US20190218359A1 - Use of geopolymeric additive in combination with non-brominated flame retardant in polymer foams - Google Patents

Use of geopolymeric additive in combination with non-brominated flame retardant in polymer foams Download PDF

Info

Publication number
US20190218359A1
US20190218359A1 US16/319,182 US201716319182A US2019218359A1 US 20190218359 A1 US20190218359 A1 US 20190218359A1 US 201716319182 A US201716319182 A US 201716319182A US 2019218359 A1 US2019218359 A1 US 2019218359A1
Authority
US
United States
Prior art keywords
geopolymer
flame retardants
additive
phosphorus
polymer
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US16/319,182
Other languages
English (en)
Inventor
Filip Lukasz KONDRATOWICZ
Kamil UTRATA
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Synthos SA
Original Assignee
Synthos SA
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Family has litigation
First worldwide family litigation filed litigation Critical https://patents.darts-ip.com/?family=56507559&utm_source=google_patent&utm_medium=platform_link&utm_campaign=public_patent_search&patent=US20190218359(A1) "Global patent litigation dataset” by Darts-ip is licensed under a Creative Commons Attribution 4.0 International License.
Application filed by Synthos SA filed Critical Synthos SA
Publication of US20190218359A1 publication Critical patent/US20190218359A1/en
Assigned to SYNTHOS S.A. reassignment SYNTHOS S.A. ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: KONDRATOWICZ, Filip Lukasz, UTRATA, Kamil
Abandoned legal-status Critical Current

Links

Images

Classifications

    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
    • C08J9/00—Working-up of macromolecular substances to porous or cellular articles or materials; After-treatment thereof
    • C08J9/16—Making expandable particles
    • C08J9/18—Making expandable particles by impregnating polymer particles with the blowing agent
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B28/00—Compositions of mortars, concrete or artificial stone, containing inorganic binders or the reaction product of an inorganic and an organic binder, e.g. polycarboxylate cements
    • C04B28/006—Compositions of mortars, concrete or artificial stone, containing inorganic binders or the reaction product of an inorganic and an organic binder, e.g. polycarboxylate cements containing mineral polymers, e.g. geopolymers of the Davidovits type
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
    • C08K3/00—Use of inorganic substances as compounding ingredients
    • C08K3/34—Silicon-containing compounds
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
    • C08J9/00—Working-up of macromolecular substances to porous or cellular articles or materials; After-treatment thereof
    • C08J9/0014—Use of organic additives
    • C08J9/0028—Use of organic additives containing nitrogen
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
    • C08J9/00—Working-up of macromolecular substances to porous or cellular articles or materials; After-treatment thereof
    • C08J9/0014—Use of organic additives
    • C08J9/0038—Use of organic additives containing phosphorus
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
    • C08J9/00—Working-up of macromolecular substances to porous or cellular articles or materials; After-treatment thereof
    • C08J9/0066—Use of inorganic compounding ingredients
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
    • C08J9/00—Working-up of macromolecular substances to porous or cellular articles or materials; After-treatment thereof
    • C08J9/0095—Mixtures of at least two compounding ingredients belonging to different one-dot groups
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
    • C08J9/00—Working-up of macromolecular substances to porous or cellular articles or materials; After-treatment thereof
    • C08J9/04—Working-up of macromolecular substances to porous or cellular articles or materials; After-treatment thereof using blowing gases generated by a previously added blowing agent
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
    • C08J9/00—Working-up of macromolecular substances to porous or cellular articles or materials; After-treatment thereof
    • C08J9/04—Working-up of macromolecular substances to porous or cellular articles or materials; After-treatment thereof using blowing gases generated by a previously added blowing agent
    • C08J9/12—Working-up of macromolecular substances to porous or cellular articles or materials; After-treatment thereof using blowing gases generated by a previously added blowing agent by a physical blowing agent
    • C08J9/14—Working-up of macromolecular substances to porous or cellular articles or materials; After-treatment thereof using blowing gases generated by a previously added blowing agent by a physical blowing agent organic
    • C08J9/141—Hydrocarbons
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
    • C08J9/00—Working-up of macromolecular substances to porous or cellular articles or materials; After-treatment thereof
    • C08J9/16—Making expandable particles
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
    • C08J9/00—Working-up of macromolecular substances to porous or cellular articles or materials; After-treatment thereof
    • C08J9/22—After-treatment of expandable particles; Forming foamed products
    • C08J9/228—Forming foamed products
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
    • C08K3/00—Use of inorganic substances as compounding ingredients
    • C08K3/02—Elements
    • C08K3/04—Carbon
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
    • C08K3/00—Use of inorganic substances as compounding ingredients
    • C08K3/02—Elements
    • C08K3/08—Metals
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
    • C08K3/00—Use of inorganic substances as compounding ingredients
    • C08K3/18—Oxygen-containing compounds, e.g. metal carbonyls
    • C08K3/20—Oxides; Hydroxides
    • C08K3/22—Oxides; Hydroxides of metals
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
    • C08K3/00—Use of inorganic substances as compounding ingredients
    • C08K3/32—Phosphorus-containing compounds
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
    • C08K5/00—Use of organic ingredients
    • C08K5/0008—Organic ingredients according to more than one of the "one dot" groups of C08K5/01 - C08K5/59
    • C08K5/0066—Flame-proofing or flame-retarding additives
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
    • C08K5/00—Use of organic ingredients
    • C08K5/16—Nitrogen-containing compounds
    • C08K5/17—Amines; Quaternary ammonium compounds
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
    • C08K5/00—Use of organic ingredients
    • C08K5/49—Phosphorus-containing compounds
    • C08K5/51—Phosphorus bound to oxygen
    • C08K5/53—Phosphorus bound to oxygen bound to oxygen and to carbon only
    • C08K5/5313—Phosphinic compounds, e.g. R2=P(:O)OR'
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
    • C08K5/00—Use of organic ingredients
    • C08K5/49—Phosphorus-containing compounds
    • C08K5/51—Phosphorus bound to oxygen
    • C08K5/53—Phosphorus bound to oxygen bound to oxygen and to carbon only
    • C08K5/5317—Phosphonic compounds, e.g. R—P(:O)(OR')2
    • C08K5/5333—Esters of phosphonic acids
    • C08K5/5353—Esters of phosphonic acids containing also nitrogen
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
    • C08K5/00—Use of organic ingredients
    • C08K5/49—Phosphorus-containing compounds
    • C08K5/51—Phosphorus bound to oxygen
    • C08K5/53—Phosphorus bound to oxygen bound to oxygen and to carbon only
    • C08K5/5397—Phosphine oxides
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
    • C08K9/00—Use of pretreated ingredients
    • C08K9/02—Ingredients treated with inorganic substances
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
    • C08L25/00—Compositions of, homopolymers or copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and at least one being terminated by an aromatic carbocyclic ring; Compositions of derivatives of such polymers
    • C08L25/02—Homopolymers or copolymers of hydrocarbons
    • C08L25/04—Homopolymers or copolymers of styrene
    • C08L25/06—Polystyrene
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2103/00—Function or property of ingredients for mortars, concrete or artificial stone
    • C04B2103/60—Agents for protection against chemical, physical or biological attack
    • C04B2103/63—Flame-proofing agents
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2111/00—Mortars, concrete or artificial stone or mixtures to prepare them, characterised by specific function, property or use
    • C04B2111/20—Resistance against chemical, physical or biological attack
    • C04B2111/28—Fire resistance, i.e. materials resistant to accidental fires or high temperatures
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
    • C08J2201/00—Foams characterised by the foaming process
    • C08J2201/02—Foams characterised by the foaming process characterised by mechanical pre- or post-treatments
    • C08J2201/03—Extrusion of the foamable blend
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
    • C08J2203/00—Foams characterized by the expanding agent
    • C08J2203/14—Saturated hydrocarbons, e.g. butane; Unspecified hydrocarbons
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
    • C08J2203/00—Foams characterized by the expanding agent
    • C08J2203/18—Binary blends of expanding agents
    • C08J2203/182—Binary blends of expanding agents of physical blowing agents, e.g. acetone and butane
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
    • C08J2203/00—Foams characterized by the expanding agent
    • C08J2203/22—Expandable microspheres, e.g. Expancel®
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
    • C08J2325/00—Characterised by the use of homopolymers or copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and at least one being terminated by an aromatic carbocyclic ring; Derivatives of such polymers
    • C08J2325/02—Homopolymers or copolymers of hydrocarbons
    • C08J2325/04—Homopolymers or copolymers of styrene
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
    • C08J2325/00—Characterised by the use of homopolymers or copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and at least one being terminated by an aromatic carbocyclic ring; Derivatives of such polymers
    • C08J2325/02—Homopolymers or copolymers of hydrocarbons
    • C08J2325/04—Homopolymers or copolymers of styrene
    • C08J2325/06—Polystyrene
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
    • C08J2325/00—Characterised by the use of homopolymers or copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and at least one being terminated by an aromatic carbocyclic ring; Derivatives of such polymers
    • C08J2325/02—Homopolymers or copolymers of hydrocarbons
    • C08J2325/04—Homopolymers or copolymers of styrene
    • C08J2325/08—Copolymers of styrene
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
    • C08K3/00—Use of inorganic substances as compounding ingredients
    • C08K3/32—Phosphorus-containing compounds
    • C08K2003/321—Phosphates
    • C08K2003/322—Ammonium phosphate
    • C08K2003/323—Ammonium polyphosphate
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
    • C08K3/00—Use of inorganic substances as compounding ingredients
    • C08K3/32—Phosphorus-containing compounds
    • C08K2003/329—Phosphorus containing acids
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
    • C08K2201/00—Specific properties of additives
    • C08K2201/002—Physical properties
    • C08K2201/005—Additives being defined by their particle size in general
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
    • C08K2201/00—Specific properties of additives
    • C08K2201/002—Physical properties
    • C08K2201/006—Additives being defined by their surface area
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
    • C08K2201/00—Specific properties of additives
    • C08K2201/019—Specific properties of additives the composition being defined by the absence of a certain additive
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y02—TECHNOLOGIES OR APPLICATIONS FOR MITIGATION OR ADAPTATION AGAINST CLIMATE CHANGE
    • Y02P—CLIMATE CHANGE MITIGATION TECHNOLOGIES IN THE PRODUCTION OR PROCESSING OF GOODS
    • Y02P40/00—Technologies relating to the processing of minerals
    • Y02P40/10—Production of cement, e.g. improving or optimising the production methods; Cement grinding

Definitions

  • the present invention relates to the use of i) geopolymer and ii) non-brominated, phosphorus- and/or nitrogen-based flame retardants selected for improving the self-extinguishing properties of a composition comprising polymer. Further, the invention relates to a process for the production of expandable polymer granulate by an extrusion or a suspension process, preferably wherein the polymer is a vinyl aromatic polymer. Moreover, the invention relates to a composition comprising polymer, the composition further comprising i) geopolymer and ii) non-brominated, phosphorus- and/or nitrogen-based flame retardants.
  • Vinyl aromatic polymers are known and are used for the preparation of expanded products that are adopted in a variety of applications, of which the most important one is for thermal insulation. This is why there is a continuously increasing demand for expanded vinyl aromatic polymers with low thermal conductivity as well as good mechanical and self-extinguishing properties.
  • Hexabromocyclododecane has been used as a flame retardant in vinyl aromatic polymer foams for many years. Only very small quantities of HBCD are needed to meet the self-extinguishing standards. In vinyl aromatic polymer foams, such as expandable polystyrene, the required final concentration is in a range of from 0.5 to 1.0 wt. %.
  • HBCD was recognized as Substance of Very High Concern and was placed by the European Chemical Agency onto the SVHC list (decision of 28 Oct. 2008). Also, HBCD has been found widely present in biological samples from remote areas, and there is supporting evidence for its classification as persistent, bioaccumulative and toxic (PBT) and that it undergoes long-range environmental transportation.
  • HBCD polystyrene foam producers
  • pFR polymeric brominated flame retardant
  • bromine as incorporated into the polymeric foam as pFR is not eluted, it can be found in the environment after tens or hundreds of years, due to degradation of the polymer matrix if exposed to the degenerative activity of the sun's UV radiation, humidity, air, and water. The same problem is associated with other polymeric materials which are self-extinguished by brominated macro- or simple molecules and are exposed to the environment.
  • halogenated FRs in particular brominated FRs, have limited thermal stability, which puts constraints on the processing of the compositions to which they are added.
  • Elimination of brominated flame retardants for use in polymers in general is the only sustainable way to produce more environmentally and human-friendly products which are not persistent, bioaccumulative and toxic.
  • One of the solutions is the use of earth minerals in combination with phosphorus- and/or nitrogen-based flame retardants, but their efficiency in flame suppressing is very low and a high loading is necessary to achieve the desired flame retardancy.
  • Such synergistic compositions are widely known from the car or cable industries.
  • the function mechanism of phosphorus flame retardants varies, depending on the type of chemical structure of the phosphorus compound and its interaction with the polymer or the other additives during pyrolysis. Also, the flame retarding action may be optimized using a synergistic compound. The interaction may take place according to both physical and chemical mechanisms and may occur in the condensed or in the vapour phase. Often, two or more different mechanisms are involved in given systems.
  • the phosphorous-containing additives catalyse the clipping of polymer chains, thereby reducing polymer molecular weight and resulting in a decrease of viscosity, causing consequently heat loss due to dripping. Furthermore, phosphorus acts due to acid-catalyzed dehydratation and char formation, providing thermal insulation for underlying polymer and preventing fuel release.
  • the phosphorous-rich flame retardants cause an initial crosslinking reaction through the polymer, and this means that the polymer is prevented from volatilising (thus, less combustible species are formed). Another mode action is via intumescence (swelling).
  • phosphorus compounds cause radical recombination as well as replacement of hydrogen and hydroxyl radicals by other, less effective radicals, thus inhibiting combustion.
  • phosphorus- and nitrogen-containing flame retardants are ammonium polyphosphates (e.g. Exolit 462), melamine phosphates (e.g. Melpur 200), triphenylphosphate (e.g. Disflammol TP), bisphenol A bis-(biphenylphosphate) (e.g. Fyroflex BDP), and 9,10-Dihydro-9-oxa-10-phosphaphenanthrene 10-oxide (e.g. STRUKTUROL).
  • ammonium polyphosphates e.g. Exolit 462
  • melamine phosphates e.g. Melpur 200
  • triphenylphosphate e.g. Disflammol TP
  • bisphenol A bis-(biphenylphosphate) e.g. Fyroflex BDP
  • Nitrogen compounds are characterised by low toxicity and relatively low release of smoke during fire, as well as a high decomposition temperature, which is an advantages for thermoplastic polymers that are processed via extrusion or injection moulding.
  • the interaction mechanism is usually physical, although a chemical mode of action is also known.
  • Nitrogenous agents like melamine cyanurate or melamine undergo sublimation at ca. 350° C., whereby a significant amount of thermal energy is absorbed.
  • Degradation of cyanuric acid also costs energy which consequently leads to decrease of the temperature in the fire zone.
  • the decomposition of melamine results in the elimination of ammonia and the formation of inert gases.
  • Oxygen or other combustible gases dilute in inert gases, which consequently results in the formation of thermally stable condensates. Melamine as well as it salts promote dripping, resulting in the withdrawal of fuel.
  • Melamine compounds are usually used together with other flame retardants offering synergistic effects, and such an effect with phosphorus based formulations is well known. Melamine, melamine cyanurate and other melamine salts and compounds are currently the most used group of nitrogen-containing flame retardants.
  • EP 1 997 849 A1 teaches inorganic materials as binder coating on expandable or expanded polystyrene beads or particles.
  • the disadvantage of coated beads is that foam having a with very high density (of above 70 kg/m 3 ) is formed, because the coating has to be with a high loading, such as 80% by weight or more. Such foams also suffer from a high water adsorption, and only interior applications are possible.
  • foams prepared from coated beads have a high stiffness, which results in problems during cutting. Because the coating is applied onto beads, so one needs specific mixers and special moulds. Consequently, this technology is not applicable for current customers equipment, and results in foams having limited applications.
  • WO2008/113609 A2 discloses geopolymer compositions and coatings prepared therefrom.
  • WO 2016/113321 A1 teaches that the addition of geopolymer or its composite as prepared with various types of athermanous additives makes it possible to maintain the polymer foam's self-extinguishing and mechanical properties in the same range as in an expanded polymer without addition of filler or any other athermanous additive, while at the same time the thermal conductivity can be decreased significantly.
  • the geopolymer itself gives fire resistance, and further encapsulates the particles of athermanous additive, especially of those additives that are based on carbon or mineral, and separates them from any disadvantageous interactions with the flame, the polymer, or the flame retardant.
  • the presence of geopolymer further decreases thermal conductivity, because of its own heat radiation scattering effect.
  • Geopolymers are inorganic amorphous polymers with a three-dimensional, crosslinked alumina silicate structure, consisting of Si—O—Al—O bonds.
  • the structure may be created in a sol-gel method by metal alkali activation of alumina silicate precursors.
  • the formed gel product contains alkaline cations which compensate for the deficit charges associated with the aluminium-for-silicon substitution.
  • an intermediate, aluminium rich phase is first formed which then gives way to a more stable, silicon-rich product.
  • Geopolymer was coined in view of the transformation of mineral polymers from amorphous to crystalline reaction through a geochemical process at low temperature and short curing time. Geopolymers are represented by the general chemical formula of M n [—(Si—O 2 ) z —Al—O] n .w H 2 O, in which M is an alkali metal, z is 1, 2 or 3 and n is the degree of polymerization.
  • geopolymers can be amorphous or semi crystalline, depending on the condensation temperature. Amorphous polymers are obtained at 20-90° C., whereas semi-crystalline polymers are obtained in the range 150-1200° C. This class of materials demonstrates ceramic-like properties, including extreme fire resistance.
  • Geopolymers can be amorphous or crystalline materials. They possess a microstructure on a nanometre scale (as observed by TEM and measured by mercury porosimetry) which comprises small aluminosilicate clusters with pores dispersed within a highly porous network. The cluster size is typically between 5 and 10 nm.
  • geopolymerization process involves polycondensation phenomena of aluminate and silicate groups, with formation of Si—O—Al type bonds.
  • WO2015/191817 A1 teaches geopolymer aggregates and their use in a variety of applications.
  • US 2008/0 249 199 A1 teaches a method for the manufacture of foamed or foamable particles from a polymer melt.
  • a recycled polymer melt is introduced into the polymer melt through a side extruder and may include additive. This is said to be more economical than the use of a masterbatch. If bromide-containing flame protection agents or other thermally unstable additives are present in the recycled polymer, or are added to the recycled polymer, the process temperature in the side extruder and in all following system components should not exceed a temperature and dwell time limiting value which is defined by the thermal stability of the additives.
  • WO 2006/058733 A1 teaches expandable styrene polymer granulates containing a) athermanous additive selected from the group of inorganic powder materials such as silicic acid and b) carbon black or graphite. Further, EP 0 863 175, EP 0 981 574, EP 1 758 951 and EP 1 771 502 A2 teach the use of graphite in polystyrene foam obtained by an extrusion process.
  • WO 2006/058733 also teaches that the mechanical properties of thermoplastic polymers containing fillers can be improved by using adhesion promoters (coupling agents), such as maleic anhydride modified styrene copolymers, epoxy group containing polymers, organosilanes or styrene copolymers having isocyanate or acid group.
  • adhesion promoters such as maleic anhydride modified styrene copolymers, epoxy group containing polymers, organosilanes or styrene copolymers having isocyanate or acid group.
  • WO 2006/058733 A1 also proposes to use side extruders for introducing additives such as solids and thermally sensitive additives. This arrangement is, however, undesirable in situations where additives that are not thermally sensitive, but rather require thorough mixing, are to be introduced. This is because large amounts of material would need to be processed if additives that require thorough mixing were to be introduced into a main portion of the polymer. This is
  • WO 2004/087798 A1 teaches expandable vinyl aromatic polymers comprising, in a polymer matrix, a type of carbon black having an active surface area ranging from 5 to 40 m 2 /g.
  • the thermal conductivity of a material with a density of 14 g/l is reported to be 36.5 mW/m*K.
  • WO 2006/061571 A1 teaches an expandable polystyrene composition comprising carbon black as an additive, the carbon black having a very high BET surface, as measured according to ASTM D 6556, ranging from 550 to 1,600 m 2 /g.
  • the examples report polystyrene foam with a thermal conductivity of 36.16 mW/m*K at density 13.3 g/l according to ASTM D 1622, and 34.21 mW/m*K at density 19.4 g/l, respectively.
  • WO 2008/061678 A2 discloses the use of carbon black having a specific electric conductivity, to reduce the thermal conductivity of expandable vinyl aromatic polymers.
  • the carbon black is introduced during suspension polymerization, or during polymer extrusion.
  • the examples report polystyrene foam having a thermal conductivity of 31.0 mW/m*K at a density of 17 g/l.
  • Japanese patent JP 63183941 teaches the use of aluminium pigment, titanium dioxide and graphite, having specific particle size and heat radiation reflectivity, to reduce the thermal conductivity of polystyrene foams.
  • Examples 7 to 11 teach polystyrene foam produced by an extrusion process and having a thermal conductivity of 25 to 30 mW/m*K, where masterbatches were used as starting material.
  • WO 2005/123816 A1 teaches styrene polymer particle foam materials.
  • WO 2004/087798 A1 teaches expandable polystyrenes containing carbon black. In a suspension polymerization process, the carbon black is present during the polymerization in aqueous suspension. Also disclosed is a continuous process for preparing expandable polystyrene in mass, wherein the polymer is fed together with carbon black into an extruder, and, subsequently, expanding agent and possible further additives are injected into the molten polymer before extrusion through a die.
  • thermoinsulating expanded articles comprising an expanded polymeric matrix, obtained by expansion and sintering of beads/granules of a vinyl aromatic (co)polymer, in whose interior a filler is homogeneously dispersed, which comprises at least one athermanous material selected from coke, graphite and carbon black and optionally an active inorganic additive within the wave-lengths ranging from 100 to 20,000 cm ⁇ 1 .
  • US2012/264836 A1 teaches nanocomposite compositions based on expandable thermoplastic polymers which comprise: a) a polymeric matrix, b) expanding agent englobed in the polymeric matrix; c) athermanous filler comprising nano-scaled graphene plates having specific dimensions.
  • US 2008/0028994 A1 entitles “Geopolymer Compositions and Application in Oilfield Industry” teaches a geopolymer composition formed from a suspension comprising an aluminosilicate source, a metal silicate, an alkali activator, and a carrier fluid. Lightweight particles and/or heavyweight materials may be added to control density of the composition. Barium sulphate or ilmenite are examples for heavy particles.
  • WO 2010/141 976 A1 entitles “Concrete Aggregate” discloses polymeric aggregates produced from fly ash combined with an activator. The aggregate is used in concrete, mortar, or road base.
  • WO2009/009089 A1 discloses a process for treating fly ash to render it highly usable as a concrete additive.
  • These flame retardants should not necessarily comprise bromine, and should not deteriorate mechanical and other properties of the polymers to which they are added.
  • geopolymer, geopolymer in combination with athermanous additive, or geopolymer composite as prepared with various types of athermanous additives and ii) non-brominated phosphorus- and/or nitrogen-based flame retardants in relatively small concentrations in compositions comprising polymer makes it possible to maintain the composition's self-extinguishing properties, without the need for brominated flame retardants. Indeed, and if desired, the presence of brominated flame retardants can completely be dispensed with. This is possible because the geopolymer synergistically interacts with phosphorus- and/or nitrogen-based flame retardants.
  • additives i) and ii) are incorporated into the polymer compositions as fillers.
  • These additives can be used in typical compounding technology which is common for all thermoplastic polymers. This is in contrast to the teaching of EP 1 997 849 A1, where an inorganic material is used as a binder coating on expandable or expanded polystyrene beads or particles.
  • the water content of the final (modified) geopolymer or (modified) geopolymer composite used/produced is preferably in a range of from 1 to 50 wt. %, preferably 2 to 30 wt. %, more preferably 3 to 20 wt. %.
  • (Modified) geopolymer or (modified) geopolymer composite used according to the present invention may be used together with brominated flame retardant. Because brominated flame retardants have limited compatibility with products having a certain sodium content, the sodium content of the (modified) geopolymer or (modified) geopolymer composite is preferably less than 5000 ppm, more preferably less than 500 ppm, in particular less than 200 ppm, such as less than 100 ppm, or even less than 50 ppm, each calculated on dry mass.
  • the sodium content of the (modified) geopolymer or (modified) geopolymer composite used/produced according to the present invention is not used together with brominated flame retardant, then the sodium content need not necessarily be low.
  • the sodium content of the (modified) geopolymer or (modified) geopolymer composite is preferably less than 50,000 ppm, more preferably less than 10,000 ppm, in particular less than 5,000 ppm, each calculated on dry mass.
  • thermal conductivity can be decreased.
  • the presence of geopolymer decreases thermal conductivity, because of its own heat radiation scattering effect and influence on surface modification of carbon particles phase.
  • the present invention has the following aspects:
  • the present invention relates to the use of
  • the improvement is measured according to DIN 4102 (B1, B2) and EN ISO 11925-2, more preferably the improvement is measured according to EN ISO 11925-2.
  • the polymer is selected from vinyl polymer, polyurethane, polyolefin, polycarbonate, polyester, polyamide, polyimide, silicone and polyether, more preferably the polymer is selected from vinyl aromatic polymer, polyethylene and polypropylene, most preferably the vinyl aromatic polymer is polystyrene.
  • the composition does not comprise polymeric brominated flame retardant, more preferably the composition does not comprise brominated flame retardant. It is in particular preferred that the composition does not comprise halogenated flame retardant.
  • the athermanous additive as used in admixture with geopolymer, or as contained in geopolymer composite, is one or more selected from the group consisting of
  • the carbon-based athermanous additive (1) is selected from carbon black, coke, graphitized carbon black, graphite, graphite oxides, anthracite, graphene, and graphene oxide.
  • the metal athermanous additive (2) is preferably selected from copper, bismuth, nickel, iron, tungsten, silver, cadmium, cobalt, tin, zinc.
  • the metal oxide athermanous additive (3) is preferably selected from oxides of the metals of groups IIIB, IV-VIIIA, and I-VB of the periodic table.
  • the geopolymer or geopolymer composite may be modified with one or more water-soluble compounds.
  • the water-soluble compound is selected from phosphorus compounds, nitrogen compounds, copper compounds, silver compounds, zinc compounds, tin compounds, and magnesium compounds, more preferably the modification is with a phosphorus compound, in particular the modification is with a phosphorus compound selected from phosphoric acid and ammonium polyphosphate.
  • the invention requires that geopolymer or geopolymer composite is used. Processes for the production of geopolymer are known, see e.g. WO2015/191817 A1.
  • the geopolymer is present as geopolymer composite. It may be produced in accordance with the process of WO 2016/113321 A1, which process comprises
  • the geopolymer or geopolymer composite is produced in accordance with the process of international patent application entitled “Process for the production of geopolymer or geopolymer composite” (PCT/EP2017/068346), filed on even date herewith, the disclosure of which application is incorporated herein in its entirety.
  • PCT/EP2017/068346 claims priority from EP16461542.9 filed on Jul. 20, 2016.
  • geopolymer or geopolymer composite is prepared in a process comprising
  • Step a) is preferably performed by mixing of precursor for aluminate and silicate, to form a sol-gel, wherein the mixing is under alkaline conditions.
  • the mixing in step a) may comprise the mixing of an aluminosilicate, a phosphoaluminate, an alkaline silicate and/or an alkaline aluminate.
  • the sol-gel is prepared, for instance from a mixture of aluminosilicate precursor and activator such as sodium aluminate or sodium disilicate, with addition of water. It is also preferred to use sodium disilicate or sodium aluminate or their potassium analogues.
  • the alkaline solution is a water-diluted sodium aluminate or sodium disilicate, in particular sodium aluminate.
  • a geopolymer or a geopolymer composite prepared from a mixture of aluminosilicate precursor and phosphoaluminate further enhances the self-extinguishing effect in vinyl aromatic polymer foams. Also, this improvement is achieved when this type of athermanous and flame retarding constituent is used in other expandable vinyl polymers such as polyethylene and polypropylene or even other type of polymers such as polyamides, polyurethanes, polyesters, polyimides or various types of resins.
  • the mixing in step a) involves one or more materials selected from the group consisting of dehydroxylated kaolinite, metakaolin, metakaolinite, fly ash, furnace slag, red mud, thermal silica, fumed silica, halloysite, mine tailings, pozzolan, kaolin, and building residues.
  • Particularly preferred precursors are dehydroxylated kaolinite, metakaolin or metakaolinite, but also fly ash, furnace slag, red mud, thermal silica, fumed silica, halloysite and a mixture thereof.
  • step c) After activation and dissolution, the ortho-sialate monomer [(HO) 3 —Si—O—Al—(OH) 3 ] polycondensates and forms a sol-gel, so called “gel”.
  • the mixing is in a third step c) continued.
  • step b) there is an addition of an additive, in micro or in nano powder form.
  • step a), b) or c) water can be introduced as a viscosity modification additive, and/or silane and/or latex as adhesion modifiers.
  • Si/Al ratio Changes in the Si/Al ratio can drastically affect the flexibility of obtained modified geopolymer.
  • the smaller the value of the Si/Al ratio the more flexible is the modified geopolymer. This was especially observed in the case of a Si/Al ratio of about 1, where aluminosilicates formed “more flexible” poly(sialate) structures, as compared to a 3D network of poly(sialate-siloxo) and poly(sialate-disiloxo) exhibiting shrinkage and cracks. From the literature, it is known that such flexibility was observed when the molar Si/Al ratio exceeds 30, with the much higher content of Si in matrix constituents.
  • silane may preferably be added to the gel, in order to improve adhesion of geopolymer in particular to carbon-based athermanous additives and later to the filled polymer.
  • concentration of silane is preferably in the range of from 0.01 to 10 wt. %, more preferably in the range of from 0.05 to 5 wt. %, most preferably from 0.1 to 3 wt. %.
  • Geopolymer or geopolymer composite may thus be modified by reaction with coupling agents, to obtain better adhesion to the vinyl aromatic expandable polymers.
  • Different coupling agents may be used, depending on when the addition during the preparation of the geopolymer or the geopolymer composite takes place. However, this depends on the type of geopolymer used and the type of additive within the geopolymer composite.
  • silanes Whilst various silanes can be used, the best adhesion performance is achieved when using aminopropyltriethoxysilane (e.g. Dynasylan AMEO from Evonik), aminopropyltrimethoxysilane (e.g. Dynasylan AMMO from Evonik), phenyltriethoxysilane (e.g. Dynasylan 9265 from Evonik), 3-methacryloxypropyltrimethoxysilane (e.g. Dynasylan MEMO form Evonik) and vinyltrimethoxy-silane (e.g. Dynasylan VTMO from Evonik).
  • aminopropyltriethoxysilane e.g. Dynasylan AMEO from Evonik
  • aminopropyltrimethoxysilane e.g. Dynasylan AMMO from Evonik
  • phenyltriethoxysilane e.g. Dynasylan 9265 from Evonik
  • the process further preferably comprises the addition of a butadiene latex in one or more of steps a), b) and c) (preferably, the addition of the butadiene latex is in one or more of steps a) and step b)).
  • Silane may also be added to the geopolymer composite in any one of step e), optional step f) and step g). Then, the silane is preferably selected from aminopropyltriethoxysilane, aminopropyltrimethoxysilane, phenyltriethoxysilane, 3-methacryloxypropyltrimethoxysilane, and mixtures thereof.
  • silane is added in an amount of from 0.01 to 10 wt. %, more preferably from 0.05 to 5 wt. %, most preferably from 0.1 to 3 wt. %, based on the weight of modified geopolymer or modified geopolymer composite.
  • the additive is an athermanous additive, preferably selected from the group consisting of
  • the additive as used in combination with (preferably modified) geopolymer or as incorporated into (preferably modified) geopolymer composite is one or more selected from the group consisting of
  • the second and optional step b) is thus the incorporation of additives, preferably one or more athermanous additives.
  • additives preferably one or more athermanous additives.
  • such additive could be carbon black, graphite, coke, anthracite, graphite oxide.
  • cokes could be used: petroleum coke, metallurgical coke, shot coke, sponge coke, fluid coke, beaded coke, needle coke, pitch coke or anode coke.
  • anthracites could be used: green anthracite, semianthracite, anthracite, meta-anthracite or gas calcined anthracite and electrically calcined anthracite or dealkalized and desulphurized types of anthracite.
  • carbon based additive examples include sea coal, graphene oxide, nanotubes or carbon fibers.
  • additive a. is selected from coke, graphitized carbon black, graphite oxides, graphite, anthracite, graphene oxide, and nano-graphite and carbon nanotubes (single and multilayer).
  • additive a is selected from coke, graphitized carbon black, graphite oxides, graphite, anthracite, graphene oxide, and nano-graphite and carbon nanotubes (single and multilayer).
  • the athermanous additive is a carbon athermanous additive selected from graphene oxide, nano-graphite, and mixtures thereof.
  • metal oxides could be added, preferably, titanium dioxide, iron oxide, chromium oxide, silicon oxide or nickel oxide or their nanoforms.
  • metal sulfides such as tungsten sulfide or nickel sulfide are possible as additives.
  • the additive or a minimum of two additives, is preferably added in an amount of from 0.01 to 80 wt. %, more preferably from 0.05 to 60 wt. %, most preferably from 0.1 to 50 wt. % depending on the type of the additive or additive mixture, based on the weight of geopolymer composite. Different mixtures and different ratios between the additives are possible.
  • the thixotropic gel is further high speed mixed, to result in a homogenous consistence. Water can then be added, to regulate the final viscosity. The water is added in a preferred ratio from 1/10 to 10/10 or depending on additive type and its bulk density as well as hydrophilic properties and specific surface.
  • step f) comprises the addition of an acid solution, and subsequent drying.
  • step f) comprises addition of an acid solution, washing with water, and subsequent drying.
  • the second preferred embodiment for the geopolymer or geopolymer composite production process further may comprise modification with one or more water-soluble compounds, preferably the modification is in one or more of step f) and step g), resulting in modified geopolymer or modified geopolymer composite, respectively.
  • the water-soluble compound is preferably selected from phosphorus compounds, nitrogen compounds, copper compounds, silver compounds, zinc compounds, tin compounds, and magnesium compounds.
  • the modification is with a phosphorus compound, in particular with a phosphorus compound selected from phosphoric acid and ammonium polyphosphate.
  • the modification of geopolymer or geopolymer composite gives materials having a better stability, such as improved adhesion to the polymers into which they are incorporated.
  • the modification allows one to use certain types of additives that would otherwise be unsuitable for use in expandable vinyl aromatic polymers and expanded vinyl aromatic polymer foams.
  • the geopolymer or geopolymer composite is produced in several process steps in which if needed additive (such as coke or anthracite or graphene oxide or metal oxide or sulfide or metal) becomes encapsulated by chemical and physical bonding into the geopolymer matrix.
  • additive such as coke or anthracite or graphene oxide or metal oxide or sulfide or metal
  • This type of geopolymer is suitable for performing a self-extinguishing action and further reducing the thermal conductivity properties of vinyl aromatic polymers and expanded foam products made thereof.
  • a relatively small amount of modifier e.g. a phosphorus compound such as phosphoric acid or ammonium polyphosphate, is used to alter the surface of geopolymer or geopolymer composite. It was found that this surface modification can help to reduce the amount of brominated flame retardant or completely eliminate the need to use any brominated flame retardant.
  • geopolymer or geopolymer composite suspended in water can be ion exchanged.
  • an ion exchange can be performed.
  • Such ion-exchanged particles of modified geopolymer or of modified geopolymer composite (incorporating ions of Ag, Zn, Cu, Cu, Ni, Sn, Mg) further improves the reduction of thermal conductivity of polymeric foams, acting additionally as antimicrobial agent.
  • Final step g) of the process may thus comprise
  • the surface modification may be performed, for instance by treating the precipitated cake with a demineralized water solution of acid, preferably phosphoric acid or phosphates or its salts or polyphosphates or its salts.
  • the surface modification by phosphorus and/or nitrogen based compounds may thus be performed with the use of an aqueous solution.
  • the aqueous solution of the phosphorus and/or nitrogen based compound is transferred in one or more cycles through the filter press. If this step is needed because of the application of the resultant modified geopolymer or modified geopolymer composite, it is often performed before the membrane squeeze and vacuum drying in the membrane filter press.
  • the modification can alternatively be an ion exchange, with the use of a water solution of a salt such as copper chloride, silver nitrate, or magnesium sulphate, or some other salt which is soluble in cold or hot water.
  • step e) of the second preferred embodiment for the geopolymer or geopolymer composite production process there are two alternatives, namely
  • the process includes step e1), decantation.
  • the process preferably comprises
  • the process includes step e2), namely adding of an organic phase, emulsifying, and stripping of the organic phase, and the process preferably comprises
  • modified geopolymer or geopolymer composite is produced in accordance with the process of international patent application entitled “Modified geopolymer and modified geopolymer composite and process for the production thereof” (PCT/EP2017/068371), filed on even date herewith, the disclosure of which application is incorporated herein in its entirety.
  • PCT/EP2017/068371 claims priority from EP16461540.3, filed Jul. 20, 2016.
  • modified geopolymer or modified geopolymer composite is prepared in a process comprising
  • step a) is preferably performed by mixing of precursor for aluminate and silicate, to form a sol-gel, wherein the mixing is under alkaline conditions.
  • the invention further requires that, in addition to geopolymer or geopolymer composite, phosphorus- and/or nitrogen-based flame retardant is used.
  • the phosphorus-based flame retardant a is preferably selected from red phosphorus, organic and inorganic phosphates, phosphonates, phosphinates, and phosphoramidates.
  • the organic phosphate may be selected from triphenyl phosphate (TPP), resorcinol bis(diphenylphosphate) (RDP), bisphenol A bis(diphenylphosphate) (BADP), tricresyl phosphate (TCP), and resorcinol bis(2,6-dixylenylphosphate) (RDX).
  • the phosphinate may be selected from aluminium phosphinates, calcium phosphinates and zinc phosphinates.
  • the phosphoramidate may be 9,10-Dihydro-9-oxa-10-phosphaphenanthrene-10-oxide (DOPO).
  • the nitrogen-based flame retardant b) may be selected from hindered amine stabilizer, ammonium octamolybdate, melamine octamolybdate, benzoguanamine, tris(hydroxyethyl) isocyanurate, allantois, glycoluril, melamine, melamine cyanurate, dicyandiamide, guanidine, carbodiimides, condensation products of melamine, and derivatives thereof.
  • the phosphorus/nitrogen-based flame retardant c) is preferably selected from melamine phosphate, melamine pyrophosphate, melamine polyphosphate ammonium polyphosphate, and ethylene diamine phosphate.
  • the nitrogen retardant preferably comprises condensation products of melamine.
  • condensation products of melamine are melem, melam, or melon, or compounds of this type with a higher condensation level, or else a mixture of the same, and, by way of example, may be prepared by the process described in WO96/16948.
  • the phosphorus/nitrogen flame retardants preferably comprise reaction products of melamine with phosphoric acid or with condensed phosphoric acids, or comprise reaction products of condensation products of melamine with phosphoric acid or condensed phosphoric acids, or else comprise a mixture of the specified products.
  • the reaction products with phosphoric acid or with condensed phosphoric acids are compounds which arise via reaction of melamine or of the condensed melamine compounds, such as melam, melem, or melon etc., with phosphoric acid.
  • these are dimelamine phosphate, dimelamine pyrophosphate, melamine phosphate, melamine pyrophosphate, melamine polyphosphate, melam polyphosphate, melon polyphosphate, and melem polyphosphate, and mixed polysalts, e.g. those described in WO98/39306.
  • non-brominated flame retardant ii) is a non-halogenated flame retardant.
  • the geopolymer or geopolymer composite has an average particle size (D50) in the range of 0.1 to 10 ⁇ m.
  • the invention relates to process for the production of expandable polymer granulate by an extrusion or a suspension process, the process comprising the addition of
  • the polymer is a vinyl aromatic polymer.
  • the present invention thus relates to a process for the production of expandable (vinyl aromatic) polymer in the form of granulate of so-called expandable particles (micro-pellets or beads).
  • expandable particles micro-pellets or beads.
  • an extrusion process e.g. XEPS
  • a suspension polymerization process e.g. EPS
  • incorporation of i) and ii) favourably contributes to both the process conditions and the properties of the product.
  • the invention relates to an extrusion process for the production of expandable vinyl aromatic polymers, preferably by twin-screw extrusion consisting of a two-step mixing of the additive and flame retardant in two twin-screw extruders.
  • Mixing takes place in a side twin screw extruder to which the additive (modified geopolymer, or combination of modified geopolymer with additive or mixture of additives, or modified geopolymer composite) is added through the two side feeders, in order to better degas the melt from excess of water and air.
  • the additive modified geopolymer, or combination of modified geopolymer with additive or mixture of additives, or modified geopolymer composite
  • the filler masterbatch is created “in situ” and the filled melt is then (preferably directly, i.e. as melt) transferred to the main 32D twin-screw extruder.
  • the main extruder is filled with general purpose polystyrene (the same as the one dosed to the side twin screw extruder), and non-brominated flame retardant. Then, the melt is impregnated with blowing agent (propellant, typically pentanes, or a suitable mixture). The melt containing all additives is then cooled in a single screw extruder. The melt is then downstream processed in a pressurized underwater pelletization process, to obtain vinyl aromatic polymer granulate. The granulate is finally coated with a mixture of zinc (or magnesium) stearate, glycerine monostearate and glycerine tristearate. If a brominated flame retardant is present, the modified geopolymer or modified geopolymer composite preferably has a low alkali content.
  • expandable vinyl aromatic polymer granulate is preferably prepared in an extrusion process as shown in detail in WO 2016/113321 A1.
  • a brominated flame retardant can in accordance with the present invention be reduced or even be dispensed with. Especially if no brominated flame retardant is present, the geopolymer or geopolymer composite as used in combination with ii) non-brominated flame retardant need not have a low alkali content.
  • expandable vinyl aromatic polymer is prepared in a suspension polymerization process.
  • radically initiated copolymerization preferably takes place in the presence of powder of a. geopolymer, or b. combination of geopolymer with additive, or c. geopolymer composite, each preferably hydrophobized on the surface by the coupling agents, in particularly by vinyl silanes.
  • mixing of prepolymer as obtained in first step with vinyl aromatic polymer takes place, preferably in a twin-screw co-rotating extruder.
  • Underwater pelletization gives a masterbatch in the form of granulate. Then, this masterbatch is preferably dissolved in styrene, together with non-brominated flame retardant. Water is then added, followed by peroxide and surfactants.
  • the polymerization is continued at a temperature in a range of from 75 to 130° C.
  • the resultant polymer is centrifuged to remove the water from the polymer particles (granulate), the particles are dried and are finally coated with a mixture of magnesium (or zinc) stearate and/or mono- and/or di- and/or tristearate of glycerine.
  • the suspension process preferably comprises the steps as described in more detail in WO 2016/113321 A1.
  • the invention relates to a composition comprising one or more polymers, the composition further comprising
  • composition may be in the form of an expandable granulate, wherein the polymer is a vinyl aromatic polymer, the granulate further comprising one or more propellants.
  • the granulate is obtainable according to the process of the second aspect.
  • the polymer is selected from vinyl polymer, polyurethane, polyolefin, polycarbonate, polyester, polyamide, polyimide, silicone and polyether. More preferably, the polymer is selected from vinyl aromatic polymer, polyethylene and polypropylene, most preferably the vinyl aromatic polymer is polystyrene.
  • the composition can be in the form of expandable vinyl aromatic polymer granulate, in the form of expanded vinyl polymer foam, or in the form of a masterbatch.
  • expandable vinyl aromatic polymer granulate and an expanded foam products made thereof, which comprises vinyl aromatic polymer prepared from styrene monomer with optional incorporation of one or more vinyl comonomers, and
  • Expandable vinyl aromatic polymer granulate may be expanded to form foam with a uniform structure independently from the concentration of geopolymer or geopolymer composite in the foam.
  • a uniform structure is characterized by the cell size distribution, as measured by a statistical analysis of the picture prepared by an optical microscopy measurement.
  • the invention relates to the expandable vinyl aromatic polymer granulate (particles) as obtainable according to the second aspect, preferably in an extrusion or a suspension processes.
  • the expandable vinyl aromatic polymer granulate comprises polymer, one or more propellants, geopolymer additive i) and non-brominated flame retardants ii), where i) is a. geopolymer, or b. a combination of a geopolymer with an additive, but is preferably c. the geopolymer composite as prepared from geopolymer and a suitable additive such as those from the group of carbon based athermanous additives, with optional modification of the geopolymer.
  • the vinyl aromatic polymer used in all aspects of the invention is in particular polystyrene or a vinyl aromatic styrene copolymer.
  • a part of styrene monomer is substituted with unsaturated comonomers, the reactivity of which is close to styrene monomer's reactivity, such as p-methyl styrene and its dimers, vinyl toluene, t-butyl styrene or divinylbenzene.
  • typically used vinyl aromatic polymers have a different number average molecular weight.
  • a general purpose type of polystyrene (or a copolymer with unsaturated styrene derivative) with a number average molecular weight (Mn) of from 40 to 100 kg/mol, preferably of from 50 to 80 kg/mol, more preferably of from 55 to 70 kg/mol, and a suitable polydispersity of Mw/Mn in a range of from 2.0 to 5.0, preferably of from 2.5 to 4.0, more preferably of from 3.0 to 3.5, and Mz/Mw in the range of from 1.5 to 2.5.
  • Mn number average molecular weight
  • the vinyl aromatic polymer as produced in the suspension process preferably has a number average molecular weight (Mn) from 50 to 120 kg/mol, preferably of from 60 to 100 kg/mol, more preferably of from 70 to 90 kg/mol, and a suitable polydispersity Mw/Mz in a range of from 2.0 to 4.5, preferably from 2.5 to 4.0, more preferably from 3.0 to 4.0, and Mz/Mw in the range of from 1.5 to 2.5.
  • Mn number average molecular weight
  • composition when in the form of expanded vinyl polymer foam has
  • the expanded vinyl polymer is a vinyl aromatic polymer. More preferably, the foam is obtainable by expansion of the granulate according to the second aspect.
  • any additive by weight of polymer
  • the carbon additive namely petroleum coke (Ranco 9895 from Richard Anton KG having a mean diameter particle size of 3 ⁇ m, a BET surface area of 28.5 m 2 /g, a total surface area of pores 12.1 m 2 /g, and a sulphur content of 10100 ppm) was added in an amount of 52 kg, and 46.8 l of water was added subsequently to the gel and mixed during the next 1 min, also with a high speed of 300 rpm. After that, the viscous, homogenous gel was discharged from the mixer directly to the open mould made of polished stainless steel in a total amount of 170 kg. The mould was then closed and left for 24 h to perform geopolymerization.
  • petroleum coke Rosin 9895 from Richard Anton KG having a mean diameter particle size of 3 ⁇ m, a BET surface area of 28.5 m 2 /g, a total surface area of pores 12.1 m 2 /g, and a sulphur content of 10100 pp
  • the mould was opened and transported to the drier to perform a drying process, for 8 h at a temperature of 70° C., and for 16 h at a temperature of 120° C. Under these conditions, the geopolymer composite was dried over 24 h, and approx. 29 wt. % of water excess was evaporated from the material. Still approx. 10% of water remained in the material.
  • the dried geopolymer composite block was then placed into a crusher to obtain the granulate.
  • the granulate with an average particles size of 10 mm was jet milled with the use of hot air as milling medium, to obtain free flowing powder.
  • the fine powder containing about 3 wt. % of water (amount of approx. 107 kg) was then placed in a 0.6 m 3 in heated dissolver (reactor), equipped with a high speed agitator and a ribbon stirrer turning closely to the dissolver walls. Immediately thereafter, 214 l of filtrated process water were charged into the dissolver and mixing was started simultaneously. An amount of 46.2 kg of concentrated aqueous hydrochloric acid (30%) was then over 5 min added to the reactor and dealkalization was performed. The starting pH, as measured before acid addition, was 13, and after 60 min of mixing and dealkalization, the final pH was 7.5.
  • the water (filtrate) having a conductivity of about 80,000 ⁇ S/cm was filtrated from the powder of geopolymer composite and a precipitate was obtained, containing approx. 50 wt. % of water. Then, a portion of process water was used to wash remaining sodium chloride and other chlorides from the precipitate. Washing was continued for 20 min, to obtain a filtrate having conductivity below 400 ⁇ S/cm. Alternatively, demineralized water could be used, reducing the filtrate conductivity below 300 ⁇ S/cm. To help destruct a thixotropic effect, the washing with 0.1% hydrochloric acid solution could be performed after the wash with process or demineralized water.
  • 3 wt. % of a solution of phosphoric acid (preferably 75% concentrated) in demineralized water may be pumped through the filter press to modify the surface of geopolymer or geopolymer composite.
  • the precipitate with water content of about 45 wt. % was then finally vacuum dried over 4 h at a temperature 120° C. and pressure level of about 0.2 mbar.
  • % of phosphoric acid in its structure was then granulated and deagglomerated in an impact mill, to receive a fine powder with a D50 of about 2.7 ⁇ m as presented in FIG. 1 .
  • the 5 wt. % content of phosphoric acid was analysed in the geopolymer.
  • the content of analysed sodium was 200 ppm.
  • the geopolymer or geopolymer composite modification in the repulpation step could be performed by creating 1-15% solutions with water. Further, modification could be more sufficient if the solution of H 3 PO 4 or APP is used after demineralized water washing in the second step of membrane filtration. When the modification is done in the repulpation step, the washing step with the use of demineralized water must be excluded in that case, so as to not elute the modifier.
  • the sodium content is presented as the most important one from an improved process point of view. It will be shown below how the sodium content and the phosphorus compound content influence the foam's self-extinguishing properties, and to which content, in the foam, brominated flame retardant could be reduced.
  • a crucible with 0.05 g dried sample is placed in the oven for 5 h at 500° C. for burning.
  • the ash after burning is cooled down, in the next step ca. 10 ml deionized water with 1 ml HCl (35-38%) is added to the crucible with sample, and the content is heated using a laboratory hotplate at 140° C. for 30 min.
  • the sample is cooled down and transferred through the filter (cleaned beforehand for a minimum of 3 times using deionized water) into the 100 ml flask, in the next step 8 ml 1 M nitric acid with 4 ml spectral buffer of cesium chloride (2.5% Cs) is added.
  • one control (blank) sample is prepared using the same procedure and the same reagents.
  • sample solution as prepared applying the procedure described above is measured by Atomic Absorption Spectrometer, using a device AA iCE 3500 GFS35Z, and following parameters: working mode: absorption, wave length: 589.0 nm, gap: 0.2 nm,
  • the presented analytical procedure is based on the standard defining Na analysis PN-ISO 9964-1:1994+Ap1:2009, sample preparation for measurement is based on internal procedure standard 61/A issue 3 dated 30 Apr. 2009.
  • H 3 PO 4 and ammonium polyphosphate content were concluded from x-ray spectroscopy (XRF), by measuring the content of phosphorus, calculated as content of P 2 O 5 .
  • XRF was performed with the use of a vessel for powders and oils analysis on the Prolen foil with thickness of 4 ⁇ m.
  • a WD-XRF model S8 Tiger apparatus from Bruker was used to perform analysis.
  • the specific surface area was determined using a Gemini 2360 (Micromeritics) device.
  • the measurement minimum of the Gemini 2360 apparatus for specific surface was from 0.01 m 2 /g, the total surface range was from 0.1 to 300 m 2 , and the pore size starting from 4.10 ⁇ 6 cm 3 /g.
  • Analysis was performed in a range P/P 0 from 0.05 to 0.3. Degasification of sample was made in an inert gas atmosphere of nitrogen (with flow of 50 cm 3 /min.). Later, the sample was dried over 2 h at a temperature of 110° C. Nitrogen was used as measurement gas.
  • the pore size of the samples was measured using an Autopore IV 9500 device according to an internal standard. Mercury contact angle is 130°. Before the measurement, each sample was conditioned for 2 h at 200° C.
  • the melt temperature in main extruder was 180° C.
  • the geopolymer composite powder as prepared in EXAMPLE 1 in a concentration of 10 wt. % was dosed to the side arm (54D/25 mm) twin-screw co-rotating extruder via two side feeders, and the vinyl aromatic polymer (in the form of granules) was dosed to the main hopper of this extruder.
  • the blowing agent (n-pentane/isopentane mixture 80/20%) was injected to the main 32D/40 mm extruder downstream from the injection of the melt from the side twin-screw extruder.
  • the concentration of blowing agent was 5.5 wt. %, calculated on total mass of product.
  • the melt of vinyl aromatic polymer containing 0.5-5.0 wt. % of P/N flame retardant, bicumyl, nucleating agent, geopolymer composite and blowing agent was transported to the 30D/90 mm cooling extruder and pumped through a 60 mm length static mixer, melt pump, screen changer, diverter valve and extruded through the die head with 0.75 mm diameter holes, and underwater pelletized by the rotating knifes. Downstream, the rounded product, a granulate with a particle size distribution of 99.9% of the fraction 0.8-1.6 mm was centrifuged to remove the water, and was finally coated by the suitable mixture of magnesium stearate with glycerine monostearate and tristearate.
  • the melt temperature in the cooling extruder was 170° C.
  • the coated beads were expanded, to measure the final general properties of expanded foam composite:
  • the expandable granulate with a particle size distribution 0.8 to 1.6 mm was in the pre-expander vessel treated for 50 sec. with steam having a pressure of 0.2 kPa, and was then dried in a connected fluid bed drier.
  • the obtained beads' density was 15 kg/m 3 .
  • the expanded beads were conditioned in a silo for 24 h and introduced to the block mould with dimensions of 1000 ⁇ 1000 ⁇ 500 mm.
  • Steam having a pressure of 0.7 kPa was used to weld the beads, and to obtain moulded blocks having a density of 15.5 kg/m 3 .
  • the mould cooling time in this case was 70 sec.
  • the ready block was cut into plates and then specimens taken after 6 days of conditioning at room temperature.
  • This example is a comparative one, to show that geopolymer composite does not sufficiently act as effective flame retardant by itself.
  • the self-extinguishing test results as obtained are presented in Table 2.
  • Example 3 This example is comparable with Example 1 and it gives reference that also a combination of synergist (bicumyl) and geopolymer composite does not give the required self-extinguishing properties for EPS foam.
  • the self-extinguishing test results as obtained are presented in Table 3.
  • This example is a comparative one, to show that addition of ammonium polyphosphate (only) in an amount of 2 wt. % is not sufficient to make self-extinguished foams.
  • the self-extinguishing test results as obtained are presented in Table 4.
  • Example 5 This example is comparable with Example 3, except that the ammonium polyphosphate content was increased up to 5 wt. %, to show that this does not make a big difference in terms of the self-extinguishing effect in EPS foams.
  • the self-extinguishing test results as obtained are presented in Table 5.
  • This example is the first one with the use of geopolymer composite in combination with ammonium polyphosphate (2 wt. %). In this case for the first time a self-extinguishing effect was discovered.
  • the self-extinguishing test results as obtained are presented in Table 6.
  • Example 8 This example is comparable with Example 5. In this case instead adding of ammonium polyphosphate Exolite 422 (D50 17 ⁇ m), the grade Exolite 423 (D50 8 ⁇ m) was added. It is shown that smaller particles of ammonium polyphosphate have a better surface contact with geopolymer composite, thus self-extinguishing of EPS foam was improved. The self-extinguishing test results as obtained are presented in Table 8.
  • Example 5 This example is comparable with Example 5. It shows that, when ammonium polyphosphate (APP) is placed in the mezo-, microstructure of geopolymer composite via wet method modification, the self-extinguishing effect of EPS foam is strengthened significantly with the use of even lower amount of APP, in comparison to Example 5 or 7.
  • the self-extinguishing test results as obtained are presented in Table 10.
  • Example 9 This example is comparable with Example 9 and shows that complex wet modification with the use of phosphoric acid with ammonium polyphosphate (APP) (at separated stages of geopolymer composite preparation) and as well addition to the polymer of D50 8 ⁇ m Exolite AP 433 in an amount of 0.5 wt. % only can help to decrease the total amount of APP (more expensive then H 3 PO 4 ) in ESP foam, while maintaining the self-extinguishing effect at the same level.
  • APP ammonium polyphosphate

Landscapes

  • Chemical & Material Sciences (AREA)
  • Organic Chemistry (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Health & Medical Sciences (AREA)
  • Medicinal Chemistry (AREA)
  • Polymers & Plastics (AREA)
  • Engineering & Computer Science (AREA)
  • Materials Engineering (AREA)
  • Inorganic Chemistry (AREA)
  • Ceramic Engineering (AREA)
  • Structural Engineering (AREA)
  • Life Sciences & Earth Sciences (AREA)
  • General Life Sciences & Earth Sciences (AREA)
  • Geochemistry & Mineralogy (AREA)
  • Geology (AREA)
  • Environmental & Geological Engineering (AREA)
  • Compositions Of Macromolecular Compounds (AREA)
  • Fireproofing Substances (AREA)
  • Silicates, Zeolites, And Molecular Sieves (AREA)
  • Civil Engineering (AREA)
  • Manufacture Of Porous Articles, And Recovery And Treatment Of Waste Products (AREA)
  • Molecular Biology (AREA)
US16/319,182 2016-07-20 2017-07-20 Use of geopolymeric additive in combination with non-brominated flame retardant in polymer foams Abandoned US20190218359A1 (en)

Applications Claiming Priority (3)

Application Number Priority Date Filing Date Title
EP16461541 2016-07-20
EP16461541.1 2016-07-20
PCT/EP2017/068390 WO2018015502A1 (en) 2016-07-20 2017-07-20 Use of geopolymeric additive in combination with non-brominated flame retardant in polymer foams

Related Parent Applications (1)

Application Number Title Priority Date Filing Date
PCT/EP2017/068390 A-371-Of-International WO2018015502A1 (en) 2016-07-20 2017-07-20 Use of geopolymeric additive in combination with non-brominated flame retardant in polymer foams

Related Child Applications (1)

Application Number Title Priority Date Filing Date
US17/877,183 Continuation US11993691B2 (en) 2016-07-20 2022-07-29 Use of geopolymeric additive in combination with non-brominated flame retardant in polymer foams

Publications (1)

Publication Number Publication Date
US20190218359A1 true US20190218359A1 (en) 2019-07-18

Family

ID=56507559

Family Applications (3)

Application Number Title Priority Date Filing Date
US16/319,182 Abandoned US20190218359A1 (en) 2016-07-20 2017-07-20 Use of geopolymeric additive in combination with non-brominated flame retardant in polymer foams
US17/877,183 Active US11993691B2 (en) 2016-07-20 2022-07-29 Use of geopolymeric additive in combination with non-brominated flame retardant in polymer foams
US18/656,028 Pending US20240294722A1 (en) 2016-07-20 2024-05-06 Use of geopolymeric additive in combination with non-brominated flame retardant in polymer foams

Family Applications After (2)

Application Number Title Priority Date Filing Date
US17/877,183 Active US11993691B2 (en) 2016-07-20 2022-07-29 Use of geopolymeric additive in combination with non-brominated flame retardant in polymer foams
US18/656,028 Pending US20240294722A1 (en) 2016-07-20 2024-05-06 Use of geopolymeric additive in combination with non-brominated flame retardant in polymer foams

Country Status (17)

Country Link
US (3) US20190218359A1 (ja)
EP (1) EP3475241B1 (ja)
JP (1) JP6761892B2 (ja)
KR (1) KR20190040189A (ja)
CN (1) CN109562998A (ja)
AU (1) AU2017300726B2 (ja)
BR (1) BR112019000679A2 (ja)
CA (1) CA3031424A1 (ja)
DK (1) DK3475241T3 (ja)
EA (1) EA201990351A1 (ja)
ES (1) ES2810905T3 (ja)
HU (1) HUE051595T2 (ja)
IL (1) IL264296A (ja)
LT (1) LT3475241T (ja)
PL (1) PL3475241T3 (ja)
UA (1) UA125517C2 (ja)
WO (1) WO2018015502A1 (ja)

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US11440843B2 (en) 2016-07-20 2022-09-13 Synthos S.A. Modified geopolymer and modified geopolymer composite and process for the production thereof
US12122720B2 (en) 2016-07-20 2024-10-22 Synthos S.A. Process for the production of geopolymer or geopolymer composite

Families Citing this family (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
KR102393513B1 (ko) * 2019-09-27 2022-05-02 롯데첨단소재(주) 열가소성 수지 조성물 및 이로부터 형성된 성형품
KR102425031B1 (ko) * 2019-12-23 2022-07-25 롯데첨단소재(주) 열가소성 수지 조성물 및 이로부터 형성된 성형품
CN114507057A (zh) * 2022-03-01 2022-05-17 江苏佳核新能源科技有限公司 高耐火低热传导复合材料
KR102534085B1 (ko) * 2022-10-06 2023-05-18 주식회사 퍼시픽인터켐코포레이션 다기능성 난연 보조제

Family Cites Families (53)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE3421086A1 (de) 1984-06-06 1985-12-12 F. Willich GmbH & Co, 4600 Dortmund Organomineralprodukte, verfahren zu ihrer herstellung und ihre verwendung
JPS63183941A (ja) 1987-01-27 1988-07-29 Asahi Chem Ind Co Ltd 断熱用熱可塑性樹脂発泡体
US4798749A (en) 1988-04-25 1989-01-17 Arco Chemical Company Isopentane as blowing agent to improve coffee retention in foam cups molded from expandable polystrene
BE1008947A3 (nl) 1994-12-01 1996-10-01 Dsm Nv Werkwijze voor de bereiding van condensatieproducten van melamine.
JP3018341U (ja) 1995-05-19 1995-11-21 株式会社トイボックス 表示装置
FR2758323B1 (fr) 1997-01-15 1999-08-06 Cordi Geopolymere Sa Methodes de fabrication de ciments geopolymeriques et ciments obtenus par ces methodes
TW425391B (en) 1997-03-04 2001-03-11 Nissan Chemical Ind Ltd Melamine-melam-melem salt of a polyphosphoric acid and process for its production
DE19709119A1 (de) 1997-03-06 1998-09-10 Basf Ag Schaumstoffplatten mit verminderter Wärmeleitfähigkeit
EP0981574B1 (de) 1997-05-14 2000-09-06 Basf Aktiengesellschaft Graphitpartikel enthaltende expandierbare styrolpolymerisate
US20020072547A1 (en) 2000-04-17 2002-06-13 Fina Technology, Inc. Expandable polystyrenes
DE10309385B4 (de) 2003-03-03 2007-01-18 Clariant Produkte (Deutschland) Gmbh Flammschutzmittel-Stabilisator-Kombination für thermoplastische Polymere und ihre Verwendung sowie flammfest ausgerüstete Kunststoff-Formmassen
ITMI20030627A1 (it) 2003-03-31 2004-10-01 Polimeri Europa Spa Polimeri vinilaromatici espandibili e procedimento per la loro preparazione.
WO2005054340A1 (en) 2003-12-02 2005-06-16 Commonwealth Scientific And Industrial Research Organisation Hybrid inorganic polymer systems
DE10358786A1 (de) 2003-12-12 2005-07-14 Basf Ag Partikelschaumformteile aus expandierbaren, Füllstoff enthaltenden Polymergranulaten
DE102004028768A1 (de) 2004-06-16 2005-12-29 Basf Ag Styrolpolymer-Partikelschaumstoffe mit verringerter Wärmeleitfähigkeit
DE102004034516A1 (de) 2004-07-15 2006-02-16 Basf Ag Verfahren zur Herstellung von flammgeschütztem, expandierbarem Polystyrol
DE102004058586A1 (de) 2004-12-03 2006-06-14 Basf Ag Halogenfrei flammgeschützte, expandierbare Styrolpolymerisate
DE102004058583A1 (de) 2004-12-03 2006-06-14 Basf Ag Expandierbare Styrolpolymergranulate und Partikelschaumstoffe mit verringerter Wärmeleitfähigkeit
WO2006061571A1 (en) 2004-12-06 2006-06-15 Ineos Europe Limited Expandable polystyrene composition
NL1028357C2 (nl) 2005-02-21 2006-08-22 Synbra Tech Bv Deeltjesvormig, expandeerbaar polystyreen (EPS), werkwijze ter vervaardiging van deeltjesvormig expandeerbaar polystyreen, alsmede een bijzondere toepassing van polystyreenschuimmateriaal.
US7794537B2 (en) 2006-08-07 2010-09-14 Schlumberger Technology Corporation Geopolymer composition and application in oilfield industry
JP5165991B2 (ja) 2006-11-23 2013-03-21 スルザー ケムテック アクチェンゲゼルシャフト ポリマー粒子を製造するための方法及びプラント
ITMI20062245A1 (it) 2006-11-23 2008-05-24 Polimeri Europa Spa Polimeri vinilaromatici espandibili a migliorata capacita' di isolamento termico e procedimento per la loro preparazione
CN101045832A (zh) 2007-03-22 2007-10-03 袁景华 地聚涂料组合物及其制备方法
ITMI20071003A1 (it) 2007-05-18 2008-11-19 Polimeri Europa Spa Compositi a base di polimeri vinilaromatici aventi migliorate proprieta' di isolamento termico e procedimento per la loro preparazione
EP1997849A1 (en) * 2007-05-30 2008-12-03 Nova Innovene International S.A. Fire retardant polystyrene
RU2470042C2 (ru) * 2007-05-30 2012-12-20 Инеос Нова Интернэшнл Са Огнестойкий полистирол
US8172940B2 (en) 2007-07-12 2012-05-08 Ceramatec, Inc. Treatment of fly ash for use in concrete
IT1393962B1 (it) 2009-05-05 2012-05-17 Polimeri Europa Spa Articoli espansi con ottima resistenza allo irraggiamento solare e ottime proprieta' termoisolanti e meccaniche
CN102741191B (zh) 2009-05-28 2014-09-17 陶氏环球技术有限责任公司 改性地质聚合物组合物、方法及用途
WO2010141976A1 (en) 2009-06-12 2010-12-16 Polyrox Pty Ltd Concrete aggregate
US20120184635A1 (en) 2009-07-03 2012-07-19 Sunpor Kunststoff Ges m.b.H. Flameproof expandable polymerizates
IT1396193B1 (it) 2009-10-07 2012-11-16 Polimeri Europa Spa Composizioni polimeriche nanocomposite termoplastiche espansibili con migliorata capacita' di isolamento termico.
KR101339390B1 (ko) * 2009-12-10 2013-12-09 주식회사 엘지화학 실리콘 및 팽창 질석을 포함하는 발포성 폴리스티렌 비드 및 이의 제조방법
KR101825249B1 (ko) 2010-12-02 2018-02-02 다우 글로벌 테크놀로지스 엘엘씨 팽창성, 할로겐-무함유 규소-인-질소계 중합체성 난연제
WO2012146577A1 (en) 2011-04-28 2012-11-01 Ineos Styrenics International Sa Fire retardant polystyrene
CN102430419B (zh) 2011-09-16 2013-04-24 西安建筑科技大学 Ni2+掺杂地质聚合物催化剂的制备及在有机物降解中的应用
WO2013044016A2 (en) 2011-09-21 2013-03-28 Arizona Board Of Regents, A Body Corporate Of The State Of Arizona Acting For And On Behalf Of Arizona State University Geopolymer resin materials, geopolymer materials, and materials produced thereby
CN102604291B (zh) * 2012-02-15 2014-01-22 四川大学 无卤阻燃聚乙烯醇泡沫材料及其制备方法
US9321681B2 (en) 2012-04-27 2016-04-26 United States Gypsum Company Dimensionally stable geopolymer compositions and method
KR101431002B1 (ko) * 2013-07-25 2014-09-22 주식회사 지케이 발포 폴리스티렌폼용 난연성 코팅 조성물
CN103449794A (zh) 2013-08-26 2013-12-18 温州大学 一种粉煤灰基地质聚合物稻壳保温砂浆
EP3087125B1 (en) * 2013-12-27 2020-11-25 Synthos Dwory 7 Spolka z ograniczona odpowiedzialnoscia spolka jawna Combination of a mineral component with carbon black and its use for decreasing the thermal conductivity of vinyl aromatic polymer
CN104803619B (zh) 2014-01-26 2017-05-03 神华集团有限责任公司 地质聚合物组合物及地质聚合物材料
FR3019176A1 (fr) 2014-03-27 2015-10-02 Commissariat Energie Atomique Procede de preparation d'un geopolymere macroporeux et mesoporeux, a porosite controlee
CN103980313A (zh) 2014-05-23 2014-08-13 厦门大学 一种磷氮协同阻燃多元醇及其制备方法
EP3154917A4 (en) 2014-06-12 2018-03-28 Arizona Board Of Regents, For And On Behalf Of Arizona State University Geopolymer aggregates
CN104341612B (zh) 2014-10-20 2016-11-30 南阳理工学院 一种磷氮阻燃剂及其制备方法
US10961154B2 (en) 2015-01-14 2021-03-30 Synthos S.A. Geopolymer composite and expandable vinyl aromatic polymer granulate and expanded vinyl aromatic polymer foam comprising the same
CN105400131B (zh) * 2015-12-12 2017-11-14 盐城市科恒达材料有限公司 一种特种电缆用复合材料、其制备方法及特种电缆
CN105462164B (zh) 2015-12-26 2018-12-21 唐思钊 一种耐低温特种电缆护套材料及其制备方法
CA3030685A1 (en) 2016-07-20 2018-01-25 Synthos S.A. Modified geopolymer and modified geopolymer composite and process for the production thereof
CN109476544A (zh) 2016-07-20 2019-03-15 西索斯公司 用于生产地质聚合物或地质聚合物复合材料的方法

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US11440843B2 (en) 2016-07-20 2022-09-13 Synthos S.A. Modified geopolymer and modified geopolymer composite and process for the production thereof
US12122720B2 (en) 2016-07-20 2024-10-22 Synthos S.A. Process for the production of geopolymer or geopolymer composite

Also Published As

Publication number Publication date
JP6761892B2 (ja) 2020-09-30
CA3031424A1 (en) 2018-01-25
EP3475241B1 (en) 2020-05-13
WO2018015502A1 (en) 2018-01-25
ES2810905T3 (es) 2021-03-09
AU2017300726A1 (en) 2019-02-14
CN109562998A (zh) 2019-04-02
DK3475241T3 (da) 2020-08-17
PL3475241T3 (pl) 2020-12-14
EA201990351A1 (ru) 2019-06-28
LT3475241T (lt) 2020-08-25
JP2019528334A (ja) 2019-10-10
US20240294722A1 (en) 2024-09-05
HUE051595T2 (hu) 2021-03-01
US20230052386A1 (en) 2023-02-16
US11993691B2 (en) 2024-05-28
IL264296A (en) 2019-02-28
UA125517C2 (uk) 2022-04-13
KR20190040189A (ko) 2019-04-17
BR112019000679A2 (pt) 2019-04-24
AU2017300726B2 (en) 2021-12-02
EP3475241A1 (en) 2019-05-01

Similar Documents

Publication Publication Date Title
US11993691B2 (en) Use of geopolymeric additive in combination with non-brominated flame retardant in polymer foams
US11708306B2 (en) Geopolymer composite and expandable vinyl aromatic polymer granulate and expanded vinyl aromatic polymer foam comprising the same
JP7050136B2 (ja) 低減した熱伝導度を有する発泡性ビニル芳香族ポリマー顆粒状物の生産のためのプロセス
JP2019521070A (ja) 改質ジオポリマー及び改質ジオポリマー複合材並びにこれらの生産のためのプロセス
WO2016113328A1 (en) Use of a mineral having perovskite structure in vinyl aromatic polymer foam

Legal Events

Date Code Title Description
STPP Information on status: patent application and granting procedure in general

Free format text: DOCKETED NEW CASE - READY FOR EXAMINATION

AS Assignment

Owner name: SYNTHOS S.A., POLAND

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:KONDRATOWICZ, FILIP LUKASZ;UTRATA, KAMIL;REEL/FRAME:052435/0827

Effective date: 20200325

STPP Information on status: patent application and granting procedure in general

Free format text: NON FINAL ACTION MAILED

STPP Information on status: patent application and granting procedure in general

Free format text: RESPONSE TO NON-FINAL OFFICE ACTION ENTERED AND FORWARDED TO EXAMINER

STPP Information on status: patent application and granting procedure in general

Free format text: FINAL REJECTION MAILED

STPP Information on status: patent application and granting procedure in general

Free format text: NON FINAL ACTION MAILED

STCB Information on status: application discontinuation

Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION