US20220259705A1 - Magnesium alloy and method for producing same - Google Patents

Magnesium alloy and method for producing same Download PDF

Info

Publication number
US20220259705A1
US20220259705A1 US17/625,359 US202017625359A US2022259705A1 US 20220259705 A1 US20220259705 A1 US 20220259705A1 US 202017625359 A US202017625359 A US 202017625359A US 2022259705 A1 US2022259705 A1 US 2022259705A1
Authority
US
United States
Prior art keywords
magnesium alloy
magnesium
heat treatment
aluminum
strength
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
US17/625,359
Other languages
English (en)
Inventor
Stefan Gneiger
Clemens SIMSON
Simon Frank
Alexander GROßALBER
Andreas Betz
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
LKR Leichtmetallkompetenzzentrum Ranshofen GmbH
Original Assignee
LKR Leichtmetallkompetenzzentrum Ranshofen GmbH
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by LKR Leichtmetallkompetenzzentrum Ranshofen GmbH filed Critical LKR Leichtmetallkompetenzzentrum Ranshofen GmbH
Assigned to LKR LEICHTMETALLKOMPETENZZENTRUM RANSHOFEN GMBH reassignment LKR LEICHTMETALLKOMPETENZZENTRUM RANSHOFEN GMBH ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: BETZ, ANDREAS, FRANK, SIMON, Gneiger, Stefan, GROSSALBER, Alexander, Simson, Clemens
Publication of US20220259705A1 publication Critical patent/US20220259705A1/en
Pending legal-status Critical Current

Links

Images

Classifications

    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C23/00—Alloys based on magnesium
    • C22C23/02—Alloys based on magnesium with aluminium as the next major constituent
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C23/00—Alloys based on magnesium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C14/00—Alloys based on titanium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C21/00—Alloys based on aluminium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C21/00—Alloys based on aluminium
    • C22C21/02—Alloys based on aluminium with silicon as the next major constituent
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C21/00—Alloys based on aluminium
    • C22C21/06—Alloys based on aluminium with magnesium as the next major constituent
    • C22C21/08—Alloys based on aluminium with magnesium as the next major constituent with silicon
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C21/00—Alloys based on aluminium
    • C22C21/10—Alloys based on aluminium with zinc as the next major constituent
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C21/00—Alloys based on aluminium
    • C22C21/12—Alloys based on aluminium with copper as the next major constituent
    • C22C21/16—Alloys based on aluminium with copper as the next major constituent with magnesium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C24/00—Alloys based on an alkali or an alkaline earth metal
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C9/00—Alloys based on copper
    • C22C9/04—Alloys based on copper with zinc as the next major constituent
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22F—CHANGING THE PHYSICAL STRUCTURE OF NON-FERROUS METALS AND NON-FERROUS ALLOYS
    • C22F1/00—Changing the physical structure of non-ferrous metals or alloys by heat treatment or by hot or cold working
    • C22F1/04—Changing the physical structure of non-ferrous metals or alloys by heat treatment or by hot or cold working of aluminium or alloys based thereon
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22F—CHANGING THE PHYSICAL STRUCTURE OF NON-FERROUS METALS AND NON-FERROUS ALLOYS
    • C22F1/00—Changing the physical structure of non-ferrous metals or alloys by heat treatment or by hot or cold working
    • C22F1/04—Changing the physical structure of non-ferrous metals or alloys by heat treatment or by hot or cold working of aluminium or alloys based thereon
    • C22F1/043—Changing the physical structure of non-ferrous metals or alloys by heat treatment or by hot or cold working of aluminium or alloys based thereon of alloys with silicon as the next major constituent
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22F—CHANGING THE PHYSICAL STRUCTURE OF NON-FERROUS METALS AND NON-FERROUS ALLOYS
    • C22F1/00—Changing the physical structure of non-ferrous metals or alloys by heat treatment or by hot or cold working
    • C22F1/04—Changing the physical structure of non-ferrous metals or alloys by heat treatment or by hot or cold working of aluminium or alloys based thereon
    • C22F1/047—Changing the physical structure of non-ferrous metals or alloys by heat treatment or by hot or cold working of aluminium or alloys based thereon of alloys with magnesium as the next major constituent
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22F—CHANGING THE PHYSICAL STRUCTURE OF NON-FERROUS METALS AND NON-FERROUS ALLOYS
    • C22F1/00—Changing the physical structure of non-ferrous metals or alloys by heat treatment or by hot or cold working
    • C22F1/04—Changing the physical structure of non-ferrous metals or alloys by heat treatment or by hot or cold working of aluminium or alloys based thereon
    • C22F1/05—Changing the physical structure of non-ferrous metals or alloys by heat treatment or by hot or cold working of aluminium or alloys based thereon of alloys of the Al-Si-Mg type, i.e. containing silicon and magnesium in approximately equal proportions
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22F—CHANGING THE PHYSICAL STRUCTURE OF NON-FERROUS METALS AND NON-FERROUS ALLOYS
    • C22F1/00—Changing the physical structure of non-ferrous metals or alloys by heat treatment or by hot or cold working
    • C22F1/06—Changing the physical structure of non-ferrous metals or alloys by heat treatment or by hot or cold working of magnesium or alloys based thereon
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22F—CHANGING THE PHYSICAL STRUCTURE OF NON-FERROUS METALS AND NON-FERROUS ALLOYS
    • C22F1/00—Changing the physical structure of non-ferrous metals or alloys by heat treatment or by hot or cold working
    • C22F1/16—Changing the physical structure of non-ferrous metals or alloys by heat treatment or by hot or cold working of other metals or alloys based thereon
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22F—CHANGING THE PHYSICAL STRUCTURE OF NON-FERROUS METALS AND NON-FERROUS ALLOYS
    • C22F1/00—Changing the physical structure of non-ferrous metals or alloys by heat treatment or by hot or cold working
    • C22F1/16—Changing the physical structure of non-ferrous metals or alloys by heat treatment or by hot or cold working of other metals or alloys based thereon
    • C22F1/18—High-melting or refractory metals or alloys based thereon
    • C22F1/183—High-melting or refractory metals or alloys based thereon of titanium or alloys based thereon

Definitions

  • the invention relates to a magnesium alloy.
  • the invention also relates to a method for producing a magnesium alloy.
  • magnesium alloys constitute frequently used structural alloys or structural materials, especially in the field of the automotive industry and aircraft industry. It is known that a ductility of magnesium alloys can be improved by adding lithium (Li), wherein a shift from a hexagonal crystal system to a body-centered cubic crystal system typically takes place in the magnesium alloy as the lithium amount increases. This is associated with an increased number of slip planes, whereby the occurrence of a markedly improved ductility as the lithium amount increases can be explained.
  • this approach can be accompanied by a reduction in the strength and corrosion resistance of the magnesium alloy, so that other alloying elements, such as aluminum or zinc for example, are often added in order to lessen these disadvantages and to normally achieve at least moderate strengths and corrosion resistances.
  • the object of the invention is to specify a magnesium alloy that has a high strength, in particular a high compressive strength, and a good deformability.
  • the object is attained with a magnesium alloy comprising, in particular being made from, (in at %)
  • the basis of the invention is the finding that, with an aforementioned alloy composition of a magnesium alloy having a corresponding amount of lithium (Li) as well as a mandatory amount of aluminum (Al) in a specific, aforementioned aluminum-to-magnesium ratio range, a micro-scale microstructure or a fine, in particular fine lamellar, microstructure forms in the magnesium alloy.
  • the theoretical foundation of these characteristics is considered to be a eutectic transformation of the magnesium alloy which occurs at an aforementioned ratio of aluminum to magnesium.
  • the fine-scale microstructure is accompanied by a high strength, in particular a high compressive strength, wherein a good deformability of the magnesium alloy is ensured at the same time at corresponding aforementioned amounts of lithium in the magnesium alloy.
  • the orientation composition or orientation line in the phase diagram is in particular a ratio of aluminum to magnesium (in atomic percent, abbreviated by at %) of approx. 3:6, since a particularly homogeneous fine-scale or homogeneous fine lamellar microstructure or morphology is found at this ratio.
  • the fine, in particular fine lamellar, microstructure or morphology is also found in a varyingly pronounced degree, which is accordingly normally associated with varyingly pronounced magnitudes of strength, in particular a magnitude of compressive strength, as well as deformability or ductility of the magnesium alloy. Because of these special morphological characteristics in the stated composition range, a formation of a magnesium alloy that has both a high strength, in particular compressive strength, and also a good deformability is thus enabled.
  • the magnesium alloy comprises (in at %) 30.0% to 60.0%, in particular 40% to 50%, lithium.
  • a pronounced strength and a particularly pronounced deformability can be achieved. This is likely due in particular to a combination of finely structured morphology and a transformation to a body-centered cubic crystal system in the stated lithium range.
  • a high strength and also a high deformability emerge particularly strongly if the magnesium alloy comprises (in at %) 45% to 50%, in particular 45% to 48%, lithium.
  • the magnesium alloy comprises (in at %) greater than 0.05%, in particular greater than 0.1%, normally greater than 1% aluminum.
  • magnesium-based alloy thereby denotes a magnesium alloy which, taking the alloy amounts thereof in percentage by weight (wt %) as a basis, contains magnesium as the main element or as the largest alloy amount.
  • wt % percentage by weight
  • magnesium alloy is (in at %) 30.0% to 60.0% lithium and a ratio of aluminum to magnesium (in at %) is 2.5:6 to 3.5:6, in particular 2.8:6 to 3.3:6, preferably approximately 3:6.
  • a particularly pronounced homogeneity can also be achieved if the magnesium alloy thereby comprises (in at %) 40.0% to 60.0% lithium.
  • the magnesium alloy comprises greater than 0.0 to 3.0 wt %, in particular greater than 0.0 to 2.0 wt %, preferably greater than 0.0 to 1.5 wt %, calcium (Ca).
  • a lower limit of content ranges, in particular those mentioned above, for calcium is greater than 0.05 wt %.
  • a reduced oxidation tendency of the magnesium alloy can thus be realized, advantageously typically in that a stable oxidation layer forms on a surface of the magnesium alloy.
  • a grain-refining effect in the magnesium alloy can be utilized or achieved so that a high stability of the fine-scale microstructure is achievable and a strength of the magnesium alloy can be further increased. Both a high oxidation resistance and also an increased strength or a stabilization of the strength properties can be achieved if the magnesium alloy comprises 0.5 wt % to 1.0 wt % calcium.
  • the effects stated above are in particular based on a formation of CaO. Accordingly, it can be specifically provided that calcium is added to the magnesium alloy as an alloy amount or contained in the magnesium alloy at least partially, in particularly predominantly, preferably completely, in the form of CaO. A homogeneous distribution of calcium or CaO in the magnesium alloy can thus be facilitated. It is thus particularly advantageous if the magnesium alloy comprises CaO with the amounts stated above for calcium.
  • the magnesium alloy comprises greater than 0.0 to 3.0 wt %, preferably 1.0 wt % to 2.0 wt %, rare earth metals, in particular yttrium (Y).
  • Y yttrium
  • a formation of Y 2 O 3 occurring in the magnesium alloy is of particular relevance. Accordingly, it can be specifically provided that yttrium is added to the magnesium alloy as an alloy amount or contained in the magnesium alloy at least partially, in particular predominantly, preferably completely, in the form of Y 2 O 3 . It is thus advantageous if the magnesium alloy comprises Y 2 O 3 with the amounts stated above for yttrium.
  • An oxidation tendency can be reduced in particular if both calcium, in particular in the form of CaO, and also rare earth metals, in particular yttrium, preferably in the form of Y 2 O 3 , are respectively contained in the magnesium alloy according to the aforementioned content ranges, wherein in particular calcium at greater than 0.0, in particular greater than 0.05 wt % to 1.5 wt %, and yttrium at 1.0 wt % to 2.0 wt % have proven effective.
  • a particularly pronounced corrosion resistance can be achieved if the magnesium alloy contains calcium and rare earth metals, in particular yttrium, wherein a total amount of calcium and rare earth metals, in particular yttrium, is greater than 0.0, in particular greater than 0.05 wt % to 3.0 wt %, preferably 1.0 wt % to 2.5 wt %.
  • a compressive strength of the magnesium alloy is at least 300 MPa, in particular at least 350 MPa, preferably at least 380 MPa, particularly preferably at least 400 MPa.
  • an alloy composition provided according to the invention for the magnesium alloy as a result of the finely structured microstructure thereof, in particular according to a production of the magnesium alloy by casting.
  • the aforementioned values apply to a maximum compressive strength, specifically for a compressive yield point or compressive yield strength, of the magnesium alloy.
  • the compressive strength or maximum compressive strength, or compressive yield point or compressive yield strength, of the magnesium alloy can be at least 410 MPa, specifically at least 430 MPa. This can typically be feasibly achieved with a heat treatment, in particular as described below.
  • the magnesium alloy has a good aging capacity, wherein a strength, in particular compressive strength, and/or a deformability of the magnesium alloy can be further optimized, or preferably increased, by heat treatment of the magnesium alloy. It is therefore advantageously provided that a specific compressive strength, in particular a maximum specific compressive strength, of the magnesium alloy, in particular at room temperature, in an aged state is at least 300 Nm/g, in particular at least 330 Nm/g, preferably at least 350 Nm/g.
  • the aged state thereby denotes a state of the magnesium alloy after a completed heat treatment of the magnesium alloy. Boundary conditions of the heat treatment that are beneficial thereto are further explained below, in particular as part of a method for producing a magnesium alloy, acid can be applied accordingly.
  • the stated material characteristics for the magnesium alloy primarily values for compressive strength or specific compressive strength, are thereby based in particular on a room temperature that typically lies between 20° C. and 25° C., normally approximately 20° C.
  • the magnesium alloy comprises 18.0 wt % to 24.0 wt %, in particular 18.0 wt % to 22 wt % lithium and 15.0 wt % to 30.0 wt %, in particular 16.5 wt % to 28.0 wt % aluminum.
  • a hardness of the magnesium alloy in particular as part of a heat treatment that is carried out, can be optimized or can be set in a targeted manner.
  • the magnesium alloy also comprises calcium at greater than 0.0, in particular greater than 0.05 wt %, to 2.5 wt %, in particular 0.1 wt % to 2.0 wt %, preferably 0.3 wt % to 1.5 wt %. It is thus possible not only to influence or improve a corrosion resistance or oxidation tendency using calcium specifically in this content range of lithium and aluminum, but also to influence a hardness of the magnesium alloy.
  • the magnesium alloy comprises 18.0 wt % to 22 wt % lithium and 16.5 wt % to 28.0 wt % aluminum, particularly prominently at 0.1 wt % to 2.0 wt %, in particular at 0.3 wt % to 1.5 wt %, calcium.
  • the hardness typically increases as a duration of heat treatment increases, so that a hardness of the magnesium alloy can be set as a function of a duration of the heat treatment. It is beneficial to a high hardness if a heat treatment between 200° C. and 450° C. has a heat treatment duration of greater than 1 hour, in particular greater than 3 hours.
  • an easily manageable and easily processable composition or magnesium alloy can be obtained if the magnesium alloy comprises 20 wt % lithium and 15.0 to 30.0 wt %, in particular 16.5 wt % to 28.0 wt %, particularly preferably 18.0 wt % to 0.26.0 wt %, aluminum. This is especially true if calcium is also contained in the magnesium alloy as stated above.
  • the mechanical properties of the magnesium alloy can be optimized for a specific intended application through additions of other alloying elements.
  • a strength, in particular the compressive strength, of the magnesium alloy it is beneficial if the magnesium alloy comprises 3.0 wt % to 10.0 wt % zinc.
  • An optimization of the compressive strength, in particular without notably limiting a deformability, can be achieved if the magnesium alloy comprises 7.0 wt % to 10.0 wt % zinc.
  • the magnesium alloy comprises 2.0 wt % to 10.0 wt %, preferably 3.0 wt % to 7.0 wt %, silicon.
  • a method for producing a magnesium alloy according to the invention normally involves starting materials of the magnesium alloy being mixed and, proceeding from a liquid or semi-liquid phase, being cooled.
  • the magnesium alloy according to the invention, or a feedstock, semi-finished product, or element having or being made from the magnesium alloy can easily be produced by means of typical casting processes, for example using mold casting processes, die-casting processes, continuous casting processes or permanent mold casting processes. It has proven advantageous in particular if the production of the magnesium alloy according to the invention comprises a heat treatment in order to optimize a microstructure or morphology of the magnesium alloy with regard to a strength, in particular compressive strength, or deformability.
  • the other object of the invention is attained with a method for producing a magnesium alloy according to the invention, wherein a heat treatment of the magnesium alloy is carried out in order to optimize or increase a strength, in particular compressive strength, and/or deformability of the magnesium alloy. It has been shown that, through a heat treatment of the magnesium alloy, a strength, in particular compressive strength, and deformability of the magnesium alloy can be further optimized or increased so that they can be set in a targeted manner in particular, preferably such that they are adjusted for an intended, application of the magnesium alloy.
  • the heat treatment is carried out at a temperature greater than 200° C., in particular between 200° C. and 450° C., for more than 20 minutes, in particular more than 1 hour.
  • a heat treatment at a temperature between 250° C. and 400° C., preferably between 270° C. and 350° C. has proven particularly suitable for a pronounced increase in strength, in particular compressive strength.
  • the heat treatment is carried out for more than 1 hour (h), preferably between 1 hour and 10 hours, particularly preferably between 1 hour and 6 hours, in order to efficiently set the strength.
  • a heat treatment between 300° C. and 350° C., preferably between 320° C.
  • a feedstock, semi-finished product, or element is advantageously realized having, in particular being made from, a magnesium alloy according to the invention or such that it is obtainable using a method according to the invention for producing a magnesium alloy according to the invention.
  • a feedstock, semi-finished product, or element formed with a magnesium alloy also has an advantageously high strength, in particular compressive strength, and good deformability.
  • FIG. 1 shows a schematic phase diagram illustration for Mg—Li—Al, in which composition ranges of the magnesium alloy according to the invention are indicated;
  • FIG. 2 shows a yield stress diagram of multiple magnesium alloy specimens from a magnesium alloy according to the invention
  • FIG. 3 and FIG. 4 show scanning electron microscope images of a magnesium alloy specimen from a magnesium alloy according to the invention at different magnifications
  • FIG. 5 shows a yield stress diagram of magnesium alloy specimens from a magnesium alloy according to the invention after completed heat treatments
  • FIG. 6 shows a yield stress diagram of magnesium alloy specimens from a further magnesium alloy according to the invention after completed heat treatments
  • FIG. 7 shows a hardness diagram of magnesium alloy specimens from a magnesium alloy according to the invention.
  • FIG. 1 shows a schematic phase diagram illustration (in at %) for magnesium-lithium-aluminum (Mg—Li—Al) according, to a typical ternary phase diagram design, wherein composition ranges or content ranges of alloy amounts of a magnesium alloy according to the invention are indicated.
  • 3:6 is depicted as dash-dotted line A, since in accordance with a finding on which the invention is based, a particularly homogeneous, fine-scale, in particular fine lamellar, microstructure or morphology is found in a content range of 15.0 at % to 70.0 at % lithium at this ratio of aluminum to magnesium. In a range encompassing this ratio, indicated by an aluminum-to-magnesium ratio (in at %) of 1:6 to 4:6, this fine-scale or finely structured microstructure is furthermore found in a varyingly pronounced degree and explains an advantageously high strength, in particular compressive strength, and good deformability of the magnesium alloy in this range.
  • a composition range (in at %) of 15.0% to 70.0% lithium and an aluminum-to-magnesium ratio (in at %) of 1:6 to 4:6 are illustrated clearly in FIG. 1 by a quadrangle depicted by a solid line, denoted by reference numeral 1.
  • a pronounced strength and particularly pronounced deformability are found in particular in a composition range (in at %) of 30.0% to 60.0% lithium and an aluminum-to-magnesium ratio (in at %) of 1:6 to 4:6.
  • This composition range is illustrated in FIG. 1 by a quadrangle depicted by a dashed line, denoted by reference numeral 2.
  • magnesium alloy specimens were produced by means of permanent mold casting, wherein in particular magnesium alloy specimens having a cylindrical shape, with a diameter of 5 mm and a length of 10 mm, were fabricated.
  • the magnesium alloy specimens were subjected to compression tests at room temperature, approximately 20° C. and yield curves which depict a yield stress, in MPa, as a function of a degree of deformation, in %, were calculated as a result.
  • FIG. 2 shows a yield stress diagram with yield curves as a result of compression tests at room temperature using magnesium alloy specimens fabricated from Mg-20% Li-15% Al-1% Ca-0.5% Y (in wt %).
  • Yield curves of magnesium alloy specimens immediately following a production of the magnesium alloy specimens (as cast) are illustrated, shown in FIG. 2 as solid lines, denoted by reference numeral 3.
  • yield curves of magnesium alloy specimens after a completed heat treatment (aged) of the magnesium alloy specimens are illustrated, shown in FIG. 2 as dashed lines, denoted by reference numeral 4.
  • magnesium alloy specimens were subjected to a heat treatment at 330° C. for 3 hours, and yield curves were then calculated by means of compression tests.
  • a clear influence of the heat treatment on the compressive strength and deformability of the magnesium alloy specimens is evident, as a result of which there is the potential to set the compressive strength, and deformability in an optimized manner using heat treatment, in particular for an eventual intended application.
  • FIG. 3 and FIG. 4 show scanning electron microscope images of the magnesium alloy specimens fabricated from Mg-20% Li-15% Al-1% Ca-0.5% Y (in wt %) at different magnifications.
  • light grain boundary phases in whitish-gray
  • a markedly different fine structure in particular in the proximity of the grain boundary phases.
  • FIG. 5 shows a yield stress diagram with yield curves as a result of compression tests at room temperature using magnesium alloy specimens fabricated from Mg-20% Li-15% Al-1% Ca-0.5% Y (in wt %), wherein magnesium alloy specimens were examined after completed heat treatments at different heat treatment temperatures.
  • Yield curves of magnesium alloy specimens which were subjected to a heat treatment at 270° C. for 4 hours are illustrated, depicted in FIG. 5 as dashed lines, denoted by reference numeral 5, and yield curves of magnesium alloy specimens which were subjected to a heat treatment at 330° C. for 4 hours, depicted in FIG. 5 as solid lines, denoted by reference numeral 6.
  • FIG. 6 shows a yield stress diagram with yield curves as a result of compression tests at room temperature using magnesium alloy specimens fabricated from Mg-20% Li-15% Al-1% Ca-0.5% Y (in wt %), wherein magnesium alloy specimens were examined after completed heat treatments at different heat treatment temperatures.
  • Yield curves of magnesium alloy specimens which were subjected to a heat treatment at 270° C. for 4 hours are illustrated, depicted in FIG. 6 as dashed lines, denoted by reference numeral 7, and yield curves of magnesium alloy specimens which were subjected to a heat treatment at 330° C. for 4 hours, depicted in FIG. 6 as solid lines, denoted by reference numeral 8.
  • FIG. 6 shows a yield stress diagram with yield curves as a result of compression tests at room temperature using magnesium alloy specimens fabricated from Mg-20% Li-15% Al-1% Ca-0.5% Y (in wt %), wherein magnesium alloy specimens were examined after completed heat treatments at different heat treatment temperatures.
  • FIG. 7 shows a hardness diagram as a result of Vickers hardness tests at room temperature, approximately 20° C., using magnesium alloy specimens fabricated from Mg-20% Li-15% Al-1% Ca-0.5% Y (in wt %), wherein magnesium alloy specimens were examined after completed heat treatments with different heat treatment durations. 330° C. was used as a heat treatment temperature.
  • mean values of Vickers hardnesses (HV 0.1) from multiple measurements are respectively shown as a function of different heat treatment durations t, from 0 minutes (min) to 300 minutes, of the magnesium alloy specimens.
  • a magnesium alloy according to the invention thus advantageously exhibits both a high strength and also a good deformability, both of which can be optimized, or preferably increased, by means of heat treatment in particular. Specifically, there is also the possibility of optimizing, or setting in a defined manner, a hardness of the magnesium alloy.
  • the magnesium alloy according to the invention, or an element having or being made from the magnesium alloy according to the invention thus offers the potential to realize, preferably such that they suit a purpose, robust and resilient components, especially structural components, in particular in the automotive industry, aircraft industry, and/or space industry.

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Materials Engineering (AREA)
  • Mechanical Engineering (AREA)
  • Metallurgy (AREA)
  • Organic Chemistry (AREA)
  • Physics & Mathematics (AREA)
  • Thermal Sciences (AREA)
  • Crystallography & Structural Chemistry (AREA)
  • Powder Metallurgy (AREA)
  • Continuous Casting (AREA)
  • Forging (AREA)
US17/625,359 2019-07-08 2020-03-25 Magnesium alloy and method for producing same Pending US20220259705A1 (en)

Applications Claiming Priority (3)

Application Number Priority Date Filing Date Title
EP19184999.1 2019-07-08
EP19184999.1A EP3763845B1 (de) 2019-07-08 2019-07-08 Magnesiumlegierung und verfahren zur herstellung derselben
PCT/EP2020/058280 WO2021004662A1 (de) 2019-07-08 2020-03-25 Magnesiumlegierung und verfahren zur herstellung derselben

Publications (1)

Publication Number Publication Date
US20220259705A1 true US20220259705A1 (en) 2022-08-18

Family

ID=67211617

Family Applications (2)

Application Number Title Priority Date Filing Date
US17/625,359 Pending US20220259705A1 (en) 2019-07-08 2020-03-25 Magnesium alloy and method for producing same
US17/625,360 Pending US20220267881A1 (en) 2019-07-08 2020-07-07 Alloy having fine-scale eutectic, in particular nanoeutectic, structure and production of such an alloy

Family Applications After (1)

Application Number Title Priority Date Filing Date
US17/625,360 Pending US20220267881A1 (en) 2019-07-08 2020-07-07 Alloy having fine-scale eutectic, in particular nanoeutectic, structure and production of such an alloy

Country Status (7)

Country Link
US (2) US20220259705A1 (zh)
EP (2) EP3763845B1 (zh)
JP (2) JP2022540542A (zh)
KR (2) KR20220030244A (zh)
CN (2) CN114026260B (zh)
CA (2) CA3137604A1 (zh)
WO (2) WO2021004662A1 (zh)

Family Cites Families (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
GB683813A (en) * 1949-09-29 1952-12-03 Magnesium Elektron Ltd Improvements in or relating to magnesium base alloys
DE1255928B (de) * 1966-01-13 1967-12-07 Metallgesellschaft Ag Verfahren zur Erzielung eines langanhaltenden Veredelungseffektes in Aluminium-Silicium-Legierungen
CN104060137A (zh) * 2014-06-29 2014-09-24 应丽红 一种耐磨硅铝合金
JP6794264B2 (ja) * 2015-01-27 2020-12-02 株式会社三徳 マグネシウム−リチウム合金、圧延材及び成型品
JP6768637B2 (ja) * 2015-03-25 2020-10-14 株式会社Ｓｕｂａｒｕ マグネシウム−リチウム合金、マグネシウム−リチウム合金からなる圧延材及びマグネシウム−リチウム合金を素材として含む被加工品
CN108352513B (zh) * 2015-11-10 2019-10-01 日产自动车株式会社 电气设备用负极活性物质和使用了其的电气设备
JP6290520B1 (ja) * 2016-07-26 2018-03-07 株式会社三徳 マグネシウム−リチウム合金及びマグネシウム空気電池
CN106148786B (zh) * 2016-08-22 2018-12-18 上海交通大学 高强度铸造镁锂合金及其制备方法

Also Published As

Publication number Publication date
CN114096690A (zh) 2022-02-25
CN114026260A (zh) 2022-02-08
JP2022540544A (ja) 2022-09-16
EP3997251A1 (de) 2022-05-18
CN114026260B (zh) 2023-06-20
EP3763845B1 (de) 2021-08-18
EP3763845A1 (de) 2021-01-13
WO2021004662A1 (de) 2021-01-14
KR20220030244A (ko) 2022-03-10
CA3138658A1 (en) 2021-01-14
WO2021005062A1 (de) 2021-01-14
JP2022540542A (ja) 2022-09-16
CA3137604A1 (en) 2021-01-14
KR20220030243A (ko) 2022-03-10
US20220267881A1 (en) 2022-08-25

Similar Documents

Publication Publication Date Title
Jiang et al. Microstructure and mechanical properties of WE43 magnesium alloy fabricated by direct-chill casting
Socjusz-Podosek et al. Effect of yttrium on structure and mechanical properties of Mg alloys
Zhao et al. Effect of Y content on microstructure and mechanical properties of as-cast Mg–8Li–3Al–2Zn alloy with duplex structure
Wu et al. Effects of Ce-rich RE additions and heat treatment on the microstructure and tensile properties of Mg–Li–Al–Zn-based alloy
Zhang et al. Microstructures and mechanical properties of heat-resistant high-pressure die-cast Mg–4Al–xLa–0.3 Mn (x= 1, 2, 4, 6) alloys
Pan et al. High-conductivity binary Mg–Zn sheet processed by cold rolling and subsequent aging
JP5252583B2 (ja) Ｍｇ合金およびその製造方法
Bhattacharjee et al. Effect of microalloyed Zr on the extruded microstructure of Mg–6.2 Zn-based alloys
Zhang et al. Microstructures and mechanical properties of heat-resistant HPDC Mg–4Al-based alloys containing cheap misch metal
JIANG et al. Effect of neodymium, gadolinium addition on microstructure and mechanical properties of AZ80 magnesium alloy
Hu et al. Microstructure and mechanical properties of Mg–Gd–Zr alloys with low gadolinium contents
Liu et al. Ageing behavior and mechanisms of strengthening and toughening of ultrahigh-strength Mg-Gd-Y-Zn-Mn alloy
Xu et al. Effect of Sr content on microstructure and mechanical properties of Mg-Li-Al-Mn alloy
WO2009039581A1 (en) Permanent mould cast magnesium alloy
Khan et al. Formation of nanoscaled precipitates and their effects on the high-temperature shape-memory characteristics of a Ti50Ni15Pd25Cu10 alloy
JP2010196112A (ja) 高強度Ａｌ−Ｃｕ−Ｍｇ合金押出材およびその製造方法
Chen et al. Alloying behavior of erbium in an Al–Cu–Mg alloy
Zhang et al. Mechanical properties and damping capacity after grain refinement in A356 alloy
Trojanova et al. Tensile and fracture properties of an Mg-RE-Zn alloy at elevated temperatures
US20220259705A1 (en) Magnesium alloy and method for producing same
JP5404391B2 (ja) Ｍｇ基合金
Huang et al. Microstructure and mechanical properties of strontium-modified ADC12 alloy processed by heat treatment
CN109477169B (zh) 铝合金塑性加工材料及其制造方法
JP5419061B2 (ja) マグネシウム合金
Rogachev et al. Thermal Stability of Al-Ca and Al-Ce Alloys Obtained by High-Pressure Torsion

Legal Events

Date Code Title Description
AS Assignment

Owner name: LKR LEICHTMETALLKOMPETENZZENTRUM RANSHOFEN GMBH, AUSTRIA

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:GNEIGER, STEFAN;SIMSON, CLEMENS;FRANK, SIMON;AND OTHERS;REEL/FRAME:058596/0104

Effective date: 20211027

STPP Information on status: patent application and granting procedure in general

Free format text: DOCKETED NEW CASE - READY FOR EXAMINATION