Classifications

• • C—CHEMISTRY; METALLURGY
  • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
  • C09D—COATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
  • C09D1/00—Coating compositions, e.g. paints, varnishes or lacquers, based on inorganic substances
  • C09D1/02—Coating compositions, e.g. paints, varnishes or lacquers, based on inorganic substances alkali metal silicates
  • C09D1/04—Coating compositions, e.g. paints, varnishes or lacquers, based on inorganic substances alkali metal silicates with organic additives
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
  • C08J9/00—Working-up of macromolecular substances to porous or cellular articles or materials; After-treatment thereof
  • C08J9/22—After-treatment of expandable particles; Forming foamed products
  • C08J9/224—Surface treatment
• • C—CHEMISTRY; METALLURGY
  • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
  • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
  • C04B16/00—Use of organic materials as fillers, e.g. pigments, for mortars, concrete or artificial stone; Treatment of organic materials specially adapted to enhance their filling properties in mortars, concrete or artificial stone
  • C04B16/04—Macromolecular compounds
  • C04B16/08—Macromolecular compounds porous, e.g. expanded polystyrene beads or microballoons
• • C—CHEMISTRY; METALLURGY
  • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
  • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
  • C04B30/00—Compositions for artificial stone, not containing binders
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
  • C08J9/00—Working-up of macromolecular substances to porous or cellular articles or materials; After-treatment thereof
  • C08J9/22—After-treatment of expandable particles; Forming foamed products
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
  • C08J9/00—Working-up of macromolecular substances to porous or cellular articles or materials; After-treatment thereof
  • C08J9/22—After-treatment of expandable particles; Forming foamed products
  • C08J9/228—Forming foamed products
  • C08J9/232—Forming foamed products by sintering expandable particles
• • C—CHEMISTRY; METALLURGY
  • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
  • C09D—COATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
  • C09D5/00—Coating compositions, e.g. paints, varnishes or lacquers, characterised by their physical nature or the effects produced; Filling pastes
  • C09D5/18—Fireproof paints including high temperature resistant paints
• • C—CHEMISTRY; METALLURGY
  • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
  • C09K—MATERIALS FOR MISCELLANEOUS APPLICATIONS, NOT PROVIDED FOR ELSEWHERE
  • C09K21/00—Fireproofing materials
  • C09K21/14—Macromolecular materials
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
  • C08J2201/00—Foams characterised by the foaming process
  • C08J2201/02—Foams characterised by the foaming process characterised by mechanical pre- or post-treatments
  • C08J2201/038—Use of an inorganic compound to impregnate, bind or coat a foam, e.g. waterglass
• • E—FIXED CONSTRUCTIONS
  • E04—BUILDING
  • E04B—GENERAL BUILDING CONSTRUCTIONS; WALLS, e.g. PARTITIONS; ROOFS; FLOORS; CEILINGS; INSULATION OR OTHER PROTECTION OF BUILDINGS
  • E04B1/00—Constructions in general; Structures which are not restricted either to walls, e.g. partitions, or floors or ceilings or roofs
  • E04B1/62—Insulation or other protection; Elements or use of specified material therefor
  • E04B1/92—Protection against other undesired influences or dangers
  • E04B1/94—Protection against other undesired influences or dangers against fire
• • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
  • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
  • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
  • Y10T428/00—Stock material or miscellaneous articles
  • Y10T428/249921—Web or sheet containing structurally defined element or component
  • Y10T428/249953—Composite having voids in a component [e.g., porous, cellular, etc.]
  • Y10T428/249987—With nonvoid component of specified composition
  • Y10T428/24999—Inorganic

Definitions

• the present invention relates to aqueous compositions, precursor systems for producing such compositions and also application systems for applying said compositions, e.g. as coatings, to a surface or substrate.
• Soluble silicates are widely used as adhesives, coatings and bondings. Whilst their inherent solubility is an asset in many of the applications for which they are used, it is disadvantageous for applications where, for example, water resistance, integrity and strength of structure are deemed essential.
• Fire retardant coating compositions find wide application in the construction and building maintenance industries, for example for application to flammable building materials before, or after, their incorporation in a building structure.
• flammable materials are polymer tiling and sheeting, e.g. of expanded polystyrene or urethane plastics and composites containing such plastics.
• Wood, wood chip and paper based materials can also benefit from application of such coatings.
• intumescent coating which exert their protectant action partly by swelling when exposed to heat or fire.
• flammable materials are sold with the fire retardant coating pre-applied.
• an intumescent fire retardant coating known as SafeCoat E84TM is pre-applied to expanded polystyrene/polyurethane foam articles prior to sale.
• U.S. Pat. No. 5,462,699 relates to a fire retardant composition for application to, inter alia, building materials, the composition containing a silicate, water and surfactant.
• silicate based fire retardant composition for building insulation materials such as expanded polystyrene (e.g. roofing insulation) is that, until needed, such materials are often left exposed to the adverse weather conditions after delivery to the building site, Unless precautions are taken to protect them against the wet, such exposure can result in significant loss of the fire retardancy properties of the silicate-based composition.
• expanded polystyrene e.g. roofing insulation
• compositions according to the present invention suitable for use as fire retardant compositions.
• the invention is not limited to aqueous compositions for fire retardancy use; other applications such as use of the composition as an adhesive or binder are within the ambit of the present invention.
• a further advantage of the compositions of the invention is that they may be used to prepare fire retardant systems that are substantially free of halogen-containing compounds. Halogen-containing compounds are undesirable because of their potential environmental risk.
• the present invention provides an aqueous gel-forming composition
• an aqueous gel-forming composition comprising an aluminosilicate and an organic liquid which enhances the integrity of films formed by application of the composition as a coating to a surface followed by drying.
• the invention provides an aqueous gel-forming composition comprising:
• Boiling points in this specification are to be measured at standard atmospheric pressure.
• compositions of the invention comprise at least 20% by weight of water, preferably at least 30%, more preferably at least 40%.
• the term “gel” refers to a substance that contains a continuous solid skeleton (in the present invention based on the aluminosilicate) enclosing a continuous liquid phase (in the present case, predominantly water)—see for example Sol-Gel Science, The Physics and Chemistry of Sol-Gel Processing (C J Brinker and G W Scheer) published by Academic Press Inc., 1990, for example page 8. These materials may also be referred to as co-gels or coagels.
• the solid may be in the form of dispersed, discontinuous solid particles (a sol), but these individual particles coalesce to form a continuous solid network.
• the compositions of the invention are initially in the form of a sol which converts over time to a gel.
• compositions according to the first aspect of the present invention consist of those which comprise:
• any reference herein to a liquid means a substance which is liquid, preferably pourable, at 25° C. at atmospheric pressure, unless explicitly stated to the contrary. Further, all viscosities stated herein which refer to non-Newtonian liquids or gels are viscosities measured at a shear rate of 23 s ⁇ 1 and at 25° C.
• the organic liquid is preferably one which is substantially water-immiscible.
• the degree of immiscibility is such that, at 25° C., the organic liquid dissolves to the extent of less than about 10% by weight (preferably less than about 5% by weight, more preferably less than 1% by weight) in water, or water dissolves to the extent of less than about 10% by weight (preferably less than about 5% by weight, more preferably less than 1% by weight) in the organic liquid.
• composition of the present invention can be applied as a fire retardant coating to a surface or substrate, it is not limited to this particular application and may, for example, be used as a binder or adhesive or a water-resistant coating, irrespective of whether the composition serves to confer fire retardancy in such other applications.
• aluminosilicate as used in the present invention is typically formed by the sol-gel route and this can be effected in situ by forming the aluminosilicate at the point of use, by mixing precursor liquids.
• a second aspect of the present invention provides a precursor system for forming a coating composition according to the first aspect of the invention, the precursor system comprising:
• a sol-gel is basically a reaction product which is initially formed from the components of the precursor system as a liquid, but which subsequently forms a gel and ultimately solidifies.
• solid aluminate is admixed with an aqueous silicate solution or aqueous aluminate solution is admixed with an aqueous silicate solution.
• At least part of the organic liquid may be incorporated in component (i) and/or component (ii).
• the organic liquid may initially be entirely separate from both of components (i) and (ii) and be admixed contemporaneously with, or subsequent to, the admixture of components (i) and (ii).
• the organic liquid is incorporated into component (i) and/or (ii) prior to admixing the components to form the sol-gel system.
• composition comprising an aqueous solution of a metal aluminate and at least one organic liquid selected from the group consisting of polyhydroxy alcohols, mineral oils, liquid paraffin oils, glycol ethers, silicone oils and mixtures thereof.
• This composition is suitable as a part of the precursor system of the second aspect of the invention.
• a fourth aspect of the invention provides an aqueous solution of a metal silicate and at least one organic liquid selected from the group consisting of polyhydroxy alcohols, mineral oils, liquid paraffin oils, glycol ethers, silicone oils and mixtures thereof.
• This composition is suitable as a part of the precursor system of the second aspect of the invention.
• a further aspect of the present invention provides an application system for forming a coating composition according to the first aspect of the invention from a precursor system according to the second aspect of the invention and applying the coating composition so formed to a substrate, the application system comprising means for admixture of components (i), (ii) and (iii) and application means for effecting coating of the substrate with the resulting mixture.
• the application system for forming a coating composition and applying the coating composition so formed to a substrate suitable comprises a metal aluminate (i) stored in a first storage means, an aqueous solution of metal silicate (ii) in a second storage means and an organic liquid (iii) in a third storage means or in the first and/or second storage means, a means for admixture of components (i), (ii) and (iii) and application means for effecting coating of the substrate with the resulting mixture.
• the organic liquid may be stored in its own, separate storage means, or may be admixed with either or both of the metal aluminate or the aqueous solution of metal aluminate in their respective storage means.
• the metal aluminate may be in the form of an aqueous solution.
• Suitable storage means are tanks, containers or vessels in fluid connection with the means for admixture of the components.
• the transport of the components to and from the means for admixture may be effected by an arrangement of pumps and valves to meter the dosage of each component to the admixture means.
• a further aspect of the present invention provides a method of making a coating composition according to the first aspect of the present invention, the method comprising admixture of the following components:
• Coatings formed from compositions according to the present invention exhibit superior physical integrity and long term stability, in comparison with conventional silicate systems. Without wishing to be bound by any theory, it is thought that this improvement arises by virtue of the aluminosilicate being present in the form of a network of bonded molecules that extends throughout the solution and by virtue of the presence of said organic liquid.
• composition of the first aspect of the invention prior to application to a surface or substrate comprises at least 5% by weight of the aluminosilicate, and at least 0.1% by weight of said organic liquid.
• the preferred values for ingredients detailed below apply to all aspects of the invention. However the values are expressed in terms of the composition of the first aspect of the invention. When applied, for instance, to the precursor system or the application system or the precursor compositions, the preferred values apply to the values achieved in the resulting sol-gel composition.
• the amount of water in compositions of the invention is preferably from 60% to 95%, more preferably from 70% to 90% by weight of the total composition.
• the aluminosilicate is typically amorphous, which may be assessed by the absence of sharp peaks in the x-ray powder diffraction spectrum of the material.
• the mole ratio of Si:Al in the composition is typically from 3 to 30, preferably from 4 to 15 and more preferably from 5 to 10.
• the reference to mole ratio of Si:Al is based on the amount of silicon (in moles) in the silicate and aluminium (in moles) in the aluminate used for preparation of the compositions.
• the aluminosilicate is usually formed by the sol-gel route, preferably in situ from admixture of precursor components at the point of use.
• Compositions according the present invention preferably also comprise a metal or metal oxide to inhibit water absorption and/or to aid preservation of the film forming properties of the composition, especially film integrity, upon storage.
• the metal or oxide will usually be in particulate form and be sparingly soluble in water.
• the volume median particle diameter of the metal or metal oxide will be 50 ⁇ m or less.
• less than 1% by volume of the metal or metal oxide particles will exceed 200 ⁇ m.
• Amphoteric or acidic oxides are typically employed for this purpose.
• the term “acidic oxide” means an oxide which reacts with either an alkali or base to form a salt plus water.
• amphoteric oxide means an oxide which can display either acidic or basic character depending on the reactant which is reacted with it and/or upon the reaction conditions.
• the metal oxide may, for example, be selected from amphoteric oxides of Group III elements, preferably aluminium boron and gallium oxides, or zinc oxide and mixtures thereof.
• the metal oxide may for example be selected from acidic oxides of Group IV elements, preferably silicon, tin oxides and germanium oxides, or zirconium oxide and mixtures thereof. Mixtures of one or more amphoteric oxides with one or more amphoteric oxides may also be used.
• the oxide may alternatively be formed in situ as a result of adding the metal per se to the composition. Without wishing to be bound by theory, it is believed that the zinc or other metal oxide reacts with any residual silicate to reduce solubility of films formed by coating or otherwise applying the composition to substrates.
• the amount of the metal oxide or metal is 0.1% to 10%, preferably from 0.3% to 5% by weight (e.g. from 0.3% to 3% by weight) of the total composition.
• compositions of the first aspect of the invention preferably comprise from 0.1% to 10%, preferably from 0.3% to 5% (e.g. 0.3% to 4%) by weight of the organic liquid.
• the organic liquid has a boiling point (at atmospheric pressure) greater than 110° C.
• the organic liquid has a boiling point (at atmospheric pressure) of at least about 120° C., typically at least about 130° C. and typically up to about 500° C.
• the boiling point is no more than 500° C., preferably no more than 300° C.
• the organic liquid is desirably one which is stable under alkaline conditions, by which is meant that it can withstand storage in an aqueous composition of pH 9 or more, preferably pH 12 or more without significant chemical degradation (i.e. less than 1% loss by weight of the liquid by degradation at 25° C. for 30 days storage) and also stable with respect to oxidation, heat and light.
• the organic liquid is typically one having a viscosity of less than 5000 mPa ⁇ s, preferably less than 2000 mPa ⁇ s (e.g. less than 1000 mPa ⁇ s), at a temperature of 25° C. measured at a shear rate of 23 sec ⁇ 1 .
• the organic liquid may comprise one or more substantially water immiscible organic solvents selected from polyhydroxy alcohols, mineral oils, liquid paraffin oils, glycol ethers, silicone oils and mixtures thereof. Of these, silicone oils are especially preferred. It is preferred if the organic liquid is a silicone oil.
• Suitable silicone oils for use in compositions according to the present invention and precursor systems therefore are organosiloxanes, typically having the general formula (I):
• n is the number of repeating units in the polymer and can range from 2, e.g. from 10, up to 1,000,000, more preferably from 30, e.g. from 50, up to 500,000 and R 1 can be selected from hydrogen or methyl groups and R 2 can be selected from hydrogen or SiR 5 in which R 5 can be either hydrogen, hydroxyl or methyl and wherein R 3 and R 4 can be independently selected from C 1 to C 12 straight chain or branched, saturated or unsaturated alkyl, alkenyl or phenyl moieties or from units according to formula (I) above or from substituted alkyl or substituted phenyl moieties in which substituents can be halogens, amino groups, sulphate groups, sulphonate groups, carboxy groups, hydroxy groups or nitro groups.
• R 3 and R 4 are methyl groups.
• the silicone oils for use in the invention are free from halogen substituents.
• compositions according to any aspect of the present invention may beneficially be incorporated in compositions according to any aspect of the present invention, e.g. in amounts from 0.001% to 5%, such as 0.01% to 2% by weight of the composition for any or each class, and may for example be selected from any of the classes:—
• compositions according to the present invention may for example be applied to the substrate by means of a spray gun (optionally air or gas pressurised), a roller system or a brush system.
• a spray gun optionally air or gas pressurised
• the material to be treated may be coated or impregnated by immersion of the material in the coating composition while the coating composition is contained in a suitable vessel.
• compositions according to the present invention which are to be used as fire retardants may be applied to any appropriate flammable substrate but are especially suited to those which comprise an expanded or foamed polymer.
• that polymer is one which is substantially insoluble in the organic liquid at room temperature, i.e. the liquid component is selected with that requirement in mind.
• the composition may instead be applied to a substrate comprising one or more substances selected from wood, non-foamed polymer, metal, glass, ceramic, concrete, composite building material such as breezeblock, tile or brickwork, paper or china, or other vitreous ware.
• the composition of the invention is used to prepare fire retardant systems, it is preferred if the resulting system is substantially free of halogen-containing compounds, i.e. containing less than 1% by weight, preferably less than 0.5% by weight of such compounds.
• the moisture content of the resultant cured or dried composition film is no greater than 40%, more preferably no greater than 30%, still more preferably no greater than 25% and yet more preferably no greater than 20% by weight. Even more preferably, the moisture content of the dried composition is 17% by weight or less.
• the properties of the film resulting from the compositions of the invention may be improved by holding the composition at a temperature of 50° C. or more, while the composition is has a moisture content greater than 20% by weight, for at least 30 minutes.
• the properties of the film may be enhanced by applying onto the film a low melting point wax, such as for example micronized polyethylene wax (a low molecular weight polyethylene polymer that is oxidized or non-oxidized and because of its low molecular weight has wax-like physical characteristics) or a stearate, such as glycol stearate (for example glycol tristrearate) or a metal stearate (for example Zn, Ca, Na, Mg Stearate) or a combination of one or more waxes and one or more stearates.
• the wax, stearate or mixture thereof should preferably have a melting point from 60° C. to 150° C., more preferably from 80° C.
• Zinc Stearate with a melting point of 120-130° C. can be applied onto the film to serve as a lubrication agent to facilitate further processing of the coated film when applied to a polymeric material.
• Preferred coatings have a long term solubility of no greater than 25%, typically no greater than 20%, preferably no greater than 15%, and more preferably no greater than 10%, as determined by the water resistance/solubility methodology defined hereinafter, after oven drying the film at 80° C. to a water content of about 17% and then soaking in water at a temperature of about 22° C. for 7 days.
• Another aspect of the invention provides a method of coating, impregnating or otherwise applying to a substrate which is other than an article or part of an article being substantially formed only of foamed polymer, the method comprising coating, impregnating or applying to said substrate, a composition according to the first aspect of the present invention.
• sodium silicate solution (8.6% Na 2 O, 29% SiO 2 , balance water) was weighed directly into a plastic beaker. The silicate solution was vigorously stirred. To the vigorously stirred silicate solution, 40 grams of sodium aluminate solution (2.6% Na 2 O, 3.6% Al 2 O 3 ) was added dropwise over 3 to 4 minutes. After a further 10-20 seconds of mixing, stirring was stopped.
• Approximately 25 grams of the resultant clear aluminosilicate sol formed was accurately weighed and poured onto a preweighed flat circular ( ⁇ 10 centimetre in diameter) plastic dish.
• the aluminosilicate sol was allowed to set for about 5 minutes to form a gel network. All of the foregoing steps were carried out under room temperature conditions (about 22° C.).
• the coated dish was placed in an oven at 80° C. for 24 hours and the plastic and the dried contents were then weighed.
• the dried aluminosilicate formed was a continuous and strong circular shaped sheet with about 1 mm thickness and its solid content was 74% by weight (i.e. water content of 26% by weight).
• Example 2 The experiment of Example 1 was repeated but this time no aluminate solution was added and instead of the aluminate solution 37.5 grams of pure water was added. Once again, the resulting film (silicate only) was dried to a final moisture content of 26% by weight.
• the dried film is first broken into large (about 2 cm across) pieces. 2.0 g of the pieces are put in a SterelinTM jar and 28 g of water added. The pieces are fully submerged in the water and left to stand for 24 hours at ambient temperature (about 22° C.). The contents of the solution are analysed (using titration and gravimetric methods) and the solubility of the pieces after 24 hours soaking, is determined using the following formula:
• Example 1 The film formed in Example 1 was strong and clear. However, when such film was oven dried beyond 24 hours, it gradually started to form white patches and within 72 hours, it had turned to a weak and white flaky/powdery material.
• the dried film made according to Example 1 had a moisture content of 26%. When this film was soaked for 24 hours, it remained fairly intact. However, when the soaking in water was extended to 3 and then to 7 days, the solubility of the film increased proportionally. Reducing the moisture content of the film by for example prolonging drying time, would have minimised its water solubility. However, this is not an option for a film produced according to Example 1 as prolonged drying to minimise its moisture content, will result in weak and powdery film. However, the films made according to Example 3 and containing silicone oil had no such problem, and thus the silicone-oil-containing film of Example 3 using the 50 mPa ⁇ s silicone oil was dried to longer times to generate films with different moisture contents. The effect of film moisture content on the solubility of such film was conducted and the results are given below:
• the aluminosilicate film (with moisture content of 17%) made according to Example 4 and soaked for 7 days has good water resistance. However, when the same film is soaked for more than 7 days, for example 10 and 25 days, its water resistance decreases with increased soaking time.
• Example 4 was repeated but 1 gram of zinc oxide was added to and thereby suspended in the silicate and silicone oil mixture.
• the solubility of films made according to Examples 4 and 5 were assessed using the methodology defined hereinbefore using soaking times of 7, 10 and 25 days. The following results were obtained:

Landscapes

• Chemical & Material Sciences (AREA)
• Engineering & Computer Science (AREA)
• Materials Engineering (AREA)
• Organic Chemistry (AREA)
• Ceramic Engineering (AREA)
• Health & Medical Sciences (AREA)
• Chemical Kinetics & Catalysis (AREA)
• Medicinal Chemistry (AREA)
• Polymers & Plastics (AREA)
• Wood Science & Technology (AREA)
• Life Sciences & Earth Sciences (AREA)
• Structural Engineering (AREA)
• Inorganic Chemistry (AREA)
• Paints Or Removers (AREA)
• Application Of Or Painting With Fluid Materials (AREA)
• Compositions Of Macromolecular Compounds (AREA)
• Laminated Bodies (AREA)
• Manufacture Of Porous Articles, And Recovery And Treatment Of Waste Products (AREA)
• Processing And Handling Of Plastics And Other Materials For Molding In General (AREA)
• Adhesives Or Adhesive Processes (AREA)
• Silicates, Zeolites, And Molecular Sieves (AREA)
• Fireproofing Substances (AREA)
• Lubricants (AREA)
• Building Environments (AREA)

Applications Claiming Priority (5)

Publications (1)

Family

ID=37683695

Family Applications (2)

Family Applications After (1)

Country Status (14)

Cited By (5)

Families Citing this family (13)

Citations (9)

Family Cites Families (22)

• 2006
  • 2006-07-24 RU RU2008106923/15A patent/RU2008106923A/ru not_active Application Discontinuation
  • 2006-07-24 JP JP2008523442A patent/JP2009507940A/ja active Pending
  • 2006-07-24 KR KR1020087002046A patent/KR20080028967A/ko not_active Application Discontinuation
  • 2006-07-24 MX MX2008001242A patent/MX2008001242A/es active IP Right Grant
  • 2006-07-24 US US11/996,718 patent/US20090000518A1/en not_active Abandoned
  • 2006-07-24 US US11/996,763 patent/US7998570B2/en not_active Expired - Fee Related
  • 2006-07-24 AU AU2006273817A patent/AU2006273817A1/en not_active Abandoned
  • 2006-07-24 KR KR1020087001959A patent/KR20080037660A/ko not_active Application Discontinuation
  • 2006-07-24 WO PCT/EP2006/007264 patent/WO2007012441A2/en active Application Filing
  • 2006-07-24 CA CA002616339A patent/CA2616339A1/en not_active Abandoned
  • 2006-07-24 WO PCT/GB2006/002760 patent/WO2007012832A2/en active Application Filing
  • 2006-07-24 PT PT06776375T patent/PT1907461E/pt unknown
  • 2006-07-24 EP EP06776375A patent/EP1907461B1/en not_active Not-in-force
  • 2006-07-24 RU RU2008106948/04A patent/RU2414489C2/ru not_active IP Right Cessation
  • 2006-07-24 JP JP2008523208A patent/JP5207967B2/ja not_active Expired - Fee Related
  • 2006-07-24 CN CN2006800326372A patent/CN101258192B/zh not_active Expired - Fee Related
  • 2006-07-24 AU AU2006274265A patent/AU2006274265B2/en not_active Ceased
  • 2006-07-24 DK DK06776375.5T patent/DK1907461T3/da active
  • 2006-07-24 MX MX2008001169A patent/MX2008001169A/es unknown
  • 2006-07-24 EP EP06765087A patent/EP1907322A2/en not_active Withdrawn
  • 2006-07-24 AT AT06776375T patent/ATE523553T1/de not_active IP Right Cessation
  • 2006-07-24 BR BRPI0613989-2A patent/BRPI0613989A2/pt not_active IP Right Cessation
  • 2006-07-24 BR BRPI0614160A patent/BRPI0614160A2/pt not_active IP Right Cessation
  • 2006-07-24 CA CA002615971A patent/CA2615971A1/en not_active Abandoned

Patent Citations (9)

Also Published As

Similar Documents

Legal Events