US20060278323A1 - Holding and sealing material and manufacturing method thereof - Google Patents
Holding and sealing material and manufacturing method thereof Download PDFInfo
- Publication number
- US20060278323A1 US20060278323A1 US11/444,484 US44448406A US2006278323A1 US 20060278323 A1 US20060278323 A1 US 20060278323A1 US 44448406 A US44448406 A US 44448406A US 2006278323 A1 US2006278323 A1 US 2006278323A1
- Authority
- US
- United States
- Prior art keywords
- holding
- organic binder
- sealing material
- mat
- emulsion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Links
Images
Classifications
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01D—SEPARATION
- B01D53/00—Separation of gases or vapours; Recovering vapours of volatile solvents from gases; Chemical or biological purification of waste gases, e.g. engine exhaust gases, smoke, fumes, flue gases, aerosols
- B01D53/34—Chemical or biological purification of waste gases
- B01D53/92—Chemical or biological purification of waste gases of engine exhaust gases
- B01D53/94—Chemical or biological purification of waste gases of engine exhaust gases by catalytic processes
- B01D53/9445—Simultaneously removing carbon monoxide, hydrocarbons or nitrogen oxides making use of three-way catalysts [TWC] or four-way-catalysts [FWC]
- B01D53/9454—Simultaneously removing carbon monoxide, hydrocarbons or nitrogen oxides making use of three-way catalysts [TWC] or four-way-catalysts [FWC] characterised by a specific device
-
- F—MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
- F01—MACHINES OR ENGINES IN GENERAL; ENGINE PLANTS IN GENERAL; STEAM ENGINES
- F01N—GAS-FLOW SILENCERS OR EXHAUST APPARATUS FOR MACHINES OR ENGINES IN GENERAL; GAS-FLOW SILENCERS OR EXHAUST APPARATUS FOR INTERNAL COMBUSTION ENGINES
- F01N3/00—Exhaust or silencing apparatus having means for purifying, rendering innocuous, or otherwise treating exhaust
- F01N3/08—Exhaust or silencing apparatus having means for purifying, rendering innocuous, or otherwise treating exhaust for rendering innocuous
- F01N3/10—Exhaust or silencing apparatus having means for purifying, rendering innocuous, or otherwise treating exhaust for rendering innocuous by thermal or catalytic conversion of noxious components of exhaust
- F01N3/24—Exhaust or silencing apparatus having means for purifying, rendering innocuous, or otherwise treating exhaust for rendering innocuous by thermal or catalytic conversion of noxious components of exhaust characterised by constructional aspects of converting apparatus
- F01N3/28—Construction of catalytic reactors
-
- F—MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
- F01—MACHINES OR ENGINES IN GENERAL; ENGINE PLANTS IN GENERAL; STEAM ENGINES
- F01N—GAS-FLOW SILENCERS OR EXHAUST APPARATUS FOR MACHINES OR ENGINES IN GENERAL; GAS-FLOW SILENCERS OR EXHAUST APPARATUS FOR INTERNAL COMBUSTION ENGINES
- F01N3/00—Exhaust or silencing apparatus having means for purifying, rendering innocuous, or otherwise treating exhaust
- F01N3/08—Exhaust or silencing apparatus having means for purifying, rendering innocuous, or otherwise treating exhaust for rendering innocuous
- F01N3/10—Exhaust or silencing apparatus having means for purifying, rendering innocuous, or otherwise treating exhaust for rendering innocuous by thermal or catalytic conversion of noxious components of exhaust
- F01N3/18—Exhaust or silencing apparatus having means for purifying, rendering innocuous, or otherwise treating exhaust for rendering innocuous by thermal or catalytic conversion of noxious components of exhaust characterised by methods of operation; Control
- F01N3/20—Exhaust or silencing apparatus having means for purifying, rendering innocuous, or otherwise treating exhaust for rendering innocuous by thermal or catalytic conversion of noxious components of exhaust characterised by methods of operation; Control specially adapted for catalytic conversion ; Methods of operation or control of catalytic converters
-
- F—MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
- F01—MACHINES OR ENGINES IN GENERAL; ENGINE PLANTS IN GENERAL; STEAM ENGINES
- F01N—GAS-FLOW SILENCERS OR EXHAUST APPARATUS FOR MACHINES OR ENGINES IN GENERAL; GAS-FLOW SILENCERS OR EXHAUST APPARATUS FOR INTERNAL COMBUSTION ENGINES
- F01N3/00—Exhaust or silencing apparatus having means for purifying, rendering innocuous, or otherwise treating exhaust
- F01N3/08—Exhaust or silencing apparatus having means for purifying, rendering innocuous, or otherwise treating exhaust for rendering innocuous
- F01N3/10—Exhaust or silencing apparatus having means for purifying, rendering innocuous, or otherwise treating exhaust for rendering innocuous by thermal or catalytic conversion of noxious components of exhaust
- F01N3/24—Exhaust or silencing apparatus having means for purifying, rendering innocuous, or otherwise treating exhaust for rendering innocuous by thermal or catalytic conversion of noxious components of exhaust characterised by constructional aspects of converting apparatus
-
- F—MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
- F01—MACHINES OR ENGINES IN GENERAL; ENGINE PLANTS IN GENERAL; STEAM ENGINES
- F01N—GAS-FLOW SILENCERS OR EXHAUST APPARATUS FOR MACHINES OR ENGINES IN GENERAL; GAS-FLOW SILENCERS OR EXHAUST APPARATUS FOR INTERNAL COMBUSTION ENGINES
- F01N3/00—Exhaust or silencing apparatus having means for purifying, rendering innocuous, or otherwise treating exhaust
- F01N3/08—Exhaust or silencing apparatus having means for purifying, rendering innocuous, or otherwise treating exhaust for rendering innocuous
- F01N3/10—Exhaust or silencing apparatus having means for purifying, rendering innocuous, or otherwise treating exhaust for rendering innocuous by thermal or catalytic conversion of noxious components of exhaust
- F01N3/24—Exhaust or silencing apparatus having means for purifying, rendering innocuous, or otherwise treating exhaust for rendering innocuous by thermal or catalytic conversion of noxious components of exhaust characterised by constructional aspects of converting apparatus
- F01N3/28—Construction of catalytic reactors
- F01N3/2839—Arrangements for mounting catalyst support in housing, e.g. with means for compensating thermal expansion or vibration
- F01N3/2853—Arrangements for mounting catalyst support in housing, e.g. with means for compensating thermal expansion or vibration using mats or gaskets between catalyst body and housing
-
- Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y02—TECHNOLOGIES OR APPLICATIONS FOR MITIGATION OR ADAPTATION AGAINST CLIMATE CHANGE
- Y02T—CLIMATE CHANGE MITIGATION TECHNOLOGIES RELATED TO TRANSPORTATION
- Y02T10/00—Road transport of goods or passengers
- Y02T10/10—Internal combustion engine [ICE] based vehicles
- Y02T10/12—Improving ICE efficiencies
-
- Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
- Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
- Y10T29/00—Metal working
- Y10T29/49—Method of mechanical manufacture
- Y10T29/49345—Catalytic device making
-
- Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
- Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
- Y10T428/00—Stock material or miscellaneous articles
- Y10T428/249921—Web or sheet containing structurally defined element or component
- Y10T428/249953—Composite having voids in a component [e.g., porous, cellular, etc.]
- Y10T428/249962—Void-containing component has a continuous matrix of fibers only [e.g., porous paper, etc.]
- Y10T428/249964—Fibers of defined composition
-
- Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
- Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
- Y10T442/00—Fabric [woven, knitted, or nonwoven textile or cloth, etc.]
- Y10T442/20—Coated or impregnated woven, knit, or nonwoven fabric which is not [a] associated with another preformed layer or fiber layer or, [b] with respect to woven and knit, characterized, respectively, by a particular or differential weave or knit, wherein the coating or impregnation is neither a foamed material nor a free metal or alloy layer
- Y10T442/2926—Coated or impregnated inorganic fiber fabric
Definitions
- the present invention relates to a holding and sealing material of a catalytic converter for purifying an exhaust gas discharged from an internal combustion engine or the like.
- a catalytic converter 90 for purifying an exhaust gas has been used for purifying an exhaust gas discharged from an internal combustion engine 92 or the like.
- the catalytic converter 90 has a catalyst carrier 1 , a shell 95 made of metal and covering the outside of the catalyst carrier, and a holding and sealing material 91 which is set between the both.
- the holding and sealing material 91 can prevent the exhaust gas from leaking out from between the catalyst carrier 1 and the shell 95 , and also, it can prevent the catalyst carrier 1 from damage in contact with the shell 95 .
- the holding and sealing material 91 is wound around the catalyst carrier 1 , and the wound unit is set within the shell 95 . Then, an inlet connection 97 and an outlet connection 98 are respectively connected to both ends of the shell 95 by welding.
- the catalytic converter 90 manufactured in the manner mentioned above is set in the middle of a pipe 99 for an exhaust gas discharged from the engine 92 .
- the holding and sealing material 91 As the holding and sealing material 91 , the material made by infiltrating a mat-like material 911 made of alumina-silica based ceramic fibers (inorganic fibers) or the like with an organic binder 912 has been used. Because the holding and sealing material 91 is an aggregate of filaments and its specific gravity is small, there is a risk that a part of the inorganic fibers flies in all directions in the air from a surface of the holding and sealing material 91 at a time of manufacturing the catalytic converter 90 by mounting the holding and sealing material 91 in the catalyst carrier 1 and the shell 95 ,. Therefore, there is a risk of deteriorating a working environment of a working area for the mounting work, and it is necessary for a worker to work with wearing an antidust mask or the like.
- alumina fibers aggregate whose average fiber diameter and minimum fiber diameter are controlled to specific range has been developed so far (refer to Patent document 1).
- the alumina fibers aggregate is assembled to the catalyst carrier 1 and the shell 95 as the holding and sealing material 91 , it is possible to reduce a flying amount of inorganic fibers (alumina).
- a manufacturing method of a holding and sealing material which is configured to be set between a catalyst carrier and a shell covering the outside of the catalyst carrier in a catalytic converter for purifying an exhaust gas comprising:
- a infiltrating step for infiltrating a mat-like material formed by arranging inorganic fibers in a mat shape with emulsion made by dispersing a organic binder into water;
- a drying step for attaching the organic binder to the mat-like material by means of drying the mat-like material containing the emulsion and obtaining the holding and sealing material
- the organic binder has a glass transition point Tg (° C.) of less than or equal to approximately 5° C.
- the infiltrating step and the drying step are conducted as described above.
- the mat-like material formed by arranging inorganic fibers in a mat shape is infiltrated with emulsion made by dispersing the organic binder into water.
- the drying step by drying the mat-like material containing the emulsion, liquid ingredient in the emulsion is evaporated.
- the organic binder is attached to a surface and inside and the like of the mat-like material, and the holding and sealing material is obtained.
- an organic binder with a low glass transition point Tg (° C.) of less than or equal to 5° C. is used as the organic fiber. Therefore, the organic binder attached to the holding and sealing material can exhibit high motility rubbery state at room temperature (e.g. temperature which is equal to or more than glass transition point of the organic binder). Accordingly, at a time of mounting the holding and sealing material in the catalyst carrier and the shell, the organic binder can combine the inorganic fibers each other of the mat-like material and also can exhibit excellent extensity, and it is possible to absorb damage such as a shock or the like given to the holding and sealing material.
- Tg glass transition point
- the organic binder can suppress a break of the inorganic fibers of the mat-like material and can hold the inorganic fibers. Therefore, the holding and sealing material can prevent the inorganic fibers from flying in all directions without increasing an amount of an inorganic binder.
- a holding and sealing material which is configured to be set between a catalyst carrier and a shell covering the outside of the catalyst carrier in a catalytic converter for purifying an exhaust gas comprising:
- the organic binder with the glass transition point Tg (° C.) of less than or equal to approximately 5° C. is attached to the mat-like material.
- FIG. 1 is a perspective view which shows a state of mounting a holding and sealing material in a catalyst carrier and a shell, in accordance with an embodiment 1;
- FIG. 2 is an explanatory drawing which shows a state of setting a catalytic converter for purifying an exhaust gas built-in a holding and sealing material in the middle of the exhaust pipe of the engine, in accordance with the embodiment 1 ;
- FIG. 3 is an explanatory drawing which (A) shows a state prior to winding the holding and sealing material around the catalyst carrier and (B) shows a state of winding the holding and sealing material around the catalyst carrier, in accordance with the embodiment 1;
- FIG. 4 is an explanatory drawing which shows a state of setting a unit formed by winding the holding and sealing material around the catalyst carrier within the shell, in accordance with the embodiment 1;
- FIG. 5 is an explanatory drawing which shows a state of setting a conventional catalytic converter for purifying an exhaust gas assembled in the middle of the exhaust pipe of the engine.
- the holding and sealing material can be manufactured.
- the mat-like material formed by arranging inorganic fibers in a mat shape is infiltrated with emulsion made by dispersing the organic binder into water.
- the one with the glass transition point Tg (° C.) of less than or equal to approximately 5° C. is employed.
- the glass transition point Tg (° C.) exceeds approximately 5° C., it is impossible that the organic binder adequately suppresses a break of the inorganic fibers of the mat-like material at a time of mounting the holding and sealing material, and there is a risk that a part of the inorganic fibers flies in all directions in the air while at assembling work.
- the glass transition point Tg (° C.) of the organic binder is equal to or more than approximately ⁇ 20° C.
- the organic binder is hardly to exude outside from the holding and sealing material at the mounting work, and there is almost no risk that the working environment around the mounting jig or the like is polluted by the organic binder.
- the organic binder is a rubber on which is not conducted a crosslinking process.
- the organic binder in the infiltrating step, is easy to adapt to a surface of the mat-like material, and it is possible to equally infiltrate a surface of the inorganic fibers of the mat-like material with the emulsion. Accordingly, in the drying step, the organic binder is attached almost equally on the surface or inside of the mat-like material, it is possible to suppress a flying ratio more of the inorganic fibers from the holding and sealing material.
- organic binder for example, acrylic based rubber, styrene-butadiene rubber (SBR), acrylate based rubber, methacrylate based rubber or the like can be employed.
- SBR styrene-butadiene rubber
- acrylate based rubber methacrylate based rubber or the like
- the organic binder is an acrylate based rubber or a methacrylate based rubber.
- the organic binder is more equally attached on the surface or the like of the inorganic fibers of mat-like material.
- the elongation of the organic binder becomes better after the drying step, and it is possible to prevent the fibers from being tied up constrainedly. Therefore, it is possible to prevent the inorganic fibers from breaking at a time of mounting in the catalyst carrier and the shell, and to prevent the inorganic fibers from flying in all directions further.
- the emulsion has a surface tension of less than or equal to approximately 60 mN/M at the room temperature.
- a surface tension of the emulsion is less than or equal to approximately 60 mN/M, the emulsion is easy to adapt to a surface of the mat-like material, and thus, organic binder is easily to be attached equally in the mat-like material.
- surface tension of the emulsion should be equal to or more than approximately 20 mN/m.
- the emulsion with less than or equal to approximately 60 mN/m of surface tension can be manufactured by, for example, using rubber on which is not conducted a crosslinking process as described above.
- Surface tension of the emulsion can be measured, for example, by a ring method.
- the emulsion has an emulsion particle diameter of less than or equal to approximately 300 nm.
- the emulsion particle diameter is less than or equal to approximately 300 nm, in the infiltrating step, it is easy to infiltrate the surface of the mat-like material with the emulsion. More preferably, the emulsion particle diameter is not greater than approximately 150 nm, and much more preferably, not greater than approximately 100 nm.
- the the emulsion particle diameter can be measured by evaluating average value of the particle diameter of, for example, 100 pieces of the emulsion by measured by using a transmission electron microscope.
- the drying step by drying the mat-like material containing the emulsion, the organic binder is attached to the mat-like material and then the holding and sealing material is manufactured.
- the mat-like material containing the emulsion is dried with heating and pressing.
- the drying step is conducted under the temperature between approximately 95 to 155° C.
- the drying temperature is equal to or greater than 95° C., there is almost no risk that the drying time gets longer and manufacturing efficiency decreases. On the other hand, in the case the drying temperature is lower than or equal to 155° C., there is almost no risk that dissolution of the organic binder starts and the adhesion property of the organic binder is spoiled. In addition, it is preferable that the drying time is equal to or more than 100 minutes. If the drying time is more than 100 minutes, enough drying is performed easily.
- compression is performed under the compression interval of 4 to 15 mm.
- the compression interval is equal to or longer than approximately 4 mm, damage of the inorganic fibers hardly occurs.
- the compression interval is smaller than or equal to approximately 15 mm, it is easy to obtain the above described effect by the compression sufficiently.
- crosslinking reaction of the organic binder can be proceeded by heating at the drying step.
- the crosslinking reaction is too proceeded, there is a risk that extensity of the organic binder is spoiled. Therefore, in the drying step, it is preferable to making the crosslinking degree of the organic binder lower than or equal to approximately 70%. Since the crosslinking degree of the organic binder is varies, for example, by composition or the like of the organic binder, the organic binder whose final the crosslinking degree after the drying step is less than or equal to approximately 70% can be chosen.
- the crosslinking degree of the organic binder can be measured, for example, by gel content measurement method.
- attached ratio of the organic binder in the holding and sealing material is preferably in the range of 0.5 wt % to 1.5 wt %.
- the attached ratio is equal to or more than approximately 0.5 wt %, it is easy to prevent the inorganic fibers fully from flying in all directions from a surface of the holding and sealing material.
- the attached ratio is less than or equal to approximately 1.5 wt %, amount of the organic binder increases, and there is almost no risk that the poisonous gas such as nonmethane hydrocarbons, nitrogen oxide or the like might be occurred from the holding and sealing material.
- a solid content removal step for removing extra solid content of the organic binder attached in the mat-like material.
- a solid content removal step can be conducted, for example, by suction or the like.
- the holding and sealing material is comprised by attaching the organic binder into the mat-like material which is formed by arranging the inorganic fibers in a mat shape.
- the material similar to the one in the first aspect of the present invention can be used.
- the one with a glass transition point Tg (° C.) of less than or equal to 5° C. is employed.
- the reason for the critical point is similar to the one in the first aspect of the present invention and it is preferable that the glass transition Tg of the organic binder is equal to or more than ⁇ 20° C.
- organic binder as same as the first aspect of the present invention, for example, acrylic based rubber, styrene-butadiene rubber (SBR), acrylate based rubber, methacrylate based rubber or the like can be employed.
- SBR styrene-butadiene rubber
- acrylate based rubber methacrylate based rubber or the like
- the organic binder is an acrylate based rubber or a methacrylate based rubber.
- the elongation of the organic binder becomes better and it is possible to prevent the fibers from being tied up constrainedly. Therefore, it is possible to prevent the inorganic fibers from breaking at a time of mounting in the catalyst carrier and the shell, and to prevent the inorganic fibers from flying in all directions further.
- a flying ratio of the inorganic fibers is less than or equal to 0.15 wt %.
- a flying ratio of the inorganic fibers is more preferably less than or equal to 0.10 wt %.
- the flying ratio of the inorganic fibers can be defined by a pace of decrease of weight when a device according to Japanese Industrial Standards K6830-1996-26 low temperature resistant test•26.2 test device (4) impact testing machine is used.
- the crosslinking degree of the organic binder attached in the holding and sealing material is less than or equal to approximately 70%.
- crosslinking degree is less than or equal to approximately 70%, extensity of the organic binder is lowered and there is almost no risk that the prevention effect for the flying of the inorganic fibers from the holding and sealing material is reduced.
- FIG. 1 to FIG. 4 the holding and sealing material relates to the embodiment in the present invention is explained with FIG. 1 to FIG. 4 .
- the holding and sealing material 2 of the present embodiment is used as being disposed on between the catalyst carrier 1 and the shell 95 which covers outer of the catalyst carrier 1 in the catalytic converter for purifying an exhaust gas 10 .
- the mat-like material is formed by arranging the inorganic fibers in mat shape, and the organic binder 22 with the glass transition point Tg (° C.) of less than or equal to 5° C. is attached to the mat-like material 21 (refer to FIGS. 3 (A) and (B)).
- the catalyst carrier 1 As the catalyst carrier 1 , a cordierite carrier whose a transverse sectional surface is formed in a honeycomb shape. A lot of rectangular holes 11 are provided along an axial direction in this catalyst carrier 1 . Further, a lot of honeycomb walls 12 which is the partition walls of the rectangular holes 11 are formed between the rectangular holes 11 (refer to FIG. 1 ). Further, a catalyst mainly composed of a platinum or a palladium is supported on the catalyst carrier 1 .
- inorganic fibers constituting the mat-like material 21 crystalline alumina fibers which is non-expansible fibers arranged so as not to expand so much by heat.
- the infiltrating step and the drying step are conducted.
- the infiltrating step the emulsion made by dispersing the organic binder 22 into water is infiltrated into the mat-like material 21 formed by arranging inorganic fibers in a mat shape.
- the drying step the holding and sealing material 2 is obtained by attaching the organic binder 22 to the mat-like material 21 by means of drying the mat-like material 21 containing the emulsion.
- the organic binder the one with a glass transition point Tg (° C.) of less than or equal to 5° C. is used.
- a solid content removal step for removing extra solid content of the organic binder 22 attached in the mat-like material 21 is conducted in between the infiltrating step and the drying step.
- the mat-like material 21 with dimensions of lengthwise 500 to 1400 mm ⁇ crosswise 51,000 to 52,500 mm, and thickness 1.5 to 12 m was prepared.
- the mat-like material 21 was infiltrated with the emulsion containing the organic binder.
- acrylonitrile-butadiene copolymer latex (the emulsion particle diameter: 50 nm, the glass transition point of the organic binder: ⁇ 21° C., the density of the organic binder: 1 wt %) made by dispersing acrylonitrile-butadiene copolymer rubber to water was prepared.
- This emulsion was infiltrated by pouring method into the mat-like material 21 set on the conveyer.
- suction for equal to or more than 1 minute was conducted to remove solid content of the extra organic binder attaching to the mat-like material 21 .
- the suction when the impregnated rate of the emulsion was measured by weighing instrument, the emulsion 22 of 100 parts by weight was impregnated against the mat-like material 21 of 100 parts by weight.
- Heating, compressing, and drying of the mat-like material 21 was conducted. Heating, compressing, and drying was conducted under the condition of temperature of 95 to 155° C., drying time of equal to or more than 100 minutes, and interval pressurisation at the time of drying of 4 to 15 mm.
- the holding and sealing material 2 with the attached rate of the organic binder of 1.0 wt % and thickness of 3 to 15 mm was obtained.
- the catalyst was supported on the catalyst carrier 1 in advance.
- the holding and sealing material 2 was wound (refer to FIGS. 3 (A) and (B)) onto the catalyst carrier 1 and the wound unit 20 was set into the inside of the shell 95 (refer to FIG. 4 ).
- mounting of the holding and sealing material 2 was conducted, an inlet connection 97 and an outlet connection 98 were respectively connected to the both ends of the shell 95 by welding (refer to FIG. 2 ).
- the catalytic converter for purifying an exhaust gas 10 manufactured by this means can be used by setting in the midstream of a pipe for exhaust gas discharged by an engine.
- the one with glass transition point Tg (° C.) of less than or equal to 5° C. is used (refer to FIG. 1 ).
- the organic binder 22 attached to the holding and sealing material 2 can exhibit the rubber state with high motility at room temperature.
- the organic binder exhibits an excellent extensity and making it possible to absorb damages such as impacts or the like given to the inorganic fibers of the holding and sealing material 2 .
- the workers can comfortably work without wearing the antidust mask or the like and it is possible to keep the working environment of working area for the amounting work good.
- a drop test was conducted as described below in order to make sure of difficulty of flying the inorganic fibers contained in the holding and sealing material in all directions in the air.
- a plural number of holding and sealing materials (sample E 1 to sample E 4 , sample C 1 to sample C 4 ) was manufactured by using the emulsion containing the organic binders having different glass transition point (Tg). And then, they were dropped from the specific height and difficulty of flying the inorganic fibers in all directions in the air at this time was evaluated.
- Sample E 1 was manufactured by infiltrating with acrylonitrile-butadiene copolymer latex (the glass transition point Tg of the organic binder: ⁇ 21° C., the emulsion particle diameter: 50 nm, the density of the organic binder: about 1 wt %) made by dispersing acrylonitrile-butadiene copolymer rubber into water as the emulsion, and then, by conducting suction, heating, compressing, and drying as well as embodiment 1.
- the holding and sealing material in sample E 1 is the same as the one in embodiment 1.
- Sample E 2 was manufactured by infiltrating with denatured acrylic ester copolymer latex (the glass transition point Tg of the organic binder: ⁇ 5° C., the emulsion particle diameter: 80 nm, the density of the organic binder: about 1 wt %) made by dispersing denatured acrylic ester copolymer rubber into water as the emulsion, and then, by conducting suction, heating, compressing, and drying as well as embodiment 1.
- denatured acrylic ester copolymer latex the glass transition point Tg of the organic binder: ⁇ 5° C., the emulsion particle diameter: 80 nm, the density of the organic binder: about 1 wt %
- sample E 3 is manufactured by infiltrating with denatured acrylic ester copolymer latex (the glass transition point Tg of the organic binder: 1° C., the emulsion particle diameter: 110 nm, the density of the organic binder: about 1 wt %), and then, by conducting suction, heating, compressing, and drying as well as embodiment 1.
- denatured acrylic ester copolymer latex the glass transition point Tg of the organic binder: 1° C., the emulsion particle diameter: 110 nm, the density of the organic binder: about 1 wt %
- sample E 4 is manufactured by infiltrating with denatured acrylic ester copolymer latex (the glass transition point Tg of the organic binder: ⁇ 10° C., the emulsion particle diameter: 260 nm, the density of the organic binder: about 1 wt %), and then, by conducting suction, heating, compressing, and drying as well as embodiment 1.
- denatured acrylic ester copolymer latex the glass transition point Tg of the organic binder: ⁇ 10° C., the emulsion particle diameter: 260 nm, the density of the organic binder: about 1 wt %
- sample C 1 is manufactured by infiltrating with acrylonitrile-butadiene-styrene three dimension copolymer latex (the glass transition point Tg of the organic binder: 26° C., the emulsion particle diameter: 40 nm, the density of the organic binder: about 1 wt %) made by dispersing acrylonitrile-butadiene-styrene three dimension copolymer rubber into water as the emulsion, and then, by conducting suction, heating, compressing, and drying as well as embodiment 1.
- acrylonitrile-butadiene-styrene three dimension copolymer latex the glass transition point Tg of the organic binder: 26° C., the emulsion particle diameter: 40 nm, the density of the organic binder: about 1 wt % made by dispersing acrylonitrile-butadiene-styrene three dimension copolymer rubber into water as the emulsion, and then, by conducting suction,
- sample C 2 is manufactured by infiltrating with denatured styrene-butadiene copolymer latex (glass transition point Tg of the organic binder: 12° C., the emulsion particle diameter: 80 nm, density of the organic binder: about 1 wt %) made by dispersing denatured styrene-butadiene copolymer rubber into water as the emulsion, and then, by conducting suction, heating, compressing, and drying as well as embodiment 1.
- denatured styrene-butadiene copolymer latex glass transition point Tg of the organic binder: 12° C., the emulsion particle diameter: 80 nm, density of the organic binder: about 1 wt % made by dispersing denatured styrene-butadiene copolymer rubber into water as the emulsion, and then, by conducting suction, heating, compressing, and drying as well as embodiment 1.
- sample C 3 is manufactured by infiltrating with denatured styrene-butadiene copolymer latex (glass transition point Tg of the organic binder: 20° C., the emulsion particle diameter: 160 nm, density of the organic binder: about 1 wt %), and then, by conducting suction, heating, compressing, and drying as well as embodiment 1.
- sample C 4 is manufactured by infiltrating with denatured acrylic ester copolymer latex (the glass transition point Tg of the organic binder: 25° C., the emulsion particle diameter: 110 nm, the density of the organic binder: about 1 wt %), and then, by conducting suction, heating, compressing, and drying as well as embodiment 1.
- denatured acrylic ester copolymer latex the glass transition point Tg of the organic binder: 25° C., the emulsion particle diameter: 110 nm, the density of the organic binder: about 1 wt %
- the organic binder of approximately 1.0 wt % was attached to the mat-like material as is the case with the embodiment 2.
- the holding and sealing material of sample E 1 to sample E 4 manufactured by using the emulsion containing the organic binder with low glass transition point Tg shows very low flying ratio of more than 0.116 wt % at the maximum.
- the holding and sealing material of sample C 1 to sample C 4 manufactured by using the emulsion containing the organic binder with high glass transition point Tg shows high flying ratio. This is because the organic binder shows the rubber state with high motility at room temperature and exhibits excellent extensity, and impacts given to the inorganic fibers of the holding and sealing material can be sufficiently absorbed in the sample E 1 to sample E 4 .
- sample E 1 to sample E 4 and sample C 1 to sample C 4 small amount of about 1.0 wt % of the organic binder is attached.
- Sample E 1 to sample E 4 can exhibits low flying ratio as described above even if such as a small amount of the organic binder is used. Accordingly, sample E 1 to sample E 4 is safe for the environment and it is possible to sufficiently prevent the inorganic fibers from flying in all directions at the time of handling.
- JP 2003-105658 and Japanese Industrial Standards K6830-1996•26 are incorporated herein by reference.
Landscapes
- Chemical & Material Sciences (AREA)
- Engineering & Computer Science (AREA)
- Chemical Kinetics & Catalysis (AREA)
- Health & Medical Sciences (AREA)
- Combustion & Propulsion (AREA)
- Toxicology (AREA)
- Mechanical Engineering (AREA)
- General Engineering & Computer Science (AREA)
- Biomedical Technology (AREA)
- Environmental & Geological Engineering (AREA)
- Analytical Chemistry (AREA)
- General Chemical & Material Sciences (AREA)
- Oil, Petroleum & Natural Gas (AREA)
- Exhaust Gas After Treatment (AREA)
- Catalysts (AREA)
- Treatments For Attaching Organic Compounds To Fibrous Goods (AREA)
Priority Applications (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
US12/257,459 US8533950B2 (en) | 2005-06-10 | 2008-10-24 | Method of manufacturing holding and sealing material |
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
JP2005171221A JP4665618B2 (ja) | 2005-06-10 | 2005-06-10 | 保持シール材の製造方法 |
JP2005-171221 | 2005-06-10 |
Related Child Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
US12/257,459 Division US8533950B2 (en) | 2005-06-10 | 2008-10-24 | Method of manufacturing holding and sealing material |
Publications (1)
Publication Number | Publication Date |
---|---|
US20060278323A1 true US20060278323A1 (en) | 2006-12-14 |
Family
ID=36997899
Family Applications (2)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
US11/444,484 Abandoned US20060278323A1 (en) | 2005-06-10 | 2006-06-01 | Holding and sealing material and manufacturing method thereof |
US12/257,459 Active 2027-06-15 US8533950B2 (en) | 2005-06-10 | 2008-10-24 | Method of manufacturing holding and sealing material |
Family Applications After (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
US12/257,459 Active 2027-06-15 US8533950B2 (en) | 2005-06-10 | 2008-10-24 | Method of manufacturing holding and sealing material |
Country Status (5)
Country | Link |
---|---|
US (2) | US20060278323A1 (ko) |
EP (1) | EP1731729B2 (ko) |
JP (1) | JP4665618B2 (ko) |
KR (1) | KR100762116B1 (ko) |
CN (1) | CN1876748B (ko) |
Cited By (30)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US20030049180A1 (en) * | 2000-03-22 | 2003-03-13 | Koji Fukushima | Catalyst converter and diesel, particulate filter system |
US20040022699A1 (en) * | 2000-11-10 | 2004-02-05 | Koji Fukushima | Catalytic converter and method for manufacture thereof |
US20040052694A1 (en) * | 2000-10-17 | 2004-03-18 | Yoshio Nishikawa | Holding seal material for catalytic converter and method of manufacturing the holding and seal material |
US20090041967A1 (en) * | 2007-08-10 | 2009-02-12 | Nichias Corporation | Holding material for catalytic converter |
US20090075812A1 (en) * | 2001-05-25 | 2009-03-19 | Ibiden Co., Ltd | Alumina-silica-based fiber, ceramic fiber, ceramic fiber complex, retaining seal material, production method thereof, and alumina fiber complex production method |
US20090081455A1 (en) * | 2007-09-26 | 2009-03-26 | Ibiden Co., Ltd. | Inorganic fiber mat, holding sealer, sound absorber, and method for manufacturing inorganic fiber mat |
EP2042636A1 (en) * | 2007-09-28 | 2009-04-01 | Ibiden Co., Ltd. | Mat member, method of fabrication mat member, exhaust gas treating apparatus, and silencing device |
US20090257925A1 (en) * | 2008-04-15 | 2009-10-15 | Ibiden Co., Ltd. | Holding sealing material, exhaust gas purifying apparatus, and method for manufacturing holding sealing material |
US20100007094A1 (en) * | 2008-07-10 | 2010-01-14 | Ibiden Co., Ltd | Holding sealing material, exhaust gas purifying apparatus and method for manufacturing exhaust gas purifying apparatus |
US8071040B2 (en) | 2009-09-23 | 2011-12-06 | Unifax I LLC | Low shear mounting mat for pollution control devices |
US8075843B2 (en) | 2009-04-17 | 2011-12-13 | Unifrax I Llc | Exhaust gas treatment device |
US8211373B2 (en) | 2008-08-29 | 2012-07-03 | Unifrax I Llc | Mounting mat with flexible edge protection and exhaust gas treatment device incorporating the mounting mat |
US8263512B2 (en) | 2008-12-15 | 2012-09-11 | Unifrax I Llc | Ceramic honeycomb structure skin coating |
US8349265B2 (en) | 2010-08-13 | 2013-01-08 | Unifrax I Llc | Mounting mat with flexible edge protection and exhaust gas treatment device incorporating the mounting mat |
US8524161B2 (en) | 2007-08-31 | 2013-09-03 | Unifrax I Llc | Multiple layer substrate support and exhaust gas treatment device |
US8679415B2 (en) | 2009-08-10 | 2014-03-25 | Unifrax I Llc | Variable basis weight mounting mat or pre-form and exhaust gas treatment device |
US8734726B2 (en) | 2009-12-17 | 2014-05-27 | Unifrax I Llc | Multilayer mounting mat for pollution control devices |
US8765069B2 (en) | 2010-08-12 | 2014-07-01 | Unifrax I Llc | Exhaust gas treatment device |
US8926911B2 (en) | 2009-12-17 | 2015-01-06 | Unifax I LLC | Use of microspheres in an exhaust gas treatment device mounting mat |
US8951323B2 (en) | 2009-09-24 | 2015-02-10 | Unifrax I Llc | Multiple layer mat and exhaust gas treatment device |
US9120703B2 (en) | 2010-11-11 | 2015-09-01 | Unifrax I Llc | Mounting mat and exhaust gas treatment device |
US9174169B2 (en) | 2009-08-14 | 2015-11-03 | Unifrax I Llc | Mounting mat for exhaust gas treatment device |
US9452719B2 (en) | 2015-02-24 | 2016-09-27 | Unifrax I Llc | High temperature resistant insulation mat |
US9631529B2 (en) | 2009-04-21 | 2017-04-25 | Saffil Automotive Limited | Erosion resistant mounting mats |
US9650935B2 (en) | 2009-12-01 | 2017-05-16 | Saffil Automotive Limited | Mounting mat |
EP3051186A4 (en) * | 2013-09-24 | 2017-05-31 | Ibiden Co., Ltd | Holding seal material, production method for holding seal material, press-fitting method for winding body, and exhaust gas purification device |
US9790836B2 (en) | 2012-11-20 | 2017-10-17 | Tenneco Automotive Operating Company, Inc. | Loose-fill insulation exhaust gas treatment device and methods of manufacturing |
US9816420B2 (en) | 2009-12-17 | 2017-11-14 | Unifrax I Llc | Mounting mat for exhaust gas treatment device |
US9924564B2 (en) | 2010-11-11 | 2018-03-20 | Unifrax I Llc | Heated mat and exhaust gas treatment device |
US11536180B2 (en) * | 2021-02-26 | 2022-12-27 | Ngk Insulators, Ltd. | Tubular member for exhaust gas treatment device and exhaust gas treatment device using the tubular member, and method of manufacturing tubular member for exhaust gas treatment device |
Families Citing this family (30)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JP4665618B2 (ja) * | 2005-06-10 | 2011-04-06 | イビデン株式会社 | 保持シール材の製造方法 |
JP4959206B2 (ja) * | 2006-03-02 | 2012-06-20 | イビデン株式会社 | 耐熱シートおよび排気ガス浄化装置 |
JP4802048B2 (ja) * | 2006-06-16 | 2011-10-26 | イビデン株式会社 | 保持シール材、排ガス処理装置およびその製造方法 |
JP2008045521A (ja) * | 2006-08-21 | 2008-02-28 | Ibiden Co Ltd | 保持シール材および排気ガス処理装置 |
JP2008051004A (ja) * | 2006-08-24 | 2008-03-06 | Ibiden Co Ltd | 保持シール材および排気ガス処理装置 |
EP1953357B1 (en) * | 2007-01-26 | 2009-08-26 | Ibiden Co., Ltd. | Sheet member and manufacturing method thereof, exhaust gas treating apparatus and manufacturing method thereof, and silencing device |
JP5014113B2 (ja) * | 2007-01-26 | 2012-08-29 | イビデン株式会社 | シート材、その製造方法、排気ガス処理装置および消音装置 |
JP4959499B2 (ja) * | 2007-09-28 | 2012-06-20 | イビデン株式会社 | マット材、排気ガス処理装置および消音装置 |
JP2009085091A (ja) * | 2007-09-28 | 2009-04-23 | Ibiden Co Ltd | マット材、排気ガス処理装置および消音装置 |
CN101883917B (zh) | 2007-10-09 | 2015-01-28 | 3M创新有限公司 | 包括无机纳米粒子的安装垫和制造该安装垫的方法 |
JP5014070B2 (ja) * | 2007-11-06 | 2012-08-29 | イビデン株式会社 | マット材および排気ガス処理装置 |
JP2009156254A (ja) * | 2007-12-05 | 2009-07-16 | Ibiden Co Ltd | 排気ガス処理体の保持シール部材及び排気ガス処理装置 |
JP5164633B2 (ja) * | 2008-03-27 | 2013-03-21 | イビデン株式会社 | 排気ガス処理装置およびその製造方法 |
JP2010101308A (ja) | 2008-09-25 | 2010-05-06 | Ibiden Co Ltd | マット製品、マット製品を製造する方法、排気ガス処理装置および消音装置 |
CN102421598B (zh) * | 2009-03-13 | 2014-12-17 | 3M创新有限公司 | 垫及带垫装置 |
DE102009021269A1 (de) | 2009-05-14 | 2010-11-18 | Volkswagen Ag | Verfahren zum Herstellen einer Abgasreinigungsvorrichtung |
JP5971894B2 (ja) * | 2011-01-31 | 2016-08-17 | スリーエム イノベイティブ プロパティズ カンパニー | 汚染コントロール要素用保持材、その製造方法及び汚染コントロール装置 |
JP5990393B2 (ja) * | 2012-04-03 | 2016-09-14 | イビデン株式会社 | 保持シール材、及び、排ガス浄化装置 |
JP6059447B2 (ja) * | 2012-04-13 | 2017-01-11 | ニチアス株式会社 | 気体処理装置用保持材、気体処理装置及びこれらに関する方法 |
JP2012189081A (ja) * | 2012-04-26 | 2012-10-04 | Ibiden Co Ltd | マット材、マット材を作製する方法、排気ガス処理装置および消音装置 |
GB2502953B (en) * | 2012-05-24 | 2017-02-08 | Imp Innovations Ltd | Catalytic converter substrate |
JP2014092150A (ja) | 2012-11-07 | 2014-05-19 | Ibiden Co Ltd | 保持シール材、及び保持シール材の製造方法、排ガス浄化装置 |
JP2014202188A (ja) | 2013-04-09 | 2014-10-27 | イビデン株式会社 | 保持シール材、保持シール材の製造方法、及び、排ガス浄化装置 |
JP2014202187A (ja) * | 2013-04-09 | 2014-10-27 | イビデン株式会社 | 保持シール材、保持シール材の製造方法及び排ガス浄化装置 |
JP6411721B2 (ja) * | 2013-09-24 | 2018-10-24 | イビデン株式会社 | 保持シール材の製造方法 |
JP6218529B2 (ja) * | 2013-09-24 | 2017-10-25 | イビデン株式会社 | 保持シール材、保持シール材の製造方法、排ガス浄化装置の製造方法、及び、排ガス浄化装置 |
JP6294147B2 (ja) * | 2014-05-08 | 2018-03-14 | イビデン株式会社 | 保持シール材、保持シール材の製造方法及び排ガス浄化装置 |
DE102015107164A1 (de) * | 2015-05-07 | 2016-11-10 | Faurecia Emissions Control Technologies, Germany Gmbh | Thermoelektrische Generatoreinheit und Abgassystem |
JP6430446B2 (ja) * | 2016-08-15 | 2018-11-28 | 本田技研工業株式会社 | 排気浄化装置 |
EP3339594B1 (en) | 2016-12-21 | 2019-07-24 | 3M Innovative Properties Company | Mounting mat for pollution control elements |
Citations (19)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US4230573A (en) * | 1979-06-08 | 1980-10-28 | Amf Incorporated | Cartridge filter and method of making same |
US5212130A (en) * | 1992-03-09 | 1993-05-18 | Corning Incorporated | High surface area washcoated substrate and method for producing same |
US5996228A (en) * | 1995-04-13 | 1999-12-07 | Mitsubishi Chemical Corporation | Monolith-holding element, process for producing the same, catalytic converter using a monolith member and process for producing the same |
US20030049180A1 (en) * | 2000-03-22 | 2003-03-13 | Koji Fukushima | Catalyst converter and diesel, particulate filter system |
US20030104189A1 (en) * | 2000-06-21 | 2003-06-05 | Masanao Agata | Holding/sealing material for use in catalytic converter for clarifying gaseous emission |
US6579396B2 (en) * | 1999-08-06 | 2003-06-17 | Tex Tech Industries, Inc. | Methods of manufacturing high performance insulations |
US20040052694A1 (en) * | 2000-10-17 | 2004-03-18 | Yoshio Nishikawa | Holding seal material for catalytic converter and method of manufacturing the holding and seal material |
US20040234428A1 (en) * | 2001-05-25 | 2004-11-25 | Kazutomo Tanahashi | Alumina-silica-based fiber, ceramic fiber, ceramic fiber complex, retaining seal material, production method thereof, and alumina fiber complex production method |
US20080181831A1 (en) * | 2007-01-26 | 2008-07-31 | Ibiden Co., Ltd. | Sheet member and manufacturing method thereof, exhaust gas treating apparatus and manufacturing method thereof, and silencing device |
US20080178566A1 (en) * | 2007-01-26 | 2008-07-31 | Ibiden Co., Ltd. | Sheet member, forming method of the same, exhaust gas treatment apparatus, and muffling apparatus |
US20090049690A1 (en) * | 2005-06-10 | 2009-02-26 | Ibiden Co., Ltd. | Holding and sealing material and manufacturing method thereof |
US20090075812A1 (en) * | 2001-05-25 | 2009-03-19 | Ibiden Co., Ltd | Alumina-silica-based fiber, ceramic fiber, ceramic fiber complex, retaining seal material, production method thereof, and alumina fiber complex production method |
US20090081455A1 (en) * | 2007-09-26 | 2009-03-26 | Ibiden Co., Ltd. | Inorganic fiber mat, holding sealer, sound absorber, and method for manufacturing inorganic fiber mat |
US20090087352A1 (en) * | 2007-09-28 | 2009-04-02 | Ibiden Co., Ltd. | Mat material, exhaust gas treating apparatus, and muffler |
US20090087353A1 (en) * | 2007-09-28 | 2009-04-02 | Ibiden Co., Ltd. | Mat member, exhaust gas treatment apparatus, and muffling apparatus |
US20090084268A1 (en) * | 2007-09-28 | 2009-04-02 | Ibiden Co., Ltd. | Mat member, method of fabricating mat member, exhaust gas treating apparatus, and silencing device |
US20090114097A1 (en) * | 2007-11-06 | 2009-05-07 | Ibiden Co., Ltd. | Mat material and exhaust gas treatment device |
US20090148356A1 (en) * | 2007-12-05 | 2009-06-11 | Ibiden Co., Ltd. | Holding member to hold exhaust gas treating element and exhaust gas treating device including the holding member |
US7575727B2 (en) * | 2000-11-10 | 2009-08-18 | Ibiden Co., Ltd. | Catalytic converter and method for manufacturing the same |
Family Cites Families (17)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US5384188A (en) † | 1992-11-17 | 1995-01-24 | The Carborundum Company | Intumescent sheet |
JP4295832B2 (ja) † | 1994-12-27 | 2009-07-15 | 三菱樹脂株式会社 | 無機質繊維成形体およびその製造方法 |
US5686039A (en) | 1995-06-30 | 1997-11-11 | Minnesota Mining And Manufacturing Company | Methods of making a catalytic converter or diesel particulate filter |
ES2237962T3 (es) * | 1998-12-08 | 2005-08-01 | Unifrax Corporation | Estera de fibras inorganicas no intumiscentes amorfa para dispositivos de tratamiento de gases de escape a baja temperatura. |
JP4170526B2 (ja) * | 1999-07-15 | 2008-10-22 | 電気化学工業株式会社 | 触媒コンバーター用モノリス保持材の製造方法 |
JP2002066331A (ja) * | 2000-08-25 | 2002-03-05 | Nichias Corp | 触媒担体保持部材及びその製造方法並びに触媒コンバータ |
JP2002302859A (ja) * | 2001-04-02 | 2002-10-18 | Mitsubishi Chemicals Corp | 耐熱性マットの製造方法 |
JP2002302875A (ja) * | 2001-04-02 | 2002-10-18 | Mitsubishi Chemicals Corp | 耐熱性マット及びその製造方法ならびに排気ガス浄化用触媒コンバータ |
JP2002038379A (ja) † | 2001-06-08 | 2002-02-06 | Mitsubishi Chemicals Corp | 無機質繊維構造体の製造方法 |
JP4026433B2 (ja) | 2001-07-23 | 2007-12-26 | 三菱化学産資株式会社 | アルミナ繊維集合体の製造方法 |
JP2005074243A (ja) † | 2003-08-29 | 2005-03-24 | Three M Innovative Properties Co | 汚染コントロール要素の保持材及び汚染コントロール装置 |
JP2006223920A (ja) * | 2005-02-15 | 2006-08-31 | Three M Innovative Properties Co | 汚染コントロール要素の保持材及び汚染コントロール装置 |
JP4959206B2 (ja) * | 2006-03-02 | 2012-06-20 | イビデン株式会社 | 耐熱シートおよび排気ガス浄化装置 |
JP2007292040A (ja) * | 2006-03-31 | 2007-11-08 | Ibiden Co Ltd | シート材、排気ガス処理装置およびその製造方法 |
JP4802048B2 (ja) * | 2006-06-16 | 2011-10-26 | イビデン株式会社 | 保持シール材、排ガス処理装置およびその製造方法 |
JP2008045521A (ja) | 2006-08-21 | 2008-02-28 | Ibiden Co Ltd | 保持シール材および排気ガス処理装置 |
JP2008051004A (ja) * | 2006-08-24 | 2008-03-06 | Ibiden Co Ltd | 保持シール材および排気ガス処理装置 |
-
2005
- 2005-06-10 JP JP2005171221A patent/JP4665618B2/ja active Active
-
2006
- 2006-06-01 US US11/444,484 patent/US20060278323A1/en not_active Abandoned
- 2006-06-07 EP EP06011736.3A patent/EP1731729B2/en active Active
- 2006-06-09 CN CN2006100916653A patent/CN1876748B/zh active Active
- 2006-06-09 KR KR1020060052067A patent/KR100762116B1/ko active IP Right Grant
-
2008
- 2008-10-24 US US12/257,459 patent/US8533950B2/en active Active
Patent Citations (23)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US4230573A (en) * | 1979-06-08 | 1980-10-28 | Amf Incorporated | Cartridge filter and method of making same |
US5212130A (en) * | 1992-03-09 | 1993-05-18 | Corning Incorporated | High surface area washcoated substrate and method for producing same |
US5996228A (en) * | 1995-04-13 | 1999-12-07 | Mitsubishi Chemical Corporation | Monolith-holding element, process for producing the same, catalytic converter using a monolith member and process for producing the same |
US6579396B2 (en) * | 1999-08-06 | 2003-06-17 | Tex Tech Industries, Inc. | Methods of manufacturing high performance insulations |
US20030049180A1 (en) * | 2000-03-22 | 2003-03-13 | Koji Fukushima | Catalyst converter and diesel, particulate filter system |
US20030104189A1 (en) * | 2000-06-21 | 2003-06-05 | Masanao Agata | Holding/sealing material for use in catalytic converter for clarifying gaseous emission |
US20080312071A1 (en) * | 2000-10-17 | 2008-12-18 | Ibiden Co., Ltd. | Holding and sealing material for catalytic converter and method of manufacturing the holding seal material |
US20040052694A1 (en) * | 2000-10-17 | 2004-03-18 | Yoshio Nishikawa | Holding seal material for catalytic converter and method of manufacturing the holding and seal material |
US7575727B2 (en) * | 2000-11-10 | 2009-08-18 | Ibiden Co., Ltd. | Catalytic converter and method for manufacturing the same |
US20090081442A1 (en) * | 2001-05-25 | 2009-03-26 | Ibiden Co., Ltd. | Alumina-silica-based fiber, ceramic fiber, ceramic fiber complex, retaining seal material, production method thereof, and alumina fiber complex production method |
US20090143217A1 (en) * | 2001-05-25 | 2009-06-04 | Ibiden Co., Ltd | Alumina-silica-based fiber, ceramic fiber, ceramic fiber complex, retaining seal material, production method thereof, and alumina fiber complex production method |
US20040234428A1 (en) * | 2001-05-25 | 2004-11-25 | Kazutomo Tanahashi | Alumina-silica-based fiber, ceramic fiber, ceramic fiber complex, retaining seal material, production method thereof, and alumina fiber complex production method |
US20090075812A1 (en) * | 2001-05-25 | 2009-03-19 | Ibiden Co., Ltd | Alumina-silica-based fiber, ceramic fiber, ceramic fiber complex, retaining seal material, production method thereof, and alumina fiber complex production method |
US20090072498A1 (en) * | 2001-05-25 | 2009-03-19 | Ibiden Co., Ltd. | Alumina-silica-based fiber, ceramic fiber, ceramic fiber complex, retaining seal material, production method thereof, and alumina fiber complex production method |
US20090049690A1 (en) * | 2005-06-10 | 2009-02-26 | Ibiden Co., Ltd. | Holding and sealing material and manufacturing method thereof |
US20080178566A1 (en) * | 2007-01-26 | 2008-07-31 | Ibiden Co., Ltd. | Sheet member, forming method of the same, exhaust gas treatment apparatus, and muffling apparatus |
US20080181831A1 (en) * | 2007-01-26 | 2008-07-31 | Ibiden Co., Ltd. | Sheet member and manufacturing method thereof, exhaust gas treating apparatus and manufacturing method thereof, and silencing device |
US20090081455A1 (en) * | 2007-09-26 | 2009-03-26 | Ibiden Co., Ltd. | Inorganic fiber mat, holding sealer, sound absorber, and method for manufacturing inorganic fiber mat |
US20090087352A1 (en) * | 2007-09-28 | 2009-04-02 | Ibiden Co., Ltd. | Mat material, exhaust gas treating apparatus, and muffler |
US20090087353A1 (en) * | 2007-09-28 | 2009-04-02 | Ibiden Co., Ltd. | Mat member, exhaust gas treatment apparatus, and muffling apparatus |
US20090084268A1 (en) * | 2007-09-28 | 2009-04-02 | Ibiden Co., Ltd. | Mat member, method of fabricating mat member, exhaust gas treating apparatus, and silencing device |
US20090114097A1 (en) * | 2007-11-06 | 2009-05-07 | Ibiden Co., Ltd. | Mat material and exhaust gas treatment device |
US20090148356A1 (en) * | 2007-12-05 | 2009-06-11 | Ibiden Co., Ltd. | Holding member to hold exhaust gas treating element and exhaust gas treating device including the holding member |
Cited By (47)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US7572415B2 (en) | 2000-03-22 | 2009-08-11 | Ibiden Co., Ltd. | Catalyst converter and diesel, particulate filter system |
US20030049180A1 (en) * | 2000-03-22 | 2003-03-13 | Koji Fukushima | Catalyst converter and diesel, particulate filter system |
US20040052694A1 (en) * | 2000-10-17 | 2004-03-18 | Yoshio Nishikawa | Holding seal material for catalytic converter and method of manufacturing the holding and seal material |
US20040022699A1 (en) * | 2000-11-10 | 2004-02-05 | Koji Fukushima | Catalytic converter and method for manufacture thereof |
US7575727B2 (en) | 2000-11-10 | 2009-08-18 | Ibiden Co., Ltd. | Catalytic converter and method for manufacturing the same |
US8790581B2 (en) | 2001-05-25 | 2014-07-29 | Ibiden Co., Ltd. | Alumina-silica-based fiber, ceramic fiber, ceramic fiber complex, retaining seal material, production method thereof, and alumina fiber complex production method |
US8540941B2 (en) | 2001-05-25 | 2013-09-24 | Ibiden Co., Ltd. | Alumina-silica-based fiber, ceramic fiber, ceramic fiber complex, retaining seal material, production method thereof, and alumina fiber complex production method |
US8303901B2 (en) | 2001-05-25 | 2012-11-06 | Ibiden Co., Ltd. | Alumina-silica-based fiber, ceramic fiber, ceramic fiber complex, retaining seal material, production method thereof, and alumina fiber complex production method |
US7790121B2 (en) | 2001-05-25 | 2010-09-07 | Ibiden Co., Ltd. | Alumina-silica-based fiber, ceramic fiber, ceramic fiber complex, retaining seal material, production method thereof, and alumina fiber complex production method |
US20090072498A1 (en) * | 2001-05-25 | 2009-03-19 | Ibiden Co., Ltd. | Alumina-silica-based fiber, ceramic fiber, ceramic fiber complex, retaining seal material, production method thereof, and alumina fiber complex production method |
US20090075812A1 (en) * | 2001-05-25 | 2009-03-19 | Ibiden Co., Ltd | Alumina-silica-based fiber, ceramic fiber, ceramic fiber complex, retaining seal material, production method thereof, and alumina fiber complex production method |
US8168273B2 (en) | 2007-08-10 | 2012-05-01 | Nichias Corporation | Holding material for catalytic converter |
US20090041967A1 (en) * | 2007-08-10 | 2009-02-12 | Nichias Corporation | Holding material for catalytic converter |
US8524161B2 (en) | 2007-08-31 | 2013-09-03 | Unifrax I Llc | Multiple layer substrate support and exhaust gas treatment device |
US20090081455A1 (en) * | 2007-09-26 | 2009-03-26 | Ibiden Co., Ltd. | Inorganic fiber mat, holding sealer, sound absorber, and method for manufacturing inorganic fiber mat |
US7951731B2 (en) | 2007-09-26 | 2011-05-31 | Ibiden Co., Ltd. | Inorganic fiber mat, holding sealer, sound absorber, and method for manufacturing inorganic fiber mat |
US20090084268A1 (en) * | 2007-09-28 | 2009-04-02 | Ibiden Co., Ltd. | Mat member, method of fabricating mat member, exhaust gas treating apparatus, and silencing device |
US7972464B2 (en) | 2007-09-28 | 2011-07-05 | Ibiden Co., Ltd. | Mat member, method of fabricating mat member, exhaust gas treating apparatus, and silencing device |
EP2042636A1 (en) * | 2007-09-28 | 2009-04-01 | Ibiden Co., Ltd. | Mat member, method of fabrication mat member, exhaust gas treating apparatus, and silencing device |
US20090257925A1 (en) * | 2008-04-15 | 2009-10-15 | Ibiden Co., Ltd. | Holding sealing material, exhaust gas purifying apparatus, and method for manufacturing holding sealing material |
US8580207B2 (en) * | 2008-04-15 | 2013-11-12 | Ibiden Co., Ltd. | Holding sealing material, exhaust gas purifying apparatus, and method for manufacturing holding sealing material |
US20100007094A1 (en) * | 2008-07-10 | 2010-01-14 | Ibiden Co., Ltd | Holding sealing material, exhaust gas purifying apparatus and method for manufacturing exhaust gas purifying apparatus |
US7678345B2 (en) | 2008-07-10 | 2010-03-16 | Ibiden Co., Ltd. | Holding sealing material, exhaust gas purifying apparatus and method for manufacturing exhaust gas purifying apparatus |
US8211373B2 (en) | 2008-08-29 | 2012-07-03 | Unifrax I Llc | Mounting mat with flexible edge protection and exhaust gas treatment device incorporating the mounting mat |
US8696807B2 (en) | 2008-12-15 | 2014-04-15 | Unifrax I Llc | Ceramic honeycomb structure skin coating |
US9163148B2 (en) | 2008-12-15 | 2015-10-20 | Unifrax I Llc | Ceramic honeycomb structure skin coating |
US8263512B2 (en) | 2008-12-15 | 2012-09-11 | Unifrax I Llc | Ceramic honeycomb structure skin coating |
US8679615B2 (en) | 2008-12-15 | 2014-03-25 | Unifrax I Llc | Ceramic honeycomb structure skin coating |
US8075843B2 (en) | 2009-04-17 | 2011-12-13 | Unifrax I Llc | Exhaust gas treatment device |
US9631529B2 (en) | 2009-04-21 | 2017-04-25 | Saffil Automotive Limited | Erosion resistant mounting mats |
US8679415B2 (en) | 2009-08-10 | 2014-03-25 | Unifrax I Llc | Variable basis weight mounting mat or pre-form and exhaust gas treatment device |
US9174169B2 (en) | 2009-08-14 | 2015-11-03 | Unifrax I Llc | Mounting mat for exhaust gas treatment device |
US8071040B2 (en) | 2009-09-23 | 2011-12-06 | Unifax I LLC | Low shear mounting mat for pollution control devices |
US8951323B2 (en) | 2009-09-24 | 2015-02-10 | Unifrax I Llc | Multiple layer mat and exhaust gas treatment device |
US9650935B2 (en) | 2009-12-01 | 2017-05-16 | Saffil Automotive Limited | Mounting mat |
US8926911B2 (en) | 2009-12-17 | 2015-01-06 | Unifax I LLC | Use of microspheres in an exhaust gas treatment device mounting mat |
US8734726B2 (en) | 2009-12-17 | 2014-05-27 | Unifrax I Llc | Multilayer mounting mat for pollution control devices |
US9816420B2 (en) | 2009-12-17 | 2017-11-14 | Unifrax I Llc | Mounting mat for exhaust gas treatment device |
US8765069B2 (en) | 2010-08-12 | 2014-07-01 | Unifrax I Llc | Exhaust gas treatment device |
US8992846B2 (en) | 2010-08-12 | 2015-03-31 | Unifrax I Llc | Exhaust gas treatment device |
US8349265B2 (en) | 2010-08-13 | 2013-01-08 | Unifrax I Llc | Mounting mat with flexible edge protection and exhaust gas treatment device incorporating the mounting mat |
US9120703B2 (en) | 2010-11-11 | 2015-09-01 | Unifrax I Llc | Mounting mat and exhaust gas treatment device |
US9924564B2 (en) | 2010-11-11 | 2018-03-20 | Unifrax I Llc | Heated mat and exhaust gas treatment device |
US9790836B2 (en) | 2012-11-20 | 2017-10-17 | Tenneco Automotive Operating Company, Inc. | Loose-fill insulation exhaust gas treatment device and methods of manufacturing |
EP3051186A4 (en) * | 2013-09-24 | 2017-05-31 | Ibiden Co., Ltd | Holding seal material, production method for holding seal material, press-fitting method for winding body, and exhaust gas purification device |
US9452719B2 (en) | 2015-02-24 | 2016-09-27 | Unifrax I Llc | High temperature resistant insulation mat |
US11536180B2 (en) * | 2021-02-26 | 2022-12-27 | Ngk Insulators, Ltd. | Tubular member for exhaust gas treatment device and exhaust gas treatment device using the tubular member, and method of manufacturing tubular member for exhaust gas treatment device |
Also Published As
Publication number | Publication date |
---|---|
EP1731729B1 (en) | 2012-12-26 |
CN1876748B (zh) | 2010-11-17 |
JP2006342774A (ja) | 2006-12-21 |
JP4665618B2 (ja) | 2011-04-06 |
KR20060128742A (ko) | 2006-12-14 |
CN1876748A (zh) | 2006-12-13 |
US8533950B2 (en) | 2013-09-17 |
KR100762116B1 (ko) | 2007-10-02 |
EP1731729B2 (en) | 2023-03-08 |
US20090049690A1 (en) | 2009-02-26 |
EP1731729A1 (en) | 2006-12-13 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
US8533950B2 (en) | Method of manufacturing holding and sealing material | |
EP1165209B1 (en) | Amorphous non-intumescent inorganic fiber mat for low temperature exhaust gas treatment devices | |
EP0765993B1 (en) | Monolith holding material, method for producing the same, catalytic converter using the monolith, and method for producing the same | |
US8186058B2 (en) | Exhaust system component having insulated double wall | |
EP1267048B1 (en) | Holding and sealing mat material | |
KR101224288B1 (ko) | 오염제어장치용 다층 매트 | |
US6960386B2 (en) | Holding/sealing material for use in catalytic converter for clarifying gaseous emission | |
KR101426177B1 (ko) | 오염 제어 장치용 저전단 장착 매트 | |
EP1825109B1 (en) | Method of cutting an inorganic fiber sheet material for a pollution cotrol device | |
JP2002506166A (ja) | 触媒コンバーター等の脆弱構造体用の支持要素 | |
EP1348841A2 (en) | Holding material for catalytic converter and method for producing the same | |
WO2007044485A1 (en) | Multilayer mounting mats and pollution control devices containing same | |
US20110259192A1 (en) | Exhaust gas purifying system, method for manufacturing the exhaust gas purifying system and exhaust gas purifying method using the exhaust gas purifying system | |
EP1832729B1 (en) | Fiber sheet member and exhaust gas purifying device using the same as a support mat | |
EP2226425A1 (en) | Mat material, exhaust gas treating apparatus, and method of manufacturing mat material | |
EP1776995B1 (en) | Retaining seal member and exhaust gas cleaning apparatus |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
AS | Assignment |
Owner name: IBIDEN CO., LTD., JAPAN Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNOR:EGUCHI, MASAYUKI;REEL/FRAME:018063/0677 Effective date: 20060612 |
|
STCB | Information on status: application discontinuation |
Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION |