TWI744369B - 矽晶圓粗研磨用組成物之濃縮液 - Google Patents
矽晶圓粗研磨用組成物之濃縮液 Download PDFInfo
- Publication number
- TWI744369B TWI744369B TW106126003A TW106126003A TWI744369B TW I744369 B TWI744369 B TW I744369B TW 106126003 A TW106126003 A TW 106126003A TW 106126003 A TW106126003 A TW 106126003A TW I744369 B TWI744369 B TW I744369B
- Authority
- TW
- Taiwan
- Prior art keywords
- polishing
- water
- less
- weight
- soluble polymer
- Prior art date
Abstract
本發明提供稀釋後可發揮良好研磨性能且安定性優異之矽晶圓粗研磨用組成物之濃縮液。本發明所提供之矽晶圓粗研磨用組成物之濃縮液包含研磨粒、鹼性化合物及水溶性高分子。前述濃縮液中之前述水溶性高分子之慣性半徑rg[nm]相對於前述研磨粒之粒子間距離d[nm]之比[rg/d]為4.7以下。
Description
[0001] 本發明有關矽晶圓粗研磨用組成物之濃縮液。 本申請案係基於2016年8月2日提出申請之日本國專利申請號2016-152324號主張優先權,其申請全部內容併入本說明書中作為參考。
[0002] 半導體製品之製造等所用之矽基板表面一般經過研削步驟與拋光步驟而修飾為高品質之鏡面。上述拋光步驟典型上包含預拋光步驟與精拋光步驟。又,預拋光步驟亦稱為粗研磨步驟。經拋光步驟亦稱為精研磨步驟。此種研磨用組成物,基於製造或流通、保存等時之便利性或成本減低等之觀點,在供給於研磨對象物之前可為經濃縮之形態。亦即,上述研磨用組成物可為研磨液之濃縮液形態。所調製之濃縮液以水等稀釋後,使用於研磨。作為揭示此種先前技術之文獻舉例為專利文獻1。專利文獻2係揭示研磨用組成物所用之羥基纖維素之慣性半徑的文獻。 [先前技術文獻] [專利文獻] [0003] [專利文獻1] 日本專利申請公開2012-89862號公報 [專利文獻2] 日本專利申請公開2015-124231號公報
[發明欲解決之課題] [0004] 本發明人等針對矽晶圓粗研磨用組成物之性能提高進行檢討之結果,獲得如下見解:添加水溶性高分子且其慣性半徑越大,越能改善研磨性能。此處所稱研磨性能典型上為平坦度例如GBIR(Global Backside Ideal Range,總體背面理想範圍)。然而另一方面,水溶性高分子之慣性半徑過大時,成為於濃縮液階段之安定性降低之傾向。具體而言,上述濃縮液由於以比使用時更高濃度含有研磨粒、水溶性高分子等之成分,故有含有成分分離、凝集等而無法獲得良好安定性之虞。若能提供即使為高濃度之濃縮液形態,安定性亦優異且稀釋後能發揮良好研磨性能之研磨用組成物,則就便利性、成本減低等方面亦有利,實用上之優點大。 [0005] 本發明係鑑於上述情況而完成者,目的在於提供稀釋後可發揮良好研磨性能且安定性優異之矽晶圓粗研磨用組成物之濃縮液。 [用以解決課題之手段] [0006] 依據本發明,提供包含研磨粒、鹼性化合物及水溶性高分子之矽晶圓粗研磨用組成物之濃縮液。前述濃縮液中之前述水溶性高分子之慣性半徑rg[nm]相對於前述研磨粒之粒子間距離d[nm]之比[rg/d]為4.7以下。該構成之濃縮液顯示優異之安定性,稀釋後可發揮良好研磨性能。上述研磨性能典型上係平坦度改善效果。
[0007] 以下,說明本發明之較佳實施形態。又,本說明書中特別提及之事項以外之情況之實施本發明必要之情況係熟悉該技藝者基於該領域中之以往技術能以設計事項而掌握者。本發明可基於本說明書中揭示之內容與該領域中之技術知識而實施。 [0008] <研磨用組成物之濃縮液> (特性) 本文揭示之研磨用組成物之濃縮液包含研磨粒及水溶性高分子。上述研磨用組成物之濃縮液於以下有時簡稱為「濃縮液」。因此,該濃縮液之特徵為水溶性高分子之慣性半徑rg[nm]相對於研磨粒之粒子間距離d[nm]之比[rg/d]為4.7以下。滿足上述特性之濃縮液顯示優異之安定性。作為其理由雖非特別限定而解釋者,但認為係因為藉由滿足上述比[rg/d],濃縮液中水溶性高分子於研磨粒粒子間可安定存在,可使濃縮液之主要含有成分的研磨粒粒子及水溶性高分子於濃縮液中可安定分散之故。且,稀釋該濃縮液作為研磨液使用時,藉由含有上述水溶性高分子,可發揮對於研磨對象基板亦即矽晶圓之良好研磨性能。上述研磨性能具體而言為平坦度提高效果。上述比[rg/d],基於安定性提高之觀點,較好為3.8以下,更好為2.8以下,又更好為2.5以下,特佳為1.9以下。特佳之一樣態中,上述比[rg/d]典型上為1.0以下。上述比[rg/d]之下限並未特別限定,基於濃縮液之濃縮效率或研磨性能等之觀點,通常可為約0.3以上,例如可為0.6以上。研磨粒之粒子間距離[nm]及水溶性高分子之慣性半徑rg[nm]係藉後述方法測定。 [0009] (研磨粒) 本文揭示之研磨粒係以研磨粒之粒子間距離d[nm]滿足上述比[rg/d]之含量含於濃縮液中。較佳一樣態中,上述研磨粒之粒子間距離d為200nm以下。依據本文揭示之技術,如上述之研磨粒之粒子間距離d為特定值以下,且濃縮液中研磨粒粒子為比較接近之狀態,亦可實現優異之安定性。上述粒子間距離d,基於濃縮液之濃縮效率之觀點,更好為150nm以下,又更好為100nm以下,特佳為80nm以下。特佳一樣態中,上述粒子間距離d典型上為70nm以下。再者,於滿足上述比[rg/d]之範圍內,上述粒子間距離d亦可為例如60nm以下,進而為40nm以下。 [0010] 又,本說明書中之研磨粒之粒子間距離d[nm]係假定為濃縮液中所含之研磨粒均一分散,基於球之最密填充率[74%],由下式求得之理論值: d[nm]=Rs
×2-D1 此處,Rs
係以一個研磨粒子為中心,與鄰接之研磨粒粒子之對應球外切之球的半徑[nm],D1係研磨粒粒子之平均一次粒徑[nm]。Rs
換句話說係為濃縮液中具有分配於一個研磨粒粒子之濃縮液體積之球的半徑[nm],係藉如下方法求得。具體而言,將單位體積例如1L之濃縮液肢體基乘以填充率74%之值除以該單位體積之濃縮液所含之研磨粒粒子個數,求出一個研磨粒粒子可佔據之最大尺寸之球的體積Vs
,由式:Vs
=4/3×πRs 3
而求出Rs
。單位體積之濃縮液所含之研磨粒粒子個數係藉由將單位體積例如每1L之濃縮液之研磨粒重量[g/L]除以每1個研磨粒粒子之重量[g]而求得。單位體積之每濃縮液之研磨粒重量係由濃縮液中之研磨粒粒子含量及比重,以及濃縮液所含之研磨粒以外之成分的含量及比重而求出。研磨粒之比重於例如氧化矽研磨粒時,為2.2g/cm3
。濃縮液所含之研磨粒以外之成分通常以水系溶劑為主成分。每1個研磨粒粒子之重量[g]係自研磨粒粒子之平均一次粒徑[nm],將一次粒子視為真球時之球體積與研磨粒粒子之比重而求出。 [0011] 本文揭示之技術中,濃縮液、稀釋該濃縮液所得之研磨用組成物中所含之研磨粒之材質或性狀並未特別限制,可根據使用目的或使用樣態適當選擇。作為研磨粒之例舉例為無機粒子、有機粒子及有機無機複合粒子。無機粒子之具體例列舉為氧化矽粒子、氧化鋁粒子、氧化鈰粒子、氧化鉻粒子、二氧化鈦粒子、氧化鋯粒子、氧化鎂粒子、二氧化錳粒子、氧化鋅粒子、氧化鐵(Bengala)粒子等之氧化物粒子;氮化矽粒子、氮化硼粒子等之氮化物粒子;碳化矽粒子、碳化硼粒子等之碳化物粒子;金剛石粒子;碳酸鈣或碳酸鋇等之碳酸鹽等。有機粒子之具體例列舉為聚甲基丙烯酸甲酯(PMMA)粒子或聚(甲基)丙烯酸粒子、聚丙烯腈粒子等。該等研磨粒可單獨使用1種,亦可組合2種以上使用。又,所謂(甲基)丙烯酸意指包括丙烯酸及甲基丙烯酸。 [0012] 作為上述研磨粒較好為無機粒子,其中較好為由金屬或半金屬之氧化物所成之粒子。本文揭示之技術中作為特佳研磨粒舉例為氧化矽粒子。本文揭示之技術可較好地以上述研磨粒實質上由氧化矽粒子所成之樣態而實施。本文所謂「實質上」意指構成研磨粒之粒子之95重量%以上,較好98重量%以上,更好99重量%以上為氧化矽粒子,亦可為構成研磨粒之粒子的100重量%為氧化矽粒子。 [0013] 作為氧化矽之具體例,列舉為膠體二氧化矽、發煙二氧化矽、沉降二氧化矽等。氧化矽粒子可單獨使用1種或組合2種以上使用。基於於研磨對象物表面不易產生刮痕,且可發揮良好研磨性能之觀點,特佳為膠體氧化矽。此處所謂良好研磨性能係指使表面粗糙度降低之性能等。作為膠體氧化矽,可較好地採用將例如以水玻璃為原料藉由離子交換法製作之膠體氧化矽或烷氧化物法膠體氧化矽。又,水玻璃意指矽酸鈉。所謂烷氧化物法膠體氧化矽係藉由烷氧基矽烷之水解縮合反應而製造之膠體氧化矽。膠體氧化矽可單獨使用1種或組合2種以上使用。 [0014] 構成氧化矽粒子之氧化矽的真比重較好為1.5以上,更好為1.6以上,又更好為1.7以上。藉由增大氧化矽之真比重,有提高研磨速率之傾向。基於該觀點,特佳為真比重2.0以上之氧化矽粒子。特佳之一樣態中,上述真比重為例如2.1以上。氧化矽之真比重上限並未特別限制,典型上為2.3以下,例如2.2以下。作為氧化矽之真比重可採用使用乙醇作為置換液之液體置換法所得之測定值。 [0015] 本文揭示之研磨粒之平均一次粒徑並未特別限定。上述研磨粒典型上為氧化矽粒子。基於研磨速率等之觀點,上述平均一次粒徑為5nm以上為適當,較好為10nm以上,更好為30nm以上,又更好為40nm以上,特佳為45nm以上。於特佳一樣態中,上述平均一次粒徑為例如50nm以上。且,基於防止刮傷等之觀點,研磨粒之平均一次粒徑設為200nm以下為適當,較好為100nm以下,更好為80nm以下,又更好為70nm以下。於特佳一樣態中,研磨粒之平均一次粒徑為60nm以下,例如可為55nm以下。 又,本說明書中所謂平均一次粒徑意指自利用BET法測定之比表面積(BET值),藉由BET徑[nm]=6000/(真密度[g/cm3
]×BET值[m2
/g])之式算出之粒徑。此處,利用BET法測定之比表面積稱為BET值。例如氧化矽粒子時,可藉由BET徑[nm]=2727/BET值[m2
/g]算出BET徑。比表面積之測定例如可使用MICRO MATERIALS公司製之表面積測定裝置,商品名「Flow Sorb II 2300」進行。 [0016] 研磨粒之形狀可為球形,亦可為非球形。上述形狀係外形。成為非球形之粒子之具體例列舉為花生形狀、繭型形狀、金平糖形狀、橄欖球形狀等。花生形狀即為落花生之殼形狀。例如,可較好地採用粒子大多為花生形狀之研磨粒。 [0017] 雖無特別限制,但研磨粒之長徑/短徑比之平均值原理上為1.0以上,較好為1.05以上,更好為1.1以上。研磨粒之長徑/短徑比之平均值亦稱為平均長寬比。藉由增大平均長寬比,可實現更高之研磨速率。且,研磨粒之平均長寬比,基於減少刮痕等之觀點,較好為3.0以下,更好為2.0以下,又更好為1.5以下。 [0018] 研磨粒之形狀(外形)或平均長寬比可利用例如電子顯微鏡觀察而掌握。掌握平均長寬比之具體順序為例如使用掃描型電子顯微鏡(SEM),針對可辨識獨立粒子形狀之既定個數之氧化矽粒子,描繪出外切於各粒子圖像之最小長方形。所謂既定個數例如為200個。接著,針對對各粒子圖像描繪出之長方形,將其長邊之長度(長徑之值)除以短邊之長度(短徑之值)之值作為長徑/短徑比(長寬比)而算出。藉由算術平均上述既定個數之粒子長寬比,可求出平均長寬比。 [0019] 本文揭示之濃縮液中之研磨粒含量(濃度)並未特別限制,較好為50重量%以上。基於濃縮液之安定性或過濾性等之觀點,通常研磨粒含量為45重量%以下,例如40重量%以下,典型上為35重量%以下為適當。上述研磨粒含量較好為30重量%以下,更好為25重量%以下,又更好為20重量%以下。於進而較佳一樣態中,上述研磨粒含量為例如15重量%以下。上述濃縮液中之研磨粒含量,基於稀釋後之研磨用組成物之研磨粒濃度、或製造、流通、保存等之便利性等之觀點,通常為1重量%以上,例如3重量%以上,典型上為5重量%以上為適當。上述研磨粒含量較好為8重量%以上。於較佳一樣態中,上述研磨粒含量為例如10重量%以上,進而為12重量%以上。 [0020] (水溶性高分子) 本文揭示之濃縮液所含之水溶性高分子係使用具有滿足特定值以下之比[rg/d]的慣性半徑(rg:radius of gyration)者。包含該水溶性高分子之研磨漿料對於研磨對象基板可充分濡濕並親和,其結果,可改善研磨性能。此處所謂研磨性能典型上為平坦度。又,水溶性高分子之慣性半徑rg,主要可由該高分子之親水性、分子量等決定,係水溶液中水溶性高分子一分子之尺寸。上述慣性半徑rg之上限值由於限制了比[rg/d]之上限,故成為與上述粒子間距離d之相對關係中受限制之值。一樣態之水溶性高分子之慣性半徑rg約為500nm以下,且300nm以下左右為適當。又,使用慣性半徑rg為220nm以下,更好為150nm以下之水溶性高分子時,可較好地滿足上述比[rg/d]。亦有濃縮效率獲得改善之傾向。上述慣性半徑rg可為約100nm以下,例如可為70nm以下。且,較佳一樣態中,水溶性高分子之慣性半徑rg為30nm以上,更好為50nm以上。基於研磨對象基板之濡濕性之觀點,上述慣性半徑rg更好為80nm以上,又更好為100nm以上,特佳為120nm以上。特佳一樣態中,慣性半徑rg為例如140nm以上。依據本文揭示之技術,水溶性高分子之慣性半徑rg為特定值以上,濃縮液亦可實現優異之安定性。且使用包含慣性半徑rg為特定值以上之水溶性高分子的研磨液時,更良好地發揮對基板表面之濡濕性,有進一步改善研磨性能之傾向。此處所稱之研磨性能典型上為平坦度。又,本說明書中之水溶性高分子之慣性半徑rg可藉後述實施例中記載之方法測定。 [0021] 本文揭示之濃縮液所含之水溶性高分子之種類並未特別限定,可自研磨用組成物之領域中習知水溶性高分子種類之中適當選擇。水溶性高分子可單獨使用1種或組合2種以上使用。作為水溶性高分子之例,舉例為纖維素衍生物、澱粉衍生物、含氧基伸烷基單位之聚合物、含有氮原子之聚合物、聚乙烯醇等。其中,基於平坦度提高之觀點,較好為纖維素衍生物、澱粉衍生物,更好為纖維素衍生物。 [0022] 纖維素衍生物係含有β-葡萄糖單位作為主要重複單位之聚合物。作為纖維素衍生物之具體例舉例為羥基乙基纖維素(HEC)、羥基丙基纖維素、羥基乙基甲基纖維素、羥基丙基甲基纖維素、甲基纖維素、乙基纖維素、乙基羥基乙基纖維素、羧基甲基纖維素等。其中以HEC較佳。 [0023] 澱粉衍生物係含有α-葡萄糖單位作為主要重複單位之聚合物。作為澱粉衍生物之具體例舉例為α化澱粉、普魯蘭多糖(pullulan)、羧甲基澱粉、環糊精等。其中較好為普魯蘭多糖。 [0024] 含氧基伸烷基單位之聚合物例示為聚環氧乙烷(PEO)、或環氧乙烷(EO)與環氧丙烷(PO)或與環氧丁烷(BO)之嵌段共聚物、EO與PO或與BO之無規共聚物等。其中,較好為EO與PO之嵌段共聚物或EO與PO之無規共聚物。EO與PO之嵌段共聚物可為含有PEO嵌段與聚環氧丙烷(PPO)嵌段之二嵌段體、三嵌段體等。上述三嵌段體之例包含PEO-PPO-PEO型三嵌段體及PPO-PEO-PPO型三嵌段體。通常更好為PEO-PPO-PEO型三嵌段體。 EO與PO之嵌段共聚物或無規共聚物中,構成該共聚物之EO與PO之莫耳比[EO/PO],基於於水中之溶解性或洗淨性等之觀點,較好大於1,更好為2以上,又更好為3以上。進而較佳一樣態中,上述莫耳比[EO/PO]為例如5以上。 [0025] 作為含有氮原子之聚合物,主鏈中含有氮原子之聚合物及於側鏈官能基(側鏈基)中具有氮原子之聚合物之任一者均可使用。藉由使用含有氮原子之聚合物,可改善基板表面粗糙度。作為主鏈中含有氮原子之聚合物之例,舉例為N-醯基伸烷基亞胺型單體之均聚物及共聚物。N-醯基伸烷基亞胺型單體之具體例舉例為N-乙醯基伸乙基亞胺、N-丙醯基伸乙基亞胺等。作為於側鏈基中具有氮原子之聚合物舉例為例如含有N-乙烯基型之單體單位之聚合物等。例如可採用N-乙烯基吡咯啶酮之均聚物及共聚物等。本文揭示之技術中,可較好地採用N-乙烯基吡咯啶酮以50莫耳%以上比例聚合之N-乙烯基吡咯啶酮之均聚物及共聚物之至少一種(以下亦稱為「PVP」)。 [0026] 使用聚乙烯醇作為水溶性高分子時,該聚乙烯醇之皂化度並未特別限定。 [0027] 本文揭示之技術中,水溶性高分子P1之分子量可在滿足特定值以下之比[rg/d]的範圍內適當設定。基於安定性或濃縮效率等之觀點,水溶性高分子之重量平均分子量(Mw)可為約200×104
以下,通常為150×104
以下,例如100×104
以下為適當。上述Mw亦可為例如50×104
以下,亦可為30×104
以下。且,基於基板表面之保護性或研磨性能提高之觀點,通常Mw為1×104
以上為適當,更好為10×104
以上,又更好為20×104
以上。上述Mw為例如50×104
以上,可為100×104
以上。上述Mw對於纖維素衍生物可特別佳地採用。作為上述纖維素衍生物舉例為例如HEC。 [0028] 又,作為水溶性高分子之Mw,可採用基於水系之凝膠滲透層析法(GPC)之值(水系,聚環氧乙烷換算)。 [0029] 本文揭示之技術,較好以併用2種以上之水溶性高分子之樣態實施。基於兼具研磨性能(平坦度)與表面粗糙度之觀點,更好併用選自纖維素衍生物及澱粉衍生物之1種或2種以上之水溶性高分子P1與纖維素衍生物及澱粉衍生物以外之水溶性高分子P2之1種或2種以上。水溶性高分子P1典型上為纖維素衍生物例如HEC。水溶性高分子P2較好為主鏈中含有氮原子之聚合物、於側鏈官能基(側鏈基)中具有氮原子之聚合物,更好為含有N-乙烯基型之單體單位之聚合物。其中,特佳為N-乙烯基吡咯啶酮之均聚物及共聚物(典型上為PVP)等。 [0030] 本文揭示之技術中,組合使用水溶性高分子P1與水溶性高分子P2時,水溶性高分子P1與水溶性高分子P2之調配比例並未特別限定,例如水溶性高分子P2對於水溶性高分子P1之含量之比[P2/P1]為0.1以上為適當。上述比[P2/P1]為例如0.25以上。且,上述比[P2/P1]為約10以下為適當。上述比[P2/P1]為例如2.5以下,典型上未達1。又,上述水溶性高分子P1為例如HEC等之纖維素衍生物,上述水溶性高分子P2為例如PVP等之包含N-乙烯基型之單體單位的聚合物。 [0031] 併用水溶性高分子P1、P2之樣態中,水溶性高分子P1之分子量可於滿足特定值以下之比[rg/d]的範圍內適當設定。水溶性高分子P1之重量分子量(Mw),基於安定性或濃縮效率等之觀點,可為約200×104
以下,通常為150×104
以下,例如100×104
以下為適當。上述Mw亦可為例如50×104
以下,可為30×104
以下。且,基於基板表面之保護性或研磨性能提高之觀點,通常Mw為1×104
以上為適當,更好為10×104
以上,又更好為20×104
以上。上述Mw為例如50×104
以上,可為100×104
以上。上述Mw對於纖維素衍生物可特別佳地採用。作為上述纖維素衍生物舉例為例如HEC。 [0032] 水溶性高分子P2之分子量並未特別限定。水溶性高分子P2之重量平均分子量(Mw)可為約300×104
以下,通常為150×104
以下,例如50×104
以下為適當。基於安定性等之觀點,上述Mw亦可為30×104
以下,例如可為5×104
以下。且,基於表面保護性提高之觀點,通常Mw為1×104
以上為適當,更好為2×104
以上,又更好為3×104
以上。上述Mw對於N-乙烯基吡咯啶酮之均聚物及共聚物(典型上為PVP)可特別佳地採用。 [0033] 本文揭示之濃縮液中之水溶性高分子之含量(濃度)並未特別限定,可設為0.0001重量份以上。基於研磨性能提高等之觀點,較佳含量為0.001重量份以上,更好為0.0025重量份以上,例如為0.005重量份以上。上述研磨性能具體為平坦度。且,基於研磨速率等之觀點,上述含量較好為1重量份以下,更好為0.2重量份以下,又更好為0.1重量份以下,特佳為0.05重量%以下。特佳一樣態中,上述水溶性高分子之含量為例如0.02重量%以下。 [0034] 又,本文揭示之濃縮液中之水溶性高分子之含量,可由與濃縮液中所含之研磨粒之相對關係而特定。具體而言,水溶性高分子之含量,相對於研磨粒100重量份,設為0.001重量份以上為適當,基於研磨性能提高等之觀點,較好為0.005重量份以上,更好為0.01重量份以上,又更好為0.015重量份以上。進而較佳一樣態中,上述水溶性高分子之含量,相對於研磨粒100重量份,為例如0.03重量份以上。上述研磨性能具體為平坦度。且,基於安定性或研磨速率等之觀點,水溶性高分子之含量,相對於研磨粒100重量份,設為10重量份以上為適當,較好為1重量份以下,更好為0.5重量份以下,又更好為0.1重量份以下。進而較佳一樣態中,上述水溶性高分子之含量,相對於研磨粒100重量份,為例如0.05重量份以下。 [0035] (鹼性化合物) 本文揭示之濃縮液含有鹼性化合物。本說明書中所謂鹼性化合物係指具有藉由溶解於水中而提高水溶液之pH之功能的化合物。作為鹼性化合物可使用含氮之有機或無機之鹼性化合物、鹼金屬之氫氧化物、鹼土類金屬之氫氧化物、各種碳酸鹽或碳酸氫鹽等。作為含氮之鹼性化合物之例舉例為四級銨化合物、四級鏻化合物、氨、胺等。上述胺較好為水溶性胺。此等鹼性化合物可單獨使用1種或組合2種以上使用。 [0036] 作為鹼金屬之氫氧化物之具體例舉例為氫氧化鉀、氫氧化鈉等。作為碳酸鹽或碳酸氫鹽之具體例舉例為碳酸氫銨、碳酸銨、碳酸氫鉀、碳酸鉀、碳酸氫鈉、碳酸鈉等。作為胺之具體例舉例為甲胺、二甲胺、三甲胺、乙胺、二乙胺、三乙胺、乙二胺、單乙醇胺、N-(β-胺基乙基)乙醇胺、六亞甲基二胺、二伸乙基三胺、三伸乙基四胺、無水哌嗪、哌嗪六水合物、1-(2-胺基乙基)哌嗪、N-甲基哌嗪、胍、咪唑或三唑等唑(azole)類等。作為四級鏻化合物之具體例舉例為氫氧化四甲基鏻、氫氧化四乙基鏻等之氫氧化四級鏻。 [0037] 作為四級銨化合物可較好地使用四烷基銨鹽、氫氧化烷基三烷基銨鹽等之四級銨鹽。上述四級銨鹽典型為強鹼。該四級銨鹽中之陰離子成分可為例如OH-
、F-
、Cl-
、Br-
、I-
、ClO4 -
、BH4 -
等。其中作為較佳例舉例為陰離子係OH-
之四級銨鹽,亦即氫氧化四級銨。作為氫氧化四級銨之具體例舉例為氫氧化四甲基銨、氫氧化四乙基銨、氫氧化四丙基銨、氫氧化四丁基銨、氫氧化四戊基銨及氫氧化四己基銨等之氫氧化四烷基銨;氫氧化2-羥基乙基三甲基銨(亦稱為膽鹼)等之氫氧化羥基烷基三烷基銨等。該等中較好為氫氧化四烷基銨,其中較好為氫氧化四甲基銨(TMAH)。 [0038] 本文揭示之濃縮液可組合含有如上述之四級銨化合物與弱酸鹽。上述四級銨化合物可例如TMAH等之氫氧化四烷基銨。作為弱酸鹽可使用於使用氧化矽粒子之研磨,可適當選擇可藉由與四級銨化合物之組合而發揮期望緩衝作用者。弱酸鹽可單獨使用1種或組合2種以上使用。作為弱酸鹽之具體例舉例為碳酸鈉、碳酸鉀、碳酸氫鈉、碳酸氫鉀、原矽酸鈉、原矽酸鉀、碳酸鈉、乙酸鉀、丙酸鈉、丙酸鉀、碳酸鈣、碳酸氫鈣、乙酸鈣、丙酸鈣、乙酸鎂、丙酸鎂、丙酸鋅、乙酸錳、乙酸鈷等。較好為陰離子成分係碳酸離子或碳酸氫離子之弱酸鹽,特佳為陰離子成分係碳酸離子之弱酸鹽。又,作為陽離子成分,宜為鉀、鈉等之鹼金屬離子。作為特佳之弱酸鹽,舉例為碳酸鈉、碳酸鉀、碳酸氫鈉及碳酸氫鉀。其中,較佳為碳酸鉀(K2
CO3
)。 [0039] 作為鹼性化合物,於組合使用四級銨化合物與弱酸鹽時,四級銨化合物與弱酸鹽之調配比率並未特別限定,例如四級銨化合物:弱酸鹽設為1:9~9:1為適當,較好為3:7~8:2,更好為5:5~7:3。上述四級銨化合物為例如TMAH等之氫氧化四烷基銨。弱酸鹽為例如K2
CO3
等之陰離子成分為碳酸離子之弱酸鹽。 [0040] 本文揭示之濃縮液中之鹼性化合物之含量(濃度),基於濃縮液之安定性、稀釋後之研磨用組成物所致之研磨速率提高等之觀點,例如為0.1重量%以上,典型上為0.3重量%以上為適當,較好為0.5重量%以上,更好為0.6重量%以上,又更好為0.8重量%以上。進而較佳一樣態中,上述鹼性化合物含量例如為1.0重量%以上,典型上為1.2重量%以上。例如濃縮液以高倍率稀釋使用時,稀釋後之研磨粒濃度相對變低,有研磨粒之加工力亦呈降低傾向之情況。此等情況下,於濃縮液階段藉由增加鹼性化合物量,可強化稀釋後之化學研磨。上述濃縮液中之鹼性化合物含量之上限,基於保存安定性或表面品質等之觀點,設為10重量%以下為適當,較好為5重量%以下。於較佳一樣態中,上述鹼性化合物之含量為例如3重量%以下。 [0041] 又,濃縮液中之鹼性化合物之含量,亦可由與濃縮液中所含之研磨粒之相對關係而特定。具體而言,濃縮液中之鹼性化合物含量,相對於研磨粒100重量份,設為0.1重量份以上為適當,基於研磨速率提高等之觀點,較好為1重量份以上,更好為3重量份以上,又更好為6重量份以上。上述濃縮液中之鹼性化合物含量,例如約為12重量份以上,亦可為22重量份以上。且基於安定性或表面品質等之觀點,鹼性化合物之含量,相對於研磨粒100重量份,設為50重量份以下為適當,較好為30重量份以下。上述濃縮液中之鹼性化合物含量,相對於研磨粒100重量份,可為例如20重量份以下,可為10重量份以下。 [0042] (水) 本文揭示之濃縮液典型上包含水。水較好使用離子交換水(去離子水)、純水、超純水、蒸餾水等。為了極力避免阻礙濃縮液中所含之其他成分之作用,使用之水較好為例如過渡金屬離子之合計含量為100ppb以下。例如,可藉離子交換樹脂去除雜質離子,藉過濾去除異物,藉蒸餾等操作提高水之純度。又,本文揭示之濃縮液亦可視需要進一步含有可與水均勻混合之有機溶劑。上述有機溶劑為低級醇、低級酮等。通常濃縮液中所含之溶劑較好其90體積%以上為水,更好95體積%以上為水。更佳一樣態中,典型上濃縮液中所含之溶劑之99~100體積%為水。又本說明書中,有時使用水系溶劑之用語作為包含上述溶劑及水之總稱。 [0043] (螯合劑) 本文揭示之濃縮液可含有螯合劑作為任意成分。螯合劑藉由與濃縮液中可含之金屬雜質形成錯離子並捕捉其,而抑制因金屬雜質所致之研磨對象物之汙染發揮作用。螯合劑之例列舉為胺基羧酸系螯合劑及有機膦酸系螯合劑。胺基羧酸系螯合劑之例包含乙二胺四乙酸、乙二胺四乙酸鈉、氮基三乙酸、氮基三乙酸鈉、氮基三乙酸銨、羥基乙基乙二胺三乙酸、羥基乙基乙二胺三乙酸鈉、二伸乙基三胺五乙酸、二伸乙基三胺五乙酸鈉、三伸乙基四胺六乙酸及三伸乙基四胺六乙酸鈉。有機膦酸系螯合劑之例包含2-胺基乙基膦酸、1-羥基亞乙基-1,1-二膦酸、胺基三(亞甲基膦酸)、乙二胺肆(亞甲基膦酸)、二伸乙基三胺五(亞甲基膦酸)、乙烷-1,1-二膦酸、乙烷-1,1,2-三膦酸、乙烷-1-羥基-1,1-二膦酸、乙烷-1-羥基-1,1,2-三膦酸、乙烷-1,2-二羧基-1,2-二膦酸、甲烷羥基膦酸、2-膦醯基丁烷-1,2-二羧酸、1-膦醯基丁烷-2,3,4-三羧酸及α-甲基膦醯基琥珀酸。該等中以有機膦酸系螯合劑較佳。其中較佳者列舉為乙二胺肆(亞甲基膦酸)、二伸乙基三胺五(亞甲基膦酸)及二伸乙基三胺五乙酸。特佳之螯合劑列舉為乙二胺肆(亞甲基膦酸)及二伸乙基三胺五(亞甲基膦酸)。螯合劑可單獨使用1種或組合2種以上使用。 [0044] (其他成分) 本文揭示之濃縮液在不顯著妨礙本發明效果之範圍內,亦可視需要進一步含有界面活性劑、有機酸、有機酸鹽、無機酸、無機酸鹽、防腐劑、防黴劑等之可使用於研磨漿料之習知添加劑。作為界面活性劑,可較好地採用非離子性、陰離子性、陽離子性等之各種界面活性劑。其中,基於防止聚乙烯醇等之水溶性高分子之析出之觀點,較好為非離子性界面活性劑。上述研磨漿料典型為矽基板之拋光步驟所用之研磨漿料。 [0045] 本文揭示之濃縮液較好實質上不含氧化劑。其理由為於濃縮液中含氧化劑時,藉由將該濃縮液稀釋後之研磨漿料供給至研磨對象物(此處為矽基板)而使該研磨對象物表面氧化,生成氧化膜,藉此有使研磨速率降低之情況。本文所稱之氧化劑之具體例舉例為過氧化氫(H2
O2
)、過硫酸鈉、過硫酸銨、二氯異氰脲酸鈉等。又,所謂濃縮液實質上不含氧化劑意指至少不刻意含有氧化劑。 [0046] (pH) 本文揭示之濃縮液之pH典型上為8.0以上,較好為8.5以上,更好為9.0以上,又更好為9.5以上,例如10.0以上,特佳為10.5以上。濃縮液之pH若提高,則有稀釋後之研磨液之pH亦變高,提高研磨性能之傾向。另一方面,基於防止研磨粒溶解,抑制該研磨粒之機械研磨作用降低之觀點,濃縮液之pH為12.0以下為適當,較好為11.8以下,更好為11.5以下。上述研磨粒為例如氧化矽粒子。 [0047] 又,本文揭示之技術中,液狀組成物之pH係藉由使用pH計,使用標準緩衝液,經3點校正後,將玻璃電極放入測定對象的組成物中,測定經過2分鐘以上安定後之值而掌握。上述液狀組成物可為研磨漿料、其濃縮液等。又,作為pH計係使用例如堀場製作所製造之玻璃電極式氫離子濃度指示計(型號F-23)。再者,標準緩衝液為鄰苯二甲酸鹽pH緩衝液 pH:4.01(25℃),中性磷酸鹽pH緩衝液 pH:6.86 (25℃),碳酸鹽pH緩衝液 pH:10.01(25℃)。 [0048] 濃縮液之調製方法並未特別限制。例如可使用翼式攪拌機、超音波分散機、均質混合機等之習知混合裝置,混合濃縮液中所含之各成分。混合該等成分之樣態並未特別限制,例如可一次混合全部成分,亦可依適當設定之順序混合。關於後述之研磨用組成物,於濃縮液之稀釋前後,亦可適當採用同樣之混合方法。 [0049] (稀釋) 本文揭示之研磨用組成物之濃縮液以體積基準計大於5倍之倍率稀釋調製為研磨液後,使用於研磨對象物之粗研磨。研磨對象基板具體而言為矽晶圓。如此以特定以上之倍率稀釋之濃縮液由於含有成分往往成為高濃度,故該成分易分離、凝集而難以獲得良好安定性。此等構成中,藉由以上述比[rg/d]成為特定值以下之方式調製濃縮液,而使該濃縮液顯示優異安定性。依據本文揭示之技術,使用以體積基準計為大於10倍之倍率稀釋之濃縮液之構成中,於該濃縮液時亦顯示優異安定性,且稀釋後之研磨用組成物可實現良好之研磨性能。上述稀釋倍率以體積基準計可為15倍以上,例如為25倍以上。上述稀釋倍率之上限並未特別限定,以體積基準計為約50倍以下,例如為40倍以下,典型上可為35倍以下。 [0050] 上述稀釋可在期望時點進行。典型上,上述稀釋可藉由於上述濃縮液中添加上述水系溶劑並混合而進行。水系溶劑典型上為水。作為稀釋所用之液體,基於處理性、作業性等之觀點,較好使用實質上由水所成之水系溶劑。水典型上為離子交換水。上述水系溶劑係例如99.5~100體積%為水的水系溶劑。又,上述水系溶劑為混合溶劑時,可僅添加該水系溶劑之構成成分中之一部分成分進行稀釋,亦可添加以與上述水系溶劑不同之量比含有該等之構成成分之混合溶劑予以稀釋。 [0051] <研磨用組成物> 本文揭示之研磨用組成物含有上述濃縮液中所含之研磨粒、水溶性高分子及鹼性化合物。又,典型上含有水,進而可含有螯合劑、其他成分作為任意成分。針對該等具體例,由於如上述,故此處不再反覆重複說明。又研磨用組成物亦稱為研磨液或研磨用漿料。 [0052] 將本文揭示之濃縮液稀釋所得之研磨用組成物中之研磨粒含量,可由濃縮液之研磨粒濃度及稀釋倍率決定。一樣態中,上述含量較好為0.05重量%以上,更好為0.1重量%以上,又更好為0.3重量%以上。進而較佳樣態中,上述含量為例如0.5重量%以上。藉由增大研磨粒含量,可實現更高研磨速率。且,基於自研磨對象物之去除性等之觀點,上述含量通常10重量%以下為適當,較好為7重量%以下,更好為5重量%以下,又更好為3重量%以下。進而較佳一樣態中,上述含量為例如2重量%以下。 [0053] 上述研磨用組成物中之水溶性高分子之含量,基於研磨性能或表面品質提高等之觀點,適當為1×10-5
重量%以上,例如為5×10-5
重量%以上,較好為1×10-4
重量%以上。較佳一樣態中,水溶性高分子之含量為例如2×10-4
重量%以上。上述研磨用組成物中之水溶性高分子之含量上限可為例如1重量%以下。基於濃縮液之安定性或研磨速率、洗淨性等之觀點,水溶性高分子之含量較好為0.1重量%以下,更好為0.05重量%以下,又更好為0.02重量%以下。進而較佳之一樣態中,上述水溶性高分子之含量為例如0.01重量%以下,典型上為0.005重量%以下。 [0054] 又,研磨用組成物中之水溶性高分子之含量,相對於研磨粒100重量份,設為0.001重量份以上為適當,基於研磨性能提高等之觀點,較好為0.005重量份以上,更好為0.01重量份以上,又更好為0.015重量份以上。進而較佳之一樣態中,研磨用組成物中之水溶性高分子之含量,相對於研磨粒100重量份,為例如0.03重量份以上。上述研磨性能具體而言為平坦度。且,基於安定性或研磨速率等之觀點,水溶性高分子之含量,相對於研磨粒100重量份,設為10重量份以下為適當,較好為1重量份以下,更好為0.5重量份以下,又更好為0.1重量份以下。進而較佳之一樣態中,水溶性高分子之含量,相對於研磨粒100重量份,為例如0.05重量份以下。 [0055] 本文揭示之技術中,研磨用組成物中之鹼性化合物之含量例如為0.001重量%以上,典型上為0.01重量%以上為適當,基於研磨速率提高之觀點,較好為0.05重量%以上,更好為0.07重量%以上,又更好為0.09質量%以上。藉由增加鹼性化合物含量,亦可提高安定性。上述鹼性化合物含量之上限為5重量%以下為適當,基於表面品質等之觀點,較好為1重量%以下。於較佳一樣態中,上述鹼性化合物之含量為例如0.5重量%以下,典型上為0.2重量%以下。 [0056] 本文揭示之技術之研磨用組成物之pH為8.0以上,較好例如為8.5以上,更好為9.0以上,又更好為9.5以上。進而較佳一樣態中,上述pH例如為10.0以上。研磨液之pH若提高,則有提高研磨速率之傾向。研磨液之pH上限值並未特別限定,但基於更良好研磨研磨對象物之觀點,為12.0以下,較好例如11.5以下,更好11.0以下。基於提高表面品質之觀點,上述pH進而較好為10.8以下。進而較佳一樣態中,上述pH例如為10.6以下,典型上為10.5以下。又,上述表面品質提高典型上意指表面粗糙度減低。上述pH可較好地應用於例如矽晶圓之研磨所用之研磨液中。上述研磨液為例如粗研磨用之研磨液。 [0057] (用途) 本文揭示之技術,可較好地適用於以矽基板(尤其是矽晶圓)為研磨對象物之研磨中。本文所稱之矽晶圓之典型例為矽單晶晶圓,例如切割矽單晶錠塊所得之矽單晶晶圓。本文揭示之技術中之研磨對象面典型上為由矽所成之表面。 [0058] 上述矽基板,於使用本文揭示之研磨液之研磨步驟之前,亦可施以磨削或蝕刻等之比粗研磨步驟更上游之步驟中之可適用於矽基板之一般處理。又,本文揭示之技術中,使用上述研磨液之研磨步驟後,可對矽基板實施精研磨步驟。上述精研磨包含1或2次以上之拋光步驟,經過最終拋光,將矽晶圓精加工為高品質鏡面。又,最終拋光係指目的物製造製程中之最終拋光步驟。亦即,最終拋光係指該步驟後不再進行拋光之步驟。因此,本文揭示之研磨液、或稀釋前之濃縮液可用於經過磨削之矽晶圓之拋光。且,上述研磨液或濃縮液可用於矽晶圓之最終拋光前進行之粗研磨中。粗研磨亦稱為預拋光。 [0059] <研磨> 研磨對象物之研磨可例如以下般進行。亦即,將本文揭示之濃縮液稀釋而準備研磨用組成物(研磨漿料)。其次,將該研磨漿料(作用漿料)供給於研磨對象物,藉由常用方法予以研磨。矽晶圓之粗研磨中,典型上將經過研削步驟之研磨對象物(矽晶圓)裝設於研磨裝置,通過固定於該研磨裝置之壓盤(研磨壓盤)之研磨墊,於上述研磨對象物表面(研磨對象面)供給研磨漿料。典型上,邊連續供給上述研磨漿料,邊對研磨對象物表面抵壓研磨墊使兩者相對移動。上述移動可為例如旋轉移動。經過該研磨步驟而完成研磨對象物之研磨。 [0060] 上述研磨步驟使用之研磨墊並無特別限制。例如可使用發泡聚胺基甲酸酯類型、不織布類型、麂皮類型等之研磨墊。各研磨墊可含研磨粒,亦可不含研磨粒。 [0061] 作為研磨裝置可使用同時對磨研磨對象物兩面進行研磨之兩面研磨裝置,亦可使用僅對研磨對象物單面進行研磨之單面研磨裝置。雖未特別限定,但例如粗研磨步驟中可較好地採用兩面研磨裝置。兩面研磨裝置為例如批式之兩面研磨裝置。研磨裝置可為構成為每次研磨一片研磨對象物之單片式研磨裝置,亦可為於同一壓盤上可同時研磨複數研磨對象物之批式研磨裝置。 [0062] <洗淨> 結束粗研磨步驟之研磨對象物於開始精研磨步驟之前,典型上經洗淨。該洗淨可使用適當洗淨液進行。所使用之洗淨液並未特別限制,可使用例如半導體等領域中之一般SC-1洗淨液、SC-2洗淨液等。SC-1洗淨液係氫氧化銨(NH4
OH)與過氧化氫(H2
O2
)與水(H2
O)之混合液)。SC-2洗淨液係HCl、H2
O2
與H2
O之混合液。洗淨液之溫度可為例如室溫以上、至多約90℃左右之範圍。此處所謂室溫典型上指約15℃~25℃。基於提高洗淨效果之觀點,可較好使用50℃~85℃左右之洗淨液。 [0063] 經過如上述之粗研磨步驟、或洗淨步驟、精研磨步驟,而完成研磨對象物之研磨。上述研磨對象物於本文為矽基板,典型上為矽單晶晶圓。因此,依據本說明書,提供包含上述研磨步驟之研磨物之製造方法。上述製造方法具體而言為矽晶圓之製造方法。 [0064] 以上,依據本實施形態,提供包含研磨粒、鹼性化合物及水溶性高分子之矽晶圓粗研磨用組成物之濃縮液。前述濃縮液中之前述水溶性高分子之慣性半徑rg[nm]相對於前述研磨粒之粒子間距離d[nm]之比[rg/d]為4.7以下。該構成之濃縮液顯示優異之安定性,稀釋後可發揮良好之研磨性能。上述研磨性能典型上為平坦度改善效果。 [0065] 本文揭示之濃縮液之較佳一樣態中,前述比[rg/d]為2.5以下。藉由此構成,實現更優異之安定性。 [0066] 本文揭示之濃縮液之較佳一樣態中,前述研磨粒之粒子間距離d為200nm以下。依據本文揭示之技術,如上述般研磨粒之粒子間距離d為特定值以下,亦可實現優異之安定性。又,如上述般粒子間距離d為特定值以下之濃縮液,可濃縮為高濃度者,故就便利性或成本降低方面有利。 [0067] 本文揭示之濃縮液之較佳一樣態中,前述水溶性高分子之慣性半徑rg為30nm以上。依據本文揭示之技術,如上述般水溶性高分子之慣性半徑為特定值以上,濃縮液亦可實現優異之安定性。且,如上述般水溶性高分子之慣性半徑為特定值以上之研磨液可發揮更優異之研磨性能。上述研磨性能典型上為平坦度改善效果。 [0068] 本文揭示之濃縮液之較佳一樣態中,前述研磨粒之濃度為5重量%以上。依據本文揭示之技術,如上述般研磨粒之濃度為特定值以上,亦可實現優異之安定性。又,如上述具有特定值以上之研磨粒濃度之濃縮液,可濃縮為高濃度者,故就便利性或成本降低方面有利。 [0069] 本文揭示之濃縮液之較佳一樣態中,前述水溶性高分子之濃度為0.001~0.05重量%之範圍內。藉由使水溶性高分子之濃度為上述範圍,濃縮液有安定性優異之傾向,且稀釋後易於發揮更良好之研磨性能。 [0070] 本文揭示之較佳一樣態中,係以體積基準以大於10倍之倍率稀釋而使用於矽晶圓之粗研磨。依據本文揭示之技術,即使以特定以上之倍率稀釋之方式為高濃縮倍率,濃縮液之安定性亦優異。且,如上述濃縮為特定以上濃度之濃縮液基於便利性或成本減低方面較有利。 [0071] 本文揭示之典型一樣態中,前述濃縮液係使用於經過研削之矽晶圓之拋光。更具體而言,前述濃縮液使用於矽晶圓之最終拋光前所進行之粗研磨(預拋光)中。粗研磨亦稱為預拋光。 [實施例] [0072] 以下,說明本發明有關之數個實施例,但並非意圖將本發明限制於該實施例所示者。又,以下說明中之「%」只要未特別說明,則為重量基準。 [0073] 《實驗1》 <實施例1-1~1-11及比較例1-1> [研磨用組成物之濃縮液之調製] 將作為研磨粒之膠體氧化矽(平均一次粒徑54nm)、水溶性高分子(HEC,PVP)、TMAH、K2
CO3
與離子交換水混合,而分別調製實施例1-1~1-11及比較例1-1之研磨用組成物之濃縮液。各例之濃縮液中研磨粒及水溶性高分子之濃度如表1所示,TMAH及K2
CO3
之濃度分別為1.62%及1.05%。針對各例之濃縮液,求出研磨粒之粒子間距離d[nm],且以下述方法測定水溶性高分子之慣性半徑rg[nm]。由所得值,求出水溶性高分子之慣性半徑rg[nm]相對於研磨粒之粒子間距離d[nm]之比[rg/d]。各例中之研磨粒之粒子間距離d[nm]、水溶性高分子之慣性半徑rg[nm]及比[rg/d]示於表1。 [0074] [慣性半徑之測定方法] 水溶性高分子之慣性半徑rg之測定係首先以使水溶性高分子濃度成為0.1~1mg/mL之範圍之方式調製水溶液,針對所調製之各樣品使用光散射光度計「DLS-8000」(大塚電子公司製),以測定角度20~150度之範圍每10度進行測定,藉由1濃法作圖解析進行慣性半徑[nm]之計算。研磨用組成物之濃縮液中含複數種水溶性高分子時,以成為其濃度比之方式調節水溶性高分子進行測定。 [0075] [安定性] 將各例之濃縮液100g放入直徑2.5cm、高25cm之玻璃管中,於25℃靜置保存。藉由目視以下述5基準評價自保存開始後經過24小時後之上述濃縮液中之水溶性高分子有無分離。亦即,未見到液中水溶性高分子分離時評價為「A」,見到分離時,於上澄液之層未達2mm時評價為「B」,於上澄液之層為2mm以上且未達4mm時評價為「C」,於上澄液之層為4mm以上且未達5mm時評價為「D」,於上澄液之層為5mm以上時評價為「E」。A~D為實用上合格程度,E視為不合格。結果示於表1。 [0076][0077] 《實驗2》 <實施例2-1~2-14及比較例2-1~2-2> [研磨用組成物之濃縮液之調製] 將作為研磨粒之膠體氧化矽(平均一次粒徑54nm)、水溶性高分子(HEC,PVP,PVA)、TMAH、K2
CO3
與離子交換水混合,而分別調製實施例2-1~2-14及比較例2-1~2-2之研磨用組成物之濃縮液。各例之濃縮液中研磨粒及水溶性高分子之濃度如表2所示,TMAH及K2
CO3
係以稀釋後之研磨用組成物(研磨液)中分別成為0.067%及0.043%之方式添加於濃縮液中。針對實施例2-14之研磨用組成物,將作為非離子界面活性劑之聚氧伸乙基月桂基醚添加為0.001%之濃度。針對各例之濃縮液,求出研磨粒之粒子間距離d[nm],且以與實驗1同樣方法測定水溶性高分子之慣性半徑rg[nm],由所得值,求出水溶性高分子之慣性半徑rg[nm]相對於研磨粒之粒子間距離d[nm]之比[rg/d]。且,針對濃縮液之安定性,亦以與實驗1同樣方法進行評價。粒子間距離d[nm]、水溶性高分子之慣性半徑rg[nm]、比[rg/d]及濃縮液安定性之評價結果示於表2。 [0078] [矽晶圓之研磨] 使用離子交換水將各例之濃縮液以表2所示之稀釋倍率(體積基準)進行稀釋,獲得研磨液(作用漿料)。使用該研磨液以下述條件實施粗研磨。 (研磨條件) 研磨裝置:日本THINKY公司製的單面研磨機,型號「EJ-380IN」 研磨墊:NITTA HAAS公司製,商品名「MH S-15A」 研磨壓力:26.6kPa 漿料流量:100mL/分鐘 壓盤旋轉數:50rpm 壓頭旋轉數:50rpm 研磨量:8μm 工件種類:裸矽P-
<100> 工件尺寸:□60mm×60mm [0079] [研磨性能(平坦度)] 作為GBIR之代替評價,以下述方法評價平坦度。具體而言,使用NIKON公司製之評價機「DIGIMICRO MH-15M」,針對研磨後之晶圓面,於縱橫各6點以等間隔測定36點之厚度,將其最大值與最小值之差定義為晶圓厚度差,以下述4基準評價各例之晶圓厚度差。亦即,晶圓厚度差未達2.5μm時評價為「A」,晶圓厚度差為2.5μm以上且未達3.0μm時評價為「B」,晶圓厚度差為3.0μm以上且3.2μm以下時評價為「C」,晶圓厚度差為大於3.2μm時評價為「D」。A~C為實用上合格程度,D視為不合格。結果示於表2。 [0080] [研磨性能(表面粗糙度Ra)] 針對各例之粗研磨後之矽晶圓(完成粗研磨及隨後之洗淨之試驗片),使用非接觸表面形狀測定機(商品名「NewView 5032」,Zygo公司製),測定表面粗糙度Ra(算術平均表面粗糙度)。所得測量值換算為以比較例2-1之表面粗糙度Ra設為100%之相對值,藉以下2階段評價。結果示於表2。 A:未達100% B:超過100% [0081] [濃縮效率] 將各例之濃縮液之稀釋倍率視為濃縮效率(可濃縮倍率),藉以下3基準分類。亦即,可濃縮倍率大於20倍時記為「A」,可濃縮倍率大於10倍且20倍以下時記為「B」,可濃縮倍率為10倍以下時記為「C」。結果示於表2。 [0082][0083] 如表1所示,實驗1中,水溶性高分子之慣性半徑rg[nm]相對於研磨粒之粒子間距離d[nm]之比[rg/d]為4.7以下之實施例1-1~1-11之濃縮液,係安定性評價為合格程度。尤其,上述比[rg/d]為2.5以下之實施例1-1~1-7及1-11,安定性評價結果為A或B,可達成更優異之安定性。另一方面,上述比[rg/d]大於4.7之比較例1-1,濃縮液之安定性為不合格程度。 [0084] 又,如表2所示,實驗2中,上述比[rg/d]為4.7以下之實施例2-1~2-14之濃縮液,安定性評價為合格程度。尤其,上述比[rg/d]為2.5以下之實施例2-1~2-10、2-13及2-14,安定性評價結果為A或B,可達成更優異之安定性。另一方面,上述比[rg/d]大於4.7之比較例2-1,濃縮液之安定性為不合格程度。又,使用含水溶性高分子之實施例2-1~2-14,研磨性能(具體為平坦度)均為合格程度,相對於此,未使用水溶性高分子之比較例2-2,無法獲得良好之研磨性能(具體為平坦度)。 [0085] 以上,雖已詳細說明本發明之具體例,但該等不過為例示,並非限定專利申請範圍者。專利申請範圍所記載之技術中包含以上例示之具體例的各種變形、變更者。
Claims (6)
- 一種矽晶圓粗研磨用組成物之濃縮液,其係包含研磨粒、鹼性化合物及水溶性高分子者,前述濃縮液中之前述水溶性高分子之慣性半徑rg[nm]相對於前述研磨粒之粒子間距離d[nm]之比[rg/d]為4.7以下,前述研磨粒之粒子間距離d為100nm以下。
- 如請求項1之濃縮液,其中前述比[rg/d]為2.5以下。
- 如請求項1或2之濃縮液,其中前述水溶性高分子之慣性半徑rg為30nm以上。
- 如請求項1或2之濃縮液,其中前述研磨粒之濃度為5重量%以上。
- 如請求項1或2之濃縮液,其中前述水溶性高分子之濃度為0.001~0.05重量%之範圍內。
- 如請求項1或2之濃縮液,其係以體積基準計以大於10倍之倍率稀釋而使用於矽晶圓之粗研磨。