WO1994004352A1 - Particle binders - Google Patents

Particle binders Download PDF

Info

Publication number
WO1994004352A1
WO1994004352A1 PCT/US1993/007781 US9307781W WO9404352A1 WO 1994004352 A1 WO1994004352 A1 WO 1994004352A1 US 9307781 W US9307781 W US 9307781W WO 9404352 A1 WO9404352 A1 WO 9404352A1
Authority
WO
WIPO (PCT)
Prior art keywords
binder
particles
fibers
fibrous material
product
Prior art date
Application number
PCT/US1993/007781
Other languages
English (en)
French (fr)
Inventor
Michael R. Hansen
Richard H. Young, Sr.
Original Assignee
Weyerhaeuser Company
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Family has litigation
First worldwide family litigation filed litigation Critical https://patents.darts-ip.com/?family=27560346&utm_source=google_patent&utm_medium=platform_link&utm_campaign=public_patent_search&patent=WO1994004352(A1) "Global patent litigation dataset” by Darts-ip is licensed under a Creative Commons Attribution 4.0 International License.
Priority claimed from US07/931,059 external-priority patent/US5543215A/en
Priority claimed from US07/931,213 external-priority patent/US5300192A/en
Priority claimed from US07/931,278 external-priority patent/US5352480A/en
Priority claimed from US07/931,277 external-priority patent/US5538783A/en
Priority claimed from US07/931,279 external-priority patent/US5589256A/en
Priority claimed from US07/931,284 external-priority patent/US5308896A/en
Priority to CA002140263A priority Critical patent/CA2140263C/en
Priority to JP50651494A priority patent/JP3539957B2/ja
Priority to DE69332336T priority patent/DE69332336T3/de
Priority to AU50199/93A priority patent/AU5019993A/en
Priority to ES93920180T priority patent/ES2181693T5/es
Application filed by Weyerhaeuser Company filed Critical Weyerhaeuser Company
Priority to AT93920180T priority patent/ATE224808T1/de
Priority to BR9306921A priority patent/BR9306921A/pt
Priority to EP93920180A priority patent/EP0655971B2/en
Publication of WO1994004352A1 publication Critical patent/WO1994004352A1/en
Priority to KR1019950700602A priority patent/KR950702910A/ko

Links

Classifications

    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B5/00—Layered products characterised by the non- homogeneity or physical structure, i.e. comprising a fibrous, filamentary, particulate or foam layer; Layered products characterised by having a layer differing constitutionally or physically in different parts
    • B32B5/16—Layered products characterised by the non- homogeneity or physical structure, i.e. comprising a fibrous, filamentary, particulate or foam layer; Layered products characterised by having a layer differing constitutionally or physically in different parts characterised by features of a layer formed of particles, e.g. chips, powder or granules
    • D—TEXTILES; PAPER
    • D21—PAPER-MAKING; PRODUCTION OF CELLULOSE
    • D21H—PULP COMPOSITIONS; PREPARATION THEREOF NOT COVERED BY SUBCLASSES D21C OR D21D; IMPREGNATING OR COATING OF PAPER; TREATMENT OF FINISHED PAPER NOT COVERED BY CLASS B31 OR SUBCLASS D21G; PAPER NOT OTHERWISE PROVIDED FOR
    • D21H11/00—Pulp or paper, comprising cellulose or lignocellulose fibres of natural origin only
    • D21H11/16—Pulp or paper, comprising cellulose or lignocellulose fibres of natural origin only modified by a particular after-treatment
    • A—HUMAN NECESSITIES
    • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
    • A61F—FILTERS IMPLANTABLE INTO BLOOD VESSELS; PROSTHESES; DEVICES PROVIDING PATENCY TO, OR PREVENTING COLLAPSING OF, TUBULAR STRUCTURES OF THE BODY, e.g. STENTS; ORTHOPAEDIC, NURSING OR CONTRACEPTIVE DEVICES; FOMENTATION; TREATMENT OR PROTECTION OF EYES OR EARS; BANDAGES, DRESSINGS OR ABSORBENT PADS; FIRST-AID KITS
    • A61F13/00—Bandages or dressings; Absorbent pads
    • A61F13/02—Adhesive bandages or dressings
    • A61F13/0203—Adhesive bandages or dressings with fluid retention members
    • A61F13/0206—Adhesive bandages or dressings with fluid retention members with absorbent fibrous layers, e.g. woven or non-woven absorbent pads or island dressings
    • A61F13/0209—Adhesive bandages or dressings with fluid retention members with absorbent fibrous layers, e.g. woven or non-woven absorbent pads or island dressings comprising superabsorbent material
    • A—HUMAN NECESSITIES
    • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
    • A61F—FILTERS IMPLANTABLE INTO BLOOD VESSELS; PROSTHESES; DEVICES PROVIDING PATENCY TO, OR PREVENTING COLLAPSING OF, TUBULAR STRUCTURES OF THE BODY, e.g. STENTS; ORTHOPAEDIC, NURSING OR CONTRACEPTIVE DEVICES; FOMENTATION; TREATMENT OR PROTECTION OF EYES OR EARS; BANDAGES, DRESSINGS OR ABSORBENT PADS; FIRST-AID KITS
    • A61F13/00—Bandages or dressings; Absorbent pads
    • A61F13/15—Absorbent pads, e.g. sanitary towels, swabs or tampons for external or internal application to the body; Supporting or fastening means therefor; Tampon applicators
    • A—HUMAN NECESSITIES
    • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
    • A61F—FILTERS IMPLANTABLE INTO BLOOD VESSELS; PROSTHESES; DEVICES PROVIDING PATENCY TO, OR PREVENTING COLLAPSING OF, TUBULAR STRUCTURES OF THE BODY, e.g. STENTS; ORTHOPAEDIC, NURSING OR CONTRACEPTIVE DEVICES; FOMENTATION; TREATMENT OR PROTECTION OF EYES OR EARS; BANDAGES, DRESSINGS OR ABSORBENT PADS; FIRST-AID KITS
    • A61F13/00—Bandages or dressings; Absorbent pads
    • A61F13/15—Absorbent pads, e.g. sanitary towels, swabs or tampons for external or internal application to the body; Supporting or fastening means therefor; Tampon applicators
    • A61F13/53—Absorbent pads, e.g. sanitary towels, swabs or tampons for external or internal application to the body; Supporting or fastening means therefor; Tampon applicators characterised by the absorbing medium
    • A—HUMAN NECESSITIES
    • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
    • A61L—METHODS OR APPARATUS FOR STERILISING MATERIALS OR OBJECTS IN GENERAL; DISINFECTION, STERILISATION OR DEODORISATION OF AIR; CHEMICAL ASPECTS OF BANDAGES, DRESSINGS, ABSORBENT PADS OR SURGICAL ARTICLES; MATERIALS FOR BANDAGES, DRESSINGS, ABSORBENT PADS OR SURGICAL ARTICLES
    • A61L15/00—Chemical aspects of, or use of materials for, bandages, dressings or absorbent pads
    • A61L15/16—Bandages, dressings or absorbent pads for physiological fluids such as urine or blood, e.g. sanitary towels, tampons
    • A61L15/42—Use of materials characterised by their function or physical properties
    • A61L15/60—Liquid-swellable gel-forming materials, e.g. super-absorbents
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B27—WORKING OR PRESERVING WOOD OR SIMILAR MATERIAL; NAILING OR STAPLING MACHINES IN GENERAL
    • B27N—MANUFACTURE BY DRY PROCESSES OF ARTICLES, WITH OR WITHOUT ORGANIC BINDING AGENTS, MADE FROM PARTICLES OR FIBRES CONSISTING OF WOOD OR OTHER LIGNOCELLULOSIC OR LIKE ORGANIC MATERIAL
    • B27N3/00—Manufacture of substantially flat articles, e.g. boards, from particles or fibres
    • D—TEXTILES; PAPER
    • D04—BRAIDING; LACE-MAKING; KNITTING; TRIMMINGS; NON-WOVEN FABRICS
    • D04H—MAKING TEXTILE FABRICS, e.g. FROM FIBRES OR FILAMENTARY MATERIAL; FABRICS MADE BY SUCH PROCESSES OR APPARATUS, e.g. FELTS, NON-WOVEN FABRICS; COTTON-WOOL; WADDING ; NON-WOVEN FABRICS FROM STAPLE FIBRES, FILAMENTS OR YARNS, BONDED WITH AT LEAST ONE WEB-LIKE MATERIAL DURING THEIR CONSOLIDATION
    • D04H1/00—Non-woven fabrics formed wholly or mainly of staple fibres or like relatively short fibres
    • D04H1/40—Non-woven fabrics formed wholly or mainly of staple fibres or like relatively short fibres from fleeces or layers composed of fibres without existing or potential cohesive properties
    • D04H1/58—Non-woven fabrics formed wholly or mainly of staple fibres or like relatively short fibres from fleeces or layers composed of fibres without existing or potential cohesive properties by applying, incorporating or activating chemical or thermoplastic bonding agents, e.g. adhesives
    • D04H1/587—Non-woven fabrics formed wholly or mainly of staple fibres or like relatively short fibres from fleeces or layers composed of fibres without existing or potential cohesive properties by applying, incorporating or activating chemical or thermoplastic bonding agents, e.g. adhesives characterised by the bonding agents used
    • D—TEXTILES; PAPER
    • D04—BRAIDING; LACE-MAKING; KNITTING; TRIMMINGS; NON-WOVEN FABRICS
    • D04H—MAKING TEXTILE FABRICS, e.g. FROM FIBRES OR FILAMENTARY MATERIAL; FABRICS MADE BY SUCH PROCESSES OR APPARATUS, e.g. FELTS, NON-WOVEN FABRICS; COTTON-WOOL; WADDING ; NON-WOVEN FABRICS FROM STAPLE FIBRES, FILAMENTS OR YARNS, BONDED WITH AT LEAST ONE WEB-LIKE MATERIAL DURING THEIR CONSOLIDATION
    • D04H1/00—Non-woven fabrics formed wholly or mainly of staple fibres or like relatively short fibres
    • D04H1/40—Non-woven fabrics formed wholly or mainly of staple fibres or like relatively short fibres from fleeces or layers composed of fibres without existing or potential cohesive properties
    • D04H1/58—Non-woven fabrics formed wholly or mainly of staple fibres or like relatively short fibres from fleeces or layers composed of fibres without existing or potential cohesive properties by applying, incorporating or activating chemical or thermoplastic bonding agents, e.g. adhesives
    • D04H1/64—Non-woven fabrics formed wholly or mainly of staple fibres or like relatively short fibres from fleeces or layers composed of fibres without existing or potential cohesive properties by applying, incorporating or activating chemical or thermoplastic bonding agents, e.g. adhesives the bonding agent being applied in wet state, e.g. chemical agents in dispersions or solutions
    • D—TEXTILES; PAPER
    • D06—TREATMENT OF TEXTILES OR THE LIKE; LAUNDERING; FLEXIBLE MATERIALS NOT OTHERWISE PROVIDED FOR
    • D06M—TREATMENT, NOT PROVIDED FOR ELSEWHERE IN CLASS D06, OF FIBRES, THREADS, YARNS, FABRICS, FEATHERS OR FIBROUS GOODS MADE FROM SUCH MATERIALS
    • D06M13/00—Treating fibres, threads, yarns, fabrics or fibrous goods made from such materials, with non-macromolecular organic compounds; Such treatment combined with mechanical treatment
    • D06M13/10—Treating fibres, threads, yarns, fabrics or fibrous goods made from such materials, with non-macromolecular organic compounds; Such treatment combined with mechanical treatment with compounds containing oxygen
    • D06M13/184—Carboxylic acids; Anhydrides, halides or salts thereof
    • D—TEXTILES; PAPER
    • D06—TREATMENT OF TEXTILES OR THE LIKE; LAUNDERING; FLEXIBLE MATERIALS NOT OTHERWISE PROVIDED FOR
    • D06M—TREATMENT, NOT PROVIDED FOR ELSEWHERE IN CLASS D06, OF FIBRES, THREADS, YARNS, FABRICS, FEATHERS OR FIBROUS GOODS MADE FROM SUCH MATERIALS
    • D06M13/00—Treating fibres, threads, yarns, fabrics or fibrous goods made from such materials, with non-macromolecular organic compounds; Such treatment combined with mechanical treatment
    • D06M13/244—Treating fibres, threads, yarns, fabrics or fibrous goods made from such materials, with non-macromolecular organic compounds; Such treatment combined with mechanical treatment with compounds containing sulfur or phosphorus
    • D06M13/248—Treating fibres, threads, yarns, fabrics or fibrous goods made from such materials, with non-macromolecular organic compounds; Such treatment combined with mechanical treatment with compounds containing sulfur or phosphorus with compounds containing sulfur
    • D06M13/256—Sulfonated compounds esters thereof, e.g. sultones
    • D—TEXTILES; PAPER
    • D06—TREATMENT OF TEXTILES OR THE LIKE; LAUNDERING; FLEXIBLE MATERIALS NOT OTHERWISE PROVIDED FOR
    • D06M—TREATMENT, NOT PROVIDED FOR ELSEWHERE IN CLASS D06, OF FIBRES, THREADS, YARNS, FABRICS, FEATHERS OR FIBROUS GOODS MADE FROM SUCH MATERIALS
    • D06M13/00—Treating fibres, threads, yarns, fabrics or fibrous goods made from such materials, with non-macromolecular organic compounds; Such treatment combined with mechanical treatment
    • D06M13/244—Treating fibres, threads, yarns, fabrics or fibrous goods made from such materials, with non-macromolecular organic compounds; Such treatment combined with mechanical treatment with compounds containing sulfur or phosphorus
    • D06M13/282—Treating fibres, threads, yarns, fabrics or fibrous goods made from such materials, with non-macromolecular organic compounds; Such treatment combined with mechanical treatment with compounds containing sulfur or phosphorus with compounds containing phosphorus
    • D06M13/285—Phosphines; Phosphine oxides; Phosphine sulfides; Phosphinic or phosphinous acids or derivatives thereof
    • D—TEXTILES; PAPER
    • D06—TREATMENT OF TEXTILES OR THE LIKE; LAUNDERING; FLEXIBLE MATERIALS NOT OTHERWISE PROVIDED FOR
    • D06M—TREATMENT, NOT PROVIDED FOR ELSEWHERE IN CLASS D06, OF FIBRES, THREADS, YARNS, FABRICS, FEATHERS OR FIBROUS GOODS MADE FROM SUCH MATERIALS
    • D06M13/00—Treating fibres, threads, yarns, fabrics or fibrous goods made from such materials, with non-macromolecular organic compounds; Such treatment combined with mechanical treatment
    • D06M13/244—Treating fibres, threads, yarns, fabrics or fibrous goods made from such materials, with non-macromolecular organic compounds; Such treatment combined with mechanical treatment with compounds containing sulfur or phosphorus
    • D06M13/282—Treating fibres, threads, yarns, fabrics or fibrous goods made from such materials, with non-macromolecular organic compounds; Such treatment combined with mechanical treatment with compounds containing sulfur or phosphorus with compounds containing phosphorus
    • D06M13/288—Phosphonic or phosphonous acids or derivatives thereof
    • D—TEXTILES; PAPER
    • D06—TREATMENT OF TEXTILES OR THE LIKE; LAUNDERING; FLEXIBLE MATERIALS NOT OTHERWISE PROVIDED FOR
    • D06M—TREATMENT, NOT PROVIDED FOR ELSEWHERE IN CLASS D06, OF FIBRES, THREADS, YARNS, FABRICS, FEATHERS OR FIBROUS GOODS MADE FROM SUCH MATERIALS
    • D06M13/00—Treating fibres, threads, yarns, fabrics or fibrous goods made from such materials, with non-macromolecular organic compounds; Such treatment combined with mechanical treatment
    • D06M13/244—Treating fibres, threads, yarns, fabrics or fibrous goods made from such materials, with non-macromolecular organic compounds; Such treatment combined with mechanical treatment with compounds containing sulfur or phosphorus
    • D06M13/282—Treating fibres, threads, yarns, fabrics or fibrous goods made from such materials, with non-macromolecular organic compounds; Such treatment combined with mechanical treatment with compounds containing sulfur or phosphorus with compounds containing phosphorus
    • D06M13/292—Mono-, di- or triesters of phosphoric or phosphorous acids; Salts thereof
    • D—TEXTILES; PAPER
    • D06—TREATMENT OF TEXTILES OR THE LIKE; LAUNDERING; FLEXIBLE MATERIALS NOT OTHERWISE PROVIDED FOR
    • D06M—TREATMENT, NOT PROVIDED FOR ELSEWHERE IN CLASS D06, OF FIBRES, THREADS, YARNS, FABRICS, FEATHERS OR FIBROUS GOODS MADE FROM SUCH MATERIALS
    • D06M13/00—Treating fibres, threads, yarns, fabrics or fibrous goods made from such materials, with non-macromolecular organic compounds; Such treatment combined with mechanical treatment
    • D06M13/322—Treating fibres, threads, yarns, fabrics or fibrous goods made from such materials, with non-macromolecular organic compounds; Such treatment combined with mechanical treatment with compounds containing nitrogen
    • D06M13/325—Amines
    • D06M13/342—Amino-carboxylic acids; Betaines; Aminosulfonic acids; Sulfo-betaines
    • D—TEXTILES; PAPER
    • D06—TREATMENT OF TEXTILES OR THE LIKE; LAUNDERING; FLEXIBLE MATERIALS NOT OTHERWISE PROVIDED FOR
    • D06M—TREATMENT, NOT PROVIDED FOR ELSEWHERE IN CLASS D06, OF FIBRES, THREADS, YARNS, FABRICS, FEATHERS OR FIBROUS GOODS MADE FROM SUCH MATERIALS
    • D06M23/00—Treatment of fibres, threads, yarns, fabrics or fibrous goods made from such materials, characterised by the process
    • D—TEXTILES; PAPER
    • D06—TREATMENT OF TEXTILES OR THE LIKE; LAUNDERING; FLEXIBLE MATERIALS NOT OTHERWISE PROVIDED FOR
    • D06M—TREATMENT, NOT PROVIDED FOR ELSEWHERE IN CLASS D06, OF FIBRES, THREADS, YARNS, FABRICS, FEATHERS OR FIBROUS GOODS MADE FROM SUCH MATERIALS
    • D06M23/00—Treatment of fibres, threads, yarns, fabrics or fibrous goods made from such materials, characterised by the process
    • D06M23/08—Processes in which the treating agent is applied in powder or granular form
    • A—HUMAN NECESSITIES
    • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
    • A61F—FILTERS IMPLANTABLE INTO BLOOD VESSELS; PROSTHESES; DEVICES PROVIDING PATENCY TO, OR PREVENTING COLLAPSING OF, TUBULAR STRUCTURES OF THE BODY, e.g. STENTS; ORTHOPAEDIC, NURSING OR CONTRACEPTIVE DEVICES; FOMENTATION; TREATMENT OR PROTECTION OF EYES OR EARS; BANDAGES, DRESSINGS OR ABSORBENT PADS; FIRST-AID KITS
    • A61F13/00—Bandages or dressings; Absorbent pads
    • A61F13/15—Absorbent pads, e.g. sanitary towels, swabs or tampons for external or internal application to the body; Supporting or fastening means therefor; Tampon applicators
    • A61F13/51—Absorbent pads, e.g. sanitary towels, swabs or tampons for external or internal application to the body; Supporting or fastening means therefor; Tampon applicators characterised by the outer layers
    • A61F13/511—Topsheet, i.e. the permeable cover or layer facing the skin
    • A—HUMAN NECESSITIES
    • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
    • A61F—FILTERS IMPLANTABLE INTO BLOOD VESSELS; PROSTHESES; DEVICES PROVIDING PATENCY TO, OR PREVENTING COLLAPSING OF, TUBULAR STRUCTURES OF THE BODY, e.g. STENTS; ORTHOPAEDIC, NURSING OR CONTRACEPTIVE DEVICES; FOMENTATION; TREATMENT OR PROTECTION OF EYES OR EARS; BANDAGES, DRESSINGS OR ABSORBENT PADS; FIRST-AID KITS
    • A61F13/00—Bandages or dressings; Absorbent pads
    • A61F13/15—Absorbent pads, e.g. sanitary towels, swabs or tampons for external or internal application to the body; Supporting or fastening means therefor; Tampon applicators
    • A61F13/53—Absorbent pads, e.g. sanitary towels, swabs or tampons for external or internal application to the body; Supporting or fastening means therefor; Tampon applicators characterised by the absorbing medium
    • A61F13/531—Absorbent pads, e.g. sanitary towels, swabs or tampons for external or internal application to the body; Supporting or fastening means therefor; Tampon applicators characterised by the absorbing medium having a homogeneous composition through the thickness of the pad
    • A61F13/532—Absorbent pads, e.g. sanitary towels, swabs or tampons for external or internal application to the body; Supporting or fastening means therefor; Tampon applicators characterised by the absorbing medium having a homogeneous composition through the thickness of the pad inhomogeneous in the plane of the pad
    • A61F13/533—Absorbent pads, e.g. sanitary towels, swabs or tampons for external or internal application to the body; Supporting or fastening means therefor; Tampon applicators characterised by the absorbing medium having a homogeneous composition through the thickness of the pad inhomogeneous in the plane of the pad having discontinuous areas of compression
    • A—HUMAN NECESSITIES
    • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
    • A61F—FILTERS IMPLANTABLE INTO BLOOD VESSELS; PROSTHESES; DEVICES PROVIDING PATENCY TO, OR PREVENTING COLLAPSING OF, TUBULAR STRUCTURES OF THE BODY, e.g. STENTS; ORTHOPAEDIC, NURSING OR CONTRACEPTIVE DEVICES; FOMENTATION; TREATMENT OR PROTECTION OF EYES OR EARS; BANDAGES, DRESSINGS OR ABSORBENT PADS; FIRST-AID KITS
    • A61F13/00—Bandages or dressings; Absorbent pads
    • A61F2013/00089—Wound bandages
    • A61F2013/00246—Wound bandages in a special way pervious to air or vapours
    • A61F2013/00251—Wound bandages in a special way pervious to air or vapours with macroscopic openings
    • A—HUMAN NECESSITIES
    • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
    • A61F—FILTERS IMPLANTABLE INTO BLOOD VESSELS; PROSTHESES; DEVICES PROVIDING PATENCY TO, OR PREVENTING COLLAPSING OF, TUBULAR STRUCTURES OF THE BODY, e.g. STENTS; ORTHOPAEDIC, NURSING OR CONTRACEPTIVE DEVICES; FOMENTATION; TREATMENT OR PROTECTION OF EYES OR EARS; BANDAGES, DRESSINGS OR ABSORBENT PADS; FIRST-AID KITS
    • A61F13/00—Bandages or dressings; Absorbent pads
    • A61F2013/00361—Plasters
    • A61F2013/00365—Plasters use
    • A61F2013/00463—Plasters use haemostatic
    • A61F2013/00472—Plasters use haemostatic with chemical means
    • A—HUMAN NECESSITIES
    • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
    • A61F—FILTERS IMPLANTABLE INTO BLOOD VESSELS; PROSTHESES; DEVICES PROVIDING PATENCY TO, OR PREVENTING COLLAPSING OF, TUBULAR STRUCTURES OF THE BODY, e.g. STENTS; ORTHOPAEDIC, NURSING OR CONTRACEPTIVE DEVICES; FOMENTATION; TREATMENT OR PROTECTION OF EYES OR EARS; BANDAGES, DRESSINGS OR ABSORBENT PADS; FIRST-AID KITS
    • A61F13/00—Bandages or dressings; Absorbent pads
    • A61F2013/00361—Plasters
    • A61F2013/00727—Plasters means for wound humidity control
    • A61F2013/00731—Plasters means for wound humidity control with absorbing pads
    • A—HUMAN NECESSITIES
    • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
    • A61F—FILTERS IMPLANTABLE INTO BLOOD VESSELS; PROSTHESES; DEVICES PROVIDING PATENCY TO, OR PREVENTING COLLAPSING OF, TUBULAR STRUCTURES OF THE BODY, e.g. STENTS; ORTHOPAEDIC, NURSING OR CONTRACEPTIVE DEVICES; FOMENTATION; TREATMENT OR PROTECTION OF EYES OR EARS; BANDAGES, DRESSINGS OR ABSORBENT PADS; FIRST-AID KITS
    • A61F13/00—Bandages or dressings; Absorbent pads
    • A61F2013/00361—Plasters
    • A61F2013/00727—Plasters means for wound humidity control
    • A61F2013/00748—Plasters means for wound humidity control with hydrocolloids or superabsorbers
    • A—HUMAN NECESSITIES
    • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
    • A61F—FILTERS IMPLANTABLE INTO BLOOD VESSELS; PROSTHESES; DEVICES PROVIDING PATENCY TO, OR PREVENTING COLLAPSING OF, TUBULAR STRUCTURES OF THE BODY, e.g. STENTS; ORTHOPAEDIC, NURSING OR CONTRACEPTIVE DEVICES; FOMENTATION; TREATMENT OR PROTECTION OF EYES OR EARS; BANDAGES, DRESSINGS OR ABSORBENT PADS; FIRST-AID KITS
    • A61F13/00—Bandages or dressings; Absorbent pads
    • A61F2013/00361—Plasters
    • A61F2013/00855—Plasters pervious to air or vapours
    • A61F2013/00859—Plasters pervious to air or vapours with macroscopic openings
    • A—HUMAN NECESSITIES
    • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
    • A61F—FILTERS IMPLANTABLE INTO BLOOD VESSELS; PROSTHESES; DEVICES PROVIDING PATENCY TO, OR PREVENTING COLLAPSING OF, TUBULAR STRUCTURES OF THE BODY, e.g. STENTS; ORTHOPAEDIC, NURSING OR CONTRACEPTIVE DEVICES; FOMENTATION; TREATMENT OR PROTECTION OF EYES OR EARS; BANDAGES, DRESSINGS OR ABSORBENT PADS; FIRST-AID KITS
    • A61F13/00—Bandages or dressings; Absorbent pads
    • A61F2013/00361—Plasters
    • A61F2013/00902—Plasters containing means
    • A61F2013/0091—Plasters containing means with disinfecting or anaesthetics means, e.g. anti-mycrobic
    • A—HUMAN NECESSITIES
    • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
    • A61F—FILTERS IMPLANTABLE INTO BLOOD VESSELS; PROSTHESES; DEVICES PROVIDING PATENCY TO, OR PREVENTING COLLAPSING OF, TUBULAR STRUCTURES OF THE BODY, e.g. STENTS; ORTHOPAEDIC, NURSING OR CONTRACEPTIVE DEVICES; FOMENTATION; TREATMENT OR PROTECTION OF EYES OR EARS; BANDAGES, DRESSINGS OR ABSORBENT PADS; FIRST-AID KITS
    • A61F13/00—Bandages or dressings; Absorbent pads
    • A61F2013/00361—Plasters
    • A61F2013/00902—Plasters containing means
    • A61F2013/00927—Plasters containing means with biological activity, e.g. enzymes for debriding wounds or others, collagen or growth factors
    • A—HUMAN NECESSITIES
    • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
    • A61F—FILTERS IMPLANTABLE INTO BLOOD VESSELS; PROSTHESES; DEVICES PROVIDING PATENCY TO, OR PREVENTING COLLAPSING OF, TUBULAR STRUCTURES OF THE BODY, e.g. STENTS; ORTHOPAEDIC, NURSING OR CONTRACEPTIVE DEVICES; FOMENTATION; TREATMENT OR PROTECTION OF EYES OR EARS; BANDAGES, DRESSINGS OR ABSORBENT PADS; FIRST-AID KITS
    • A61F13/00—Bandages or dressings; Absorbent pads
    • A61F13/15—Absorbent pads, e.g. sanitary towels, swabs or tampons for external or internal application to the body; Supporting or fastening means therefor; Tampon applicators
    • A61F13/15203—Properties of the article, e.g. stiffness or absorbency
    • A61F2013/15284—Properties of the article, e.g. stiffness or absorbency characterized by quantifiable properties
    • A61F2013/15422—Density
    • A—HUMAN NECESSITIES
    • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
    • A61F—FILTERS IMPLANTABLE INTO BLOOD VESSELS; PROSTHESES; DEVICES PROVIDING PATENCY TO, OR PREVENTING COLLAPSING OF, TUBULAR STRUCTURES OF THE BODY, e.g. STENTS; ORTHOPAEDIC, NURSING OR CONTRACEPTIVE DEVICES; FOMENTATION; TREATMENT OR PROTECTION OF EYES OR EARS; BANDAGES, DRESSINGS OR ABSORBENT PADS; FIRST-AID KITS
    • A61F13/00—Bandages or dressings; Absorbent pads
    • A61F13/15—Absorbent pads, e.g. sanitary towels, swabs or tampons for external or internal application to the body; Supporting or fastening means therefor; Tampon applicators
    • A61F13/15577—Apparatus or processes for manufacturing
    • A61F2013/15821—Apparatus or processes for manufacturing characterized by the apparatus for manufacturing
    • A61F2013/15934—Apparatus or processes for manufacturing characterized by the apparatus for manufacturing for making non-woven
    • A61F2013/15951—Apparatus or processes for manufacturing characterized by the apparatus for manufacturing for making non-woven by wet-laid technique
    • A—HUMAN NECESSITIES
    • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
    • A61F—FILTERS IMPLANTABLE INTO BLOOD VESSELS; PROSTHESES; DEVICES PROVIDING PATENCY TO, OR PREVENTING COLLAPSING OF, TUBULAR STRUCTURES OF THE BODY, e.g. STENTS; ORTHOPAEDIC, NURSING OR CONTRACEPTIVE DEVICES; FOMENTATION; TREATMENT OR PROTECTION OF EYES OR EARS; BANDAGES, DRESSINGS OR ABSORBENT PADS; FIRST-AID KITS
    • A61F13/00—Bandages or dressings; Absorbent pads
    • A61F13/15—Absorbent pads, e.g. sanitary towels, swabs or tampons for external or internal application to the body; Supporting or fastening means therefor; Tampon applicators
    • A61F13/51—Absorbent pads, e.g. sanitary towels, swabs or tampons for external or internal application to the body; Supporting or fastening means therefor; Tampon applicators characterised by the outer layers
    • A61F2013/51002—Absorbent pads, e.g. sanitary towels, swabs or tampons for external or internal application to the body; Supporting or fastening means therefor; Tampon applicators characterised by the outer layers with special fibres
    • A61F2013/51038—Absorbent pads, e.g. sanitary towels, swabs or tampons for external or internal application to the body; Supporting or fastening means therefor; Tampon applicators characterised by the outer layers with special fibres being a mixture of fibres
    • A61F2013/5104—Absorbent pads, e.g. sanitary towels, swabs or tampons for external or internal application to the body; Supporting or fastening means therefor; Tampon applicators characterised by the outer layers with special fibres being a mixture of fibres with pulp and polymeric fibres
    • A—HUMAN NECESSITIES
    • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
    • A61F—FILTERS IMPLANTABLE INTO BLOOD VESSELS; PROSTHESES; DEVICES PROVIDING PATENCY TO, OR PREVENTING COLLAPSING OF, TUBULAR STRUCTURES OF THE BODY, e.g. STENTS; ORTHOPAEDIC, NURSING OR CONTRACEPTIVE DEVICES; FOMENTATION; TREATMENT OR PROTECTION OF EYES OR EARS; BANDAGES, DRESSINGS OR ABSORBENT PADS; FIRST-AID KITS
    • A61F13/00—Bandages or dressings; Absorbent pads
    • A61F13/15—Absorbent pads, e.g. sanitary towels, swabs or tampons for external or internal application to the body; Supporting or fastening means therefor; Tampon applicators
    • A61F13/51—Absorbent pads, e.g. sanitary towels, swabs or tampons for external or internal application to the body; Supporting or fastening means therefor; Tampon applicators characterised by the outer layers
    • A61F2013/51078—Absorbent pads, e.g. sanitary towels, swabs or tampons for external or internal application to the body; Supporting or fastening means therefor; Tampon applicators characterised by the outer layers being embossed
    • A—HUMAN NECESSITIES
    • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
    • A61F—FILTERS IMPLANTABLE INTO BLOOD VESSELS; PROSTHESES; DEVICES PROVIDING PATENCY TO, OR PREVENTING COLLAPSING OF, TUBULAR STRUCTURES OF THE BODY, e.g. STENTS; ORTHOPAEDIC, NURSING OR CONTRACEPTIVE DEVICES; FOMENTATION; TREATMENT OR PROTECTION OF EYES OR EARS; BANDAGES, DRESSINGS OR ABSORBENT PADS; FIRST-AID KITS
    • A61F13/00—Bandages or dressings; Absorbent pads
    • A61F13/15—Absorbent pads, e.g. sanitary towels, swabs or tampons for external or internal application to the body; Supporting or fastening means therefor; Tampon applicators
    • A61F13/53—Absorbent pads, e.g. sanitary towels, swabs or tampons for external or internal application to the body; Supporting or fastening means therefor; Tampon applicators characterised by the absorbing medium
    • A61F2013/530007—Absorbent pads, e.g. sanitary towels, swabs or tampons for external or internal application to the body; Supporting or fastening means therefor; Tampon applicators characterised by the absorbing medium being made from pulp
    • A—HUMAN NECESSITIES
    • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
    • A61F—FILTERS IMPLANTABLE INTO BLOOD VESSELS; PROSTHESES; DEVICES PROVIDING PATENCY TO, OR PREVENTING COLLAPSING OF, TUBULAR STRUCTURES OF THE BODY, e.g. STENTS; ORTHOPAEDIC, NURSING OR CONTRACEPTIVE DEVICES; FOMENTATION; TREATMENT OR PROTECTION OF EYES OR EARS; BANDAGES, DRESSINGS OR ABSORBENT PADS; FIRST-AID KITS
    • A61F13/00—Bandages or dressings; Absorbent pads
    • A61F13/15—Absorbent pads, e.g. sanitary towels, swabs or tampons for external or internal application to the body; Supporting or fastening means therefor; Tampon applicators
    • A61F13/53—Absorbent pads, e.g. sanitary towels, swabs or tampons for external or internal application to the body; Supporting or fastening means therefor; Tampon applicators characterised by the absorbing medium
    • A61F2013/530131—Absorbent pads, e.g. sanitary towels, swabs or tampons for external or internal application to the body; Supporting or fastening means therefor; Tampon applicators characterised by the absorbing medium being made in fibre but being not pulp
    • A61F2013/530182—Absorbent pads, e.g. sanitary towels, swabs or tampons for external or internal application to the body; Supporting or fastening means therefor; Tampon applicators characterised by the absorbing medium being made in fibre but being not pulp characterized by the connection between the fibres
    • A61F2013/530189—Absorbent pads, e.g. sanitary towels, swabs or tampons for external or internal application to the body; Supporting or fastening means therefor; Tampon applicators characterised by the absorbing medium being made in fibre but being not pulp characterized by the connection between the fibres with thermoplastic adhesive
    • A—HUMAN NECESSITIES
    • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
    • A61F—FILTERS IMPLANTABLE INTO BLOOD VESSELS; PROSTHESES; DEVICES PROVIDING PATENCY TO, OR PREVENTING COLLAPSING OF, TUBULAR STRUCTURES OF THE BODY, e.g. STENTS; ORTHOPAEDIC, NURSING OR CONTRACEPTIVE DEVICES; FOMENTATION; TREATMENT OR PROTECTION OF EYES OR EARS; BANDAGES, DRESSINGS OR ABSORBENT PADS; FIRST-AID KITS
    • A61F13/00—Bandages or dressings; Absorbent pads
    • A61F13/15—Absorbent pads, e.g. sanitary towels, swabs or tampons for external or internal application to the body; Supporting or fastening means therefor; Tampon applicators
    • A61F13/53—Absorbent pads, e.g. sanitary towels, swabs or tampons for external or internal application to the body; Supporting or fastening means therefor; Tampon applicators characterised by the absorbing medium
    • A61F2013/530437—Absorbent pads, e.g. sanitary towels, swabs or tampons for external or internal application to the body; Supporting or fastening means therefor; Tampon applicators characterised by the absorbing medium having a part with elevated absorption means
    • A61F2013/530445—Absorbent pads, e.g. sanitary towels, swabs or tampons for external or internal application to the body; Supporting or fastening means therefor; Tampon applicators characterised by the absorbing medium having a part with elevated absorption means by defining a target or acquisition or vulnerability zone
    • A—HUMAN NECESSITIES
    • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
    • A61F—FILTERS IMPLANTABLE INTO BLOOD VESSELS; PROSTHESES; DEVICES PROVIDING PATENCY TO, OR PREVENTING COLLAPSING OF, TUBULAR STRUCTURES OF THE BODY, e.g. STENTS; ORTHOPAEDIC, NURSING OR CONTRACEPTIVE DEVICES; FOMENTATION; TREATMENT OR PROTECTION OF EYES OR EARS; BANDAGES, DRESSINGS OR ABSORBENT PADS; FIRST-AID KITS
    • A61F13/00—Bandages or dressings; Absorbent pads
    • A61F13/15—Absorbent pads, e.g. sanitary towels, swabs or tampons for external or internal application to the body; Supporting or fastening means therefor; Tampon applicators
    • A61F13/53—Absorbent pads, e.g. sanitary towels, swabs or tampons for external or internal application to the body; Supporting or fastening means therefor; Tampon applicators characterised by the absorbing medium
    • A61F2013/530481—Absorbent pads, e.g. sanitary towels, swabs or tampons for external or internal application to the body; Supporting or fastening means therefor; Tampon applicators characterised by the absorbing medium having superabsorbent materials, i.e. highly absorbent polymer gel materials
    • A61F2013/530489—Absorbent pads, e.g. sanitary towels, swabs or tampons for external or internal application to the body; Supporting or fastening means therefor; Tampon applicators characterised by the absorbing medium having superabsorbent materials, i.e. highly absorbent polymer gel materials being randomly mixed in with other material
    • A61F2013/530496—Absorbent pads, e.g. sanitary towels, swabs or tampons for external or internal application to the body; Supporting or fastening means therefor; Tampon applicators characterised by the absorbing medium having superabsorbent materials, i.e. highly absorbent polymer gel materials being randomly mixed in with other material being fixed to fibres
    • A—HUMAN NECESSITIES
    • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
    • A61F—FILTERS IMPLANTABLE INTO BLOOD VESSELS; PROSTHESES; DEVICES PROVIDING PATENCY TO, OR PREVENTING COLLAPSING OF, TUBULAR STRUCTURES OF THE BODY, e.g. STENTS; ORTHOPAEDIC, NURSING OR CONTRACEPTIVE DEVICES; FOMENTATION; TREATMENT OR PROTECTION OF EYES OR EARS; BANDAGES, DRESSINGS OR ABSORBENT PADS; FIRST-AID KITS
    • A61F13/00—Bandages or dressings; Absorbent pads
    • A61F13/15—Absorbent pads, e.g. sanitary towels, swabs or tampons for external or internal application to the body; Supporting or fastening means therefor; Tampon applicators
    • A61F13/53—Absorbent pads, e.g. sanitary towels, swabs or tampons for external or internal application to the body; Supporting or fastening means therefor; Tampon applicators characterised by the absorbing medium
    • A61F2013/530481—Absorbent pads, e.g. sanitary towels, swabs or tampons for external or internal application to the body; Supporting or fastening means therefor; Tampon applicators characterised by the absorbing medium having superabsorbent materials, i.e. highly absorbent polymer gel materials
    • A61F2013/53051—Absorbent pads, e.g. sanitary towels, swabs or tampons for external or internal application to the body; Supporting or fastening means therefor; Tampon applicators characterised by the absorbing medium having superabsorbent materials, i.e. highly absorbent polymer gel materials being only in particular parts or specially arranged
    • A61F2013/530525—Absorbent pads, e.g. sanitary towels, swabs or tampons for external or internal application to the body; Supporting or fastening means therefor; Tampon applicators characterised by the absorbing medium having superabsorbent materials, i.e. highly absorbent polymer gel materials being only in particular parts or specially arranged the maximum being at front or rear
    • A—HUMAN NECESSITIES
    • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
    • A61F—FILTERS IMPLANTABLE INTO BLOOD VESSELS; PROSTHESES; DEVICES PROVIDING PATENCY TO, OR PREVENTING COLLAPSING OF, TUBULAR STRUCTURES OF THE BODY, e.g. STENTS; ORTHOPAEDIC, NURSING OR CONTRACEPTIVE DEVICES; FOMENTATION; TREATMENT OR PROTECTION OF EYES OR EARS; BANDAGES, DRESSINGS OR ABSORBENT PADS; FIRST-AID KITS
    • A61F13/00—Bandages or dressings; Absorbent pads
    • A61F13/15—Absorbent pads, e.g. sanitary towels, swabs or tampons for external or internal application to the body; Supporting or fastening means therefor; Tampon applicators
    • A61F13/53—Absorbent pads, e.g. sanitary towels, swabs or tampons for external or internal application to the body; Supporting or fastening means therefor; Tampon applicators characterised by the absorbing medium
    • A61F2013/530481—Absorbent pads, e.g. sanitary towels, swabs or tampons for external or internal application to the body; Supporting or fastening means therefor; Tampon applicators characterised by the absorbing medium having superabsorbent materials, i.e. highly absorbent polymer gel materials
    • A61F2013/53051—Absorbent pads, e.g. sanitary towels, swabs or tampons for external or internal application to the body; Supporting or fastening means therefor; Tampon applicators characterised by the absorbing medium having superabsorbent materials, i.e. highly absorbent polymer gel materials being only in particular parts or specially arranged
    • A61F2013/530547—Absorbent pads, e.g. sanitary towels, swabs or tampons for external or internal application to the body; Supporting or fastening means therefor; Tampon applicators characterised by the absorbing medium having superabsorbent materials, i.e. highly absorbent polymer gel materials being only in particular parts or specially arranged positioned in a separate layer or layers
    • A61F2013/530554—Absorbent pads, e.g. sanitary towels, swabs or tampons for external or internal application to the body; Supporting or fastening means therefor; Tampon applicators characterised by the absorbing medium having superabsorbent materials, i.e. highly absorbent polymer gel materials being only in particular parts or specially arranged positioned in a separate layer or layers and being fixed to a web
    • A—HUMAN NECESSITIES
    • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
    • A61F—FILTERS IMPLANTABLE INTO BLOOD VESSELS; PROSTHESES; DEVICES PROVIDING PATENCY TO, OR PREVENTING COLLAPSING OF, TUBULAR STRUCTURES OF THE BODY, e.g. STENTS; ORTHOPAEDIC, NURSING OR CONTRACEPTIVE DEVICES; FOMENTATION; TREATMENT OR PROTECTION OF EYES OR EARS; BANDAGES, DRESSINGS OR ABSORBENT PADS; FIRST-AID KITS
    • A61F13/00—Bandages or dressings; Absorbent pads
    • A61F13/15—Absorbent pads, e.g. sanitary towels, swabs or tampons for external or internal application to the body; Supporting or fastening means therefor; Tampon applicators
    • A61F13/53—Absorbent pads, e.g. sanitary towels, swabs or tampons for external or internal application to the body; Supporting or fastening means therefor; Tampon applicators characterised by the absorbing medium
    • A61F2013/530481—Absorbent pads, e.g. sanitary towels, swabs or tampons for external or internal application to the body; Supporting or fastening means therefor; Tampon applicators characterised by the absorbing medium having superabsorbent materials, i.e. highly absorbent polymer gel materials
    • A61F2013/530569—Absorbent pads, e.g. sanitary towels, swabs or tampons for external or internal application to the body; Supporting or fastening means therefor; Tampon applicators characterised by the absorbing medium having superabsorbent materials, i.e. highly absorbent polymer gel materials characterized by the particle size
    • A—HUMAN NECESSITIES
    • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
    • A61F—FILTERS IMPLANTABLE INTO BLOOD VESSELS; PROSTHESES; DEVICES PROVIDING PATENCY TO, OR PREVENTING COLLAPSING OF, TUBULAR STRUCTURES OF THE BODY, e.g. STENTS; ORTHOPAEDIC, NURSING OR CONTRACEPTIVE DEVICES; FOMENTATION; TREATMENT OR PROTECTION OF EYES OR EARS; BANDAGES, DRESSINGS OR ABSORBENT PADS; FIRST-AID KITS
    • A61F13/00—Bandages or dressings; Absorbent pads
    • A61F13/15—Absorbent pads, e.g. sanitary towels, swabs or tampons for external or internal application to the body; Supporting or fastening means therefor; Tampon applicators
    • A61F13/53—Absorbent pads, e.g. sanitary towels, swabs or tampons for external or internal application to the body; Supporting or fastening means therefor; Tampon applicators characterised by the absorbing medium
    • A61F2013/530481—Absorbent pads, e.g. sanitary towels, swabs or tampons for external or internal application to the body; Supporting or fastening means therefor; Tampon applicators characterised by the absorbing medium having superabsorbent materials, i.e. highly absorbent polymer gel materials
    • A61F2013/530583—Absorbent pads, e.g. sanitary towels, swabs or tampons for external or internal application to the body; Supporting or fastening means therefor; Tampon applicators characterised by the absorbing medium having superabsorbent materials, i.e. highly absorbent polymer gel materials characterized by the form
    • A—HUMAN NECESSITIES
    • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
    • A61F—FILTERS IMPLANTABLE INTO BLOOD VESSELS; PROSTHESES; DEVICES PROVIDING PATENCY TO, OR PREVENTING COLLAPSING OF, TUBULAR STRUCTURES OF THE BODY, e.g. STENTS; ORTHOPAEDIC, NURSING OR CONTRACEPTIVE DEVICES; FOMENTATION; TREATMENT OR PROTECTION OF EYES OR EARS; BANDAGES, DRESSINGS OR ABSORBENT PADS; FIRST-AID KITS
    • A61F13/00—Bandages or dressings; Absorbent pads
    • A61F13/15—Absorbent pads, e.g. sanitary towels, swabs or tampons for external or internal application to the body; Supporting or fastening means therefor; Tampon applicators
    • A61F13/53—Absorbent pads, e.g. sanitary towels, swabs or tampons for external or internal application to the body; Supporting or fastening means therefor; Tampon applicators characterised by the absorbing medium
    • A61F2013/530481—Absorbent pads, e.g. sanitary towels, swabs or tampons for external or internal application to the body; Supporting or fastening means therefor; Tampon applicators characterised by the absorbing medium having superabsorbent materials, i.e. highly absorbent polymer gel materials
    • A61F2013/530583—Absorbent pads, e.g. sanitary towels, swabs or tampons for external or internal application to the body; Supporting or fastening means therefor; Tampon applicators characterised by the absorbing medium having superabsorbent materials, i.e. highly absorbent polymer gel materials characterized by the form
    • A61F2013/530613—Absorbent pads, e.g. sanitary towels, swabs or tampons for external or internal application to the body; Supporting or fastening means therefor; Tampon applicators characterised by the absorbing medium having superabsorbent materials, i.e. highly absorbent polymer gel materials characterized by the form in fibres
    • D—TEXTILES; PAPER
    • D06—TREATMENT OF TEXTILES OR THE LIKE; LAUNDERING; FLEXIBLE MATERIALS NOT OTHERWISE PROVIDED FOR
    • D06M—TREATMENT, NOT PROVIDED FOR ELSEWHERE IN CLASS D06, OF FIBRES, THREADS, YARNS, FABRICS, FEATHERS OR FIBROUS GOODS MADE FROM SUCH MATERIALS
    • D06M2200/00—Functionality of the treatment composition and/or properties imparted to the textile material
    • D—TEXTILES; PAPER
    • D06—TREATMENT OF TEXTILES OR THE LIKE; LAUNDERING; FLEXIBLE MATERIALS NOT OTHERWISE PROVIDED FOR
    • D06M—TREATMENT, NOT PROVIDED FOR ELSEWHERE IN CLASS D06, OF FIBRES, THREADS, YARNS, FABRICS, FEATHERS OR FIBROUS GOODS MADE FROM SUCH MATERIALS
    • D06M2400/00—Specific information on the treatment or the process itself not provided in D06M23/00-D06M23/18
    • D06M2400/01—Creating covalent bondings between the treating agent and the fibre
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10S—TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10S428/00—Stock material or miscellaneous articles
    • Y10S428/913—Material designed to be responsive to temperature, light, moisture
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/29—Coated or structually defined flake, particle, cell, strand, strand portion, rod, filament, macroscopic fiber or mass thereof
    • Y10T428/2913—Rod, strand, filament or fiber
    • Y10T428/2933—Coated or with bond, impregnation or core
    • Y10T428/2938—Coating on discrete and individual rods, strands or filaments
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/29—Coated or structually defined flake, particle, cell, strand, strand portion, rod, filament, macroscopic fiber or mass thereof
    • Y10T428/2913—Rod, strand, filament or fiber
    • Y10T428/2933—Coated or with bond, impregnation or core
    • Y10T428/2964—Artificial fiber or filament
    • Y10T428/2965—Cellulosic
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/29—Coated or structually defined flake, particle, cell, strand, strand portion, rod, filament, macroscopic fiber or mass thereof
    • Y10T428/2982—Particulate matter [e.g., sphere, flake, etc.]
    • Y10T428/2991—Coated
    • Y10T428/2998—Coated including synthetic resin or polymer
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/31504—Composite [nonstructural laminate]
    • Y10T428/31536—Including interfacial reaction product of adjacent layers
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T442/00—Fabric [woven, knitted, or nonwoven textile or cloth, etc.]
    • Y10T442/20—Coated or impregnated woven, knit, or nonwoven fabric which is not [a] associated with another preformed layer or fiber layer or, [b] with respect to woven and knit, characterized, respectively, by a particular or differential weave or knit, wherein the coating or impregnation is neither a foamed material nor a free metal or alloy layer
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T442/00—Fabric [woven, knitted, or nonwoven textile or cloth, etc.]
    • Y10T442/20—Coated or impregnated woven, knit, or nonwoven fabric which is not [a] associated with another preformed layer or fiber layer or, [b] with respect to woven and knit, characterized, respectively, by a particular or differential weave or knit, wherein the coating or impregnation is neither a foamed material nor a free metal or alloy layer
    • Y10T442/2041—Two or more non-extruded coatings or impregnations
    • Y10T442/2049—Each major face of the fabric has at least one coating or impregnation
    • Y10T442/209—At least one coating or impregnation contains particulate material
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T442/00—Fabric [woven, knitted, or nonwoven textile or cloth, etc.]
    • Y10T442/60—Nonwoven fabric [i.e., nonwoven strand or fiber material]
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T442/00—Fabric [woven, knitted, or nonwoven textile or cloth, etc.]
    • Y10T442/60—Nonwoven fabric [i.e., nonwoven strand or fiber material]
    • Y10T442/699—Including particulate material other than strand or fiber material

Definitions

  • PA TICLE BINDERS FIELD OF THE INVENTION This invention concerns polymeric and non- polymeric binders for fibers and the use of such binders in binding particles to fibers.
  • the fibers and bound particles may be easily densified by external application of pressure.
  • the binders are reactivatable, and may be applied to fibers on a wet-laid fiber sheet manufacturing line.
  • the invention concerns binding superabsorbent particles to cellulosic fibers which may then be used, for example, to make absorbent fibers that are densified and incorporated into absorbent products.
  • the invention concerns the activation and use of such fibers, preferably at an article manufacturing plant, at a location remote from a pulp sheet manufacturing line to bind superabsorbent and/or other particles to cellulosic fibers which may then be used, for example, as absorbent fibers incorporated into absorbent products.
  • Superabsorbent polymers have been developed in recent years that are capable of absorbing many times their own weight of liquid. These polymers, which are also known as water insoluble hydrogels, have been used to increase the absorbency of sanitary products such as diapers and sanitary napkins.
  • Superabsorbent polymers are often provided in the form of particulate powders, granules, or fibers that are distributed throughout absorbent cellulosic products to increase the absorbency of the product.
  • Superabsorbent particles are described, for example, in U.S. Patent No. 4,160,059; U.S. Patent No. 4,676,784; U.S. Patent No. 4,673,402; U.S. Patent No.
  • the polyaluminum binder suffers from the drawback of being an inorganic product that is not readily biodegradable. Moreover, that European patent does not offer any guidance for selecting binders other than polyaluminum chloride that would be useful in binding absorbent particles.
  • a method of immobilizing superabsorbents is disclosed in U.S. Patent No. 4,410,571 in which a water swellable absorbent polymer is converted to a non- particulate immobilized confluent layer.
  • Polymer particles are converted to a coated film by plasticizing them in a polyhydroxy organic compound such as glycerol, ethylene glycol, or propylene glycol.
  • the superabsorbent assumes a non-particulate immobilized form that can be foamed onto a substrate.
  • the individual particulate identity of the superabsorbent polymer is lost in this process.
  • the confluent nature of the superabsorbent material can also result in gel blocking, in which absorption is diminished as the water swollen polymers block liquid passage through the film layer.
  • U.S. Patent No. 4,412,036 and U.S. Patent No. 4,467,012 disclose absorbent laminates in which a hydrolyzed starch polyacrylonitrile graft copolymer and glycerol mixture is laminated between two tissue layers.
  • the tissue layers are laminated to each other by applying external heat and pressure.
  • the reaction conditions form covalent bonds between the tissue layers that firmly adhere the tissue layers to one another.
  • binders Numerous other patents have described methods of applying binders to fibrous webs. Examples include U.S. Patent No. 2,757,150; U.S. Patent No. 4,584,357; and U.S. Patent No. 4,600,462. Such binders are not described as being useful in binding particulates, such as superabsorbent particles, to fibers. Yet other patents disclose crosslinking agents such as polycarboxylic acids that form covalent intrafiber bonds with individualized cellulose fibers, as in European Patent Application 440 472 Al; European Patent Application 427 317 A2; European Patent Application 427 316 A2; and European Patent Application 429 112 A2.
  • the covalent intrafiber bonds are formed at elevated temperatures and increase the bulk of cellulose fibers treated with the crosslinker by forming intrafiber ester crosslinks. Crosslinking must occur under acidic conditions to prevent reversion of the ester bonds.
  • the covalent bonds within the fibers produce a pulp sheet that is more difficult to compress to conventional pulp sheet densities than in an untreated sheet. Covalent crosslink bonds may also form between the fibers and particles, and occupy functional groups that would otherwise be available for absorption, hence absorption efficiency is decreased.
  • a particular disadvantage of forming covalent ester intrafiber crosslinks is that the resulting fiber product resists densification. Energy requirements for making densified absorbent products are increased because very high compression pressures must be used to densify the absorbent product. It would be advantageous to provide a method of enhancing densification of crosslinked fibers by reducing energy requirements for densification.
  • particles other than superabsorbents may be added to fibers for different end uses.
  • Antimicrobials, zeolites and fire retardants are but a few examples of particles that are added to fibers. It would be advantageous to provide a method of attaching particles that could be accommodated to the many different particle needs of end users. Moreover, it would be advantageous to reduce particulate waste in the attachment process, and simplify shipment of fiber products that require particulate addition. It would be further advantageous to bind particulates to fibers without requiring the shipment of bulk fibers with adhered particulates because shipping and excessive handling of these fibers subject them to mechanical impact which can dislodge some particles from the fibers. It would also be advantageous to incorporate binders onto fibers during the initial pulp sheet manufacturing process so that the fibers are ready for activation and use at a remote product manufacturing location.
  • the foregoing and other problems have been overcome by providing fibers with hydrogen bonding functional sites, and binders that have a volatility less than water.
  • the binder has a functional group that is capable of forming a hydrogen bond with the fibers, and a functional group that is also capable of forming a hydrogen bond or a coordinate covalent bond with particles that have a hydrogen bonding or coordinate covalent bonding functionality.
  • the fibers of the present invention may have particles bound to the fibers with a polymeric or non- polymeric binder.
  • the binders comprise binder molecules.
  • the polymeric binder may be selected from the group consisting of polyglycols [especially poly(propyleneglycol) ] , a polycarboxylic acid, a polycarboxylate, a poly(lactone) polyol, such as diols, a polyamide, a polyamine, a polysulfonic acid, a polysulfonate and combinations thereof.
  • polyglycols may include polypropylene glycol (PPG) and polyethylene glycol (PEG) ; poly(lactone) diols include poly(caprolactone) diol;, polycarboxylic acid include polyacrylic acid (PAA) ; polyamides include polyacrylamide or polypeptides; polyamines include polyethylenimine and polyvinylpyridine; polysulfonic acids or polysulfonates include poly(sodium-4-styrenesulfonate) or poly(2- acrylamido-methyl-1-propanesulfonic acid) ; and copolymers thereof (for example a polypropylene glycol/polyethylene glycol copolymer) .
  • the polymeric binder typically has repeating units.
  • the repeating unit may be the backbone of a compound, such as with a polypeptide, wherein the repeating polyamides occur in the peptide chain.
  • the repeating unit also may refer to units other than backbones, for instance a repeating acrylic acid unit. In such a case, the repeating units may be the same or different.
  • the binder molecules have at least one functional group capable of forming a hydrogen bond or a coordinate covalent bond with particles, and at least one functional group capable of forming a hydrogen bond with the fibers.
  • the most preferred polymeric binder is polyethylene glycol although another especially preferred polymeric binder is an amide binder such as a polypeptide binder with polyglycine being a specifically preferred example.
  • the non-polymeric binder has a volatility less than water.
  • the non-polymeric binder molecules have at least one functional group that is capable of forming a hydrogen bond or coordinate covalent bond with the particles, and at least one functional group that is capable of forming hydrogen bonds with the cellulose fibers.
  • the non-polymeric binder is an organic binder, and preferably includes a functional group selected from the group consisting of a carboxy1 (for example, carboxylic acids) , a carboxylate, a carbonyl (for example, aldehydes) , a sulfonic acid, a sulfonate, a phosphoric acid, a phosphate, a hydroxy1 (for example, an alcohol or polyol) , an amide, amine, and combinations thereof (for example, amino acid or hydroxy acid) , wherein there are at least two functionalities on the molecule selected from this group, and the two functionalities are the same or different.
  • a functional group selected from the group consisting of a carboxy1 (for example, carboxylic acids) , a carboxylate, a carbonyl (for example, aldehydes) , a sulfonic acid, a sulfonate, a phosphoric acid, a phosphate, a
  • binders examples include polyols, polyamines (a non- polymeric organic binder with more than one amine group) , polyamides (a non-polymeric organic binder with more than one amide group) , polycarboxylic acids (a non- polymeric organic binder with more than one carboxylic acid functionality) , polyaldehydes (a non-polymeric organic binder with more than one aldehyde) , amino alcohols, hydroxy acids. These binders have functional groups that are capable of forming the specified bonds with the particles and fibers.
  • the organic non-polymeric binder is selected from the group consisting of glycerin, a glycerin monoester, a glycerin diester, glyoxal, ascorbic acid, urea, glycine, pentaerythritol, a monosaccharide or a disaccharide, citric acid, tartaric acid, taurine (2-aminoethanesulfonic acid) , p-aminosalicylic acid, dipropylene glycol, and urea derivatives, such as DMDHEU, and combinations thereof.
  • Suitable saccharides include glucose, sucrose, lactose, ribose, fructose, mannose, arabinose, and erythrose.
  • the preferred binders a. - non-polymeric molecules with a plurality of hydrogen bonding functionalities that permit the binder to form hydrogen bonds to both the fibers and particles.
  • Particularly preferred binders include those that can form five or six membered rings, most preferably six membered rings, with a functional group on the particle surface.
  • glycerin glycerin, glycerin monoesters, including monoglycerides, a glycerin diester, including diglycerides, polyglycerin oligomers, a propylene glycol oligomer, urea and combinations thereof (such as glycerin and urea) .
  • an oligomer refers to a condensation product of polyols, wherein the condensation product contains less than ten monomer units.
  • a polyglycerin oligomer as referred to herein means a condensation product of two or more glycerin molecules.
  • a propylene glycol oligomer as referred to herein means a condensation product of two or more propylene glycol molecules.
  • a specifically preferred non- polymeric binder is glycerin.
  • the fibrous material may be cellulosic or synthetic fibers that are capable of forming hydrogen bonds with the binder, while the particles are selected to be of the type that are capable of forming hydrogen bonds or coordinate covalent bonds with the binder. It has unexpectedly been found that this binder system secures particles to fibers exceptionally well. A superior fibrous product is therefore produced that has improved absorbent properties as compared to unbound or covalently bound particles. Formation of the noncovalent bond allows production of a fiber product that is easily manufactured and a web that is easily densified, and that is readily biodegradable and disposable.
  • an absorbent product comprises a fibrous cellulosic mat that contains superabsorbent hydrogel particles in particulate form.
  • the superabsorbent particles are capable of forming hydrogen bonds or coordinate covalent bonds with the binder, depending upon the binder, while the binder in turn forms hydrogen bonds with the hydroxy1 groups of the cellulose fibers.
  • These noncovalent, relatively flexible bonds between the binder and particles maintain the particles in contact with the fibers, and resist dislodgement of the particles by mechanical forces applied to the mat during manufacture, storage or use.
  • the amount of binder present typically depends on a number of factors, including the nature of the binder and particles, and whether the particles are immediately added to the fibers or after a period of time.
  • the binder may suitably be present in an amount of from about l to 80 percent of the total weight of the fibrous material.
  • An especially suitable range of binder is l to 40 percent by weight, or 1 to 25 percent by weight of the fibrous material.
  • the particles bound by the binder of the present invention may suitably be present in an amount of .05 to 80 percent, preferably 1 to 80 percent or 3 to 80 percent, or more than 3 percent by weight of the total weight of the fibrous material and the particles.
  • a particularly suitable range of particles is 3 to 40 percent by weight of the fibrous material and particles.
  • a preferred weight ratio of particle to binder is 8:1 to 50:1.
  • An example of a suitable particle is a superabsorbent polymer such as a starch graft polyacrylate hydrogel fine or larger size particle such as a granule, which forms hydrogen bonds with the binder.
  • the binder also forms hydrogen bonds with the hydroxyl groups of the cellulose, thereby securely attaching the superabsorbent particles to the fibers.
  • the present invention also includes a method of binding particles to fibers wherein the particles are substantially insoluble in the binder (and soluble in water) and therefore retain their solid particulate form following binding.
  • the particles whether or not water soluble, preferably have functional groups that can form hydrogen bonds or coordinate covalent bonds with the binder, and the binder in turn is capable of forming hydrogen bonds to the fibers.
  • Other particles without the desired functionality also may be included in the fiber product, but such particles will not be bound as strongly in the same manner.
  • the fibers are cellulosic and the particles are superabsorbent particles that are bound to the binder by hydrogen bonds.
  • the fibers may also be continuous or discontinuous synthetic or natural fibers having a hydrogen bonding functional group that hydrogen bonds with the binder.
  • the binder is suitably applied to the fibers in an amount of at least 1 percent, and preferably no more than 80 percent, by total weight of the fibrous material.
  • the particles may be bound to the fibers at less than 150° C or without any external application of heat at ambient temperature (e.g., about 25° C) . Particles may also be bound in the absence of any external application of pressure, or in the absence of external heat and pressure.
  • the binder is associated with the fibers as a solid (for example, a dry powder or a dried liquid) , and the fibers contain at least 7 percent water by weight when the binding step is performed. This level of moisture in the fibers provides sufficient mobility of reactants to allow the particles and fibers to bind well to each other.
  • a liquid binder for example, glycerin or a solution of glycine powder
  • the fibers suitably contain at least about 0.5 percent water by weight.
  • a solid binder is suitably used with fibers having less than 0.5 percent water by weight if the binder is heated above its melting point to liquefy it.
  • the solid can be applied to the fibers as a supersaturated solution or the solid binder may be heated above its melting point to liquefy the binder, which is later applied to the fibers. Upon solidifying the binder is deactivated.
  • a solid binder may be thermoplastic or meltable, such that it can be heated above its melting point/or softening point and then cooled to fuse fibers to each other.
  • the thermoplastic properties of the binder can also provide additional mechanical adherence between the particles and fibers.
  • a thermoplastic binder such as urea may be employed which can adhere particles both thermoplastically and with hydrogen bonding.
  • the particles are soluble in water but have reduced solubility in the binder such that the particles can be bound in solid particulate form to the fibers.
  • Addition of the binder does not dissolve the particle and cause it to diffuse away from its desired site of attachment to the fibers.
  • the binder attaches the particles to the fibers, and forms a bond that has been found to be resistant to mechanical disruption.
  • a significant advantage of these binders is that the binder and particle together on the fiber have been found to reduce the pressure required to densify the fibers.
  • the binders can also be present on fibers in an inactive state for more than a week, a month, or a even a year, then later activated or reactivated to bind particles to the fibers.
  • Liquid binders (which includes neat liquids or aqueous solutions of solid binders) can be placed on the fibers, dried, and later activated by moistening the fibers.
  • a dry solid binder may be added to the fibers and later activated by addition of a liquid.
  • An inactive binder can also be activated by applying kinetic energy to the fibers after the binder and fibers reach an equilibrium moisture content with the atmosphere (hereinafter referred to as "air dry”) .
  • Kinetic energy can be applied to the binder and fibers, for example and without limitation, by applying mechanical agitation, pressure from an external source, or using ultrasonics.
  • the binder may be activated or reactivated by heating the fibers after applying the binder to the fibers.
  • the capacity for activation or reactivation allows the binder to be applied to the fibers, which are then shipped to distribution points with the binder in an inactive form.
  • the binder is then activated at the distribution point (for example, a customer's facility) where particles are added to the fibers and bound thereto.
  • binder "activation" includes both activation of previously inactive binders (such as solid binders in the absence of liquid) or activation of previously active binders (such as a liquid binder that has been dried) .
  • an activation fluid such as an activation liquid
  • an activation liquid can be applied to the areas of a diaper that will be initially moistened by urine during use.
  • a suitable activation liquid include water, lower-alky1 alcohols, polyols such as the glycols, acetone, and combinations thereof, such as water and glycerin.
  • the activating fluid is a liquid such as water
  • the water may be sprayed or otherwise applied and may be provided in the form of steam or moisture-laden gas, such as humid air.
  • Other liquid activation fluids may be applied in the same manner.
  • Superabsorbent particles can be added to activated areas of the diaper and adhered almost exclusively in those areas where initial urine absorption is required. Targeted activation of binder allows particles to be efficiently and economically attached to the fibers, with reduced particle wastage. Moreover, targeted binder activation and particle adherence increases the absorptive efficiency of the product by diminishing excessive wicking of liquid within the plane of an absorptive product.
  • the invention also is directed to fibrous products produced by any of the methods described herein, and to absorbent articles comprised of such fibrous products.
  • fibrous products include fibers with inactive or activatable binders.
  • a fibrous product may be individual fibers or webs made thereof.
  • FIG. 1 is a schematic illustration of a wet laid sheet manufacturing line illustrating the application of binders in accordance with the present invention during the manufacture of a fiber sheet.
  • FIG. 2 is a schematic illustration of a binder activation and particulate attachment process in accordance with the present invention.
  • FIG. 3 is a schematic depiction of the components of an apparatus of the present invention that produce high bulk fibers.
  • FIG. 4 is a top plan view of a structure into which fibers of the present invention are incorporated with attached particles, the fibers being in the form of an illustrated absorbent pad.
  • FIG. 5 represents a partial sectional view of the pad of FIG. 4.
  • FIG. 6 illustrates a plan view of a bandage incorporating fibers of the present invention.
  • FIG. 7 is a sectional view of the bandage of
  • FIG. 8 is a plan view of a disposable diaper including a core of fibers of the present invention.
  • FIG. 9 is a vertical sectional view along line 9-9 of the diaper of FIG. 8.
  • FIG. 10 is a view of an enlarged fiber with particles bonded to the fiber with the binders of the present invention.
  • FIG. 11 is a schematic view of a cellulose mat with particles bound to all its surfaces and throughout its depth.
  • FIG. 12 is a photomicrograph of particles adhered to fibers with an ascorbic acid binder.
  • FIGS. 13A, 13B, 13C, and 13D are photomicrographs of particles bound to fibers with lactose.
  • FIG. 14 is a photomicrograph of oxalic acid particles bound to a fiber with a glycerin binder.
  • FIG. 15 is a photomicrograph of aluminum sulfate (alum) bound to a fiber with a glycerin binder.
  • FIG. 16 is a photomicrograph of EDTA (ethylenediaminetetraacetic acid) particles bound to a crosslinked fiber with a glycerin binder.
  • EDTA ethylenediaminetetraacetic acid
  • FIG. 1A illustrates a wet laid sheet manufacturing line such as a pulp sheet manufacturing line 10.
  • a pulp slurry 12 is delivered from a headbox 14 through a slice 16 and onto a Fourdrinier wire 18.
  • the pulp slurry 12 typically includes cellulose fibers such as wood pulp fibers and may also include synthetic or other non- cellulose fibers as part of the slurry.
  • drying section 30 may include multiple canister dryers with the pulp mat 20 following a serpentine path around the respective canister dryers and emerging as a dried sheet or mat 32 from the outlet of the drying section 30.
  • Other alternate drying mechanisms alone or in addition to canister dryers, may be included in the drying stage 30.
  • the dried pulp sheet 32 has a maximum moisture content pursuant to the manufacturer's specifications. Typically, the maximum moisture content is no more than 10% by weight of the fibers and most preferably no more than about 6% to 8% by weight. Otherwise, the fibers tend to be too damp. Unless overly damp fibers are immediately used, these fibers are subject to degradation by, for example, mold or the like.
  • the dried sheet 32 is taken up on a roll 40 for transportation to a remote location, that is, one separate from the pulp sheet manufacturing line, such as at a user's plant for use in manufacturing products. Alternatively, the dried sheet 32 is collected in a baling apparatus 42 from which bales of the pulp 44 are obtained for transport to a remote location.
  • a binder of the type explained in detail below is applied to the pulp sheet from one or more binder applying devices, one of which is indicated at 50 in
  • any binder applying device may be used, such as sprayers, roll coaters, immersion applicators or the like. Sprayers are typically easier to utilize and incorporate into a pulp sheet manufacturing line. As indicated by the arrows 52, 54 and 56, the binder may be applied at various locations or at multiple locations on the pulp sheet manufacturing line, such as ahead of the drying stage 30 (indicated by line 52) , intermediate the drying stage 30 (as indicated by line 54) , or downstream from the drying stage 30 (as indicated by the line 56) . Water-based binders, such as non-polymeric urea, are typically applied at a location where sufficient drying can still take place in the drying stage to produce a dried binder containing fiber sheet with no more than the maximum desired moisture content.
  • water-based binders are typically applied at locations 52 or 54. At location 52, the water remaining in the sheet or mat 20 at this stage tends to interfere with the penetration of the binder into the sheet. Consequently, application of the binder after some drying has taken place, for example at location 54, is preferable. If water-based binders are applied at location 56 in an amount which would cause the moisture content of the sheet to exceed the desired maximum level, an additional drying stage (not shown) may be included in the pulp manufacturing line to bring the moisture content down to the desired level.
  • a non-aqueous based binder such as glycerin, is most preferably added downstream from the drying stage at location 56 or during the drying stage as indicated by location 54.
  • liquid non-aqueous binders may also be added at a location, such as location 52, upstream of the drying stage. At this latter location, the water in the wet web at this point may tend to attract these binders into the mat or sheet as the binders tend to be hydroscopic. Since non-aqueous binders typically do not enhance the degradation of the product due to the addition of moisture to the sheet, they can be applied downstream from the drying stage without bringing the moisture content of the sheet above the desired maximum level.
  • the particulate materials may be added to the sheet and adhered thereto by the binders on the pulp manufacturing line, such as indicated by the particulate applicator 60, which may comprise a bulk or volumetric metering device. These particles may be sprinkled, poured or otherwise added to the sheet. To facilitate the adherence of these particulates to the sheet at this location, enough moisture must remain in the sheet, in the case of aqueous binders, to enable the bonding between the particles and fibers as explained below.
  • the particles in this case are preferably added while the binder is still wet or heated to facilitate the reaction.
  • Particles can be added on the pulp sheet manufacturing line in this manner, with a subsequent drying stage being utilized to reduce the moisture content following particulate addition.
  • a water-based binder makes the fibers too wet following the addition of the particles, this is not the preferred approach.
  • Particles with a relatively short shelf life such as certain zeolites (e.g. Abscents with odor absorbing materials which can become saturated with odors over time) being one example, may also degrade over time.
  • zeolites with silver salts as antimicrobial agents which can photodegrade. Therefore, it is also advantageous to provide a fibrous product in which the end user of the product may incorporate the desired particles at the time the fibers are converted into products. Therefore, in keeping with this latter preferred approach, as illustrated in FIG. 2, the respective rolls 40 or bales 44 of binder-containing fibers, without particles, are transported to a remote location for use by a user.
  • a typical fiberizing apparatus 70 is a hammermill which may be used alone or in conjunction with other devices such as picker rolls or the like for breaking up the sheet 32 or bales 42 into individual fibers.
  • a particulate material adding mechanism 72 (e.g., like mechanism 60) delivers the desired particulate materials to the fibers at the desired location in the user's process.
  • the device 72 typically comprises a metering mechanism, although any suitable device for adding particulates to fibrous materials may be used.
  • the particulates may be delivered as indicated by line 74 to the fiberizing apparatus 70.
  • agitation of fibers within the fiberizer 70 activates the binders and causes the particulates to be adhered to the fibers by the binder.
  • an activating fluid which may be a liquid such as water, glycerin, lower- alkyl alcohols, polyols such as the glycols, acetone, and combinations thereof such as water and glycerin
  • an activating fluid may be sprayed or otherwise applied to the fibers, such as from an activation fluid tank or source 78 by way of a sprayer (not shown) at location 80.
  • the particles may then be applied, as indicated by line 84 to the fibers downstream from the application of the activation liquid 80.
  • the particles which may be added prior to or at location 80 are adhered to the fibers by the binder upon activation of the binder at location 80.
  • the fiberized fibers are delivered to an air-laying device 90 and reformed into a desired product such as a web indicated at 92.
  • the activation fluid or liquid may be applied to the web at location 96 with the particles then being added at location 98 as shown with the activated binder then adhering the particles to the fibers.
  • the particles may be applied at a location in the process upstream from the application of the activating liquid at location 96.
  • the activating fluid may be added simultaneously with the addition of particles, so that the activation occurs simultaneously with the addition of particles.
  • the activating fluid also may be added after the particles are added to the fibers.
  • the binder may be activated at specifically defined locations on the web 92, such as in target zones of an absorbent core of a product with the particles then only being applied to these target zones, thereby minimizing the wasting of the particulate material.
  • a specific example of a target zone is the crotch region of a diaper where most diaper wetting would occur.
  • the application of superabsorbent particles to such a zone places these particles at a location where they are most useful in absorbing liquid.
  • the web 92, with or without other components of the end user's product, is then processed into the user's product, such as being included within a disposable diaper 100.
  • the end user of the fibers may readily select particles to be applied to its product and may activate the binder as required to enhance the efficient production of the user's product.
  • the user has flexibility in air laying or otherwise combining the binder containing fibers into a finished product with the desired particulates.
  • the binder containing fibers because the binders are all water soluble, are preferably not wet laid because wet laying would remove at least some of the binder.
  • enhanced adhesion of particulates to the fibers results because the particles are not subjected to mechanical forces between the location of manufacture of the fibers and the location at which the particulate materials are added.
  • the present invention includes a method of binding particles to fibers, and the product, including absorbent end-products, that are produced by such method.
  • the product is a cellulosic or synthetic fiber to which superabsorbent hydrogel polymer particles are adhered by a binder, and absorbent products made therefrom.
  • Suitable fibers include wood pulp fibers, which can be obtained from well known chemical processes such as the kraft and sulfite processes.
  • the invention also includes a combination of wood pulp and certain binders, which for the purpose of this combination are bulk fibers in roll form having a basis weight of at least 350 grams per square meter (g/m 2 ) or bale form.
  • the bulk fibers can have a density of at least about 400 kg/m 3 .
  • Preferred bulk fibers are wood pulp fibers or softwood pulp fibers.
  • the pulp fibers may be chemical or thermomechanical or chemithermomechanical or combinations thereof.
  • the preferred pulp fiber is chemical. In these processes, the best starting material is prepared from long fiber coniferous wood species, such as pine, douglas fir, spruce and hemlock.
  • Wood pulp fibers can also be obtained from mechanical processes, such as ground wood, mechanical, thermomechanical, chemimechanical, and chemithermomechanical pulp processes.
  • the fibers are preferably elongated, for example having a length to width ratio of about 10:1 to 5:1.
  • the fibers of the present invention also include fibers that are pretreated prior to the application of a binder to the fibers.
  • This pretreatment may include physical treatment, such as subjecting the fibers to steam or chemical treatment, such as cross-linking the fibers.
  • examples of pretreating fibers include the application of fire retardants to the fibers, such as by spraying the fibers with fire retardant chemicals.
  • Specific fire-retardant chemicals include, by way of example, sodium borate/boric acid, urea, urea/phosphates, etc.
  • the fibers may be pretreated with surfactants or other liquids, such as water or solvents, which modify the surface of the fibers.
  • Other pretreatments include exposure to antimicrobials or pigments.
  • the fibers also may be pretreated in a way which increases their wetability.
  • the fibers also may be pretreated with conventional cross-linking materials and may be twisted or crimped, as desired.
  • Pretreating cellulose fibers with chemicals which result in lignin or cellulose rich fiber surfaces also may be performed in a conventional manner. Bleaching processes, such as chlorine or ozone/oxygen bleaching may also be used in pretreating the fibers.
  • the fibers may be pretreated, as by slurrying the fibers in baths containing various solutions. For example, antimicrobial solutions (such as solutions of antimicrobial particles as set forth below) , as well as solutions of fertilizers and pesticides, and/or fragrances and flavors, for release over time during the life of the fibers. Fibers pretreated with other chemicals, such as thermoplastic and thermoset resins also may be used. Combinations of pretreatments also may be employed with the resulting pretreated fibers then being subjected to the application of the binder coating as explained below.
  • Ground wood fibers recycled or secondary wood- pulp fibers, and bleached and unbleached wood-pulp fibers can be used. Details of the production of wood pulp fibers are well known to those skilled in the art. These fibers are commercially available from a number of companies, including Weyerhaeuser Company, the assignee of the present invention.
  • the fibers also can be any of a variety of other natural or synthetic fibers; however, all of the fibers to which particles are attached in accordance with the present invention include a hydrogen-bonding functionality. This does not preclude the blending of such fibers with fibers lacking this characteristic. However, the fibers lacking a hydrogen bonding functionality will not have particles bonded thereto with the strength and manner of the bonds that would be present if the fibers had a hydrogen-bonding functionality.
  • a hydrogen bond is an intermolecular force that occurs between hydrogen atoms that are covalently bonded to small, strongly electronegative elements (such as nitrogen and oxygen) and nonbonding electron pairs on other such electronegative elements.
  • a hydrogen bonding functionality is a functional group that contains an oxygen or nitrogen atom, for example hydroxyls, carboxyls, sulfonic acids, sulfonamides, ethers, esters, epoxides, carbonyls, amines, urethanes and others, that is capable of forming a hydrogen bond.
  • the orbital ⁇ of the nonbonding electron pairs on the oxygen or nitrogen overlap with the relatively empty Is orbital of the hydrogen covalently bonded to another nitrogen or oxygen atom.
  • the Is orbital of the hydrogen is relatively empty due to the unequal sharing of the electrons in the covalent bond between it and the small electronegative atom (oxygen or nitrogen) to which it is bound.
  • natural fibers that contain a hydrogen bonding functionality include chopped silk fibers, wood pulp fibers, bagasse, hemp, jute, rice, wheat, bamboo, corn, sisal, cotton, flax, kenaf, peat moss, and mixtures thereof.
  • Suitable synthetic fibers with hydrogen bondi g functionalities include acrylic, polyester, carbox ⁇ lated polyolefins, rayon and nylon.
  • the hydrogen-bonding functionality is an ester in acrylic fibers and a carboxylic acid in carboxylated polyolefin fibers, an ester in polyester, an amide in nylon, and a hydroxyl in rayon.
  • Polyethylene and polypropylene would be unsuitable fibers for use in particle to fiber bonding in the manner of the present invention because they include only carbons and hydrogens without any other atoms, such as oxygens or nitrogens, that can participate in hydrogen bonds.
  • the fibers are individualized, for example by defiberization in a hammermill. Such individualized fibers are conventionally formed into a mat, and are commercially available, for example as NB 416 fibers from the Weyerhaeuser Company.
  • Another suitable cellulosic mat would include Rayfloc JLD from ITT Rayonier.
  • the cellulose fibers may be in the form of a cellulosic web or loose cellulose fibers.
  • particles are added to the fibers to give the fibers desired properties, such as, by way of example only, increased absorbency, abrasiveness, or antimicrobial activity.
  • the particle can be any particulate material that has the desired property and which is capable of forming hydrogen bonds or coordinate covalent bonds with the binder. Hydrogen bonds can be formed, as discussed above, by particles that contain certain functional groups, particularly those having an oxygen or nitrogen. Coordinate covalent bonds, in contrast, are formed by donation of a lone pair of electrons on one atom to an empty orbital of another atom.
  • Coordinate covalent bonds differ from covalent bonds in that covalent bonds are formed by a pair of electrons wherein one of the electrons is donated from each of the atoms that participate in the bond. Particles can form coordinate covalent bonds if they have an empty p or d or f orbital that is capable of accepting a pair of electrons from the binder.
  • a coordinate covalent bond occurs between a donor atom that has a lone pair of electrons to donate to the bond, and an acceptor atom that has an empty orbital to accept the lone pair of electrons from the donor.
  • electrons occupy the lobes of atomic orbitals one at a time with a maximum of two electrons (with opposite spins) per lobe.
  • the most basic orbital is the s orbital, which is available for bonding the elements in the first row of the periodic table.
  • electrons fill first the 2s orbital of Li and Be.
  • metals in periods less than three do not have sufficient affinity for electrons to participate in coordinate covalent bonding.
  • Group IIIB boron
  • the three p orbitals participate in coordinate covalent bonding and the lobes of the p orbitals begin to fill.
  • Boron has one electron in one of the 2p orbitals, thus leaving the other 2p orbitals empty and available for coordinate covalent bonding.
  • An example of a coordinate covalently bonded boron containing particle is boric acid, which is used as an astringent, antiseptic and fire retardant.
  • the boron atom of boric acid acts as an acceptor for a lone pair of electrons donated by an oxygen atom of polypropylene glycol (PPG) , thereby forming a coordinate covalent bond between a boric acid particle and a PPG binder.
  • PPG polypropylene glycol
  • boric acid shown below is not typical of the aqueous chemistry of boron, but rather is provided to illustrate the type of bonding that is believed to occur in a coordinate covalent bond.
  • the next element, carbon usually hybridizes to have one electron in the 2s orbital and the three remaining electrons are singly placed in the three p orbitals. This leaves no lobes empty for coordinate
  • Sodium and magnesium have empty d orbitals available for coordination. Examples of magnesium coordination compounds are common. Then aluminum, like boron, places one electron in one of the 3p lobes, and the two other 3p lobes are empty and available for coordinate covalent bonding. The same trends continue across the third row, but the third row elements also have available five 3d lobes so the potential for coordination bonding exists even though 3p orbitals are occupied in the third row. Hence, Al, P, S, and Cl are capable of accepting a pair of electrons from an electron-pair donor to form a coordinate covalent bond. An example of this is found in the bonding in PC1 5 , aluminum trihydrate, or phosphorous pentasulfide.
  • a phosphorous pentasulfide particle can be used to increase flammability of a product, while aluminum trihydrate is a fire retardant.
  • An example of a coordinate covalently bonded aluminum compound is aluminum trihydrate, which may participate in a coordinate covalent bond with a polypropylene glycol
  • the aluminum atom of aluminum trihydrate acts as an electron acceptor for an electron pair donated by an oxygen atom of the polypropylene glycol (PPG) binder.
  • PPG polypropylene glycol
  • the 4s orbital is filled first, then the 3d lobes begin to fill—one electron per lobe until all have added a single then a second electron to each lobe until all lobes are filled.
  • 4p and 4f orbitals also are available, hence many of the transition elements are capable of forming coordinate covalent bonds.
  • the elements that have empty orbitals that participate in coordinate covalent bonding include all those except the metals (which excludes hydrogen) in periods one and two, and C, N, O, F, Ne and He. These metals do not have sufficient affinity for electrons to participate in coordinate covalent bonding.
  • Especially preferred particles contain boron, aluminum, iron, rhodium, osmium, platinum, and palladium, and most particularly boron.
  • particles that are capable of coordinate covalent bonding are aluminum trihydrate, antimony oxide, arsenic disulfide, bismuth aluminate, bismuth iodide oxide, bismuth phosphate, bismuth subcarbonate, bismuth subgallate, cadmium salycilate, chromic carbonate, chromic hydroxide, chromic oxide, and chromic phosphate.
  • polyglycols such as PPG
  • polycarboxylic acids such as PAA
  • poly(lactone) diols such as poly(caprolactone) diol
  • polyamides such as polyamines, etc.
  • the added particles are superabsorbent particles, which comprise polymers that swell on exposure to water and form a hydrated gel (hydrogel) by absorbing large amounts of water.
  • superabsorbents are defined herein as materials that exhibit the ability to absorb large quantities of liquid, i.e., in excess of 10 to 15 parts of liquid per part thereof. These superabsorbent materials generally fall into three classes, namely starch graft copolymers, crosslinked carboxymethylcellulose derivatives and modified hydrophilic polyacrylates.
  • absorbent polymers examples include hydrolyzed starch-acrylonitrile graft copolymer, a neutralized starch-acrylic acid graft copolymer, a saponified acrylic acid ester-vinyl acetate copolymer, a hydrolyzed acrylonitrile copolymer or acrylamide copolymer, a modified cross-linked polyvinyl alcohol, a neutralized self-crosslinking polyacrylic acid, a crosslinked polyacrylate salt, carboxylated cellulose, and a neutralized crosslinked isobutylene- maleic anhydride copolymer.
  • Superabsorbent particles are available commercially, for example starch graft polyacrylate hydrogel fines (IM 1000F) from Hoechst-Celanese of Portsmouth, VA, or larger particles such as granules.
  • Other superabsorbent particles are marketed under the trademarks SANWET (supplied by Sanyo Kase.. Kogyo Kabushiki Kaisha) , SUMIKA GEL (supplied by Sumitomo Kagaku Kabushiki Kaisha and which is emulsion polymerized and spherical as opposed to solution polymerized ground particles) , FAVOR (supplied by Stockhausen of Greensboro, North Carolina) , and NORSOCRYL (supplied by Atochem) .
  • SANWET supplied by Sanyo Kase.. Kogyo Kabushiki Kaisha
  • SUMIKA GEL supplied by Sumitomo Kagaku Kabushiki Kaisha and which is emulsion polymerized and spherical as
  • the superabsorbent particles come in a variety of sizes and morphologies, for example IM 1000 and IM 1000F.
  • the 1000F is finer and will pass through a 200 mesh screen whereas IM 1000 has some particles that will not pass through a 60 mesh screen.
  • Another type of superabsorbent particle is IM 5600 (agglomerated fines) .
  • Superabsorbent particulate hydrophilic polymers also are described in detail in U.S. Patent No. 4,102,340. That patent discloses hydrocolloid absorbent materials such as cross-linked polyacrylamides.
  • Suitable water-insoluble particles include proteins, vitamins, zeolites and silica, each of which contains electronegative atoms, such as oxygen or nitrogen groups, or both.
  • An example of a suitable zeolite is Abscents odor absorber available from UOP of Tarrytown, New York.
  • An example of a suitable antimicrobial particle is chlorhexidine (N,N"-Bis(4- chlorophenyl)-3,12-diimino-2,4,11,13- tetraazatetradecanediimidamide) .
  • the list in Table I is by no means exhaustive as it can be readily determined for each type of particle whether it is capable of forming a hydrogen bond or a coordinate covalent bond. Many of the particles are non-absorbent, or not superabsorbent polymers.
  • the particles listed in Table I have chemical properties that make them suitable for binding to fibers with the binders of the present invention.
  • the listed particles are organic or inorganic compounds that have little or no water solubility, yet have the capacity to hydrogen bond.
  • Water solubility is preferably low, for example, less than 10 g dissolves completely in 300 ml of water at 25°C, more preferably less than about 1 g in 300 ml at 25°C. This low solubility allows the particles to remain solid, and the hydrogen-bonding capacity allows them to adhere to the fibers even in cases when an aqueous binder is used.
  • Once bound the particles substantially retain a discrete particulate form instead of dissolving or fusing. Hence, once bound more of the particles are discrete than fused.
  • Many water-soluble particles that are capable of forming hydrogen bonds or coordinate covalent bonds are suitable for use with the binders of the present invention. Some such water-soluble particles are listed in Table II with an indication of the function of the listed particles.
  • Table II The list in Table II is by no means exhaustive as it can be readily determined for each type of particle whether it is capable of forming a hydrogen bond or a coordinate covalent bond. All or most of the particles are non-absorbent, or not superabsorbent polymers. Solubility of the particle in water and the binder can be easily ascertained, for example in standard chemical reference materials.
  • the particles listed in Table II have chemical properties that make them suitable for binding to fibers with the binders of the present invention.
  • the listed particles are organic or inorganic compounds that are water soluble, yet have the capacity to hydrogen bond.
  • Water solubility is preferably high. By water soluble it is meant that more than about 10 g of the particles will dissolve in 300 ml of water at 25° C.
  • the range of solubilities can extend, for example, from a lower limit of 10 g in 300 ml of water at 25° C, to an upper limit in which the particle is miscible in all proportions with water at 25° C.
  • aqueous liquids such as urine
  • the hydrogen bonding capacity allows them to adhere to the fibers in the presence of binder but in the absence of aqueous liquid during use by an end user after the manufacturing process is completed.
  • the particles While bound, the particles substantially retain a discrete particulate form instead of dissolving or fusing, at least until they are exposed to an aqueous liquid. More of the particles are discrete rather than agglomerated while bound in the absence of an aqueous liquid. If the particles are exposed to fibers with binder in liquid form, for the particles to retain their particulate form, a binder is preferably selected so that the particles are sparingly soluble in the binder.
  • sparingly soluble it is meant that no more than about 5 g of particles dissolve in 300 ml of the binder at 25° C.
  • Particles may be soluble in the binder as long as a sufficiently small amount of binder is used so that an effective portion of the particles remain in particulate form.
  • the amount of particles added to the fibers can vary widely, for example from .05 to 80 percent of the total weight of the fibrous material and particles.
  • Antimicrobials such as chlorhexidine or other nonabsorbent particles, are effective in very low amounts, such as .05 to 10 percent.
  • Superabsorbent particles are preferably added in an amount of 3-70 percent, especially 20-40 percent by weight of the fibrous materials and particles.
  • the particles may be combined to include more than one type of particle, for example superabsorbent and nonsuperabsorbent particles, or two types of superabsorbent particles. When two types of particles are used, the total weight of the particles will not exceed 80 percent of the total weight of the fibrous material and particles.
  • the particles may be bound to the fibers by a polymeric binder, which may be water soluble, selected from a predetermined group of polymeric binders.
  • the polymeric binders comprise binder molecules, wherein the binder molecules have at least one hydrogen bonding functionality or coordinate covalent bond forming functionality.
  • the polymeric binder may comprise repeating units, wherein each repeating unit of the polymer preferably, but not necessarily, includes at least one hydrogen bonding functionality or coordinate covalent bond forming functionality.
  • the predetermined groups of polymeric binders include the group of binders consisting of polyglycols [especially poly(propyleneglycol) ] , a polycarboxyic acid, a polycarboxylate, a poly(lactone) polyol, such as diols, a polyamide, a polyamine, a polysulfonic acid, a polysulfonate, and combinations thereof.
  • polyglycols may include polypropylene glycol (PPG) ; poly(lactone) diols include poly(caprolactone) diol; polycarboxylic acid include polyacrylic acid (PAA) ; polyamides include polyacrylamide or polypeptides; polyamines include polyethylenimine and polyvinylpyridine; polysulfonic acids or polysulfonates include poly(sodium-4- styrenesulfonate) or poly(2-acrylamido-methyl-l- propanesulfonic acid; and copolymers thereof (for example a polypropylene glycol/polyethylene glycol copolymer) .
  • PPG polypropylene glycol
  • lactone diols include poly(caprolactone) diol
  • polycarboxylic acid include polyacrylic acid (PAA)
  • polyamides include polyacrylamide or polypeptides
  • polyamines include polyethylenimine and polyvinylpyridine
  • the polymeric binder typically has repeating units.
  • the repeating unit may be the backbone of a compound, such as with a polypeptide, wherein the repeating polyamides occur in the peptide chain.
  • the repeating unit also may refer to units other than backbones, for instance repeating acrylic-acid units. In such a case, the repeating units may be the same or different.
  • the binder molecule has a functional group capable of forming a hydrogen bond or a coordinate covalent bond with particles, and a functional group capable of forming a hydrogen bond with the fibers.
  • a polymer is a macromolecule formed by chemical union of 5 or more identical or different combining units (monomers) .
  • a polyamine is a polymer that contains amine functional groups and a polyamide is a polymer that contains amide functional groups.
  • Each of the binders has a hydrogen bonding or a coordinate covalent bonding functionality.
  • the functionality may be a hydroxyl, a carboxyl, a carboxylate, a sulfonic acid, a sulfonate, an amide, an ether, an amine or combinations thereof.
  • These binders are capable of forming hydrogen bonds because they have a functional group that contains an electronegative element, such as oxygen or a nitrogen.
  • the polyglycol has repeating ether units with hydroxyl groups at the terminal ends of the molecule.
  • the polycarboxylic acid such as polyacrylic acid
  • the polyamide (such as a polypeptide) or polyamine has a repeating NR group in which a hydrogen may be bound to an electronegative nitrogen that also leaves the hydrogen partially positively charged.
  • the hydrogen in both cases can then interact with an electronegative atom, particularly oxygen or nitrogen, on the particle or fiber to form a hydrogen bond that adheres the binder to the particle and fiber.
  • the electronegative oxygen or nitrogen of the binder also can form a hydrogen bond with hydrogen atoms in the particle or fiber that have positive dipoles induced by electronegative atoms, such as oxygens or nitrogens, to which the hydrogen is attached.
  • the polyamide also has a carbonyl group with an electronegative oxygen that can interact with hydrogen atoms in the particles or fibers.
  • the polymeric binders can enhance the hydrogen bonding (a) between the fibers and binder; and (b) in the case of particles with hydrogen bonding functionalities, between the binder and the particles.
  • the polymeric binder may form a coordinate covalent bond with the particles and a hydrogen bond to the fibers.
  • the oxygen or nitrogen on the binder has an unbound pair of electrons that can be donated to an empty orbital in the particle to form a coordinate covalent bond.
  • one free pair of electrons on the oxygen or nitrogen can be donated to the empty p orbital of a boron-containing particle to form a coordinate covalent bond that adheres the particle to the binder.
  • the fibers themselves contain functional groups that can form hydrogen bonds with the binder, and allow the binder to adhere to the fiber.
  • Cellulosic and synthetic fibers may contain hydroxyl, carboxyl, carbonyl, amine, amide, ether and ester groups that will hydrogen bond with the hydroxyl, carboxylic acid, amide or amine groups of the binder.
  • the polymeric binder will adhere the particle with a coordinate covalent bond and the fiber will adhere with a hydrogen bond.
  • the polymeric binder is bound to both the fibers and the particle by hydrogen bonds.
  • a polypropylene glycol binder for example, can be used to bind water-insoluble polyacrylate hydrogel particles to cellulosic fibers.
  • the hydroxyl and ether groups on the glycol binder participate in hydrogen-bonding interactions with the hydroxyl groups on the cellulose fibers and the carboxyl groups on the polyacrylate hydrogel, as shown below:
  • a polypropylene glycol (PPG) binder for example, can be used to bind a water-soluble particle to cellulosic fibers.
  • PPG polypropylene glycol
  • the hydroxyl and ether groups on the glycol binder participate in hydrogen bonding interactions with the hydroxyl groups on the cellulose fibers and appropriate functionalities on the water- soluble particle, as shown below:
  • the binder will adhere both the particle and fiber with hydrogen bonds.
  • the presence of a hydrogen- bonding functionality on each repeating unit of the polymeric binder has been found to increase the number of hydrogen bonding interactions per-unit-mass of polymer, which provides superior binding efficiency and diminishes separation of particles from the fibers.
  • the repeating ether functionality on the glycol binder provides this efficiency in the examples diagrammed above.
  • a repeating carboxyl group is the repeating functionality on polyacrylic acid, while repeating carbonyls and NR groups (wherein R is either an H or alkyl, preferably lower alkyl i.e., less than five carbon atoms, in a normal or iso configuration) of the amide linkages are the repeating functionalities on polyamides such as polypeptides.
  • a repeating amine group is present on polyamines.
  • the polymeric organic binders of the present invention have been found to increase in binding efficiency as the length of the polymer increases, at least within the ranges of molecular weights that are reported in the examples below. This increase in binding efficiency is attributable to the increased number of hydrogen bonding or coordinate covalent bonding groups on the polymer with increasing molecular length.
  • Each of the polymeric binders has a hydrogen bonding or coordinate covalent bonding functionality. If each repeating unit of the polymer has repeating functionalities, longer polymers provide more hydrogen bonding groups or coordinate covalent bonding groups that can participate in hydrogen bonding interactions or in coordinate covalent bonds.
  • polymeric binders having a molecular weight greater than 500 grams/mole are preferred because they provide attractive physical properties, and the solid is less volatile as compared to low-molecular-weight polymeric binders.
  • Polymeric binders with molecular weights greater than 4000 grams/mole are especially preferred because they have minimal volatility and are less likely to evaporate from the fibers.
  • Low-molecular weight materials typically are more mobile than are the higher- molecular weight materials. Low-molecular weight materials can more easily move to the fiber-particle interface, and are more easily absorbed by the fiber where they are less available to bond the particles to the fibers.
  • the higher molecular weight materials are less apt to be absorbed by the fibers, and are less volatile than the low-molecular weight materials.
  • higher molecular weight polymeric binders to a greater extent, remain on the surface of the particles where they are more available to bond particles to fibers.
  • polymers with molecular weights between 4000 and 8000 grams/mole have been used. Polymers with molecular weights above 8000 may be used, but such exceedingly high molecular weight polymers may decrease binding efficiency because of processing difficulties
  • polyme c binders have greater binding efficiency because their repeating functionality is a more efficient hydrogen bonding group. It has been found that repeating amide groups are more efficient than repeating carboxyl functionalities, which are more efficient than repeating hydroxyl functionalities, which in turn are more efficient than amine or ether functionalities. Hence, polymeric binders may be preferred that have repeating amine or ether functionalities, more preferably repeating hydroxyl functionalities, and even more preferably repeating carbonyl or carboxyl functionalities, and most preferably repeating amide functionalities. Binding may occur at any pH, but is suitably performed at a neutral pH of 5-8, preferably 6-8, to diminish acid hydrolysis of the resulting fibrous product.
  • Suitable binders may be selected from the group consisting of polyglycols such as polyethylene glycol or polypropylene glycol, polycarboxylic acids such as polyacrylic acid, polyamides, polyamines, poly(lactone) diols, such as poly(caprolactone) diol and combinations or copolymers thereof.
  • the particles may be bound to the fibers by a non-polymeric organic binder selected from a predetermined group of binders that each have a volatility less than water.
  • the vapor pressure of the binder may, for example, be less than 10 mm Hg at 25° C, and more preferably less than 1 mm Hg at 25° C.
  • the non-polymeric binders comprise non-polymeric binder molecules wherein the molecules have at least one functional group that forms hydrogen bonds or coordinate covalent bonds with the particles.
  • the predetermined group of non- polymeric binders may include a functional group selected from the group consisting of a carboxyl, a carboxylate, a carbonyl, a sulfonic acid, a sulfonate, a phosphate, a phosphoric acid, a hydroxyl, an amide, an amine, and combinations thereof (such as an amino acid or hydroxy acid) wherein each binder includes at least two such functionalities, and the two functionalities are the same or different.
  • a requirement for the non- polymeric binder is that it have a plurality of functional groups that are capable of hydrogen bonding, or at least one group that can hydrogen bond and at least one group that can form coordinate covalent bonds.
  • non-polymeric refers to a monomer, dimer, trimer, tetramer, and oligomers, although some particular non-polymeric binders are monomeric and dimeric, preferably monomeric.
  • non-polymeric organic binders are capable of forming five or six membered rings with a functional group on the surface of the particle.
  • An example of such a binder is an amine or amino acid (for example, a primary amine or an amino acid such as glycine) which forms six-membered rings by forming hydrogen bonds: n er
  • a six-membered ring also is formed by the hydroxyl groups of carboxylic acids, alcohols, and amino acids, for example:
  • a five membered ring can be formed by the binder and the functionality on the surface of the particle, for example: R" ⁇
  • the particle is a water-insoluble particle such as SAP and the binder is an alcohol, such as a polyol with hydroxyl groups on adjacent carbons, for example 2,3-butanediol.
  • a binder that forms a five-membered ring can also be used with a water soluble particle, for example wherein the particle is EDTA and the binder is an alcohol, such as a polyol with hydroxyl groups on adjacent carbons, for example 2,3-butanediol.
  • alcohols that do not form a five-membered ring also can be used, for example alcohols that do not have hydroxyl groups on adjacent carbons.
  • suitable alcohols include primary, secondary or tertiary alcohols.
  • Amino alcohol binders are alcohols that contain an amino group (-NR 2 ) , and include binders such as ethanolamine (2-aminoethanol) , and diglycolamine (2-(2- aminoethoxy)ethanol) ) .
  • Non-polymeric polycarboxylic acids contain more than one carboxylic acid functional group, and include such binders as citric acid, propane tricarboxylic acid, maleic acid, butanetetracarboxylic acid, cyclopentanetetracarboxylic acid, benzene tetracarboxylic acid and tartaric acid.
  • a polyol is an alcohol that contains a plurality of hydroxyl groups, and includes diols such as the glycols (dihydric alcohols) , ethylene glycol, propylene glycol and trimethylene glycol; triols such as glycerin (1,2,3- propanetriol) .
  • Esters of hydroxy1-containing binders also may be used with mono- and di-esters of glycerin, such as monoglycerides and diglycerides, being especially preferred.
  • At least one of the esterifying acid moieties must also include a functional group that is capable of forming at least one hydrogen bond with the fibers, or at least one functional group capable of forming a hydrogen bond or a coordinate covalent bond with the particles.
  • a functional group that is capable of forming at least one hydrogen bond with the fibers or at least one functional group capable of forming a hydrogen bond or a coordinate covalent bond with the particles.
  • polyhydroxy or polycarboxylic acid compounds include tartaric acid or ascorbic acid (vitamin C) :
  • Hydroxy acid binders are acids that contain a hydroxyl group, and include hydroxyacetic acid (CH 2 OHCOOH) and lactic, tartaric, ascorbic, citric, and salicylic acid.
  • Amino acid binders include any amino acid, such as glycine, alanine, valine, serine, threonine, cysteine, glutamic acid, lysine, or ⁇ alanine.
  • Sulfonic acid binders and sulfonates are compounds that contain a sulfonic acid group (-S0 3 H) or a sulfonate (-S0 3 ) .
  • Amino-sulfonic acids also can be used.
  • One example of an amino-sulfonic acid binder suitable for the present invention is taurine, which is 2-aminoethanesulfonic acid.
  • Non-polymeric polyamide binders are small molecules (for example, monomers or dimers) that have more than one amide group, such as oxamide, urea and biuret.
  • a non-polymeric polyamine binder is a non-polymeric molecule that has more than one amine group, such as ethylene diamine, EDTA or the amino acids asparagine and glutamine.
  • the non-polymeric organic binder is preferably selected from the group consisting of glycerin, a glycerin monoester, a glycerin diester, glyoxal, ascorbic acid, urea, glycine, pentaerythritol, a monosaccharide, a disaccharide, citric acid, taurine, tartaric acid, dipropyleneglycol, urea derivatives, phosphate, phosphoric acid, a hydroxy acid, and combinations thereof.
  • the non-polymeric binder also is most preferably selected from the group consisting of glycerin, a glycerin monoester, a glycerin diester, polyglycerin oligomers, urea and combinations thereof.
  • the non-polymeric binders also preferably include functionalities selected from the group consisting of a carboxyl, a carboxylate, a carbonyl, a sulfonic acid, a sulfonate, a phosphate, a phosphoric acid, a hydroxyl, an amine, an amide, and combinations thereof (such as an amino acid or hydroxy acid) .
  • the non-polymeric binders must have at least two functionalities from such group, and the groups may be the same or different.
  • Each of the non-polymeric binders disclosed above is capable of forming hydrogen bonds because it has a functional group that contains electronegative atoms, particularly oxygens or nitrogens, or has electronegative groups, particularly groups containing oxygens or nitrogens, and that also include a hydrogen.
  • the amino alcohol, amino acid, carboxylic acid, alcohol and hydroxy acid all have a hydroxyl group in which a hydrogen is bound to an electronegative oxygen, creating a dipole that leaves the hydrogen partially positively charged.
  • the amino alcohol, amino acid, amide and amine all have an NR group in which a hydrogen may be bound to an electronegative nitrogen that also leaves the hydrogen partially positively charged.
  • the partially positively charged hydrogen in both cases then can interact with an electronegative element, such as oxygen or nitrogen, on the particle or fiber to help adhere the binder to the particle and fiber.
  • an electronegative element such as oxygen or nitrogen
  • the polycarboxylic acid, hydroxy acid, amino acid and amide also have a carboxyl group with an electronegative oxygen that can interact with hydrogen atoms in the particles and fibers, or in intermediate molecules between the binder and particles or fibers.
  • electronegative atoms (such as oxygen or nitrogen) on the fiber or particle can interact with hydrogen atoms on the binder that have positive dipoles
  • partially positive hydrogen atoms on the fiber or particle can interact with electronegative atoms on the binder.
  • the hydrogen bonding interactions are shown as dotted lines.
  • One such interaction is shown between the nitrogen of glycine and a hydrogen of an -OH on cellulose.
  • a hydrogen bond with glycine is also shown between an oxygen of the -OH on glycine and the hydroxy hydrogen of an alcohol sidechain on cellulose.
  • Hydrogen bonding interactions of the 1,3-propanediol are shown in dotted lines between an oxygen on an -OH group of the binder and a hydrogen of an -OH group on the cellulose molecule.
  • Another hydrogen bond is also shown between a hydrogen on an -OH group of the glycol binder and an oxygen in an alcohol sidechain of the cellulos- It also is possible for water or other hydrogen bonding molecules to be interposed between the fiber and binder, such that the fiber and binder are both hydrogen bonded to the water molecule.
  • an atom on the binder may have an unbound pair of electrons, such as a lone pair of electrons from an oxygen or nitrogen atom, that can be donated to an empty orbital of an acceptor atom in the particle to form a coordinate covalent bond.
  • the free pair of electrons on the oxygen or nitrogen can be donated to the empty p, d or f orbital of a particle (for example a boron-containing particle) to form a coordinate covalent bond that adheres the particle to the binder.
  • the fibers themselves do not normally contain functional groups that can act as electron acceptors in the formation of coordinate covalent bonds with the binders, but hydrogen bonding interactions allow the binder to adhere to the fiber.
  • Cellulosic and synthetic fibers for example, contain hydroxyl, carboxyl and ester groups that will hydrogen bond with the hydroxyl, carboxylic acid, amide, amine or other groups of the binder.
  • Non-cellulosic or non-synthetic fibers that have these functionalities also can be used, for example silk, which has an amide linkage. Hence the binder will adhere the particle with a coordinate covalent bond and the fiber with a hydrogen bond.
  • the binder is bound to both the fibers and the particle by hydrogen bonds.
  • a polyol binder for example, can be used to bind polyacrylate hydrogel particles to cellulosic fibers.
  • the hydroxyl groups on the polyol binder participate in hydrogen-bonding interactions with the hydroxyl groups on the cellulose fibers and the carboxyl groups on the polyacrylate hydrogel.
  • the binder will adhere to both the particle and fiber with hydrogen bonds.
  • These hydrogen bonds provide excellent binding efficiency and diminish separation of bound particles from the fibers.
  • a structural drawing is shown below in which citric acid, vitamin C and urea adhere water-insoluble SAP particles to cellulose with hydrogen bonds, or water-soluble EDTA particles. Some of the possible hydrogen bonding interactions are shown as dashed lines. It is possible that other molecules (such as water molecules) also may participate in some of these bonds, for example, as an intermediary between the binder and particle or fiber.
  • Particularly efficient hydrogen bonding binders include those with carboxyl groups, such as ascorbic acid, or amide groups, such as urea. Hydroxyl groups are also very efficient binders. Amine and ether functionalities are less efficient binders.
  • Binders have functional groups that may be selected independently or in combination from the group consisting of a carboxyl, a carboxylate, a carbonyl, a hydroxyl, a sulfonic acid, a sulfonate, a phosphoric acid, a phosphate, an amide, an amine, and combinations thereof.
  • a carboxyl group could be provided by carboxylic acids, such as ascorbic acid; a carboxylate, which is an ionized carboxylic acid, could be provided by a material such as ascorbate; a carbonyl group can be provided by an aldehyde, such as ketone; a hydroxyl, such as an alcohol or a polyol, such as glycerol, or a mono- or diglyceride, which are esters of glycerol; an amide, such as a peptide; and an amine, which may be provided by an alkyl amine, such as ethylenimine wherein the binder has at least two of these functional groups, and each of the functional groups can be the same (for example, a polyol, polyaldehyde, polycarboxylic acid, polyamine or polyamide) or different (for example, an amino alcohol, hydroxyamide, carboxyamide, or amino acid) .
  • Functional groups also may be selected independently or in combination from the group consisting of carboxyl, an alcohol, an amide and an amine.
  • An aldehyde may optionally be a member of each of these groups, particularly if it is oxidized to a carboxylic acid.
  • the binders of the present invention also provide numerous process advantages. Binding of particles to the fibers can occur, for example, without external application of heat. Hence, if desired, particle binding may occur at ambient temperature. The present invention therefore is distinct from prior-art crosslinking processes in which elevated temperatures are required to covalently crosslink cellulose groups to one another. Moreover, the binders of the present invention have the advantage of being activatable by addition of a fluid, such as a liquid solvent (sometimes referred to herein as a activation liquid, one example of which is water) .
  • a fluid such as a liquid solvent (sometimes referred to herein as a activation liquid, one example of which is water) .
  • a liquid binder (which would include a solution of a solid or liquid binder, or a binder that has a melting point or softening point below room temperature) can be applied to a cellulose mat in the absence of the particles to be bound and the binder allowed to dry, for example until the fiber product reaches an equilibrium moisture content with the moisture in the ambient air.
  • the binders then may be activated to bind the particles in place. Some of the binders (especially the liquid binders) diffuse throughout the fibers to reach an equilibrium distribution of the binder.
  • the binder can be applied as a solid, for example as particles or a powder.
  • water or another activating fluid or liquid may be added to those portions of the mat where particulate binding is desired.
  • the particles then may be added to the mat and adhered to those portions of the mat that have been moistened. Alternatively, the particles may be added to the mat prior to or simultaneously with activation of the binder.
  • the binders may be liquids at room temperature (such as glycerin) , or liquid solutions of binders that are solids at room temperature (for example, an aqueous solution of glycine) , or liquid hot melts of solid binders.
  • Solid binders can be applied to the fibers as a supersaturated solution or the solid binder may be heated above its melting point and applied to the fibers. Upon solidifying the binder is deactivated.
  • Solid binders may be added to fibers in particulate form, for example, by sprinkling binder particles on the fibers, provided they are fixed by the subsequent application of heat or liquid.
  • the binding reaction of the present invention can occur across a broad range of pH without requiring a catalyst.
  • a suitable pH range without a catalyst is 1-14, but preferred ranges are 5-8 or 6-8 because such neutral pH ranges will produce fibrous products (such as cellulose products) that are less prone to damage by acid hydrolysis.
  • a non-acidic pH (7 or greater) will provide an environment that inhibits formation of ester bonds, and promotes formation of the hydrogen bonds or coordinate covalent bonds that adhere the particles of the present invention to the fibers with the binder.
  • the moisture content of the fibers during the binding reaction is 0.5—50%, suitably 5—40%, or preferably 5—20% water by weight of the fibers, binder and particle.
  • a moisture content greater than 20%, preferably 30%, or in the range 20—50%, or 30—50%, can be used even though such high moisture contents interfere with intermediate anhydride formation and inhibits formation of covalent bonds in the production of high-bulk crosslinked fibers.
  • the moisture content of the fibers during the binding reaction is 0.5-30%, suitably 5-25%, preferably 12-20%.
  • Particles may be added to the fibers with the particles distributed throughout a fibrous product without being confined to a surface of the product. The particles can be distributed throughout the depth of a fiber product such as a mat or web.
  • the binder suitably is present in the treated product in an amount of at least 1 percent, and no more than 80 percent, by weight of the fibrous material ("percent by weight") .
  • the binder is present in an amount of
  • binder 1 - 80, or more preferably, 1 to 40 or 1 to 25 percent by weight of the fibrous material. Below about 1 percent, when placed on the fiber, an insufficient amount of binder is present to achieve adequate binding. Using excessive amounts of binder can introduce unnecessary expense into the binding process. High percentages of binder can also cause processing problems because the binder material transfers to equipment surfaces. Therefore, it is often preferred to use no more binder than is required to bind the particles and fibers.
  • Thermoplastic binders also may be used to help bind fibers to each other and particles to fibers.
  • the binder that has the hydrogen bonding or coordinate covalent bonding functionalities itself may be thermoplastic.
  • the polymeric binders and some non- polymeric binders of the present invention have the advantage of being thermoplastic solids.
  • fibers treated in accordance with the present invention can be thermobonded by elevating the fiber temperature above the softening temperature of the binder to soften the thermoplastic binder and thermoplastically bind the fibers to each other and the fibers to the particles.
  • an auxiliary or second binder can be applied to the fibers as a solid at room temperature, and the temperature of the second binder elevated above its softening point to thermobond the fibers and particles.
  • the auxiliary binder may be applied to the fibers either before or after the primary binder is applied, but before thermobonding.
  • the binders of the present invention may be used with fibers that have substantial intrafiber covalent crosslinks (such as HBA available from
  • Binders of the present invention can therefore be used with natural fibers that have substantial interfiber bonding, which are defined as fibers that have not been processed as in European Applications 440 472 Al and 427 317 A2 to substantially eliminate interfiber bonds. Cellulose fibers that have not been so processed are substantially free of intrafiber bonds.
  • the fibrous product of the present method may further be densified by external application of pressure.
  • the densified product is compact and easily transported. And, when the particles are superabsorbent particles, the resulting fibrous product has superior properties as compared to nondensified products.
  • the inventors have found that the binders of the present invention produce - a product that can be easily densified. Easy densification is associated with the hydrogen bonds and coordinate covalent bonds formed between the binder and the particles and fibers.
  • the fibers are particularly easily densified when at least 5% by weight of the fibers, particles and binder, more preferably 10%, are SAP particles adhered to the fibers.
  • the binders may be applied to fibers before, subsequent, or simultaneously with addition of the particles. Simultaneous addition can be accomplished by two separate streams of particles and binder that are simultaneously directed at a fibrous substrate, or alternatively merged immediately or some time prior to impacting against the substrate. Without limiting the invention, it appears that the addition of small amounts of moisture to the particles may help bind superabsorbent particles and perhaps other types of particles to the fibers. For example, exposing the particles to air at 65 percent humidity as they are delivered to binder containing fibers has been found to enhance the particle bonding.
  • Binding may be performed under conditions that favor formation of hydrogen bonds or coordinate covalent bonds, and discourage formation of covalent bonds.
  • Conditions that favor covalent bonds are those disclosed in U.S. Patent No. 4,412,036 and U.S. Patent No. 4,467,012 wherein particle and binder would be laminated between tissue layers under high temperature and pressure to form laminated adherent tissue layers. That patent teaches that minimal adhesion occurs at 200 pli (pounds per linear inch, as in a calendar press) if no external heat is supplied, but adhesion improves as the reaction temperature increases. Improved adhesion of the tissue layers occurs because of enhanced covalent bonding as the temperature increases.
  • Fibers that have high bulk from intrafiber covalent crosslinks are prepared by individualizing the fibers (for example, in a fiberizer) and curing them at an elevated temperature (above 150° C) .
  • Initial application of the binder on such high-bulk fibers preferably occurs after the curing step, particularly if the binder is capable of functioning as a crosslinking material.
  • the specific types of binders disclosed herein that also can crosslink are polyols, polyaldehydes, polycarboxylic acids, and polyamines (polymeric or nonpolymeric binders with more than one amine group) . If such binders are present during curing, the binder will be consumed during the curing step to form covalently crosslinked bonds.
  • the fibers should contain at least 20% water (or 20-50% water) by weight if the particles and binder are present in the fibers when curing occurs.
  • the water inhibits covalent bond formation, and prevents all of the binder from being used to form covalent intrafiber crosslinks. Hence, some of the binder remains available to form the non-covalent bonds with the particles and produce ease of densification in fiber products made by the process of the present invention.
  • the present invention in contrast, produces a product under conditions that favor formation of hydrogen or coordinate covalent bonds.
  • the particles can be bound to the fibers in the absence of the external application of heat or pressure.
  • Particles also may be bound and the resulting fiber product densified, for example at less than 200 pli (about 8000 psi) with SAP, or less than 100 pli (about 4000 psi) with SAP, in the absence of external application of heat to produce a product in which a substantial portion of the particles are bound by non- covalent bonds (hydrogen or coordinate covalent bonds) .
  • a substantial portion of particles bound by non-covalent bonds means at least half of the bonds binding particles to fibers are other than covalent bonds, for example, hydrogen or coordinate covalent bonds.
  • particles may be bound in the absence of external application of pressure, but at elevated temperatures.
  • the particles are substantially entirely bound to the fibers non-covalently.
  • Binders and Water Insoluble Particles Several examples are provided below to illustrate using the polymeric binders within the present invention to attach superabsorbent particles to southern bleached kraft pulp.
  • EXAMPLE 1 A 321 gram amount of NB-416 southern bleached kraft fluff obtained from Weyerhaeuser Company may be air-entrained in a blender-like mixing device and 100 grams of poly(caprolactone) diol (average molecular weight 2000, supplied by Aldrich Chemical Company of Milwaukee, Wisconsin) dissolved in 100 ml of deionized water may be sprayed onto the fluff as a binder. Then 435 grams of starch graft polyacrylate hydrogel fines (IM 1000F; supplied by Hoechst-Celanese of Portsmouth, Virginia) may be added and mixed. The product may then be removed from the blender, and spread out in a fume hood to dry overnight.
  • poly(caprolactone) diol average molecular weight 2000, supplied by Aldrich Chemical Company of Milwaukee, Wisconsin
  • the resulting product may then be airlaid on a small airlay line, from M & J Machines (of Horsens, Denmark) and thermobonded at 140° C for one minute to produce a web containing 40% superabsorbent particles (SAP) attached to the individualized fibers.
  • This binder has a low melting point, hence raising the temperature to 140° C melted the binder and allows it to flow over the fibers and particles to enhance hydrogen bonding interactions, thereby further binding the fibers and particles.
  • This is an example of activating a solid binder by heating it, without liquid addition.
  • a polypropylene glycol/polyethylene glycol copolymer binder would also behave in this manner.
  • polyacrylate hydrogel FAVOR 800 supplied by Stockhausen of Greensboro, North Carolina
  • the classes of polymeric binders that encompass those described in Examples 1-4 are especially preferred over other multiple hydrogen bonding functionality polymers for a number of reasons.
  • One important reason is that their functionalities produce very strong, effective hydrogen bonding.
  • Other important reasons include their relative lack of activity (as compared with polyaldehydes or polyisocyanates) and their low toxicity (again, as compared with polyaldehydes or polyisocyanates) .
  • EXAMPLE 5 As previously described, repetition of a hydrogen bonding group on each repeating unit of a polymer has been found to produce a binder that provides superior binding of particles to fibers, as compared to polymeric binders in which the hydrogen bonding functionality is not present on all the repeating units.
  • This example shows the difference in binding efficiency between a 20% carboxylated polymer and a 100% carboxylated polymer.
  • a bound sample was prepared as in Example 1 using a 20% carboxylated ethylene acrylic acid copolymer and a 100% carboxylated PAA.
  • a 3171 gram amount of southern bleached kraft fluff was air-entrained in a blender-like mixing device and 1000 grams of glycerin (96%, USP; supplied by Dow Chemical Co. of Midland, MI) diluted with 300 ml of deionized water was sprayed onto the fluff. Then 4348 grams of starch graft polyacrylate hydrogel fines (IM 1000F; supplied by Hoechst-Celanese of Portsmouth, VA) were added to the mixing device and mixed with the fluff and binder.
  • glycerin 96%, USP; supplied by Dow Chemical Co. of Midland, MI
  • the material was then shunted into a flash tube dryer at 142° F, blown into a cyclone and fed into a Danweb airlay machine to form a web containing bound 40% IM 1000F that is substantially immobile in the web because the particles are bound to the fibers instead of mechanically entrapped by the matrix.
  • Glycerin is advantageous because it tends to penetrate the fibers and soften them in addition to binding the particles to the fibers. However, over time less glycerin is available at the surface of the fibers for use in binding particles in the event the glycerin/fiber material is stored for long periods prior to use in adhering particles (e.g. if activation is delayed for several weeks or more) .
  • a 900 gram amount of southern bleached kraft fluff pulp sheet was sprayed with a 50% solution of pentaerythritol (supplied by Aldrich of Milwaukee, WI) so that the moisture content was 17-21% as the sheet was fed into a Fitz hammermill fitted with a three-eighths- inch hole screen.
  • Starch graft polyacrylate hydrogel fines I 1000F; supplied by Hoechst-Celanese of Portsmouth, VA) were simultaneously added to the mill by a screw feed device, mixed with the fluff, shunted to an M & J airlay forming machine and airlaid to form a web.
  • the web that resulted contained 20% SAP attached to the fibers.
  • EXAMPLE 9 A 900-gram amount of southern bleached kraft fluff pulp sheet was fed into a Fitz hammermill fitted with a three-eighths-inch hole screen. The sheet was defiberized, shunted to an M & J airlay line, and airlaid into a web. As the web emerged, target zones of the web were misted with a 50% solution of lactose to raise the moisture content to 17-21%. Five gram aliquots of starch graft polyacrylate hydrogel fines (IM 1000F; supplied by Hoechst-Celanese of Portsmouth, VA) were subsequently sifted onto the target zones. The web that resulted contained target zones with 5 grams of SAP attached to the fibers of each target zone.
  • I 1000F starch graft polyacrylate hydrogel fines
  • Target-zone application of SAP can be advantageous because it reduces the cost of the product to provide SAP only in areas of a product where the SAP is needed, for example, the crotch area of a diaper. Placement of SAP in the area where a liquid insult is expected also decreases the necessity for wicking liquid to a SAP impregnated region. This is an advantage because the requirement for wicking can increase liquid leakage in an absorbent product such as a diaper.
  • EXAMPLE 10 A 321 gram amount of southern bleached kraft fluff was air-entrained in a blender-like mixing device and 100 grams of glycerin (96%, USP; supplied by Dow of Midland, MI) diluted with 30 ml of deionized water were sprayed onto the fluff. 71 grams of Abscents (an odor absorbing zeolite supplied by UOP of Tarrytown, NY) was then added and mixed in the mixing device with the fibers and glycerin for 15 seconds until a homogenous mixture was achieved. The material was then spread out in a fume hood overnight to dry, airlaid into a web and tested for particulate retention by an ash test. The pad so produced contained 7% particulate. The original addition amount should have produced 15%, hence 50% particle retention was observed. This compares favorably to particulate retention with latex binders under similar conditions in which only about 3% of particles are retained. XI. Binding Examples for Water-Soluble Particles
  • binders of the present invention to attach water-soluble particles to southern bleached kraft pulp.
  • EXAMPLE 11 A 321 gram amount of NB-416 southern bleached kraft fluff obtained from Weyerhaeuser Company (Tacoma, Washington) was air-entrained in a blender-like mixing device and 50 grams of glycerin (supplied by Dow
  • HBA pulp a crosslinked high bulk fiber available from Weyerhaeuser Company, Tacoma Washington
  • glycerin supplied by Dow Chemical of Midland, Michigan
  • sodium bicarbonate supplied by J.T. Baker Chemical Co. of Phillipsburg, New Jersey
  • EXAMPLE 13 An NB 416 pulp sheet (southern bleached kraft available from Weyerhaeuser Company of Tacoma, Washington) was treated with glycerin on a roll coater so that the product contained 10% glycerin by weight. That pulp sheet was fed into a hammermill and ground while simultaneously adding a polyacrylate hydrogel (IM 3900, supplied by Hoechst Celanese of Portsmouth, Virginia) and ethylenediamine tetraacetic acid to the mill at rates such that the product contained 54% treated fiber, 42% IM 3900, and 4% EDTA. That mixture was shunted to an airlay device from M & J Machines (of Horsens, Denmark) and airlaid into a continuous web. The resulting product was examined by scanning electron microscope and revealed fibers with attached polyacrylate hydrogel and EDTA particles.
  • IM 3900 polyacrylate hydrogel
  • EXAMPLE 14 A procedure similar to the one described in Example 13 was performed using KittyHawk pulp (a thermobondable blend of southern bleached kraft and polyethylene fibers available from Weyerhaeuser Company of Tacoma, Washington) . The resulting product was ther obonded by passing the web through a through-air oven at 140° C for 0.5 minutes. The resulting product was examined by scanning electron microscope, and revealed fibers with attached polyacrylate hydrogel and EDTA particles.
  • KittyHawk pulp a thermobondable blend of southern bleached kraft and polyethylene fibers available from Weyerhaeuser Company of Tacoma, Washington
  • EXAMPLE 15 In this example, oxalic acid is bound to the fibers by the binders of the present invention.
  • a pulp sheet with 10% binder was prepared as in Example 13. The pulp sheet was conditioned at 90% relative humidity for 4 hours, then the sheet was fiberized in a Waring blender. Particles of oxalic acid were then added to the blender and blending continued. The product was dried and an SEM obtained, which is shown in FIG. 14. The feathery particle of oxalic acid is shown near the center of the photograph bound to the cellulose fiber by the glycerin.
  • Fibers were prepared as in Example 15, except aluminum sulfate (alum) was substituted for oxalic acid.
  • the SEM of alum bound to the fibers is shown in FIG. 15.
  • EXAMPLE 17 A mixture of binders also may be used to bind particles to the fibers. Fibers may be supplied as in Example 11, but the 50 grams of glycerin would be substituted with a mixture of urea and glycerin.
  • urea/glycerin mixture 40/60 mixture (by weight) of urea and glycerin is mixed by dissolving urea in the glycerin, and heating the solution to 70-80° C. The heated binder mixture is then applied to bind the particles to the fibers as in Example 11.
  • the urea/glycerin mixture provides several advantages over the use of glycerin alone. Urea lowers the cost of the binder, while glycerin softens the fibers. The mixture also provides manufacturing advantages. In other embodiments urea alone as well as the other binders of the type specified in the foregoing detailed description of the invention and combinations thereof may be used as the binder.
  • EXAMPLE 18 Superabsorbent particles were bound to cellulose fibers with a glycerin binder, as described in Example 6 above. For purposes of comparison, superabsorbent particles were bound to a separate sample of cellulose fibers using a polyvinyl acetate (PVAc) binder that was about 3% carboxylated, that is only about 3% of the PVA monomers were carboxylated. Binding was performed as in Example 6, but PVAc was substituted for glycerin. A 100-gram sample of the glycerin and PVAc treated fluff with attached SAP was fed into a fan that was connected by a hose to a small cyclone mounted on top of a material containment box.
  • PVAc polyvinyl acetate
  • a 2.00 gram sample of the fibers that remained near the top of the sieve column was then placed in a 75 ml sample of 0.9% saline for exactly one minute. After that minute, the liquid that was not absorbed was poured off into a separate, tared beaker and weighed. The relative amounts of liquid absorbed is indicative of the amounts of SAP bound to the fiber. Fiber retaining higher amounts of SAP tend to absorb more liquid and give a smaller amount of liquid not absorbed.
  • Table III illustrates that the glycerin binder provides a product that has an absorbency increase of 400% compared to the PVAc binder. A substantial portion of this improvement is believed to be due to better adhesion between the fibers and SAP, such that the particles are not dislodged from the fibers.
  • Pad integrity was compared in fibrous products that used no binder and a glycerin binder at 7% and 11% by weight. Each of these binders was used to bind SAP to fibers as in Example 6, and properties of the pad were measured and are shown in Table IV:
  • Pad integrity (low density)
  • the glycerin binder in this example produced a product that had a higher tensile index than an untreated product.
  • the increased tensile strength was especially enhanced in the densified (high density) product, and particularly when at least 11% of the binder was used.
  • NB-316 a standard southern bleached kraft pulp with no binder
  • GNB as used herein is an NB pulp (a standard southern bleached kraft pulp) with 25% glycerin (entrained and sprayed)
  • HBA pulp a high bulk intra ⁇ fiber crosslinked fiber available from the Weyerhaeuser Company that contains intrafiber covalent crosslinks
  • GHBA as used herein is HBA fibers treated with a glycerin binder in amounts of 12.5% and 25% by weight. Results are given in Tables V and VI.
  • FAQ time was determined by airlaying a specific quantity (4.00 grams) of the fluff to be tested into a clear plastic tube that was fitted with a screen at one end. The fluff and tube were then placed into a well in the test device and a metal plunger was lowered onto the fluff and the pad's bulk calculated. Water then flowed from underneath the pad, passed through the screen and wicked up through the pad. Absorbency time was measured from when the liquid makes contact with the bottom screen until the water completes an electrical circuit by contacting the foot of the plunger resting on top of the pad. Lower absorbency times indicate better absorbency. Since the absorption of the liquid by the pad was accompanied with some collapse of the pad's structure, the bulk of the wet pad was then recalculated. The amount of liquid absorbed was then measured and a gram-per-gram capacity for the material was calculated.
  • Table V gives FAQ time as a measure of wettability. A lower FAQ time indicates a product that is more absorbent and wicks faster.
  • Table VI gives wet bulk of fibers and the adjusted bulk of the fibers. The adjusted bulk is a calculated number obtained by dividing the bulk by the actual percent of pulp in the sample.
  • NB-316 is a pulp sheet available from Weyerhaeuser Company in which no binder is used. HBA pulp is described in Example 20. HBA/Gly SAP was an HBA pulp fiber that was bound with glycerin (12% binder, 48% fiber) and which contained 40% SAP particles. NB- 316/Gly SAP is NB-316 fibers to which glycerin and SAP fibers were added. The procedure for determining liquid retention was to weigh triplicate small portions (near 0.2 grams) of samples to the nearest 0.0001 gram and then heat-seal the small portions inside an envelope of a heat- sealable, nonwoven tea bag.
  • the samples were then immersed in an excess of 0.9% saline for thirty minutes, then drained by suspending them from a clip for fifteen minutes. The samples were weighed to determine the amount of liquid absorbed. The grams of liquid absorbed per gram of sample were calculated and the samples were spun in a centrifuge for one minute. The samples were then reweighed and a percent-liquid-retention was calculated.
  • an auxiliary binder or additional binder or binders can be used in addition to the non-polymeric or polymeric binders or combinations thereof in accordance with the present invention.
  • the additional binder(s) is selected to not react with the binder or binder combination of the present invention in a manner which prevents this latter binder from having the required functionality.
  • the preferred auxiliary binders are non-reactive in this way.
  • polymeric and non-polymeric binders of the invention may be combined with one another and with other binders as long as they do not react to block the desired functionality.
  • EXAMPLE 22 A 321 gram amount of a southern bleached kraft fiber (NB-416, supplied by Weyerhaeuser) was air entrained in a blenderlike mixing device and sprayed with 212.8 grams of a polyvinylacetate latex (PN-3666H, supplied by H B Fuller of Minneapolis, Minnesota) . While still mixing, 438 grams of a water swellable polyacrylate hydrogel (Favorsab 800, supplied by Stockhausen of Greensboro, NC) was added and the resulting mixture was then sprayed with 100 grams of a 50% solution of glycerin (supplied by Dow of Midland, Michigan) . The blender was then stopped and the mixture was vacuumed from the blender and placed in a fume hood to air dry overnight.
  • PN-3666H polyvinylacetate latex
  • the dried product was then airlaid into a 6" diameter pad in a laboratory padformer, pressed to a density of approximately 0.077 g/cc, and thermobonded at 140° C for thirty seconds.
  • the resulting pads had 40% bound SAP and improved tensile strength as compared to untreated fluff with SAP and as also compared to binder treated fluff with SAP without the auxiliary binder.
  • Tensile strength was highest with polyvinylacetate alone, followed by a combination of polyvinylacetate and glycerin, then glycerin alone. Lowest tensile strength was seen with no binder at all.
  • Binders of the present invention may be used to bind particles to pulp fibers that contain synthetic thermobonding fibers.
  • Kittyhawk pulp available from Weyerhaeuser Company
  • the Kittyhawk pulp is used to produce a pulp web, with SAP bound to the fibers as described in Example 3.
  • the web with adhered SAP is then passed through a thermobonder to soften the polyethylene fibers and fuse the fibers of the web to each other to increase web strength.
  • EXAMPLE 24 Solid sample 13 C NMR spectra were obtained on cellulose fibers treated with ascorbic acid to bind SAP to the fibers. An NMR spectra also was obtained on L-ascorbic acid. In both cases, separate spectra were acquired using recovery delays of 1 sec and 5 sec between acquisitions.
  • the peaks in the treated-fiber spectrum were assigned readily to the components: SAP polyacrylate carboxyl (185 ppm) and backbone (50-30 ppm) carbons; cellulose (106, 90, 84, 76, 73 and 66 ppm); and ascorbic acid ring carbons C-l, C-2 and C-3 (175, 119 and 156/153 ppm, respectively) ; the other ascorbic acid carbons are in the cellulose region, two of them being resolved at 69 and 61 ppm.
  • the ascorbic acid carbon chemical shifts in this ternary mixture were essentially identical (+ 0.2 ppm) to their values in pure ascorbic acid. This indicated that the ascorbic acid in the treated fibers had undergone no gross structural changes, such as total neutralization, oxidation or ring opening.
  • the NMR of the treated fibers would show the ascorbic acid in the salt form.
  • NMR reference spectra were found of the acid and its salt in aqueous solution, and C-3 is seen to shift dramatically on ionization of its OH group: 156 ppm in the acid to 176 ppm in the salt.
  • the NMR spectrum of the ternary mixture contains the peaks at around 156 ppm, the ascorbic acid in this system is not ionized.
  • ascorbic and polyacrylic acids have nearly identical pK a values (4.2 vs 5, respectively) . They are both typical strong organic acids with weak conjugate bases. Thus, there is no compelling reason for one of these acids to be neutralized (ionized) by the conjugate base of the other acid. Rather, there should be a strong tendency for an ascorbic acid and an acrylate ion to share a hydrogen ion between them, resulting in a long hydrogen bond between partially ionic ascorbic and acrylic acid units. This sharing of hydrogen ions would certainly be reflected in the IR spectrum, yet satisfies the NMR data by not invoking full ionization of ascorbic acid.
  • the spectroscopic data are fully consistent with a hydrogen bonding mechanism between ascorbic acid and an acrylate unit in the superabsorber.
  • Infrared transmission spectra of the untreated NB316 pulp, the treated NB316 pulp, ascorbic acid, and the IM 10OF superabsorber were prepa ed. Then, a subtraction spectrum representing the treated pulp minus the untreated control was obtained.
  • the higher frequency bands (3300-3600 cm' 1 ) in ascorbic acid are indicative of bonded OH groups.
  • the infrared bands at 1319, 1119, and 1026 cm “1 may also be associated with OH vibrations. Consequently, the IR suggested that the subtraction spectrum reflected primarily a loss of the OH groups that were attached directly to the ring. A likely possibility is that the OH groups were replaced by sodium.
  • the binders of the present invention have the advantage of being activatable from an inactive state on the fibers by addition of liquid, heating, or by kinetic energy such as may be supplied by mechanical agitation, pressure, or ultrasonics.
  • a liquid binder can be applied to cellulose fibers, loose or in another form, such as a cellulose mat, in the absence of the particles to be bound.
  • the binder is then dried or allowed to dry, for example until the binder and fiber reach an equilibrium moisture content with ambient air.
  • the binder can be applied as a solid, for example, particles sprinkled onto a fiber mat.
  • a liquid such as water is added to the fibers resulting in an activation of the binder.
  • the particulates may then be added, and the binder secures the particulates to the fibers.
  • This subsequent processing of the fibers to attach the particles can occur, for example, at a separate location from the location where the binder was applied to the fibers. Therefore, manufacturers of products can add particulates of interest (e.g. , superabsorbent particles or fibers; antimicrobial particles, etc.) at the place of manufacture of the end products that incorporate the treated fibers.
  • particulates of interest e.g. , superabsorbent particles or fibers; antimicrobial particles, etc.
  • more than one type of particulate material including water soluble and water insoluble particles
  • Particles without the required functionality would not be bound in the same manner.
  • binders of the present invention can be activated by mechanical agitation (the application of kinetic energy) .
  • glycerin binder may be applied to fibrous cellulose.
  • the glycerin binder may be allowed to dry, and the fibers then mechanically agitated in the presence of superabsorbent particles and/or other particles to activate the glycerin binder and bind the particles to the fibers.
  • Mechanical agitation may take place, for example, in a defiberizer where a sheet or mat of glycerin treated cellulose fibers are defiberized while being intimately mixed with SAP that is bound to the fibers by the mechanical agitation.
  • Binder activation in the present invention allows binder to be added to fibers either before or after particles are added to the fibers.
  • the binder is subsequently activated by addition of liquid, heat, or by kinetic energy such as resulting from agitation, and particles are bound to the fibers.
  • the particles may be added to the fibers either before binder activation, after binder activation, or simultaneous with activation. If SAP and/or other particles are to be added to cellulose fibers, for example, the binder may be applied to a pulp sheet which is subsequently fiberized.
  • a liquid such as water may be added to the pulp before or after fiberization, and SAP may be added before or after water addition, or simultaneously with the water.
  • SAP should be applied to the fibers prior to complete evaporation of the added water from the fibers.
  • Water also can be added in other ways, such as by very humid air, a fog or mist, or as steam.
  • Activation can be of all the fibers, or only portions of the fibers, such as target zones or portions of the mat where particulate binding is desired.
  • the particles may then be added to the mat and adhered to the target zones of the mat which have been activated.
  • the binder is applied as a solid and heated during a later processing stage to activate the binder by softening it such that it binds the particles to the fibers.
  • the particles may be added in a pattern corresponding to a desired distribution (for example a non-homogeneous distribution) of particles in the fibrous material.
  • activation is accomplished by using a binder solvent to moisten a targeted area of the product into which an inactive (dry or dried) binder has already been introduced.
  • the binder is applied to the fibers and then activated by applying kinetic energy to the fibers.
  • binder for example, may be sprayed on fibers and allowed to dry. Desired particles are then added to the fibers as the fibers are mechanically agitated in a blender or defiberizer to kinetically activate the binder and bind the particles to the fibers.
  • the binder may be added as a liquid or a solid to the fibers.
  • the liquid is allowed to dry, and then activated by mechanically agitating the fibers and binder.
  • solid binder addition the binder is applied as a solid, and then moistened (for example, to a total fiber moisture content of about 7%) and then mechanically agitated.
  • Activation of the binder may be performed prior to adding the particles, subsequent to adding the particles, or simultaneously with addition of the particles.
  • the binder adheres a substantial portion of the particles to the fibers, wherein "a substantial portion” refers to about half of the particles added, at least where the particles are not added in excess. Of the particles that are adhered, at least half of them (and more typically substantially all of them, e.g., over 80%) are adhered to the fibers.
  • the activating step can comprise applying a liquid to the fibers after the binder has been applied to the fibers, shortly before the binder is applied to the fibers, or simultaneously with application of the binder to the fibers.
  • the activating step may be performed after the curing step is complete, if a curing step is to be performed.
  • Example 1 The method of Example 1 above could be modified such that the SAP is not added until after the web is heated to 140° C.
  • a solid polyethylene glycol/poly- propylene glycol copolymer could be substituted for the binder of Example 1, and it would melt well below 140° C, and in its liquid form bind the SAP to the fibers.
  • the SAP could be applied randomly across the heated product, or applied specifically to a targeted zone of the product where enhanced absorbency is specifically desired.
  • EXAMPLE 27 A southern kraft pulp sheet would be immersed or sprayed with 154 grams of a 65% solution of polyacrylic acid diluted with 100 ml of deionized water. The sheet is then allowed to dry overnight, heated in an oven at 80° C for thirty minutes and conditioned in a 50% relative humidity chamber overnight. The sheet is then misted with water to raise its moisture content to 17-20% as it is fed into a Fitz hammermill filled with a three-eighths inch hole screen.
  • Polyacrylate hydrogel particles of FAVOR 800 supplied by Stockhausen would simultaneously be added to the mill by a screw feed device, mixed with the fluff, shunted to an M & J airlay forming machine and airlaid to form a web containing bound SAP throughout the web, i.e., without being confined to a surface of the web.
  • Mixing SAP throughout the fluff helps produce a product in which SAP is homogeneously or randomly distributed, which diminishes problems of gel blocking.
  • KittyHawk pulp sheet from the Weyerhaeuser Co. , containing 22% synthetic fiber
  • the 5 inch wide sheet was then uncoiled on a lab bench to dry overnight, heated in an oven at 80° C for thirty minutes and conditioned in a 50% relative humidity chamber overnight.
  • the sheet is fed into a Fitz hammermill fitted with a three-eighths inch hold screen, defiberized, shunted to an M & J airlay line, and airlaid into a web.
  • circular target zones of the web are misted with water from a spray bottle to raise the moisture content to 17—21% in the target zone.
  • EXAMPLE 29 A 900 gram amount of a southern bleached kraft pulp sheet was immersed in a 2% by mass solution of ascorbic acid (supplied as a dry powder by Aldrich
  • a 900 gram amount of KittyHawk pulp sheet (from the Weyerhaeuser Co., containing 22% synthetic fibers) was immersed in a 10% by weight solution of urea (supplied by Aldrich of Milwaukee, WI) for thirty minutes.
  • the 5-inch-wide sheet was then uncoiled on a lab bench to dry overnight, heated in an oven at 80° C for thirty minutes and conditioned in a 50% relative humidity chamber overnight.
  • the sheet was then gravimetrically determined to be about 30% by weight urea.
  • the sheet was fed into a Fitz hammermill fitted with a three-eighths-inch hole screen, defiberized, shunted to an M & J airlay line, and airlaid into a web.
  • the binder in the dried web was activated by misting target zones of the web with deionized water in a circular pattern from a spray bottle to raise the moisture content of the web or the target zones to 17—21%.
  • Five gram aliquots of polyacrylate hydrogel (FAVOR 800 supplied by Stockhausen of Greensboro, North Carolina) were subsequently sifted onto each activated target zone.
  • the web that resulted contained target zones with 5 grams of SAP attached to the fibers in each target zone.
  • Alternative spray patterns could be provided by selecting spray heads or different control devices that mist different patterns.
  • auxiliary binder also may be used to help bind fibers to each other above the melting point of the auxiliary binder.
  • the auxiliary binder may be a solid thermoplastic material that is applied to the fibers and softened by elevating the temperature during the binding step to above the softening temperature of the auxiliary binder.
  • the auxiliary binder is thereby temporarily softened, rendered more fluid (which for purposes of convenience may be referred to as auxiliary binder melting) and subsequently resolidified as the temperature eels, which thermoplastically binds the fibers to each other, and the particles to the fibers.
  • the auxiliary binder may also contain a hydrogen bonding functionality that hydrogen bonds the particles to the fiber.
  • auxiliary binders that are thermoplastic and also contain hydrogen bonding groups include ethylene vinyl alcohol, polyvinyl acetate, acrylates, polycarbonates, polyesters and polyamides. Further information about the use of such auxiliary binders can be found in U.S. Patent No. 5,057,166.
  • the auxiliary or second binder can be added to the fibers, either before or after a first binder, to help bind the fibers to each other and provide additional binding between the fibers and particles.
  • a suitable second binder would be a thermoplastic or thermosetting binder.
  • the polymers may be a material which remains permanently thermoplastic.
  • such polymers may be a material which is partially or fully crosslinkable, with or without an external catalyst, into a thermosetting type polymer.
  • suitable thermoplastic binders can be made of the following materials: ethylene vinyl alcohol, polyvinyl acetate, acrylic, polyvinyl acetate acrylate, acrylates, polyvinyl dichloride, ethylene vinyl acetate, ethylene vinyl chloride, polyvinyl chloride, styrene, styrene acrylate, styrene/butadiene, styrene/acrylonitrile, butadiene/acrylonitrile, aerylonitrile/butadiene/styrene, ethylene acrylic acid, polyethylene, urethanes, polycarbonate, oxide, polypropylene, polyesters, and polyimides.
  • thermoset binders include those made of the following materials: epoxy, phenolic, bismaleimide, polyimide, melamine/formaldehyde, polyester, urethanes, urea, and urea/formaldehyde. More than one of these materials may be used to treat the fibers. For example, a first coating or sheath of a thermoset material may be used followed by a second coating of a thermoplastic material. The superabsorbent particles or other particles are then typically adhered to the outer binder material. During subsequent use of the fibers to make products, the thermoplastic material may be heated to its softening or tack temperature without raising the thermoset material to its curing temperature.
  • thermoset material permits subsequent heating of the fibers to cure the thermoset material during further processing.
  • the thermoset material may be cured at the same time the thermoplastic material is heated by heating the fibers to the curing temperature of the thermoset with the thermoplastic material also being heated to its tack temperature.
  • binders enhance the fire resistance of the treated fibers, and thereby products made from these fibers.
  • polyvinyl chloride, polyvinyl dichloride, ethylene vinyl chloride and phenolic are fire retardant.
  • Surfactants may also be included in the liquid binder as desired.
  • Other materials may also be mixed with the liquid binder to impart desired characteristics to the treated fibers.
  • particulate material such as pigments, may also be included in the binder for application to the fibers.
  • an auxiliary binder can be used in addition to the polymeric binders of the present invention.
  • a 3210 gram amount of southern bleached kraft binder (NB-416, supplied by Weyerhaeuser Company) is air entrained in a blenderlike mixing device and sprayed with 2128 grams of a polyvinyl acetate latex (PN-3666H, supplied by H.B. Fuller of Minneapolis, Minnesota) .
  • a water swellable polyacrylate hydrogel (IM 1000-60, supplied by Hoechst-Celanese of Portsmouth, Virginia) is added and the resulting mixture is then sprayed with 1160 grams of a 50% solution of polypropylene glycol (supplied by Union Carbide of Danbury, Connecticut) .
  • the blender is not stopped and the mixture is shunted into a flash tube dryer.
  • the dried product is then airlaid as a 16 inch wide web on a Danweb airlay machine, pressed to a density of approximately 0.15 g/cc, and thermobonded at 140° C for thirty seconds.
  • the resulting web would have 40% bound SAP and improved tensile strength (as compared to untreated fluff with SAP) .
  • the binders of the present invention can be added to the fibers in any convenient manner.
  • One such procedure is to spray the binder or binders on a web of the fibers that is conveyed past a sprayer on a conveyor belt.
  • loose fibers may be allowed to fall past a sprayer, or loose fibers may be moved on a conveyor belt past a sprayer.
  • the loose fibers may also be slurried with or immersed in binder.
  • blending of the fiber and binder may be accomplished or the binder may simply be sprinkled onto or otherwise comingled with the fibers, followed by a fixation step such as addition of heat or liquid.
  • the fibers may also be sprayed or immersed in the binder, or binder particles may be applied thereto. These fibers can, while still wet in the case of a liquid binder or following activation of a liquid or solid, be combined with the particles.
  • the fibers also can be allowed to dry for later activation with an activation fluid, such as an activation liquid, and combined with the particles at that time.
  • an activation fluid such as an activation liquid
  • An example of when it may be desirable to apply the binder to the fiber and thereafter activate the binder in the presence of particles is when the particles are added at a remote site. For instance, the binder may be activated from an inactive state at a second location that is remote from a first location where the binder is applied to the fibers.
  • the second location may be, for example, a location where a manufacturer combines fibers and particles into articles, such as absorbent articles. Particles may be added from conventional volumetric feeders in a hammermill or from injectors on a paper making line.
  • One method for uniformly coating the fibers with a binder and adding the particles is shown in U.S. Patent No. 5,064,689. However, the invention is not limited to any specific mechanism for combining the fiber, binder and particles.
  • the apparatus 110 (FIG. 3) of the present invention comprises a conveying device 112 for transporting a mat 114 of cellulose fibers or other fibers through a fiber treatment zone 116; an applicator 118 for applying a treatment substance such as a crosslinking substance from a source 119 thereof to the mat 114 at the fiber treatment zone 116; a fiberizer 120 for completely separating the individual cellulose fibers comprising the mat 114 to form a fiber output comprised of substantially unbroken cellulose fibers substantially without nits or knots; and a dryer 122 coupled to the fiberizer for flashevaporating residual moisture from the fiber output and for curing the crosslinking substance, thereby forming dried and cured cellulose fibers.
  • a conveying device 112 for transporting a mat 114 of cellulose fibers or other fibers through a fiber treatment zone 116
  • an applicator 118 for applying a treatment substance such as a crosslinking substance from a source 119 thereof to the mat 114 at the fiber treatment zone 116
  • the mat 114 of cellulose fibers is preferably in an extended sheet form stored in the form of a roll 124 until use. It is normally not necessary that the cellulose fibers comprising the mat 114 be completely dry. Since cellulose is a hydrophilic substance, molecules thereof will typically have a certain level of residual moisture, even after drying. The level of residual moisture is generally 10% wt/wt or less, which is not detectable as "wetness.”
  • FIG. 3 also shows that more than one supply, such as multiple rolls 124, of the mat 114 of cellulosic fibers can be simultaneously processed using the present invention.
  • sprayers or other applicators 118 apply chemicals such as crosslinking agents to the mat. Typically chemicals are applied uniformly to both sides of the mat. The wetted mat passes between a pair of rollers 128 which assist in distributing the chemicals uniformly through the mat. Other applicators may also, of course, be used.
  • the crosslinking substance is a liquid solution of any of a variety of crosslinking solutes known in the art. If required, the crosslinking substance can include a catalyst to accelerate the bonding reactions between molecules of the crosslinking substance and cellulose molecules. However, many if not most crosslinking substances do not require a catalyst.
  • crosslinking substances are selected from a group consisting of urea derivatives such as methylolated urea, methylolated cyclic ureas, methylolated lower alkyl substituted cyclic ureas, methylolated dihydroxy cyclic ureas, and mixtures thereof.
  • a specifically preferred crosslinking substance would be dimethyloldihydroxyethylene urea
  • crosslinking substances can be polycarboxylic acids, such as citric acid.
  • Crosslinking materials are known in the art, such as described in the previously mentioned Chung patent, U.S. Patent No. 4,935,022 to Lash, et al., U.S. Patent No. 4,889,595 to Herron, et al., U.S. Patent No. 3,819,470 to Shaw, et al., U.S. Patent No. 3,658,613 to Steijer, al., U.S. Patent No. 4,822,453 to Dean, et al., and U.S. Patent No. 4,853,086 to Graef, et al.
  • Suitable catalysts include acidic salts which can be useful when urea-based crosslinking substances are used. Such salts include ammonium chloride, ammonium sulfate, aluminum chloride, magnesium chloride, or mixtures of these or other similar compounds. Alkali metal salts of phosphorus-containing acids may also be used.
  • the crosslinking substance applied to the mat 114 is obtained from a supply 119 thereof, such as a tank or analogous vessel.
  • Crosslinkec cellulose fibers are individual fibers each comprised of multiple cellulose molecules where at least a portion of the hydroxyl groups on the cellulose molecules have been covalently bonded to hydroxyl groups on neighboring cellulose molecules in the same fiber via crosslinking reactions with extraneously added chemical reagents termed "crosslinking substances" or "crosslinking agents.”
  • crosslinking substances or "crosslinking agents.”
  • crosslinking agents are generally of the bifunctional type which create covalently bonded "bridges" between said neighboring hydroxyl groups.
  • each mat 114 of cellulosic fibers is conveyed by a conveying device 112, which carries the mats through the fiber treatment zone 116.
  • FIG. 3 also shows a further portion of one type of conveying device comprised of a first pair of rollers 126 and a second pair of rollers 128 for each mat 114.
  • the first and second pair of rollers 126, 128 are particularly effective for urging the corresponding mat at a substantially constant and controlled rate of speed.
  • C. Fiber Treatment Zone Each mat 114 is urged by the first and second pair of rollers 126, 128 through the fiber treatment zone 116 where the mat 114 is impregnated with a liquid crosslinking substance.
  • the crosslinking substance is preferably applied to one or both surfaces of the mat using any of a variety of methods known in the art useful for such a purpose, such as spraying, rolling, dipping, or analogous method. Combinations of spray and roller applicators can also be employed.
  • the crosslinking substance is typically applied in an amount ranging from about 2 kg to about 200 kg chemical per ton of cellulose fiber and preferably about 20 kg to about 100 kg chemical per ton of cellulose fiber.
  • Fiberizer 120 which serves to comminute one or more mats 130 impregnated with the crosslinking substance into individual substantially unbroken cellulose fibers comprising a fiber output.
  • a first conveyer fan 260 of conventional design can be utilized for propelling the fibers from the outlet 162 of the attrition device 132 through a conduit 262.
  • An optional component of the fiberizer 120 is a first cyclone 264 or similar apparatus known in the art, utilized in a conventional manner to concentrate the fibers passing out of the outlet 162 of the attrition device 132.
  • the first cyclone 264 receives the fibers through the conduit 262 coupled thereto.
  • a disk refiner 268 is another optional component of the fiberizer 120 which can be employed to effect additional separation of fibers (removal of knots) if required.
  • the disk refiner 268 is of a type known in the art and comprises a disk refiner inlet 270 and a disk refiner outlet 272.
  • a representative disk refiner 268 is type DM36 manufactured by Sprout-Bauer, Incorporated of Muncie, Pennsylvania. If the disk refiner 268 is used, the inlet 270 thereof is coupled via a conduit 274 to an outlet 276 of the first cyclone 264.
  • a second conveyor fan 278 may optionally be utilized to urge propagation of the fibers through a conduit 180 downstream of the disk refiner 268. Excess air can be recovered from the top 266 of the first cyclone 264 and routed via a conduit 281 to a tee 282 just upstream of the second conveyor fan 278.
  • fluff generator 290 Another optional component of the fiberizer 120 is a fluff generator 290 which receives the fibers from the optional second conveyor fan 278 through a conduit 284.
  • the fluff generator is described in detail below and in copending U.S. Patent Application Serial No. 07/607,157.
  • a preferred embodiment of the present apparatus 110 includes a dryer 122 which is utilized to perform two sequential functions: remove residual moisture from the fibers and cure the crosslinking agent.
  • the dryer 122 comprises a drying zone 373 for receiving fibers, e.g. from fluff generator outlet 304 and for removing residual moisture from the fibers via a "flash drying” method and a second drying zone 360, 362 for curing the crosslinking agent.
  • the curing starts in zone 360 and continues through zone 362.
  • zone 373 is coupled to the fluff generator outlet by a conduit 372 and to a source 374 of heated air, typically produced by combustion of a supply of natural gas 376 and fresh air 378.
  • the temperature of heated air is regulated to maintain the temperature of the drying zone 373 within a range of about 200° C to about 315° C.
  • the wet fibers comprising the fiber output are substantially instantaneously exposed to the high temperature in this zone.
  • Such rapid exposure to high temperature imparts a "flash drying" effect to the fibers, thereby causing rapid and thorough drying and separation of the fibers.
  • the passage time through the drying zone 373 is preferably less than one second.
  • the FIG. 3 embodiment shows that the first zone 360 is comprised of a first tower 364 comprised of a body portion 366, an inlet 368, and a first tower outlet 370.
  • the dryer zone 373 is coupled via a conduit 372 to the outlet of the fluff generator 290.
  • the first tower 364 is shown preferably coupled via a conduit 380 to a down tube 382, which is coupled via a conduit 384 to a third conveyor fan 386 located at an inlet 388 of a second tower 390.
  • the third conveyor fan 386 transports the fibers through the dryer which thereby pass into the second tower 390.
  • the fibers are lofted through the second tower 390, they are still exposed to a curing temperature within a range of about 140° C to about 180° C, which is sufficient to effect curing of the crosslinking agent without scorching the dry fibers.
  • the lofting keeps the fibers separated until the crosslinking reaction is complete.
  • the curing temperature depends upon the type of crosslinking material used to treat the fibers and also is set at a level so as to not scorch the fibers during curing. It should be noted that single stage dryers may also be used.
  • the dried and cured fibers exiting the dryer outlet of tower 390 have an extremely low level of nits and virtually no knots. Further, they are not discolored from scorching and the like, and have a median fiber length substantially unchanged from the median length of the fibers comprising the mat 14.
  • FIG. 3 also shows a second cyclone 400 of conventional design coupled via a conduit 402 to the outlet of tower 390, serving to concentrate the fibers passing therethrough in preparation for collection.
  • the resulting concentrated fibers can be collected using any of a number of collection devices 408 known in the art, such as fiber bagging devices.
  • non-woven fibrous mats were impregnated with a crosslinking agent, fiberized, dried, and cured using the apparatus as diagrammed schematically in FIG. 3.
  • a crosslinking agent fiberized, dried, and cured using the apparatus as diagrammed schematically in FIG. 3.
  • Two 52-inch-wide mats of southern pine kraft wood pulp fibers (type NB316 from Weyerhaeuser Company) and having a basis weight of 680 g/m 2 were fed to the apparatus.
  • the mats were impregnated using dimethyloldihydroxyethylene urea at a concentration of about 5%, applied over both sides of each mat using a combination of spray nozzles and impregnation rollers.
  • the loading level of crosslinking agent was about 4.5% w/w.
  • the treated fiber mats were fed at the rate of 8 meters/min to the attrition device 32.
  • the specific attrition device used in this example was equipped with six mat inlets and a rotor having 16 rows of hammers as described above around the circumference of the rotor.
  • the rotor had a diameter of 30 inches and was rotated at an angular velocity of 1200 rpm by an electric motor. Other rpm rates have also been tested and have proven satisfactory, including extremely high rpm rates.
  • Random samples of fibers were obtained from the output attrition device and observed for nits. These samples were 2.6 grams and were consistently observed to have fewer than three nits on the average with most samples having no nits. The attrition device was flushed with water once every sixteen hours for cleaning purposes.
  • a disk refiner was employed downstream of the attrition device. This specific disk refiner was a DM36 refiner as previously mentioned. A fluff generator as described in FIGS. 7—9 was also employed in this downstream of the disk refiner.
  • the temperature at the dryer input in this example was within the range of 200° C to 315° C.
  • the temperature at the second tower outlet was within the range of 140° C to 180° C.
  • Crosslinked fiber at the output of the dryer was produced at a rate of about 5000 pounds per hour.
  • the particle binders and particles of the present invention can be added before, after, or simultaneously with curing.
  • the term "curing in the presence of the binder" means that the binder is added before or simultaneously with curing.
  • Curing in the presence of the binder is not usually a problem because the binder cannot always participate in the intrafiber crosslinking reaction, and the binder is not affected by the curing step. In certain situations, however, the binder can also form covalent intrafiber crosslinks.
  • Polycarboxylic acids such as citric acid
  • polyols such as dipropylene glycol
  • polyamines such as ethylene diamine
  • Formation of the intrafiber covalent ester bond requires an anhydride intermediate. Formation of the anhydride intermediate can be inhibited by the presence of water.
  • the present inventors have found that about 20% water (more preferably at least 30% water) by weight in the fibers will sufficiently retard curing so that adequate binder functional groups will remain available in the fibers to bind the particles to the fibers.
  • the fibers should contain at least about 20% water by weight of the fibers when curing begins.
  • absorbent structures or articles may be made from the fibers, with binder and adhered particulates. These articles may be composite structures (e.g., made of plural materials) . For example, the articles may have a core of plural types of fibers, or fiber layers, with or without covering materials. These products are capable of absorbing significant quantities of water and other fluids, such as urine and other body fluids. Such products include, but are not limited to, disposable diapers, sanitary napkins, incontinent pads, towels and the like.
  • FIGS. 4—5 illustrate an absorbent pad structure which may be formed from fibers of the present invention, whether or not they are blended with other fibers. FIGS.
  • a pad having a cover sheet 414 and a backing sheet 416 may be formed, for example, by placing a square fiber piece cut from the sheet onto a corresponding precut backing sheet. A corresponding precut cover sheet is placed over the top of the fiber 418 on the backing sheet. This assembly may then be adhesively bonded around a continuous margin 420.
  • an absorbent structure in the form of a bandage is shown.
  • a bandage 430 for application to a wound to absorb blood and other bodily fluids is shown.
  • An absorbent pad 440 is securely mounted to an exterior or pad mounting surface 434 of a backing strip 436. Fibers 441 are contained in pad 440, and particles are attached to the fibers 441 in accordance with the present invention. Any suitable mounting or securing means may be used to affix pad 440 to the surface 434 of the strip 436. However, it is preferable for surface 434 to be coated with an adhesive so that the pad 440 may be adhesively mounted in place.
  • An exemplary adhesive is ethylene vinyl acetate adhesive.
  • the overall surface 438 of backing strip 436 is coated with a conventional adhesive.
  • Surface 438 is the surface which is affixed to the area of the skin surrounding the wound.
  • Conventional "peel-back" tabs may be used to protect the adhesive coating and pad 440 until the bandage is to be applied.
  • This type of backing strip is well known in the art.
  • the backing strip 436 may be of any known flexible material suitable for application to the skin. It is preferable for the strip 416 to be of a material which is impermeable to the passage of liquid so that fluid from a wound is contained by the bandage. However, the strip 436 may be apertured or otherwise breathable to permit air to reach the wound to promote the healing process.
  • a specific example of a suitable backing strip 436 is a polyethylene film.
  • the fibers 441 of such a bandage may be used in the fibers 441 of such a bandage.
  • the particles are adhered securely in place when the particles have a hydrogen bonding or a coordinate covalent bonding functionality, the fibers to which these particles are bound have a hydrogen bonding functionality, and wherein the binder is selected from the group consisting of a polypropylene glycol, a polypropylene glycol/polyethylene glycol copolymer, a polycarboxylic acid, such as polyacrylic acid, a poly(lactone) diol, such as poly(caprolactone) diol, a polyamide, a polyamine, a polysulfonic acid, a polysulfonate, polycarboxylate and combinations thereof.
  • the polymeric binder has a hydrogen bonding or a coordinate covalent bond forming functionality.
  • Nonpolymeric binders would include organic binders such as glycerin, monoglycerides, diglycerides, ascorbic acid, urea, glycine, pentaerythritol, a monosaccharide or a disaccharide, citric acid, tartaric acid, taurine, dipropylene glycol, and urea derivatives such as DMDHEU.
  • Suitable saccharides include glucose, sucrose, lactose, ribose, fructose, mannose, arabinose, and erythrose. Two different particles, such as different antimicrobials in particulate form, may be adhered to the same fiber.
  • each different type of antimicrobial particle or other particle may be adhered separately to different fibers.
  • blends of fibers may be included in absorbent structures such as pad 366.
  • these blends may include fibers with adhered antimicrobial (one or more antimicrobials) particles and adhered superabsorbent particles; fibers with one or more antimicrobial particles without superabsorbent particles blended with fibers having adhered superabsorbent particles with or without antimicrobial particles; and combinations of such fibers with untreated fibers and/or binder coated fibers without superabsorbent particles or antimicrobial particles.
  • other particles such as anticoagulants or hemostatics may be attached to the fibers.
  • the absorbent pad of bandage 430 may also include a cover sheet that is typically made of any suitable material which will readily permit the passage of liquid through the cover sheet to the fibers 441, such as nonwoven fiber webs of fibers such as, for example, rayon, nylon, polyester, propylene and blends thereof.
  • a cover sheet material is a 70 percent rayon/30 percent polyester blend having a basis weight of 18 g/m 2 from Scott Paper Company.
  • FIGS. 8 and 9 illustrate a conventional disposable diaper 550 with a core 552 which is comprised of fibers of the present invention with adhered superabsorbent particulate materials.
  • These particulate materials may be confined to a target zone (for example, the front or crotch portion of a diaper indicated at 556) or of a heavier concentration in the target zone. This can be accomplished by airlaying fibers of the present invention in such a zone.
  • the core may be activated by melting the binder or moistening the target zone with water.
  • the superabsorbent particles may be sprinkled on or otherwise applied to this wetted zone. As the zone dries, the particles are adhered in place.
  • the products such as described above, as well as webs of the fibers of the present invention, can also be densified by external application of pressure to the web.
  • the web could be densified by passing it through a set of calendar rolls set at 60 and 90 pli (pounds per linear inch, as in a calendar press) respectively to yield sheets with increased densities.
  • Densification may alternatively be provided by compaction rolls or presses. The inventors have found that densification is facilitated in SAP-containing products treated with binders of the present invention, when the densification occurs with the binder in an active state. Products that are treated with these binders require less heat and pressure than untreated fibers to densify to a given density.
  • Densification is preferably performed to produce a product that has a density of about 0.05 to 0.7 g/cc, more preferably 0.1 to 0.3 g/cc.
  • An example of densification using some of the binders of the present invention is given below: EXAMPLE 33
  • the products of the present invention can be formed into 550 gram/square meter sheets, six inches in diameter, in a laboratory padformer. Those pads are then passed through a set of calendar rolls set at 60 and 90 pli, respectively to yield sheets with densities of 0.3 and 0.5 g/cc.
  • EXAMPLE 34 A 50 gram amount of polypropylene glycol is diluted with 50 grams deionized water. The resulting solution is sprayed on 321 grams of an intrafiber crosslinked cellulose fluff (HBA pulp from Weyerhaeuser Company of Tacoma, WA) that was air entrained in a blender like mixing device. While the HBA fiber is still damp, 438 grams of IM 1000F (supplied by Hoechst- Celanese, of Portsmouth, Virginia) is added to the mixture. The resultant mixture is then vacuumed from the blender and spread on a counter to dry overnight. Then 550 gram/square meter handsheets, six inches in diameter, are made in a laboratory padformer.
  • HBA pulp HBA pulp from Weyerhaeuser Company of Tacoma, WA
  • IM 1000F supplied by Hoechst- Celanese, of Portsmouth, Virginia
  • pads are then pressed at 2000 and 3000 psi (or 60 and 90 pli in a calendar roll) , respectively, to yield sheets with densities of 0.3 and 0.5 g/cc.
  • pads of untreated HBA pulp blended with 45% IM 1000F would require heating to 100° C and pressures between 8,000 and 11,000 psi to produce pads of similar densities.
  • HBA pulp with 40% IMIOOOF and HBA pulp with 12% glycerin and 40% IMIOOOF were formed into six-inch pads in the padformer then pressed at about 6500 psi for 15 seconds.
  • HBA pulp without glycerin binder reached a density of 0.4 g/cc
  • HBA pulp with glycerin bound particles reached a density of 0.57 g/cc.
  • This example illustrates that fibers treated with the method of the present invention achieve a greater density than untreated fibers at the same compression pressure.
  • XXII Water Addition
  • a crosslinking material is added to the fibers and cured to form intrafiber covalent bonds that produce high bulk fibers.
  • crosslinking material and binder are the same (for example, a polycarboxylic acid) , or are both different but capable of intrafiber crosslinking, and the binder is added before curing occurs, substantially all of the crosslinking material/binder will be used in the covalent crosslinking reaction, such that none will be available for subsequent binding of the particles to the fibers with hydrogen bonds and coordinate covalent bonds.
  • water may be added to the fibers before curing to retard initiation of the curing step and ensure that a portion of the binder's functionality is not consumed in the crosslinking reaction. At least 20% water by weight in the fibers sufficiently retards intrafiber covalent bond formation to allow residual polycarboxylic acid on the fibers to bind the particles to the fibers. The following example illustrates this process.
  • EXAMPLE 36 A 100 gram pulp sheet was sprayed with 44.5% intrafiber crosslinking material, and the pulp sheet was then delaminated and fed in small bits into a padformer while adding superabsorbent particles to delaminated pulp sheet at the same time. The material was run a second time through the padformer to fluff it up, and the material was then subsequently cured for 20 minutes in an oven at 150° C.
  • the crosslinking material was a modified ethylene urea and citric acid, while the particulate material was IMIOOOF.
  • To the 100 g pulp sheet was added 63.4 grams of the ethylene urea, 16.76 grams citric acid, and 70 grams of IM1000F, for a final crosslinker content of 35.2% ethylene urea and 9.3% citric acid, by weight. No water was added in this run.
  • the 100 gram pulp sheet was crosslinked with 30.83 grams of a polyaldehyde (glyoxal) , 5.03 grams of a glycol, 0.2 grams alum, 0.2 grams citric acid, and 15 grams distilled water. Curing was performed after 70 grams of IMIOOOF SAP was added to the pad.
  • a polyaldehyde glycoxal
  • Electron microscopic examination of the fibers from these runs showed that particle bonding did not occur in the absence of the 50 g water addition. In the presence of 50 grams distilled water, however, electromicroscopic data showed actual bonding of the particles to the fibers.
  • FIG. 10 shows an isolated, enlarged cellulose fiber 600 with SAP particles 602 bound to it by a binder of the present invention.
  • This drawing illustrates an example of the SAP retaining its discrete particulate form following binding to the fibers.
  • Some particle to particle fusion may occur in accordance with this invention, but maintenance of a discrete particulate form excludes formation of a completely confluent film in which the particles lose their particulate identity.
  • Such a confluent film produces gel blocking that interferes with efficient liquid absorption into the fibers.
  • the shown fiber 600 is elongated, and has an aspect ratio (ratio of length to width) of about 10:1 to 5:1, preferably about 10:1.
  • FIG. 11 shows the particles 602 distributed substantially uniformly throughout the depth 604 of a pad 606.
  • the particles are also shown adhering to all the surfaces of the pad.
  • Particles may be distributed in any desired pattern throughout the pad in accordance with this invention, and need not necessarily adhere to all surfaces or be distributed throughout the volume of the mat, or distributed uniformly.
  • the particles are not encapsulated by the binders.
  • the particles and fibers of the present invention are not encapsulated with the binder.
  • the binder does not agglomerate the fibers together, and in many embodiments does not bind fibers to each other. Discrete individual particles retain their identity on the surface of the fibers, instead of being subsumed in a thermoplastic encasement around the fiber and particle.
  • XXIV. Electron Photomicrographs An electron photomicrograph of superabsorbent particles (SAP) bound to cellulose fibers with an ascorbic acid binder is shown in FIG. 12.
  • SAP superabsorbent particles
  • the SAP is at the left margin of the photograph, and is bound to the fiber which occupies the central portion of the photomicrograph.
  • the particle is seen to be bound to the fiber, and the fiber has undergone some shear damage that resulted in a fracture of the fiber. It is significant that the fiber has experienced shear damage while the particle has remained bound to the fiber, because this indicates that the particle-fiber bond formed by the ascorbic acid is very strong and resilient, resisting mechanical disruption.
  • FIGS. 13A, 13B, 13C and 13D show several electron photomicrographs that illustrate individual particles bound to fibers with a lactose binder.
  • FIG. 13C shows that SAP retains its individual particulate form when adhered to the fiber with a lactose binder. The particles do not form a fused confluent mass without particulate identity.
  • FIG. 14 An electron photomicrograph of oxalic acid particles bound to cellulose fibers with a glycerin binder is shown in FIG. 14.
  • the bound oxalic acid is near the center of the photograph, and is seen bound to the fiber without mechanical encapsulation of the fiber and particle by an encapsulating binder.
  • FIG. 15 is an SEM illustrating a particle of aluminum sulfate (alum) bound to a cellulose fiber with a glycerin binder.
  • the alum particle is seen at the center of the photograph, and the particle retains its individual particulate form when adhered to the fiber.
  • the particles do not form a confluent mass lacking particulate identity.
  • the particles are not encapsulated by a material that mechanically holds the particle in contact with the fiber.
  • the fibers of the present invention can be mixed with other types of fibers, such as that disclosed in U.S. Patent No. 5,057,166.
  • the latex coated fibers of that patent can be mixed with the fibers of the present invention to produce an absorbent product that has characteristics of both types of fibers.
  • U.S. Patent No. 3,903,889 discloses a process for adhering absorbent particles to pulp fibers using syrup, honey, and other polysaccharides such as dextrins.
  • An essential requirement of these adhesive agents is that they must possess the property of being permanently pliable, and not rigidifying into a brittle film.
  • the binders of the present invention in contrast, are capable of functioning as a binder after solidifying into a rigid crystalline material. Even the binders of the present invention that do not rigidify into a solid (such as glycerin and PPG) are very hygroscopic, and can be present on fibers having a total water content of no more than 15%, or even 12%.
  • polysaccharides such as corn syrup, honey and dextrins
  • binders are excluded as binders from some embodiments of the invention because they remain tacky upon drying. Tacky binders make processing the binder- coated fibers difficult.
  • the polysaccharide polymers are also excluded from nonpolymeric embodiments of the binder of the present invention.
  • the nonpolymeric saccharides such as monosaccharides and disaccharides, lack the high viscosity and tacky- adhesive physical properties of polysaccharides such as corn syrup and honey.
  • the nonpolymeric saccharides of the present invention may be solids, which avoid the viscosity and handling problems associated with polymers.
  • a particle that is soluble in water will completely dissolve at least lOg of the particle in 300 ml water at 25° C.
  • a particle that is sparingly soluble in the binder will completely dissolve no more than about 5 g of the particle in 300 ml of the binder at 25° C.
  • Some of the binders of the present invention are also water soluble.
  • a binder that is soluble in water will completely dissolve at least 10 g of the binder in 300 ml water at 25° C.

Landscapes

  • Engineering & Computer Science (AREA)
  • Textile Engineering (AREA)
  • Health & Medical Sciences (AREA)
  • Life Sciences & Earth Sciences (AREA)
  • Public Health (AREA)
  • Animal Behavior & Ethology (AREA)
  • General Health & Medical Sciences (AREA)
  • Veterinary Medicine (AREA)
  • Chemical & Material Sciences (AREA)
  • Vascular Medicine (AREA)
  • Heart & Thoracic Surgery (AREA)
  • Biomedical Technology (AREA)
  • Epidemiology (AREA)
  • Dispersion Chemistry (AREA)
  • Hematology (AREA)
  • Materials Engineering (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • General Chemical & Material Sciences (AREA)
  • Wood Science & Technology (AREA)
  • Manufacturing & Machinery (AREA)
  • Forests & Forestry (AREA)
  • Treatments For Attaching Organic Compounds To Fibrous Goods (AREA)
  • Nonwoven Fabrics (AREA)
  • Absorbent Articles And Supports Therefor (AREA)
  • Chemical Or Physical Treatment Of Fibers (AREA)
  • Solid-Sorbent Or Filter-Aiding Compositions (AREA)
  • Yarns And Mechanical Finishing Of Yarns Or Ropes (AREA)
  • Manufacturing Of Micro-Capsules (AREA)
  • Polyurethanes Or Polyureas (AREA)
  • Processes Of Treating Macromolecular Substances (AREA)
  • Glanulating (AREA)
PCT/US1993/007781 1992-08-17 1993-08-16 Particle binders WO1994004352A1 (en)

Priority Applications (9)

Application Number Priority Date Filing Date Title
EP93920180A EP0655971B2 (en) 1992-08-17 1993-08-16 Method of binding particles to fibers
BR9306921A BR9306921A (pt) 1992-08-17 1993-08-16 Processo para ligar partículas a fibras com um aglutinante e produto fibroso
AT93920180T ATE224808T1 (de) 1992-08-17 1993-08-16 Verfahren zum binden von partikeln an fasern
CA002140263A CA2140263C (en) 1992-08-17 1993-08-16 Particle binders
ES93920180T ES2181693T5 (es) 1992-08-17 1993-08-16 Metodo de union de particulas de fibras.
AU50199/93A AU5019993A (en) 1992-08-17 1993-08-16 Particle binders
DE69332336T DE69332336T3 (de) 1992-08-17 1993-08-16 Verfahren zum binden von partikeln an fasern
JP50651494A JP3539957B2 (ja) 1992-08-17 1993-08-16 粒子バインダー
KR1019950700602A KR950702910A (ko) 1992-08-17 1995-02-16 입자 결합제

Applications Claiming Priority (12)

Application Number Priority Date Filing Date Title
US931,284 1992-08-17
US931,059 1992-08-17
US931,279 1992-08-17
US07/931,059 US5543215A (en) 1992-08-17 1992-08-17 Polymeric binders for binding particles to fibers
US931,277 1992-08-17
US07/931,284 US5308896A (en) 1992-08-17 1992-08-17 Particle binders for high bulk fibers
US07/931,279 US5589256A (en) 1992-08-17 1992-08-17 Particle binders that enhance fiber densification
US931,213 1992-08-17
US07/931,277 US5538783A (en) 1992-08-17 1992-08-17 Non-polymeric organic binders for binding particles to fibers
US07/931,278 US5352480A (en) 1992-08-17 1992-08-17 Method for binding particles to fibers using reactivatable binders
US07/931,213 US5300192A (en) 1992-08-17 1992-08-17 Wet laid fiber sheet manufacturing with reactivatable binders for binding particles to fibers
US931,278 1992-08-17

Publications (1)

Publication Number Publication Date
WO1994004352A1 true WO1994004352A1 (en) 1994-03-03

Family

ID=27560346

Family Applications (2)

Application Number Title Priority Date Filing Date
PCT/US1993/007780 WO1994004351A1 (en) 1992-08-17 1993-08-16 Particle binding to fibers
PCT/US1993/007781 WO1994004352A1 (en) 1992-08-17 1993-08-16 Particle binders

Family Applications Before (1)

Application Number Title Priority Date Filing Date
PCT/US1993/007780 WO1994004351A1 (en) 1992-08-17 1993-08-16 Particle binding to fibers

Country Status (12)

Country Link
US (10) US5693411A (US06596103-20030722-C00008.png)
EP (4) EP1217120A1 (US06596103-20030722-C00008.png)
JP (2) JP3497166B2 (US06596103-20030722-C00008.png)
KR (2) KR950702909A (US06596103-20030722-C00008.png)
AT (3) ATE280264T1 (US06596103-20030722-C00008.png)
AU (2) AU5019893A (US06596103-20030722-C00008.png)
BR (2) BR9306920A (US06596103-20030722-C00008.png)
CA (2) CA2140264C (US06596103-20030722-C00008.png)
DE (3) DE69332336T3 (US06596103-20030722-C00008.png)
ES (3) ES2181693T5 (US06596103-20030722-C00008.png)
NZ (2) NZ255814A (US06596103-20030722-C00008.png)
WO (2) WO1994004351A1 (US06596103-20030722-C00008.png)

Cited By (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO1995019191A1 (en) * 1994-01-12 1995-07-20 Weyerhaeuser Company Method and compositions for enhancing blood absorbence by absorbent materials
WO1995022655A1 (en) * 1994-02-16 1995-08-24 Weyerhaeuser Company Densifying agents for enhancing fiber densification
WO1996031644A1 (en) * 1995-04-04 1996-10-10 Weyerhaeuser Company Binder treated fibrous webs and products
US5800418A (en) * 1994-12-09 1998-09-01 The Procter & Gamble Company Absorbent composites and absorbent articles containing the same
US5853867A (en) * 1995-09-14 1998-12-29 Nippon Shokubai Co., Ltd. Absorbent composite, method for production thereof, and absorbent article
US6533978B1 (en) 2000-08-03 2003-03-18 Kimberly-Clark Worldwide, Inc. Process and apparatus for forming a stabilized absorbent web
US6533989B1 (en) 2000-08-03 2003-03-18 Kimberly-Clark Worldwide, Inc. Multi-chamber process and apparatus for forming a stabilized absorbent web
WO2003104543A1 (de) * 2002-06-11 2003-12-18 Basf Aktiengesellschaft Verfahren zum binden von teilchenförmigen, wasserabsorbierenden, säuregruppen enthaltenden polymeren an ein trägermaterial
US10702419B2 (en) 2012-07-30 2020-07-07 Kci Licensing, Inc. Incisional absorbent dressing

Families Citing this family (216)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5998032A (en) 1992-08-17 1999-12-07 Weyerhaeuser Company Method and compositions for enhancing blood absorbence by superabsorbent materials
ES2181693T5 (es) 1992-08-17 2006-05-16 Weyerhaeuser Company Metodo de union de particulas de fibras.
US6391453B1 (en) 1992-08-17 2002-05-21 Weyernaeuser Company Binder treated particles
US6340411B1 (en) 1992-08-17 2002-01-22 Weyerhaeuser Company Fibrous product containing densifying agent
JP4045365B2 (ja) * 1993-11-15 2008-02-13 株式会社日本吸収体技術研究所 抗菌性複合不織布およびその製造方法
WO1996015301A1 (en) * 1994-11-10 1996-05-23 Weyerhaeuser Company Densified cellulose fiber pads and method of making the same
US5660854A (en) * 1994-11-28 1997-08-26 Haynes; Duncan H Drug releasing surgical implant or dressing material
DE19505708A1 (de) * 1995-02-20 1996-08-22 Stockhausen Chem Fab Gmbh Flächenförmige, superabsorbierende Gebilde
US7214847B1 (en) 1997-09-22 2007-05-08 Argentum Medical, L.L.C. Multilayer conductive appliance having wound healing and analgesic properties
US8455710B2 (en) * 1997-09-22 2013-06-04 Argentum Medical, Llc Conductive wound dressings and methods of use
US6861570B1 (en) * 1997-09-22 2005-03-01 A. Bart Flick Multilayer conductive appliance having wound healing and analgesic properties
US8801681B2 (en) * 1995-09-05 2014-08-12 Argentum Medical, Llc Medical device
US5814094A (en) 1996-03-28 1998-09-29 Becker; Robert O. Iontopheretic system for stimulation of tissue healing and regeneration
US5624303A (en) * 1996-01-22 1997-04-29 Micron Technology, Inc. Polishing pad and a method for making a polishing pad with covalently bonded particles
JP3822329B2 (ja) * 1996-10-15 2006-09-20 キレスト株式会社 金属キレート形成能を有する繊維およびその製法、並びに該繊維を用いた金属イオン捕捉法
CA2275605A1 (en) * 1996-12-20 1998-07-02 The Procter & Gamble Company A dry laid structure comprising particulate material
EP0850616A1 (en) * 1996-12-20 1998-07-01 The Procter & Gamble Company A dry laid structure comprising odour control means
US5780088A (en) 1997-01-17 1998-07-14 David R. Zittel Electric motor driven abrasive roller peeler and cleaning machine
EP1260626A3 (en) * 1997-01-28 2002-12-11 Camelot Superabsorbents Ltd Process for bonding fibrous web
US5795439A (en) * 1997-01-31 1998-08-18 Celanese Acetate Llc Process for making a non-woven, wet-laid, superabsorbent polymer-impregnated structure
US5760052A (en) * 1997-02-06 1998-06-02 Peacock; Robert Composition for use as a fungistat and for the treatment of fungal infections
US5792513A (en) * 1997-03-07 1998-08-11 Koslow Technologies Corporation Continuous solid state web coating process
DE69819321T2 (de) * 1997-04-22 2004-07-22 Chelest Corp. Metallchelatbildende fasern, verfahren zu deren herstellung und verfahren zum binden von metallen und daraus hergestellte filter
US6599631B2 (en) * 2001-01-26 2003-07-29 Nanogram Corporation Polymer-inorganic particle composites
US7226966B2 (en) 2001-08-03 2007-06-05 Nanogram Corporation Structures incorporating polymer-inorganic particle blends
EP0898950A1 (en) * 1997-08-27 1999-03-03 The Procter & Gamble Company Disposable absorbent article having a dilatant behaviour
US20030187102A1 (en) 1997-09-02 2003-10-02 Marshall Medoff Compositions and composites of cellulosic and lignocellulosic materials and resins, and methods of making the same
US20050084671A1 (en) * 1997-09-02 2005-04-21 Xyleco, Inc., A Massachusetts Corporation Texturized fibrous materials from poly-coated paper and compositions and composites made therefrom
US6623576B2 (en) 1998-10-28 2003-09-23 Basf Aktiengesellschaft Continuous manufacture of superabsorbent/ion exchange sheet material
US6342298B1 (en) 1997-11-19 2002-01-29 Basf Aktiengesellschaft Multicomponent superabsorbent fibers
US6072101A (en) 1997-11-19 2000-06-06 Amcol International Corporation Multicomponent superabsorbent gel particles
US6222091B1 (en) 1997-11-19 2001-04-24 Basf Aktiengesellschaft Multicomponent superabsorbent gel particles
BR9814329A (pt) * 1997-12-23 2003-02-18 Kimberly Clark Co Processo para produzir um composto absorvente expansìvel para produto de higiene pessoal
US5938995A (en) * 1998-02-06 1999-08-17 Air Products And Chemicals, Inc. Compression resistant cellulosic-based fabrics having high rates of absorbency
US6153207A (en) * 1998-03-05 2000-11-28 Pugliese; Peter T. Anti-cellulite pantyhose
US6632209B1 (en) * 1998-03-30 2003-10-14 Paragon Trade Brands, Inc. Thin absorbent core made from folded absorbent laminate
US6068620A (en) 1998-03-30 2000-05-30 Paragon Trade Brands Absorbent laminate
US6162961A (en) * 1998-04-16 2000-12-19 Kimberly-Clark Worldwide, Inc. Absorbent article
US6403857B1 (en) 1998-06-08 2002-06-11 Buckeye Technologies Inc. Absorbent structures with integral layer of superabsorbent polymer particles
US6479415B1 (en) 1998-06-08 2002-11-12 Bki Holding Corporation Absorbent structures having fluid acquisition and distribution layer
US7045673B1 (en) * 1998-12-08 2006-05-16 Quick-Med Technologies, Inc. Intrinsically bactericidal absorbent dressing and method of fabrication
AU2176600A (en) 1998-12-10 2000-06-26 Kimberly-Clark Worldwide, Inc. An absorbent structure including a thin, calendered airlaid composite and a process for making the composite
US6368609B1 (en) 1999-04-12 2002-04-09 Kimberly-Clark Worldwide, Inc. Absorbent structure including a thin, calendered airlaid composite and a process for making the composite
US6344109B1 (en) 1998-12-18 2002-02-05 Bki Holding Corporation Softened comminution pulp
US6562743B1 (en) 1998-12-24 2003-05-13 Bki Holding Corporation Absorbent structures of chemically treated cellulose fibers
KR20010104385A (ko) * 1999-04-06 2001-11-24 추후기재 악취 방지성 위생 흡수재
US6540792B1 (en) * 1999-04-14 2003-04-01 Toray Industries, Inc. Cellulose fiber-containing structure
US6300259B1 (en) 1999-04-26 2001-10-09 Weyerhaeuser Company Crosslinkable cellulosic fibrous product
US6281407B1 (en) * 1999-05-28 2001-08-28 Kimberly-Clark Worldwide, Inc. Personal care product containing a product agent
US6215038B1 (en) * 1999-05-28 2001-04-10 Kimberly-Clark Worldwide, Inc. Diaper with osmotic pressure control
US6613955B1 (en) 1999-10-01 2003-09-02 Kimberly-Clark Worldwide, Inc. Absorbent articles with wicking barrier cuffs
US6486379B1 (en) 1999-10-01 2002-11-26 Kimberly-Clark Worldwide, Inc. Absorbent article with central pledget and deformation control
US6492574B1 (en) 1999-10-01 2002-12-10 Kimberly-Clark Worldwide, Inc. Center-fill absorbent article with a wicking barrier and central rising member
US6660903B1 (en) 1999-10-01 2003-12-09 Kimberly-Clark Worldwide, Inc. Center-fill absorbent article with a central rising member
US6764477B1 (en) 1999-10-01 2004-07-20 Kimberly-Clark Worldwide, Inc. Center-fill absorbent article with reusable frame member
US6700034B1 (en) 1999-10-01 2004-03-02 Kimberly-Clark Worldwide, Inc. Absorbent article with unitary absorbent layer for center fill performance
US6534554B1 (en) 1999-10-27 2003-03-18 Basf Aktiengesellschaft Multicomponent ion exchange resins
US6949143B1 (en) * 1999-12-15 2005-09-27 Applied Materials, Inc. Dual substrate loadlock process equipment
WO2001047569A1 (en) * 1999-12-28 2001-07-05 Kimberly-Clark Worldwide, Inc. Superabsorbent polymers
WO2001047568A1 (en) * 1999-12-28 2001-07-05 Kimberly-Clark Worldwide, Inc. Fibrous materials
US6677256B1 (en) 1999-12-28 2004-01-13 Kimberly-Clark Worldwide, Inc. Fibrous materials containing activating agents for making superabsorbent polymers
AUPQ544900A0 (en) * 2000-02-04 2000-02-24 Commonwealth Scientific And Industrial Research Organisation Treatment of cellulosic material
US20050054532A1 (en) * 2000-05-11 2005-03-10 Jean Kocur Combination of crop protection agents with hydrogen bond-forming polymers
US7687681B2 (en) 2000-05-26 2010-03-30 Kimberly-Clark Worldwide, Inc. Menses specific absorbent systems
US7147898B2 (en) * 2000-10-25 2006-12-12 Synergistic Ventures, Inc. Highly absorbent products and process of making such products
WO2002055774A2 (en) * 2000-11-14 2002-07-18 Weyerhaeuser Co Crosslinked cellulosic product formed by extrusion process
US6749721B2 (en) * 2000-12-22 2004-06-15 Kimberly-Clark Worldwide, Inc. Process for incorporating poorly substantive paper modifying agents into a paper sheet via wet end addition
JP4339593B2 (ja) * 2001-02-21 2009-10-07 コロプラスト アクティーゼルスカブ 接着剤組成物
US6620293B2 (en) * 2001-04-11 2003-09-16 Rayonier Inc. Crossed-linked pulp and method of making same
WO2002084017A1 (en) * 2001-04-12 2002-10-24 Firstex L.L.C. Functional treatment of textile materials
US20020176964A1 (en) * 2001-05-24 2002-11-28 Koslow Technologies Corp. Rapid absorbent structures
GB0117522D0 (en) * 2001-07-19 2001-09-12 Procter & Gamble Solvent welding process
US20030144379A1 (en) * 2001-08-22 2003-07-31 Mitchell Michael A. Multicomponent superabsorbent gel particles
DE60229698D1 (de) * 2001-09-06 2008-12-18 Japan Vilene Co Ltd Verfahren und Vorrichtung zur Herstellung von Fasern und Vlies, welche Feststoffpartikel enthalten
ATE406986T1 (de) * 2001-10-29 2008-09-15 Shinji Gotou Verfahren zur herstellung von recyceltem bauholz
US7351373B2 (en) * 2001-11-13 2008-04-01 Gebrueder Loedige Maschinebau-Gesellschaft Mbh Method for the oxidative treatment of bulk material
US6809231B2 (en) * 2001-11-21 2004-10-26 The United States Of America As Represented By The Secretary Of Agriculture Flexible and absorbent alginate wound dressing
US20030129915A1 (en) * 2002-01-04 2003-07-10 Tyco Healthcare Retail Services Ag Process for making a super absorbent polymer-impregnated non-woven absorbent core for personal hygiene products
US20050101929A1 (en) * 2002-01-17 2005-05-12 Andrew Waksmundzki Absorbent core with three-dimensional sub-layer
US20050107759A1 (en) * 2002-01-17 2005-05-19 Andrew Waksmundzki Absorbent article with three-dimensional extrudate forming sap containment wells
US20030236512A1 (en) * 2002-06-19 2003-12-25 Baker Andrew A. Absorbent core with folding zones for absorbency distribution
EP1382730A1 (de) * 2002-07-15 2004-01-21 Paul Hartmann AG Kosmetisches Wattepad
US6822135B2 (en) * 2002-07-26 2004-11-23 Kimberly-Clark Worldwide, Inc. Fluid storage material including particles secured with a crosslinkable binder composition and method of making same
US7297395B2 (en) * 2002-07-30 2007-11-20 Kimberly-Clark Worldwide, Inc. Superabsorbent materials having low, controlled gel-bed friction angles and composites made from the same
US20040023589A1 (en) * 2002-07-30 2004-02-05 Kainth Arvinder Pal Singh Superabsorbent materials having high, controlled gel-bed friction angles and composites made from the same
US20040023579A1 (en) * 2002-07-30 2004-02-05 Kainth Arvinder Pal Singh Fiber having controlled fiber-bed friction angles and/or cohesion values, and composites made from same
US20040044320A1 (en) * 2002-08-27 2004-03-04 Kainth Arvinder Pal Singh Composites having controlled friction angles and cohesion values
TW200412890A (en) * 2002-09-05 2004-08-01 Novalabs L L C Toilet cleaning apparatus and caddy
US20040058605A1 (en) * 2002-09-19 2004-03-25 Hansen Michael R. Polysaccharide treated cellulose fibers
US6916402B2 (en) * 2002-12-23 2005-07-12 Kimberly-Clark Worldwide, Inc. Process for bonding chemical additives on to substrates containing cellulosic materials and products thereof
US6939492B2 (en) * 2002-12-26 2005-09-06 Kimberly-Clark Worldwide, Inc. Method for making fibrous web materials
US6936136B2 (en) * 2002-12-31 2005-08-30 Kimberly-Clark Worldwide, Inc. Amino-functionalized pulp fibers
US20050000669A1 (en) * 2003-03-14 2005-01-06 Hugh West Saccharide treated cellulose pulp sheets
US7022756B2 (en) * 2003-04-09 2006-04-04 Mill's Pride, Inc. Method of manufacturing composite board
US20040253428A1 (en) * 2003-06-12 2004-12-16 General Electric Company Weatherable multilayer articles and method for their preparation
US20040253440A1 (en) * 2003-06-13 2004-12-16 Kainth Arvinder Pal Singh Fiber having controlled fiber-bed friction angles and/or cohesion values, and composites made from same
US20040253890A1 (en) * 2003-06-13 2004-12-16 Ostgard Estelle Anne Fibers with lower edgewise compression strength and sap containing composites made from the same
US20050010183A1 (en) * 2003-06-24 2005-01-13 Weyerhaeuser Company Absorbent structure for absorbing blood
DE10328567A1 (de) * 2003-06-24 2005-01-20 Saueressig Gmbh + Co. Verfahren zum Herstellen eines absorberhaltigen Faserproduktes
US7311968B2 (en) * 2004-06-30 2007-12-25 The Procter & Gamble Company Absorbent structures comprising coated super-absorbent polymer particles
US7175741B2 (en) * 2003-07-16 2007-02-13 Weyerhaeuser, Co. Reducing odor in absorbent products
US20050031841A1 (en) * 2003-08-05 2005-02-10 Weyerhaeuser Company Attachment of superabsorbent materials to fibers using oil
US20050045296A1 (en) * 2003-08-29 2005-03-03 Adam Gabriel Hammam Stabilized absorbent composite material and method for making
EP1518567B1 (en) * 2003-09-25 2017-06-28 The Procter & Gamble Company Absorbent articles comprising fluid acquisition zones with coated superabsorbent particles
US7195695B2 (en) * 2003-10-02 2007-03-27 Rayonier Products & Financial Services Company Cross-linked cellulose fibers and method of making same
US20050079361A1 (en) * 2003-10-14 2005-04-14 Hamed Othman A. Materials useful in making cellulosic acquisition fibers in sheet form
US7186318B2 (en) 2003-12-19 2007-03-06 Kimberly-Clark Worldwide, Inc. Soft tissue hydrophilic tissue products containing polysiloxane and having unique absorbent properties
US20050133180A1 (en) * 2003-12-19 2005-06-23 Hugh West Densification agent and oil treated cellulose fibers
US7479578B2 (en) 2003-12-19 2009-01-20 Kimberly-Clark Worldwide, Inc. Highly wettable—highly flexible fluff fibers and disposable absorbent products made of those
US7811948B2 (en) 2003-12-19 2010-10-12 Kimberly-Clark Worldwide, Inc. Tissue sheets containing multiple polysiloxanes and having regions of varying hydrophobicity
US7147752B2 (en) 2003-12-19 2006-12-12 Kimberly-Clark Worldwide, Inc. Hydrophilic fibers containing substantive polysiloxanes and tissue products made therefrom
EP1696972B1 (en) * 2003-12-19 2016-10-26 Buckeye Technologies Inc. Fibers of variable wettability and materials containing the fibers
US20050142965A1 (en) * 2003-12-29 2005-06-30 Kimberly-Clark Worldwide, Inc. Surface charge manipulation for improved fluid intake rates of absorbent composites
US20050143571A1 (en) * 2003-12-30 2005-06-30 Weyerhaeuser Company Method for forming individualized intrafiber crosslinked cellulosic fibers with improved brightness and color
US20050145350A1 (en) * 2003-12-30 2005-07-07 Weyerhaeuser Company Individualized intrafiber crosslinked cellulosic fibers with improved brightness and color
US20050178518A1 (en) * 2004-02-13 2005-08-18 Hugh West Sodium sulfate treated pulp
US20070190125A1 (en) 2004-03-03 2007-08-16 Constantine Georgiades Positioning feature for aiding use of film or strip product
US7842382B2 (en) 2004-03-11 2010-11-30 Knauf Insulation Gmbh Binder compositions and associated methods
US20050217812A1 (en) * 2004-03-31 2005-10-06 Weyerhaeuser Company Bleached crosslinked cellulosic fibers with high color and brightness
CN101022773B (zh) * 2004-09-16 2010-06-16 麦克内尔-Ppc股份有限公司 可悬垂的吸收性卫生巾
US20060069367A1 (en) * 2004-09-29 2006-03-30 Andrew Waksmundzki Absorbent core having two or more types of superabsorbent
US20060069375A1 (en) * 2004-09-29 2006-03-30 Andrew Waksmundzki Absorbent article with C-folded moisture barrier and methods of manufacturing same
US20060070712A1 (en) * 2004-10-01 2006-04-06 Runge Troy M Absorbent articles comprising thermoplastic resin pretreated fibers
AU2005294611B2 (en) * 2004-10-05 2011-10-06 Fallbrook Intellectual Property Company Llc Continuously variable transmission
US8603631B2 (en) 2004-10-13 2013-12-10 Knauf Insulation Gmbh Polyester binding compositions
US7846005B2 (en) * 2004-11-05 2010-12-07 Hbi Branded Apparel Enterprises, Llc Molded non-woven fabrics and methods of molding
US20060100338A1 (en) * 2004-11-08 2006-05-11 Akzo Nobel N.V. Pigment composition
US20060112855A1 (en) * 2004-11-08 2006-06-01 Akzo Nobel N.V. Pigment composition
US20060099408A1 (en) * 2004-11-08 2006-05-11 Akzo Nobel N.V. Pigment composition
US7670459B2 (en) 2004-12-29 2010-03-02 Kimberly-Clark Worldwide, Inc. Soft and durable tissue products containing a softening agent
WO2006076191A2 (en) * 2005-01-10 2006-07-20 Elc Management Llc Discontinuous surface coating for particles
DK2564931T3 (da) 2005-03-24 2014-08-25 Xyleco Inc Fremgangsmåder til fremstilling af fibrøse materialer
US7708214B2 (en) 2005-08-24 2010-05-04 Xyleco, Inc. Fibrous materials and composites
US20150328347A1 (en) 2005-03-24 2015-11-19 Xyleco, Inc. Fibrous materials and composites
ES2942678T3 (es) 2005-07-26 2023-06-05 Knauf Insulation Gmbh Aglutinantes y materiales fabricados con los mismos
GB0520336D0 (en) * 2005-10-06 2005-11-16 Urgo Ltd Method of making a bandage
US7745685B2 (en) * 2005-10-31 2010-06-29 Kimberly-Clark Worldwide, Inc. Absorbent articles with improved odor control
US20070116890A1 (en) * 2005-11-21 2007-05-24 Honeywell International, Inc. Method for coating turbine engine components with rhenium alloys using high velocity-low temperature spray process
US7921578B2 (en) * 2005-12-30 2011-04-12 Whirlpool Corporation Nebulizer system for a fabric treatment appliance
SE531569C2 (sv) * 2006-09-19 2009-05-26 Centri Ab Protesprodukt med kompositmaterialvägg, samt metod för framställning av protesprodukten
US9078785B2 (en) * 2006-11-28 2015-07-14 Synergistic Ventures, Inc. Absorbent product and method of making
US9578820B2 (en) 2006-11-28 2017-02-28 Jeno Muthiah Watering systems
US7972691B2 (en) * 2006-12-22 2011-07-05 Nanogram Corporation Composites of polymers and metal/metalloid oxide nanoparticles and methods for forming these composites
BRPI0721232B1 (pt) 2007-01-25 2023-01-24 Knauf Insulation Limited Placa de madeira compósita
SI2126179T1 (sl) 2007-01-25 2014-12-31 Knauf Insulation Izolacijski proizvod na osnovi mineralnih vlaken brez formaldehida
EP2125650B1 (en) 2007-01-25 2024-05-15 Knauf Insulation Mineral fibre board
PL2108006T3 (pl) 2007-01-25 2021-04-19 Knauf Insulation Gmbh Spoiwa i wytworzone z nich materiały
US8119233B2 (en) * 2007-02-17 2012-02-21 Nanogram Corporation Functional composites, functional inks and applications thereof
WO2008127936A2 (en) 2007-04-13 2008-10-23 Knauf Insulation Gmbh Composite maillard-resole binders
EP2158266B1 (de) * 2007-06-13 2011-08-31 Basf Se Verfahren zur herstellung von formkörpern
WO2008157033A1 (en) 2007-06-20 2008-12-24 Mcneil-Ppc, Inc Products for whitening teeth
GB0715100D0 (en) 2007-08-03 2007-09-12 Knauf Insulation Ltd Binders
JP2009108001A (ja) * 2007-10-31 2009-05-21 Fuairudo Kk 疼痛緩和用組成物とその利用
US8308997B2 (en) * 2007-12-17 2012-11-13 U.S. Borax Inc. Fire resistant cellulosic materials and method of making the same
DE102008008537A1 (de) * 2008-02-06 2009-08-13 Beiersdorf Ag Wundversorgungsartikel
US20090304780A1 (en) * 2008-03-28 2009-12-10 Albertus Justus Johannes Van Den Berg Wound dressings incorporating honey
US20090292042A1 (en) * 2008-05-21 2009-11-26 Patterson Greg S Biodegradable material and plant container
US7833384B2 (en) * 2008-06-30 2010-11-16 Weyerhaeuser Nr Company Method for making fiber having biodegradable superabsorbent particles attached thereto
JP5472639B2 (ja) * 2008-07-03 2014-04-16 国立大学法人京都大学 加熱・加圧により硬化する組成物
US20100028758A1 (en) * 2008-08-04 2010-02-04 Eaves Stephen S Suppression of battery thermal runaway
EP2320844A1 (de) * 2008-09-05 2011-05-18 Birgit Riesinger Wundpflegeartikel, aufweisend einen anteil an modifizierten naturfasern oder an kunstfasern
US9533479B2 (en) 2008-09-18 2017-01-03 Medline Industries, Inc. Absorbent articles having antimicrobial properties and methods of manufacturing the same
WO2010080684A2 (en) 2009-01-08 2010-07-15 Nanogram Corporation Composites of polysiloxane polymers and inorganic nanoparticles
EP2206523B1 (en) 2009-01-13 2012-07-18 Rohm and Haas Company Treated cellulosic fibers and absorbent articles made from them
JP5636005B2 (ja) * 2009-02-24 2014-12-03 シュナイダー, デヴィッド, ジェイ.Schneider, David, J. 臭気抑制体排出液吸収体
US9717818B2 (en) 2009-05-08 2017-08-01 Medline Industries, Inc. Absorbent articles having antimicrobial properties and methods of manufacturing the same
US20110151158A1 (en) * 2009-05-26 2011-06-23 Stall Alan D Method of making a food casing
PL2462276T3 (pl) 2009-08-05 2015-04-30 Int Paper Co Dodatek do suchego arkusza z celulozowej masy puchowej
PL2462277T3 (pl) 2009-08-05 2015-04-30 Int Paper Co Proces stosowania kompozycji zawierającej trójwartościowy kation metalu i rozklejacz oraz arkusz pulpy puchowej uzyskany za jego pomocą
MY162376A (en) 2009-08-05 2017-06-15 Shell Int Research Method for monitoring a well
EP2462169B1 (en) 2009-08-07 2019-02-27 Knauf Insulation Molasses binder
DE102009055951A1 (de) 2009-11-27 2011-06-01 Glatfelter Falkenhagen Gmbh Absorbierende Struktur
EP2507271B1 (en) * 2009-12-02 2022-11-30 Huntsman Petrochemical LLC Preparation and use of poymeric dispersant compositions
US20110142898A1 (en) * 2009-12-11 2011-06-16 Jerry Fan Devices for treatment of skin disorders
BR112012028526B1 (pt) 2010-05-07 2020-11-17 Knauf Insulation método de preparação de uma tábua de madeira compósita com um aglutinante polimérico, termorrígido, curado
JP6223823B2 (ja) 2010-05-07 2017-11-01 ナフ インサレーション エセペーアールエル 炭水化物ポリアミン結合剤およびそれを用いて作製される材料
EP2576882B1 (en) 2010-06-07 2015-02-25 Knauf Insulation Fiber products having temperature control additives
ES2952420T3 (es) 2010-07-20 2023-10-31 Int Paper Co Composición que contiene un metal catiónico multivalente y un agente antiestático que contiene amina y métodos de fabricación y uso
CN103003488B (zh) 2010-07-22 2015-04-15 国际纸业公司 使用阳离子型染料和解胶剂型表面活性剂制造绒毛浆片材的方法和由该方法制得的绒毛浆片材
US20120117741A1 (en) * 2010-11-16 2012-05-17 Michael Patterson Wipes for cleaning coffee cups
WO2012152731A1 (en) 2011-05-07 2012-11-15 Knauf Insulation Liquid high solids binder composition
FR2983758B1 (fr) 2011-12-13 2015-11-27 Saint Gobain Abrasives Inc Composition resinique aqueuse pour articles abrasifs et articles resultants.
FR2983759B1 (fr) * 2011-12-13 2014-08-01 Saint Gobain Abrasives Inc Composition resinique aqueuse pour articles abrasifs et articles resultants.
GB201206193D0 (en) 2012-04-05 2012-05-23 Knauf Insulation Ltd Binders and associated products
GB201214734D0 (en) 2012-08-17 2012-10-03 Knauf Insulation Ltd Wood board and process for its production
ES2921601T3 (es) 2012-12-05 2022-08-30 Knauf Insulation Sprl Aglutinante
CN103040550B (zh) * 2013-01-24 2015-01-28 张兴平 医用自适应预塑形夹板装置
JP2015004914A (ja) * 2013-06-24 2015-01-08 ソニー株式会社 表示装置および電子機器
US9572729B2 (en) 2013-09-30 2017-02-21 Kimberly-Clark Worldwide, Inc. Method of forming an absorbent structure
US10596042B2 (en) 2013-09-30 2020-03-24 Kimberly-Clark Worldwide, Inc. Method of forming an absorbent structure
US9717817B2 (en) 2013-12-30 2017-08-01 International Paper Company Binary odor control system for absorbent articles
KR101586558B1 (ko) * 2014-01-21 2016-01-18 경북대학교 산학협력단 기능화된 탄소 나노입자 및 이를 이용한 기능성 고분자 섬유
EP3102587B1 (en) 2014-02-07 2018-07-04 Knauf Insulation, LLC Uncured articles with improved shelf-life
US10266986B2 (en) * 2014-02-21 2019-04-23 Cocona, Inc. Incorporation of active particles into substrates
US9777143B2 (en) 2014-04-11 2017-10-03 Georgia-Pacific Consumer Products Lp Polyvinyl alcohol fibers and films with mineral fillers and small cellulose particles
US9777129B2 (en) 2014-04-11 2017-10-03 Georgia-Pacific Consumer Products Lp Fibers with filler
JP6442857B2 (ja) 2014-04-14 2018-12-26 セイコーエプソン株式会社 シート製造装置
GB201408909D0 (en) 2014-05-20 2014-07-02 Knauf Insulation Ltd Binders
WO2016132220A1 (en) 2015-02-20 2016-08-25 Osmotica Kereskedelmi Es Szolgaltato Kft Controlled release oral dosage form of gaba receptor agonist
WO2016200112A1 (ko) * 2015-06-09 2016-12-15 주식회사 엘지화학 습윤 강도가 강화된 흡수 코어의 제조 방법
JP6603509B2 (ja) * 2015-08-05 2019-11-06 ヘンケルジャパン株式会社 水系接着用組成物
GB201517867D0 (en) 2015-10-09 2015-11-25 Knauf Insulation Ltd Wood particle boards
EP3387285B1 (en) 2015-12-08 2021-01-13 BorgWarner Inc. Friction material
US9820897B2 (en) * 2015-12-28 2017-11-21 Veronica Lee Berry Composite liquid-retentive substrate for a hygiene article
FI129075B (fi) * 2016-03-24 2021-06-30 Paptic Ltd Menetelmä luonnonkuituja ja synteettisiä kuituja sisältävän kuituradan valmistamiseksi
GB201610063D0 (en) 2016-06-09 2016-07-27 Knauf Insulation Ltd Binders
CN107620773B (zh) 2016-07-15 2021-03-19 博格华纳公司 摩擦材料
EP3354242B1 (en) 2017-01-25 2021-07-14 Mölnlycke Health Care AB Fiber materials with improved properties for use in wound treatment
GB201701569D0 (en) 2017-01-31 2017-03-15 Knauf Insulation Ltd Improved binder compositions and uses thereof
EP4238440A3 (en) * 2017-12-20 2023-10-18 Zephyros Inc. Breathable, wicking nonwoven material
EP3754102A4 (en) * 2018-02-13 2021-12-29 Nippon Paper Industries Co., Ltd. Flame-retardant composite fiber and method for producing same
GB201804907D0 (en) 2018-03-27 2018-05-09 Knauf Insulation Ltd Composite products
GB201804908D0 (en) 2018-03-27 2018-05-09 Knauf Insulation Ltd Binder compositions and uses thereof
US11471555B2 (en) 2018-05-25 2022-10-18 International Paper Company Methods of reducing trimethylamine
US11473242B2 (en) 2019-04-01 2022-10-18 International Paper Company Treated pulp and methods of making and using same
JP2021029685A (ja) * 2019-08-26 2021-03-01 花王株式会社 吸収体及び吸収性物品

Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO1990009236A1 (de) * 1989-02-16 1990-08-23 Cassella Aktiengesellschaft Bindemittel für flüssigkeiten
US5057166A (en) * 1989-03-20 1991-10-15 Weyerhaeuser Corporation Method of treating discontinuous fibers

Family Cites Families (212)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CA813616A (en) * 1969-05-27 J. Bernardin Leo Manufacture of cellulosic product
CA729513A (en) 1966-03-08 Kimberly-Clark Corporation Manufacture of cellulosic product
CA806352A (en) 1969-02-18 Kimberly-Clark Corporation Sanitary product with cross-linked cellulosic layer
CA841940A (en) 1970-05-19 J. Bernardin Leo Manufacture of cellulosic product
DE310695C (US06596103-20030722-C00008.png) 1924-06-12 1900-01-01
US1702530A (en) 1926-11-20 1929-02-19 Harrison R Williams Absorbent pad
BE475209A (US06596103-20030722-C00008.png) * 1944-04-14
US2601597A (en) * 1946-09-06 1952-06-24 American Cyanamid Co Application of dispersed coating materials to cellulosic fibers
USRE24011E (en) 1949-07-07 1955-05-31 Product thereof
GB720390A (en) 1950-10-07 1954-12-15 Tampax Inc Tampons and like absorbent pads
US2849000A (en) 1953-06-08 1958-08-26 Tampax Inc Tampons and the like
US3010161A (en) * 1954-02-16 1961-11-28 Wood Conversion Co Method and means for producing mixed fiber suspensions in air and felts therefrom
US3070095A (en) * 1954-06-24 1962-12-25 Torr David Disposable multi-ply product
DE1079796B (de) 1956-05-17 1960-04-14 Du Pont Verbandstoff oder Binde, insbesondere Monatsbinde oder Tampon, aus fluessigkeitaufsaugendem Stoff
US3021242A (en) * 1957-12-16 1962-02-13 Eastman Kodak Co Bonding additives onto filament filters
US3059313A (en) * 1958-03-26 1962-10-23 Chicopee Mfg Corp Textile fabrics and methods of making the same
US3087833A (en) * 1961-01-19 1963-04-30 Johnson & Johnson Fibrous structures and methods of making the same
US3409497A (en) * 1963-02-21 1968-11-05 Minnesota Mining & Mfg Adhesive sheet materials and method of making the same
GB1061574A (en) * 1963-06-07 1967-03-15 Kimberly Clark Co Laminated fabric
FR1382716A (fr) 1964-02-17 1964-12-18 Perfectionnement aux plaques de ouate de cellulose destinées à garnir les couches des bébés
US3395201A (en) * 1964-07-14 1968-07-30 Johnson & Johnson Method and apparatus for producing an absorbent product
US3344789A (en) * 1964-12-29 1967-10-03 Azur Associates Diaper with film enclosed absorbent
US3371666A (en) 1965-01-26 1968-03-05 Tampax Inc Absorbent device
US3350486A (en) * 1965-04-29 1967-10-31 Nestor B Knoepfler Method of producing contour molded cotton batting
US3377302A (en) * 1966-01-18 1968-04-09 Agriculture Usa Saponified starch acrylate grafts
US3425971A (en) * 1966-03-02 1969-02-04 Us Agriculture Salt-resistant thickeners comprising base-saponified starch-polyacrylonitrile graft copolymers
US3670731A (en) * 1966-05-20 1972-06-20 Johnson & Johnson Absorbent product containing a hydrocolloidal composition
US3669103A (en) * 1966-05-31 1972-06-13 Dow Chemical Co Absorbent product containing a hydrocelloidal composition
FR94276E (fr) * 1967-05-11 1969-07-25 Saint Gobain Plaques ou pieces de forme a base de fibres minérales, telles que notamment fibres de verre, et procédé pour leur obtention.
US3494992A (en) * 1968-02-01 1970-02-10 Conwed Corp Method of producing a mat from an air suspension of fibers and liquid
US3777758A (en) * 1968-05-16 1973-12-11 F Mesek Disposable diaper
US3661632A (en) * 1968-06-17 1972-05-09 Commercial Solvents Corp Process for binding pigments to textiles
US3645836A (en) 1968-09-05 1972-02-29 David Torr Water-absorption fibrous materials and method of making the same
US3554788A (en) * 1968-10-09 1971-01-12 Johnson & Johnson Water dispersible nonwoven fabric
US3672945A (en) * 1968-10-18 1972-06-27 Fruitgrowers Chem Co Ltd Granules comprising inert cores coated with an absorbent powder
US3949035A (en) * 1968-12-16 1976-04-06 Kimberly-Clark Corporation Method of forming a lightweight airlaid web of wood fibers
NL6917625A (US06596103-20030722-C00008.png) * 1968-12-16 1971-05-25
GB1217452A (en) 1969-02-04 1970-12-31 Celanese Corp Articles for absorbing liquid body discharges and materials therefor
US3521638A (en) * 1969-02-10 1970-07-28 Du Pont Fabrics having water soluble discrete areas and methods of making
US3661154A (en) * 1969-05-26 1972-05-09 David Torr Water-absorbing material
US3664343A (en) 1969-10-06 1972-05-23 Union Carbide Corp Disposable articles
CA930128A (en) 1969-10-21 1973-07-17 Torr David Fiber products containing water-absorbent material
US3808088A (en) * 1969-12-29 1974-04-30 Goodrich Co B F Spot bonded laminates
US3686024A (en) 1970-02-24 1972-08-22 Dow Chemical Co Process of making a water-absorbent coated article and resultant product
US3959569A (en) 1970-07-27 1976-05-25 The Dow Chemical Company Preparation of water-absorbent articles
US3766922A (en) * 1970-08-28 1973-10-23 Scott Paper Co Throw-away boy and girl diapers
CA953890A (en) 1970-09-17 1974-09-03 Union Carbide Corporation Disposable absorbent articles
US3923592A (en) * 1970-12-04 1975-12-02 Riegel Textile Corp Process for manufacturing a flushable fibrous sheet material for use in sanitary products
US3758641A (en) * 1971-01-21 1973-09-11 Dow Chemical Co Adhesion of polymer gels to cellulose
US3788936A (en) * 1971-09-01 1974-01-29 Kimberly Clark Co Nonwoven laminate containing bonded continuous filament web
DE2208126B1 (de) * 1972-02-22 1973-07-05 Vereinigte Papienverke Schickedanz & Co, 8500 Nürnberg Umhulltes Saugkissen fur hygienische Zwecke
US4009313A (en) * 1972-08-30 1977-02-22 Minnesota Mining And Manufacturing Company Enzymatically dispersible non-woven webs
US4071636A (en) * 1972-11-09 1978-01-31 Matsushita Electric Industrial Co., Ltd. Method of producing sheet-formed bactericidal article
US3804092A (en) * 1973-01-15 1974-04-16 Johnson & Johnson Water dispersible nonwoven fabric
US4537767A (en) * 1973-01-29 1985-08-27 Pharmacia Aktiebolag Method for cleansing fluid discharging skin surfaces, wounds and mucous membranes and means for carrying out the method
US3903889A (en) * 1973-02-16 1975-09-09 First National Bank Of Nevada Disposable liquid absorbent products
US4035217A (en) * 1973-05-24 1977-07-12 Johnson & Johnson Method of manufacturing absorbent facing materials
US3978257A (en) * 1973-08-06 1976-08-31 Kimberly-Clark Corporation Internally adhesively bonded fibrous web
US3888257A (en) * 1973-10-01 1975-06-10 Parke Davis & Co Disposable absorbent articles
AR204937A1 (es) * 1973-12-12 1976-03-19 Ciba Geigy Ag Procedimiento para aprestar y proveer cuero con un acabado antimicrobiano y preparaciones para ilevarlo a cabo
US4007083A (en) * 1973-12-26 1977-02-08 International Paper Company Method for forming wet-laid non-woven webs
US3908659A (en) * 1974-03-14 1975-09-30 Procter & Gamble Absorbent pad structure, diaper construction utilizing same and methods of manufacture thereof
US3886941A (en) * 1974-06-18 1975-06-03 Union Carbide Corp Diaper insert
US3901236A (en) * 1974-07-29 1975-08-26 Union Carbide Corp Disposable absorbent articles containing hydrogel composites having improved fluid absorption efficiencies and processes for preparation
US4128692A (en) 1974-08-27 1978-12-05 Hercules Incorporated Superabsorbent cellulosic fibers having a coating of a water insoluble, water absorbent polymer and method of making the same
US4062451A (en) * 1974-09-12 1977-12-13 Johnson & Johnson Laminated structures comprising films of silane crosslinked acrylate interpolymers having water barrier properties
US4102340A (en) * 1974-12-09 1978-07-25 Johnson & Johnson Disposable article with particulate hydrophilic polymer in an absorbent bed
DE2534358C3 (de) 1975-08-01 1978-04-13 Hoechst Ag, 6000 Frankfurt Verfahren zum Beschichten eines Bandes aus hydrophilem Material mit Puder aus einem modifizierten Celluloseether
GB1563697A (en) * 1975-08-22 1980-03-26 Unilever Ltd Liquid absorption devices
US4061268A (en) * 1975-12-01 1977-12-06 Minnesota Mining And Manufacturing Company Traction mat
CA1052156A (en) 1975-12-15 1979-04-10 Marcello A. B. Malpiedi Pulp
US4051086A (en) 1976-03-25 1977-09-27 Hercules Incorporated Absorption rate of absorbent polymers by treating with glyoxal
US4055180A (en) * 1976-04-23 1977-10-25 Colgate-Palmolive Company Absorbent article with retained hydrocolloid material
JPS5913244B2 (ja) * 1976-05-12 1984-03-28 本州製紙株式会社 吸着性不織布およびその製造方法
US4103062A (en) * 1976-06-14 1978-07-25 Johnson & Johnson Absorbent panel having densified portion with hydrocolloid material fixed therein
US4066583A (en) 1977-05-16 1978-01-03 The B. F. Goodrich Company Flexible water absorbent polymer compositions comprising (a) unsaturated carboxylic acid, acrylic ester containing alkyl group 10-30 carbon atoms, additional monomer plus (b) aliphatic diol
FR2402474A1 (fr) 1977-09-13 1979-04-06 Beghin Say Sa Procede de fabrication de structures absorbantes et structures obtenues
GB2007998B (en) 1977-10-18 1982-10-20 Unilever Ltd Absorbent materials
US4289513A (en) * 1978-03-27 1981-09-15 The Mead Corporation Activated sorbtion paper and products produced thereby
US4235237A (en) 1978-05-08 1980-11-25 Johnson & Johnson Absorbent open network structure
JPS5521705A (en) * 1978-07-12 1980-02-16 Sumitomo Chemical Co Preparation of coated seed
US4337111A (en) * 1978-10-02 1982-06-29 The United States Of America As Represented By The Secretary Of The Navy Method of obtaining strong and durable adhesion to rubber through chemical covalent bonds
US4289536A (en) * 1978-10-25 1981-09-15 Owens-Corning Fiberglas Corporation Glass fiber reinforced cements and process for manufacture of same
NL7908799A (nl) * 1978-12-22 1980-06-24 Tno Werkwijze voor de bereiding van een polymeermengsel, gevormde produkten, verkregen daaruit en polymeer- legering.
JPS56500968A (US06596103-20030722-C00008.png) * 1979-07-31 1981-07-16
US4282121A (en) * 1979-10-09 1981-08-04 Henkel Corporation Resilient starch graft polymer polyhydric alcohol product
US4287536A (en) * 1979-10-12 1981-09-01 Xerox Corporation Gain control for scanning arrays
JPS56103270A (en) * 1980-01-22 1981-08-18 Teijin Ltd Friction material
US4392908A (en) 1980-01-25 1983-07-12 Lever Brothers Company Process for making absorbent articles
US4354487A (en) 1980-05-12 1982-10-19 Johnson & Johnson Fiber/absorbent polymer composites and method of forming same
JPS5710334A (en) * 1980-06-23 1982-01-19 Kao Corp Absorptive article
DE3175341D1 (en) * 1980-07-11 1986-10-23 Ici Plc Fibrous composite materials and the production and use thereof
US4410571A (en) † 1980-08-25 1983-10-18 Johnson & Johnson Absorbent products, process and compositions for immobilization of particulate absorbents
US4394172A (en) * 1980-08-26 1983-07-19 Dentsply Research & Development Corp. Non-dusting and fast-wetting impression material and method of preparing same
US4379194A (en) * 1981-01-19 1983-04-05 Formica Corporation High pressure decorative laminates containing an air-laid web of fibers and filler and method of producing same
US4381784A (en) 1981-02-17 1983-05-03 Kimberly-Clark Corporation Sanitary appliance containing blood gelling agent
US4415388A (en) 1981-06-22 1983-11-15 Johnson & Johnson Method of making absorbent bearing products
DE3128100C2 (de) 1981-07-16 1986-05-22 Chemische Fabrik Stockhausen GmbH, 4150 Krefeld Absorptionsmittel für Blut und seröse Körperflüssigkeiten
US4412036A (en) * 1981-08-05 1983-10-25 Grain Processing Corporation Composition for absorbent film and method and preparation
US4467012A (en) * 1981-08-05 1984-08-21 Grain Processing Corporation Composition for absorbent film and method of preparation
DE3313344C2 (de) 1981-10-16 1987-04-23 Chemische Fabrik Stockhausen GmbH, 4150 Krefeld Verfahren zur Herstellung eines Absorptionsmaterials und seine Verwendung
DE3141098C2 (de) † 1981-10-16 1987-01-29 Chemische Fabrik Stockhausen GmbH, 4150 Krefeld Verfahren zur Herstellung eines Absorptionsmaterials
US4424247A (en) * 1981-11-09 1984-01-03 The Dow Chemical Company Absorbent polymer-fiber composites and method for preparing the same
JPS6018690B2 (ja) 1981-12-30 1985-05-11 住友精化株式会社 吸水性樹脂の吸水性改良方法
JPS58180233A (ja) 1982-04-19 1983-10-21 Nippon Shokubai Kagaku Kogyo Co Ltd 吸収剤
JPS58183754A (ja) † 1982-04-20 1983-10-27 Sanyo Chem Ind Ltd 吸水性樹脂組成物
US4413995A (en) 1982-05-21 1983-11-08 Personal Products Company Absorbent panel suitable for use in absorbent products
US4578150A (en) 1982-07-23 1986-03-25 Amf Inc. Fibrous media containing millimicron-sized particulates
US4404250A (en) * 1982-09-23 1983-09-13 Formica Corporation Fire-retardant high pressure consolidated articles containing an air-laid web and method of producing same
US4492729A (en) * 1982-10-08 1985-01-08 Georgia-Pacific Corporation Cohesive fibrous mat for in-transit particulate control
US4500315A (en) 1982-11-08 1985-02-19 Personal Products Company Superthin absorbent product
DK167952B1 (da) * 1983-03-10 1994-01-10 Procter & Gamble Absorbentstruktur, som er en blanding af hydrofile fibre og vanduoploeselig hydrogel i form af saerskilte partikler af tvaerbundet polumert materiale, fremgangsmaade til fremstilling af samme samt engangsble fremstillet heraf
US4610678A (en) 1983-06-24 1986-09-09 Weisman Paul T High-density absorbent structures
US4481076A (en) 1983-03-28 1984-11-06 International Telephone And Telegraph Corporation Redispersible microfibrillated cellulose
US4558091A (en) * 1983-05-13 1985-12-10 Grain Processing Corporation Method for preparing aluminum and polyhydric alcohol modified liquid absorbing composition
US4457978A (en) * 1983-05-16 1984-07-03 Stanley Wawzonek Formaldehyde depressed particle board
US4597930A (en) * 1983-07-11 1986-07-01 Szal John R Method of manufacture of a felted fibrous product from a nonaqueous medium
US4552816A (en) * 1983-12-05 1985-11-12 Novacor Medical Corporation Process for producing rubber laminates
CA1256640A (en) 1984-03-05 1989-06-27 Harumasa Yamasaki Absorptive material
AU567728B2 (en) 1984-03-27 1987-12-03 Personal Products Co. Polymer absorbent
US4755178A (en) 1984-03-29 1988-07-05 Minnesota Mining And Manufacturing Company Sorbent sheet material
ZA851661B (en) 1984-03-29 1986-10-29 Minnesota Mining & Mfg Sorbent sheet material
US4676784A (en) * 1984-05-01 1987-06-30 Personal Products Company Stable disposable absorbent structure
US4851069A (en) 1984-06-20 1989-07-25 Bird Machine Company, Inc. Process for making tissue-absorbent particle laminates
US4734478A (en) 1984-07-02 1988-03-29 Nippon Shokubai Kagaku Kogyo Co., Ltd. Water absorbing agent
PH26954A (en) 1985-05-15 1992-12-03 Procter & Gamble Disposable absorbent articles
PH23956A (en) * 1985-05-15 1990-01-23 Procter & Gamble Absorbent articles with dual layered cores
JPS61275355A (ja) 1985-05-29 1986-12-05 Kao Corp 吸収性物品
US4743244A (en) * 1985-06-28 1988-05-10 Arco Chemical Company Water absorbing polymer compositions and articles prepared therefrom
FR2585284B1 (fr) 1985-07-23 1987-11-13 Beghin Say Sa Procede de fixation de polymeres retenant les liquides dans une structure poreuse ouverte
US4772492A (en) * 1985-09-30 1988-09-20 James River Corporation Binder catalyst for an antimicrobially active, non-woven web
CA1280398C (en) 1986-02-05 1991-02-19 Hideharu Shirai Water-absorbent resin and process for producing the same
US4764418A (en) 1986-02-28 1988-08-16 Kimberly-Clark Corporation Virucidal tissue products containing water-soluble humectants
US4824689A (en) 1986-02-28 1989-04-25 Kimberly-Clark Corporation Method for producing virucidal tissue products containing water-soluble humectants
US4763674A (en) 1986-04-16 1988-08-16 Hercules Incorporated Method and device for controlling hydrogen cyanide and nitric oxide concentrations in cigarette smoke
US4699808A (en) * 1986-08-15 1987-10-13 Personal Products Company Method and apparatus for providing powder into fibrous web structures
EP0261832B1 (en) * 1986-09-08 1992-07-15 Mitsui Petrochemical Industries, Ltd. Synthetic pulp and absorbent comprising the same
US4818599A (en) * 1986-10-21 1989-04-04 E. I. Dupont De Nemours And Company Polyester fiberfill
CA1300866C (en) † 1986-11-17 1992-05-19 Tadao Shimomura Body fluid-absorbing article
DE8712723U1 (de) * 1986-12-08 1987-12-17 Hanfspinnerei Steen & Co Gmbh, 2000 Hamburg Absorberflocke
DE3642498A1 (de) * 1986-12-12 1988-06-23 Pelikan Ag Alkalischer waessriger alleskleber auf poly(meth-)acrylatbasis
US5252275A (en) * 1991-03-07 1993-10-12 Weyerhauser Company Method of densifying crosslinked fibers
US5225047A (en) * 1987-01-20 1993-07-06 Weyerhaeuser Company Crosslinked cellulose products and method for their preparation
US5294249A (en) 1987-03-27 1994-03-15 Luisi Pier L Blendpolymers
US4788080A (en) * 1987-04-27 1988-11-29 Canadian Patents And Development Limited Process and apparatus for coating particles with fine powder
US4758466A (en) * 1987-05-05 1988-07-19 Personal Products Company Foam-fiber composite and process
DE3720031A1 (de) 1987-06-16 1989-01-05 Freudenberg Carl Fa Saugkoerper aus vliesstoff und verfahren zu seiner herstellung
GB8717729D0 (en) 1987-07-27 1987-09-03 Bonar Carelle Ltd Non-woven materials
GB8717949D0 (en) * 1987-07-29 1987-09-03 Yarsley Technical Centre Ltd Water absorbent structures
US4813948A (en) 1987-09-01 1989-03-21 Minnesota Mining And Manufacturing Company Microwebs and nonwoven materials containing microwebs
US4888238A (en) 1987-09-16 1989-12-19 James River Corporation Superabsorbent coated fibers and method for their preparation
US4826880B1 (en) * 1987-09-21 2000-04-25 Johnson & Johnson Inc Immobilizing particulate absorbents by conversion to hydrates
US4775178A (en) † 1987-09-25 1988-10-04 Maxaxam Corporation Final closing device for closure member on a vehicle
US4842593A (en) * 1987-10-09 1989-06-27 The Procter & Gamble Company Disposable absorbent articles for incontinent individuals
DE3878533T2 (de) 1987-10-29 1993-06-03 Nippon Catalytic Chem Ind Verfahren zur oberflaechenbehandlung eines wasser absorbierenden harzes.
US4892769A (en) * 1988-04-29 1990-01-09 Weyerhaeuser Company Fire resistant thermoplastic material containing absorbent article
US4886697A (en) * 1988-04-29 1989-12-12 Weyerhaeuser Company Thermoplastic material containing absorbent pad or other article
JPH0253965A (ja) 1988-08-19 1990-02-22 Nippon Shokubai Kagaku Kogyo Co Ltd 吸水性ポリマーの繊維状基材への固定化方法
ATA255988A (de) 1988-10-14 1993-05-15 Chemie Linz Gmbh Absorbierendes polymerisat
US5278222A (en) * 1989-02-13 1994-01-11 Rohm And Haas Company Low viscosity, fast curing binder for cellulose
US5278206A (en) 1989-02-16 1994-01-11 Cassella Aktiengesellschaft Binder for liquids
US5002986A (en) 1989-02-28 1991-03-26 Hoechst Celanese Corporation Fluid absorbent compositions and process for their preparation
US4944734A (en) 1989-03-09 1990-07-31 Micro Vesicular Systems, Inc. Biodegradable incontinence device with embedded granules
US5498478A (en) 1989-03-20 1996-03-12 Weyerhaeuser Company Polyethylene glycol as a binder material for fibers
US5432000A (en) 1989-03-20 1995-07-11 Weyerhaeuser Company Binder coated discontinuous fibers with adhered particulate materials
US5230959A (en) * 1989-03-20 1993-07-27 Weyerhaeuser Company Coated fiber product with adhered super absorbent particles
US5064689A (en) * 1989-03-20 1991-11-12 Weyerhaeuser Company Method of treating discontinuous fibers
US5161686A (en) * 1989-04-14 1992-11-10 Kimberly-Clark Corporation Odor-absorbing web material and medical material packages containing the web material
US5283123A (en) * 1989-05-03 1994-02-01 Carter Deborah H Adsorption material and method
US5100397A (en) 1989-06-14 1992-03-31 Mcneil-Ppc, Inc. Absorbent mixture
SE8903180D0 (sv) 1989-09-27 1989-09-27 Sca Development Ab Saett att behandla fibrer av cellulosahaltigt material
US5183707A (en) * 1989-11-07 1993-02-02 The Procter & Gamble Cellulose Company Individualized, polycarboxylic acid crosslinked fibers
US5190563A (en) 1989-11-07 1993-03-02 The Proctor & Gamble Co. Process for preparing individualized, polycarboxylic acid crosslinked fibers
DK0429112T3 (da) * 1989-11-07 1996-07-08 Procter & Gamble Absorberende struktur indeholdende individualiserede fibre, der er tværbundet med polycarboxylsyre
JPH03157506A (ja) * 1989-11-16 1991-07-05 Yamada Corp 往復動形アクチュエータ
US5252340A (en) * 1989-12-14 1993-10-12 Isolyser Company, Inc. Method of producing an absorbent composition
US5217445A (en) * 1990-01-23 1993-06-08 The Procter & Gamble Company Absorbent structures containing superabsorbent material and web of wetlaid stiffened fibers
FI910467A (fi) 1990-02-01 1991-08-02 James River Corp Mycket voluminoesa, elastiska fibrer, som framstaellts genom tvaerbindning av traemassafibrer med polykarboxylsyror.
US5149335A (en) 1990-02-23 1992-09-22 Kimberly-Clark Corporation Absorbent structure
JPH0717758B2 (ja) † 1990-03-30 1995-03-01 積水化成品工業株式会社 高吸水性樹脂の製法
AU637470B2 (en) 1990-04-02 1993-05-27 Nippon Shokubai Kagaku Kogyo Co. Ltd. Method for production of fluid stable aggregate
US5140076A (en) 1990-04-02 1992-08-18 Nippon Shokubai Kagaku Kogyo Co., Ltd. Method of treating the surface of an absorbent resin
US5149334A (en) 1990-04-02 1992-09-22 The Procter & Gamble Company Absorbent articles containing interparticle crosslinked aggregates
US5164459A (en) 1990-04-02 1992-11-17 Nippon Shokubai Kagaku Kogyo Co., Ltd. Method for treating the surface of an absorbent resin
US5124188A (en) * 1990-04-02 1992-06-23 The Procter & Gamble Company Porous, absorbent, polymeric macrostructures and methods of making the same
US5128082A (en) * 1990-04-20 1992-07-07 James River Corporation Method of making an absorbant structure
CA2049861C (en) † 1990-08-30 1996-09-17 Nobuyuki Harada Absorbent body and absorbent article
DE69133620D1 (de) 1990-12-21 2009-09-10 Nippon Catalytic Chem Ind Wasserabsorbierendes Material und Verfahren zu seiner Herstellung sowie wasserabsorbierender Artikel und Verfahren zu seiner Herstellung
US5300054A (en) * 1991-01-03 1994-04-05 The Procter & Gamble Company Absorbent article having rapid acquiring, wrapped multiple layer absorbent body
JP3016879B2 (ja) 1991-01-31 2000-03-06 株式会社日本触媒 高吸水性樹脂の製造方法
GB9107952D0 (en) 1991-04-15 1991-05-29 Dow Rheinmuenster Surface crosslinked and surfactant coated absorbent resin particles and method of preparation
US5217576A (en) 1991-11-01 1993-06-08 Dean Van Phan Soft absorbent tissue paper with high temporary wet strength
JP2530668Y2 (ja) 1991-11-28 1997-03-26 三洋電機株式会社 部品供給装置
CA2072454C (en) 1991-12-11 2003-04-29 Kimberly-Clark Worldwide, Inc. High absorbency composite
US5264082A (en) 1992-04-09 1993-11-23 Procter & Gamble Company Soft absorbent tissue paper containing a biodegradable quaternized amine-ester softening compound and a permanent wet strength resin
US5308896A (en) 1992-08-17 1994-05-03 Weyerhaeuser Company Particle binders for high bulk fibers
US5589256A (en) 1992-08-17 1996-12-31 Weyerhaeuser Company Particle binders that enhance fiber densification
US5538783A (en) 1992-08-17 1996-07-23 Hansen; Michael R. Non-polymeric organic binders for binding particles to fibers
US5543215A (en) 1992-08-17 1996-08-06 Weyerhaeuser Company Polymeric binders for binding particles to fibers
US5352480A (en) 1992-08-17 1994-10-04 Weyerhaeuser Company Method for binding particles to fibers using reactivatable binders
US5547541A (en) 1992-08-17 1996-08-20 Weyerhaeuser Company Method for densifying fibers using a densifying agent
US5807364A (en) 1992-08-17 1998-09-15 Weyerhaeuser Company Binder treated fibrous webs and products
US5641561A (en) 1992-08-17 1997-06-24 Weyerhaeuser Company Particle binding to fibers
ES2181693T5 (es) * 1992-08-17 2006-05-16 Weyerhaeuser Company Metodo de union de particulas de fibras.
US5300192A (en) * 1992-08-17 1994-04-05 Weyerhaeuser Company Wet laid fiber sheet manufacturing with reactivatable binders for binding particles to fibers
US5240562A (en) 1992-10-27 1993-08-31 Procter & Gamble Company Paper products containing a chemical softening composition
US5312522A (en) * 1993-01-14 1994-05-17 Procter & Gamble Company Paper products containing a biodegradable chemical softening composition
EP0691995B1 (en) 1993-03-29 2000-04-12 The Dow Chemical Company Absorbent polymer having reduced dusting tendencies
US5449551A (en) 1993-06-03 1995-09-12 Kawano Paper Co., Ltd. Highly water absorbent fibrous web and a process for producing the same
US5362776A (en) 1993-07-21 1994-11-08 Packaging Corporation Of America Recyclable cellulosic packaging material
AU1691795A (en) 1994-02-17 1995-09-04 Procter & Gamble Company, The Absorbent materials having modified surface characteristics and methods for making the same
CA2187633A1 (en) 1994-04-11 1995-10-19 Douglas R. Chambers Superabsorbent polymers and products therefrom

Patent Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO1990009236A1 (de) * 1989-02-16 1990-08-23 Cassella Aktiengesellschaft Bindemittel für flüssigkeiten
US5057166A (en) * 1989-03-20 1991-10-15 Weyerhaeuser Corporation Method of treating discontinuous fibers

Cited By (10)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO1995019191A1 (en) * 1994-01-12 1995-07-20 Weyerhaeuser Company Method and compositions for enhancing blood absorbence by absorbent materials
WO1995022655A1 (en) * 1994-02-16 1995-08-24 Weyerhaeuser Company Densifying agents for enhancing fiber densification
US5800418A (en) * 1994-12-09 1998-09-01 The Procter & Gamble Company Absorbent composites and absorbent articles containing the same
WO1996031644A1 (en) * 1995-04-04 1996-10-10 Weyerhaeuser Company Binder treated fibrous webs and products
US5853867A (en) * 1995-09-14 1998-12-29 Nippon Shokubai Co., Ltd. Absorbent composite, method for production thereof, and absorbent article
US6533978B1 (en) 2000-08-03 2003-03-18 Kimberly-Clark Worldwide, Inc. Process and apparatus for forming a stabilized absorbent web
US6533989B1 (en) 2000-08-03 2003-03-18 Kimberly-Clark Worldwide, Inc. Multi-chamber process and apparatus for forming a stabilized absorbent web
WO2003104543A1 (de) * 2002-06-11 2003-12-18 Basf Aktiengesellschaft Verfahren zum binden von teilchenförmigen, wasserabsorbierenden, säuregruppen enthaltenden polymeren an ein trägermaterial
US7351302B2 (en) 2002-06-11 2008-04-01 Basf Aktiengesellschaft Method for binding particulate, water-absorbing, acid group-containing polymers to a base material
US10702419B2 (en) 2012-07-30 2020-07-07 Kci Licensing, Inc. Incisional absorbent dressing

Also Published As

Publication number Publication date
EP0655970A1 (en) 1995-06-07
EP0655971B1 (en) 2002-09-25
WO1994004351A1 (en) 1994-03-03
EP0655971A1 (en) 1995-06-07
DE69332336T2 (de) 2003-01-30
EP1217120A1 (en) 2002-06-26
EP0655971B2 (en) 2005-11-23
US20030201051A1 (en) 2003-10-30
ES2181693T3 (es) 2003-03-01
US5672418A (en) 1997-09-30
JPH08500271A (ja) 1996-01-16
DE69332380D1 (de) 2002-11-14
DE69333678T2 (de) 2005-03-03
US6596103B1 (en) 2003-07-22
EP1219744A1 (en) 2002-07-03
US5547745A (en) 1996-08-20
DE69332380T2 (de) 2003-02-13
ATE224808T1 (de) 2002-10-15
CA2140263A1 (en) 1994-03-03
KR950702909A (ko) 1995-08-23
US5607759A (en) 1997-03-04
AU5019993A (en) 1994-03-15
US6521339B1 (en) 2003-02-18
ATE280264T1 (de) 2004-11-15
DE69332336D1 (de) 2002-10-31
US5789326A (en) 1998-08-04
JP3539957B2 (ja) 2004-07-07
ES2181693T5 (es) 2006-05-16
DE69332336T3 (de) 2006-06-01
US5693411A (en) 1997-12-02
CA2140263C (en) 2005-09-13
ATE225708T1 (de) 2002-10-15
ES2230413T3 (es) 2005-05-01
US7018490B2 (en) 2006-03-28
KR950702910A (ko) 1995-08-23
ES2182830T3 (es) 2003-03-16
US5611885A (en) 1997-03-18
CA2140264A1 (en) 1994-03-03
BR9306920A (pt) 1999-01-12
DE69333678D1 (de) 2004-11-25
NZ255814A (en) 1996-06-25
CA2140264C (en) 2005-09-13
EP1219744B1 (en) 2004-10-20
EP0655971A4 (en) 1995-07-19
AU5019893A (en) 1994-03-15
EP0655970B1 (en) 2002-10-09
US6461553B1 (en) 2002-10-08
BR9306921A (pt) 1999-01-12
JP3497166B2 (ja) 2004-02-16
EP0655970A4 (en) 1995-07-19
JPH08500270A (ja) 1996-01-16
NZ255815A (en) 1996-03-26

Similar Documents

Publication Publication Date Title
EP1219744B1 (en) Particle binders
US6340411B1 (en) Fibrous product containing densifying agent
US5547541A (en) Method for densifying fibers using a densifying agent
US7144474B1 (en) Method of binding particles to binder treated fibers
US5641561A (en) Particle binding to fibers
US6391453B1 (en) Binder treated particles
US5308896A (en) Particle binders for high bulk fibers
US5589256A (en) Particle binders that enhance fiber densification
US5352480A (en) Method for binding particles to fibers using reactivatable binders
US5300192A (en) Wet laid fiber sheet manufacturing with reactivatable binders for binding particles to fibers
US20010021453A1 (en) Particle binding to fibers
CA2412892C (en) Densifying agents for enhancing fiber densification

Legal Events

Date Code Title Description
AK Designated states

Kind code of ref document: A1

Designated state(s): AU BR CA JP KR NZ

AL Designated countries for regional patents

Kind code of ref document: A1

Designated state(s): AT BE CH DE DK ES FR GB GR IE IT LU MC NL PT SE

DFPE Request for preliminary examination filed prior to expiration of 19th month from priority date (pct application filed before 20040101)
121 Ep: the epo has been informed by wipo that ep was designated in this application
WWE Wipo information: entry into national phase

Ref document number: 2140263

Country of ref document: CA

WWE Wipo information: entry into national phase

Ref document number: 1993920180

Country of ref document: EP

WWE Wipo information: entry into national phase

Ref document number: 255815

Country of ref document: NZ

WWP Wipo information: published in national office

Ref document number: 1993920180

Country of ref document: EP

WWG Wipo information: grant in national office

Ref document number: 1993920180

Country of ref document: EP