US20060201645A1 - Method for the production of paper - Google Patents

Method for the production of paper Download PDF

Info

Publication number
US20060201645A1
US20060201645A1 US10/565,777 US56577706A US2006201645A1 US 20060201645 A1 US20060201645 A1 US 20060201645A1 US 56577706 A US56577706 A US 56577706A US 2006201645 A1 US2006201645 A1 US 2006201645A1
Authority
US
United States
Prior art keywords
paper
oil
polymer
acid
proofing agent
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US10/565,777
Other languages
English (en)
Inventor
Kenichi Ito
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
BASF SE
Seiko PMC Corp
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Publication of US20060201645A1 publication Critical patent/US20060201645A1/en
Assigned to BASF AKTIENGESELLSCHAFT reassignment BASF AKTIENGESELLSCHAFT ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: ITO, KENICHI
Assigned to SEIKO PMC CORPORATION, BASF AKTIENGESELLSCHAFT reassignment SEIKO PMC CORPORATION CORRECTIVE ASSIGNMENT TO CORRECT THE ASSIGNEE'S INFORMATION PREVIOUSLY RECORDED ON REEL 020150 FRAME 0825. ASSIGNOR(S) HEREBY CONFIRMS THE ASSIGNMENT. Assignors: ITO, KENICHI
Abandoned legal-status Critical Current

Links

Classifications

    • D—TEXTILES; PAPER
    • D21—PAPER-MAKING; PRODUCTION OF CELLULOSE
    • D21H—PULP COMPOSITIONS; PREPARATION THEREOF NOT COVERED BY SUBCLASSES D21C OR D21D; IMPREGNATING OR COATING OF PAPER; TREATMENT OF FINISHED PAPER NOT COVERED BY CLASS B31 OR SUBCLASS D21G; PAPER NOT OTHERWISE PROVIDED FOR
    • D21H21/00—Non-fibrous material added to the pulp, characterised by its function, form or properties; Paper-impregnating or coating material, characterised by its function, form or properties
    • D21H21/14—Non-fibrous material added to the pulp, characterised by its function, form or properties; Paper-impregnating or coating material, characterised by its function, form or properties characterised by function or properties in or on the paper
    • D21H21/16—Sizing or water-repelling agents
    • D—TEXTILES; PAPER
    • D21—PAPER-MAKING; PRODUCTION OF CELLULOSE
    • D21H—PULP COMPOSITIONS; PREPARATION THEREOF NOT COVERED BY SUBCLASSES D21C OR D21D; IMPREGNATING OR COATING OF PAPER; TREATMENT OF FINISHED PAPER NOT COVERED BY CLASS B31 OR SUBCLASS D21G; PAPER NOT OTHERWISE PROVIDED FOR
    • D21H17/00—Non-fibrous material added to the pulp, characterised by its constitution; Paper-impregnating material characterised by its constitution
    • D21H17/20—Macromolecular organic compounds
    • D21H17/33—Synthetic macromolecular compounds
    • D21H17/34—Synthetic macromolecular compounds obtained by reactions only involving carbon-to-carbon unsaturated bonds
    • D21H17/36—Polyalkenyalcohols; Polyalkenylethers; Polyalkenylesters
    • D—TEXTILES; PAPER
    • D21—PAPER-MAKING; PRODUCTION OF CELLULOSE
    • D21H—PULP COMPOSITIONS; PREPARATION THEREOF NOT COVERED BY SUBCLASSES D21C OR D21D; IMPREGNATING OR COATING OF PAPER; TREATMENT OF FINISHED PAPER NOT COVERED BY CLASS B31 OR SUBCLASS D21G; PAPER NOT OTHERWISE PROVIDED FOR
    • D21H17/00—Non-fibrous material added to the pulp, characterised by its constitution; Paper-impregnating material characterised by its constitution
    • D21H17/20—Macromolecular organic compounds
    • D21H17/33—Synthetic macromolecular compounds
    • D21H17/46—Synthetic macromolecular compounds obtained otherwise than by reactions only involving carbon-to-carbon unsaturated bonds
    • D21H17/54—Synthetic macromolecular compounds obtained otherwise than by reactions only involving carbon-to-carbon unsaturated bonds obtained by reactions forming in the main chain of the macromolecule a linkage containing nitrogen
    • D21H17/55—Polyamides; Polyaminoamides; Polyester-amides
    • D—TEXTILES; PAPER
    • D21—PAPER-MAKING; PRODUCTION OF CELLULOSE
    • D21H—PULP COMPOSITIONS; PREPARATION THEREOF NOT COVERED BY SUBCLASSES D21C OR D21D; IMPREGNATING OR COATING OF PAPER; TREATMENT OF FINISHED PAPER NOT COVERED BY CLASS B31 OR SUBCLASS D21G; PAPER NOT OTHERWISE PROVIDED FOR
    • D21H21/00—Non-fibrous material added to the pulp, characterised by its function, form or properties; Paper-impregnating or coating material, characterised by its function, form or properties
    • D21H21/14—Non-fibrous material added to the pulp, characterised by its function, form or properties; Paper-impregnating or coating material, characterised by its function, form or properties characterised by function or properties in or on the paper

Definitions

  • the present invention relates to a method for the production of paper, and to paper. More particularly, it relates to a paper production method which is ideal for producing paper with outstanding oil resistance, wet strength and water resistance by enhancing the level of fixing of an oil-proofing agent to the paper and, furthermore, where as well as it being possible to improve the operational characteristics such as the drainage at the time of production, it is also possible to achieve a lowering of the environmental burden and greater economic efficiency; and to paper having outstanding oil resistance, wet strength and water resistance.
  • Oil-proofing agents are used to prevent contamination of food containers, food paper-packaging, paper employed as a construction material and the like, from oil and other oily materials.
  • fluorine-containing oil-proofing agents which have low surface free energy and can impart high oil resistance are used.
  • paper containing such an internally-added fluorine-containing oil-proofing agent possesses oil resistance right into the paper interior and is characterized by having high oil resistance even in folds and cuts/tears and by having outstanding air permeability.
  • the aforesaid fluorine-containing oil-proofing agents are generally marketed in the form of aqueous solutions or aqueous dispersions, so treatment is carried out to raise the water solubility of the fluorine-containing oil-proofing compounds by incorporating ionic groups. Again, treatment is also carried out to bring about dispersion of the fluorine-containing oil-proofing agents in water using ionic or nonionic surfactants.
  • fluorine-containing oil-proofing agents have ionic character but, in terms of ease of production and safety, the majority of these fluorine-containing oil-proofing agents have anionic character.
  • the anionic oil-proofing agent and the cationic material be separately added to the pulp slurry or that the two be mixed together just before the addition.
  • cationic materials used as fixing agents for oil-proofing agents are polymers obtained by polymerization of components which include a cationic monomer, or polymers obtained by subjecting polymer obtained by the polymerization of components which include monomer with ionic character or monomer without ionic character to cationic conversion.
  • the majority of these cationic polymers have the purpose only of fixing the oil-proofing agent and they have little role in enhancing the paper strength, sizing properties or drainage properties, etc.
  • a cationic material used as a fixing agent for anionic fluorine-based oil-proofing agents there is the water-dispersible fluoro copolymer composition containing copolymer of monomer with a polyfluoroalkyl group and monomer which does not have a polyfluoroalkyl group or a carboxypolyfluoroalkyl group, and polyamine copolymer which contains amino groups or ammonium groups in side chains (JP-A-2002-220539).
  • a cationic material used as a fixing agent for anionic fluorine-based oil-proofing agents there is also known a water-repellent composition comprising an aqueous emulsion obtained by copolymerizatlon of perfluoroalkyl acrylate monomer, monomer with a carboxyl group and monoethylenic monomer in specified proportions, and a cationic water-soluble polymer material such as a polyallylamine salt (JP-A-6-49319).
  • the present invention aims to overcome such difficulties, and it addresses the problem of providing a method of paper production wherein the level of fixing of the oil-proofing agent to the paper is enhanced and which is ideal for the production of paper having outstanding oil resistance, wet strength and water resistance and, in addition, wherein operational characteristics such as the drainage at the time of production are improved, while at the same time achieving a reduction in the environmental burden and a raising of economic efficiency; and it also addresses the problem of providing a paper which has outstanding oil resistance, wet strength and water resistance.
  • the present inventor has carried out considerable research into fixing agents for use along with anionic fluorine-based oil-proofing agents in order to resolve the aforesaid problems, as a result of which he has discovered that by using, as a fixing agent, polymer in which at least N-vinylformamide is a polymerization component and/or a derivative of such polymer, it is possible to resolve the aforesaid problems.
  • the present invention has been perfected based on this discovery.
  • a first means for overcoming the aforesaid problems according to the present invention is
  • Preferred embodiments of this first means are the following paper production methods (a) to (d).
  • the aforesaid anionic fluorine-based oil-proofing agent is an oil-proofing agent comprising a compound having a phosphoric acid group or phosphate ester group.
  • a method of paper production in which the level of fixing of the oil-proofing agent to the paper is enhanced and which is ideal for the production of paper having outstanding oil resistance, wet strength and water resistance and, in addition, in which operational characteristics such as the drainage at the time of production are improved, while at the same time achieving a reduction in the environmental burden and a raising of economic efficiency; and there is also provided paper which has outstanding oil resistance, wet strength and water resistance.
  • the invention makes a very great contribution to the industrial field of papermaking.
  • anionic fluorine-based oil-proofing agent used in the present invention is not particularly restricted providing that it manifests oil resistance or oil repellency when fixed in the paper interior.
  • anionic refers to the case where the oil-proofing agent itself contains a functional group which exhibits anionic character, or to the case of an aqueous emulsion formed by dispersing in an aqueous medium an oil-proofing agent which does not have anionic character and a material containing a functional group which shows anionic character.
  • the functional group which exhibits anionic character there are the carboxyl group, phosphoric acid group, phosphate ester group, sulphonic acid group, sulphate ester group and the like.
  • the phosphoric acid group and phosphate ester group are preferred, with the phosphate ester group being particularly preferred.
  • the oil-proofing agent may also include additives for enhancing the dispersion stability at the time of synthesis or during storage, or for enhancing the sizing properties, etc.
  • oil-proofing agents comprising compounds with a phosphoric acid group or a phosphate ester group.
  • the compound from which the oil-proofing agent is composed may itself have a phosphoric acid group or a phosphate ester group, or the oil-proofing agent may comprise a mixture of a compound which does not have a phosphoric acid group or phosphate ester group and a compound which does have a phosphoric acid group or phosphate ester group.
  • anionic fluorine-based oil-proofing agents are the salts of phosphate esters which contain a polyfluoroalkyl group and phosphate esters with a poly(fluoroalkylene oxide).
  • salts of phosphate esters containing a polyfluoroalkyl group include the hydrolysates of the reaction products of N-alkylperfluoroalkanesulphonamidoalkylalcohols and phosphorus oxychloride (see JP-B-40-6857) or dichlorophosphoric acid (see JP-B-54-7776), and the hydrolysates of the reaction products of polyfluoroalkanols and phosphorus oxyhalide, phosphorus pentoxido or dialkylphosphite (see JP-B-48-4770) and their ethanolamine salts (see JP-A-53-77015).
  • a fluoro- or chlorofluoro-aliphatic hydrocarbon see JP-A-56-138197
  • an anionic surfactant see JP-A-64-6196
  • a specified nonionic surfactant see JP-A-2000-144120
  • phosphate esters with a poly(fluoroalkylene oxide) there are the compounds represented by [XCF 2 CF 2 O(CFXCF 2 O) x CFXCF 2 O] 2 PO(OM) (where X is an atom or group selected from F and CF 3 , x is an integer in the range 1 to 8, and M is a water-soluble cation selected from alkali metal ions, ammonium ions and substituted ammonium ions) (see U.S. Pat. No. 3492374).
  • a and B are phosphate ester groups represented by —[CH 2 O(RO) p ] k —P(O)(OH) 3-k (where R is an alkylene group, in particular ethylene or propylene, p is an integer in the range 1 to 10, and k is 1 or 2) (see JP-A-2000-219847).
  • the anionic fluorine-based oil-proofing agent used in the present invention may comprise copolymer of monomer with a fluoroalkyl group and other monomer, fluoroalkylcarboxylic acids, polyperfluoroalkyl-substituted polyamides, organosilicon compounds which contain a fluoroalkyl group and polymer formed from at least one type of monoethylenically unsaturated monomer selected from those with nonionic, anionic and cationic groups, monoethylenically unsaturated monomer containing a fluoroalkyl group and monoethylenically unsaturated monomer containing a silicone group.
  • anionic fluorine-based oil-proofing agents there are the Asahi Guard AG series (produced by the Asahi Glass Co.), the Fluorolink PT series (produced by Solvey Solexis), the Zonyl series (produced by DuPont) and the Scotchban series (produced by 3M).
  • the fixing agent used in the present invention is a polymer in which at least N-vinylformamide is a polymerization component and/or a derivative of such polymer.
  • polymer in which at least N-vinylformamide is a polymerization component
  • homopolymer obtained by the polymerization of N-vinylformamide and the copolymers obtained by the copolymerization of N-vinylformamide and monomers copolymerizable with N-vinylformamide (below said homopolymer and copolymer are merely referred to together as ‘polymer’).
  • polymer there can also be used mixtures of homopolymer and copolymer.
  • Examples of the aforesaid monomers which are copolymerizable with N-vinylformamide include vinyl compounds with a side chain group which contains a nitrogen atom, the vinyl or propenyl esters of saturated carboxylic acids, nonionic (meth)allyl monomers, (meth)allyl monomers having a side chain which contains a nitrogen atom, olefins, ethylenically-unsaturated carboxylic acids, esters or amides of these ethylenically-unsaturated carboxylic acids, monomers with a nitrile group, monomers with a sulphonic acid group, monomers with a phosphoric acid group and styrene-type monomers.
  • N-vinyl carboxylic acid amides such as N-vinylacetamide and N-vinylpropionamide
  • N-substituted-N-vinyl carboxylic acid amides such as N-methyl-N-vinylacetamide and N-ethyl-N-vinylacetamide
  • N-vinyl lactams such as N-vinyl-pyrrolidone and N-vinylcaprolactam
  • N-vinyl-N-alkylamines in which an alkyl group with from 1 to 6 carbon atoms is bonded to the nitrogen atom such as N-vinyl-N-methylamine and N-vinyl-N-ethylamine
  • vinyl-heterocyclic compounds such as N-vinylimidazole, 2-vinylimidazole, N-vinyl-2-methyl-imidazole, N-vinyl-4-
  • the N-vinylimidazole and N-vinylimidazoline can be employed in their free base form, or they can be employed in the form obtained by neutralization with acid or in the quaternized form.
  • said acid are mineral acids such as hydrochloric acid, carbonic acid, sulphuric acid and nitric acid, and organic acids such as sulphonic or carboxylic acids like formic acid, acetic acid and propionic acid.
  • the quaternization can be carried out for example using an alkyl halide such as methyl chloride or methyl bromide, an aralkyl halide such as benzyl chloride or benzyl bromide, a dialkyl sulphate such as dimethyl sulphate or diethyl sulphate, or an epihalohydrin such as epichlorohydrin or epibromohydrin.
  • an alkyl halide such as methyl chloride or methyl bromide
  • an aralkyl halide such as benzyl chloride or benzyl bromide
  • a dialkyl sulphate such as dimethyl sulphate or diethyl sulphate
  • an epihalohydrin such as epichlorohydrin or epibromohydrin.
  • vinyl esters of saturated carboxylic acids there are vinyl formate, vinyl acetate, vinyl propionate and vinyl butyrate, and as examples of the propenyl esters of saturated carboxylic acids, there are propenyl formate, propenyl acetate and propenyl propionate.
  • nonionic (meth)allyl monomers examples include (meth)allyl alcohols such as allyl alcohol and methallyl alcohol, (meth)allyl halides such as allyl chloride, allyl bromide, methallyl chloride and methallyl bromide, (meth)allyl ethers in which an alkyl group with from 1 to 18 carbons is ether-bonded such as allyl methyl ether, allyl ethyl ether, methallyl methyl ether and methallyl ethyl ether, and (meth)allyl esters of saturated carboxylic acids with from 1 to 18 carbons such as allyl formate, allyl acetate, allyl propionate, methallyl formate and methallyl acetate.
  • (meth)allyl alcohols such as allyl alcohol and methallyl alcohol
  • (meth)allyl halides such as allyl chloride, allyl bromide, methallyl
  • Examples of the aforesaid (meth)allyl monomers with a side chain group which contains a nitrogen atom are (meth)allylamines like allylamine and methallylamine, N-alkyl (meth)allylamines which have an alkyl group with from 1 to 18 carbons bonded to the nitrogen atom such as N-methylallylamine, N-ethylallylamine, N-stearylallylamine, N-methylmethallylamine and N-ethylmethallylamine, N,N-dialkyl (meth)allylamines which have alkyl groups with from 1 to 18 carbons bonded to the nitrogen atom such as N,N-dimethylallylamine, N,N-diethylallylamine, N,N-dimethylmethallylamine, N,N-diethylmethallylamine, N-methyl-N-stearylmethallylamine and N,N-distearylmethallylamine, N,N
  • the aforesaid (meth)allylamines, N-alkyl(meth)allylamines, N,N-dialkyl(meth)allylamines and N-alkyldi(meth)allylamines can be employed in their free base form, or they can be employed in the form obtained by neutralization with acid or in the quaternized form.
  • said acid are mineral acids such as hydrochloric acid, carbonic acid, sulphuric acid and nitric acid, and organic acids such as sulphonic or carboxylic acids like formic acid, acetic acid and propionic acid.
  • the quaternization can be carried out for example using an alkyl halide such as methyl chloride or methyl bromide, an aralkyl halide such as benzyl chloride or benzyl bromide, a dialkyl sulphate such as dimethyl sulphate or diethyl sulphate, or an epihalohydrin such as epichlorohydrin or epibromohydrin.
  • an alkyl halide such as methyl chloride or methyl bromide
  • an aralkyl halide such as benzyl chloride or benzyl bromide
  • a dialkyl sulphate such as dimethyl sulphate or diethyl sulphate
  • an epihalohydrin such as epichlorohydrin or epibromohydrin.
  • olefins there are ethylene, propylene and butadiene.
  • ethylenically-unsaturated carboxylic acids there are acrylic acid, methacrylic acid, crotonic acid, maleic acid, maleic anhydride, fumaric acid, itaconic acid, itaconic anhydride, citraconic acid, citraconic anhydride, cinnamic acid, vinyl ester acids, 2-(meth)acrylamidoglycolic acid, ⁇ , ⁇ -unsaturated-tricarboxylic acids and ⁇ , ⁇ -unsaturated tetracarboxylic acids, together with the alkali metal salts, alkaline earth metal salts and ammonium salts thereof.
  • Examples of the aforesaid ethylenically unsaturated carboxylic acid esters are (meth)acrylate esters in which an alkyl group with from 1 to 18 carbon atoms is ester-bonded, such as methyl acrylate, methyl methacrylate, ethyl acrylate, ethyl methacrylate, isobutyl methacrylate, tert-butyl methacrylate, 2-ethylhexyl acrylate and stearyl acrylate, (meth)acrylate esters where only a single hydroxy group has been esterified such as hydroxyethyl acrylate, hydroxyethyl methacrylate, hydroxypropyl acrylate, hydroxybutyl acrylate, hydroxypropyl methacrylate, hydroxybutyl methacrylate, 2-methoxybutyl acrylate, 2-methoxybutyl methacrylate and the acrylic acid monoesters of a polyalkylene glycol of
  • carboxylic acid esters of aminoalcohols can be employed in their free base form, or they may be employed in the form obtained by neutralization with acid or in the quaternized form.
  • acid examples include mineral acids such as hydrochloric acid, carbonic acid, sulphuric acid and nitric acid, and organic acids such as sulphonic or carboxylic acids like formic acid, acetic acid and propionic acid.
  • the quaternization can be carried out for example using an alkyl halide such as methyl chloride or methyl bromide, an aralkyl halide such as benzyl chloride or benzyl bromide, a dialkyl sulphate such as dimethyl sulphate or diethyl sulphate, or an epihalohydrin such as epichlorohydrin or epibromohydrin.
  • an alkyl halide such as methyl chloride or methyl bromide
  • an aralkyl halide such as benzyl chloride or benzyl bromide
  • a dialkyl sulphate such as dimethyl sulphate or diethyl sulphate
  • an epihalohydrin such as epichlorohydrin or epibromohydrin.
  • the aforesaid amides of the unsaturated carboxylic acids include the N-alkyl mono-amides and N-alkyldiamides of monoethylenically unsaturated carboxylic acids which have an alkyl group with from 1 to 6 carbons, examples of which are acrylamide, methacrylamide, N-methylacrylamide, N,N-dimethylacrylamide, N-methylmethacrylamide, N-ethylacrylamide, N-isopropylacrylamide and N-tert-butylacrylamide, and N,N-dialkylaminoalkyl (meth)acrylamides such as dimethylaminoethyl acrylamide, dimethylaminoethyl methacrylamide, diethylaminoethyl acrylamide, diethylaminoethyl methacrylamide, dimethylaminopropyl acrylamide, diethylaminopropyl acrylamide, dimethylaminopropyl methacrylamide and die
  • N,N-dialkylaminoalkyl (meth)acrylamides can be employed in their free base form, or they can be employed in the form obtained by neutralization with acid or in the quaternized form.
  • acid examples include mineral acids such as hydrochloric acid, carbonic acid, sulphuric acid and nitric acid, and organic acids such as sulphonic or carboxylic acids like formic acid, acetic acid and propionic acid.
  • the quaternization can be carried out for example using an alkyl halide such as methyl chloride or methyl bromide, an aralkyl halide such as benzyl chloride or benzyl bromide, a dialkyl sulphate such as dimethyl sulphate or diethyl sulphate, or an epihalohydrin such as epichlorohydrin or epibromohydrin.
  • an alkyl halide such as methyl chloride or methyl bromide
  • an aralkyl halide such as benzyl chloride or benzyl bromide
  • a dialkyl sulphate such as dimethyl sulphate or diethyl sulphate
  • an epihalohydrin such as epichlorohydrin or epibromohydrin.
  • Examples of the aforesaid monomers with a nitrile group are acrylonitrile, methacrylonitrile and 2-methylene-glutaronitrile.
  • Examples of the aforesaid monomers with a sulphonic acid group are vinylsulphonic acid, allylsulphonic acid, methallylsulphonic acid, isoprenesulphonic acid, 3-allyloxy-2-hydroxy-propanesulphonic acid, styrene-sulphonic acid, 3-sulphopropyl acrylate, 2-acrylamido-2-methylpropanesulphonic acid, 2-methacrylamido-2-methylpropanesulphonic acid, sulphoethyl acrylate, the sulphate ester of hydroxyethyl acrylate and the sulphate ester of polyoxyalkyleneoxide acrylate, together with the alkali metal salts, alkaline earth metal salts and ammonium salts, etc, of these acids.
  • examples of the aforesaid monomers with a phosphoric acid group there are vinylphosphonic acid and styrene-phosphonic acid, together with the alkali metal salts, alkaline earth metal salts and ammonium salts, etc, of these acids.
  • styrene-type monomers there are styrene per se, ⁇ -methylstyrene, ⁇ -methylstyrene dimer and vinylbenzylamine.
  • the vinylbenzylamine can be employed in its free base form, or it can be employed in the form obtained by neutralization with acid or in the quaternized form.
  • acid mineral acids such as hydrochloric acid, carbonic acid, sulphuric acid and nitric acid, and organic acids such as sulphonic or carboxylic acids like formic acid, acetic acid and propionic acid.
  • the quaternization can be carried out using for example an alkyl halide such as methyl chloride or methyl bromide, an aralkyl halide such as benzyl chloride or benzyl bromide, a dialkyl sulphate such as dimethyl sulphate or diethyl sulphate, or an epihalohydrin such as epichlorohydrin or epibromohydrin.
  • an alkyl halide such as methyl chloride or methyl bromide
  • an aralkyl halide such as benzyl chloride or benzyl bromide
  • a dialkyl sulphate such as dimethyl sulphate or diethyl sulphate
  • an epihalohydrin such as epichlorohydrin or epibromohydrin.
  • N-vinylformamide polymer there may be used any polymerization method such as an ionic polymerization method like anionic or cationic polymerization, or a radical polymerization method.
  • a radical polymerization method is preferred from the point of view of ready control of the molecular weight, and there can be used for example the method described in JP-A-11-322849.
  • N-vinylformamide polymer can be carried out by a method such as bulk polymerization, solution polymerization, suspension polymerization or emulsion polymerization.
  • the polymerization reaction is generally conducted under a current of inert gas, normally under temperature conditions of 30 to 100° C.
  • the polymerization is carried out using water or a polar solvent which can dissolve the N-vinylformamide, and normally it is conducted in an aqueous solution of monomer concentration 5 to 60 mass %.
  • a polar solvent which can dissolve the N-vinylformamide
  • suspension polymerization usually the polymerization of an aqueous solution of monomer of concentration 20-80 mass % is carried out in a water-in-oil type dispersion state using a hydrophobic solvent and a dispersion stabilizer.
  • emulsion polymerization normally the polymerization of an aqueous solution of monomer of concentration 20-60 mass % is carried out in an oil-in-water type or water-in-oil type emulsion state using a hydrophobic solvent and an emulsifier.
  • the aforesaid copolymer can be produced by the copolymerization of 90 to 1 mol % of the N-vinylformamide and 10 to 99 mol % of the monomer copolymerizable therewith, preferably 95 to 50 mol % and 5 to 50 mol % respectively.
  • a normal polymerization initiator as the radical polymerization catalyst employed in the polymerization reaction, in particular in a radical polymerization reaction.
  • a normal polymerization initiator there can be used for example an azo type polymerization initiator, a persulphate, a peroxide, a bromate, a perborate, a percarbonate or a perphosphate.
  • azobisisobutyronitrile 2,2′-azobis-(2,4′-dimethylvaleronitrile), 2,2′-azobis(4-methoxy-2,4-dimethylvaleronitrile), 2,2′-azobis(2-methylpropionitrile), 2,2′-azobis(2-methylbutyronitrile), 1,1-azobis-(cyclohexane-1-carbonitrile), 2,2′-azobis-[2-methyl-N-(2-hydroxyethyl)propionamide], dimethyl 2,2′-azobis(2-methylpropionate), 2,2′-azobis-(2-amidinopropane), 2,2′-azobis-(2-amidinopropane), 2,2′-azobis-(2-amidinopropane), 2,2′-azobis-(N,N′-dimethyleneisobutylamine), 2,2′-azobis-(N,N′-dimethyleneisobutylamine), 2,2′-azobis(2-imidazol
  • the persulphate there are sodium persulphate, potassium persulphate and ammonium persulphate.
  • the peroxide there are benzoyl peroxide, hydrogen peroxide, tert-butylhydroperoxide and di-tert-butylperoxide.
  • the bromate there are sodium bromate and potassium bromate.
  • the perborate there are sodium perborate and ammonium perborate.
  • the percarbonate there are sodium percarbonate, potassium percarbonate and ammonium percarbonate.
  • the perphosphate there are sodium perphosphate, potassium perphosphate and ammonium perphosphate.
  • polymerization initiators can be used on their own or they can be used in combinations of two or more.
  • Especially preferred initiators are 2,2′-azobis-4-amidinopropane hydrochloride or acetate, the sodium salt of 4,4′-azobis-4-cyanovaleric acid, and azobis-N,N′-dimethyleneisobutylamidine hydrochloride or sulphate.
  • the peroxide type polymerization initiators can also be used in the form of redox type polymerization initiators.
  • reducing agents can be used on their own or in combinations of two or more.
  • Polymerization is initiated by the addition of the polymerization initiator to the monomer solution. Moreover, with the objective of reducing the amount of unreacted monomer, a supplementary addition of some polymerization initiator may be made during the course of the polymerization reaction, or continuous addition of the polymerization initiator may be performed by a means such as the dropwise addition method. It is also possible to use the method of irradiating with ionizing radiation, an electron beam or ultraviolet light. These methods may be employed on their own or there can be used a combination of two or more types.
  • a chain transfer agent can be suitably employed.
  • the chain transfer agent are compounds having one or more hydroxy groups in the molecule, compounds having one or more mercapto groups in the molecule, compounds having one or more carbon-carbon unsaturated bonds in the molecule, peroxides such as dibutylperoxide, and hypophosphoric acid.
  • the chain transfer agents may be used on their own or in combinations of two or more.
  • a crosslinking agent may be suitably added where required.
  • the crosslinking agent are bifunctional polymerizable vinyl monomers such as di(meth)acrylates, bis(meth)acrylamides and divinyl esters which possess two unsaturated bonds, monomers with a crosslinking action due to having functional groups which undergo chain transfer with vinyl groups, monomers which have a crosslinking action due to having groups which react with vinyl groups, trifunctional polymerizable vinyl monomers which have three unsaturated bonds, tetra-functional polymerizable vinyl monomers which have four unsaturated bonds, water-soluble aziridinyl compounds, water-soluble polyfunctional epoxy compounds and silicon based compounds. These can be used on their own or in combinations of two or more.
  • the polymerization of the N-vinylformamide or the copolymerization of the N-vinylformamide and monomer copolymerizable therewith can be carried out in the presence of a water-soluble polymer such as a starch like oxidized starch, cationic starch, amphoteric starch or enzyme-modified starch, a cellulose derivative such as carboxy-methylcellulose, polyvinyl alcohol, chitosan or a gum, etc.
  • a water-soluble polymer such as a starch like oxidized starch, cationic starch, amphoteric starch or enzyme-modified starch, a cellulose derivative such as carboxy-methylcellulose, polyvinyl alcohol, chitosan or a gum, etc.
  • the derivatives of polymer in which at least N-vinylformamide is a polymerization component there are (1) polymer formed by modification of the formamide groups contained in N-vinylformamide homopolymer, (2) polymer formed by modification of the formamide groups contained in copolymer of N-vinylformamide and monomer which can copolymerize with N-vinylformamide, and (3) mixtures of polymer (1) and polymer (2).
  • Examples of said modification are hydrolysis, amide-exchange, hydrolysis followed by reaction of the amino groups with an alkyl halide such as methyl chloride or methyl bromide, an aralkyl halide such as benzyl chloride or benzyl bromide, a halo-carboxylic acid ester such as a haloformate ester or haloacetate ester, a dialkyl sulphate such as dimethyl sulphate or diethyl sulphate, an epihalohydrin such as epichlorohydrin or epibromohydrin, a saturated aliphatic or aromatic glycidyl ether compound, or urea, amidine modification based on hydrolysis in the presence of ammonia, and cyclic amidine modification conducted by heating a partially hydrolyzed derivative of the aforesaid polymer in which at least N-vinylformamide is a polymerization component.
  • an alkyl halide such as methyl chloride
  • the derivatives obtained by hydrolysis of the formyl groups in the aforesaid N-vinylformamide homopolymer and in the copolymers of N-vinylformamide and vinyl monomer polymerizable therewith are preferred.
  • the hydrolysates obtained by hydrolysis of the formyl groups in these polymers there are the hydrolysates obtained by hydrolysis of the formyl groups in these polymers.
  • Such derivatives can be obtained by performing hydrolysis in the solution state or after dehydrating or drying to produce a powder state, using known hydrolysis methods such as for example an acidic hydrolysis method, a basic hydrolysis method, a method of acidic hydrolysis in a hydrophilic solvent such as alcohol containing water, or an alcoholysis method under acidic conditions.
  • the acidic and basic hydrolysis methods are preferred.
  • the modifying agent used in acidic hydrolysis can be any compound which acts as a strong acid such as hydrochloric acid, hydrobromic acid, hydrofluoric acid, sulphuric acid, nitric acid, phosphoric acid, sulfamic acid or methanesulphonic acid, but a mono-basic acid is preferred in terms of facilitating the dissolution of the hydrolysate in water.
  • the modifying agent used in basic hydrolysis may be any compound which acts as a strong base such as sodium hydroxide, potassium hydroxide, lithium hydroxide or a quaternary ammonium hydroxide.
  • alcohols with from 1 to 4 carbons such as methanol, ethanol, propanol and butanol, but methanol is preferred.
  • the amount of modifying agent used for the hydrolysis will be suitably selected in accordance with the desired percentage modification, normally from within the range 0.05 to 5 mol per mol of formyl groups in the aforesaid polymer.
  • the reaction temperature at the time of the hydrolysis is normally in the range 30 to 110° C., and the reaction time is normally from 0.1 to 24 hours.
  • the percentage hydrolysis of the formyl groups in the polymer in which at least N-vinylformamide is a polymerization component is preferably from 10% to 90% of the total formyl groups in the polymer, with from 30% to 70% being still further preferred. If the percentage hydrolysis is too low, there may be insufficient oil-proofing agent fixing effect, while conversely if the percentage hydrolysit is too great then the ion balance in the papermaking system may be damaged, and the yield, paper quality such as texture, and operational properties may be impaired.
  • the modification may be conducted with the optional addition of a gelling inhibitor such as hydroxylamine hydrochloride or hydroxylamine sulphate.
  • a gelling inhibitor such as hydroxylamine hydrochloride or hydroxylamine sulphate.
  • hydrolysis can also be carried out after performing treatment with the gelling inhibitor prior to modification.
  • the hydrolysis can be conducted in a homogeneous solution using water or a mixture of water and a polar solvent such as methanol, or in a heterogeneous solution comprising a non-polar solvent such as hexane or toluene and a polar solvent containing at least water.
  • the solids concentration of the solution of polymer in which at least N-vinylformamide is a polymerization component and/or of derivative thereof obtained is normally from 3 to 40 mass %. Furthermore, when the viscosity of this polymer solution and/or derivative solution is measured with a Brookfield rotary viscometer at 25° C, normally it is no more than 100,000 mPa ⁇ s and preferably no more than 20,000 mPa ⁇ s. In the present invention, this polymer solution and/or derivative solution can be employed as it is for use as the fixing agent.
  • the paper raw material pulp used in the paper production method of the present invention there are kraft pulp, sulphite pulp and other such bleached and unbleached chemical pulps, groundwood pulp, mechanical pulp, thermomechanical pulp, chemithermomechanical pulp and other such bleached or unbleached high-yield pulps, and also pulps containing pulps of waste paper such as newspaper, magazine paper, cardboard and the like.
  • wood pulp there may also be used non wood-based pulps such as those based on straw or kenaf.
  • a mixture of an aforesaid pulp and a synthetic fibre such as polyamide, polyester, polyolefin or polyvinyl alcohol, etc.
  • the anionic fluorine-based oil-proofing agent and fixing agent of the present invention can be added prior to the dryer part of the papermaking process and the method of addition is not particularly restricted, but it is preferred that they be added to the paper materials prior to the wet web formation.
  • the order of addition of the anionic fluorine-based oil-proofing agent and the fixing agent may be added at the same location or they may be mixed together Just before the addition. Furthermore, one may be added prior to the other.
  • anionic fluorine-based oil-proofing agent and the fixing agent are added to the paper materials prior to the wet web formation, they may be added at the same time as, or before or after, other chemical agents.
  • these chemical agents include coagulants, dry paper strengtheners, wet paper strengtheners, sizing agents, fillers, yield enhancers and drainage enhancers, and these are added where required so that there may be manifested the properties required in accordance with the paper type, or so that the operational characteristics are enhanced.
  • One such chemical agent may be incorporated or there may be used two or more types in combination.
  • Examples of the aforesaid coagulants are poly(diallyldimethylammonium chloride) and the reaction product of amines and epihalohydrins.
  • Examples of the dry paper strengtheners are anionic polyacrylamide, cationic polyacrylamide, amphoteric polyacrylamide, cationic starch and amphoteric starch.
  • Examples of the wet paper strengtheners are polyamide epichlorohydrin resins, polyamine epichlorohydrin resins, melamine formaldehyde resin and urea formaldehyde resin, etc.
  • examples of the sizing agents are fatty acid soaps, solution rosin, acidic rosin emulsion, neutral rosin emulsion, alkenylsuccinic anhydride emulsion or its hydrolysate salts, 2-oxetanone emulsion, paraffin wax emulsion, cationic sizes obtained by the reaction of a carboxylic acid and a polyfunctional amine, emulsions of the reaction products of aliphatic oxyacids and aliphatic amines or aliphatic alcohols, and cationic styrene type emulsion sizes.
  • fillers there are calcium carbonate, talc, clay and white carbon
  • yield enhancers there are anionic high molecular weight polyacrylamides, cationic high molecular weight polyacrylamides, amphoteric high molecular weight polyacrylamides, silica sol and bentonite, etc.
  • drainage enhancers are polyethyleneimine, anionic polyacrylamide, cationic polyacrylamide and amphoteric polyacrylamide, while examples of other types of chemical agent include alum, polyaluminium chloride and other types of aluminium compounds, dyes, defoaming agents and pH regulators.
  • anionic fluorine-based oil-proofing agent and the fixing agent are applied to the paper after the wet web formation by spraying or the like, or again in the case of the coating of the surface of the paper using a coating machine or printing machine, etc.
  • other chemical agents may also be jointly employed.
  • the jointly employed chemicals and examples are surface strengtheners, interlayer paper strengtheners, surface sizes, slippage preventives and viscosity regulators, etc, and these may be suitably selected and used to manifest the properties required in accordance with paper type, or to enhance operational characteristics. They can be used on their own or two or more types can be Jointly used.
  • the amount of anionic fluorine-based oil-proofing agent added or applied to the paper in the present invention can be suitably adjusted according to the degree of oil resistance required of the paper.
  • the percentage added is normally 0.01 to 10 mass % and preferably 0.1 to 2 mass % in terms of the dry mass of raw material pulp. If the percentage anionic fluorine-based oil-proofing agent added is too low, then even where said anionic fluorine-based oil-proofing agent is fully fixed within the paper, there may not be shown the oil resisting effect required.
  • the amount applied is normally from 0.1 to 50 g/m 2 and preferably 1 to 20 g/m 2 in terms of the dry mass of paper, and it can be suitably adjusted in accordance with the degree of oil resistance of the paper required.
  • the amount of fixing agent added or applied to the paper in the present invention the optimum value thereof needs to be selected in accordance with the degree of oil resistance and other properties required of the paper, the added or applied amount of the anionic fluorine-based oil-proofing agent, the ion balance within the papermaking system and the operational characteristics, etc.
  • the amount of fixing agent added is normally from 0.01 to 10 times, and preferably from 0.1 to 2 times, the added amount by solids concentration of the anionic fluorine-based oil-proofing agent.
  • the anionic fluorine-based oil-proofing agent, and the fixing agent comprising polymer in which at least N-vinylformamide is a polymerization component and/or derivative of said polymer, are the same as those used in the aforesaid method of paper production (1).
  • the paper of the present invention can be produced by the method of paper production in (1) above.
  • Paper in the present invention also includes sheet/board.
  • Examples of the paper types are food packaging paper, food containers, packaging paper for metals and other types of oil-resistant paper, PPC paper, inkjet printing paper, laser printer paper, paper business forms, thermal transfer paper, heat-sensitive recording paper, pressure-sensitive recording paper, groundwood paper and other types of paper employed for information purposes, photographic printing paper and its base paper, art paper, cast-coat paper, lightweight coated paper and other types of coated paper and the base paper therefor, kraft paper, pure white roll paper and other types of packaging paper, and also writing paper, paper for books, various types of paper for printing, newspaper roll paper, manila board, white board, chipboard and other types of board for paperware articles/boxes, liners, water-resistant liners, packing, water-resistant packing, gypsum board base paper and other types of board/sheet, etc.
  • N-vinylformamide 80 g (1125 mmol) of N-vinylformamide was dissolved in 385 g of water in a 2 L capacity flask equipped with a stirrer, thermometer and a means for operating under a nitrogen atmosphere. 0.65 g (2.4 mmol) of 2,2′-azobis-(2-amidinopropane) hydrochloride was mixed therewith and, by introducing nitrogen, oxygen was eliminated. The reaction mixture was then heated to 55° C. within 1 hour. After maintaining for 5 hours at this temperature, in order to enhance the conversion the temperature was raised to 60° C. for 30 minutes and the percentage conversion made 100%.
  • aqueous hydrochloric acid 36% aqueous hydrochloric acid was mixed with the viscous polymer solution thus obtained, then heating carried out for 2 hours at 90° C. and hydrolysis performed.
  • the aqueous polymer solution obtained totalled 534.5 g and its viscosity was 1500 mPa ⁇ s (Brookfield viscosity, 25° C.). It was confirmed by 1 H-NMR that 60% of the formyl groups had been hydrolysed.
  • Reaction was carried out in the same way as in Example 1 except that, instead of 68.5 g (676 mmol) of the 36% aqueous hydrochloric acid used in Fixing Agent Production Example 1, there was mixed 40.5 g (400 mmol) of 36% aqueous hydrochloric acid solution.
  • An aqueous polymer solution was obtained of viscosity 1400 mPa ⁇ s (Brookfield field viscosity, 25° C.) where 40% of the formyl groups had been hydrolysed (as confirmed by 1 H-NMR).
  • Reaction was carried out in the same way as in Example 1 except that, instead of the 68.5 g (676 mmol) of 36% aqueous hydrochloric acid used in Fixing Agent Production Example 1, there was mixed 81.0 g (800 mmol) of 36% aqueous hydrochloric acid solution.
  • An aqueous polymer solution was obtained of viscosity 1600 mPa ⁇ s (Brookfield viscosity, 25° C.) where 80% of the formyl groups had been hydrolysed (as confirmed by 1 H-NMR).
  • the drainage property was determined using equipment identical to the “Dynamic Drainage Jar” described on page 46 of the Tappi Journal Vol. 56, No. 10 (1973), with 500 ml of the pulp slurry being poured into a jar of diameter 7.5 cm and, while stirring at 600 rpm, the lower cock was opened and fluid allowed to pass through a 100 mesh strainer. The time taken to obtain 250 g of filtrate was measured and used for the evaluation.
  • wet paper of weight per unit area 80 g/m 2 was obtained by means of a Noble and Wood handsheet machine.
  • the papermaking pH at this time was 6.8.
  • the wet paper obtained was pressed and then dried for 80 seconds at 100° C. with a drum dryer.
  • the handsheet paper obtained was conditioned for 24 hours at 23° C. and 50% RH, after which measurement of the oil resistance was carried out by means of the “Paper and Board—Oil Repellency Test Method—Kit Method” in Japan Tappi No.41.
  • Handsheet paper was produced in the same way as in Example 1 except that no fixing agent was added.
  • the evaluations were conducted in the same way as in Example 1 and the results are shown in Table 1.
  • Handsheet paper was produced in the same way as in Example 1 except that there was added 0.3% of a commercial fixing agent (produced by Meisel Chemical Works Co., commercial name “AG Fix M-15”) which is a cationic (methacrylate ester/acrylamide type polymer.
  • AG Fix M-15 a commercial fixing agent which is a cationic (methacrylate ester/acrylamide type polymer.
  • Handsheet paper was produced in the same way as in Example 1 except that there was added 0.3% of a commercial fixing agent (produced by the Seiko PMC Corporation, commercial name “Fikstar X-15”) which is a cationic (diallylamine/acrylamide) type polymer.
  • the evaluations were conducted in the same way as in Example 1 and the results are shown in Table 1.
  • TABLE 1 Wet Paper 250 g Oil Stockigt Breaking Drainage Resistance Sizing Length Fixing Agent (secs) (—) (secs) (km)
  • Example 1 Production 14.1 9.0 61 0.39
  • Example 2 Production 8.7 8.5 48 0.46
  • Example 3 Comp. Ex. 1 none 55.7 1.0 28 0.10 Comp. Ex. 2 as stated 18.2 7.0 45 0.15 Comp. Ex. 3 as stated 27.5 4.0 39 0.25
  • Table 1 confirms that by using the fixing agents produced in Production Examples 1 to 3, it is possible to confer on paper outstanding oil resistance, together with outstanding wet strength and water resistance. In addition, it is possible to realize an enhancement in the drainage property.

Landscapes

  • Paper (AREA)
  • Making Paper Articles (AREA)
US10/565,777 2003-07-25 2004-07-20 Method for the production of paper Abandoned US20060201645A1 (en)

Applications Claiming Priority (3)

Application Number Priority Date Filing Date Title
JP2003280455A JP2005042271A (ja) 2003-07-25 2003-07-25 紙の製造方法及び紙
JP03/280455 2003-07-25
PCT/EP2004/008088 WO2005014931A1 (en) 2003-07-25 2004-07-20 A method for the production of paper

Publications (1)

Publication Number Publication Date
US20060201645A1 true US20060201645A1 (en) 2006-09-14

Family

ID=34131471

Family Applications (1)

Application Number Title Priority Date Filing Date
US10/565,777 Abandoned US20060201645A1 (en) 2003-07-25 2004-07-20 Method for the production of paper

Country Status (8)

Country Link
US (1) US20060201645A1 (ja)
EP (1) EP1651814B1 (ja)
JP (2) JP2005042271A (ja)
CN (1) CN100485125C (ja)
AT (1) ATE553254T1 (ja)
CA (1) CA2532943A1 (ja)
PL (1) PL1651814T3 (ja)
WO (1) WO2005014931A1 (ja)

Cited By (10)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2014078102A1 (en) * 2012-11-15 2014-05-22 Ecolab Usa Inc. Emulsification of alkenyl succinic anhydride with an amine-containing homopolymer or copolymer
US8771470B2 (en) 2012-01-17 2014-07-08 Agc Chemicals Americas, Inc. Method of preparing a treated article and treated article formed therefrom
US9702086B2 (en) 2014-10-06 2017-07-11 Ecolab Usa Inc. Method of increasing paper strength using an amine containing polymer composition
US9920482B2 (en) 2014-10-06 2018-03-20 Ecolab Usa Inc. Method of increasing paper strength
US9951475B2 (en) 2014-01-16 2018-04-24 Ecolab Usa Inc. Wet end chemicals for dry end strength in paper
US10145067B2 (en) 2007-09-12 2018-12-04 Ecolab Usa Inc. Method of improving dewatering efficiency, increasing sheet wet web strength, increasing sheet wet strength and enhancing filler retention in papermaking
CN110792004A (zh) * 2019-11-18 2020-02-14 界首市天路包装材料有限公司 一种可降解食品包装纸的抗菌防油改性方法
US10648133B2 (en) 2016-05-13 2020-05-12 Ecolab Usa Inc. Tissue dust reduction
US10889939B2 (en) 2015-12-25 2021-01-12 Ecolab Usa Inc. Sizing method for making paper and paper prepared thereof
US20220356650A1 (en) * 2019-06-27 2022-11-10 Spcm Sa Process for manufacturing paper or cardboard

Families Citing this family (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2005171410A (ja) * 2003-12-10 2005-06-30 Seiko Pmc Corp 紙及び製造方法
WO2009057716A1 (ja) 2007-11-01 2009-05-07 Asahi Glass Company, Limited 含フッ素共重合体および耐水耐油剤組成物、ならびにその製造方法
JP5882047B2 (ja) * 2011-12-22 2016-03-09 大王製紙株式会社 着色板紙
CN103866615B (zh) * 2014-02-25 2016-08-24 苏州恒康新材料有限公司 一种纸张防水剂及其制备方法
JP2018109242A (ja) * 2015-05-13 2018-07-12 旭硝子株式会社 耐油紙および耐油紙の製造方法

Citations (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3492374A (en) * 1963-06-14 1970-01-27 Du Pont Polyfluoropolyoxa-alkyl phosphates
US3597314A (en) * 1967-11-29 1971-08-03 Hoechst Ag Method of improving the drainage of cellulose fiber suspensions with polymers of n-vinyl-n-methyl-formamide
US4808683A (en) * 1986-06-19 1989-02-28 Mitsubishi Chemical Industries Limited Vinylamine copolymer, flocculating agent using the same, and process for preparing the same
US5334287A (en) * 1991-08-22 1994-08-02 Basf Aktiengesellschaft Graft polymers of natural substances containing saccharide structures or derivatives thereof and ethylenically unsaturated compounds and their use
US5491199A (en) * 1995-02-22 1996-02-13 Air Products And Chemicals, Inc. One step production of low salt vinylamine polymers
US6359093B1 (en) * 1995-06-09 2002-03-19 Mitsui Chemicals, Inc. Amphipathic compound having succinic acid skeleton
US6566470B2 (en) * 2000-04-14 2003-05-20 Ciba Specialty Chemicals Corporation Fluorinated polymeric paper sizes and soil-release agents

Family Cites Families (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP0280115B1 (en) * 1987-02-12 1993-01-13 Daikin Industries, Limited Oil proof composition for paper
JP2660312B2 (ja) 1992-05-29 1997-10-08 ヘキスト合成株式会社 含フッ素系水性撥水撥油組成物
IT1256721B (it) * 1992-12-16 1995-12-15 Ausimont Spa Processo per impartire oleo- ed idro-repellenza alla superficie di materiali ceramici porosi
US5672731A (en) * 1994-05-20 1997-09-30 Air Products And Chemicals, Inc. N-vinylformamide/alkyl acrylate Michael adducts

Patent Citations (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3492374A (en) * 1963-06-14 1970-01-27 Du Pont Polyfluoropolyoxa-alkyl phosphates
US3597314A (en) * 1967-11-29 1971-08-03 Hoechst Ag Method of improving the drainage of cellulose fiber suspensions with polymers of n-vinyl-n-methyl-formamide
US4808683A (en) * 1986-06-19 1989-02-28 Mitsubishi Chemical Industries Limited Vinylamine copolymer, flocculating agent using the same, and process for preparing the same
US5334287A (en) * 1991-08-22 1994-08-02 Basf Aktiengesellschaft Graft polymers of natural substances containing saccharide structures or derivatives thereof and ethylenically unsaturated compounds and their use
US5491199A (en) * 1995-02-22 1996-02-13 Air Products And Chemicals, Inc. One step production of low salt vinylamine polymers
US6359093B1 (en) * 1995-06-09 2002-03-19 Mitsui Chemicals, Inc. Amphipathic compound having succinic acid skeleton
US6566470B2 (en) * 2000-04-14 2003-05-20 Ciba Specialty Chemicals Corporation Fluorinated polymeric paper sizes and soil-release agents

Cited By (16)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US10145067B2 (en) 2007-09-12 2018-12-04 Ecolab Usa Inc. Method of improving dewatering efficiency, increasing sheet wet web strength, increasing sheet wet strength and enhancing filler retention in papermaking
US8852400B2 (en) 2010-11-02 2014-10-07 Ecolab Usa Inc. Emulsification of alkenyl succinic anhydride with an amine-containing homopolymer or copolymer
US9624623B2 (en) 2010-11-02 2017-04-18 Ecolab Usa Inc. Emulsification of alkenyl succinic anhydride with an amine-containing homopolymer or copolymer
US10227731B2 (en) 2010-11-02 2019-03-12 Ecolab Usa Inc. Emulsification of alkenyl succinic anhydride with an amine-containing homopolymer of copolymer
US8771470B2 (en) 2012-01-17 2014-07-08 Agc Chemicals Americas, Inc. Method of preparing a treated article and treated article formed therefrom
US9133584B2 (en) 2012-01-17 2015-09-15 Agc Chemicals Americas, Inc. Method of preparing a treated article and treated article formed therefrom
US9499943B2 (en) 2012-01-17 2016-11-22 Agc Chemicals Americas, Inc. Method of preparing a treated article and treated article formed therefrom
WO2014078102A1 (en) * 2012-11-15 2014-05-22 Ecolab Usa Inc. Emulsification of alkenyl succinic anhydride with an amine-containing homopolymer or copolymer
US9951475B2 (en) 2014-01-16 2018-04-24 Ecolab Usa Inc. Wet end chemicals for dry end strength in paper
US9920482B2 (en) 2014-10-06 2018-03-20 Ecolab Usa Inc. Method of increasing paper strength
US9840810B2 (en) 2014-10-06 2017-12-12 Ecolab Usa Inc. Method of increasing paper bulk strength by using a diallylamine acrylamide copolymer in a size press formulation containing starch
US9702086B2 (en) 2014-10-06 2017-07-11 Ecolab Usa Inc. Method of increasing paper strength using an amine containing polymer composition
US10889939B2 (en) 2015-12-25 2021-01-12 Ecolab Usa Inc. Sizing method for making paper and paper prepared thereof
US10648133B2 (en) 2016-05-13 2020-05-12 Ecolab Usa Inc. Tissue dust reduction
US20220356650A1 (en) * 2019-06-27 2022-11-10 Spcm Sa Process for manufacturing paper or cardboard
CN110792004A (zh) * 2019-11-18 2020-02-14 界首市天路包装材料有限公司 一种可降解食品包装纸的抗菌防油改性方法

Also Published As

Publication number Publication date
JP2006528733A (ja) 2006-12-21
CN100485125C (zh) 2009-05-06
JP2005042271A (ja) 2005-02-17
ATE553254T1 (de) 2012-04-15
WO2005014931A1 (en) 2005-02-17
EP1651814B1 (en) 2012-04-11
CA2532943A1 (en) 2005-02-17
EP1651814A1 (en) 2006-05-03
CN1829842A (zh) 2006-09-06
PL1651814T3 (pl) 2012-09-28

Similar Documents

Publication Publication Date Title
CA2547687C (en) Filler-containing paper and a method for the production of filler-containing paper
EP1651814B1 (en) A method for the production of paper
US4749444A (en) Production of paper and cardboard
EP3204554B1 (en) Method of increasing paper bulk strength by using a diallylamine acryamide copolymer in a size press formulation containing starch
EP2363528B1 (en) Aldehyde-functionalized polymers and their use in enhancing paper machine dewatering
US20100000693A1 (en) Method for producing a multi layer fiber web from cellulose fibers
US5262008A (en) Production of paper, board and cardboard in the presence of copolymers containing N-vinylformamide units
KR100187902B1 (ko) 제지용첨가제 및 제지방법
JPS6274902A (ja) 高い乾燥強度及び湿潤強度を有する紙の製法
EP3204553A1 (en) Method of increasing paper strength
KR101186382B1 (ko) 반응성 사이즈제의 수성 분산액, 그의 제조 방법 및 용도
AU2002352927B2 (en) High molecular weight cationic and anionic polymers comprising zwitterionic monomers
CN112601860A (zh) 造纸用添加剂、纸及纸的制造方法
WO2005059251A1 (en) Polyvinylamine as a wet strength resin
JP4868277B2 (ja) 板紙の製造方法
JP4501386B2 (ja) 汚れ防止剤及び汚れ防止方法
JP4562477B2 (ja) 表面サイズ剤、表面サイジング組成物及び紙
JP2002317393A (ja) 層間強度向上剤
JP2005042270A (ja) 蛍光抑制剤及び蛍光抑制方法
JPH1161681A (ja) エマルション組成物、製紙用添加剤、製紙方法及びその製紙方法により製造された紙
NO175383B (no) Fremgangsmåte for fremstilling av papir, papp og kartong i nærvær av kopolymerisater som inneholder N-vinylformamid-andeler

Legal Events

Date Code Title Description
AS Assignment

Owner name: BASF AKTIENGESELLSCHAFT, GERMANY

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNOR:ITO, KENICHI;REEL/FRAME:020150/0825

Effective date: 20040820

AS Assignment

Owner name: BASF AKTIENGESELLSCHAFT, GERMANY

Free format text: CORRECTIVE ASSIGNMENT TO CORRECT THE ASSIGNEE'S INFORMATION PREVIOUSLY RECORDED ON REEL 020150 FRAME 0825;ASSIGNOR:ITO, KENICHI;REEL/FRAME:020375/0176

Effective date: 20040820

Owner name: SEIKO PMC CORPORATION, JAPAN

Free format text: CORRECTIVE ASSIGNMENT TO CORRECT THE ASSIGNEE'S INFORMATION PREVIOUSLY RECORDED ON REEL 020150 FRAME 0825;ASSIGNOR:ITO, KENICHI;REEL/FRAME:020375/0176

Effective date: 20040820

STCB Information on status: application discontinuation

Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION