrical current and heat from the fuel cells, to facilitate the conveyance of oxygen-containing gas and fuel gas to respective sides of each fuel cell, and to keep the oxygen-containing gas and fuel gas apart.
• interconnect means are effectively terminal plates which transfer electrical current and heat from the fuel cell and facilitate the conveyance of oxygen-containing gas and fuel gas to respective sides of the fuel cell.
• end interconnect means in a stack of planar fuel cells are effectively terminal plates.
• all the aforementioned interconnect means, whether between adjacent fuel cells or terminal plates, will hereinafter be referred to as "interconnect members”.
• the fuel cells and interconnect members have the same cross-sectional area and the electrical contact between the cells and interconnect members and the sealing of respective sides of each fuel cell from each other is maintained by using the force imparted by the weight of the cell(s) and/or interconnect members above any one cell.
• the fuel cells are fully load bearing. Examples of such an arrangement are described in international patent applications PCT/AU96/00140 and PCT/AU96/00594.
• the problem with this approach is that the lower cells in the stack carry greater weight than the upper cells. For a stack with a large number of fuel cells the load on the lower cells can be significant.
• the carrying load of a ceramic is much higher in compression than in tension and the fully load-bearing arrangement described above assumes that, in a perfect system, the cells carry only a compressive load.
• This compression- only model acquires near perfect flatness of all load carrying parts since unevenness will lead to tensile forces in the structure and to the possible breakage of the fuel cells. In practice it is not possible to ensure such a quality of flatness in all of the load carrying parts.
• a further problem with a fuel cell in a stack carrying the full mass of the fuel cells and interconnects above it is that the relatively weak porous electrode layers of the fuel cell may collapse under the load.
• European patent application EP 0568991 describes a fuel cell assembly comprising a stack of a plurality of planar fuel cell structures, each comprising a fuel cell and a single interconnect member on one side.
• Each fuel cell structure is located in a hollow plate and is separated from an adjacent fuel cell structure by a hollow intermediate plate, with the interconnect member of one fuel cell structure being maintained in electrical contact with the anode of an adjacent fuel cell structure by a felt-like nickel metal conductive material disposed in the hollow intermediate plate.
• Each fuel cell carries the load of the associated interconnect member.
• each fuel cell structure is compressed between a seal element and inlet defining elements of the adjacent intermediate plates so that increasing compressive loads may still be applied to fuel cells down the stack. It is an object of the present invention to alleviate the aforementioned disadvantages of the prior art.
• a fuel cell assembly comprising a stack of a plurality of planar fuel cells each comprising an electrolyte layer having an anode layer on one side and a cathode layer on the other side and a plurality of interconnect members, each fuel cell being disposed between and in electrical contact with an adjacent pair of interconnect members with oxygen-containing gas passage means being formed between the cathode layer of each fuel cell and the adjacent interconnect member and fuel gas passage means being formed between the anode layer of each fuel cell and the adjacent interconnect member, and wherein a chamber of greater height than the thickness of the respective fuel cell is defined between the adjacent interconnect members in each pair within which the fuel cell is received, and electrically conductive compressible means also disposed within the chamber in electrical contact with a first side of the fuel cell and the adjacent interconnect member urges the fuel cell towards the adjacent interconnect member on the second side thereof to maintain the fuel cell in electrical contact with both adjacent interconnect members.
• each fuel cell is displaceably received within the respective chamber but for the associated electrically conductive compressible means and the compressive load on each fuel cell is provided by the respective compressible means.
• the compressive load on each fuel cell is independent of the position of the fuel cell in the stack.
• a reduced compressive load may be applied to each fuel cell which is particularly advantageous for the aforementioned solid oxide electrolyte fuel cells in which the electrolyte layer is not a primary load bearing layer.
• the load conditions in each chamber can be the same throughout the stack, so that the properties of the materials used in the stack do not need to vary according to the position of the fuel cell in the stack.
• the invention is also applicable to a fuel cell assembly comprising a single fuel cell.
• the invention further provides a fuel cell assembly comprising a planar fuel cell having an electrolyte layer with an anode layer on one side and a cathode layer on the other side, the fuel cell being disposed between and in electrical contact with respective interconnect members, oxygen-containing gas passage means being formed between the cathode layer and the adjacent interconnect member and fuel gas passage means being formed between the anode layer and the adjacent interconnect member, and wherein a chamber of greater height than the thickness of the fuel cell is defined between the interconnect members within which the fuel cell is received and electrically conductive compressible means also disposed within the chamber in electrical contact with a first side of the fuel cell and the adjacent interconnect member urges the fuel cell towards the adjacent interconnect member on the second side thereof to maintain the fuel cell in electrical contact with both interconnect members.
• the compressible means may take any of a variety of forms which maintain at least a minimum desired compressive force on the fuel cell even at the operating temperature of the fuel cell assembly. It is desirable that the compressible means maintains electrical contact between the fuel cell and the interconnect member during the full life of the fuel cell in use and therefore that it is not subject to more than minimal creep under the compression load. Any creep should not be so great as to cause the electrical contact to be broken.
• the compressible means is disposed on the anode side of the fuel cell.
• the metal or metallic material which may be used for or in a compressible means on the anode side of the fuel cell include nickel, nickel alloy such as nickel-chrome and nickel- aluminium, and oxide dispersion strengthened nickel.
• the nickel may be replaced by other suitable metal or metals from Groups 8-11 of the Periodic Table.
• the compressible means for use on the anode side of the fuel cell include a structure, such as a metallic corrugation or a porous metallic felt, which retains some resilience at the operating temperature; and a composite of a porous brittle material and a metal.
• the composite of brittle material, such as a ceramic, and a metal may be designed such that the brittle material yields at, the applied loading but does not fail completely so that it will maintain pressure on the fuel cell between upper and lower limits.
• the metal maintains the electrical path, and preferably a heat path, through the composite and may provide reinforcement for the brittle material.
• the compressible means is resilient so that a compressive load may be maintained during, for example, temperature cycling of the fuel cell assembly.
• the resistance is provided by a corrugated metal or metallic sheet, optionally with a substantially flat sheet of metal or metallic material disposed between the corrugated sheet and the first side of the fuel cell to alleviate any sliding movement between the corrugated sheet and the first side of the fuel cell as the corrugated sheet is compressed.
• the flat sheet must permit the gas to contact the first side of the fuel cell and may be porous or otherwise have gas flow passages therethrough.
• the flat sheet is formed of expanded material, that is with an array of slits formed in the material and the sheet being stretched to open up the slits.
• the corrugated sheet must be porous or otherwise have gas flow passages therethrough.
• the corrugated sheet is formed of expanded material.
• the corrugated sheet may be used to define the gas passage means, in which case it may not need to have gas flow passages therethrough.
• the corrugated sheet may be joined to the adjacent interconnect member, for example by spot welding, in order to control the compressibility of the corrugated sheet.
• the substantially flat sheet of metal or metallic material may be disposed between the corrugated sheet and the adjacent interconnect member and may be joined to the corrugated sheet by, for example, spot welding.
• This substantially flat sheet may also be of expanded material or otherwise have gas flow passages therethrough and may be joined to the interconnect member, for example by spot welding.
• the compressible layer may alternatively comprise an integral compliant layer on the interconnect member which is adjacent the first side of the fuel cell.
• the material should be resistant to oxidation, for example a form of ceramic felt or other fibre structure.
• Electrically conductive compressible means as described above may also be disposed within the chamber in electrical contact with the second side of the fuel cell and the adjacent interconnect member.
• compressible means on only one side is disposed on the upper side of the fuel cell.
• the chamber for the fuel cell may be defined by a recess in one or both of the adjacent interconnect members, with the interconnect members being electrically insulated from each other around the chamber, and/or by an insulating spacer between the adjacent interconnect members around the chamber.
• the insulating spacer may be formed of an insulating material, for example a ceramic such as alumina, or, for example, of a conductive material, such as a metal, having an insulating coating or surface layer thereon.
• Gas flow channels across one or both sides of the interconnect members for flow of oxygen- containing gas and/or fuel gas to respective sides of the fuel cells may be formed in the interconnect members.
• the channels for gas flow to at least the first side of the fuel cell are advantageously defined by the compressible means, as described above, and the compressible means advantageously contacts a flat side of the adjacent interconnect member.
• the interconnect member may conveniently be formed of a stainless steel.
• the fuel cell assembly may be externally manifolded for the gas flows, for example as described in the aforementioned EP 0568991, but is preferably internally manifolded.
• the oxygen-containing gas and fuel gas supply and exhaust passages preferably pass through the interconnect members, and possibly through the aforementioned insulating spacer if provided.
• a seal which is advantageously compressible in use is conveniently provided around a peripheral portion of the fuel cell between the second side thereof and the adjacent interconnect member to seal the fuel gas and the oxygen-containing gas in the chamber from each other.
• the electrode layers may have a degree of porosity, it is desirable for the electrode layer on the second side of the fuel cell, preferably the cathode layer as described above, to not extend into the peripheral portion of the fuel cell, so that the seal engages the electrolyte layer.
• the compressible means is provided on only the first side of the fuel cell, the seal is compressible in use to the extent that the electrode on the second side of the fuel cell abuts and makes electrical contact with the adjacent interconnect member at the operating temperature.
• the seal is solid at room temperature, and therefore during assembly, but becomes viscous at the operating temperature, for example 700°C to 1,000°C, of the fuel cell assembly.
• the seal is a glass-containing gasket which may comprise plural layers of glass containing material.
• the seal may extend between the adjacent interconnect members or between the interconnect member adjacent the second side of the fuel cell and the aforementioned insulating spacer.
• a further seal member which may be thinner than the seal and/or the first-mentioned seal member may be provided between the insulating spacer and the interconnect member adjacent the first side of the fuel cell.
• the first and second mentioned seal members may be formed of the same or similar material to the seal and may also be compressed in use of the fuel cell assembly.
• the or each fuel cell may be one of an array of fuel cells in a respective layer of plural planar fuel cells in the assembly, with each fuel cell being disposed in a chamber in accordance with the present invention.
• the interconnect members adjacent a common side of all or more than one of the fuel cells in each array are formed in a single plate.
• the aforementioned insulating spacer, if provided, may define partly or wholly all or more than one of the chambers for the fuel cells in each array.
• Figure 1 is a sectional elevation of a fuel cell assembly including one fuel cell, taken on the line A- A of Figure 2;
• Figure 2 is an exploded perspective view of the fuel cell assembly of Figure 1 ;
• Figure 3 is a plan view from above of one of the interconnect members shown in Figure 1 ;
• Figure 4 is a plan view from below of the interconnect member of Figure 3;
• Figure 5 is a plan view from above of the insulating spacer plate of the assembly of Figure 1;
• Figure 6 is a plan view from above of an alternative interconnect plate incorporating four interconnect members for a use in a fuel cell assembly having an array of four parallel sets of fuel cells;
• Figure 7 is a sectional view along the line A-A of Figure 6;
• Figure 8 is a sectional view along the line B-B of Figure 6;
• Figure 9 is a plan view from above of an insulating spacer plate for use with the interconnect plate of Figure 6;
• Figure 10 is a sectional view along the line A-A of Figure 9;
• Figure 11 is a graph showing the power curve for the single cell assembly of Example
• Figure 12 is a graph showing the power curve for the six cell fuel cell stack of Example 2.
• Figure 13 is a graph showing the time curve for the six cell stack of Example 2.
• the single fuel cell assembly 10 comprises a pair of spaced interconnect plates 12 and 14 with a single fuel cell 16 between them.
• the present invention is particularly applicable to a stack of a plurality of fuel cells, but will operate with a single fuel cell and is described accordingly for convenience.
• the fuel cell 16 is illustrated as of the type in which the anode 18 is the primary load bearing layer with a thin electrolyte layer 20 on one surface and a thin cathode layer 22 applied to the 5 electrolyte layer 20.
• Such cells are known for intermediate temperature operation of a fuel cell assembly, at around 800°C, but the fuel cell 16 could be replaced by, for example, a fuel cell as described in the aforementioned International patent applications.
• the solid oxide electrolyte layer 20 may comprise Y 2 O 3 -doped ZrO 2 (YSZ)
• the cathode layer 22 may comprise strontium doped lanthanum manganite (LSM) having a thickness of about 50 to 100 microns.
• the anode and cathode layers 18 and 22 are porous, and the cathode layer 22 is of reduced 15 area compared to the anode and electrolyte layers 18 and 20, not extending to the periphery of the electrolyte 20, for sealing purposes.
• the interconnect plates 12 and 14 may be formed of any of the materials described in the aforementioned International patent applications, but are preferably formed of corrosion
• the cathode side 24 may have a coating of La-Sr-CrO 3 (LSC), while the anode side 26 may have a nickel coating.
• LSC La-Sr-CrO 3
• interconnect plates 12 and 14 are shown ribbed on only the cathode side 24 to facilitate air flow across the cathode layer 22 of the fuel cell 16, and the channels 28 between the ribs
• fuel gas flow on the anode side 26 of the interconnect plates is directed by a compression member 32, as described hereinafter, but it could be facilitated by cooperating channels in the anode side 26 of the interconnect plates, or the fuel gas distribution across the anode side 18 of the fuel cell 16 may be performed substantially only by channels on the anode side 26 of the 5 interconnect plates, for example as described in the aforementioned International patent applications.
• the interconnect plates 12 and 14 are spaced apart by an insulating spacer plate 34 having an opening 36 therethrough defining a chamber between the interconnect plates within which the fuel cell 16 is received.
• the spacer plate may be formed of, for example, alumina or a conducting material such as stainless steel with an insulating coating, for example of alumina.
• the insulating spacer plate 34 is of greater thickness than the fuel cell 16, and the compression member 32 is disposed between the interconnect plate 12 and the anode layer 18 of the fuel cell 16 within the chamber defined by the opening 36 of the spacer 34.
• the compression member 32 may be formed of for example nickel or nickel alloy and maintains electrical contact between the interconnect plate 12 and the anode layer 18 of the fuel cell.
• the compression member 32 applies pressure to the fuel cell 16 from the interconnect plate 12 to maintain the cathode layer 22 in electrical contact with the cathode side 24 of the interconnect plate 14.
• this pressure is limited by the spacer plate 34 so that it is independent of the number of fuel cell assemblies which may be above the assembly 10 in a stack. This greatly enhances use of the relatively weak fuel cell 16
• the compression member 32 comprises three sheets of superposed expanded nickel mesh.
• the outer sheets 38 and 40 are flat, but the inner sheet 42 is corrugated.
• Each of the sheets has a thickness of about quarter of a millimetre, and the overall thickness of the compression member 32 is 1.5 to 2mm, for example about 1.7mm. 5
• the corrugated nature of the inner sheet 42 facilitates fuel gas flow across the chamber defined by the opening 36, and the open mesh nature of the expanded sheets allows the distributed fuel gas to contact the anode layer 18 of the fuel cell.
• the corrugated inner sheet 42 also gives the member 32 a degree of compressibility through its thickness so as to provide the desired compressive force between the interconnect plate 12 and the fuel cell.
• the compressive force must be able to be maintained throughout use of the fuel cell, in order to maintain electrical contact between the fuel cell and both interconnect plates 12 and 14, and the inner sheet 42 is advantageously secured to one of the outer sheets
• the inner sheet 42 is spot welded to the outer sheet 38 and the outer sheet 40 alleviates any sliding contact between the inner sheet 42 as it is compressed and the anode layer 18 of the fuel cell.
• the outer sheet 38 may be omitted and the corrugated inner sheet 42 may be spot welded directly to the interconnect plate 12.
• the outer sheet 38 may be omitted and the corrugated inner sheet 42 may be spot welded directly to the interconnect plate 12.
• the outer sheet 40 could also be omitted.
• the corrugated inner sheet 42 could be bonded to one of the outer sheets 38 and 40, as by spot welding, and the other outer sheet may be omitted. It is envisaged that a replacement of the nickel material of the compression member 32 by nickel alloy may improve the desirable characteristics of the compression member.
• the cathode layer 22 of the fuel cell is porous, it does not extend into the peripheral region 46 and the gasket 44 contacts the fully dense solid oxide electrolyte layer 20 in the peripheral region 46. If desired, the portion of the gasket 44 contacting the peripheral region 46 of the fuel cell could be separate from the portion of the gasket contacting the spacer plate 34.
• a thinner glass containing gasket 48 is disposed between the spacer plate 34 and the anode side 26 of the interconnect plate 12 to seal the anode side of the chamber.
• the gaskets 44 and 48 are conveniently formed of plural layers of glass containing material which is rigid under ambient conditions but which becomes viscous at the operating temperature of the fuel cell. This enables the gaskets 44 and 48, particularly the thicker gasket 44, to compress and thereby ensure the desired seal, with the compression in practice being such as to ensure the cathode layer 22 on the fuel cell is urged by the compression member 32 into contact with the cathode side 24 of the interconnect plate 14. As the gaskets 44 and 48 are compressed, the interconnect plates 12 and 14 move towards each other, but this movement is limited by the spacer plate 34 so that the degree of compression applied to the fuel cell by the compression member 32 is limited and is independent of the position of the fuel cell assembly 10 in a stack of fuel cells.
• the fuel cell assembly 10 is internally manifolded, that is manifolds for the oxygen-containing gas and fuel gas extend through the interconnect plates 12 and 14 and the spacer plate 34, as well as through the gaskets 44 and 48.
• this is not essential and the fuel cell assembly 10 could be externally manifolded.
• the oxygen-containing gas inlet and outlet manifolds 50 and 52 communicate with the distribution channels 28 in the interconnect plate by way of inlet and outlet passages 58 and 60 and distributors 62 and 64 defined by grooves in the interconnect plate.
• the inlet and outlet channels 58 and 60 are recessed on each side at 66 to receive a sealing shim (not shown), for example of stainless steel.
• the gasket 44 may extend over the sealing shim.
• the spacer plate 34 has fuel gas inlet and outlet passages 68 and 70 defined by respective grooves extending between the manifold passages 54 and 56 therethrough and the opening 36 defining the chamber for the fuel cell 16 and compression member 32.
• the present invention may be applied also to a fuel cell assembly incorporating a parallel array of, for example, four fuel cells.
• One interconnect plate 80 and one spacer plate 82 are illustrated for this purpose in Figures 6 to 8 and Figures 9 and 10 respectively.
• the fuel cells are not shown, but they will be individual and may be identical to the fuel cell 16 described above.
• interconnect plate 80 and spacer plate 82 will be assembled in identical manner as has been described above with correspondingly shaped sealing gaskets above and below the spacer plate 82 extending around the four openings 84 in the spacer plate defining chambers within which respective assemblies of a fuel cell and a compression member such as the member 32 will be received.
• the interconnect plate 80 and spacer plate 82 are also internally manifolded, but in a different manner to the manifolding in the fuel assembly 10.
• a cross flow arrangement is used so that the compression member 32 would be rotated through 90° compared to its orientation in the fuel assembly 10 with the distribution channels defined by the corrugations of the inner sheet 42 extending perpendicularly to the air side distribution channels 86 in the interconnect plate 80.
• This arrangement allows the arrayed fuel cell assemblies to be paired for manifolding purposes.
• each array has a respective oxygen-containing gas inlet manifold passage 88 for each fuel cell, respective oxygen- containing gas outlet manifold passages 90 are common to paired fuel cells.
• each array has a respective fuel gas inlet manifold passage 92 for each fuel cell, but fuel gas outlet manifold passages 94 are common to respective pairs of the fuel cells.
• the manifold passages all extend at least substantially across the full width of the respective opening(s) 84. It will be appreciated that the respective gas flows may be reversed by swapping the inlet and outlet manifold passages.
• Example 1 only a single fuel cell was tested, but in Example 2 the fuel cell assembly comprised a six cell stack.
• the cell assemblies in the Examples were identical and comprised 50mm by 50mm fuel cells, each comprising a Ni/YSZ anode layer of greater than 0.5mm thickness having a 20 micron YSZ electrolyte layer laminated thereto with a 100 micron LSM cathode layer on the other side of the electrolyte.
• the compression member in each cell assembly comprise a corrugated expanded nickel mesh with flat sheets of nickel mesh on each side, one of which was spot welded to the corrugated mesh, to give a total thickness of about 1.7mm, each sheet having a thickness of about 230 microns.
• the interconnect members were corrosion resistant stainless steel having an LSC conducting layer on the ribs and an alumina coating in the distribution channels on the cathode side, and a nickel coating on the fuel side. The composition of the stainless steel was, in wt.
• the spacer plate in each fuel cell assembly was of alumina, with a thickness of 2mm, and the gaskets were of a glass-containing material which became viscous at the operating temperature of 800°C. The thicknesses of the gaskets were adjusted so as to be optimum for providing the desired sealing.
• the stack was heated in the test station to 800°C. Then the stack was tested with 4 % water in hydrogen as the fuel gas and air as the oxidant gas. The stack sealed well, with all six cells reaching the theoretical open circuit voltage of 1.084 N. The stack reached a peak power of 29 W at 10 A, as shown in Figure 12. The stack was then operated at 150 mA/cm 2 and 200 mA/cm 2 for a period of 250 hours before being shut down for analysis, and the results are shown in Figure 14. The stack sealed well over the complete test period. In-situ electrochemical tests indicated excellent contact between the cells and the interconnect plates, demonstrating the compression members were working well.

Landscapes

• Chemical & Material Sciences (AREA)
• Life Sciences & Earth Sciences (AREA)
• Engineering & Computer Science (AREA)
• Manufacturing & Machinery (AREA)
• Sustainable Development (AREA)
• Sustainable Energy (AREA)
• Chemical Kinetics & Catalysis (AREA)
• Electrochemistry (AREA)
• General Chemical & Material Sciences (AREA)
• Composite Materials (AREA)
• Fuel Cell (AREA)

Priority Applications (6)

Applications Claiming Priority (2)

Publications (1)

Family

ID=3801540

Family Applications (1)

Country Status (7)

Cited By (17)

Families Citing this family (88)

Citations (2)

Family Cites Families (13)

• 1997
  • 1997-06-10 AU AUPO7249A patent/AUPO724997A0/en not_active Abandoned
• 1998
  • 1998-06-10 NZ NZ501642A patent/NZ501642A/en unknown
  • 1998-06-10 EP EP98923931A patent/EP0988655B1/en not_active Expired - Lifetime
  • 1998-06-10 WO PCT/AU1998/000437 patent/WO1998057384A1/en not_active Ceased
  • 1998-06-10 US US09/445,735 patent/US6492053B1/en not_active Expired - Lifetime
  • 1998-06-10 DE DE69837848T patent/DE69837848T2/de not_active Expired - Lifetime
  • 1998-06-10 JP JP50113999A patent/JP2002503381A/ja not_active Ceased

Patent Citations (2)

Non-Patent Citations (1)

Also Published As

Similar Documents

Legal Events