US20160083814A1 - High temperature oxidation-resistant coated steel plate and hot stamping method thereof - Google Patents
High temperature oxidation-resistant coated steel plate and hot stamping method thereof Download PDFInfo
- Publication number
- US20160083814A1 US20160083814A1 US14/594,544 US201514594544A US2016083814A1 US 20160083814 A1 US20160083814 A1 US 20160083814A1 US 201514594544 A US201514594544 A US 201514594544A US 2016083814 A1 US2016083814 A1 US 2016083814A1
- Authority
- US
- United States
- Prior art keywords
- high temperature
- temperature oxidation
- steel plate
- resistant
- coated steel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Links
Images
Classifications
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
- C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
- C21D8/0247—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the heat treatment
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B21—MECHANICAL METAL-WORKING WITHOUT ESSENTIALLY REMOVING MATERIAL; PUNCHING METAL
- B21D—WORKING OR PROCESSING OF SHEET METAL OR METAL TUBES, RODS OR PROFILES WITHOUT ESSENTIALLY REMOVING MATERIAL; PUNCHING METAL
- B21D22/00—Shaping without cutting, by stamping, spinning, or deep-drawing
- B21D22/02—Stamping using rigid devices or tools
- B21D22/022—Stamping using rigid devices or tools by heating the blank or stamping associated with heat treatment
-
- C—CHEMISTRY; METALLURGY
- C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
- C09D—COATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
- C09D1/00—Coating compositions, e.g. paints, varnishes or lacquers, based on inorganic substances
-
- C—CHEMISTRY; METALLURGY
- C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
- C09D—COATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
- C09D5/00—Coating compositions, e.g. paints, varnishes or lacquers, characterised by their physical nature or the effects produced; Filling pastes
- C09D5/08—Anti-corrosive paints
- C09D5/10—Anti-corrosive paints containing metal dust
- C09D5/103—Anti-corrosive paints containing metal dust containing Al
-
- C—CHEMISTRY; METALLURGY
- C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
- C09D—COATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
- C09D7/00—Features of coating compositions, not provided for in group C09D5/00; Processes for incorporating ingredients in coating compositions
- C09D7/40—Additives
- C09D7/60—Additives non-macromolecular
- C09D7/61—Additives non-macromolecular inorganic
-
- C—CHEMISTRY; METALLURGY
- C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
- C09D—COATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
- C09D7/00—Features of coating compositions, not provided for in group C09D5/00; Processes for incorporating ingredients in coating compositions
- C09D7/40—Additives
- C09D7/66—Additives characterised by particle size
- C09D7/69—Particle size larger than 1000 nm
-
- C—CHEMISTRY; METALLURGY
- C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
- C09D—COATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
- C09D7/00—Features of coating compositions, not provided for in group C09D5/00; Processes for incorporating ingredients in coating compositions
- C09D7/40—Additives
- C09D7/70—Additives characterised by shape, e.g. fibres, flakes or microspheres
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D1/00—General methods or devices for heat treatment, e.g. annealing, hardening, quenching or tempering
- C21D1/62—Quenching devices
- C21D1/673—Quenching devices for die quenching
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C24/00—Coating starting from inorganic powder
- C23C24/08—Coating starting from inorganic powder by application of heat or pressure and heat
- C23C24/082—Coating starting from inorganic powder by application of heat or pressure and heat without intermediate formation of a liquid in the layer
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
- C08K3/00—Use of inorganic substances as compounding ingredients
- C08K3/02—Elements
- C08K3/08—Metals
- C08K2003/0812—Aluminium
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
- C08K3/00—Use of inorganic substances as compounding ingredients
- C08K3/18—Oxygen-containing compounds, e.g. metal carbonyls
- C08K3/20—Oxides; Hydroxides
- C08K3/22—Oxides; Hydroxides of metals
- C08K2003/2227—Oxides; Hydroxides of metals of aluminium
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D2211/00—Microstructure comprising significant phases
- C21D2211/008—Martensite
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D9/00—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
- C21D9/46—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for sheet metals
Definitions
- the disclosure relates to a steel plate and hot stamping method thereof, more particular to a high temperature oxidation-resistant coated steel plate and hot stamping method thereof.
- Hot stamping technologies in the automobile industry due to advantages such as excellent formability, good dimensional stability, fewer forming steps and being capable of manufacturing automotive structural parts with a tensile strength more than 1470 MPa, have become major application technologies of manufacturing automotive metal plate parts at present.
- the temperature may usually exceed 900° C. during hot stamping, causing serious high temperature rust scales on a surface of the steel plate, so that a workpiece must be sandblasted after formation, so as to remove the rust scales.
- the high temperature rust scales on the surface of the steel plate may also cause serious pollution and wear to hot stamping molds, which not only cause trouble to production operations but also increase production costs.
- alumina and iron oxides may still exist on the surface of the steel plate, and the alumina and the iron oxides may cause high interface electric resistance, so that a great amount of heat during spot welding is generated, which easily causes expulsion.
- the copper electrode cap is easy to react with steels and cause bonding between them.
- iron and aluminum oxides exist in the weld nugget, mechanical properties of it is deteriorate.
- the conventional coating still has disadvantages of poor high temperature oxidation resistance and spot weldability. Therefore, it is necessary to provide a high temperature oxidation-resistant coated steel plate and hot stamping method thereof, so as to solve the foregoing deficiencies in the prior art.
- a high temperature oxidation-resistant coated steel plate includes a steel base material and a high temperature oxidation-resistant coating.
- the high temperature oxidation-resistant coating is formed by coating a high temperature oxidation-resistant paint onto the steel base material and baking in an oven.
- the high temperature oxidation-resistant paint includes a binder and a plurality of micron aluminum flakes.
- the binder has a three-dimensional molecular structure of Al—O.
- the micron aluminum flakes has a micron-sized thickness and a length ranging from 5 to 30 ⁇ m inclusive.
- a hot stamping method of a high temperature oxidation-resistant coated steel plate includes steps in which a high temperature oxidation-resistant coated steel plate is provided. The method continues with step in which the high temperature oxidation-resistant coated steel plate is heated to an austenitizing state. The method continues with step in which the high temperature oxidation-resistant coated steel plate is transferred to a mold for hot stamping, to form an object.
- a paint is formed with a binder and micron aluminum flakes and applied to a steel base material to form a high temperature oxidation-resistance coating.
- the coating enhances the high temperature oxidation-resistance and hot stamping characteristics of the coated steel plate, and makes objects after hot stamping have good spot weldability and coating performance.
- FIG. 1 is a schematic structural view of a high temperature oxidation-resistant coated steel plate according to the present disclosure.
- FIG. 2 is a flow diagram of a hot stamping method of a high temperature oxidation-resistant coated steel plate according to the present disclosure.
- FIG. 1 is a schematic structural view of a high temperature oxidation-resistant coated steel plate according to the present disclosure.
- the high temperature oxidation-resistant coated steel plate 10 of the present disclosure includes a steel base material 12 and a high temperature oxidation-resistant coating 14 .
- the steel base material 12 is a manganese-boron steel base material.
- the high temperature oxidation-resistant coating 14 is formed by coating a high temperature oxidation-resistant paint onto the steel base material 12 and baking in an oven.
- the thickness of the high temperature oxidation-resistant coating 14 needs to be controlled between 2 and 10 ⁇ m inclusive, because high temperature oxidation resistance of the coating will be reduced when the thickness is less than 2 ⁇ m, and spot weldability of the steel plate will be worsened when the thickness is greater than 10 ⁇ m.
- the baking temperature of the high temperature oxidation-resistant coating 14 should be controlled between 120 and 300° C. inclusive, and the baking time should be controlled between 36 and 90 seconds inclusive.
- the coating method of the high temperature oxidation-resistant paint is selected from one of the following: spraying, roller coating and dip coating.
- the high temperature oxidation-resistant paint includes a binder and a plurality of micron aluminum flakes.
- the binder has a three-dimensional molecular structure of Al—O, and the binder is made with a sol-gel method.
- the micron aluminum flakes has a micron-sized thickness (about 0.5 to 1 ⁇ m thick) and a length ranging from 5 to 30 ⁇ m inclusive, and preferably, the weight of the micron aluminum flakes is 5-30% of the total weight of the paint.
- the high temperature oxidation-resistant coated steel plate 10 can adopt continuous steel coil production or discontinuous blank production. If the continuous steel coil production is adopted, the production process can be: unwinding ⁇ alkali washing ⁇ drying ⁇ roller coating or dip coating (two sides) ⁇ baking ⁇ coiling. If the discontinuous chip production is adopted, the production process can be: blanking ⁇ alkali washing ⁇ drying ⁇ spraying (one side) ⁇ baking ⁇ spraying (the other side) ⁇ baking ⁇ stacking and packing.
- FIG. 2 is a flow diagram of a hot stamping method of a high temperature oxidation-resistant coated steel plate according to the present disclosure.
- a high temperature oxidation-resistant coated steel plate 10 is provided.
- the high temperature oxidation-resistant coated steel plate 10 includes a steel base material 12 and a high temperature oxidation-resistant coating 14 .
- the high temperature oxidation-resistant coating 14 is formed by coating a high temperature oxidation-resistant paint onto the steel base material 12 and baking in an oven.
- the high temperature oxidation-resistant paint includes a binder and a plurality of micron aluminum flakes.
- the binder has a three-dimensional molecular structure of Al—O, and the micron aluminum flakes has a micron-sized thickness (about 0.5 to 1 ⁇ m thick) and a length ranging from 5 to 30 ⁇ m inclusive.
- a tensile strength of the high temperature oxidation-resistant coated steel plate 10 is 500 to 600 MPa inclusive.
- the high temperature oxidation-resistant coated steel plate 10 is heated to an austenitizing state.
- the heating temperature is 870 to 950° C. inclusive, and the heating time is 3 to 5 minutes inclusive.
- the high temperature oxidation-resistant coated steel plate 10 is transferred to a mold (not shown) for hot stamping, to form an object.
- the step includes: performing pressure holding and quenching treatment on the object at a cooling rate greater than 27° C./s, so as to make the object to have a uniform martensite organization, thereby obtaining a tensile strength greater than 1400 MPa.
- the high temperature oxidation-resistant paint is composed of the binder and the micron aluminum flakes, and the high temperature oxidation-resistant paint is applied to a high temperature oxidation-resistant coating 14 formed on a steel base material 12 , which can enhance the high temperature oxidation-resistance and hot stamping characteristics of the coated steel plate 10 , and makes objects after hot stamping to have good spot weldability and coating performance.
- a high temperature oxidation-resistant paint was prepared by mixing binder and aluminum flakes.
- the weight of micron aluminum flakes added to the paint was 30% of the total weight of the paint.
- the length of the micron aluminum flakes was 5 to 10 ⁇ m.
- An appropriate amount of dispersing agent was added to make the micron aluminum flakes mix uniformly and completely with binder to obtain a solid content of 50 to 60 wt %.
- the paint was coated onto a manganese-boron steel base material through spraying.
- the thickness of the coating was 3 ⁇ 1 ⁇ m.
- the steel plate was baked in oven at 270° C. for 48 seconds.
- the coated steel plate after baking was placed in an air oven of 930° C. for 5 minutes, and then was quickly transferred to a mold for hot-stamping forming.
- the cross-cut test (ASTM D3359) is performed on the coated steel plate after baking, and the coating did not fall off at all after tape was removed. It represented good coating adhesion between steel plate and the coating. Similarly, the cross-cut test was performed on the object after hot stamping, and the coating did not fall off at all neither.
- a planar light source resistance measurement module (Surface Resistance Meter, Manufacturer/Model: Mitsubishi Chemical Analytech/Loresta-GP MCP-T610) was used to measure the surface electric resistance of the hot-stamping object with a four-point probe at a given current. The surface electric resistance of the object was measured to be less than 1 ⁇ 10 ⁇ 2 ⁇ .
- the spot welding test result showed no phenomenon of expulsion and no sign of spot welding electrode cap bonding with the hot-stamping object, indicating that its welding characteristics were identical with those of the bare steel.
- the hot-stamping object could also be coated by electro-deposition coating process. The tensile strength of the object after hot stamping reached 1500 MPa.
- a high temperature oxidation-resistant paint was prepared by mixing binder and aluminum flakes.
- the weight of micron aluminum flakes added to the paint was 15% of the total weight of the paint.
- the length of the micron aluminum flakes was 5 to 10 ⁇ m.
- An appropriate amount of dispersing agent was added to make the micron aluminum flakes mix uniformly and completely with binder to obtain a solid content of 40 to 50 wt %.
- the paint was coated onto a manganese-boron steel base material through spraying.
- the thickness of the coating was 5 ⁇ 1 ⁇ m.
- the steel plate was baked in oven at 150° C. for 36 seconds.
- the coated steel plate after baking was placed in an air oven of 890° C. for 5 minutes, and then was quickly transferred to a mold for hot-stamping forming.
- the cross-cut test (ASTM D3359) is performed on the coated steel plate after baking, and the coating did not fall off at all when the tape was removed. It represented good adhesion between steel plate and the coating. Similarly, the cross-cut test was performed on the object after hot stamping, and the coating did not fall off at all neither when the tape was removed.
- a planar light source resistance measurement module (Surface Resistance Meter, Manufacturer/Model: Mitsubishi Chemical Analytech/Loresta-GP MCP-T610) was used to measure the surface electric resistance of the hot-stamping object with a four-point probe at a given current. The surface electric resistance of the object was measured to be less than 1 ⁇ 10 ⁇ 2 ⁇ .
- the spot welding test result showed no phenomenon of expulsion and no sign of spot welding electrode cap bonding with the hot-stamping object, indicating that its welding characteristics were identical with those of the bare steel.
- the tensile strength of the object after hot stamping reached 1500 MPa.
- a high temperature oxidation-resistant paint was prepared by mixing binder and aluminum flakes.
- the weight of micron aluminum flakes added to the paint was 10% of the total weight of the paint.
- the length of the micron aluminum flakes was 5 to 10 ⁇ m.
- An appropriate amount of dispersing agent was added to make the micron aluminum flakes mix uniformly and completely with binder to obtain a solid content of 35 to 45 wt %.
- the paint was coated onto a manganese-boron steel base material through spraying.
- the thickness of the coating was 9 ⁇ 1 ⁇ m.
- the steel plate was baked in oven at 300° C. for 60 seconds.
- the coated steel plate after baking was placed in an air oven of 870° C. for 5 minutes, and then was quickly transferred to a mold for hot-stamping forming.
- the cross-cut test (ASTM D3359) is performed on the coated steel plate after baking, and the coating did not fall off at all after tape was removed. It represented good coating adhesion between steel plate and the coating. Similarly, the cross-cut test was performed on the object after hot stamping, and the coating did not fall off at all neither.
- a planar light source resistance measurement module (Surface Resistance Meter, Manufacturer/Model: Mitsubishi Chemical Analytech/Loresta-GP MCP-T610) was used to measure the surface electric resistance of the hot-stamping object with a four-point probe at a given current. The surface electric resistance of the object was measured to be less than 1 ⁇ 10 ⁇ 2 ⁇ .
- the spot welding test result showed no phenomenon of expulsion and no sign of spot welding electrode cap bonding with the hot-stamping object, indicating that its welding characteristics were identical with those of the bare steel.
- the hot-stamping object could also be coated by electro-deposition coating process. The tensile strength of the object after hot stamping reached 1480 MPa.
- a high temperature oxidation-resistant paint was prepared by mixing binder and aluminum flakes.
- the weight of micron aluminum flakes added to the paint was 20% of the total weight of the paint.
- the length of the micron aluminum flakes was 5 to 10 ⁇ m.
- An appropriate amount of dispersing agent was added to make the micron aluminum flakes mix uniformly and completely with binder to obtain a solid content of 45 to 55 wt %.
- the cross-cut test (ASTM D3359) is performed on the coated steel plate after baking, and the coating falled off partially (about 5%) after tape was removed. It represented poor coating adhesion between steel plate and the coating. Similarly, the cross-cut test was performed on the object after hot stamping, and the coating did not fall off.
- a planar light source resistance measurement module (Surface Resistance Meter, Manufacturer/Model: Mitsubishi Chemical Analytech/Loresta-GP MCP-T610) was used to measure the surface electric resistance of the hot-stamping object with a four-point probe at a given current. The surface electric resistance of the object was measured to be 2 ⁇ 10 ⁇ 2 ⁇ , which indicates that the surface electric resistance is high.
- spot welding test result showed slight expulsion and spot welding electrode cap bonding with the hot-stamping object, indicating that its welding characteristics were worse then those of the bare steel.
- the hot-stamping object could be coated by electro-deposition coating process.
- a high temperature oxidation-resistant paint was prepared by mixing binder and aluminum flakes.
- the weight of micron aluminum flakes added to the paint was 5% of the total weight of the paint.
- the length of the micron aluminum flakes was 5 to 10 ⁇ m.
- An appropriate amount of dispersing agent was added to make the micron aluminum flakes mix uniformly and completely with binder to obtain a solid content of 25 to 35 wt %.
- the paint was coated onto a manganese-boron steel base material through spraying.
- the thickness of the coating was 5 ⁇ 1 ⁇ m.
- the steel plate was baked in oven at 120° C. for 90 seconds.
- the coated steel plate after baking was placed in an air oven of 870° C. for 5 minutes, and then was quickly transferred to a mold for hot-stamping forming.
- the cross-cut test (ASTM D3359) is performed on the coated steel plate after baking, and the coating falled off partially (about 5%) after tape was removed. It represented poor coating adhesion between steel plate and the coating. Similarly, the cross-cut test was performed on the object after hot stamping, and the coating did not fall off.
- a planar light source resistance measurement module (Surface Resistance Meter, Manufacturer/Model: Mitsubishi Chemical Analytech/Loresta-GP MCP-T610) was used to measure the surface electric resistance of the hot-stamping object with a four-point probe at a given current. The surface electric resistance of the object was measured to be 1 ⁇ 10 ⁇ 1 ⁇ , which indicates that the surface electric resistance is high.
- spot welding test result showed slight expulsion and spot welding electrode cap bonding with the hot-stamping object, indicating that its welding characteristics were worse then those of the bare steel.
- the reason for the high surface electric resistance was that the weight of the added micron aluminum flakes was excessively low.
- the hot-stamping object could be coated by electro-deposition coating process.
Landscapes
- Chemical & Material Sciences (AREA)
- Engineering & Computer Science (AREA)
- Materials Engineering (AREA)
- Organic Chemistry (AREA)
- Mechanical Engineering (AREA)
- Life Sciences & Earth Sciences (AREA)
- Wood Science & Technology (AREA)
- Metallurgy (AREA)
- Thermal Sciences (AREA)
- Physics & Mathematics (AREA)
- Crystallography & Structural Chemistry (AREA)
- Inorganic Chemistry (AREA)
- Chemical Kinetics & Catalysis (AREA)
- Nanotechnology (AREA)
- Shaping Metal By Deep-Drawing, Or The Like (AREA)
- Paints Or Removers (AREA)
- Chemically Coating (AREA)
- Heat Treatment Of Articles (AREA)
- Other Surface Treatments For Metallic Materials (AREA)
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
TW103131986 | 2014-09-16 | ||
TW103131986A TWI488925B (zh) | 2014-09-16 | 2014-09-16 | Anti - high temperature oxidation coating steel plate and its hot stamping method |
Publications (1)
Publication Number | Publication Date |
---|---|
US20160083814A1 true US20160083814A1 (en) | 2016-03-24 |
Family
ID=52432648
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
US14/594,544 Abandoned US20160083814A1 (en) | 2014-09-16 | 2015-01-12 | High temperature oxidation-resistant coated steel plate and hot stamping method thereof |
Country Status (4)
Country | Link |
---|---|
US (1) | US20160083814A1 (ja) |
EP (1) | EP2998366A1 (ja) |
JP (1) | JP6282578B2 (ja) |
TW (1) | TWI488925B (ja) |
Cited By (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US20190376155A1 (en) * | 2017-01-09 | 2019-12-12 | Henkel Ag & Co., Kgaa | Curable protective coating composition |
Families Citing this family (3)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
TWI615207B (zh) * | 2016-01-21 | 2018-02-21 | 中國鋼鐵股份有限公司 | 抗高溫氧化塗裝鋼板及其製造方法與應用 |
CN107470427B (zh) * | 2017-08-01 | 2019-03-01 | 清华大学 | 一种金属及其合金微纳米结构或纳米线阵列的制备方法 |
CN110773721B (zh) * | 2019-09-25 | 2020-10-09 | 马鞍山市三川机械制造有限公司 | 一种钢结构材料热处理前的抗氧化处理工艺 |
Citations (4)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US3776473A (en) * | 1972-03-27 | 1973-12-04 | Int Nickel Co | Highly reflective aluminum flake |
US4863516A (en) * | 1987-01-23 | 1989-09-05 | Sermatech International, Inc. | Coating composition |
US20100175794A1 (en) * | 2007-08-13 | 2010-07-15 | Stefan Sepeur | Process for Producing an Active Cathodic Anti-Corrosion Coating on Steel Elements |
US20130000372A1 (en) * | 2010-03-17 | 2013-01-03 | Nano-X Gmbh | Process for producing a coated metal strip |
Family Cites Families (11)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JPS6187877A (ja) * | 1984-10-05 | 1986-05-06 | Nippon Steel Corp | ステンレス鋼への耐高温酸化性皮膜形成方法 |
US5478413A (en) * | 1994-12-27 | 1995-12-26 | Sermatech International, Inc. | Environmentally friendly coating compositions |
JP2002115084A (ja) * | 2000-08-02 | 2002-04-19 | Ishizuka Glass Co Ltd | 表面処理剤、表面処理膜、表面改質金属材料 |
DE102004049413A1 (de) * | 2004-10-08 | 2006-04-13 | Volkswagen Ag | Verfahren zur Beschichtung von metallischen Oberflächen |
PL2086755T3 (pl) * | 2006-10-30 | 2018-05-30 | Arcelormittal | Powlekane taśmy stalowe, sposoby wytwarzania takich powlekanych taśm, sposoby zastosowania takich powlekanych taśm, półfabrykaty do wytłaczania przygotowane z powlekanych taśm, wyroby wytłaczane przygotowane z powlekanych taśm, wyroby zawierające takie wyroby wytłaczane |
WO2009081452A1 (ja) * | 2007-12-25 | 2009-07-02 | Restoration Environment Rebirth Co., Ltd. | 防食剤およびその製造方法 |
US8101242B2 (en) * | 2008-03-07 | 2012-01-24 | Sri International | Method of imparting corrosion resistance to a substrate surface, and coated substrates prepared thereby |
CN100590156C (zh) * | 2008-04-28 | 2010-02-17 | 山东大学 | 一种无铬达克罗涂料 |
MX2012014594A (es) * | 2010-06-14 | 2013-02-21 | Nippon Steel & Sumitomo Metal Corp | Articulo moldeado y estampado en caliente, proceso para produccion de placa de acero para estampado en caliente, y proceso para produccion de un articulo moldeado y estampado en caliente. |
KR101119173B1 (ko) * | 2011-09-30 | 2012-02-22 | 현대하이스코 주식회사 | 레이저 열처리를 이용한 이종강도를 갖는 강 제품 제조 방법 및 이에 이용되는 열처리 경화강 |
CN103614640B (zh) * | 2013-12-12 | 2016-10-05 | 马鸣图 | 一种抗高温氧化的非镀层热冲压成形用钢 |
-
2014
- 2014-09-16 TW TW103131986A patent/TWI488925B/zh active
- 2014-11-27 JP JP2014240257A patent/JP6282578B2/ja active Active
-
2015
- 2015-01-12 US US14/594,544 patent/US20160083814A1/en not_active Abandoned
- 2015-01-15 EP EP15151285.2A patent/EP2998366A1/en not_active Withdrawn
Patent Citations (4)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US3776473A (en) * | 1972-03-27 | 1973-12-04 | Int Nickel Co | Highly reflective aluminum flake |
US4863516A (en) * | 1987-01-23 | 1989-09-05 | Sermatech International, Inc. | Coating composition |
US20100175794A1 (en) * | 2007-08-13 | 2010-07-15 | Stefan Sepeur | Process for Producing an Active Cathodic Anti-Corrosion Coating on Steel Elements |
US20130000372A1 (en) * | 2010-03-17 | 2013-01-03 | Nano-X Gmbh | Process for producing a coated metal strip |
Non-Patent Citations (1)
Title |
---|
Schlenk, "World of Metallics, Pigments," March 2011, downloaded from www.schlenk.com (on 22 November 2017) (20 pages). * |
Cited By (2)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US20190376155A1 (en) * | 2017-01-09 | 2019-12-12 | Henkel Ag & Co., Kgaa | Curable protective coating composition |
US11186883B2 (en) * | 2017-01-09 | 2021-11-30 | Henkel Ag & Co. Kgaa | Curable protective coating composition |
Also Published As
Publication number | Publication date |
---|---|
TW201612256A (en) | 2016-04-01 |
JP2016060965A (ja) | 2016-04-25 |
EP2998366A1 (en) | 2016-03-23 |
TWI488925B (zh) | 2015-06-21 |
JP6282578B2 (ja) | 2018-02-21 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
US20160083814A1 (en) | High temperature oxidation-resistant coated steel plate and hot stamping method thereof | |
US9593391B2 (en) | Strip, sheet or blank suitable for hot forming and process for the production thereof | |
CN103221581B (zh) | 热压用钢板及使用热压用钢板而成的热压部件的制造方法 | |
CN103342958B (zh) | 一种耐高温的粉末涂料 | |
JP6011732B2 (ja) | 熱間プレス用Alめっき鋼板及び熱間プレス用Alめっき鋼板の製造方法 | |
JP5607179B2 (ja) | 優れた溶接性、加工性、耐食性を有するプレコート鋼板用樹脂組成物、これを利用したプレコート鋼板の製造方法及び鋼板 | |
CN103421362A (zh) | 一种抗氧化涂料及其制备方法 | |
JP5365154B2 (ja) | 熱間プレス加工用鋼板 | |
CN104112550A (zh) | 一种铝铜合金漆包线的制作方法 | |
CN102911599A (zh) | 一种应用于越野车刹车盘类零件的耐热保护涂层 | |
JP5672167B2 (ja) | 熱処理用表面処理鋼板、熱処理鋼材の製造方法、および熱処理鋼材 | |
CN107240995A (zh) | 一种定转子铁心的防锈方法 | |
EP2500109A1 (en) | Powder coating method | |
CN108411087B (zh) | 一种附着力优良的无取向电工钢生产方法 | |
CN111087892A (zh) | 一种石墨烯锌铝涂料 | |
WO2013056847A1 (en) | Anti-scale and anti-corrosion hybrid coatings for steel substrates | |
CN103320007B (zh) | 耐高温的粉末涂料的制备方法 | |
CN105618360A (zh) | 抗高温氧化涂装钢板及其热冲压成形方法 | |
CN108715989A (zh) | 一种等离子喷涂绝缘涂层的制备方法 | |
TWI589362B (zh) | 抗高溫氧化塗裝鋼板及其製造方法與應用 | |
CN103147036B (zh) | 汽车空调压缩机配件的局部渗碳方法 | |
JP2011157576A (ja) | 熱間プレス鋼材の製造方法 | |
TWI615207B (zh) | 抗高溫氧化塗裝鋼板及其製造方法與應用 | |
CN202088615U (zh) | 具有绝缘涂层的铝带材 | |
JP2016215630A (ja) | 表面処理アルミニウム材及びその製造方法、並びに複合成形体及びその製造方法 |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
AS | Assignment |
Owner name: CHINA STEEL CORPORATION, TAIWAN Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:HSIEH, SHEAU-HWA;WANG, SHI-WEI;HSU, CHENG-EN;AND OTHERS;REEL/FRAME:034683/0207 Effective date: 20141127 |
|
AS | Assignment |
Owner name: CHINA STEEL CORPORATION, TAIWAN Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:HSIEH, SHEAU-HWA;WANG, SHI-WEI;HSU, CHENG-EN;AND OTHERS;SIGNING DATES FROM 20150212 TO 20150226;REEL/FRAME:035163/0681 |
|
STCB | Information on status: application discontinuation |
Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION |