WO1998033866A1 - Systeme hote-client fluorescent - Google Patents

Systeme hote-client fluorescent Download PDF

Info

Publication number
WO1998033866A1
WO1998033866A1 PCT/EP1998/000318 EP9800318W WO9833866A1 WO 1998033866 A1 WO1998033866 A1 WO 1998033866A1 EP 9800318 W EP9800318 W EP 9800318W WO 9833866 A1 WO9833866 A1 WO 9833866A1
Authority
WO
WIPO (PCT)
Prior art keywords
host
group
guest
polymer
polymerisable
Prior art date
Application number
PCT/EP1998/000318
Other languages
English (en)
Inventor
Brian Gerrard Devlin
Junji Otani
Kazuhiko Kunimoto
Abul Iqbal
Sameer Hosam Eldin
Original Assignee
Ciba Specialty Chemicals Holding Inc.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Ciba Specialty Chemicals Holding Inc. filed Critical Ciba Specialty Chemicals Holding Inc.
Priority to KR10-1999-7006960A priority Critical patent/KR100511708B1/ko
Priority to DE69803834T priority patent/DE69803834T2/de
Priority to AU62120/98A priority patent/AU730993B2/en
Priority to EP98904111A priority patent/EP0968253B1/fr
Priority to ES98904111T priority patent/ES2171289T3/es
Priority to AT98904111T priority patent/ATE213265T1/de
Priority to JP53250898A priority patent/JP2001509832A/ja
Priority to DK98907969T priority patent/DK0968254T3/da
Priority to PCT/EP1998/000318 priority patent/WO1998033866A1/fr
Publication of WO1998033866A1 publication Critical patent/WO1998033866A1/fr

Abstract

L'invention concerne une composition comprenant un matériau de support organique solide, auquel des chromophores hôtes fluorescents et des chromophores clients fluorescents sont liés par covalence, directement ou via un groupe formant pont. Ainsi, le spectre d'émission de fluorescence du chromophore hôte chevauche le spectre d'absorption du chromophore client, le chromophore hôte étant sélectionné dans le groupe se composant de benzo[4,5]imidazo[2,11-a]iso-indol-11-ones.
PCT/EP1998/000318 1997-02-03 1998-01-21 Systeme hote-client fluorescent WO1998033866A1 (fr)

Priority Applications (9)

Application Number Priority Date Filing Date Title
KR10-1999-7006960A KR100511708B1 (ko) 1997-02-03 1998-01-21 형광 호스트-게스트-시스템
DE69803834T DE69803834T2 (de) 1997-02-03 1998-01-21 Fluorezentes guest-host-system
AU62120/98A AU730993B2 (en) 1997-02-03 1998-01-21 Fluorescent host-guest-system
EP98904111A EP0968253B1 (fr) 1997-02-03 1998-01-21 Systeme hote-client fluorescent
ES98904111T ES2171289T3 (es) 1997-02-03 1998-01-21 Sistema fluorescente hospedante-huesped.
AT98904111T ATE213265T1 (de) 1997-02-03 1998-01-21 Fluorezentes guest-host-system
JP53250898A JP2001509832A (ja) 1997-02-03 1998-01-21 蛍光ホスト−ゲスト−システム
DK98907969T DK0968254T3 (da) 1997-02-03 1998-01-21 Fluorescerende materialer og deres anvendelse
PCT/EP1998/000318 WO1998033866A1 (fr) 1997-02-03 1998-01-21 Systeme hote-client fluorescent

Applications Claiming Priority (6)

Application Number Priority Date Filing Date Title
EP97810049.3 1997-02-03
EP97810051.9 1997-02-03
EP97810050.1 1997-02-03
EP97810054.3 1997-02-04
EP97810055.0 1997-02-04
PCT/EP1998/000318 WO1998033866A1 (fr) 1997-02-03 1998-01-21 Systeme hote-client fluorescent

Publications (1)

Publication Number Publication Date
WO1998033866A1 true WO1998033866A1 (fr) 1998-08-06

Family

ID=8166841

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/EP1998/000318 WO1998033866A1 (fr) 1997-02-03 1998-01-21 Systeme hote-client fluorescent

Country Status (1)

Country Link
WO (1) WO1998033866A1 (fr)

Cited By (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2002012402A2 (fr) * 2000-08-07 2002-02-14 Eastman Chemical Company Composes colorants contenant des groupes vinyle polymerisables
EP1739135A2 (fr) * 2000-08-07 2007-01-03 Eastman Chemical Company Composés colorant contenant des groupes vinyle polymérisables
WO2007059449A2 (fr) * 2005-11-10 2007-05-24 Beckman Coulter, Inc. Derives de bleu de nil lies par covalence pour des sondes optiques
US8242203B2 (en) 2005-11-10 2012-08-14 Eric Bakker Covalently attached nile blue derivatives for optical sensors

Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP0456609A1 (fr) * 1990-05-08 1991-11-13 Ciba-Geigy Ag Pigments fluorescents jaunes à base de tétrachloro-1,2,3,4-11H-isoindolo-(2,1-a)-benzimidazolone-11
WO1994015441A1 (fr) * 1992-12-18 1994-07-07 Cambridge Display Technology Limited Dispositif electroluminescent comportant une composition polymere chromophore
GB2292947A (en) * 1994-09-12 1996-03-13 Motorola Inc A conjugated polymer with built-in fluorescent centres

Patent Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP0456609A1 (fr) * 1990-05-08 1991-11-13 Ciba-Geigy Ag Pigments fluorescents jaunes à base de tétrachloro-1,2,3,4-11H-isoindolo-(2,1-a)-benzimidazolone-11
WO1994015441A1 (fr) * 1992-12-18 1994-07-07 Cambridge Display Technology Limited Dispositif electroluminescent comportant une composition polymere chromophore
GB2292947A (en) * 1994-09-12 1996-03-13 Motorola Inc A conjugated polymer with built-in fluorescent centres

Cited By (12)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2002012402A2 (fr) * 2000-08-07 2002-02-14 Eastman Chemical Company Composes colorants contenant des groupes vinyle polymerisables
WO2002012402A3 (fr) * 2000-08-07 2002-10-17 Eastman Chem Co Composes colorants contenant des groupes vinyle polymerisables
JP2004506063A (ja) * 2000-08-07 2004-02-26 イーストマン　ケミカル　カンパニー 共重合性ビニル基を含有する着色剤化合物
US6727372B2 (en) 2000-08-07 2004-04-27 Eastman Chemical Company Colorant compounds containing copolymerizable vinyl groups
US7030244B2 (en) 2000-08-07 2006-04-18 Eastman Chemical Company Colorant compounds containing copolymerizable vinyl groups
US7060829B2 (en) 2000-08-07 2006-06-13 Eastman Chemical Company Colorant compounds containing copolymerizable vinyl groups
US7138539B2 (en) 2000-08-07 2006-11-21 Eastman Chemical Company Colorant compounds containing copolymerizable vinyl groups
EP1739135A2 (fr) * 2000-08-07 2007-01-03 Eastman Chemical Company Composés colorant contenant des groupes vinyle polymérisables
EP1739135A3 (fr) * 2000-08-07 2008-12-10 Eastman Chemical Company Composés colorant contenant des groupes vinyle polymérisables
WO2007059449A2 (fr) * 2005-11-10 2007-05-24 Beckman Coulter, Inc. Derives de bleu de nil lies par covalence pour des sondes optiques
WO2007059449A3 (fr) * 2005-11-10 2007-08-09 Beckman Coulter Inc Derives de bleu de nil lies par covalence pour des sondes optiques
US8242203B2 (en) 2005-11-10 2012-08-14 Eric Bakker Covalently attached nile blue derivatives for optical sensors

Similar Documents

Publication Publication Date Title
EP0968253B1 (fr) Systeme hote-client fluorescent
CN101184803B (zh) 官能化的纳米颗粒
WO1998033866A1 (fr) Systeme hote-client fluorescent
KR100511708B1 (ko) 형광 호스트-게스트-시스템
WO1998033862A1 (fr) Materiaux fluorescents et leur utilisation
CZ273399A3 (cs) Fluorescenční systém hostitel/host, způsob jeho přípravy a prostředky, které jej obsahují
KR100511709B1 (ko) 형광 물질용 조성물 및 이의 제조방법
TW526252B (en) Solid compositions, their preparation process and their use
TW557322B (en) Novel benzo [4,5] imidazo [2,1-a] isoindol-11-ones, the composition comprising the same, the process for the preparation of said composition, and the applications thereof
CZ273199A3 (cs) Fluorescenční prostředky, způsob jejich přípravy a jejich použití
CZ273299A3 (cs) Fluorescenční chromofor kovalentně vázaný na organický nosič, způsob jeho přípravy a jeho použití

Legal Events

Date Code Title Description
WWE Wipo information: entry into national phase

Ref document number: 98802281.8

Country of ref document: CN

AK Designated states

Kind code of ref document: A1

Designated state(s): AL AM AT AU AZ BA BB BG BR BY CA CH CN CU CZ DE DK EE ES FI GB GE GH GM GW HU ID IL IS JP KE KG KP KR KZ LC LK LR LS LT LU LV MD MG MK MN MW MX NO NZ PL PT RO RU SD SE SG SI SK SL TJ TM TR TT UA UG UZ VN YU ZW

AL Designated countries for regional patents

Kind code of ref document: A1

Designated state(s): GH GM KE LS MW SD SZ UG ZW AM AZ BY KG KZ MD RU TJ TM AT BE CH DE DK ES FI FR GB GR IE IT LU MC NL PT SE BF BJ CF CG CI CM GA GN ML MR NE SN TD TG

121 Ep: the epo has been informed by wipo that ep was designated in this application
WWE Wipo information: entry into national phase

Ref document number: 1998904111

Country of ref document: EP

WWE Wipo information: entry into national phase

Ref document number: 62120/98

Country of ref document: AU

WWE Wipo information: entry into national phase

Ref document number: PV1999-2733

Country of ref document: CZ

Ref document number: 1019997006960

Country of ref document: KR

ENP Entry into the national phase

Ref document number: 1998 532508

Country of ref document: JP

Kind code of ref document: A

REG Reference to national code

Ref country code: DE

Ref legal event code: 8642

WWP Wipo information: published in national office

Ref document number: 1998904111

Country of ref document: EP

WWP Wipo information: published in national office

Ref document number: PV1999-2733

Country of ref document: CZ

WWP Wipo information: published in national office

Ref document number: 1019997006960

Country of ref document: KR

WWR Wipo information: refused in national office

Ref document number: PV1999-2733

Country of ref document: CZ

WWG Wipo information: grant in national office

Ref document number: 62120/98

Country of ref document: AU

WWG Wipo information: grant in national office

Ref document number: 1998904111

Country of ref document: EP

WWG Wipo information: grant in national office