USH2042H1 - Method for forming a breathable film - Google Patents

Method for forming a breathable film Download PDF

Info

Publication number
USH2042H1
USH2042H1 US08/853,301 US85330197A USH2042H US H2042 H1 USH2042 H1 US H2042H1 US 85330197 A US85330197 A US 85330197A US H2042 H USH2042 H US H2042H
Authority
US
United States
Prior art keywords
film
roll
teeth
regions
breathable
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US08/853,301
Other languages
English (en)
Inventor
George C. Dobrin
Thomas M. Goens
Donna S. Phillips
John J. Curro
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Procter and Gamble Co
Original Assignee
Procter and Gamble Co
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Procter and Gamble Co filed Critical Procter and Gamble Co
Priority to US08/853,301 priority Critical patent/USH2042H1/en
Assigned to PROCTER & GAMBLE COMPANY, THE reassignment PROCTER & GAMBLE COMPANY, THE ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: CURRO, JOHN J., DOBRIN, GEORGE C., GOENS, THOMAS M., PHILLIPS, DONNA S.
Priority to TR1999/02749T priority patent/TR199902749T2/xx
Priority to IL13271298A priority patent/IL132712A0/xx
Priority to CA002289671A priority patent/CA2289671C/en
Priority to AU69322/98A priority patent/AU6932298A/en
Priority to CN98806547A priority patent/CN1261304A/zh
Priority to HU0002241A priority patent/HUP0002241A3/hu
Priority to JP10548963A priority patent/JP2000512934A/ja
Priority to ES98915042T priority patent/ES2187953T3/es
Priority to IDW991357A priority patent/ID27385A/id
Priority to EP98915042A priority patent/EP1007329B1/en
Priority to DE69808650T priority patent/DE69808650T2/de
Priority to PCT/IB1998/000663 priority patent/WO1998051475A1/en
Priority to KR1019997010266A priority patent/KR20010012314A/ko
Priority to AT98915042T priority patent/ATE225705T1/de
Priority to EG49598A priority patent/EG21541A/xx
Priority to ZA983870A priority patent/ZA983870B/xx
Priority to PE1998000353A priority patent/PE86799A1/es
Priority to ARP980102178A priority patent/AR017501A1/es
Priority to CO98026120A priority patent/CO5050262A1/es
Priority to TW087107157A priority patent/TW422781B/zh
Priority to NO995466A priority patent/NO995466L/no
Publication of USH2042H1 publication Critical patent/USH2042H1/en
Application granted granted Critical
Abandoned legal-status Critical Current

Links

Images

Classifications

    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
    • B29C55/00—Shaping by stretching, e.g. drawing through a die; Apparatus therefor
    • B29C55/02—Shaping by stretching, e.g. drawing through a die; Apparatus therefor of plates or sheets
    • B29C55/18—Shaping by stretching, e.g. drawing through a die; Apparatus therefor of plates or sheets by squeezing between surfaces, e.g. rollers

Definitions

  • the present invention relates to a method for forming a breathable film, and more particularly, to a method for forming a breathable film comprising a blend of a thermoplastic polymer with an inorganic material.
  • the breathable film is particularly useful as a backsheet on a disposable absorbent article.
  • Disposable absorbent articles having many different basic designs are known to the art. It is also known that the exterior of disposable diapers can be covered with a flexible, liquid and vapor impervious sheet to prevent any absorbed liquid from passing through the diaper and soiling adjacent articles such as clothing, bedding and the like. These outer covers, generally referred to as backsheets, are often constructed from fluid impervious films such as polyethylene. Although such backsheets do prevent liquid from passing through the diaper, they also can make the diaper feel hot and uncomfortable to wear because of their impermeability to air and/or moisture.
  • Backsheets which are pervious to vapor are generally known as breathable backsheets and have been described in the art. In general, these backsheets are intended to allow the passage of vapor through them while retarding the passage of liquid.
  • U.S. Pat. No. 3,156,242 issued to Crowe, Jr. on Nov. 10, 1964 teaches the use of a microporous film as a breathable backsheet.
  • U.S. Pat. No. 3,881,489 issued to Hartwell on May 6, 1975 teaches a breathable backsheet comprising in combination two layers, the first of which is a low void volume perforated thermoplastic film and the, second of which is a porous high void volume hydrophobic tissue.
  • U.S. Pat. No. 3,989,867 issued to Sisson on Nov. 2, 1976 teaches a breathable backsheet provided with tapered hollow bosses which prevent the passage of liquids while allowing vapors to readily pass.
  • Microporous films typically comprise a blend of a thermoplastic polymer and an inorganic filler such as calcium carbonate. The blend undergoes pore formation upon stretching as the inorganic filler separates from the polymer due to stress concentration. The formation of micropores permits the film to be breathable allowing the passage of vapor through the micropores while retarding the passage of liquid.
  • a method for forming a breathable film is comprised of a blend of a thermoplastic. polymer with an inorganic material being selected from the group consisting of calcium carbonate, clay and titanium dioxide, with the preferred inorganic filler being calcium carbonate.
  • the blended film is fed between a pair of opposing first and second rolls.
  • the first roll comprises a plurality of toothed regions spaced apart by a plurality of grooved regions wherein the toothed regions comprises a plurality of teeth.
  • the second roll comprises a plurality of teeth which mesh with the teeth on the first roll.
  • the portion of the film passing between the grooved regions on the first roll and the teeth on the second roll remains substantially planar forming a first region in the film while the portion of the film passing between the teeth on the first roll and the teeth on the second roll is formed into second regions having raised rib-like elements.
  • FIG. 1 is a schematic illustration of an exemplary process for forming the breathable film of the present invention
  • FIG. 2 is an enlarged illustration of the opposing pairs of rolls of the process of FIG. 1;
  • FIG. 3 is a plan view illustration of a preferred embodiment of a breathable polymeric film having a first region and a second region of the present invention with the rib-like elements of the second region facing toward the viewer;
  • FIG. 3A is a segmented, perspective illustration of the breathable film of FIG. 3 in an untensioned condition
  • FIG. 4 is an enlarged photograph of the breathable film of the present invention
  • FIGS. 4A and 4B are enlarged photographs of the breathable films cross-section illustrating the formation of micropores in the portions of the film which have been stretched or thinned;
  • FIG. 5 is an illustration of an alternative embodiment of the opposing pairs of rolls of the process of FIG. 1;
  • FIG. 6 is an illustration of another embodiment of the opposing pairs of rolls of the process of FIG. 1;
  • FIG. 7 is a schematic illustration of an alternative process for forming the breathable film of the present invention.
  • a film 12 is unwound from supply roll 11 and travels in the direction indicated by the arrows associated therewith as the supply roll 11 rotates in the direction indicated by the arrows associated therewith.
  • the film 12 comprises a blend of a thermoplastic polymer with an inorganic material.
  • Suitable thermoplastic polymers include polyolefins such as polyethylenes, including linear low density polyethylene (LLDPE), low density polyethylene (LDPE), ultra low density polyethylene (ULDPE), high density polyethylene (HDPE), or polypropylene and blends thereof with the above and other materials.
  • thermoplastic polymers examples include, but are not limited to, polyester, polyurethanes, compostable or biodegradable polymers, heat shrink polymers, thermoplastic elastomers, and metallocene catalyst-based polymers (e.g., INSITE® available from Dow Chemical Company and Exxact® available from Exxon).
  • the inorganic material or filler is selected from the group consisting of calcium carbonate, clay and titanium dioxide, with the preferred inorganic filler being calcium carbonate.
  • Inorganic fillers having a particle size of from about 1 to about 5 microns and constitute of from about 5 to about 70 percent by weight of the blend, preferably from about 20 to about 60 percent by weight of the blend.
  • the inorganic filler may be coated with a fatty acid ester to obtain higher loadings in the polymer.
  • the inorganic filler and the thermoplastic polymer are blended together to form a homogeneous mixture in a suitable mixing extruder, or in a separate preliminary compounding step.
  • the mixture is then cast or blown into a film.
  • Roll 52 comprises a plurality of toothed regions 56 and grooved regions 58 extending about the circumference of the roll.
  • the toothed regions 56 include a plurality of teeth 57 .
  • Teeth 57 are substantially parallel to the axis of roll 52 .
  • Roll 54 comprises a plurality of toothed regions 60 and grooved regions 62 extending about the circumference of the roll.
  • the toothed regions 60 include a plurality of teeth 61 . Teeth 61 are substantially parallel to the axis of roll 54 .
  • the grooved regions 58 of roll 52 are aligned with the grooved regions 62 of roll 54 .
  • the toothed regions 56 of roll 52 are aligned with the toothed regions 60 of roll 54 permitting teeth 57 of roll 52 to engage or intermesh with teeth 61 of roll 54 .
  • the portions of the film 12 passing between the grooved regions 58 and 62 will be unformed, i.e., the film 12 will not be formed or stretched and will remain substantially planar, while the portions of the film passing between toothed regions 56 and 60 will be formed and/or stretched producing rib-like elements in the film.
  • the above sequence may be repeated any number of times until the desired properties are obtained. Furthermore, the degree of engagement of opposing rolls, the dimension, shape and spacing of the teeth on the opposing rolls, and the size of the rolls can be chosen to produce the desired properties.
  • FIG. 3 there is illustrated a preferred embodiment of a breathable film 12 after having passed through the pair of opposing rolls 52 and 54 of apparatus 50 .
  • the breathable film 12 is shown in FIG. 3 in its substantially untensioned condition.
  • the breathable film 12 is particularly well suited for use as a backsheet on an absorbent article, such as a sanitary napkin or a disposable diaper.
  • the film 12 has two centerlines, a longitudinal centerline, which is also referred to hereinafter as an axis, line, or direction “1” and a transverse or lateral centerline, which is also referred to hereinafter as an axis, line, or direction “t”.
  • the transverse centerline “t” is generally perpendicular to the longitudinal centerline “1”.
  • film 12 includes a network of distinct regions.
  • the network includes at least a first region 64 and a second region 66 .
  • Film 12 includes a transitional region 65 which is at the interface between the first region 64 and the second region 66 .
  • Film 12 has a first surface 52 a and an opposing second surface 52 b.
  • the film includes a plurality of first regions 64 and a plurality of second regions 66 .
  • the first regions 64 have a first axis 68 and a second axis 69 , wherein the first axis 68 is preferably longer than the second axis 69 .
  • the first axis 68 of the first region 64 is substantially parallel to the longitudinal axis of the film 12 while the second axis 69 is substantially parallel to the transverse axis of the film 12 .
  • the second regions 66 have a first axis 70 and a second axis 71 .
  • the first axis 70 is substantially parallel to the longitudinal axis of the film 12
  • the second axis 71 is substantially parallel to the transverse axis of the film 12 .
  • the first regions 64 and the second regions 66 are substantially linear, extending continuously in a direction substantially parallel to the longitudinal axis of the film 12 .
  • the film 12 is comprised of at least a first region and a second region, wherein the first region is visually distinct from the second region.
  • visually distinct refers to features of the film which are readily discernible to the normal naked eye when the film or objects embodying the film are subjected to normal use.
  • the first regions 64 are substantially planar. That is, the material within the first region 64 is in substantially the same condition before and after the formation step undergone by film 12 .
  • the second regions 66 include a plurality of raised rib-like elements 74 .
  • the rib-like elements 74 have a first or major axis 76 which is substantially parallel to the transverse axis of the film 12 and a second or minor axis 77 which is substantially parallel to the longitudinal axis of the film 12 .
  • the first axis 76 of the rib-like elements 74 is at least equal to, and preferably longer than the second axis 77 .
  • the ratio of the first axis 76 to the second axis 77 is at least about 1:1 or greater, and more preferably at least about 2:1 or greater.
  • the rib-like elements 74 in the second region 66 may be separated from one another by unformed areas.
  • the rib-like elements 74 are adjacent one another and are separated by an unformed area of less than 0.10 inches as measured perpendicular to the major axis 76 of the rib-like elements 74 , and more preferably, the rib-like elements 74 are contiguous having no unformed areas between them.
  • the dimension of the rib-like elements can also be varied.
  • FIG. 4 there is shown an enlarged photograph of the film 12 after having passed through a pair of opposing rolls of the present invention, like opposing rolls 52 and 54 of apparatus 50 .
  • the film 12 includes substantially planar first regions 64 and second regions 66 which include raised rib-like elements 74 .
  • the portions of the film 12 forming the rib-like elements 74 of the second region 66 have been stretched or thinned as opposed to the thicker first regions 64 which have not been stretched or thinned. While the second regions 66 have been stretched or thinned, the stretching or thinning is not necessarily uniform throughout the second regions 66 .
  • FIGS. 4A and 4B are enlarged photographs of portions of the films in cross-section.
  • the portion of the film in FIG. 4A has been stretched to a greater degree than the portion of the film in FIG. 4 B and as a result has a thickness dimension less than that of the portion of the film in FIG. 4 B.
  • the film shown in FIG. 4A has an increased pore volume compared to the film shown in FIG. 4 B.
  • the stretching of the film separates the inorganic filler from the polymer due to stress concentration creating pores in the film.
  • the formation of micropores permits the film to be breathable allowing the passage of vapor therethrough while retarding the passage of liquid.
  • the breathable film of the present invention when used as a backsheet on a disposable diaper should have a moisture vapor transmission rate of from about 500 g/m 2 /24 hr. to about 5000 g/m 2 /24 hr., more preferably from about 1000 g/m 2 /24 hr. to about 5000 g/m 2 /24 hr., and most preferably from about 2000 g/m 2 /24 hr. to about 5000 g/m 2 /24 hr.
  • the moisture vapor transmission rate is measured by the method set forth below.
  • a known amount of CaCl 2 is put into a flanged cup.
  • a sample material is placed on top of the cup and held securely by a retaining ring and gasket.
  • the assembly is then weighed and recorded as the initial weight.
  • the assembly is placed in a constant temperature (40° C.) and humidity (75% RH) chamber for five (5) hours.
  • the assembly is then removed from the chamber and allowed to equilibrate for at least 30 minutes at the temperature of the room where the balance is located.
  • the assembly is then weighed and recorded as the final weight.
  • the moisture vapor transmission rate is calculated and expressed in g/m 2 /24 hr.
  • MVTR ( final ⁇ ⁇ weight - initial ⁇ ⁇ weight ) ⁇ 24.0 area ⁇ ⁇ of ⁇ ⁇ sample ⁇ ⁇ in ⁇ ⁇ meters ⁇ 5.0 ⁇ ⁇ ( time ⁇ ⁇ in ⁇ ⁇ chamber )
  • OCR oxygen permeation rate
  • the oxygen permeation rate is measured by the method set forth below.
  • the rate of oxygen permeation through a material is measured using a glass chamber with an oxygen monitor and probe.
  • a sample is cut approximately equal in diameter to an aluminum foil disc having a 12 cm diameter, Mocon Part #025-493. The sample is placed on top of the disc.
  • the glass chamber is placed on the disc and a circle is traced. The circle in the sample is cut.
  • the sample disc (foil side down) is clamped between the glass chamber containing the probe and the center glass piece.
  • a circular piece of rubber is placed between the center glass piece and the open ended glass chamber and sealed with a second clamp.
  • the chamber is flushed with nitrogen to a concentration of 0.1% oxygen on both sides of the film.
  • OPR ( 5.57 * 10 4 ) ⁇ ( volume ⁇ ⁇ ( mL ) ) ( average ⁇ ⁇ time ⁇ ⁇ ( sec ) )
  • Average time Average value of the time interval associated with a 0.5% increase in oxygen concentration.
  • the blended film Prior to undergoing the process of the present invention the blended film has a moisture vapor transmission rate of less than about 100 g/m 2 /24 hr. and an oxygen permeation rate of less than about 0.5 cu. meters/sq. meter/24 hrs.
  • blended film does not provide the desired breathability achieved by the film after having undergone the process of the present invention.
  • the method of the present invention expands the film out of the x-y plane, i.e., in the z direction to provide the film with an increased caliper via the raised rib-like elements.
  • traditional incremental stretching equipment such as disclosed in U.S. Pat. No. 4,116,892 issued to Schwarz on Sep. 26, 1978, expands the film in the x-y plane, in either the longitudinal or transverse directions or both.
  • traditional incremental stretching equipment produces a film of larger planar dimension, e.g., a film having a larger width and/or length dimension. Producing a film of larger dimension may be undesirable in certain circumstances as this may require modifying existing production equipment to handle the larger film.
  • the process of the present invention provides a film having a cloth-like appearance. This is particularly important if the film is to be used as a backsheet on a disposable diaper.
  • the present invention may also provide the breathable film with elastic-like properties allowing the film to stretch under relatively low forces. The ability to stretch under normal wearing forces can be very beneficial for disposable diapers to provide increased comfort and improved fit for the wearer.
  • the film 12 may be fed through the nip 51 of opposing rolls 52 and 54 without first being stored on a supply roll.
  • the film 12 may be fed through the nip 51 directly from an extruder.
  • the film 12 may be wound up onto a take-up roll.
  • the film may be fed directly to a disposable absorbent article converter where it forms the backsheet of a disposable absorbent article.
  • the present invention may also be practiced by subjecting to formation only a portion thereof For example, it may be desirable to provide specific portions of the diaper backsheet with breathability, such as the side portions while leaving other portions, such as the central portion of the backsheet nonbreathable.
  • the breathable film of the present invention may be secured to other materials to form a laminate.
  • the breathable film of the present invention is secured to a nonwoven web.
  • the nonwoven web may comprise natural fibers (e.g., cotton or wood fibers), or may comprise synthetic fibers such as polyethylene, polypropylene, polyester, or any combination of such fibers.
  • the nonwoven web may be carded, spunmelt, meltblown, or air-through bonded, or have any other characteristic or be manufactured in any manner known in the art.
  • Nonwoven webs are preferred when the laminate is to be used as a diaper backsheet as the nonwoven web forms the outermost cover of the diaper providing the diaper with a cloth-like look and feel.
  • the outer nonwoven web cover may provide the diaper with a landing zone capable of engaging the hooks of a hook and loop type fastener.
  • the breathable film is secured to other materials such as woven webs, foams, scrims, films, loose fibers, or any other material or combination that will give the diaper a cloth-like look and feel.
  • the laminates may be made by any number of methods known to those skilled in the art. Such bonding methods include but are not limited to heat bonds, adhesive bonds (using any of a number of adhesives including but not limited to spray adhesives, hot melt adhesives, latex based adhesives and the. like), pressure bonds, ultrasonic bonds, dynamic mechanical bonds, sonic bonds, or any other suitable attachment technique or combinations of these attachment techniques as are known in the art.
  • the blended film may first be secured to another material to form a laminate prior to being formed according to the method of the present invention as described above.
  • the laminate may comprise any of the aforementioned structures.
  • the laminate is formed by extruding the breathable blend onto a nonwoven web.
  • the blended film is extruded directly onto a nonwoven web while still in a partially molten state, thereby bonding the blended film to one side of the nonwoven web.
  • the laminate may then be subjected to the process of the present invention.
  • the laminate may be formed by vacuum laminating a nonwoven web to the breathable blend. The laminate may then be subjected to the process of the present invention.
  • FIG. 5 there is shown an illustration of an alternative embodiment of the opposing pairs of rolls of the process of FIG. 1 .
  • Roll 152 comprises a plurality of toothed regions 156 and grooved regions 158 extending about the circumference of the roll.
  • the toothed regions 156 include a plurality of teeth 157 .
  • Teeth 157 are substantially parallel to the axis of roll 152 .
  • Roll 154 comprises a plurality of teeth 161 extending about the circumference of the roll. Teeth 161 are substantially parallel to the axis of roll 154 .
  • Teeth 157 of roll 152 engage or intermesh with teeth 161 of roll 154 .
  • the portions of the film 12 passing between the grooved regions 58 of roll 152 and the teeth 161 of roll 154 will be unformed, i.e., the film 12 will not be formed or stretched and will remain substantially planar, while the portions of the film passing between toothed regions 156 comprising teeth 157 and the teeth 161 of roll 154 will be formed and/or stretched producing rib-like elements in the film.
  • FIG. 6 there is shown an illustration of an alternative embodiment of the opposing pairs of rolls of the process of FIG. 1 .
  • Roll 252 comprises a plurality of toothed regions 256 and grooved regions 258 that extend parallel to the axis of roll 252 .
  • the toothed regions 256 include a plurality of teeth 257 .
  • Teeth 257 are substantially perpendicular to the axis of roll 252 .
  • Roll 254 comprises a plurality of teeth 261 extending about the circumference of the roll. Teeth 261 are substantially perpendicular to the axis of roll 254 .
  • Teeth 257 of roll 252 engage or intermesh with teeth 261 of roll 254 .
  • the portions of the film 12 passing between the grooved regions 258 of roll 252 and the teeth 261 of roll 254 will be unformed, i.e., the film 12 will not be formed or stretched and will remain substantially planar, while the portions of the film passing between toothed regions 256 comprising teeth 257 and the teeth 261 of roll 254 will be formed and/or stretched producing rib-like elements in the film.
  • FIG. 7 is a schematic illustration of an alternative process for forming the breathable film of the present invention.
  • a film 312 is unwound from supply roll 311 and travels in the direction indicated by the arrows associated therewith as the supply roll 311 rotates in the direction indicated by the arrows associated therewith.
  • the film 312 comprises a blend of a thermoplastic polymer with an inorganic material.
  • From the supply roll 311 the film 312 is fed through a nip 351 of a pair of opposing rolls 352 and 354 of apparatus 350 .
  • the opposing rolls 352 and 354 may be any one of those shown in any one of FIGS. 2, 5 or 6 .
  • the film 312 is fed through a nip of a pair of opposing rolls 452 and 454 of apparatus 450 .
  • the opposing rolls 452 and 454 may be any one of those shown in any one of FIGS. 2, 5 or 6 .
  • the above sequence may be repeated any number of times until the desired properties are obtained. Furthermore, the degree of engagement of opposing rolls, the dimension, shape and spacing of the teeth on the opposing rolls, and the size of the rolls can be chosen to produce the desired properties.
  • the process of the present invention may be practiced in combination with the incremental stretching operation disclosed in the aforementioned U.S. Pat. No. 4,116,892 issued to Schwarz on Sep. 26, 1978, which is incorporated herein by reference.
  • the film may be incrementally stretched as disclosed in Schwarz and then fed through the opposing rolls of the present invention.
  • the above sequence may be reversed and/or repeated to produce the desired properties in the film.

Landscapes

  • Engineering & Computer Science (AREA)
  • Mechanical Engineering (AREA)
  • Absorbent Articles And Supports Therefor (AREA)
  • Shaping Of Tube Ends By Bending Or Straightening (AREA)
  • Laminated Bodies (AREA)
  • Manufacture Of Porous Articles, And Recovery And Treatment Of Waste Products (AREA)
  • Blow-Moulding Or Thermoforming Of Plastics Or The Like (AREA)
  • Orthopedics, Nursing, And Contraception (AREA)
  • Manufacture Of Macromolecular Shaped Articles (AREA)
  • Shaping By String And By Release Of Stress In Plastics And The Like (AREA)
US08/853,301 1997-05-09 1997-05-09 Method for forming a breathable film Abandoned USH2042H1 (en)

Priority Applications (22)

Application Number Priority Date Filing Date Title
US08/853,301 USH2042H1 (en) 1997-05-09 1997-05-09 Method for forming a breathable film
EP98915042A EP1007329B1 (en) 1997-05-09 1998-05-01 Method for forming a breathable film
PCT/IB1998/000663 WO1998051475A1 (en) 1997-05-09 1998-05-01 Method for forming a breathable film
CA002289671A CA2289671C (en) 1997-05-09 1998-05-01 Method for forming a breathable film
AU69322/98A AU6932298A (en) 1997-05-09 1998-05-01 Method for forming a breathable film
CN98806547A CN1261304A (zh) 1997-05-09 1998-05-01 透气薄膜的制造方法
HU0002241A HUP0002241A3 (en) 1997-05-09 1998-05-01 Method for forming a breathable film
JP10548963A JP2000512934A (ja) 1997-05-09 1998-05-01 通気性フィルムを成形するための方法
ES98915042T ES2187953T3 (es) 1997-05-09 1998-05-01 Metodo para formar una pelicula transpirable.
IDW991357A ID27385A (id) 1997-05-09 1998-05-01 Metode pembentukan film yang dapat bernafas
TR1999/02749T TR199902749T2 (xx) 1997-05-09 1998-05-01 Gaz faz� ge�irebilir bir filmin olu�turulmas� i�in y�ntem.
DE69808650T DE69808650T2 (de) 1997-05-09 1998-05-01 Verfahren zur herstellung einer atmungsfähigen folie
IL13271298A IL132712A0 (en) 1997-05-09 1998-05-01 Method for forming a breathable film
KR1019997010266A KR20010012314A (ko) 1997-05-09 1998-05-01 통기성 필름의 제조 방법
AT98915042T ATE225705T1 (de) 1997-05-09 1998-05-01 Verfahren zur herstellung einer atmungsfähigen folie
EG49598A EG21541A (en) 1997-05-09 1998-05-06 Method for forming a breathable film
ZA983870A ZA983870B (en) 1997-05-09 1998-05-07 Method for forming a breathable film
PE1998000353A PE86799A1 (es) 1997-05-09 1998-05-08 Metodo para formar una pelicula respirable
ARP980102178A AR017501A1 (es) 1997-05-09 1998-05-11 Metodo para formar una pelicula respirable
CO98026120A CO5050262A1 (es) 1997-05-09 1998-05-11 Metodo para formar una pelicula respirable
TW087107157A TW422781B (en) 1997-05-09 1998-06-16 Method for forming a breathable film
NO995466A NO995466L (no) 1997-05-09 1999-11-08 Fremgangsmåte for forming av en pustende film

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
US08/853,301 USH2042H1 (en) 1997-05-09 1997-05-09 Method for forming a breathable film

Publications (1)

Publication Number Publication Date
USH2042H1 true USH2042H1 (en) 2002-08-06

Family

ID=25315664

Family Applications (1)

Application Number Title Priority Date Filing Date
US08/853,301 Abandoned USH2042H1 (en) 1997-05-09 1997-05-09 Method for forming a breathable film

Country Status (22)

Country Link
US (1) USH2042H1 (ja)
EP (1) EP1007329B1 (ja)
JP (1) JP2000512934A (ja)
KR (1) KR20010012314A (ja)
CN (1) CN1261304A (ja)
AR (1) AR017501A1 (ja)
AT (1) ATE225705T1 (ja)
AU (1) AU6932298A (ja)
CA (1) CA2289671C (ja)
CO (1) CO5050262A1 (ja)
DE (1) DE69808650T2 (ja)
EG (1) EG21541A (ja)
ES (1) ES2187953T3 (ja)
HU (1) HUP0002241A3 (ja)
ID (1) ID27385A (ja)
IL (1) IL132712A0 (ja)
NO (1) NO995466L (ja)
PE (1) PE86799A1 (ja)
TR (1) TR199902749T2 (ja)
TW (1) TW422781B (ja)
WO (1) WO1998051475A1 (ja)
ZA (1) ZA983870B (ja)

Cited By (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20030091796A1 (en) * 1999-12-22 2003-05-15 Uni-Charm Corporation Absorbent article with back sheet, and method for manufacturing the back sheet
US20050279470A1 (en) * 2004-06-21 2005-12-22 Redd Charles A Fibrous structures comprising a tuft
US20060008619A1 (en) * 2002-12-06 2006-01-12 Ewen Campbell Liner with different impressments at opposing surfaces
US20060144413A1 (en) * 2003-07-28 2006-07-06 Aderans Co., Ltd. Double-faced adhesive tape and wing with the same
US20060228969A1 (en) * 2005-04-07 2006-10-12 Erdman Edward P Elastic laminate
WO2012148916A1 (en) * 2011-04-25 2012-11-01 The Glad Products Company Thermoplastic films with visually-distinct stretched regions and methods for making the same

Families Citing this family (15)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US6383431B1 (en) * 1997-04-04 2002-05-07 The Procter & Gamble Company Method of modifying a nonwoven fibrous web for use as component of a disposable absorbent article
US6605172B1 (en) 1999-09-30 2003-08-12 The Procter & Gamble Company Method of making a breathable and liquid impermeable web
US20070202767A1 (en) 2006-02-24 2007-08-30 Anderson Barry J Method of making laminate structures for mechanical activation
SE515473C2 (sv) * 1999-12-21 2001-08-13 Cardia Innovation Ab Förfarande och anordning för att skapa en skyddande atmosfär i en volym
AU2301001A (en) * 2000-01-10 2001-07-24 Clopay Plastic Products Company, Inc. Antibacterial microporous film and method of making
MXPA03004503A (es) * 2000-11-22 2003-09-05 Clopay Plastic Prod Co Peliculas biodegradables permeables al aire y al vapor de humedad y metodo de fabricacion.
CN1460058A (zh) * 2001-02-06 2003-12-03 三井化学株式会社 多孔薄膜及其制造方法
JP2002316359A (ja) * 2001-04-23 2002-10-29 Mitsui Chemicals Inc 多孔フィルム・不織布複合シート及びその製造方法
KR100758843B1 (ko) * 2002-08-29 2007-09-19 더 프록터 앤드 갬블 캄파니 저밀도 고로프트 부직포 기재
DE20311313U1 (de) 2003-07-23 2003-10-02 RKW AG Rheinische Kunststoffwerke, 67547 Worms Perforierter Film mit strukturierter Oberfläche
KR20050088034A (ko) * 2004-02-28 2005-09-01 주식회사 한진피앤씨 개공필름 합지 흡수지 복합체
TWI499497B (zh) * 2008-01-17 2015-09-11 Ole-Bendt Rasmussen 展現織物性質的膜材料以及用於其之製造的方法及裝置
JP5566157B2 (ja) 2010-03-30 2014-08-06 ユニ・チャーム株式会社 透湿性及び防水性を有するフィルム、並びにその製造方法
CN103415391A (zh) 2011-03-18 2013-11-27 宝洁公司 多层聚合物膜及其形成方法
KR101949220B1 (ko) 2016-12-20 2019-02-19 주식회사 폴트리 통기성 합지 필름 및 이의 제조방법

Citations (37)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3156242A (en) 1962-03-29 1964-11-10 Johnson & Johnson Flexible absorbent sheet
US3511742A (en) 1963-08-28 1970-05-12 Rasmussen O B Foraminous plastic sheet made by successive transverse shearing of extruding polymer stream with method and apparatus for making same
US3542634A (en) 1969-06-17 1970-11-24 Kendall & Co Apertured,bonded,and differentially embossed non-woven fabrics
US3697367A (en) 1969-12-31 1972-10-10 Kimberly Clark Co Low density composite polymer film
US3839516A (en) 1971-06-25 1974-10-01 Res Triangle Inst Process for the preparation of opencelled microporous films
US3843479A (en) 1970-12-29 1974-10-22 Toyo Boseki Composite film
US3881489A (en) 1973-08-20 1975-05-06 Procter & Gamble Breathable, liquid inpervious backsheet for absorptive devices
US3932682A (en) 1970-06-04 1976-01-13 Celanese Corporation Air permeable waterproof products having fabric-like aesthetic properties and methods for making the same
US3989867A (en) 1973-02-16 1976-11-02 The Procter & Gamble Company Absorptive devices having porous backsheet
US4056639A (en) 1976-07-09 1977-11-01 Presto Products Incorporated Preserving red color in fresh red meats
US4101625A (en) 1977-01-10 1978-07-18 Fmc Corporation Method for making corrugated molecularly oriented plastic strapping
US4116892A (en) 1975-03-31 1978-09-26 Biax-Fiberfilm Corporation Process for stretching incremental portions of an orientable thermoplastic substrate and product thereof
US4144008A (en) 1975-03-31 1979-03-13 Biax-Fiberfilm Corporation Apparatus for stretching a tubularly-formed sheet of thermoplastic material
US4153751A (en) 1975-03-31 1979-05-08 Biax-Fiberfilm Corporation Process for stretching an impregnated film of material and the microporous product produced thereby
US4223059A (en) 1975-03-31 1980-09-16 Biax Fiberfilm Corporation Process and product thereof for stretching a non-woven web of an orientable polymeric fiber
US4223063A (en) 1979-03-02 1980-09-16 Sabee Reinhardt N Pattern drawing of webs, and product produced thereby
US4285100A (en) 1975-03-31 1981-08-25 Biax Fiberfilm Corporation Apparatus for stretching a non-woven web or an orientable polymeric material
US4289832A (en) 1975-03-31 1981-09-15 Biax Fiberfilm Corp. Chemically-impregnated microporous films
US4341216A (en) 1981-02-27 1982-07-27 The Procter & Gamble Company Breathable backsheet for disposable diapers
US4350655A (en) 1977-05-05 1982-09-21 Biax Fiberfilm Process for producing highly porous thermoplastic films
US4368565A (en) 1978-03-28 1983-01-18 Biax-Fiberfilm Corporation Grooved roller assembly for laterally stretching film
US4438167A (en) 1979-10-15 1984-03-20 Biax Fiberfilm Corporation Novel porous fabric
US4648876A (en) 1982-09-24 1987-03-10 Personal Products Company Breathable panty liner
US4695484A (en) 1984-12-07 1987-09-22 Dai-Ichi Kogyo Seiyaku Co., Ltd. Process for forming moisture-permeable waterproof coating on fabrics
US4815714A (en) 1986-08-04 1989-03-28 El Paso Products Company Process for the manufacture of microporous film
US4878974A (en) 1988-02-05 1989-11-07 Tonen Sekiyukagaku Kabushiki Kaisha Method of producing a gas-permeable, waterproof composite sheet
US4929303A (en) * 1987-03-11 1990-05-29 Exxon Chemical Patents Inc. Composite breathable housewrap films
US4940462A (en) 1988-02-26 1990-07-10 Mcneil-Ppc, Inc. Sanitary napkin with expandable flaps
EP0467184A1 (en) 1990-07-06 1992-01-22 McNEIL-PPC, INC. Form retentive absorbent pads
US5125918A (en) 1988-04-14 1992-06-30 Mcneil-Ppc, Inc. Sanitary napkin having an attachment system comprising biased hinges
US5143774A (en) 1989-09-01 1992-09-01 Clopay Corporation Nonwoven fibrous embossed plastic film
EP0511905A1 (fr) 1991-04-29 1992-11-04 Kaysersberg Sa Serviette périodique à souflets latéraux
US5209801A (en) 1988-09-19 1993-05-11 Weyerhaeuser Company Method of forming a disposable elastic structure
US5234422A (en) 1991-12-20 1993-08-10 The Procter & Gamble Company Elasticized sanitary napkin
US5344691A (en) 1990-03-30 1994-09-06 Minnesota Mining And Manufacturing Company Spatially modified elastic laminates
US5422178A (en) 1992-06-19 1995-06-06 Minnesota Mining And Manufacturing Company Elastic film laminate
US5518801A (en) 1993-08-03 1996-05-21 The Procter & Gamble Company Web materials exhibiting elastic-like behavior

Family Cites Families (19)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3484835A (en) * 1968-06-25 1969-12-16 Clopay Corp Embossed plastic film
DE2641533A1 (de) * 1975-09-17 1977-03-31 Biax Fiberfilm Corp Verfahren zum strecken eines thermoplastischen materials
JPS61209129A (ja) * 1985-03-01 1986-09-17 Tokuyama Soda Co Ltd 部分的に微多孔性を有するシ−トの製造方法
JPH0676501B2 (ja) * 1986-05-28 1994-09-28 三井東圧化学株式会社 多孔性フイルムの製造方法
JPH0689163B2 (ja) * 1986-12-26 1994-11-09 三井東圧化学株式会社 多孔性フイルムの製造方法
JPH0689164B2 (ja) * 1986-12-26 1994-11-09 三井東圧化学株式会社 多孔性フイルムの製造方法
JPH0684451B2 (ja) * 1986-09-08 1994-10-26 大日本印刷株式会社 柔軟性を有する透湿防水性フイルムの製造方法
JPS63182135A (ja) * 1987-01-26 1988-07-27 Mitsui Toatsu Chem Inc 凹凸模様を有する多孔性フイルムの製造方法
US4842794A (en) * 1987-07-30 1989-06-27 Applied Extrusion Technologies, Inc. Method of making apertured films and net like fabrics
JPS6449620A (en) * 1987-08-20 1989-02-27 Mitsui Toatsu Chemicals Manufacture of holey film
GB8809077D0 (en) * 1988-04-18 1988-05-18 Rasmussen O B Polymeric bags & methods & apparatus for their production
EP0350034A3 (de) * 1988-07-08 1992-01-15 Bruno Gruber Strukturierte Folie aus Kunststoff, insbesondere thermoplastischer Kunststoff wie z.b. Polyäthylen sowie Verfahren und Vorrichtung zu ihrer Herstellung
ES2055593T3 (es) * 1990-02-12 1994-08-16 Clopay Corp Pelicula de plastico grabada en relieve ultra suave y con apariencia de tejido.
JPH0812792A (ja) * 1994-06-28 1996-01-16 Daio Paper Corp エンボス付与微細・多孔フィルムの製造方法
JP3628376B2 (ja) * 1995-05-02 2005-03-09 花王株式会社 多孔性シート及びその製法並びにそれを用いた吸収性物品
JPH08300498A (ja) * 1995-05-11 1996-11-19 Kao Corp 多孔性シート及びその製造方法並びに該多孔性シートを用いた吸収性物品
JP3526971B2 (ja) * 1995-06-22 2004-05-17 花王株式会社 多孔性シート及びその製造方法
EP0861152B1 (en) * 1995-10-23 1999-12-22 Clopay Plastic Products Company, Inc. Product, apparatus and process for strip lamination of a polymer film and a nonwoven web
JPH09206331A (ja) * 1996-02-02 1997-08-12 Kao Corp 多孔性シート及びそれを用いた吸収性物品

Patent Citations (38)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3156242A (en) 1962-03-29 1964-11-10 Johnson & Johnson Flexible absorbent sheet
US3511742A (en) 1963-08-28 1970-05-12 Rasmussen O B Foraminous plastic sheet made by successive transverse shearing of extruding polymer stream with method and apparatus for making same
US3542634A (en) 1969-06-17 1970-11-24 Kendall & Co Apertured,bonded,and differentially embossed non-woven fabrics
US3697367A (en) 1969-12-31 1972-10-10 Kimberly Clark Co Low density composite polymer film
US3932682A (en) 1970-06-04 1976-01-13 Celanese Corporation Air permeable waterproof products having fabric-like aesthetic properties and methods for making the same
US3843479A (en) 1970-12-29 1974-10-22 Toyo Boseki Composite film
US3839516A (en) 1971-06-25 1974-10-01 Res Triangle Inst Process for the preparation of opencelled microporous films
US3989867A (en) 1973-02-16 1976-11-02 The Procter & Gamble Company Absorptive devices having porous backsheet
US3881489A (en) 1973-08-20 1975-05-06 Procter & Gamble Breathable, liquid inpervious backsheet for absorptive devices
US4285100A (en) 1975-03-31 1981-08-25 Biax Fiberfilm Corporation Apparatus for stretching a non-woven web or an orientable polymeric material
US4116892A (en) 1975-03-31 1978-09-26 Biax-Fiberfilm Corporation Process for stretching incremental portions of an orientable thermoplastic substrate and product thereof
US4144008A (en) 1975-03-31 1979-03-13 Biax-Fiberfilm Corporation Apparatus for stretching a tubularly-formed sheet of thermoplastic material
US4153751A (en) 1975-03-31 1979-05-08 Biax-Fiberfilm Corporation Process for stretching an impregnated film of material and the microporous product produced thereby
US4223059A (en) 1975-03-31 1980-09-16 Biax Fiberfilm Corporation Process and product thereof for stretching a non-woven web of an orientable polymeric fiber
US4289832A (en) 1975-03-31 1981-09-15 Biax Fiberfilm Corp. Chemically-impregnated microporous films
US4056639A (en) 1976-07-09 1977-11-01 Presto Products Incorporated Preserving red color in fresh red meats
US4101625A (en) 1977-01-10 1978-07-18 Fmc Corporation Method for making corrugated molecularly oriented plastic strapping
US4350655A (en) 1977-05-05 1982-09-21 Biax Fiberfilm Process for producing highly porous thermoplastic films
US4368565A (en) 1978-03-28 1983-01-18 Biax-Fiberfilm Corporation Grooved roller assembly for laterally stretching film
US4223063A (en) 1979-03-02 1980-09-16 Sabee Reinhardt N Pattern drawing of webs, and product produced thereby
US4438167A (en) 1979-10-15 1984-03-20 Biax Fiberfilm Corporation Novel porous fabric
US4341216A (en) 1981-02-27 1982-07-27 The Procter & Gamble Company Breathable backsheet for disposable diapers
US4648876A (en) 1982-09-24 1987-03-10 Personal Products Company Breathable panty liner
US4695484A (en) 1984-12-07 1987-09-22 Dai-Ichi Kogyo Seiyaku Co., Ltd. Process for forming moisture-permeable waterproof coating on fabrics
US4815714A (en) 1986-08-04 1989-03-28 El Paso Products Company Process for the manufacture of microporous film
US4929303A (en) * 1987-03-11 1990-05-29 Exxon Chemical Patents Inc. Composite breathable housewrap films
US4878974A (en) 1988-02-05 1989-11-07 Tonen Sekiyukagaku Kabushiki Kaisha Method of producing a gas-permeable, waterproof composite sheet
US4940462A (en) 1988-02-26 1990-07-10 Mcneil-Ppc, Inc. Sanitary napkin with expandable flaps
US5125918A (en) 1988-04-14 1992-06-30 Mcneil-Ppc, Inc. Sanitary napkin having an attachment system comprising biased hinges
US5209801A (en) 1988-09-19 1993-05-11 Weyerhaeuser Company Method of forming a disposable elastic structure
US5143774A (en) 1989-09-01 1992-09-01 Clopay Corporation Nonwoven fibrous embossed plastic film
US5344691A (en) 1990-03-30 1994-09-06 Minnesota Mining And Manufacturing Company Spatially modified elastic laminates
EP0467184A1 (en) 1990-07-06 1992-01-22 McNEIL-PPC, INC. Form retentive absorbent pads
EP0511905A1 (fr) 1991-04-29 1992-11-04 Kaysersberg Sa Serviette périodique à souflets latéraux
US5234422A (en) 1991-12-20 1993-08-10 The Procter & Gamble Company Elasticized sanitary napkin
US5422178A (en) 1992-06-19 1995-06-06 Minnesota Mining And Manufacturing Company Elastic film laminate
US5518801A (en) 1993-08-03 1996-05-21 The Procter & Gamble Company Web materials exhibiting elastic-like behavior
US5723087A (en) * 1993-08-03 1998-03-03 The Procter & Gamble Company Web materials exhibiting elastic-like behavior

Cited By (11)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20030091796A1 (en) * 1999-12-22 2003-05-15 Uni-Charm Corporation Absorbent article with back sheet, and method for manufacturing the back sheet
US20060008619A1 (en) * 2002-12-06 2006-01-12 Ewen Campbell Liner with different impressments at opposing surfaces
US20060144413A1 (en) * 2003-07-28 2006-07-06 Aderans Co., Ltd. Double-faced adhesive tape and wing with the same
US7909041B2 (en) * 2003-07-28 2011-03-22 Unihair Co., Ltd. Double-faced adhesive tape and wing with the same
US20050279470A1 (en) * 2004-06-21 2005-12-22 Redd Charles A Fibrous structures comprising a tuft
US7754050B2 (en) * 2004-06-21 2010-07-13 The Procter + Gamble Company Fibrous structures comprising a tuft
US20060228969A1 (en) * 2005-04-07 2006-10-12 Erdman Edward P Elastic laminate
WO2012148916A1 (en) * 2011-04-25 2012-11-01 The Glad Products Company Thermoplastic films with visually-distinct stretched regions and methods for making the same
CN103648750A (zh) * 2011-04-25 2014-03-19 格拉德产品公司 具有视觉上相异的拉伸区域的热塑性膜及其制造方法
CN103648750B (zh) * 2011-04-25 2016-08-24 格拉德产品公司 具有视觉上相异的拉伸区域的热塑性膜及其制造方法
AU2012249908B2 (en) * 2011-04-25 2017-02-23 The Glad Products Company Thermoplastic films with visually-distinct stretched regions and methods for making the same

Also Published As

Publication number Publication date
IL132712A0 (en) 2001-03-19
AR017501A1 (es) 2001-09-12
TR199902749T2 (xx) 2000-07-21
HUP0002241A2 (hu) 2000-11-28
WO1998051475A1 (en) 1998-11-19
EG21541A (en) 2001-11-28
NO995466D0 (no) 1999-11-08
EP1007329B1 (en) 2002-10-09
HUP0002241A3 (en) 2001-01-29
DE69808650T2 (de) 2003-06-18
ZA983870B (en) 1998-11-13
KR20010012314A (ko) 2001-02-15
JP2000512934A (ja) 2000-10-03
CA2289671C (en) 2004-07-13
EP1007329A1 (en) 2000-06-14
ATE225705T1 (de) 2002-10-15
NO995466L (no) 1999-12-16
ES2187953T3 (es) 2003-06-16
ID27385A (id) 2001-04-05
CO5050262A1 (es) 2001-06-27
TW422781B (en) 2001-02-21
CN1261304A (zh) 2000-07-26
DE69808650D1 (de) 2002-11-14
PE86799A1 (es) 1999-10-21
CA2289671A1 (en) 1998-11-19
AU6932298A (en) 1998-12-08

Similar Documents

Publication Publication Date Title
USH2042H1 (en) Method for forming a breathable film
US10206828B2 (en) Breathable and liquid impermeable web and method of making the web
US6258308B1 (en) Process for adjusting WVTR and other properties of a polyolefin film
TW464604B (en) Method of modifying a nonwoven fibrous web for use as a component of a disposable absorbent article
EP1578847B1 (en) Breathable, extensible films made with two-component single resins
JP2004507384A (ja) 一方向に弾性があり別の方向に伸張性がある複合弾性体
EP1040217B1 (en) Breathable web materials having cloth-like texture
MXPA99010300A (en) Method for forming a breathable film
CZ390199A3 (cs) Způsob výroby prodyšného filmu
MXPA01009510A (en) Method of modifying a nonwoven fibrous web for use as a component of a disposable absorbent article

Legal Events

Date Code Title Description
AS Assignment

Owner name: PROCTER & GAMBLE COMPANY, THE, OHIO

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:DOBRIN, GEORGE C.;GOENS, THOMAS M.;PHILLIPS, DONNA S.;AND OTHERS;REEL/FRAME:008996/0017

Effective date: 19970822

STCF Information on status: patent grant

Free format text: PATENTED CASE