US20030035231A1 - Optical film having microreplicated structures; and methods - Google Patents

Optical film having microreplicated structures; and methods Download PDF

Info

Publication number
US20030035231A1
US20030035231A1 US09/922,438 US92243801A US2003035231A1 US 20030035231 A1 US20030035231 A1 US 20030035231A1 US 92243801 A US92243801 A US 92243801A US 2003035231 A1 US2003035231 A1 US 2003035231A1
Authority
US
United States
Prior art keywords
axis
light
light directing
film
structures
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US09/922,438
Other languages
English (en)
Inventor
Kenneth Epstein
Richard Griffith
Alan Campbell
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
3M Innovative Properties Co
Original Assignee
3M Innovative Properties Co
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 3M Innovative Properties Co filed Critical 3M Innovative Properties Co
Priority to US09/922,438 priority Critical patent/US20030035231A1/en
Assigned to 3M INNOVATIVE PROPERTIES COMPANY reassignment 3M INNOVATIVE PROPERTIES COMPANY ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: GRIFFITH, RICHARD F., EPSTEIN, KENNETH A., CAMPBELL, ALAN B.
Priority to CNA2006101082004A priority patent/CN1916670A/zh
Priority to CNB2006101109079A priority patent/CN100478715C/zh
Priority to PCT/US2002/023671 priority patent/WO2003014777A2/en
Priority to KR10-2004-7001683A priority patent/KR20040020976A/ko
Priority to CNB028152468A priority patent/CN100464197C/zh
Priority to EP02756659A priority patent/EP1412779A2/en
Priority to US10/205,160 priority patent/US20030058553A1/en
Priority to AU2002322651A priority patent/AU2002322651A1/en
Priority to JP2003519655A priority patent/JP2004538506A/ja
Publication of US20030035231A1 publication Critical patent/US20030035231A1/en
Priority to US10/877,341 priority patent/US20050024754A1/en
Priority to US11/927,202 priority patent/US8579492B2/en
Abandoned legal-status Critical Current

Links

Images

Classifications

    • G—PHYSICS
    • G02—OPTICS
    • G02B—OPTICAL ELEMENTS, SYSTEMS OR APPARATUS
    • G02B5/00—Optical elements other than lenses
    • G—PHYSICS
    • G02—OPTICS
    • G02B—OPTICAL ELEMENTS, SYSTEMS OR APPARATUS
    • G02B5/00—Optical elements other than lenses
    • G02B5/02—Diffusing elements; Afocal elements
    • G02B5/0205—Diffusing elements; Afocal elements characterised by the diffusing properties
    • G02B5/0236—Diffusing elements; Afocal elements characterised by the diffusing properties the diffusion taking place within the volume of the element
    • G02B5/0242—Diffusing elements; Afocal elements characterised by the diffusing properties the diffusion taking place within the volume of the element by means of dispersed particles
    • G—PHYSICS
    • G02—OPTICS
    • G02B—OPTICAL ELEMENTS, SYSTEMS OR APPARATUS
    • G02B5/00—Optical elements other than lenses
    • G02B5/02—Diffusing elements; Afocal elements
    • G02B5/0205—Diffusing elements; Afocal elements characterised by the diffusing properties
    • G02B5/021—Diffusing elements; Afocal elements characterised by the diffusing properties the diffusion taking place at the element's surface, e.g. by means of surface roughening or microprismatic structures
    • G—PHYSICS
    • G02—OPTICS
    • G02B—OPTICAL ELEMENTS, SYSTEMS OR APPARATUS
    • G02B5/00—Optical elements other than lenses
    • G02B5/02—Diffusing elements; Afocal elements
    • G02B5/0273—Diffusing elements; Afocal elements characterized by the use
    • G02B5/0284—Diffusing elements; Afocal elements characterized by the use used in reflection
    • G—PHYSICS
    • G02—OPTICS
    • G02B—OPTICAL ELEMENTS, SYSTEMS OR APPARATUS
    • G02B5/00—Optical elements other than lenses
    • G02B5/04—Prisms
    • G02B5/045—Prism arrays
    • G—PHYSICS
    • G02—OPTICS
    • G02B—OPTICAL ELEMENTS, SYSTEMS OR APPARATUS
    • G02B5/00—Optical elements other than lenses
    • G02B5/08—Mirrors
    • G02B5/09—Multifaceted or polygonal mirrors, e.g. polygonal scanning mirrors; Fresnel mirrors

Definitions

  • LCDs are often illuminated by light which enters one major surface, called the back side, of the LCD, and leaves the other, or front side, where the viewer resides. It is also possible, by means of suitable reflectors, to illuminate LCDs from the front, or viewing, side, and produce an illuminated image by means of ambient light reflected by the reflector, which is commonly called a back reflector. LCDs illuminated in this way are commonly called reflective LCDs, or RLCDs.
  • Specular back reflectors may produce a metallic image appearance, may reflect images of objects located behind or above the viewer, and may provide unacceptably limited viewing angles, which may vary with specific ambient lighting conditions. Moreover, specular reflectors reflect incident light in such a way that the viewer's head may block incident illumination needed for best viewing. Diffuse reflectors, on the other hand, have the disadvantage of inefficient light utilization, in that they may diffuse light into locations in which viewers are unlikely to reside, thereby depriving more desirable viewing positions of illumination. These disadvantages are reduced in U.S. Pat. No.
  • the present invention provides microstructured reflective surfaces which reflect incident light at predetermined angles, and which produce particular directional distributions of reflected light.
  • the microstructured surfaces have a general overall shape with small tilted reflective microstructures built into the surface.
  • the tilted microstructures have a longitudinal variation in height or elevation which is defined by a predefined periodic height or elevation. The height may vary according to a fixed period, a variable but deterministic period, a random period, or combinations thereof.
  • a suitable tool for producing microstructured surfaces according to the present invention can be made by diamond turning the desired pattern in a cylindrical blank made of a suitable metal such as hard copper, and using this cylinder as a casting tool to coat and form a microstructured layer of curable liquid composition onto a film backing.
  • the depth function can be applied to the diamond turning process by means of a piezoelectric device incorporated into the diamond tool holder.
  • Tool holders of this type are commonly referred to as fast tool servos, or FTSs; they may also be commonly referred to as fast servo tools.
  • the signal used to drive the FTS may include single frequency or multiple frequency waves, signals from noise generators, and any other signals found to be useful.
  • Signals may be filtered, so as to, for example, limit the frequency range or spectral profile of the varying height.
  • the signals which can be used to generate the depth function are limited only by the suitability of a particular signal in producing a useful microstructure. Because of the relative simplicity of generating signals for use in the invention, it is also possible to take a very empirical approach to finding suitable signals for the generation of varying heights which produce the desired optical effects.
  • the term reflective optical surfaces includes both highly reflective surfaces, such as mirrors, and optical surfaces which only partially reflect and which transmit significant amounts of light. Partial reflectors of this type are commonly referred to as transflective optical surfaces.
  • the reflective surfaces of the present invention can be made reflective by, for example, metallizing with a suitable metal such as silver. Protective and other surface modifying coatings may also be incorporated.
  • Optical films having the reflective surfaces of the present invention are useful as back reflectors for LCDs, since they can be designed to reflect light in a useful range of directions, and can produce closely controlled distributions of light which more efficiently utilize available light and avoid glare effects.
  • additional surface treatments such as chemical etching of the tool, may also be used to provide diffusion or other directional components to the reflected light distribution.
  • Plating of the tool may be useful in improving durability of the tool and surface quality of the microstructured product.
  • the present invention is directed to a light directing film having an x-axis, a y-axis, and a z-axis, the film having a first structured surface and an opposing surface.
  • the structured surface has a plurality of elongate prismatic structures thereon, the elongate prismatic structures extending generally along the x-axis and having a spacing along the y-axis between adjacent prismatic structures.
  • the structures also have a height along the z-axis, the height of the prismatic structure varying along the x-axis in a repeating period.
  • the present invention is to an optical device comprising a microreplicated light reflecting film, the film comprising a plurality of prismatic structures having a length, each of the plurality of prismatic structures having a height varying along the length in a repeating period.
  • a metal film layer can be present on the film.
  • the invention is directed to an article made using a programmably controlled cutting tool, the article having an x-axis, a y-axis, and a z-axis, the article comprising a plurality of structures extending generally along the x-axis, the plurality of structures having a spacing along the y-axis between adjacent prismatic structures, and the structures having a height along the z-axis, the height of the structure varying along the x-axis in a repeating pattern.
  • Methods for making a reflective structured film comprise machining a master tool from a blank with a cutting tool, the cutting tool being movable in an x-direction, a y-direction, and a z-direction.
  • the machining comprises contacting the blank with the cutting tool; moving at least one of the blank and the cutting tool in relation to one another in the x-direction to cut the blank; moving at least one of the blank and the cutting tool in relation to one another in the y-direction to cut the blank; and moving at least one of the blank and the cutting tool in relation to one another in the z-direction to cut the blank.
  • On this machined master tool forming a structured film; and then applying a reflective coating to the structured film.
  • the methods of the present invention provide structured films that are more precise, more accurate, and more exact than film made by methods such as chemical etching, bead blasting, or other stochasitic surface modification techniques.
  • Methods such as chemical etching, bead blasting, and other stochasitic surface modification techniques are not capable of reproducing exactly, for example to 0.001 micrometer, and even less to 0.0001 micrometer, the exact form from one prismatic structure to the next.
  • FIG. 1A is a schematic cross-sectional view of a display apparatus incorporating a light directing construction.
  • FIG. 1B is an enlarged schematic cross-sectional view of a portion of the light direction construction of the display apparatus of FIG. 1A.
  • FIG. 2A is a schematic depiction of the coordinate system used to quantitatively describe the light distribution seen by a viewer of a display apparatus
  • FIG. 2B is a schematic perspective view of a light directing film, indicating the relative axis for the construction.
  • FIG. 2C is a schematic plan view of a cylindrical tool that can be used for manufacturing a light directing film.
  • FIG. 3 is a schematic cross-sectional view of a conventional light directing construction having a conventional structure layer.
  • FIG. 4 is a graphical representation of the reflected light intensity of the light directing film of Comparative Example 1, shown in FIG. 3, as measured on an ELDIM EZ Contrast model 160R used in the reflective mode with 34 degree incident collimated light.
  • FIG. 5 is a schematic cross-sectional view of a first embodiment of a light directing construction according to a first aspect of the present invention.
  • FIG. 6 is a schematic cross-sectional view of a second embodiment of a light directing construction according to the present invention.
  • FIG. 7 is a graphical representation of the reflected light intensity of the light directing film of Example 3A, generally shown in FIG. 6, as measured on an ELDIM EZ Contrast model 160R used in the reflective mode with 34 degree incident collimated light.
  • FIG. 8 is a graphical representation of the reflected light intensity of the light directing film of Example 3B, generally shown in FIG. 6, as measured on an ELDIM EZ Contrast model 160R used in the reflective mode with 34 degree incident collimated light.
  • FIG. 9 is a schematic cross-sectional view of a third embodiment of a light directing construction according to the present invention.
  • FIG. 10A is a schematic perspective view of a fourth embodiment of a light directing film according to the present invention.
  • FIG. 10B is a schematic perspective view of a fifth embodiment of a light directing film according to the present invention.
  • FIG. 11 is a graphical representation of the reflected light intensity of the light directing film of Example 5 as measured on an ELDIM EZ Contrast model 160R used in the reflective mode with 34 degree incident collimated light.
  • FIG. 12 is a graphical representation of the reflected light intensity of the light directing film of Example 6 as measured on an ELDIM EZ Contrast model 160R used in the reflective mode with 34 degree incident collimated light.
  • FIG. 13 is a graphical representation of the reflected light intensity of the light directing film of Example 7 as measured on an ELDIM EZ Contrast model 160R used in the reflective mode with 34 degree incident collimated light.
  • FIG. 14 is a schematic cross-sectional view of a sixth embodiment of a light directing construction according to the present invention.
  • FIG. 15 is a graphical representation of the reflected light intensity of the light directing film of Example 8 as measured on an ELDIM EZ Contrast model 160R used in the reflective mode with 34 degree incident collimated light.
  • FIG. 16 is a graphical representation of the reflected light intensity of the light directing film of Example 9 as measured on an ELDIM EZ Contrast model 160R used in the reflective mode with 34 degree incident collimated light.
  • FIG. 17 is a schematic cross-sectional view of a seventh embodiment of a light directing construction according to the present invention.
  • FIG. 18 is a schematic cross-sectional view of an eighth embodiment of a light directing construction according to the present invention.
  • FIG. 19 is a photomicrograph of a ninth embodiment of a light directing film of the present invention when viewed under a scanning electron microscope.
  • FIG. 20 is a photomicrograph of a tenth embodiment of a light directing film of the present invention when viewed under a scanning electron microscope.
  • FIG. 21 is a schematic top plan view of a light directing film according to another aspect of the present invention.
  • FIG. 22 is a graphical representation of the cross-sectional view of the reflected light intensity of the light directing film of Examples 1, 5 and 17 as measured on an ELDIM EZ Contrast model 160R used in the reflective mode with 34 degree incident collimated light.
  • the present invention is directed to an optical film that improves the utilization of light in a reflective liquid crystal display (RLCD) by precisely shaping the pattern of light diffusely reflected by the RLCD. Specifically, the distribution of reflected light is shaped as desired for greater uniformity and brightness by designing the surface features of the back reflector of the RLCD to reflect in particular directions.
  • RLCD reflective liquid crystal display
  • an optical film is a film having a structured or prismatic surface that includes structures that reflect the light at desired angles in respect to the RLDC.
  • a reflective display apparatus 10 such as an RLCD, is shown in FIG. 1A.
  • Display apparatus 10 uses ambient light to illuminate displayed information viewable through an additional optional component 14 , which may be a lens, touch screen, or other like element of display apparatus 10 .
  • Component 14 may contribute specific optical qualities to the display, and may receive input from the user of the display.
  • Display apparatus 10 further includes a light modulating layer 20 , containing a top polarizer 22 , a liquid crystal layer 24 , and a bottom polarizer 26 .
  • a light directing construction 28 which includes the light directing film, is located adjacent to bottom polarizer 26 . It has been found useful and convenient in some embodiments for light directing construction 28 to be attached to bottom polarizer 26 .
  • the light directing film of the present invention may also be incorporated into a display device that includes only one polarizer or no polarizers (for example, a guest-host LCD), although it will more commonly be used in a device having two polarizers that sandwich the liquid crystal layer.
  • a display device that includes only one polarizer or no polarizers (for example, a guest-host LCD), although it will more commonly be used in a device having two polarizers that sandwich the liquid crystal layer.
  • a typical display apparatus 10 has been described herein. It is understood that generally any of the layers may be altered or eliminated and still have a usable display 10 ; additional layers can also be added.
  • a compensation layer or film is a non-isotropic optically refractive film that can be included in the display apparatus.
  • the various layers may be rearranged or reorganized to provide a different structure that functions as a usable display. In some embodiments, a single layer may function as two layers described above. Still further, any multiple layers may be adhered or laminated together to provide fewer discrete layers. For example, the light directing film could be laminated to the polarizer or to a compensation film. All permutations of display apparatus 10 , which incorporate a light directing film as taught by the present invention, are disclosed herein.
  • an ambient light source 30 produces incoming ambient light rays 32 .
  • light ray 32 from source 30 is incident on the display apparatus at angle a from the normal.
  • the normal is the direction perpendicular to the display surface.
  • a portion of the incoming light will be reflected as glare, illustrated by glare ray 34 in FIG. 1A, by the top surface of display apparatus 10 and internal interfaces.
  • the glare ray 34 has a glare angle, b, from the normal. If the interfaces encountered by ray 32 are specularly reflecting surfaces, glare angle b will be equal to angle of incidence a. Since angle a can include a range of values, representing light from various sources which are likely to be present, glare will be visible over a range of viewing angles, but will typically have one or more brightness peaks, at, for example, glare angle b.
  • a significant portion of the incoming light will pass through light modulating layer 20 and be reflected by light directing construction 28 , thereby illuminating the display information or image, e, and emerging as image ray 38 .
  • the light directing construction 28 is designed to direct the image ray 38 so that it will emerge from the display 10 at an angle from the normal that is substantially different than the glare angle b. This is generally referred to as “beam-steering”.
  • the specific angle of image ray 38 is usually governed by Snell's Law of Refraction and the specific properties of light directing construction 28 .
  • light directing construction 28 shown as a structured layer, is provided to steer the image produced by light modulating layer 20 toward a desired viewing angle, which is substantially different than a glare angle of display 10 .
  • Light directing construction 28 may also be referred to as a beam steering film or tilted mirror film.
  • incoming light ray 32 is incident on the display apparatus at angle a from normal, represented by line 33 .
  • the normal is the direction perpendicular to the display surface.
  • Incoming light ray 32 is refracted by the various components of display 10 , creating a bend in light ray 32 , thereby forming light ray 32 ′. That portion of the incoming light not reflected as glare will pass through light modulating layer 20 and be reflected by light directing construction 28 , thereby illuminating light modulating layer 20 and producing image ray 38 .
  • the specific angle of reflectance from light directing construction 28 is dependent on the angle of facet 36 , designated by angle d. It will be appreciated that while FIG.
  • FIG. 1B portrays facet 36 as a flat surface having a single angle d, other, nonflat, facets may be used, and in some cases may be preferred, depending upon specific lighting conditions and viewing angles desired. Note again that as image ray 38 passes through display 10 , the ray is refracted, creating a bend in image ray 38 , so that it emerges at angle c from normal.
  • the range of viewing angles over which the image can be viewed, and the range of viewing angles at which peak brightness occurs, can be controlled by the specific design of light directing construction 28 .
  • the peak image angle or optimal viewing angle is nearly normal to the display, as represented by image ray 38 .
  • a viewer of the display apparatus 10 at position 44 can view the display image clearly without interference from the glare image which is at angle b from image ray 38 .
  • the peak image angle or optimal viewing angle is at angle c to the display normal, as represented by image ray 38 .
  • a viewer of the display apparatus 10 can view the display image clearly without interference from the glare image, which is at a different angle, b to the display.
  • Light directing construction 28 is a structured, prismatic, light directing film that has a smooth surface 31 and structured surface 33 , as will be described in detail below in reference to the Figures.
  • Smooth surface 31 lies away from the back of display 10 and the structured surface lies toward light modulating layer 20 , facing light source 30 .
  • the structured surface could lie facing away from display 10 .
  • surface 31 is described here as smooth, it is understood that the surface could be rough, wavy, textured, or could have prismatic structures thereon. Variations on light directing construction 28 and its operation in the invention will be described in greater detail below.
  • the present invention is directed to designing a light directing construction to provide a desired image beam intensity distribution over a desired range of angles.
  • the direction and angular extent of the reflected beam can be varied by the specific construction of the prismatic light directing film.
  • the coordinate system used to quantitatively describe the light distribution seen by a viewer of an RLCD is shown in FIG. 2A.
  • point “P” may be the viewer, a photometer for measuring luminance, a light source, or other item of interest.
  • Point “P” has spherical coordinates 0 (theta), called the azimuthal angle, or simply azimuth; ⁇ (phi), called the polar angle; and ⁇ (rho), called the radial coordinate.
  • point 29 is a point on display 25
  • edge 23 is the top of the display, as seen by a viewer.
  • Tests of distribution of reflected light are typically done using collimated light incident at a polar angle ⁇ of 34° and an azimuth of 0°.
  • the particular effects of the beam-steering can be seen when the physical examples are characterized with an ELDIM EZ Contrast model 160R photometer, a conoscopic photometer, used in the reflective mode with 34 degree incident collimated light.
  • the ELDIM instrument measures the reflected luminance as a function of ⁇ and ⁇ , and plots the data over the polar angle range from 0 degrees (film normal) to 80 degrees (10 degrees out of the film plane) and over the full 360 degree azimuthal angle range.
  • the optical gain is obtained by normalizing the sample luminance with respect to the luminance of a white lambertian standard measured under the same conditions. Plots using this coordinate system can be seen in FIGS. 4, 7, 8 , 11 , 12 , 13 , 15 and 16 , where ⁇ is represented as degrees around the circular plot, starting at the top of the plot and rotating counterclockwise, while ⁇ is represented by radial distances from the center of the plot.
  • FIG. 2B is a perspective view of a general light directing construction showing a prismatic structure.
  • the following examples will be described using the axes shown in FIG. 2B.
  • the “x-axis” or “x-direction”, also referred to as the longitudinal direction of the structure, is in the direction of the ridges, or microstructures
  • the “y-axis” or “y-direction” is orthogonal to the x-axis, and transverses the face of the structures, so that the x and y axes define reference plane 29 , which defines the overall shape of light directing element 28 , and the “z-axis” or “z-direction” is perpendicular to the plane formed by the x and y-axes, extending from the back to the front of light directing element 28 .
  • Light directing constructions having structures 33 can be conveniently produced using a cylindrical casting tool of the type portrayed in FIG. 2C.
  • cylindrical tool 40 having center axis 42 , is produced by cutting circumferential grooves 43 in a cylindrical blank.
  • the grooves are of shapes suitable for producing structures 33 when a suitably formable material is placed between grooves 43 and a backing material such as a flexible polymeric film.
  • the x and y directions relative to the tool as shown in FIG. 2C, are consistent with the x and y directions on the light directing film shown in FIG. 2B.
  • the light directing film of the present invention may be of any formable material, and is typically transparent. UV polymerizable materials, including acrylics, and polycarbonates are preferred materials.
  • the UV polymerizable composition for making the light directing film includes a vinyl monomer, for example, an alkyl styrene monomer such as methyl styrene, and various co-monomers and/or oligomers.
  • the composition comprises each of bisphenol-A epoxy diacrylate, novolak epoxy acrylate, and a vinyl monomer, which includes alkyl styrenes (for example, methyl styrene); such a composition is considered an “epoxy acrylate”.
  • An initiator may be added to provide a free radical source to initiate polymerization of the composition to a polymerized structure.
  • One example of a preferred UV polymerizable epoxy acrylate composition for use in the light directing film includes the following components, which are listed with a range of percentage weight: bisphenol-A epoxy diacrylate (55-80%), acrylated epoxy (1-10%), methyl styrene (5-25%), a photoinitiator (0.25-5%) (such as “Lucirin TPO”), and a fluorosurfactant (0.1-0.3%). Further, the composition can include a second photoinitiator, such as “Irgacure 184”, at a percentage weight up to about 5%. Additional details regarding these preferred UV-curable compositions are found in U.S.
  • a reflective coating can be provided on the structured film.
  • This reflective coating can be opaque, or can be a metal such as silver, chromium, nickel, aluminum, titanium, aluminum-titanium alloy, gold, zirconium, platinum, palladium, aluminum-chromium alloy, rhodium, or combinations.
  • a preferred reflective metal coating is silver.
  • the reflective coating may be continuous or discontinuous; discontinuous coatings can be achieved by applying a discontinuous coating or by removing portions of a continuous coating.
  • Additional layers such as adhesion promoting layers, diffusion barrier layers, and anticorrosion layers may also be used to improve the performance and durability of the reflective metal coating.
  • adhesion promoting layers such as adhesion promoting layers, diffusion barrier layers, and anticorrosion layers may also be used to improve the performance and durability of the reflective metal coating.
  • diffusion barrier layers such as diffusion barrier layers, and anticorrosion layers.
  • anticorrosion layers may also be used to improve the performance and durability of the reflective metal coating.
  • a diffuser layer is preferably coated over the structured film to hide film defects and eliminate moiré effects.
  • the light directing films of the present invention provide sufficient light diffusion because of the prismatic structure, so that the diffuser layer is not needed to provide diffusion of the reflected light.
  • a diffuser layer is a polymethyl-methacrylate polymer loaded with polymeric or glass beads.
  • the polymer host or carrier generally has a refractive index of 1.4 to 1.5, although it could be greater or less.
  • the beads either polymeric or glass, generally have a refractive index of 1.35 to 1.7.
  • the difference in refractive index between the beads and the host or carrier polymer is the determinate property when selecting beads and polymer.
  • the difference in refractive indexes in most applications, is 0.01 to 0.2, preferably 0.02 to 0.1.
  • the average diameter of the beads is generally 0.5 to 20 micrometers, with 2 to 5 micrometers being the preferred bead diameter when used for handheld display devices.
  • the amount of beads loaded into the polymer depends on the average diameter of the beads. Small diameter beads lead to less bead volume loading and larger diameter beads lead to higher volume loading. As an example, for refractive index differences about 0.05 and bead diameters about 5 micrometers, useful loading levels are 1% to 10%.
  • a diffuser layer when loaded fairly densely with beads, disperses light from distant sources to provide a uniformly luminous back reflection with no discernable image of the source and hides defects and artifacts.
  • PCT published application WO 97/01610 (Goetz et al.), incorporated herein by reference, teaches a light diffusing adhesive that can be used with the films of the present invention to mask defects and other artifacts.
  • Another technique for creating random scattering includes providing a matte finish on the tool, which can be obtained by acid etching, ionic plating, or bead blasting the structured copper tool after machining the grooves.
  • Absorbing dyes or pigments can be added to the composition, or to other layers within the light directing construction, to alter the color of the display. For example, a silver metal film, when viewed in ambient light, often has a slightly yellow appearance. An absorbing dye can be added to the construction to compensate for the yellow appearance and provide a color-neutral reflector.
  • the light directing film can be made by many different methods known in the art, such as by applying the polymerizable composition between a substrate and a tool or mold having a plurality of cavities having the inverse shape of the prism and polymerizing the composition under UV radiation, and then separating the sheet from the tool.
  • Other methods for forming prismatic structures are also known and may be utilized in the present invention. Because of the small size of the prisms, the process of producing the three-dimensional structure is often referred to as “microreplication”. For additional information regarding microreplication of three-dimensional structures, see for example, U.S. Pat. No. 5,183,597 (Lu), which is incorporated herein by reference.
  • the tool by which the prisms are formed, may be made by known diamond turning techniques, as disclosed, for example, in commonly assigned laid-open PCT Application WO 00/48037, incorporated herein by reference.
  • the master tool is made by diamond turning on a cylindrical blank known as a roll.
  • the surface of the roll is typically of hard copper, although other materials may be used.
  • the prism structures are formed in continuous patterns around the circumference of the roll.
  • the grooves are produced by a technique known as thread cutting. In thread cutting, a single, continuous groove is cut on the roll (in the x-direction) while the diamond bit is moved in a direction transverse (the y-direction) to the turning roll. The distance between adjacent cuts is referred to as the “pitch”. To provide structures with a constant pitch, the diamond bit is moved at a constant velocity.
  • the apparatus used in methods and for making the light directing films of the present invention includes a fast servo tool.
  • a fast tool servo is a solid state piezoelectric device which rapidly adjusts the position of the cutting tool.
  • FTS fast tool servo
  • One type of FTS is known as a PZT.
  • the FTS allows for major axis of movement of the cutting tool in the y-direction and the z-direction, and also provides oscillation or other minute modulation in the y-direction and the z-direction.
  • the movement in the x-direction is provided for by the rotation of the workpiece, in this case the cylinder being cut. Oscillation, if present, is generally superimposed over the major cutting tool movement.
  • the cutting tool can be rocked or rotated about the x-axis during the machining to provide yet another feature.
  • the z direction movement of the diamond cutting tool can be used to form the ridges, by, for example, driving the FTS with a signal produced by a periodic ramp function, to form a series of facets.
  • the transition between the top of one ridge and bottom of the next ridge may be somewhat rounded, due to limitations on the frequency response of the FTS.
  • Ramp functions of this sort would produce ridge-like structures which provide net changes in direction of reflected light in accordance with the present invention.
  • the longitudinal direction of the prism structures will be parallel to the axis of rotation of the tool being cut, rather than perpendicular to it.
  • the ridges may not be continuous, or synchronized, over the entire tool; rather, the ridges may be asynchronous.
  • the rounded transition regions of the casting tool may also serve to improve the appearance of the RLCD.
  • the diamond cutting tool may be provided with a curved or other suitable cutting profile in order to further modify reflected light distributions.
  • the prismatic structures can be made by methods other than described above.
  • the structure of the master tool can be transferred on other media, such as to a belt or web of polymeric material, by a cast and cure process from the master tool to form a production tool; this production tool is then used to make the prismatic structure.
  • Other methods such as electroforming can be used to copy the master tool.
  • Another alternate method to make the light directing film is to directly cut or machine a transparent material to form the prismatic structures.
  • the prismatic structures and methods of the present invention are limited only by the signals that can be generated, and frequency response of the electronics, the FTS actuator and mechanical properties of the tool surface.
  • Chemical etching, bead blasting, or other stochasitic surface modification techniques are typically not capable of forming the sharp, precise prismatic structures, and the breadth of features, desired to obtain the light diffusion characteristic achieved with a cutting tool using the methods of the present invention. These unacceptable methods are not capable of producing highly accurate, repeating structures as in accordance with the present invention, because the inherent impreciseness and unrepeatability associated with chemical etching, bead blasting, and other stochasitic surface modification techniques.
  • Example light directing films were produced by microreplicating a UV sensitized epoxy acrylate resin in a tool that had been cut with a diamond cutter or bit to produce a facet profile. While the epoxy acrylate resin was on the tool, 5 mil (127 micrometer) PET substrate was adhered to the exposed surface of the resin. After the epoxy acrylate resin was polymerized via UV radiation, the resulting light directing film was removed from the tool.
  • the master tool for each of the Examples was produced by machining a copper sheet or blank, that was formed to a cylinder, with a diamond tip cutting tool. To begin the machining process, the cutting tool was lowered into the copper blank in the z-direction. The cylinder rotated around its central axis, thus moving the cutting tool in the x-direction. The cutting tool was constantly moved along the surface of the cylinder in the y-direction, thus producing a spiral groove on the cylinder surface. For some Examples, the diamond cutting tool was moved in the z-direction by a FTS (“fast tool servo” or “fast servo tool”). The machined copper sheet was removed from the cylinder and used to make the light directing film.
  • FTS fast tool servo
  • fast servo tool fast servo tool
  • FIG. 3 is an enlarged cross-sectional view of a first example of a light directing construction 100 , which includes a conventional light directing film 110 .
  • a conventional light directing film 110 is available from Minnesota Mining and Manufacturing Company (3M) under the designation “Tilted Mirror Film 6.3”.
  • This view of light directing film 110 is similar to the orientation shown in FIG. 1B, with the y-axis extending across the structure from left to right in the figure, and the z-axis extending top to bottom of the figure. The x-axis extends into the page.
  • Light directing film 110 has a smooth surface 112 and a structured surface 114 .
  • Structured surface 114 includes a plurality of triangular prisms 140 , each having a first prism face 142 and a second prism face 144 , alternating with valleys 143 and peaks 145 .
  • First prism face 142 and second prism face 144 together define the pitch or period of the light directing film 110 .
  • light directing film 110 is defined by a repeating array of angular prisms 140 .
  • the pitch of the repeating prisms 140 measured from either valley 143 to valley 143 , or peak 145 to peak 145 , is generally between 10 ⁇ m and 100 ⁇ m and more preferably between about 30 ⁇ m and 80 ⁇ m.
  • light directing film 110 has a 50 micrometer pitch. That is, the length in the y-direction between repeating peaks 145 is 50 micrometers.
  • First prism face 142 is generally referred to as a “facet” or “reflective facet”, because the majority of light reflected by light directing construction 100 is reflected by first prism face 142 .
  • first prism face 142 has a 6 degree elevation from the y-direction, which is also referred to as mirror angle. It is understood that angles other than 6 degrees can be used. Generally, angles of 0 to 30 degrees, preferably 5 to 9 degrees, are used.
  • Each prism 140 has a peak angle or included angle, defined by first prism face 142 and second prism face 144 .
  • Each peak 45 has the same peak angle, about 86 degrees.
  • Light directing film 110 is positioned on substrate 120 ; specifically, smooth surface 112 of light directing film 110 is positioned against substrate 120 .
  • An adhesive can be used to secure light directing film 110 onto substrate 120 , or light directing film 110 can be adhered onto substrate 120 by the same material that forms prisms 140 .
  • substrate 120 is the substrate used during the microreplication process.
  • a reflective metal coating 130 which is positioned over structured surface 114 of light directing film 110 .
  • Reflective metal coating can be silver or any other useful coating.
  • a diffuser layer 135 such as a polymethylmethacrylate polymer loaded with polymeric or glass beads.
  • the diffusion caused by diffuser layer 135 is rotationally symmetrical around the peak of light reflected by light directing film 110 , thus the diffusion width in the YZ plane is the same as the width in the XZ plane.
  • Comparative Example 1 The specific prism and facet dimensions for Comparative Example 1 are provided in Tables 1 and 2 below; all measurements are provided in micrometers.
  • the light reflectance of Comparative Example 1 was measured on an ELDIM EZ Contrast model 160R used in the reflective mode with 34 degree incident collimated light;
  • FIG. 4 is the resulting plot.
  • FIG. 4 shows the sharp glare peak at 34 degrees and the broader back reflected peak centered at 14 degrees. Overall, the reflected light is present as a steep peak, with a higher intensity in the center and gradually decreasing until no reflected light is measured.
  • the light directing constructions of the present invention differ from the sample of Comparative Example 1 in that the reflection of the light is manipulated and steered by the prismatic structures to provide a desired light distribution.
  • a flat or top hat distribution of light intensity rather than a peaked or bell shaped curve distribution, is desired; this is achieved when a collimated beam of light is scattered by the surface into a constant luminance within a specified angle of width, centered in a direction also determined by the prismatic features.
  • the beam steering property may bias the reflectance angle away from the glare direction by any reasonable amount, such as from 0 to 45 degrees.
  • the structures can be formed so that each structure does not have the same facet angle as the adjacent structures.
  • the reflectance of light by the light directing film is altered, providing a diffused reflectance in the YZ plane over a wide range of angles.
  • FIG. 5 is a cross-sectional view of a light directing construction 200 , which includes a light directing film 210 , according to one aspect of the present invention.
  • This view of light directing film 210 is similar to the orientation shown in FIG. 2, with the y-axis extending across the structure from left to right in the figure, and the z-axis extending top to bottom of the figure. The x-axis extends into the page.
  • Light directing film 210 has a smooth surface 212 and a structured surface 214 , which create a plurality of prisms 240 having a first prism face 242 and a second prism face 244 that define valleys 243 and peaks 245 .
  • First prism face 242 and second prism face 244 form a pair of faces that define a composite.
  • first prism face 242 is used for reflecting light; second prism face 244 does not participate in light reflectance or direction.
  • Smooth surface 212 of film 210 is adjacent substrate 220 .
  • Overlying light direction film 210 is a metal coating 230 and a diffuser layer 235 .
  • prisms 240 are not all the same; see prisms 251 , 252 , 253 , 254 .
  • Prism 251 is different than prism 252 , which is different than prism 253 , and so on. It is understood that not every prism of light directing film 210 is different than every other prism of light directing film 210 . Rather, it is desired that a prism is different than the adjacent prism or prisms.
  • prism 252 is different than adjacent prism 251 and is also different from adjacent prism 253.
  • the prisms differ, at least, in that the reflective facets, i.e., first prism face 242 , have differing slopes, thereby increasing optical diffusion; the slope of first prism face 242 is generally measured from smooth surface 212 .
  • First prism face 242 of the various prisms will generally vary in length in relation to the slope of first prism face 242 .
  • peaks 245 of the prisms will be equally distanced from smooth surface 212 , however, in some instances, as is shown in FIG. 5, adjacent peaks 245 may have different heights.
  • Diffuser layer 235 is a low-density diffuser material, such as a polymethylmethacrylate polymer loaded with polymeric or glass beads 236 . Diffuser layer 235 , having less beads than diffuser layer 135 of light directing construction 100 , hides defects and artifacts, and integrates multiple reflection peaks generated by the varying prism angle.
  • the various angles in the YZ plane can be made by rocking the diamond cutting bit used to make the master tool with a high frequency periodic or random motion to produce a more optically diffuse surface.
  • the variable prism angle provides diffusion in the YZ plane. That diffusion, superimposed on the diffusion from volume diffuser layer 235 provides an additional degree of freedom to differentiate the diffusion widths in the XZ and YZ planes.
  • the master tool can be cut with a shaped diamond-cutting bit, resulting in the bit shape being non-planar or non-linear.
  • the tool can be cut by multiple passes with the cutting bit positioned at a different angle and in a different position than for a previous pass.
  • the resulting non-planar facets provide a beam-steering effect and controlled light diffusion in the YZ plane, which adds to the random diffusion of diffuser layer.
  • the curved or non-linear cutting edge of the diamond bit or cutter provides the variable slope desired to provide diffusion of the light. Further, the precise shape of the cutting edge determines the diffusion profile.
  • FIG. 6 is a cross-sectional view of a light directing construction 300 according to another aspect of the present invention.
  • This view of light directing construction 300 , and light directing film 310 is similar to the orientation shown in FIG. 2, with the y-axis extending across the structure from left to right in the figure, and the z-axis extending top to bottom of the figure. The x-axis extends into the page.
  • Light directing construction 300 includes a light directing film 310 having a smooth surface 312 and a structured surface 314 , which includes a plurality of prisms 340 having a first prism face 342 and a second prism face 344 that define valleys 343 and peaks 345 .
  • Smooth surface 312 is adjacent substrate 320 .
  • Overlying light direction film 310 is a metal coating 330 and a diffuser layer 335 having a low concentration of glass or polymeric beads 336 to mask artifacts and defects.
  • First prism face 342 rather than being a linear face such as face 142 of FIG. 3 and face 242 of FIG. 5, has a curvature associated with it.
  • the curved surface spans surface angles from a few degrees to several degrees around the average surface angle. That is, a line drawn tangential to first prism face 342 would have be at an angle of 0 to 30 degrees to smooth surface 312 , typically 4 to 8 degrees.
  • the curved first prism face 342 forms a reflective facet that can be used to weight the reflected light into a shaped lobe. Alternately, the curved first prism face 342 can be structured to provide a square reflectance profile.
  • Example 3A was the light directing film 310 alone, and Example 3B had coated onto light directing film 310 a diffuser layer 335 having a 6% volume concentration of polymeric beads.
  • the specific prism and facet dimensions for Examples 3A and 3B are provided in Tables 1 and 2 below.
  • Examples 3A and 3B were characterized with an ELDIM EZ Contrast model 160R used in the reflective mode with a 34 degree incident collimated light source and the resulting plots are shown in FIGS. 7 and 8, respectively.
  • Example 3A Similar to Example 2 above, the non-linear facets provides diffusion in the YZ plane, as seen in FIG. 7. As seen in FIG. 8, that diffusion, superimposed on the diffusion from volume diffuser layer 335 provides an additional degree of freedom to differentiate the diffusion widths in the XZ and YZ planes.
  • FIG. 9 is a cross-sectional view of a light directing construction 400 according to another aspect of the present invention.
  • Light directing construction 400 includes a light directing film 410 having a smooth surface 412 and a structured surface 414 .
  • Light directing film 410 is oriented similar to the orientation shown in FIG. 2, with the y-axis extending across the structure from left to right in the figure, and the z-axis extending top to bottom of the figure. The x-axis extends into the page.
  • Light directing film 410 includes a plurality of prisms 440 having a first prism face 442 and a second prism face 444 that define valleys 443 and peaks 445 .
  • Smooth surface 412 is adjacent substrate 420 .
  • Overlying light direction film 410 is a metal coating 430 and a diffuser layer 435 having a low concentration of glass or polymeric beads 436 to mask artifacts and defects.
  • First prism face 442 includes at least two sections, with adjacent sections, if linear, having different slopes, or if curved, having different curvature or different center of curvature. It is possible to have two different curvatures with different centers of curvature such that the curves blend smoothly with no discontinuity in the first derivative at their junction point.
  • first prism face 442 can be formed by a single diamond bit having multiple faces or segments on the diamond; the segments can be blended arc segments, straight segments, or a combination. Alternately, a diamond bit having a single segment can be used to make multiple cuts, or the cuts can be made with multiple diamond bits having the same or different shaped diamonds.
  • the at least two sections which form segmented first prism face 442 reflect collimated light into two or more separate peaks, depending on the number of sections.
  • diffuser layer 435 not only masks any artifacts and defects, but also combines, or at least evens out, the individual reflected light peaks formed by segmented first prism face 442 .
  • Example 4 The sectioned facets of Example 4, similar to Examples 2 and 3, provide diffusion in the YZ plane. That diffusion, superimposed on the diffusion from volume diffuser layer 435 provides an additional degree of freedom to differentiate the diffusion widths in the XZ and YZ planes.
  • the light diffusion in the orthogonal direction can be designed by varying or oscillating the structure height (in the z-axis or in the z-direction) along the length of the structure or along each row, which is the x-direction.
  • the structure height can be varied when making the master tool, by controlled coordinated motion of the diamond cutting bit in and out of the master tool surface as the tool progresses in the x-direction.
  • the motion provides a pattern of hillocks, which in turn provides variably sloped surfaces that diffuse light.
  • the precise shape of the hillocks determines the specific diffusion profile.
  • the wavelength of the hillocks, or other shaped structure is generally 10 to 1000 micrometers.
  • the amplitude is generally 0.1 to 10 micrometers, and often about 1 micrometer to 8 micrometers.
  • a fast tool servo or fast servo tool (FTS) actuator can be used to move the tip of the diamond cutting bit in the z-direction as the tool progress in the x-direction.
  • FTS fast servo tool
  • the cross-sectional shape or area of the structures in the YZ plane, such as the orientation shown for Examples 1 through 4 in FIGS. 3 through 9, can be any orientation, whether or not illustrated in the Examples.
  • FIGS. 10A and 10B Schematic drawings of light directing films having the structure height vary along the length of the structure in the x-direction are shown in FIGS. 10A and 10B.
  • FIG. 10A the cross-sectional area of the structures in the YZ plane is similar to that of light directing film 310 of FIG. 6.
  • Examples 5, 6, and 7 were produced by heat forming a 250 micron (micrometer) thick (10 mil) acrylic film on a structured copper tool under heat and pressure.
  • the copper tool had been patterned as described generally above with a curved-edge diamond bit.
  • the curved edge of the diamond bit had been lapped and polished into a single arc section from a circle having a radius of 430 microns (micrometers).
  • the diamond was oriented to cut a thread-facet having mirror angle, also known as the nominal center slope, of 6 degrees and slopes of 6 (+/ ⁇ 1 to 3) degrees at the boundaries with the neighboring threads.
  • the acrylic film having the prismatic structure thus provided a light directing film.
  • This light directing film was coated with a layer of opaque silver (such as metal coating 330 of FIG. 6).
  • a clear PSA was then pressed onto the silvered side and samples were cut and laminated to glass microscope slides.
  • FIGS. 11, 12 and 13 illustrate diffusion profiles that are generally rectangular on a polar-angle plot; that is, the diffusion patterns have relatively straight edges.
  • the plots theoretically provide a diffusion profile that is relatively constant versus the horizontal viewing angle, up to a specified horizontal angle of view (HAOV). That is, a top hat or square diffusion profile is provided in the horizontal view.
  • the diffusion profile is relatively constant versus the vertical viewing angle (VAOV), up to a specified vertical angle of view.
  • VAOV vertical viewing angle
  • a top hat or square diffusion profile is provided in the vertical view.
  • Example 5 has a narrow horizontal angle of view pattern, as seen in FIG. 11
  • Example 6 has a medium horizontal angle of view pattern, as seen in FIG. 12
  • Example 7 has a wide horizontal angle of view pattern, as seen in FIG. 13.
  • the specific diffusion pattern in the horizontal angle of view, can be controlled by the ratio of the sinusoid amplitude and the wavelength, as seen in the comparison of Examples 5, 6 and 7.
  • FIG. 14 depicts a generic light directing film 810 having a smooth surface 812 and a structured surface 814 .
  • Structured surface 814 has a regular periodic surface that includes a noisy, chaotic or random microstructure superimposed on the regular periodic surface.
  • the chaotic overlay may be random or quasi-random.
  • the chaotic overlay provides a diffusive effect and hides visible defects; in some instances, the chaotic overlay may provide a matte finish to the display screen in which light directing film 810 is incorporated.
  • the chaotic overlay also provides a grain appearance that ranges from small to large and from faint to coarse depending upon the frequency and amplitude of the noise.
  • the waveform wavelength and amplitude depend on the angle of diffusion desired and the distance from which the display or reflector will be viewed.
  • the structures on the reflector surface should be smaller than naked human eye resolution at the viewing distance. For example, on a handheld display, the sizes that are most useful are less than the 2 arc-minute size at about 40 cm distance, or, less than 300 micrometers. For a front projection screen, viewed at a distance of 5 meters, the maximum structure size should be about 3-4 mm. In a near-eye application, that distance is much closer, and the allowable feature size would be that much smaller.
  • the structures formed by the chaotic or random overlay generally have a size or wavelength of 2.5 micrometers to 250 micrometers, typically about 5 to 100 micrometers.
  • the mean amplitude of the overlay is generally no greater than about 0.5 micrometers, and is generally no less than about 0.005 micrometers.
  • Light directing film 810 is oriented with the x-axis extending across the structure from left to right in the figure, and the z-axis extending top to bottom of the figure.
  • the y-axis extends into the page.
  • FIG. 14 what is shown in FIG. 14 is a structure row extending from left to right across the page.
  • the signal to form the chaotic overlay is superimposed or electronically added on the signal to the cutting tool that forms the regular, periodic structure.
  • Examples 8 and 9 were prepared as disclosed in Example 5, except that Example 8 further included chaotic oscillation over the fundamental structure of Example 5 along the length of the composite row in the x-direction. Example 9 also included chaotic oscillation over the fundamental structure.
  • the specific prism and facet dimensions for Examples 8 and 9 are provided in Tables 1 and 2 below.
  • Examples 8 and 9 were characterized with an ELDIM EZ Contrast model 160R used in the reflective mode with a 34 degree incident collimated light source and the resulting plots are shown in FIGS. 15 and 16, respectively. The figures clearly show the sharp glare peak at 34 degrees and the broad reflected light.
  • Example 9 has a wider vertical angle of view than Example 8, and a different centroid angle. TABLE 1 Horizontal Viewing Parameters Noise Amplitude Example A ( ⁇ m) ⁇ ( ⁇ m) ( ⁇ m) HAOV-M HAOV-T Comp.
  • HAOV represents “horizontal angle of view”; the “T” follower designates “theoretical” and an “M” follower” designates “measured”.
  • the HAOV is the full width at half maximum of the luminance slice through the maximum in the horizontal direction.
  • Table 1 shows that amplitude and wavelength (theoretical HAOV-T) predict HAOV-M.
  • HAOV-T assumes no chaotic oscillation and is calculated from the amplitude and wavelength only.
  • Example 8 illustrates the widening of HAOV-M from the value predicted by the sinusoidal pattern of Example 5 having no chaotic oscillation.
  • pitch represents the thread pitch, which is the distance, in the y-direction, between adjacent rows of prismatic structures.
  • Radius is the radius of the diamond bit cutting edge.
  • VAOV represents “vertical angle of view”; the “T” follower designates “theoretical” and the “M” follower” designates “measured”.
  • the VAOV is the full width at half maximum of the luminance slice through the maximum in the vertical direction.
  • Gain peak means the maximum gain.
  • Mirror angle represents the angle of the facet face from the y-axis.
  • centroid angle represents the polar angle of the center of the reflected pattern.
  • Table 2 shows that the thread pitch, radius, and mirror angle predict the VAOV-M and the measured centroid angle.
  • the previous examples have described sinusoidal periodic motion in the XZ plane.
  • the present invention can be used with any fundamental waveform that can be programmed on a computer.
  • the waveform may take the form of a well-known mathematical function or it can be programmed as a repeating set of values (X, Z). It may be desired to seek an optimal or application-specific diffusion pattern and choose a Z(X) waveform that provides the desired diffusion pattern.
  • FIG. 17 schematically shows Example 10 in a cross-sectional view of a light directing construction 500 .
  • the light directing construction 500 which includes a light directing film 510 , is oriented in FIG. 17 with the x-axis extending across the structure from left to right in the figure, and the z-axis extending top to bottom of the figure.
  • the y-axis extends into the page.
  • FIG. 17 what is shown in FIG. 17 is a structure row extending from left to right across the page.
  • Light directing film 510 has a smooth surface 512 and a structured surface 514 , which includes a structure or prism 540 having a front face 542 and a back face 544 .
  • Front face 542 and back face 544 meet at a valley 543 and at a peak 545 .
  • front face 542 and back face 544 are the same; that is, back face 544 is a mirror image of front face 542 .
  • Front face 542 and back face 544 are defined by a set of points that describe an upright parabola.
  • Structured surface 514 comprises a plurality of attached adjacent parabolas that provides a surface having a scalloped look.
  • Smooth surface 512 of film 510 is adjacent substrate 520 .
  • a metal coating 530 and a diffuser layer 535 which can be volume diffused to soften the diffusion profile and to mask any artifacts and defects.
  • Scalloped structured surface 514 is formed by varying the depth of the diamond cutting bit during the machining of the master tooling.
  • a fast servo tool (FTS) actuator is used to move the tip of the diamond cutting bit in the z-direction as the tool progress in the x-direction.
  • the depth modulation is periodic, but could include a chaotic overlay.
  • Example 10 and FIG. 17 reflects collimated light into a top hat or square-shaped reflected light distribution. This is due to the equal spatial weight given to front face 542 and back face 544 .
  • the reflected light angle is equal to the incident angle plus 4CX.
  • the intensity of light reflected into each direction within the HAOV is constant.
  • the intensity versus angle takes on top hat shape.
  • arcs or sinusoids may provide approximations to the flat or top hat shape.
  • FIG. 18 is a schematic cross-sectional view of a light directing construction 600 , Example 11, according to yet another aspect of the present invention.
  • Light directing construction 600 is oriented similar to light directing construction 500 of FIG. 17, with the x-axis extending across the structure from left to right in the figure, and the z-axis extending top to bottom of the figure.
  • the y-axis extends into the page.
  • what is shown in FIG. 18 is a structure row extending from left to right across the page.
  • Light directing construction 600 includes a light directing film 610 having a smooth surface 612 and a structured surface 614 , which includes a prismatic structure 640 having a front face 642 and a back face 644 .
  • Front face 642 and back face 644 meet at a domed peak 645 .
  • Front face 642 and back face 644 are the same; that is, back face 644 is a mirror image of front face 642 .
  • Each of front face 642 and back face 644 are made of a concave segment and a convex segment. Additionally or alternately, the entire structured surface 614 has an alternating pattern of concave and convex segments.
  • Structure surface 614 is formed by the same techniques used to form structured surface 514 of Example 10 in FIG. 17, except that in Example 11, the set of periodic points describes a set of two parabolas, where one parabola is inverted in respect to the other, and the intersection point is blended.
  • This structure is also formed by using a fast servo tool (FTS) actuator to move the tip of the diamond cutting bit in the z-direction during machining of the master tool.
  • FTS fast servo tool
  • smooth surface 612 is adjacent substrate 620 .
  • Overlying light direction film 610 is a metal coating 630 and a diffuser layer 635 , which is used to mask defects.
  • Examples 12 and 13 are shown in the photomicrographs of FIGS. 19 and 20, respectively.
  • the photomicrographs were taken with the light directing film at a 30 degree tilt in order to show the various features of the structured surface.
  • the structure row which is the x-direction, runs 30 degrees from horizontal, as shown in the photomicrographs.
  • Each of Examples 12 and 13 was prepared by the general following procedure.
  • the Examples differed in the modulation in the height of the structures, i.e., the z-direction.
  • the specific amplitude, pitch, and wavelength were the same between Examples 12 and 13, although it is understood that these characteristics could be varied as desired.
  • Examples 12 and 13 the pitch between adjacent structure rows (measured in the y-direction) was 61 micrometers. The facet was at a 6 degree tilt. The wavelength of the sinusoidal surfaces (measured in the x-direction) was 71 micrometers; the various angles of the sinusoidal surfaces are noticeable by the striated surfaces of the structures visible in the figures. Examples 12 and 13 differ from each other in that for Example 12 in FIG. 19, the modulation in the z-direction is synchronous. That is, for Example 12, the modulation in the z-direction of adjacent structures was aligned. An example of synchronous alignment is shown schematically in FIG. 10A. For Example 13 in FIG. 20, the modulation of adjacent structures was offset by 180 degrees, creating an anti-synchronous pattern.
  • Example 13 was 180 degrees, it is understood that other offsets, such as 90 degrees, 45 degrees, and others, can be used. Randomly varying offsets can also be used.
  • One method for making asynchronous wave pattern is by digital manipulation of the FTS wave-shape.
  • Generation of a waveform for example, one that is nearly perfectly a sine wave, results from the digital specification of multiple points of a computer algorithm.
  • a nearly perfect sine wave can be generated from a discrete number of points “n”.
  • Asynchronous wave shapes can be obtained by randomly eliminating one (or more) of the “n” steps in the wave. The most logical point in the wave to do this random elimination is where the slope of the actual wave form is varying the least.
  • the elimination of the segment may be accomplished by pre-calculating the total number of the wave shapes generated (“m”), then using the computer random number generator to build a table of random numbers in the range of 1 (the first wave generated) to “m” (the last wave generated).
  • the size of the table will depend on how many waves will be treated by the elimination process.
  • the elimination of discrete points causes small changes in the wave length to result in random anti-synchronous waves.
  • the pattern of waves formed in the above method can be another way of hiding spot-type defects of small size and reducing or eliminating moiré fringes from regular interference with pixel elements.
  • the structure spacing can be designed to minimize moiré interference with the pixel pitch of the LCD.
  • the structure rows which run in the x-direction, are positioned horizontally across the display screen; the y-direction is vertical across the display screen.
  • the structure rows would extend from the left edge to the right edge.
  • Moiré interference is caused by the structures being aligned with the pixels, either in the x-direction or the y-direction.
  • Example 14 in FIG. 21 is a light directing film 910 having a plurality of prismatic structures 940 .
  • structures 940 are not linear; rather, structures 940 follow a wavy path in the XY plane. Structures 940 extend in the x-direction, but include a y-direction component. The oscillating line of structures 940 decreases moiré interference by minimizing, preferably eliminating, alignment of structures 940 with the display pixels.
  • Structures 940 can be formed by oscillating the cutting tool in the y-direction during machining of the master tool. In another method, structures 940 can be formed by rotating the cutting tool around its central axis, or another axis, during machining of the master tool.
  • spacing between rows of composites can be varied.
  • the distance in the y-direction between peaks of composite rows can be varied.
  • this may create grooves that are not parallel.
  • the rows of composites run horizontal across the display.
  • the rotation of the composite rows can be 1 to 45 degrees, generally is 5 to 20 degrees, and preferably is 5 to 10 degrees from the pixel row orientation.
  • Example 17 shows the effects of providing a volume diffuser over the light directing film, which includes reducing or eliminating moiré interference.
  • Example 17 was made by laminating a 12 micrometer thick layer of 8% volume diffuser (PSA loaded with 8% polymeric beads) to the structure of Example 5.
  • Example 17 compares Example 17 with Comparative Example 1, which had flat facets and a 25 micrometer thick, 8% loaded diffuser layer, and with Example 5, which had no volume diffuser layer.
  • Example 5 which had no volume diffuser layer.
  • HAOV represents the horizontal angle of view
  • VAOV represents the vertical angle of view
  • HAOC represents the horizontal angle of curtaining, which is the angular separation between 90% and 10% of the maximum luminance in the XZ plane.
  • VAOC represents the vertical angle of curtaining and is likewise measured but in the YZ plane. The angle of curtaining determines how abruptly the reflected light pattern appears when one rotates the LCD under illumination.
  • Periodic repetitive structures can defract light into repetitive bands of color.
  • the diffraction band color bands are faint, but still visible, because it is only the higher order diffraction effects that are expressed.
  • “Visible structures” refers to whether or not the prismatic structures were visible with a naked eye. For Example 5, faint grooves at a pitch of 133 micrometers were observed. For Comparative Example 1 and Example 17, no grooves are seen, at least partially due to the presence of the volume diffuser.
  • FIG. 22 shows a cross-sectional view plot of the light reflectance from Examples 1, 5 and 17 as measured on an ELDIM EZ Contrast model 160R used in the reflective mode with a 34 degree incident collimated light source.
  • the plot shows that for Comparative Example 1, there is a moderately strong image of the light source, which is observed as a sharp peak in the ELDIM plot.

Landscapes

  • Physics & Mathematics (AREA)
  • General Physics & Mathematics (AREA)
  • Optics & Photonics (AREA)
  • Chemical & Material Sciences (AREA)
  • Dispersion Chemistry (AREA)
  • Optical Elements Other Than Lenses (AREA)
US09/922,438 2001-08-03 2001-08-03 Optical film having microreplicated structures; and methods Abandoned US20030035231A1 (en)

Priority Applications (12)

Application Number Priority Date Filing Date Title
US09/922,438 US20030035231A1 (en) 2001-08-03 2001-08-03 Optical film having microreplicated structures; and methods
JP2003519655A JP2004538506A (ja) 2001-08-03 2002-07-25 微細複製構造を有する光学フィルム
EP02756659A EP1412779A2 (en) 2001-08-03 2002-07-25 Optical film having microreplicated structures
CNB2006101109079A CN100478715C (zh) 2001-08-03 2002-07-25 含微复制结构的光学膜及其制造方法
PCT/US2002/023671 WO2003014777A2 (en) 2001-08-03 2002-07-25 Optical film having microreplicated structures
KR10-2004-7001683A KR20040020976A (ko) 2001-08-03 2002-07-25 미세복제 구조물을 갖는 광학 필름 및 제조방법
CNB028152468A CN100464197C (zh) 2001-08-03 2002-07-25 含微复制结构的光学膜及其制造方法
CNA2006101082004A CN1916670A (zh) 2001-08-03 2002-07-25 含微复制结构的光学膜及其制造方法
US10/205,160 US20030058553A1 (en) 2001-08-03 2002-07-25 Optical film having microreplicated structures; and methods
AU2002322651A AU2002322651A1 (en) 2001-08-03 2002-07-25 Optical film having microreplicated structures
US10/877,341 US20050024754A1 (en) 2001-08-03 2004-06-25 Optical film having microeplicated structures; and methods
US11/927,202 US8579492B2 (en) 2001-08-03 2007-10-29 Optical film having microreplicated structures and methods

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
US09/922,438 US20030035231A1 (en) 2001-08-03 2001-08-03 Optical film having microreplicated structures; and methods

Related Child Applications (1)

Application Number Title Priority Date Filing Date
US10/205,160 Continuation-In-Part US20030058553A1 (en) 2001-08-03 2002-07-25 Optical film having microreplicated structures; and methods

Publications (1)

Publication Number Publication Date
US20030035231A1 true US20030035231A1 (en) 2003-02-20

Family

ID=25447051

Family Applications (4)

Application Number Title Priority Date Filing Date
US09/922,438 Abandoned US20030035231A1 (en) 2001-08-03 2001-08-03 Optical film having microreplicated structures; and methods
US10/205,160 Abandoned US20030058553A1 (en) 2001-08-03 2002-07-25 Optical film having microreplicated structures; and methods
US10/877,341 Abandoned US20050024754A1 (en) 2001-08-03 2004-06-25 Optical film having microeplicated structures; and methods
US11/927,202 Expired - Fee Related US8579492B2 (en) 2001-08-03 2007-10-29 Optical film having microreplicated structures and methods

Family Applications After (3)

Application Number Title Priority Date Filing Date
US10/205,160 Abandoned US20030058553A1 (en) 2001-08-03 2002-07-25 Optical film having microreplicated structures; and methods
US10/877,341 Abandoned US20050024754A1 (en) 2001-08-03 2004-06-25 Optical film having microeplicated structures; and methods
US11/927,202 Expired - Fee Related US8579492B2 (en) 2001-08-03 2007-10-29 Optical film having microreplicated structures and methods

Country Status (7)

Country Link
US (4) US20030035231A1 (zh)
EP (1) EP1412779A2 (zh)
JP (1) JP2004538506A (zh)
KR (1) KR20040020976A (zh)
CN (3) CN100464197C (zh)
AU (1) AU2002322651A1 (zh)
WO (1) WO2003014777A2 (zh)

Cited By (41)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20030214728A1 (en) * 2002-05-20 2003-11-20 General Electric Company Optical substrate and method of making
US20040223099A1 (en) * 2003-05-05 2004-11-11 Kotchick Keith M. Structured transflectors for enhanced ambient and backlight operation of transmissive liquid crystal displays
US20050221009A1 (en) * 2004-03-31 2005-10-06 Clemons Gregory S Process for micro-grooving a polymer alignment layer for a liquid crystal display
US20050225865A1 (en) * 2002-05-20 2005-10-13 General Electric Company Optical substrate and method of making
US20050237641A1 (en) * 2004-04-22 2005-10-27 Shih-Chieh Tang Brightness enhancement film having curved prism units
US20050237749A1 (en) * 2004-04-22 2005-10-27 3M Innovative Properties Company Transflector
US20060047358A1 (en) * 2004-08-31 2006-03-02 General Electric Company Machine tool control methods and designs for fabricating mesoscopic surface structures on substrates
US20060109645A1 (en) * 2004-11-22 2006-05-25 Ferrari John S Hand worn illuminated framework
US20060130310A1 (en) * 2004-12-20 2006-06-22 General Electric Company High speed linear motion mechanism
US20060245206A1 (en) * 2003-12-31 2006-11-02 General Electric Company Optical substrate with modulated structure
US20070012350A1 (en) * 2005-07-13 2007-01-18 Samsung Electronics Co., Ltd. Prism member, backlight assembly provided with the same, and display device provided with the same
US20070047261A1 (en) * 2005-08-27 2007-03-01 Thompson David S Direct-lit backlight having light recycling cavity with concave transflector
US20070047228A1 (en) * 2005-08-27 2007-03-01 3M Innovative Properties Company Methods of forming direct-lit backlights having light recycling cavity with concave transflector
US20070047254A1 (en) * 2005-08-27 2007-03-01 3M Innovative Properties Company Illumination assembly and system
US20070047262A1 (en) * 2005-08-27 2007-03-01 3M Innovative Properties Company Edge-lit backlight having light recycling cavity with concave transflector
US20070107566A1 (en) * 2005-11-15 2007-05-17 Ehnes Dale L Cutting tool having variable rotation about a y-direction transversely across a work piece for making microstructures
US20070107568A1 (en) * 2005-11-15 2007-05-17 Campbell Alan B Cutting tool having variable and independent movement in an X-direction and a Z-direction into and laterally along a work piece for making microstructures
US20070121227A1 (en) * 2004-07-02 2007-05-31 Efun Technology Co., Ltd. Brightness enhancement film having curved prism units and light scattering particles
US20070133094A1 (en) * 2005-12-13 2007-06-14 Walton Emma J Optical film, illuminator and display
EP1815279A1 (en) * 2004-11-22 2007-08-08 3M Innovative Properties Company Prism sheet for backlit display that reduces moire interference
US20070212177A1 (en) * 2006-03-13 2007-09-13 Matsushita Electric Industrial Co., Ltd. Machining tools having concave cutting surfaces for precision machining and methods of manufacturing such
US20070221019A1 (en) * 2006-03-13 2007-09-27 Matsushita Electric Industrial Co., Ltd. Precision machining system and methods
US20070261521A1 (en) * 2006-05-10 2007-11-15 Campbell Alan B Cutting tool using one or more machined tool tips in a continuous or interrupted cut fast tool servo
US20080166190A1 (en) * 2007-01-05 2008-07-10 3M Innovative Properties Company Cutting tool using one or more machined tool tips with diffractive features in a continuous or interrupted cut fast tool servo
US20090052045A1 (en) * 2002-05-20 2009-02-26 Sabic Innovative Plastics Ip B.V. Film, backlight displays, and methods for making the same
US20090067155A1 (en) * 2002-12-18 2009-03-12 Sabic Innovative Plastics Ip B.V. Method and apparatus for fabricating optical substrates
US20090110504A1 (en) * 2007-10-29 2009-04-30 3M Innovative Properties Company Cutting tool using one or more machined tool tips with diffractive features
US20090237615A1 (en) * 2006-06-30 2009-09-24 Das Kamal K Correction of Surgically-Induced Astigmatism During Intraocular Lens Implants
US20110181971A1 (en) * 2008-04-02 2011-07-28 Campbell Alan B Methods and systems for fabricating optical films having superimposed features
WO2015123024A1 (en) * 2014-02-14 2015-08-20 Microsoft Technology Licensing, Llc Interactive display system
US9383075B2 (en) 2011-02-22 2016-07-05 Koninklijke Philips N.V. Collimator comprising a prismatic layer stack, and lighting unit comprising such a collimator
US20160231473A1 (en) * 2015-02-09 2016-08-11 Omnivision Technologies, Inc. Wide-Angle Camera Using Achromatic Doublet Prism Array And Method of Manufacturing The Same
US20170090210A1 (en) * 2014-05-09 2017-03-30 Pure Depth Limited Diffraction grating for use with a multi-layered display system
US9632326B2 (en) 2010-10-28 2017-04-25 Philips Lighting Holding B.V. Collimator comprising a prismatic layer stack, and lighting unit comprising such collimator
US9810817B2 (en) 2008-04-02 2017-11-07 3M Innovative Properties Company Light directing film and method for making the same
US9972734B2 (en) 2012-03-27 2018-05-15 3M Innovative Properties Company Photovoltaic modules comprising light directing mediums and methods of making the same
WO2018129034A1 (en) * 2017-01-04 2018-07-12 3M Innovative Properties Company Asymmetric turning film with top-hat light output distributions
US10205041B2 (en) 2015-10-12 2019-02-12 3M Innovative Properties Company Light redirecting film useful with solar modules
WO2020044240A1 (en) 2018-08-31 2020-03-05 3M Innovative Properties Company Light redirecting film having stray-light mitigation properties useful with solar modules
CN113671619A (zh) * 2020-05-14 2021-11-19 四川龙华光电薄膜股份有限公司 反射式显示装置及其前置光源模块
US11448805B2 (en) * 2016-08-29 2022-09-20 Kyocera Corporation Optical member, method of manufacturing optical member, and image display system

Families Citing this family (85)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US9052777B2 (en) * 2001-11-02 2015-06-09 Neonode Inc. Optical elements with alternating reflective lens facets
US6692201B2 (en) * 2002-01-28 2004-02-17 Richard Soderman Portable drill press
US7106517B2 (en) * 2003-12-31 2006-09-12 General Electric Company Display optical films
JP2006017957A (ja) * 2004-06-30 2006-01-19 Sun Tec Kk レンズフィルム
US20060042681A1 (en) * 2004-08-24 2006-03-02 General Electric Company Pv laminate backplane with optical concentrator
US20060103777A1 (en) * 2004-11-15 2006-05-18 3M Innovative Properties Company Optical film having a structured surface with rectangular based prisms
GB0427607D0 (en) * 2004-12-16 2005-01-19 Microsharp Corp Ltd Structured optical film
US7220026B2 (en) * 2004-12-30 2007-05-22 3M Innovative Properties Company Optical film having a structured surface with offset prismatic structures
US7416309B2 (en) * 2004-12-30 2008-08-26 3M Innovative Properties Company Optical film having a surface with rounded structures
US7320538B2 (en) * 2004-12-30 2008-01-22 3M Innovative Properties Company Optical film having a structured surface with concave pyramid-shaped structures
US20060182409A1 (en) * 2005-02-11 2006-08-17 Eastman Kodak Company Optical films of differing refractive indices
WO2006098799A2 (en) * 2005-03-12 2006-09-21 3M Innovative Properties Company Illumination devices and methods for making the same
US20060250707A1 (en) * 2005-05-05 2006-11-09 3M Innovative Properties Company Optical film having a surface with rounded pyramidal structures
US20070024994A1 (en) * 2005-07-29 2007-02-01 3M Innovative Properties Company Structured optical film with interspersed pyramidal structures
US20080081132A1 (en) * 2006-03-30 2008-04-03 Bourdelais Robert P Light redirecting film having surface nano-nodules
TWI295355B (en) * 2006-08-30 2008-04-01 Ind Tech Res Inst Optical diffusion module and method of manufacturing optical diffusion structure
US8525402B2 (en) * 2006-09-11 2013-09-03 3M Innovative Properties Company Illumination devices and methods for making the same
US7481563B2 (en) * 2006-09-21 2009-01-27 3M Innovative Properties Company LED backlight
US8581393B2 (en) 2006-09-21 2013-11-12 3M Innovative Properties Company Thermally conductive LED assembly
KR101321909B1 (ko) 2006-12-12 2013-10-25 삼성디스플레이 주식회사 프리즘 시트 및 이의 제조 방법
US8114248B2 (en) * 2007-01-03 2012-02-14 Asahi Kasei Kabushiki Kaisha Roll-to-roll method and system for micro-replication of a pattern of large relief three-dimensional microstructures
US7543974B2 (en) * 2007-03-06 2009-06-09 Skc Haas Display Films Co., Ltd. Light redirecting film having variable thickness
US7530726B2 (en) 2007-03-06 2009-05-12 Skc Haas Display Films Co., Ltd. Light redirecting film having discontinuous coating
US20080247065A1 (en) * 2007-04-06 2008-10-09 3M Innovative Properties Company Method of making structured optical films
US20080295327A1 (en) * 2007-06-01 2008-12-04 3M Innovative Properties Company Flexible circuit
TWI342411B (en) * 2007-06-11 2011-05-21 Ind Tech Res Inst Composite lens structure and method of forming the same
US9690038B2 (en) 2007-06-22 2017-06-27 3M Innovative Properties Company Systems and methods for controlling backlight output characteristics
CN101382606B (zh) * 2007-09-07 2010-06-09 迎辉科技股份有限公司 光学膜、成型光学膜的模具及模具的制造方法
TWI363900B (en) 2007-10-04 2012-05-11 Ind Tech Res Inst Light guiding film
GB2455057A (en) 2007-10-08 2009-06-03 Sharp Kk Prismatic curved sheet optical device for use in a curved display
TW200921006A (en) * 2007-11-12 2009-05-16 Whe-Yi Chiang Lighting device
JP2009128904A (ja) * 2007-11-26 2009-06-11 Lg Electronics Inc 光学フィルム及び液晶表示装置
CN101458347B (zh) * 2007-12-14 2011-12-21 鸿富锦精密工业（深圳）有限公司 棱镜片及其制备方法，以及采用该棱镜片的液晶显示装置
TWI365305B (en) * 2008-06-20 2012-06-01 Coretronic Corp Backlight module
US20100128351A1 (en) * 2008-11-21 2010-05-27 3M Innovative Properties Company Curved sided cone structures for controlling gain and viewing angle in an optical film
KR200457969Y1 (ko) * 2009-03-09 2012-01-16 배병태 가열기를 구비한 회전테이블용 식탁
CN102362247B (zh) * 2009-03-27 2015-08-12 木本股份有限公司 防牛顿环片材和使用了其的触摸屏
JP5624608B2 (ja) 2009-04-24 2014-11-12 スリーエム イノベイティブプロパティズカンパニー ライトアセンブリ
KR20120041765A (ko) 2009-07-21 2012-05-02 쓰리엠 이노베이티브 프로퍼티즈 컴파니 광 조립체
US20110025948A1 (en) * 2009-07-31 2011-02-03 Skc Haas Display Films Co., Ltd. Patterned volume diffuser elements
WO2011078988A1 (en) 2009-12-21 2011-06-30 3M Innovative Properties Company Transflective articles and light assemblies
TW201124007A (en) * 2009-12-30 2011-07-01 Au Optronics Corp Substrate and substrate bonding device using the same
US8917447B2 (en) * 2010-01-13 2014-12-23 3M Innovative Properties Company Microreplicated film for attachment to autostereoscopic display components
JP5608385B2 (ja) * 2010-02-08 2014-10-15 デクセリアルズ株式会社 光学体およびその製造方法、窓材、建具、ならびに日射遮蔽装置
WO2011122307A1 (ja) * 2010-03-29 2011-10-06 株式会社 きもと ニュートンリング防止シート、その製造方法及びタッチパネル
FR2958425B1 (fr) * 2010-03-31 2012-06-08 Valeo Systemes Thermiques Interface homme-machine a surface superieure lisse
EP3093694A1 (en) * 2010-06-25 2016-11-16 Andrew Richard Parker Optical effect structures
JP5652192B2 (ja) * 2010-12-20 2015-01-14 セイコーエプソン株式会社 時計用文字板および時計
EP2820099B1 (en) 2012-02-28 2018-12-05 3M Innovative Properties Company Microstructured tape comprising coextensive, intersecting paint-retention and hand-tear patterns
BR112015010894A2 (pt) * 2012-11-16 2017-07-11 Koninklijke Philips Nv visor autoestereoscópico reflexivo ou transflectivo e método para melhorar a uniformidade de iluminação do painel de um visor autoestereoscópico
EP2926179A1 (en) 2012-11-30 2015-10-07 Essilor International (Compagnie Générale d'Optique) Fresnel lens and optical device
US10072816B2 (en) 2013-06-19 2018-09-11 Bright View Technologies Corporation Microstructure-based optical diffusers for creating batwing and other lighting patterns
WO2015195160A1 (en) * 2014-06-18 2015-12-23 Bright View Technologies Corporation Microstructure-based diffusers for creating batwing lighting patterns
US10302275B2 (en) 2013-06-19 2019-05-28 Bright View Technologies Corporation Microstructure-based diffusers for creating batwing lighting patterns
DE112014005403B4 (de) * 2013-11-26 2023-02-02 Yazaki Corporation Skalenscheibe mit radialen Linien und Kraftfahrzeug-Anzeigegerät mit Skalenscheibe mit radialen Linien
US9046637B1 (en) 2014-02-25 2015-06-02 3M Innovative Properties Company Tubular lighting systems with inner and outer structured surfaces
US10161593B2 (en) 2014-02-25 2018-12-25 3M Innovative Properties Company Solid state lighting device with virtual filament(s)
EP3237940A1 (en) * 2014-12-26 2017-11-01 CY Vision Inc. Apparatus for generating a coherent beam illumination
US10571696B2 (en) 2014-12-26 2020-02-25 Cy Vision Inc. Near-to-eye display device
EP3237953A1 (en) 2014-12-26 2017-11-01 CY Vision Inc. Near-to-eye display device with variable resolution
CN107430348B (zh) 2015-03-02 2021-09-24 Asml荷兰有限公司 辐射系统
US9910276B2 (en) 2015-06-30 2018-03-06 Microsoft Technology Licensing, Llc Diffractive optical elements with graded edges
US10670862B2 (en) 2015-07-02 2020-06-02 Microsoft Technology Licensing, Llc Diffractive optical elements with asymmetric profiles
US9864208B2 (en) 2015-07-30 2018-01-09 Microsoft Technology Licensing, Llc Diffractive optical elements with varying direction for depth modulation
US10038840B2 (en) 2015-07-30 2018-07-31 Microsoft Technology Licensing, Llc Diffractive optical element using crossed grating for pupil expansion
CN105044807B (zh) * 2015-08-05 2018-03-20 苏州华徕光电仪器有限公司 高反射性能测绘棱镜
US10073278B2 (en) 2015-08-27 2018-09-11 Microsoft Technology Licensing, Llc Diffractive optical element using polarization rotation grating for in-coupling
US10429645B2 (en) 2015-10-07 2019-10-01 Microsoft Technology Licensing, Llc Diffractive optical element with integrated in-coupling, exit pupil expansion, and out-coupling
US10241332B2 (en) 2015-10-08 2019-03-26 Microsoft Technology Licensing, Llc Reducing stray light transmission in near eye display using resonant grating filter
US10234686B2 (en) 2015-11-16 2019-03-19 Microsoft Technology Licensing, Llc Rainbow removal in near-eye display using polarization-sensitive grating
EP3433672B1 (en) 2016-03-25 2021-03-03 CY Vision Inc. Near-to-eye image display device delivering enhanced viewing experience
US10976705B2 (en) 2016-07-28 2021-04-13 Cy Vision Inc. System and method for high-quality speckle-free phase-only computer-generated holographic image projection
TWI616697B (zh) * 2016-10-13 2018-03-01 大立光電股份有限公司 環形光學元件、成像鏡組、成像裝置及電子裝置
CN106772725A (zh) * 2016-12-30 2017-05-31 张家港康得新光电材料有限公司 光转向膜和夹层玻璃
US10108014B2 (en) * 2017-01-10 2018-10-23 Microsoft Technology Licensing, Llc Waveguide display with multiple focal depths
CN110382254B (zh) * 2017-03-06 2021-05-25 株式会社Lg化学 装饰构件及制造装饰构件的方法
KR101966851B1 (ko) 2017-03-06 2019-04-08 주식회사 엘지화학 장식 부재 및 이의 제조방법
CN106959480A (zh) * 2017-05-02 2017-07-18 宁波长阳科技股份有限公司 一种高辉度复合反射膜
CN109298476A (zh) * 2017-12-12 2019-02-01 宁波激智科技股份有限公司 一种背板组件用反光贴条及其制备方法
US11669210B2 (en) 2020-09-30 2023-06-06 Neonode Inc. Optical touch sensor
JP7368430B2 (ja) * 2020-12-01 2023-10-24 恵和株式会社 光拡散シート、バックライトユニット、液晶表示装置、情報機器、及び光拡散シートの製造方法
WO2022118533A1 (ja) * 2020-12-01 2022-06-09 恵和株式会社 光拡散シート、バックライトユニット、液晶表示装置、情報機器、及び光拡散シートの製造方法
JP7503091B2 (ja) * 2021-11-02 2024-06-19 恵和株式会社 光拡散シート、バックライトユニット、液晶表示装置、情報機器、及び光拡散シートの製造方法
KR20240045329A (ko) * 2021-11-02 2024-04-05 케이와 인코포레이티드 광확산 시트, 백라이트 유닛, 액정표시장치, 정보기기, 및 광확산 시트의 제조방법
JP7389296B1 (ja) * 2022-05-27 2023-11-29 恵和株式会社 光拡散シート、バックライトユニット、液晶表示装置、情報機器、及び光拡散シートの製造方法

Family Cites Families (34)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3754813A (en) * 1971-12-13 1973-08-28 Eastman Kodak Co Radiation-redistributive devices
US4127693A (en) * 1975-02-10 1978-11-28 Lemelson Jerome H Reflex reflectors with pyramid-shaped indentations
US4241980A (en) * 1978-05-24 1980-12-30 William C. McGeehon Beam emission control means
CH633381A5 (de) * 1978-12-20 1982-11-30 Bbc Brown Boveri & Cie Elektrooptische anzeige mit reflektor.
US4486070A (en) * 1981-04-13 1984-12-04 Polaroid Corporation Mirror-absorber for use in the illumination of transmission holograms
US5076668A (en) * 1988-01-25 1991-12-31 Taliq Corporation Gain reflector-liquid crystal display
US4991940A (en) * 1988-01-25 1991-02-12 Taliq Corporation Gain reflector-liquid crystal display
JPH01311910A (ja) 1988-06-10 1989-12-15 Nissan Motor Co Ltd 能動型サスペンション
US5183597A (en) * 1989-02-10 1993-02-02 Minnesota Mining And Manufacturing Company Method of molding microstructure bearing composite plastic articles
US5005108A (en) * 1989-02-10 1991-04-02 Lumitex, Inc. Thin panel illuminator
US5128787A (en) 1990-12-07 1992-07-07 At&T Bell Laboratories Lcd display with multifaceted back reflector
US5552907A (en) * 1992-01-27 1996-09-03 Sekisui Chemical Co., Ltd. Light adjusting sheet having a sinusoidal surface and a non-optically flat surface and useable with an LCD
JPH0695112A (ja) * 1992-09-16 1994-04-08 Hitachi Ltd プリズムプレートおよびそれを用いた情報表示装置
EP0843195B1 (en) * 1995-07-28 2004-04-07 Sumitomo Chemical Company Limited Reflecting plate, reflection type polarizing plate and reflection type liquid crystal display device
US6067137A (en) * 1995-08-25 2000-05-23 Kuraray Co., Ltd. Image display apparatus with hydrophobic diffraction grating for an enlarged viewing angle
US5919551A (en) * 1996-04-12 1999-07-06 3M Innovative Properties Company Variable pitch structured optical film
US5975706A (en) * 1997-03-31 1999-11-02 3M Innovative Properties Company Wide incident angle reflective plate
JP3623341B2 (ja) 1997-07-18 2005-02-23 アルプス電気株式会社 反射体および反射型液晶表示装置
JPH11142622A (ja) * 1997-11-13 1999-05-28 Dainippon Printing Co Ltd レンズフィルム、面光源装置、液晶表示装置
AU752774B2 (en) * 1998-02-18 2002-09-26 Minnesota Mining And Manufacturing Company Optical film
JP3975001B2 (ja) * 1998-04-22 2007-09-12 日本カーバイド工業株式会社 三角錐型キユーブコーナー再帰反射シート
JP2000066013A (ja) 1998-08-25 2000-03-03 Dainippon Printing Co Ltd 光反射光学シート及び面光源装置
US6704077B1 (en) 1998-08-31 2004-03-09 Casio Computer Co., Ltd. Reflection type liquid crystal display with selective reflector
JP3899717B2 (ja) 1998-09-01 2007-03-28 カシオ計算機株式会社 液晶表示装置
JP2000162710A (ja) 1998-11-30 2000-06-16 Hitachi Ltd 指向性反射スクリーンおよび画像表示装置
JP4212697B2 (ja) 1998-12-18 2009-01-21 大日本印刷株式会社 ディスプレイ用反射材及び反射型ディスプレイ装置
AU771338B2 (en) * 1999-01-21 2004-03-18 Orafol Americas Inc. Durable, open-faced retroreflective prismatic construction
US6540367B1 (en) * 1999-04-07 2003-04-01 3M Innovative Properties Company Structured surface articles containing geometric structures with compound faces and methods for making same
JP2001083308A (ja) 1999-07-09 2001-03-30 Sumitomo Chem Co Ltd 反射板、それを用いた反射型偏光板及び液晶表示装置
US6264336B1 (en) * 1999-10-22 2001-07-24 3M Innovative Properties Company Display apparatus with corrosion-resistant light directing film
JP2001133614A (ja) 1999-10-29 2001-05-18 Hitachi Chem Co Ltd 拡散反射板及びその転写原型、その製造方法及びそれを用いたベースフィルム、転写フィルム、並びにこれらを用いた拡散反射板の製造方法
AU1305301A (en) 1999-11-09 2001-06-06 Omron Corporation Reflecting member and light reflecting method
WO2001069300A2 (en) * 2000-03-16 2001-09-20 Led Products, Inc. High efficiency non-imaging optics
US6581286B2 (en) * 2000-04-05 2003-06-24 3M Innovative Properties Company Method of making tool to produce optical film

Cited By (86)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US7859759B2 (en) 2002-05-20 2010-12-28 Sabic Innovative Plastics Ip B.V. Film, backlight displays, and methods for making the same
US7965447B2 (en) 2002-05-20 2011-06-21 Sabic Innovative Plastics Ip B.V. Optical substrate and method of making
US20090052045A1 (en) * 2002-05-20 2009-02-26 Sabic Innovative Plastics Ip B.V. Film, backlight displays, and methods for making the same
US6862141B2 (en) 2002-05-20 2005-03-01 General Electric Company Optical substrate and method of making
US7324284B2 (en) 2002-05-20 2008-01-29 General Electric Company Optical substrate and method of making
US20050225865A1 (en) * 2002-05-20 2005-10-13 General Electric Company Optical substrate and method of making
US20060256444A1 (en) * 2002-05-20 2006-11-16 General Electric Company Optical substrate and method of making
US20080106793A1 (en) * 2002-05-20 2008-05-08 Sabic Innovative Plastics Ip Bv Optical substrate and method of making
US7180672B2 (en) 2002-05-20 2007-02-20 General Electric Company Optical substrate and method of making
US20030214728A1 (en) * 2002-05-20 2003-11-20 General Electric Company Optical substrate and method of making
US20090067155A1 (en) * 2002-12-18 2009-03-12 Sabic Innovative Plastics Ip B.V. Method and apparatus for fabricating optical substrates
US7385659B2 (en) 2003-05-05 2008-06-10 3M Innovative Properties Company Structured transflectors for enhanced ambient and backlight operation of transmissive liquid crystal displays
US7088405B2 (en) 2003-05-05 2006-08-08 3M Innovative Properties Company Structured transflectors for enhanced ambient and backlight operation of transmissive liquid crystal displays
US20040223099A1 (en) * 2003-05-05 2004-11-11 Kotchick Keith M. Structured transflectors for enhanced ambient and backlight operation of transmissive liquid crystal displays
US20040223100A1 (en) * 2003-05-05 2004-11-11 3M Innovative Properties Company Structured transflectors for enhanced ambient and backlight operation of transmissive liquid crystal displays
US7248412B2 (en) 2003-12-31 2007-07-24 General Electric Company Optical substrate with modulated structure
US20060245206A1 (en) * 2003-12-31 2006-11-02 General Electric Company Optical substrate with modulated structure
US20070263273A1 (en) * 2003-12-31 2007-11-15 General Electric Company Optical substrate with modulated structure
US7483195B2 (en) 2003-12-31 2009-01-27 Sabic Innovative Plastics Ip B.V. Optical substrate with modulated structure
US7297369B2 (en) * 2004-03-31 2007-11-20 Intel Corporation Process for micro-grooving a polymer alignment layer for a liquid crystal display
US20050221009A1 (en) * 2004-03-31 2005-10-06 Clemons Gregory S Process for micro-grooving a polymer alignment layer for a liquid crystal display
US7448776B2 (en) * 2004-04-22 2008-11-11 Efun Technology Co., Ltd. Brightness enhancement film having curved prism units
US20050237641A1 (en) * 2004-04-22 2005-10-27 Shih-Chieh Tang Brightness enhancement film having curved prism units
US20050237749A1 (en) * 2004-04-22 2005-10-27 3M Innovative Properties Company Transflector
US20070121227A1 (en) * 2004-07-02 2007-05-31 Efun Technology Co., Ltd. Brightness enhancement film having curved prism units and light scattering particles
US7203569B2 (en) 2004-08-31 2007-04-10 General Electric Company Machine tool control methods and designs for fabricating mesoscopic surface structures on substrates
US20060047358A1 (en) * 2004-08-31 2006-03-02 General Electric Company Machine tool control methods and designs for fabricating mesoscopic surface structures on substrates
US20060109645A1 (en) * 2004-11-22 2006-05-25 Ferrari John S Hand worn illuminated framework
EP1815279A1 (en) * 2004-11-22 2007-08-08 3M Innovative Properties Company Prism sheet for backlit display that reduces moire interference
US7278771B2 (en) 2004-11-22 2007-10-09 3M Innovative Properties Company Optical film
US20070130749A1 (en) * 2004-12-20 2007-06-14 General Electric Company High speed linear motion mechanism
US7219410B2 (en) 2004-12-20 2007-05-22 General Electric Company High speed linear motion mechanism
US7356904B2 (en) 2004-12-20 2008-04-15 General Electric Company High speed linear motion mechanism
US20060130310A1 (en) * 2004-12-20 2006-06-22 General Electric Company High speed linear motion mechanism
US7824066B2 (en) 2005-07-13 2010-11-02 Samsung Electronics Co., Ltd. Prism member, backlight assembly provided with the same, and display device provided with the same
US20070012350A1 (en) * 2005-07-13 2007-01-18 Samsung Electronics Co., Ltd. Prism member, backlight assembly provided with the same, and display device provided with the same
US9857518B2 (en) 2005-08-27 2018-01-02 3M Innovative Properties Company Direct-lit backlight having light recycling cavity with concave transflector
US7537374B2 (en) 2005-08-27 2009-05-26 3M Innovative Properties Company Edge-lit backlight having light recycling cavity with concave transflector
US7695180B2 (en) 2005-08-27 2010-04-13 3M Innovative Properties Company Illumination assembly and system
US7815355B2 (en) 2005-08-27 2010-10-19 3M Innovative Properties Company Direct-lit backlight having light recycling cavity with concave transflector
US20110025947A1 (en) * 2005-08-27 2011-02-03 3M Innovative Properties Company Direct-lit backlight having light recycling cavity with concave transflector
US20070047262A1 (en) * 2005-08-27 2007-03-01 3M Innovative Properties Company Edge-lit backlight having light recycling cavity with concave transflector
US20070047254A1 (en) * 2005-08-27 2007-03-01 3M Innovative Properties Company Illumination assembly and system
US20070047228A1 (en) * 2005-08-27 2007-03-01 3M Innovative Properties Company Methods of forming direct-lit backlights having light recycling cavity with concave transflector
US20070047261A1 (en) * 2005-08-27 2007-03-01 Thompson David S Direct-lit backlight having light recycling cavity with concave transflector
US20070107566A1 (en) * 2005-11-15 2007-05-17 Ehnes Dale L Cutting tool having variable rotation about a y-direction transversely across a work piece for making microstructures
US7293487B2 (en) 2005-11-15 2007-11-13 3M Innovative Properties Company Cutting tool having variable and independent movement in an x-direction and a z-direction into and laterally along a work piece for making microstructures
US20070107568A1 (en) * 2005-11-15 2007-05-17 Campbell Alan B Cutting tool having variable and independent movement in an X-direction and a Z-direction into and laterally along a work piece for making microstructures
US7398715B2 (en) 2005-11-15 2008-07-15 3M Innovative Properties Company Method for using a cutting tool having variable rotation about a y-direction transversely across a work piece for making microstructures
US20080016992A1 (en) * 2005-11-15 2008-01-24 3M Innovative Properties Company Method for using a cutting tool having variable rotation about a y-direction transversely across a work piece for making microstructures
US7290471B2 (en) 2005-11-15 2007-11-06 3M Innovative Properties Company Cutting tool having variable rotation about a y-direction transversely across a work piece for making microstructures
US7548371B2 (en) 2005-12-13 2009-06-16 Sharp Kabushiki Kaisha Optical film, illuminator and display
US20070133094A1 (en) * 2005-12-13 2007-06-14 Walton Emma J Optical film, illuminator and display
US7788998B2 (en) 2006-03-13 2010-09-07 Panasonic Corporation Precision machining system and methods
US7614831B2 (en) 2006-03-13 2009-11-10 Panasonic Corporation Machining tools having concave cutting surfaces for precision machining and methods of manufacturing such
US20070221019A1 (en) * 2006-03-13 2007-09-27 Matsushita Electric Industrial Co., Ltd. Precision machining system and methods
US20070212177A1 (en) * 2006-03-13 2007-09-13 Matsushita Electric Industrial Co., Ltd. Machining tools having concave cutting surfaces for precision machining and methods of manufacturing such
US7677146B2 (en) 2006-05-10 2010-03-16 3M Innovative Properties Company Cutting tool using one or more machined tool tips in a continuous or interrupted cut fast tool servo
US20070261521A1 (en) * 2006-05-10 2007-11-15 Campbell Alan B Cutting tool using one or more machined tool tips in a continuous or interrupted cut fast tool servo
US20090237615A1 (en) * 2006-06-30 2009-09-24 Das Kamal K Correction of Surgically-Induced Astigmatism During Intraocular Lens Implants
US7628100B2 (en) * 2007-01-05 2009-12-08 3M Innovative Properties Company Cutting tool using one or more machined tool tips with diffractive features in a continuous or interrupted cut fast tool servo
US7852570B2 (en) 2007-01-05 2010-12-14 3M Innovative Properties Company Optical film having a set of diffractive features randomly repeating at variable distances
US20090220745A1 (en) * 2007-01-05 2009-09-03 3M Innovative Properties Company Cutting tool using one or more machined tool tips with diffractive features in a continuous or interrupted cut fast tool servo
US20080166190A1 (en) * 2007-01-05 2008-07-10 3M Innovative Properties Company Cutting tool using one or more machined tool tips with diffractive features in a continuous or interrupted cut fast tool servo
US20090110504A1 (en) * 2007-10-29 2009-04-30 3M Innovative Properties Company Cutting tool using one or more machined tool tips with diffractive features
US7669508B2 (en) * 2007-10-29 2010-03-02 3M Innovative Properties Company Cutting tool using one or more machined tool tips with diffractive features
US9810817B2 (en) 2008-04-02 2017-11-07 3M Innovative Properties Company Light directing film and method for making the same
US10197713B2 (en) 2008-04-02 2019-02-05 3M Innovative Properties Company Light directing film and method for making the same
US20110181971A1 (en) * 2008-04-02 2011-07-28 Campbell Alan B Methods and systems for fabricating optical films having superimposed features
US9632326B2 (en) 2010-10-28 2017-04-25 Philips Lighting Holding B.V. Collimator comprising a prismatic layer stack, and lighting unit comprising such collimator
US9383075B2 (en) 2011-02-22 2016-07-05 Koninklijke Philips N.V. Collimator comprising a prismatic layer stack, and lighting unit comprising such a collimator
US9972734B2 (en) 2012-03-27 2018-05-15 3M Innovative Properties Company Photovoltaic modules comprising light directing mediums and methods of making the same
WO2015123024A1 (en) * 2014-02-14 2015-08-20 Microsoft Technology Licensing, Llc Interactive display system
US9653044B2 (en) 2014-02-14 2017-05-16 Microsoft Technology Licensing, Llc Interactive display system
US20170090210A1 (en) * 2014-05-09 2017-03-30 Pure Depth Limited Diffraction grating for use with a multi-layered display system
US9791710B2 (en) * 2014-05-09 2017-10-17 Pure Depth Limited Diffraction grating for use with a multi-layered display system
US9902120B2 (en) * 2015-02-09 2018-02-27 Omnivision Technologies, Inc. Wide-angle camera using achromatic doublet prism array and method of manufacturing the same
US20160231473A1 (en) * 2015-02-09 2016-08-11 Omnivision Technologies, Inc. Wide-Angle Camera Using Achromatic Doublet Prism Array And Method of Manufacturing The Same
US10205041B2 (en) 2015-10-12 2019-02-12 3M Innovative Properties Company Light redirecting film useful with solar modules
US10510913B2 (en) 2015-10-12 2019-12-17 3M Innovative Properties Company Light redirecting film useful with solar modules
US10903382B2 (en) 2015-10-12 2021-01-26 3M Innovative Properties Company Light redirecting film useful with solar modules
US11448805B2 (en) * 2016-08-29 2022-09-20 Kyocera Corporation Optical member, method of manufacturing optical member, and image display system
WO2018129034A1 (en) * 2017-01-04 2018-07-12 3M Innovative Properties Company Asymmetric turning film with top-hat light output distributions
US11307333B2 (en) 2017-01-04 2022-04-19 3M Innovative Properties Company Asymmetric turning film with top-hat light output distributions
WO2020044240A1 (en) 2018-08-31 2020-03-05 3M Innovative Properties Company Light redirecting film having stray-light mitigation properties useful with solar modules
CN113671619A (zh) * 2020-05-14 2021-11-19 四川龙华光电薄膜股份有限公司 反射式显示装置及其前置光源模块

Also Published As

Publication number Publication date
KR20040020976A (ko) 2004-03-09
WO2003014777A2 (en) 2003-02-20
CN1963567A (zh) 2007-05-16
JP2004538506A (ja) 2004-12-24
CN1916670A (zh) 2007-02-21
CN100464197C (zh) 2009-02-25
US8579492B2 (en) 2013-11-12
US20050024754A1 (en) 2005-02-03
EP1412779A2 (en) 2004-04-28
CN1539085A (zh) 2004-10-20
AU2002322651A1 (en) 2003-02-24
US20030058553A1 (en) 2003-03-27
US20080049341A1 (en) 2008-02-28
CN100478715C (zh) 2009-04-15
WO2003014777A3 (en) 2003-10-16

Similar Documents

Publication Publication Date Title
US8579492B2 (en) Optical film having microreplicated structures and methods
US7330315B2 (en) Light-redirecting optical structures
JP5823958B2 (ja) 光再偏向フィルム及び該フィルムを使用したディスプレイ
KR102008564B1 (ko) 광 방향 전환 필름 및 이를 포함하는 디스플레이 시스템
EP2870494B1 (en) Decorative film articles utilizing fresnel lens films
KR101609400B1 (ko) 광 지향 필름 또는 광 지향 물품
JP2022130651A (ja) ファセット化された微細構造化表面
US20140009836A1 (en) Wood-like films and other decorative films utilizing fresnel mirrors
CN107533189B (zh) 渐变漫射体
JP7292253B2 (ja) ファセット化された微細構造化表面

Legal Events

Date Code Title Description
AS Assignment

Owner name: 3M INNOVATIVE PROPERTIES COMPANY, MINNESOTA

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:EPSTEIN, KENNETH A.;GRIFFITH, RICHARD F.;CAMPBELL, ALAN B.;REEL/FRAME:012871/0893;SIGNING DATES FROM 20011102 TO 20020415

STCB Information on status: application discontinuation

Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION