Classifications

• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
  • C08L23/00—Compositions of homopolymers or copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond; Compositions of derivatives of such polymers
  • C08L23/02—Compositions of homopolymers or copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond; Compositions of derivatives of such polymers not modified by chemical after-treatment
  • C08L23/10—Homopolymers or copolymers of propene
  • C08L23/14—Copolymers of propene
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
  • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
  • B29C43/00—Compression moulding, i.e. applying external pressure to flow the moulding material; Apparatus therefor
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
  • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
  • B29C45/00—Injection moulding, i.e. forcing the required volume of moulding material through a nozzle into a closed mould; Apparatus therefor
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
  • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
  • B29C49/00—Blow-moulding, i.e. blowing a preform or parison to a desired shape within a mould; Apparatus therefor
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
  • C08K3/00—Use of inorganic substances as compounding ingredients
  • C08K3/34—Silicon-containing compounds
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
  • C08K5/00—Use of organic ingredients
  • C08K5/49—Phosphorus-containing compounds
  • C08K5/51—Phosphorus bound to oxygen
  • C08K5/52—Phosphorus bound to oxygen only
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
  • C08K9/00—Use of pretreated ingredients
  • C08K9/04—Ingredients treated with organic substances
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
  • C08L23/00—Compositions of homopolymers or copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond; Compositions of derivatives of such polymers
  • C08L23/02—Compositions of homopolymers or copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond; Compositions of derivatives of such polymers not modified by chemical after-treatment
  • C08L23/04—Homopolymers or copolymers of ethene
  • C08L23/08—Copolymers of ethene
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
  • C08L23/00—Compositions of homopolymers or copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond; Compositions of derivatives of such polymers
  • C08L23/02—Compositions of homopolymers or copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond; Compositions of derivatives of such polymers not modified by chemical after-treatment
  • C08L23/04—Homopolymers or copolymers of ethene
  • C08L23/08—Copolymers of ethene
  • C08L23/0807—Copolymers of ethene with unsaturated hydrocarbons only containing more than three carbon atoms
  • C08L23/0815—Copolymers of ethene with aliphatic 1-olefins
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
  • C08L23/00—Compositions of homopolymers or copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond; Compositions of derivatives of such polymers
  • C08L23/02—Compositions of homopolymers or copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond; Compositions of derivatives of such polymers not modified by chemical after-treatment
  • C08L23/10—Homopolymers or copolymers of propene
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
  • C08L23/00—Compositions of homopolymers or copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond; Compositions of derivatives of such polymers
  • C08L23/02—Compositions of homopolymers or copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond; Compositions of derivatives of such polymers not modified by chemical after-treatment
  • C08L23/10—Homopolymers or copolymers of propene
  • C08L23/12—Polypropene
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
  • B29K—INDEXING SCHEME ASSOCIATED WITH SUBCLASSES B29B, B29C OR B29D, RELATING TO MOULDING MATERIALS OR TO MATERIALS FOR MOULDS, REINFORCEMENTS, FILLERS OR PREFORMED PARTS, e.g. INSERTS
  • B29K2023/00—Use of polyalkenes or derivatives thereof as moulding material
  • B29K2023/10—Polymers of propylene
  • B29K2023/14—Copolymers of polypropylene
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
  • B29K—INDEXING SCHEME ASSOCIATED WITH SUBCLASSES B29B, B29C OR B29D, RELATING TO MOULDING MATERIALS OR TO MATERIALS FOR MOULDS, REINFORCEMENTS, FILLERS OR PREFORMED PARTS, e.g. INSERTS
  • B29K2509/00—Use of inorganic materials not provided for in groups B29K2503/00 - B29K2507/00, as filler
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
  • B29L—INDEXING SCHEME ASSOCIATED WITH SUBCLASS B29C, RELATING TO PARTICULAR ARTICLES
  • B29L2031/00—Other particular articles
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
  • C08K5/00—Use of organic ingredients
  • C08K5/49—Phosphorus-containing compounds
  • C08K5/51—Phosphorus bound to oxygen
  • C08K5/52—Phosphorus bound to oxygen only
  • C08K5/524—Esters of phosphorous acids, e.g. of H3PO3
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
  • C08L2205/00—Polymer mixtures characterised by other features
  • C08L2205/02—Polymer mixtures characterised by other features containing two or more polymers of the same C08L -group
  • C08L2205/025—Polymer mixtures characterised by other features containing two or more polymers of the same C08L -group containing two or more polymers of the same hierarchy C08L, and differing only in parameters such as density, comonomer content, molecular weight, structure
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
  • C08L2205/00—Polymer mixtures characterised by other features
  • C08L2205/03—Polymer mixtures characterised by other features containing three or more polymers in a blend
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
  • C08L2207/00—Properties characterising the ingredient of the composition
  • C08L2207/02—Heterophasic composition
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
  • C08L23/00—Compositions of homopolymers or copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond; Compositions of derivatives of such polymers
  • C08L23/02—Compositions of homopolymers or copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond; Compositions of derivatives of such polymers not modified by chemical after-treatment
  • C08L23/04—Homopolymers or copolymers of ethene
  • C08L23/08—Copolymers of ethene
  • C08L23/0807—Copolymers of ethene with unsaturated hydrocarbons only containing more than three carbon atoms
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
  • C08L2308/00—Chemical blending or stepwise polymerisation process with the same catalyst

Definitions

• the invention relates to a process for the preparation of a composition comprising a heterophasic propylene copolymer and talc, a composition obtained or obtainable by said process and to the use of said composition.
• Heterophasic propylene copolymer also known as impact propylene copolymers or propylene block copolymers
• impact propylene copolymers also known as impact propylene copolymers or propylene block copolymers
• propylene block copolymers are an important class of polymers due to their attractive combination of mechanical properties, such as impact strength over a wide temperature range and their low cost. These copolymers find a wide range of applications ranging from the consumer industry (for example packaging and housewares), the automotive industry to electrical applications.
• peroxides initiate a breakage of the longest chains of the polymer molecules and, subsequently, this results in a decrease in viscosity of the polymer, an increase in melt flow rate, and a narrower molecular weight distribution, characteristics which are directly responsible for improved flow properties of polypropylene in order to make the product more suitable for certain applications.
• US2005/0277742A1 discloses a process for preparing a controlled rheology propylene heterophasic copolymer by degrading a polypropylene with a linear dialkyl peroxide having a backbone containing at least 6 carbon atoms and a double or triple bond comprising the steps of: either
• step (b) extruding the propylene heterophasic copolymer of step (a), with said linear dialkyl peroxide having a backbone containing at least 6 carbon atoms and a double or triple bond, and optionally with one or more filler(s), in an extruder, at a temperature sufficient to maintain the copolymer in the molten state; or
• talc may be added as a filler.
• more peroxide is needed in order to obtain the same increase in melt flow rate of a heterophasic propylene copolymer as compared to when talc is not present in the heterophasic propylene copolymer. It is undesired to use high amounts of peroxides, since high amounts of typical peroxide degradation products, for example methane and acetone may lead to safety issues during the manufacturing process.
• the use of high amounts of peroxides adds to the cost of the heterophasic polypropylene, which is undesired from an economical point of view.
• the use of high amounts of peroxides leads to high amounts of peroxide degradation products and impurities in the final polymer. These peroxide degradation products may be released during the life-time of the heterophasic propylene copolymer composition, which is undesired, as they may cause unpleasant odours and may affect organoleptic properties.
• high amounts of peroxide degradation products make the heterophasic propylene copolymer unsuitable for food contact applications.
• This object is achieved by a process for the preparation of a composition comprising a heterophasic propylene copolymer, a propylene copolymer and talc, wherein the heterophasic propylene copolymer consists of
• propylene-based matrix consists of a propylene homopolymer and/or a propylene- ⁇ -olefin copolymer consisting of at least 70% by mass of propylene and up to 30% by mass of ⁇ -olefin, for example ethylene, based on the total mass of the propylene-based matrix, and wherein the propylene-based matrix is present in an amount of 60 to 95 wt % based on the total heterophasic propylene copolymer, and
• a dispersed ethylene- ⁇ -olefin copolymer wherein the dispersed ethylene- ⁇ -olefin copolymer is present in an amount of 40 to 5 wt % based on the total heterophasic propylene copolymer and wherein the sum of the total amount of propylene-based matrix and total amount of the dispersed ethylene- ⁇ -olefin copolymer in the heterophasic propylene copolymer is 100 wt %
• composition has a desired melt flow index in the range of 1 to 200 dg/min as measured according to ISO1133 (2.16 kg/230° C.),
• a heterophasic polypropylene composition can be prepared that combines the favourable properties of a high stiffness, a good impact strength and a high flow with a decreased amount of peroxide degradation products.
• the process of the invention is an easy and cost-effective process.
• the heterophasic polypropylene composition thus prepared may maintain its (mechanical) properties.
• stiffness is determined by measuring the flexural modulus according to ASTM D790-10.
• impact strength is determined by measuring the Izod impact strength at 23° C. according to ISO 180 4A.
• flow is determined by measuring the melt flow rate, also called melt flow index or melt index according to ISO1133 (2.16 kg/230° C.).
• Heterophasic propylene copolymers are generally prepared in one or more reactors, by polymerization of propylene in the presence of a catalyst and subsequent polymerization of a propylene- ⁇ -olefin mixture.
• the resulting polymeric materials are heterophasic, but the specific morphology usually depends on the preparation method and monomer ratio.
• heterophasic propylene copolymers employed in the process according to present invention can be produced using any conventional technique known to the skilled person, for example multistage process polymerization, such as bulk polymerization, gas phase polymerization, slurry polymerization, solution polymerization or any combinations thereof.
• Any conventional catalyst systems for example, Ziegler-Natta or metallocene may be used.
• Such techniques and catalysts are described, for example, in WO06/010414; Polypropylene and other Polyolefins, by Ser van der Ven, Studies in Polymer Science 7, Elsevier 1990; WO06/010414, U.S. Pat. No. 4,399,054 and U.S. Pat. No. 4,472,524.
• the heterophasic propylene copolymer of the composition of the invention consists of a propylene-based matrix and a dispersed ethylene- ⁇ -olefin copolymer.
• the propylene-based matrix forms the continuous phase in the heterophasic propylene copolymer.
• the propylene-based matrix consists of a propylene homopolymer and/or a propylene- ⁇ -olefin copolymer consisting of at least 70% by mass of propylene and up to 30% by mass of ⁇ -olefin, for example ethylene, for example consisting of at least 80% by mass of propylene and up to 20% by mass of ⁇ -olefin, for example ethylene, for example consisting of at least 90% by mass of propylene and up to 10% by mass of ⁇ -olefin, for example ethylene, based on the total mass of the propylene-based matrix.
• the propylene-based matrix consists of a propylene homopolymer.
• the ⁇ -olefin in the propylene- ⁇ -olefin copolymer is selected from the group of ⁇ -olefins having 2 or 4-10 carbon atoms and more preferably the ⁇ -olefin is ethylene.
• the melt flow index (MFI) of the propylene-based matrix may be in the range of for example 0.3 to 200 dg/min, for example from 0.3 to 80 dg/min measured according to ISO1133 (2.16 kg/230° C.), for example in the range from 3 to 70, for example in the range from 10 to 60 dg/min, for example in the range from 15 to 40 dg/min.
• the propylene-based matrix is present in an amount of 60 to 95 wt %, for example 65 to 85 wt %, for example 70 to 85 wt %, for example 70 to 80 wt %, for example 65 to 75 wt % or 75 to 85 wt % based on the total heterophasic propylene copolymer.
• the propylene-based matrix is preferably semi-crystalline, that is it is not 100% amorphous, nor is it 100% crystalline.
• the propylene-based matrix is at least 40% crystalline, for example at least 50%, for example at least 60% crystalline and/or for example at most 80% crystalline, for example at most 70% crystalline.
• the propylene-based matrix has a crystallinity of 60 to 70%.
• the degree of crystallinity of the propylene-based matrix is measured using differential scanning calorimetry according to ISO11357-1 and ISO11357-3 of 1997, using a scan rate of 10° C./min, a sample of 5 mg and the second heating curve using as a theoretical standard for a 100% crystalline material 207.1 J/g.
• the heterophasic propylene copolymer also consists of a dispersed ethylene- ⁇ -olefin copolymer.
• the dispersed ethylene- ⁇ -olefin copolymer is also referred to herein as the ‘dispersed phase’.
• the dispersed phase is embedded in the heterophasic propylene copolymer in a discontinuous form.
• the particle size of the dispersed phase is typically in the range of 0.5 to 10 microns, as may be determined by transmission electron microscopy (TEM).
• the MFI of the dispersed ethylene- ⁇ -olefin copolymer may for example be in the range from 0.001 to 10 dg/min (measured according to ISO1133 (2.16 kg/230° C.)), preferably in the range from 0.006 to 5 dg/min.
• the dispersed ethylene- ⁇ -olefin copolymer is present in an amount of 40 to 5 wt %, for example in an amount of 35 to 15 wt % based on the total heterophasic propylene copolymer, for example in an amount of at least 20 wt % and/or for example in an amount of at most 30 wt % based on the total heterophasic propylene copolymer.
• the amount of ethylene in the ethylene- ⁇ -olefin copolymer is in the range of 20-65 wt %, for example in the range of 40 to 60 wt % based on the ethylene- ⁇ -olefin copolymer, for example the amount of ethylene in the ethylene- ⁇ -olefin copolymer is at least 30 wt % and/or for example at most 55 wt % based on the ethylene- ⁇ -olefin copolymer.
• the sum of the total weight of the propylene-based matrix and the total weight of the dispersed ethylene- ⁇ -olefin copolymer is 100 wt %
• the ⁇ -olefin in the ethylene- ⁇ -olefin copolymer is preferably chosen from the group of ⁇ -olefins having 3 to 8 carbon atoms and any mixtures thereof, preferably the ⁇ -olefin in the ethylene- ⁇ -olefin copolymer is chosen from the group of ⁇ -olefins having 3 to 4 carbon atoms and any mixture thereof, more preferably the ⁇ -olefin is propylene, in which case the ethylene- ⁇ -olefin copolymer is ethylene-propylene copolymer.
• Suitable ⁇ -olefins having 3 to 8 carbon atoms which may be employed as ethylene comonomers to form the ethylene ⁇ -olefins copolymer include but are not limited to propylene, 1-butene, 1-pentene, 4-methyl-1-pentene, 1-hexen, 1-heptene and 1-octene.
• the process of the invention comprises the steps of
• a propylene copolymer is melt-mixed with a talc to obtain a masterbatch. Melt-mixing may be performed by methods known to the skilled person, for example using an extruder and the conditions as described herein for step b).
• the propylene copolymer may be any propylene copolymer, for example a propylene- ⁇ -olefin copolymer, wherein the ⁇ -olefin is selected from the group of ⁇ -olefins having 2 or 4-10 C-atoms and wherein the ⁇ -olefin content is up to 10 wt % based on the propylene copolymer; or the propylene copolymer may be a random propylene-ethylene copolymer, for example wherein the ethylene content is up to 10 wt % based on the propylene copolymer; or the propylene copolymer may be a propylene homopolymer; or the propylene copolymer may be a heterophasic propylene copolymer.
• a propylene- ⁇ -olefin copolymer wherein the ⁇ -olefin is selected from the group of ⁇ -olefins having 2 or 4-10 C-atoms
• the propylene copolymer is a heterophasic propylene copolymer, more preferably the propylene copolymer is the same heterophasic propylene copolymer as used in step b) of the process of the invention.
• the invention relates to a process according to the invention comprising the steps of
• step b melt-mixing the masterbatch with the same heterophasic propylene copolymer (as used in step a)) and a peroxide to obtain the composition comprising the heterophasic propylene copolymer and talc.
• the weight ratio of the talc to the propylene copolymer in the masterbatch is in principle not critical and may be varied between wide ranges. In principle, the weight ratio of talc to the propylene copolymer is not critical. Preferably, the weight ratio of talc to propylene copolymer in the masterbatch is from 1:9 to 9:1, more preferably from 1:3 to 9:1, for example from 1:1 to 9:1. High weight ratios of talc to propylene copolymer in the masterbatch are preferred as this decreases the volume of the masterbatch needed. A high volume of masterbatch is undesired as this makes it impractical for dosing to the heterophasic propylene copolymer.
• the weight ratio of the propylene copolymer used in step a), preferably a heterophasic propylene copolymer, to the heterophasic propylene copolymer used in step b), preferably the same heterophasic propylene copolymer (as used in step a) is 1:1 to 1:20, for example from 1:5 to 1:20 or 1:5 to 1:15 or 1:5 to 1:10.
• the masterbatch may contain the propylene copolymer and the talc only, but may also comprise additives and/or polar substances suitable for surface-modification of the talc, for example as described herein, for example ethylene-bis-stearamide.
• melt-mixing is meant that the masterbatch, the heterophasic propylene copolymer and the peroxide are mixed at a temperature that exceeds the melting point of the heterophasic propylene copolymer and the propylene copolymer in the masterbatch.
• Melt-mixing may be done using techniques known to the skilled person, for example in an extruder. Generally, in the process of the invention, melt-mixing is performed at a temperature in the range from 20-300° C.
• melt-mixing of step a) of the process of the invention may be performed at a temperature in the range from 20-300° C.
• melt-mixing of step b) of the process of the invention may be performed at a temperature in the range from 20-330° C.
• Suitable conditions for melt-mixing such as temperature, pressure, amount of shear, screw speed and screw design when an extruder is used are known to the skilled person.
• a conventional extruder such as a twin-screw extruder may be used.
• the temperature can vary through the different zones of the extruder as required.
• the temperature may vary from 180° C. in the feed zone to 300° C. at the die.
• the temperature in the extruder varies from 200 to 265° C.; lower temperatures may impede reactions between the peroxide and an optional co-agent, for example polyfunctional monomers, such as BDDMA and, as a consequence, compositions with the desired melt flow index may not be obtained; too high temperatures may induce undesired degradation processes, which may for example result in compositions having poor mechanical properties.
• the screw speed of the extruder may be varied as needed. Typical screw speed are in the range from about 100 rpm to about 400 rpm.
• the residence time in the extruder for the heterophasic propylene copolymer may be lower than 1 minute, for example between 10 and 40 seconds.
• Talc is a relatively abundant, inexpensive, highly hydrophobic and generally unreactive mineral. It can be categorized as a hydrated magnesium silicate and its main components can be represented by, inter alia, one or more of the formulas (Si 2 O 5 ) 2 Mg 3 (OH) 2 , Si 8 Mg 6 O 20 (OH) 4 or Mg 12 Si 16 O 40 (OH) 8 .
• Talcs suitable for use as additives to a heterophasic propylene copolymer are commercially available from for example Imerys Luzenac. ‘Talc’ and ‘talcum’ are used interchangeably herein.
• Talc is available in several particle sizes, for example the particle sizes of talc are classified as ‘ultrafine’ (average particle size of lower than 1 ⁇ m, for example an average particle size in the range of 0.5 to 0.91 ⁇ m) and ‘fine’ (average particle size of at least 1 ⁇ m, for example an average particle size of 1 ⁇ m to 5 ⁇ m).
• ‘ultrafine’ average particle size of lower than 1 ⁇ m, for example an average particle size in the range of 0.5 to 0.91 ⁇ m
• fine average particle size of at least 1 ⁇ m, for example an average particle size of 1 ⁇ m to 5 ⁇ m.
• fine or ultrafine powder particles are used in the process of the present invention.
• the amount of talc used may be varied.
• the amount of surface-modified talc in the composition of the invention is preferably from 0.5 to 5 wt % based on the total amount of propylene copolymer of step a) and the heterophasic propylene copolymer of step b).
• the amount of surface-modified talc in the composition is at least 1 wt %, for example at least 1.5 wt % and/or for example at most 4 wt %, for example at most 3.5 wt %, for example at most 3 wt % based on the propylene copolymer of step a) and the heterophasic propylene copolymer of step b).
• the composition that is prepared by the process of the invention has a melt flow index in the range of 1 to 200 dg/min as measured according to ISO1133 (2.16 kg/230° C.).
• the melt flow index is at least 1, for example at least 5 or for example at least 14 dg/min and/or for example at most 200 dg/min, for example at most 80 dg/min or for example at least 20 dg/min as measured according to ISO1133 (2.16 kg/230° C.).
• the melt flow index of the composition that is prepared by the process of the invention is in the range from 5 to 80 dg/min, for example in the range from 14 to 20 dg/min as measured according to ISO1133 (2.16 kg/230° C.).
• Suitable peroxides include organic peroxides having a decomposition half-life of less than 1 minute at the average process temperature during the melt-mixing of the heterophasic propylene copolymer with the talc and the peroxide.
• Suitable organic peroxides include but are not limited to dialkyl peroxides, e.g. dicumyl peroxides, peroxyketals, peroxycarbonates, diacyl peroxides, peroxyesters and peroxydicarbonates.
• a dialkyl peroxides is employed in the process according to the present invention. More preferably, the peroxide is ⁇ , ⁇ ′-bis-(tert-butylperoxy)diisopropylbenzene, 2,5-dimethyl-2,5-di(tert-butylperoxy)-hexane or 3,6,9-Triethyl-3,6,9-trimethyl-1,4,7-triperoxonane.
• the peroxide is selected from the group of non-aromatic peroxides.
• the amount of peroxide used will lie in the range of 0.02 to 0.5 wt % based on the heterophasic propylene copolymer.
• At least part of the talc may be surface-modified, that means that mixtures of surface-modified talc with non-surface modified talc may also be used.
• at least 80 wt % of the talc used in the process of the invention or present in the composition of the invention is surface-modified, more preferably at least 90 wt %, even more preferably at least 95 wt %, in particular at least 98 wt %, more in particular at least 99 wt %, most in particular all talc used in the process of the invention or present in the composition of the invention is surface-modified.
• surface-modified talc are surface-treated talc, coated talc.
• Surface-modified talcs are known to the person skilled in the art and are commercially available from for example Imerys Luzenac.
• Surface-modified talcs may be prepared by adding a surface modifier to the talc. The nature and concentration of the modifier depends on the desired benefit in the final talc composite, like improvement of the bond between the talcum and polymer or to improve the dispersion of the talc in the polymer.
• surface modifiers are silanes, amines, glycols, stearates, sorbates and titanates.
• the surface-modified talc is a talc that is surface-modified with a polar substance selected from the group of glycols, silanes and amines
• the invention relates to a process of the invention, wherein the surface-modified talc is prepared by mixing of a talc with a polar substance, preferably ethylene-bis-stearamide. This may be done off-line (i.e. prior to melt-mixing the talc and the propylene copolymer) or the surface-modified talc may be prepared in situ (i.e. by adding the polar substance together with the talc in the melt-mixing step).
• a polar substance preferably ethylene-bis-stearamide
• the talc can be ‘coated’ in situ.
• polar substances examples are as described herein.
• the mixing of talc is done with ethylene-bis-stearamide (also referred to as EBS or EBA).
• EBS ethylene-bis-stearamide
• the invention relates to a composition obtained or obtainable by the process of the invention.
• the invention relates to a composition
• a composition comprising a heterophasic propylene copolymer, a propylene copolymer and talc, wherein the heterophasic propylene copolymer consists of
• a propylene-based matrix wherein the propylene-based matrix consists of a propylene homopolymer and/or a propylene- ⁇ -olefin copolymer consisting of at least 70% by mass of propylene and up to 30% by mass of ⁇ -olefin, for example ethylene, based on the total mass of the propylene-based matrix, wherein the propylene-based matrix is present in an amount of 60 to 95 wt % based on the total heterophasic propylene copolymer, and
• a dispersed ethylene- ⁇ -olefin copolymer wherein the dispersed ethylene- ⁇ -olefin copolymer is present in an amount of 40 to 5 wt % based on the total heterophasic propylene copolymer and wherein the sum of the total amount of propylene-based matrix and total amount of the dispersed ethylene- ⁇ -olefin copolymer in the heterophasic propylene copolymer is 100 wt %
• composition has a desired melt flow index in the range of 1 to 200 dg/min as measured according to ISO1133 (2.16 kg/230° C.), and
• the amount of volatile organic compounds as measured through the VOC-value according to VDA278 (30 min, 180° C.) and determined by gas chromatography is less than 1500 ppm based on the total composition.
• the amount of volatile organic compounds (VOC-value) as measured through the VOC-value according to VDA278 (30 min, 180° C.) and determined by gas chromatography (version October 2011) is less than 1300 ppm, more preferably less than 1000 ppm, for example less than 750 ppm, for example less than 600 ppm, for example less than 500 ppm, for example less than 400 ppm, for example less than 300 ppm based on the total composition
• the invention relates to a composition
• a composition comprising a heterophasic propylene copolymer, a propylene copolymer and talc, wherein the heterophasic propylene copolymer consists of
• a propylene-based matrix wherein the propylene-based matrix consists of a propylene homopolymer and/or a propylene- ⁇ -olefin copolymer consisting of at least 70% by mass of propylene and up to 30% by mass of ⁇ -olefin, for example ethylene, based on the total mass of the propylene-based matrix, and wherein the propylene-based matrix is present in an amount of 60 to 95 wt % based on the total heterophasic propylene copolymer, and
• a dispersed ethylene- ⁇ -olefin copolymer wherein the dispersed ethylene- ⁇ -olefin copolymer is present in an amount of 40 to 5 wt % based on the total heterophasic propylene copolymer and wherein the sum of the total amount of propylene-based matrix and total amount of the dispersed ethylene- ⁇ -olefin copolymer in the heterophasic propylene copolymer is 100 wt %, wherein the composition has a desired melt flow index in the range of 1 to 200 dg/min as measured according to ISO1133 (2.16 kg/230° C.), wherein the amount of volatile compounds (FOG-value) as measured through the FOG-value according to VDA278 on the second heating (first heating 30 min at 90° C., second heating 1 hour at 120° C.) is less than 500 ppm, for example less than 400 ppm, for example less than 350 ppm, for example less than 300 ppm
• the invention in another aspect, relates to a composition
• a composition comprising a heterophasic propylene copolymer, a propylene copolymer and talc, wherein the heterophasic propylene copolymer consists of
• a propylene-based matrix wherein the propylene-based matrix consists of a propylene homopolymer and/or a propylene- ⁇ -olefin copolymer consisting of at least 70% by mass of propylene and up to 30% by mass of ⁇ -olefin, for example ethylene, based on the total mass of the propylene-based matrix, wherein the propylene-based matrix is present in an amount of 60 to 95 wt % based on the total heterophasic propylene copolymer, and
• a dispersed ethylene- ⁇ -olefin copolymer wherein the dispersed ethylene- ⁇ -olefin copolymer is present in an amount of 40 to 5 wt % based on the total heterophasic propylene copolymer and wherein the sum of the total amount of propylene-based matrix and total amount of the dispersed ethylene- ⁇ -olefin copolymer in the heterophasic propylene copolymer is 100 wt %, wherein the composition has a desired melt flow index in the range of 1 to 200 dg/min as measured according to ISO1133 (2.16 kg/230° C.), wherein the amount of butanol emitted as measured using VDA 278 (10 min, 180° C.) as determined with gas chromatography-mass spectrometry (GC-MS) is less than 100 ppm, for example less than 80 ppm, for example less than 70 ppm, for example less than 60 ppm, for example less than 50
• Such composition having an amount of butanol of less than 100 ppm, preferably less than 80 ppm, more preferably less than 60 ppm, most preferably less than 40 ppm based on the total composition is especially suitable for use in food contact applications.
• the invention also relates to the use of a composition comprising a heterophasic propylene copolymer, a propylene copolymer and talc, wherein the heterophasic propylene copolymer consists of
• a propylene-based matrix wherein the propylene-based matrix consists of a propylene homopolymer and/or a propylene- ⁇ -olefin copolymer consisting of at least 70% by mass of propylene and up to 30% by mass of ⁇ -olefin, for example ethylene, based on the total mass of the propylene-based matrix, wherein the propylene-based matrix is present in an amount of 60 to 95 wt % based on the total heterophasic propylene copolymer, and
• a dispersed ethylene- ⁇ -olefin copolymer wherein the dispersed ethylene- ⁇ -olefin copolymer is present in an amount of 40 to 5 wt % based on the total heterophasic propylene copolymer and wherein the sum of the total amount of propylene-based matrix and total amount of the dispersed ethylene- ⁇ -olefin copolymer in the heterophasic propylene copolymer is 100 wt %, wherein the composition has a desired melt flow index in the range of 1 to 200 dg/min as measured according to ISO1133 (2.16 kg/230° C.), wherein the amount of butanol emitted as measured using VDA 278 (10 min, 180° C.) as determined with gas chromatography-mass spectrometry (GC-MS) is less than 100 ppm, for example less than 80 ppm, for example less than 70 ppm, for example less than 60 ppm, for example less than 50
• the invention in another aspect, relates to a composition
• a composition comprising a heterophasic propylene copolymer, a propylene copolymer and talc, wherein the heterophasic propylene copolymer consists of
• a propylene-based matrix wherein the propylene-based matrix consists of a propylene homopolymer and/or a propylene- ⁇ -olefin copolymer consisting of at least 70% by mass of propylene and up to 30% by mass of ⁇ -olefin, for example ethylene, based on the total mass of the propylene-based matrix, wherein the propylene-based matrix is present in an amount of 60 to 95 wt % based on the total heterophasic propylene copolymer, and
• a dispersed ethylene- ⁇ -olefin copolymer wherein the dispersed ethylene- ⁇ -olefin copolymer is present in an amount of 40 to 5 wt % based on the total heterophasic propylene copolymer and wherein the sum of the total amount of propylene-based matrix and total amount of the dispersed ethylene- ⁇ -olefin copolymer in the heterophasic propylene copolymer is 100 wt %, wherein the composition has a desired melt flow index in the range of 1 to 200 dg/min as measured according to ISO1133 (2.16 kg/230° C.), wherein the amount of acetone emitted as measured using VDA 278 (10 min, 180° C.) as determined with gas chromatography-mass spectrometry (GC-MS) is less than 4 ppm, for example less than 3 ppm, for example less than 2 ppm, for example less than 1 ppm.
• GC-MS gas chromat
• the invention in another aspect, relates to a composition
• a composition comprising a heterophasic propylene copolymer, a propylene copolymer and talc, wherein the heterophasic propylene copolymer consists of
• a propylene-based matrix wherein the propylene-based matrix consists of a propylene homopolymer and/or a propylene- ⁇ -olefin copolymer consisting of at least 70% by mass of propylene and up to 30% by mass of ⁇ -olefin, for example ethylene, based on the total mass of the propylene-based matrix, wherein the propylene-based matrix is present in an amount of 60 to 95 wt % based on the total heterophasic propylene copolymer, and
• a dispersed ethylene- ⁇ -olefin copolymer wherein the dispersed ethylene- ⁇ -olefin copolymer is present in an amount of 40 to 5 wt % based on the total heterophasic propylene copolymer and wherein the sum of the total amount of propylene-based matrix and total amount of the dispersed ethylene- ⁇ -olefin copolymer in the heterophasic propylene copolymer is 100 wt %, wherein the composition has a desired melt flow index in the range of 1 to 200 dg/min as measured according to ISO1133 (2.16 kg/230° C.), wherein the amount of isopropenylacetylbenzene as measured using VDA278 (10 min, 180° C.) as determined with gas chromatography-mass spectrometry (GC-MS) is less than 20, for example less than 15, for example less than 10 ppm based on the total composition, and/or wherein the amount of diacet
• the invention also relates a composition
• a composition comprising a heterophasic propylene copolymer, a propylene copolymer and talc, wherein the heterophasic propylene copolymer consists of
• a propylene-based matrix wherein the propylene-based matrix consists of a propylene homopolymer and/or a propylene- ⁇ -olefin copolymer consisting of at least 70% by mass of propylene and up to 30% by mass of ⁇ -olefin, for example ethylene, based on the total mass of the propylene-based matrix, wherein the propylene-based matrix is present in an amount of 60 to 95 wt % based on the total heterophasic propylene copolymer, and
• a dispersed ethylene- ⁇ -olefin copolymer wherein the dispersed ethylene- ⁇ -olefin copolymer is present in an amount of 40 to 5 wt % based on the total heterophasic propylene copolymer and wherein the sum of the total amount of propylene-based matrix and total amount of the dispersed ethylene- ⁇ -olefin copolymer in the heterophasic propylene copolymer is 100 wt %, wherein the composition has a desired melt flow index in the range of 1 to 200 dg/min as measured according to ISO1133 (2.16 kg/230° C.), and
• the amount of volatile organic compounds as measured through the VOC-value according to VDA278 (30 min, 180° C.) and determined by gas chromatography is less than 1500 ppm, preferably less than 1300 ppm, more preferably less than 1000 ppm, for example less than 750 ppm, for example less than 600 ppm, for example less than 500 ppm, for example less than 400 ppm, for example less than 300 ppm based on the total composition, and/or wherein the amount of volatile compounds (FOG-value) as measured through the FOG-value according to VDA278 on the second heating (first heating 30 min at 90° C., second heating 1 hour at 120° C.) is less than 500 ppm, for example less than 400 ppm, for example less than 350 ppm, for example less than 300 ppm, for example less than 250 ppm, for example less than 200 ppm, for example less than 150 ppm, and/or wherein the amount of butanol emitted as measured using VDA 2
• the amount of acetone emitted as measured using VDA 278 (10 min, 180° C.) as determined with gas chromatography-mass spectrometry (GC-MS) is less than 4 ppm, for example less than 3 ppm, for example less than 2 ppm, for example less than 1 ppm, and/or wherein the amount of isopropenylacetylbenzene as measured using VDA278 (10 min, 180° C.) as determined with gas chromatography-mass spectrometry (GC-MS) is less than 20, for example less than 15, for example less than 10 ppm based on the total composition, and/or wherein the amount of diacetyl benzene as measured using VDA278 (10 min, 180° C.) as determined with gas chromatography-mass spectrometry (GC-MS) is less than 90, for example less than 80, for example less than 30, for example less than 25 ppm, preferably wherein the amount of isopropenylacetylbenzen
• the invention relates to a composition obtained or obtainable by the process of the invention
• the amount of volatile organic compounds as measured through the VOC-value according to VDA278 (30 min, 180° C.) and determined by gas chromatography is less than 1500 ppm, preferably less than 1300 ppm, more preferably less than 1000 ppm, for example less than 750 ppm, for example less than 600 ppm, for example less than 500 ppm, for example less than 400 ppm, for example less than 300 ppm based on the total composition, and/or
• the amount of volatile compounds (FOG-value) as measured through the FOG-value according to VDA278 on the second heating is less than 500 ppm, for example less than 400 ppm, for example less than 350 ppm, for example less than 300 ppm, for example less than 250 ppm, for example less than 200 ppm, for example less than 150 ppm, and/or
• the amount of butanol emitted as measured using VDA 278 (10 min, 180° C.) as determined with gas chromatography-mass spectrometry (GC-MS) is less than 100 ppm, for example less than 80 ppm, for example less than 70 ppm, for example less than 60 ppm, for example less than 50 ppm, for example less than 40 ppm, for example less than 30 ppm, and/or
• the amount of acetone emitted as measured using VDA 278 (10 min, 180° C.) as determined with gas chromatography-mass spectrometry (GC-MS) is less than 4 ppm, for example less than 3 ppm, for example less than 2 ppm, for example less than 1 ppm and/or wherein the amount of isopropenylacetylbenzene as measured using VDA278 (10 min, 180° C.) as determined with gas chromatography-mass spectrometry (GC-MS) is less than 20, for example less than 15, for example less than 10 ppm based on the total composition, and/or
• the amount of diacetyl benzene as measured using VDA278 (10 min, 180° C.) as determined with gas chromatography-mass spectrometry (GC-MS) is less than 30, for example less than 25 ppm, preferably
• the amount of isopropenylacetylbenzene as measured using VDA278 (10 min, 180° C.) as determined with gas chromatography-mass spectrometry (GC-MS) is less than 20, for example less than 15, for example less than 10 ppm based on the total composition and/or wherein the amount of diacetyl benzene as measured using VDA278 (10 min, 180° C.) as determined with gas chromatography-mass spectrometry (GC-MS) is less than 90, for example less than 80, for example less than 30, for example less than 25 ppm.
• the VOC-value, the FOG-value, the amount of butanol emitted, the amount of acetone emitted and the amount of isopropenylacetylbenzene and the amount of diacetyl benzene are measured on a sample taken within 1 hour after it was prepared by melt-mixing and stored in airtight bags for no longer than 24 hours at a maximum of 23° C.
• compositions of the invention may further comprise additives
• the compositions may further contain nucleating agents, clarifiers, stabilizers, release agents, pigments, dyes, plasticizers, anti-oxidants, antistatics, scratch resistance agents, high performance fillers, impact modifiers, flame retardants, blowing agents, recycling additives, coupling agents, anti microbials, anti-fogging additives, slip additives, anti-blocking additives, polymer processing aids such as lubricants and the like, etc., surface tension modifiers, co-agents, for example 1,4-butanediol dimethacrylate (BDDMA), acrylate or methacrylate; components that enhance interfacial bonding between the polymer and the talc, for example maleated polypropylene etc.
• BDDMA 1,4-butanediol dimethacrylate
• acrylate or methacrylate for example maleated polypropylene etc.
• additives are well known in the art. The skilled person can readily select any suitable combination of additives and additive amounts without undue experimentation.
• the amount of additives depends on their type and function. Typically, their amounts will be from 0 to 30 wt %, for example from 0 to 20 wt %, for example from 0 to 10 wt % or from 0 to 5 wt % based on the total composition.
• composition comprising a heterophasic propylene copolymer and talc should add up to 100% by weight.
• the components may be pre-mixed with the polypropylene copolymer, prior to melt-mixing the heterophasic polypropylene with the talc or they may be added to the melt-mixing step a).
• the components may be added in any order and by any conventional means, for example at the same or different sites of the extruder.
• the invention relates to the use of the compositions of the invention in injection moulding, blow moulding, extrusion moulding, compression moulding, thin-walled injection moulding, etc, for example in food contact applications.
• the invention relates to a shaped article comprising the composition of the invention.
• composition of the invention may be transformed into shaped (semi)-finished articles using a variety of processing techniques.
• suitable processing techniques include injection moulding, injection compression moulding, thin wall injection moulding, extrusion, and extrusion compression moulding.
• Injection moulding is widely used to produce articles such as for example caps and closures, batteries, pails, containers, automotive exterior parts like bumpers, automotive interior parts like instrument panels, or automotive parts under the bonnet.
• Extrusion is for example widely used to produce articles, such as rods, sheets, films and pipes.
• Thin wall injection moulding may for example be used to make thin wall packaging.
• the shaped article of the invention also has the advantage of low VOC-value and/or a low FOG-value and/or a low amount of acetone and/or a low amount of butanol and/or a low amount of isopropenylacetylbenzene and/or a low amount of diacetylbenzene.
• VOC emission was measured according to VDA278 (version October 2011; 180° C., 30 min) on the granulated compounds.
• the FOG emission was measured according to VDA278 (version October 2011; first heating 90° C., 30 min, second heating 1 hour at 120° C.).
• the amount of isopropenylacetylbenzene was measured using VDA278 (10 min at 180° C.) and determined with GC-MS.
• the amount of diacetylbenzene was measured using VDA278 (10 min at 180° C.) and determined with GC-MS.
• stiffness is determined by measuring the flexural modulus according to ASTM D790-10. Flexural modulus was determined on 3.2 mm thick specimens according to ISO37/2, parallel orientation.
• impact strength is determined by measuring the Izod impact strength at 23° C. according to ISO 180 4A, Test geometry: 65*12.7*3.2 mm, notch 45° according to ISO 37/2 perpendicular orientation.
• melt flow rate also called melt flow index or melt index according to ISO1133 (2.16 kg/230° C.).
• This material is a propylene heterophasic copolymer having a propylene polymer matrix wherein the propylene-based matrix (in this case a propylene homopolymer) is present in an amount of 75 wt % based on the total heterophasic propylene copolymer and 25 wt % of an ethylene-propylene copolymer consisting of 55 wt % of ethylene.
• MFI melt flow index
• Talcum masterbatch was prepared by dosing Steamic T1CF talc (uncoated talc) or Steamic T1DF talc (coated talc) (3.4 kg) via a separate feeder in a 1:1 weight ratio with part of the heterophasic propylene copolymer (3.7 kg) and the stabilizer Irganox B225 (0.5 wt %). Steamic T1CF and Steamic T1DF were provided by Imerys Luzenac. Two talcum masterbatches were prepared: one with 0.3 wt % ethylene-bis-stearamide (EBA) and one without ethylene-bis-stearamide.
• EBA ethylene-bis-stearamide
• the talcum masterbatch was dosed to the extruder via a separate feeder to the mixture described above.
• the remaining heterophasic propylene copolymer (3.3 kg) was extruded in a twin screw ZE21 extruder with one of the talcum masterbatches or with Steamic T1CF talc and the additive mixture containing the peroxide (Luperco 802PP40, which is di(tert-butylperoxyisopropylbenzene, obtained from Imerys Luzenac).
• the amount and composition of the additive mixture was chosen such that the amount of calcium stearate in the final composition was 500 ppm (based on the total composition) and the amount of Irganox B225 was 5000 ppm (based on the total composition).
• the peroxide concentration in the additive mixture was adjusted to control the melt flow index of the finished material to the desired value.
• the amount of talc in the talcum masterbatch was chosen such that the amount of talc in the finished material was 0; 2.5 or 5 wt % based on the total composition.
• a typical temperature profile in the extruder is 20-20-40-100-170-230-240-240-240° C., at a throughput of 2.5 kg/h at 300 rpm.
• sample compositions differed on the way the talcum was introduced into the composition (via masterbatch or directly in the extruder).
• the talcum used was Steamic T1CF (uncoated), introduced via a masterbatch.
• the talcum used was Steamic T1 CF (uncoated, introduced via a masterbatch containing 0.3 wt % EBA.
• the talcum used was Steamic T1CF, which was introduced directly into the extruder.
• the talc concentration in the compositions was varied and the peroxide concentration in the powder/additive mixture was adjusted to control the melt flow index to 18 dg/min.
• Table 1 shows the amount of peroxide that is needed to obtain a melt flow index as determined as described herein of 18 dg/min.
• the amount of peroxide that is needed to shift the MFI of Sabic® PP PHC27 to 18 dg/min is considerably higher for comparative sample A, than for the compositions of the invention (which add talc in the form of a masterbatch to the heterophasic propylene copolymer in the extruder instead of directly to the heterophasic propylene copolymer in the extruder).
• the talc is coated in situ, that is preferably EBA is mixed with the talc in the masterbatch, prior to extrusion of the masterbatch with the heterophasic propylene copolymer.
• the amount of peroxide degradation products in the compositions of the invention is considerably lower than in the composition of comparative sample A. Furthermore, in situ coating of the talc in the masterbatch by mixing in EBA further reduces the amount of peroxide degradation products in the compositions of the invention. This has the advantage for organoleptic performance, lower emission levels and less safety issues.

Landscapes

• Chemical & Material Sciences (AREA)
• Health & Medical Sciences (AREA)
• Chemical Kinetics & Catalysis (AREA)
• Medicinal Chemistry (AREA)
• Polymers & Plastics (AREA)
• Organic Chemistry (AREA)
• Engineering & Computer Science (AREA)
• Mechanical Engineering (AREA)
• Manufacturing & Machinery (AREA)
• Compositions Of Macromolecular Compounds (AREA)
• Processes Of Treating Macromolecular Substances (AREA)

Applications Claiming Priority (5)

Publications (1)

Family

ID=49182274

Family Applications (3)

Family Applications After (2)

Country Status (9)

Cited By (4)

Families Citing this family (29)

Citations (5)

Family Cites Families (30)

• 2013
  • 2013-09-17 EP EP13762852.5A patent/EP2898014B1/en active Active
  • 2013-09-17 ES ES13765992.6T patent/ES2625403T3/es active Active
  • 2013-09-17 CN CN201380055400.6A patent/CN104736630B/zh active Active
  • 2013-09-17 BR BR112015005922-8A patent/BR112015005922B1/pt active IP Right Grant
  • 2013-09-17 US US14/429,217 patent/US20150232652A1/en not_active Abandoned
  • 2013-09-17 CN CN201380055375.1A patent/CN104755551A/zh active Pending
  • 2013-09-17 WO PCT/EP2013/069295 patent/WO2014044682A1/en active Application Filing
  • 2013-09-17 EP EP13765992.6A patent/EP2898016B1/en active Active
  • 2013-09-17 US US14/429,207 patent/US10072139B2/en active Active
  • 2013-09-17 ES ES13762852.5T patent/ES2623204T3/es active Active
  • 2013-09-17 BR BR112015005850-7A patent/BR112015005850B1/pt active IP Right Grant
  • 2013-09-17 KR KR1020157009893A patent/KR102088379B1/ko active IP Right Grant
  • 2013-09-17 EA EA201500331A patent/EA026860B9/ru not_active IP Right Cessation
  • 2013-09-17 US US14/428,992 patent/US9527989B2/en active Active
  • 2013-09-17 KR KR1020157009894A patent/KR102093395B1/ko active IP Right Grant
  • 2013-09-17 EA EA201500330A patent/EA027608B1/ru not_active IP Right Cessation
  • 2013-09-17 CN CN201380054813.2A patent/CN104736628B/zh active Active
  • 2013-09-17 KR KR1020157009895A patent/KR102093399B1/ko active IP Right Grant
  • 2013-09-17 CN CN201910658457.4A patent/CN110408123A/zh active Pending
  • 2013-09-17 ES ES13763069.5T patent/ES2614950T3/es active Active
  • 2013-09-17 WO PCT/EP2013/069292 patent/WO2014044680A1/en active Application Filing
  • 2013-09-17 EP EP13763069.5A patent/EP2898015B1/en active Active
  • 2013-09-17 IN IN3141DEN2015 patent/IN2015DN03141A/en unknown
  • 2013-09-17 EA EA201500329A patent/EA029083B1/ru not_active IP Right Cessation
  • 2013-09-17 WO PCT/EP2013/069296 patent/WO2014044683A1/en active Application Filing
  • 2013-09-17 BR BR112015005950-3A patent/BR112015005950B1/pt active IP Right Grant

Patent Citations (5)

Non-Patent Citations (2)

Also Published As

Similar Documents

Legal Events