US20100025255A1 - Electroplating method for magnesium and magnesium alloy - Google Patents
Electroplating method for magnesium and magnesium alloy Download PDFInfo
- Publication number
- US20100025255A1 US20100025255A1 US12/498,455 US49845509A US2010025255A1 US 20100025255 A1 US20100025255 A1 US 20100025255A1 US 49845509 A US49845509 A US 49845509A US 2010025255 A1 US2010025255 A1 US 2010025255A1
- Authority
- US
- United States
- Prior art keywords
- substrate
- electroplating
- mass concentration
- coating
- magnesium
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Links
Images
Classifications
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C18/00—Chemical coating by decomposition of either liquid compounds or solutions of the coating forming compounds, without leaving reaction products of surface material in the coating; Contact plating
- C23C18/16—Chemical coating by decomposition of either liquid compounds or solutions of the coating forming compounds, without leaving reaction products of surface material in the coating; Contact plating by reduction or substitution, e.g. electroless plating
- C23C18/31—Coating with metals
- C23C18/32—Coating with nickel, cobalt or mixtures thereof with phosphorus or boron
- C23C18/34—Coating with nickel, cobalt or mixtures thereof with phosphorus or boron using reducing agents
- C23C18/36—Coating with nickel, cobalt or mixtures thereof with phosphorus or boron using reducing agents using hypophosphites
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C18/00—Chemical coating by decomposition of either liquid compounds or solutions of the coating forming compounds, without leaving reaction products of surface material in the coating; Contact plating
- C23C18/16—Chemical coating by decomposition of either liquid compounds or solutions of the coating forming compounds, without leaving reaction products of surface material in the coating; Contact plating by reduction or substitution, e.g. electroless plating
- C23C18/1601—Process or apparatus
- C23C18/1633—Process of electroless plating
- C23C18/1646—Characteristics of the product obtained
- C23C18/165—Multilayered product
- C23C18/1653—Two or more layers with at least one layer obtained by electroless plating and one layer obtained by electroplating
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C18/00—Chemical coating by decomposition of either liquid compounds or solutions of the coating forming compounds, without leaving reaction products of surface material in the coating; Contact plating
- C23C18/16—Chemical coating by decomposition of either liquid compounds or solutions of the coating forming compounds, without leaving reaction products of surface material in the coating; Contact plating by reduction or substitution, e.g. electroless plating
- C23C18/18—Pretreatment of the material to be coated
- C23C18/1803—Pretreatment of the material to be coated of metallic material surfaces or of a non-specific material surfaces
- C23C18/1824—Pretreatment of the material to be coated of metallic material surfaces or of a non-specific material surfaces by chemical pretreatment
- C23C18/1837—Multistep pretreatment
- C23C18/1844—Multistep pretreatment with use of organic or inorganic compounds other than metals, first
-
- C—CHEMISTRY; METALLURGY
- C25—ELECTROLYTIC OR ELECTROPHORETIC PROCESSES; APPARATUS THEREFOR
- C25D—PROCESSES FOR THE ELECTROLYTIC OR ELECTROPHORETIC PRODUCTION OF COATINGS; ELECTROFORMING; APPARATUS THEREFOR
- C25D3/00—Electroplating: Baths therefor
- C25D3/02—Electroplating: Baths therefor from solutions
- C25D3/04—Electroplating: Baths therefor from solutions of chromium
- C25D3/06—Electroplating: Baths therefor from solutions of chromium from solutions of trivalent chromium
-
- C—CHEMISTRY; METALLURGY
- C25—ELECTROLYTIC OR ELECTROPHORETIC PROCESSES; APPARATUS THEREFOR
- C25D—PROCESSES FOR THE ELECTROLYTIC OR ELECTROPHORETIC PRODUCTION OF COATINGS; ELECTROFORMING; APPARATUS THEREFOR
- C25D3/00—Electroplating: Baths therefor
- C25D3/02—Electroplating: Baths therefor from solutions
- C25D3/12—Electroplating: Baths therefor from solutions of nickel or cobalt
-
- C—CHEMISTRY; METALLURGY
- C25—ELECTROLYTIC OR ELECTROPHORETIC PROCESSES; APPARATUS THEREFOR
- C25D—PROCESSES FOR THE ELECTROLYTIC OR ELECTROPHORETIC PRODUCTION OF COATINGS; ELECTROFORMING; APPARATUS THEREFOR
- C25D3/00—Electroplating: Baths therefor
- C25D3/02—Electroplating: Baths therefor from solutions
- C25D3/38—Electroplating: Baths therefor from solutions of copper
-
- C—CHEMISTRY; METALLURGY
- C25—ELECTROLYTIC OR ELECTROPHORETIC PROCESSES; APPARATUS THEREFOR
- C25D—PROCESSES FOR THE ELECTROLYTIC OR ELECTROPHORETIC PRODUCTION OF COATINGS; ELECTROFORMING; APPARATUS THEREFOR
- C25D5/00—Electroplating characterised by the process; Pretreatment or after-treatment of workpieces
- C25D5/10—Electroplating with more than one layer of the same or of different metals
- C25D5/12—Electroplating with more than one layer of the same or of different metals at least one layer being of nickel or chromium
- C25D5/14—Electroplating with more than one layer of the same or of different metals at least one layer being of nickel or chromium two or more layers being of nickel or chromium, e.g. duplex or triplex layers
-
- C—CHEMISTRY; METALLURGY
- C25—ELECTROLYTIC OR ELECTROPHORETIC PROCESSES; APPARATUS THEREFOR
- C25D—PROCESSES FOR THE ELECTROLYTIC OR ELECTROPHORETIC PRODUCTION OF COATINGS; ELECTROFORMING; APPARATUS THEREFOR
- C25D5/00—Electroplating characterised by the process; Pretreatment or after-treatment of workpieces
- C25D5/34—Pretreatment of metallic surfaces to be electroplated
- C25D5/42—Pretreatment of metallic surfaces to be electroplated of light metals
-
- C—CHEMISTRY; METALLURGY
- C25—ELECTROLYTIC OR ELECTROPHORETIC PROCESSES; APPARATUS THEREFOR
- C25D—PROCESSES FOR THE ELECTROLYTIC OR ELECTROPHORETIC PRODUCTION OF COATINGS; ELECTROFORMING; APPARATUS THEREFOR
- C25D5/00—Electroplating characterised by the process; Pretreatment or after-treatment of workpieces
- C25D5/48—After-treatment of electroplated surfaces
-
- C—CHEMISTRY; METALLURGY
- C25—ELECTROLYTIC OR ELECTROPHORETIC PROCESSES; APPARATUS THEREFOR
- C25D—PROCESSES FOR THE ELECTROLYTIC OR ELECTROPHORETIC PRODUCTION OF COATINGS; ELECTROFORMING; APPARATUS THEREFOR
- C25D5/00—Electroplating characterised by the process; Pretreatment or after-treatment of workpieces
- C25D5/627—Electroplating characterised by the visual appearance of the layers, e.g. colour, brightness or mat appearance
Landscapes
- Chemical & Material Sciences (AREA)
- Chemical Kinetics & Catalysis (AREA)
- Engineering & Computer Science (AREA)
- Materials Engineering (AREA)
- Metallurgy (AREA)
- Organic Chemistry (AREA)
- Electrochemistry (AREA)
- General Chemical & Material Sciences (AREA)
- Mechanical Engineering (AREA)
- Inorganic Chemistry (AREA)
- Electroplating Methods And Accessories (AREA)
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
CN200810303204.7 | 2008-07-30 | ||
CN200810303204A CN101638790A (zh) | 2008-07-30 | 2008-07-30 | 镁及镁合金的电镀方法 |
Publications (1)
Publication Number | Publication Date |
---|---|
US20100025255A1 true US20100025255A1 (en) | 2010-02-04 |
Family
ID=41325000
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
US12/498,455 Abandoned US20100025255A1 (en) | 2008-07-30 | 2009-07-07 | Electroplating method for magnesium and magnesium alloy |
Country Status (3)
Country | Link |
---|---|
US (1) | US20100025255A1 (zh) |
EP (1) | EP2149621A1 (zh) |
CN (1) | CN101638790A (zh) |
Cited By (49)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US20120318513A1 (en) * | 2011-06-17 | 2012-12-20 | Baker Hughes Incorporated | Corrodible downhole article and method of removing the article from downhole environment |
US20130075271A1 (en) * | 2011-09-22 | 2013-03-28 | Sikorsky Aircraft Corporation | Protection of magnesium alloys by aluminum plating from ionic liquids |
US8425651B2 (en) | 2010-07-30 | 2013-04-23 | Baker Hughes Incorporated | Nanomatrix metal composite |
US8573295B2 (en) | 2010-11-16 | 2013-11-05 | Baker Hughes Incorporated | Plug and method of unplugging a seat |
US8631876B2 (en) | 2011-04-28 | 2014-01-21 | Baker Hughes Incorporated | Method of making and using a functionally gradient composite tool |
US8714268B2 (en) | 2009-12-08 | 2014-05-06 | Baker Hughes Incorporated | Method of making and using multi-component disappearing tripping ball |
US8776884B2 (en) | 2010-08-09 | 2014-07-15 | Baker Hughes Incorporated | Formation treatment system and method |
US8783365B2 (en) | 2011-07-28 | 2014-07-22 | Baker Hughes Incorporated | Selective hydraulic fracturing tool and method thereof |
US9022107B2 (en) | 2009-12-08 | 2015-05-05 | Baker Hughes Incorporated | Dissolvable tool |
US9033055B2 (en) | 2011-08-17 | 2015-05-19 | Baker Hughes Incorporated | Selectively degradable passage restriction and method |
US9057242B2 (en) | 2011-08-05 | 2015-06-16 | Baker Hughes Incorporated | Method of controlling corrosion rate in downhole article, and downhole article having controlled corrosion rate |
US9068428B2 (en) | 2012-02-13 | 2015-06-30 | Baker Hughes Incorporated | Selectively corrodible downhole article and method of use |
US9079246B2 (en) | 2009-12-08 | 2015-07-14 | Baker Hughes Incorporated | Method of making a nanomatrix powder metal compact |
US9080098B2 (en) | 2011-04-28 | 2015-07-14 | Baker Hughes Incorporated | Functionally gradient composite article |
WO2015107255A1 (en) | 2014-01-15 | 2015-07-23 | Savroc Ltd | Method for producing chromium-containing multilayer coating and a coated object |
US9090955B2 (en) | 2010-10-27 | 2015-07-28 | Baker Hughes Incorporated | Nanomatrix powder metal composite |
US9090956B2 (en) | 2011-08-30 | 2015-07-28 | Baker Hughes Incorporated | Aluminum alloy powder metal compact |
US9101978B2 (en) | 2002-12-08 | 2015-08-11 | Baker Hughes Incorporated | Nanomatrix powder metal compact |
US9109269B2 (en) | 2011-08-30 | 2015-08-18 | Baker Hughes Incorporated | Magnesium alloy powder metal compact |
US9109429B2 (en) | 2002-12-08 | 2015-08-18 | Baker Hughes Incorporated | Engineered powder compact composite material |
US9127515B2 (en) | 2010-10-27 | 2015-09-08 | Baker Hughes Incorporated | Nanomatrix carbon composite |
US9133695B2 (en) | 2011-09-03 | 2015-09-15 | Baker Hughes Incorporated | Degradable shaped charge and perforating gun system |
US9187990B2 (en) | 2011-09-03 | 2015-11-17 | Baker Hughes Incorporated | Method of using a degradable shaped charge and perforating gun system |
US9227243B2 (en) | 2009-12-08 | 2016-01-05 | Baker Hughes Incorporated | Method of making a powder metal compact |
WO2016004393A1 (en) * | 2014-07-02 | 2016-01-07 | Superior Shot Peening, Inc. | Multi-layer coating and related methods of application |
CN105239125A (zh) * | 2015-10-29 | 2016-01-13 | 无锡桥阳机械制造有限公司 | 一种电镀工艺 |
US9243475B2 (en) | 2009-12-08 | 2016-01-26 | Baker Hughes Incorporated | Extruded powder metal compact |
US9284812B2 (en) | 2011-11-21 | 2016-03-15 | Baker Hughes Incorporated | System for increasing swelling efficiency |
US9347119B2 (en) | 2011-09-03 | 2016-05-24 | Baker Hughes Incorporated | Degradable high shock impedance material |
US9605508B2 (en) | 2012-05-08 | 2017-03-28 | Baker Hughes Incorporated | Disintegrable and conformable metallic seal, and method of making the same |
US9643144B2 (en) | 2011-09-02 | 2017-05-09 | Baker Hughes Incorporated | Method to generate and disperse nanostructures in a composite material |
US9643250B2 (en) | 2011-07-29 | 2017-05-09 | Baker Hughes Incorporated | Method of controlling the corrosion rate of alloy particles, alloy particle with controlled corrosion rate, and articles comprising the particle |
US9682425B2 (en) | 2009-12-08 | 2017-06-20 | Baker Hughes Incorporated | Coated metallic powder and method of making the same |
US9707739B2 (en) | 2011-07-22 | 2017-07-18 | Baker Hughes Incorporated | Intermetallic metallic composite, method of manufacture thereof and articles comprising the same |
US9816339B2 (en) | 2013-09-03 | 2017-11-14 | Baker Hughes, A Ge Company, Llc | Plug reception assembly and method of reducing restriction in a borehole |
US9833838B2 (en) | 2011-07-29 | 2017-12-05 | Baker Hughes, A Ge Company, Llc | Method of controlling the corrosion rate of alloy particles, alloy particle with controlled corrosion rate, and articles comprising the particle |
US9856547B2 (en) | 2011-08-30 | 2018-01-02 | Bakers Hughes, A Ge Company, Llc | Nanostructured powder metal compact |
US9910026B2 (en) | 2015-01-21 | 2018-03-06 | Baker Hughes, A Ge Company, Llc | High temperature tracers for downhole detection of produced water |
US9926766B2 (en) | 2012-01-25 | 2018-03-27 | Baker Hughes, A Ge Company, Llc | Seat for a tubular treating system |
US10016810B2 (en) | 2015-12-14 | 2018-07-10 | Baker Hughes, A Ge Company, Llc | Methods of manufacturing degradable tools using a galvanic carrier and tools manufactured thereof |
US10221637B2 (en) | 2015-08-11 | 2019-03-05 | Baker Hughes, A Ge Company, Llc | Methods of manufacturing dissolvable tools via liquid-solid state molding |
US10240419B2 (en) | 2009-12-08 | 2019-03-26 | Baker Hughes, A Ge Company, Llc | Downhole flow inhibition tool and method of unplugging a seat |
US10378303B2 (en) | 2015-03-05 | 2019-08-13 | Baker Hughes, A Ge Company, Llc | Downhole tool and method of forming the same |
US10443143B2 (en) | 2014-01-15 | 2019-10-15 | Savroc Ltd | Method for producing a chromium coating and a coated object |
US10487412B2 (en) | 2014-07-11 | 2019-11-26 | Savroc Ltd | Chromium-containing coating, a method for its production and a coated object |
US10777912B2 (en) | 2015-06-08 | 2020-09-15 | Te Connectivity Germany Gmbh | Electrical contact element and method for altering mechanical and/or electrical properties of at least one area of such |
US11167343B2 (en) | 2014-02-21 | 2021-11-09 | Terves, Llc | Galvanically-active in situ formed particles for controlled rate dissolving tools |
US11365164B2 (en) | 2014-02-21 | 2022-06-21 | Terves, Llc | Fluid activated disintegrating metal system |
US11649526B2 (en) | 2017-07-27 | 2023-05-16 | Terves, Llc | Degradable metal matrix composite |
Families Citing this family (12)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
CN102808204A (zh) * | 2012-08-21 | 2012-12-05 | 江苏增钬云表面处理有限公司 | 镁合金汽车轮毂电镀装饰铬的方法 |
CN103898561A (zh) * | 2013-06-03 | 2014-07-02 | 无锡市锡山区鹅湖镇荡口青荡金属制品厂 | 一种在镁合金压铸件表面镀铬的电镀溶液 |
CN103898585A (zh) * | 2013-06-03 | 2014-07-02 | 无锡市锡山区鹅湖镇荡口青荡金属制品厂 | 一种镁合金压铸件表面电镀铬工艺 |
CN103898560B (zh) * | 2013-06-03 | 2016-12-28 | 顾玉奎 | 一种在镁合金压铸件表面镀铬的电镀工艺 |
CN103820791B (zh) * | 2014-02-28 | 2015-12-09 | 上海造币有限公司 | 一种降低镍包钢坯饼退火温度或时间的方法 |
CN104280818A (zh) * | 2014-10-23 | 2015-01-14 | 深圳市德仓科技有限公司 | 一种导光板基板及其制造方法 |
WO2016120653A1 (en) * | 2015-01-27 | 2016-08-04 | Sophia L.A.B. Sagl | Process for surface treating a magnesium alloy and process for electroless nickel plating a treated surface |
CN105803510A (zh) * | 2016-03-25 | 2016-07-27 | 中国电子科技集团公司第三十八研究所 | 一种镁锂合金表面耐磨导电镀镍层的沉积方法 |
CN105839105B (zh) * | 2016-05-23 | 2018-09-07 | 深圳市瑞世兴科技有限公司 | 耐腐蚀性镁合金的表面处理方法 |
CN110846696A (zh) * | 2019-11-28 | 2020-02-28 | 汕头市铠嘉模具有限公司 | 提高凹版使用寿命的电镀新工艺 |
CN113373398B (zh) * | 2021-06-24 | 2023-04-28 | 重庆大学 | 一种阻燃镁合金部件 |
CN117587487B (zh) * | 2024-01-18 | 2024-04-02 | 南京海创表面处理技术有限公司 | 一种高精度镁合金工件表面电镀设备及控制方法 |
Citations (8)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US3472742A (en) * | 1966-03-15 | 1969-10-14 | Webb James E | Plating nickel on aluminum castings |
US3615281A (en) * | 1967-04-26 | 1971-10-26 | Electro Chem Eng | Corrosion-resistant chromium-plated articles |
US4022703A (en) * | 1975-01-14 | 1977-05-10 | Produits Chimiques Ugine Kuhlmann | Stabilization of hydrogen peroxide in acid baths for cleaning metals |
US4107004A (en) * | 1975-03-26 | 1978-08-15 | International Lead Zinc Research Organization, Inc. | Trivalent chromium electroplating baths and method |
US4376685A (en) * | 1981-06-24 | 1983-03-15 | M&T Chemicals Inc. | Acid copper electroplating baths containing brightening and leveling additives |
US20050221008A1 (en) * | 2004-03-30 | 2005-10-06 | Callaway Golf Company | Method of Plating a Golf Club Head |
US20060228569A1 (en) * | 2003-08-08 | 2006-10-12 | Tadaaki Kojima | Production method of substrate with black film and substrate with black film |
US20070039829A1 (en) * | 2005-08-17 | 2007-02-22 | Trevor Pearson | Pretreatment of magnesium substrates for electroplating |
Family Cites Families (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
FR2054442A1 (zh) * | 1969-07-01 | 1971-04-23 | Naphtachimie Sa |
-
2008
- 2008-07-30 CN CN200810303204A patent/CN101638790A/zh active Pending
-
2009
- 2009-07-07 US US12/498,455 patent/US20100025255A1/en not_active Abandoned
- 2009-07-22 EP EP09166146A patent/EP2149621A1/en not_active Withdrawn
Patent Citations (8)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US3472742A (en) * | 1966-03-15 | 1969-10-14 | Webb James E | Plating nickel on aluminum castings |
US3615281A (en) * | 1967-04-26 | 1971-10-26 | Electro Chem Eng | Corrosion-resistant chromium-plated articles |
US4022703A (en) * | 1975-01-14 | 1977-05-10 | Produits Chimiques Ugine Kuhlmann | Stabilization of hydrogen peroxide in acid baths for cleaning metals |
US4107004A (en) * | 1975-03-26 | 1978-08-15 | International Lead Zinc Research Organization, Inc. | Trivalent chromium electroplating baths and method |
US4376685A (en) * | 1981-06-24 | 1983-03-15 | M&T Chemicals Inc. | Acid copper electroplating baths containing brightening and leveling additives |
US20060228569A1 (en) * | 2003-08-08 | 2006-10-12 | Tadaaki Kojima | Production method of substrate with black film and substrate with black film |
US20050221008A1 (en) * | 2004-03-30 | 2005-10-06 | Callaway Golf Company | Method of Plating a Golf Club Head |
US20070039829A1 (en) * | 2005-08-17 | 2007-02-22 | Trevor Pearson | Pretreatment of magnesium substrates for electroplating |
Cited By (68)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US9109429B2 (en) | 2002-12-08 | 2015-08-18 | Baker Hughes Incorporated | Engineered powder compact composite material |
US9101978B2 (en) | 2002-12-08 | 2015-08-11 | Baker Hughes Incorporated | Nanomatrix powder metal compact |
US10240419B2 (en) | 2009-12-08 | 2019-03-26 | Baker Hughes, A Ge Company, Llc | Downhole flow inhibition tool and method of unplugging a seat |
US9243475B2 (en) | 2009-12-08 | 2016-01-26 | Baker Hughes Incorporated | Extruded powder metal compact |
US8714268B2 (en) | 2009-12-08 | 2014-05-06 | Baker Hughes Incorporated | Method of making and using multi-component disappearing tripping ball |
US9227243B2 (en) | 2009-12-08 | 2016-01-05 | Baker Hughes Incorporated | Method of making a powder metal compact |
US10669797B2 (en) | 2009-12-08 | 2020-06-02 | Baker Hughes, A Ge Company, Llc | Tool configured to dissolve in a selected subsurface environment |
US9682425B2 (en) | 2009-12-08 | 2017-06-20 | Baker Hughes Incorporated | Coated metallic powder and method of making the same |
US9022107B2 (en) | 2009-12-08 | 2015-05-05 | Baker Hughes Incorporated | Dissolvable tool |
US9079246B2 (en) | 2009-12-08 | 2015-07-14 | Baker Hughes Incorporated | Method of making a nanomatrix powder metal compact |
US8425651B2 (en) | 2010-07-30 | 2013-04-23 | Baker Hughes Incorporated | Nanomatrix metal composite |
US8776884B2 (en) | 2010-08-09 | 2014-07-15 | Baker Hughes Incorporated | Formation treatment system and method |
US9090955B2 (en) | 2010-10-27 | 2015-07-28 | Baker Hughes Incorporated | Nanomatrix powder metal composite |
US9127515B2 (en) | 2010-10-27 | 2015-09-08 | Baker Hughes Incorporated | Nanomatrix carbon composite |
US8573295B2 (en) | 2010-11-16 | 2013-11-05 | Baker Hughes Incorporated | Plug and method of unplugging a seat |
US8631876B2 (en) | 2011-04-28 | 2014-01-21 | Baker Hughes Incorporated | Method of making and using a functionally gradient composite tool |
US9080098B2 (en) | 2011-04-28 | 2015-07-14 | Baker Hughes Incorporated | Functionally gradient composite article |
US10335858B2 (en) | 2011-04-28 | 2019-07-02 | Baker Hughes, A Ge Company, Llc | Method of making and using a functionally gradient composite tool |
US9631138B2 (en) | 2011-04-28 | 2017-04-25 | Baker Hughes Incorporated | Functionally gradient composite article |
US9926763B2 (en) | 2011-06-17 | 2018-03-27 | Baker Hughes, A Ge Company, Llc | Corrodible downhole article and method of removing the article from downhole environment |
US20120318513A1 (en) * | 2011-06-17 | 2012-12-20 | Baker Hughes Incorporated | Corrodible downhole article and method of removing the article from downhole environment |
US9139928B2 (en) * | 2011-06-17 | 2015-09-22 | Baker Hughes Incorporated | Corrodible downhole article and method of removing the article from downhole environment |
US9707739B2 (en) | 2011-07-22 | 2017-07-18 | Baker Hughes Incorporated | Intermetallic metallic composite, method of manufacture thereof and articles comprising the same |
US10697266B2 (en) | 2011-07-22 | 2020-06-30 | Baker Hughes, A Ge Company, Llc | Intermetallic metallic composite, method of manufacture thereof and articles comprising the same |
US8783365B2 (en) | 2011-07-28 | 2014-07-22 | Baker Hughes Incorporated | Selective hydraulic fracturing tool and method thereof |
US9643250B2 (en) | 2011-07-29 | 2017-05-09 | Baker Hughes Incorporated | Method of controlling the corrosion rate of alloy particles, alloy particle with controlled corrosion rate, and articles comprising the particle |
US9833838B2 (en) | 2011-07-29 | 2017-12-05 | Baker Hughes, A Ge Company, Llc | Method of controlling the corrosion rate of alloy particles, alloy particle with controlled corrosion rate, and articles comprising the particle |
US10092953B2 (en) | 2011-07-29 | 2018-10-09 | Baker Hughes, A Ge Company, Llc | Method of controlling the corrosion rate of alloy particles, alloy particle with controlled corrosion rate, and articles comprising the particle |
US9057242B2 (en) | 2011-08-05 | 2015-06-16 | Baker Hughes Incorporated | Method of controlling corrosion rate in downhole article, and downhole article having controlled corrosion rate |
US9033055B2 (en) | 2011-08-17 | 2015-05-19 | Baker Hughes Incorporated | Selectively degradable passage restriction and method |
US10301909B2 (en) | 2011-08-17 | 2019-05-28 | Baker Hughes, A Ge Company, Llc | Selectively degradable passage restriction |
US9856547B2 (en) | 2011-08-30 | 2018-01-02 | Bakers Hughes, A Ge Company, Llc | Nanostructured powder metal compact |
US9925589B2 (en) | 2011-08-30 | 2018-03-27 | Baker Hughes, A Ge Company, Llc | Aluminum alloy powder metal compact |
US9109269B2 (en) | 2011-08-30 | 2015-08-18 | Baker Hughes Incorporated | Magnesium alloy powder metal compact |
US9090956B2 (en) | 2011-08-30 | 2015-07-28 | Baker Hughes Incorporated | Aluminum alloy powder metal compact |
US10737321B2 (en) | 2011-08-30 | 2020-08-11 | Baker Hughes, A Ge Company, Llc | Magnesium alloy powder metal compact |
US9802250B2 (en) | 2011-08-30 | 2017-10-31 | Baker Hughes | Magnesium alloy powder metal compact |
US11090719B2 (en) | 2011-08-30 | 2021-08-17 | Baker Hughes, A Ge Company, Llc | Aluminum alloy powder metal compact |
US9643144B2 (en) | 2011-09-02 | 2017-05-09 | Baker Hughes Incorporated | Method to generate and disperse nanostructures in a composite material |
US9187990B2 (en) | 2011-09-03 | 2015-11-17 | Baker Hughes Incorporated | Method of using a degradable shaped charge and perforating gun system |
US9347119B2 (en) | 2011-09-03 | 2016-05-24 | Baker Hughes Incorporated | Degradable high shock impedance material |
US9133695B2 (en) | 2011-09-03 | 2015-09-15 | Baker Hughes Incorporated | Degradable shaped charge and perforating gun system |
US8778163B2 (en) * | 2011-09-22 | 2014-07-15 | Sikorsky Aircraft Corporation | Protection of magnesium alloys by aluminum plating from ionic liquids |
US20130075271A1 (en) * | 2011-09-22 | 2013-03-28 | Sikorsky Aircraft Corporation | Protection of magnesium alloys by aluminum plating from ionic liquids |
US9284812B2 (en) | 2011-11-21 | 2016-03-15 | Baker Hughes Incorporated | System for increasing swelling efficiency |
US9926766B2 (en) | 2012-01-25 | 2018-03-27 | Baker Hughes, A Ge Company, Llc | Seat for a tubular treating system |
US9068428B2 (en) | 2012-02-13 | 2015-06-30 | Baker Hughes Incorporated | Selectively corrodible downhole article and method of use |
US9605508B2 (en) | 2012-05-08 | 2017-03-28 | Baker Hughes Incorporated | Disintegrable and conformable metallic seal, and method of making the same |
US10612659B2 (en) | 2012-05-08 | 2020-04-07 | Baker Hughes Oilfield Operations, Llc | Disintegrable and conformable metallic seal, and method of making the same |
US9816339B2 (en) | 2013-09-03 | 2017-11-14 | Baker Hughes, A Ge Company, Llc | Plug reception assembly and method of reducing restriction in a borehole |
WO2015107255A1 (en) | 2014-01-15 | 2015-07-23 | Savroc Ltd | Method for producing chromium-containing multilayer coating and a coated object |
US10443142B2 (en) | 2014-01-15 | 2019-10-15 | Savroc Ltd | Method for producing chromium-containing multilayer coating and a coated object |
US10443143B2 (en) | 2014-01-15 | 2019-10-15 | Savroc Ltd | Method for producing a chromium coating and a coated object |
US11167343B2 (en) | 2014-02-21 | 2021-11-09 | Terves, Llc | Galvanically-active in situ formed particles for controlled rate dissolving tools |
US11613952B2 (en) | 2014-02-21 | 2023-03-28 | Terves, Llc | Fluid activated disintegrating metal system |
US11365164B2 (en) | 2014-02-21 | 2022-06-21 | Terves, Llc | Fluid activated disintegrating metal system |
US10597951B2 (en) | 2014-07-02 | 2020-03-24 | Superior Shot Peening, Inc | Multi-layer coating and related methods of application |
WO2016004393A1 (en) * | 2014-07-02 | 2016-01-07 | Superior Shot Peening, Inc. | Multi-layer coating and related methods of application |
US10006258B2 (en) | 2014-07-02 | 2018-06-26 | Superior Shot Peening, Inc. | Multi-layer coating and related methods of application |
US10487412B2 (en) | 2014-07-11 | 2019-11-26 | Savroc Ltd | Chromium-containing coating, a method for its production and a coated object |
US9910026B2 (en) | 2015-01-21 | 2018-03-06 | Baker Hughes, A Ge Company, Llc | High temperature tracers for downhole detection of produced water |
US10378303B2 (en) | 2015-03-05 | 2019-08-13 | Baker Hughes, A Ge Company, Llc | Downhole tool and method of forming the same |
US10777912B2 (en) | 2015-06-08 | 2020-09-15 | Te Connectivity Germany Gmbh | Electrical contact element and method for altering mechanical and/or electrical properties of at least one area of such |
US10221637B2 (en) | 2015-08-11 | 2019-03-05 | Baker Hughes, A Ge Company, Llc | Methods of manufacturing dissolvable tools via liquid-solid state molding |
CN105239125A (zh) * | 2015-10-29 | 2016-01-13 | 无锡桥阳机械制造有限公司 | 一种电镀工艺 |
US10016810B2 (en) | 2015-12-14 | 2018-07-10 | Baker Hughes, A Ge Company, Llc | Methods of manufacturing degradable tools using a galvanic carrier and tools manufactured thereof |
US11649526B2 (en) | 2017-07-27 | 2023-05-16 | Terves, Llc | Degradable metal matrix composite |
US11898223B2 (en) | 2017-07-27 | 2024-02-13 | Terves, Llc | Degradable metal matrix composite |
Also Published As
Publication number | Publication date |
---|---|
CN101638790A (zh) | 2010-02-03 |
EP2149621A1 (en) | 2010-02-03 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
US20100025255A1 (en) | Electroplating method for magnesium and magnesium alloy | |
US7368047B2 (en) | Method of preparing copper plating layer having high adhesion to magnesium alloy using electroplating | |
EP1915473B1 (en) | Pretreatment of magnesium substrates for electroplating | |
JP2725477B2 (ja) | アルミニウム帯への亜鉛系電気めっき方法 | |
CA1132087A (en) | Plating on aluminum alloys | |
WO2005017235A1 (ja) | マグネシウム又はマグネシウム合金からなる製品及びその製造方法 | |
JP4736084B2 (ja) | マグネシウム又はマグネシウム合金からなる製品の製造方法 | |
CN101660183B (zh) | 一种镁合金电镀方法 | |
JP5247142B2 (ja) | 銀めっき方法 | |
CN106149042A (zh) | 一种锌合金电解剥铜剂 | |
JP2923754B2 (ja) | マグネシウム合金のめっき方法 | |
US4196061A (en) | Direct nickel-plating of aluminum | |
US20100025256A1 (en) | Surface treatment method for housing | |
KR20120127840A (ko) | 마그네슘 합금의 도금방법 및 이를 위한 전처리 방법 | |
KR20110125929A (ko) | 금속표면처리방법 | |
JP4027320B2 (ja) | 非シアン化合物を用いた亜鉛物体及び亜鉛合金物体への銅メッキ方法 | |
JPH1018055A (ja) | プラスチック表面のメッキによる金属化方法 | |
CN1641075B (zh) | 镁、镁合金的表面活化处理方法及表面镀方法 | |
CN104233296A (zh) | 铝及铝合金镀银的方法 | |
JP3020673B2 (ja) | チタン合金素材のめっき前処理法 | |
JP2962496B2 (ja) | マグネ基合金のめっき方法 | |
CN109652806A (zh) | 一种以紫铜或黄铜为基材的亮锡汽车零部件的退镀液和退镀工艺 | |
EP2342370A1 (en) | Novel cyanide-free electroplating process for zinc and zinc alloy die-cast components | |
JP2010174315A (ja) | 被膜を有するマグネシウム合金部材およびその製造方法 | |
Pearson | Pretreatment of aluminium for electrodeposition |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
AS | Assignment |
Owner name: SHENZHEN FUTAIHONG PRECISION INDUSTRY CO., LTD.,CH Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:SU, JONG-YI;CHEN, CHENG-SHIN;WANG, REN-NING;AND OTHERS;REEL/FRAME:022920/0311 Effective date: 20090620 Owner name: FIH (HONG KONG) LIMITED,HONG KONG Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:SU, JONG-YI;CHEN, CHENG-SHIN;WANG, REN-NING;AND OTHERS;REEL/FRAME:022920/0311 Effective date: 20090620 |
|
STCB | Information on status: application discontinuation |
Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION |