TWI476244B - Halogen-free resin composition - Google Patents

Halogen-free resin composition Download PDF

Info

Publication number
TWI476244B
TWI476244B TW101137677A TW101137677A TWI476244B TW I476244 B TWI476244 B TW I476244B TW 101137677 A TW101137677 A TW 101137677A TW 101137677 A TW101137677 A TW 101137677A TW I476244 B TWI476244 B TW I476244B
Authority
TW
Taiwan
Prior art keywords
resin
epoxy resin
weight
parts
bisphenol
Prior art date
Application number
TW101137677A
Other languages
English (en)
Other versions
TW201348323A (zh
Inventor
chang-yuan Li
Li Ming Chou
Li Chih Yu
Tse An Lee
Original Assignee
Elite Electronic Material Zhongshan Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Elite Electronic Material Zhongshan Co Ltd filed Critical Elite Electronic Material Zhongshan Co Ltd
Publication of TW201348323A publication Critical patent/TW201348323A/zh
Application granted granted Critical
Publication of TWI476244B publication Critical patent/TWI476244B/zh

Description

無鹵素樹脂組成物
本發明係關於一種無鹵素樹脂組成物，尤指一種應用於銅箔基板及印刷電路板之無鹵素樹脂組成物。
為因應世界環保潮流及綠色法規，無鹵素(Halogen-free)為當前全球電子產業之環保趨勢，世界各國及相關電子大廠陸續對其電子產品，制定無鹵素電子產品的量產時程表。歐盟之有害物質限用指令(Restriction of Hazardous Substances,RoHS)實施後，包含鉛、鎘、汞、六價鉻、聚溴聯苯與聚溴二苯醚等物質，已不得用於製造電子產品或其零元件。印刷電路板(Printed Circuit Board,PCB)為電子電機產品之基礎，無鹵素以對印刷電路板為首先重點管制物件，國際組織對於印刷電路板之鹵素含量已有嚴格要求，其中國際電子電機委員會(IEC)61249-2-21規範要求溴、氯化物之含量必須低於900 ppm，且總鹵素含量必須低於1500 ppm；日本電子迴路工業會(JPCA)則規範溴化物與氯化物之含量限制均為900 ppm；而綠色和平組織現階段大力推動的綠化政策，要求所有的製造商完全排除其電子產品中之聚氯乙烯及溴系阻燃劑，以符合兼具無鉛及無鹵素之綠色電子。因此，材料的無鹵化成為目前業者的重點開發項目。
新世代的電子產品趨向輕薄短小，並適合高頻傳輸， 因此電路板之配線走向高密度化，電路板的材料選用走向更嚴謹的需求。高頻電子元件與電路板接合，為了維持傳輸速率及保持傳輸訊號完整性，電路板之基板材料必須兼具較低的介電常數(dielectric constant,Dk)及介電損耗(又稱損失因數，dissipation factor,Df)。同時，為了於高溫、高濕度環境下依然維持電子元件正常運作功能，電路板也必須兼具耐熱、難燃及低吸水性的特性。環氧樹脂由於接著性、耐熱性、成形性優異，故廣泛使用於電子零元件及電機機械之覆銅箔積層板或密封材。從防止火災之安全性觀點而言，要求材料具有阻燃性，一般係以無阻燃性之環氧樹脂，配合外加阻燃劑之方式達到阻燃之效果，例如，在環氧樹脂中藉由導入鹵素，尤其是溴，而賦予阻燃性，提高環氧基之反應性。
然而，近來之電子產品，傾向於輕量化、小型化、電路微細化，在如此之要求下，比重大的鹵化物在輕量化的觀點上並不理想。另外，在高溫下經長時間使用後，可能會引起鹵化物之解離，而有微細配線腐蝕之虞。再者使用過後之廢棄電子零元件，在燃燒後會產生鹵化物等有害化合物，對環境亦不友善。為取代上述之鹵化物阻燃劑，有研究使用磷化合物作為阻燃劑，例如添加磷酸酯(中華民國專利公告I238846號)或紅磷(中華民國專利公告322507號)於環氧樹脂組成物中。然而，磷酸酯會因產生水解反應而使酸離析，導致影響其耐遷移性；而紅磷之阻燃性雖高，但在消防法中被指為危險物品，在高溫、潮濕環境下因為 會發生微量之膦氣體。
習知之銅箔基板(或稱銅箔積層板)製作之電路板技術中，係利用一環氧基樹脂與硬化劑作為熱固性樹脂組成物原料，將補強材(如玻璃纖維布)與該熱固性樹脂組成加熱結合形成一半固化膠片(prepreg)，再將該半固化膠片與上、下兩片銅箔於高溫高壓下壓合而成。先前技術一般使用環氧基樹脂與具有羥基(-OH)之酚醛(phenol novolac)樹脂硬化劑作為熱固性樹脂組成原料，酚醛樹脂與環氧基樹脂結合會使環氧基開環後形成另一羥基，羥基本身會提高介電常數及介電損耗值，且易與水分結合，增加吸濕性。
中華民國專利公告第I297346號揭露一種使用氰酸酯樹脂、二環戊二烯基環氧樹脂、矽石以及熱塑性樹脂作為熱固性樹脂組成物，此種熱固性樹脂組成物具有低介電常數與低介電損耗等特性。然而此製造方法於製作時必須使用含有鹵素(如溴)成份之阻燃劑，例如四溴環己烷、六溴環癸烷以及2,4,6-三(三溴苯氧基)-1,3,5-三氮雜苯，而這些含有溴成份之阻燃劑於產品製造、使用甚至回收或丟棄時都很容易對環境造成污染。為了提升銅箔基板之耐熱難燃性、低介電損耗、低吸濕性、高交聯密度、高玻璃轉化溫度、高接合性、適當之熱膨脹性，環氧樹脂、硬化劑及補強材的材料選擇成了主要影響因素。
就電氣性質而言，主要需考慮者包含材料的介電常數以及介電損耗。一般而言，由於基板之訊號傳送速度與基板材料之介電常數的平方根成反比，故基板材料的介電常 數通常越小越好；另一方面，由於介電損耗越小代表訊號傳遞的損失越少，故介電損耗較小之材料所能提供之傳輸品質也較為良好。
因此，如何開發出具有低介電常數以及低介電損耗之材料，並將其應用於高頻印刷電路板之製造，乃是現階段印刷電路板材料供應商亟欲解決之問題。
有鑒於上述習知技術之缺憾，發明人有感其未臻於完善，遂竭其心智悉心研究克服，憑其從事該項產業多年之累積經驗，進而研發出一種無鹵素樹脂組成物，以期達到低介電常數及高耐熱、高耐燃之目的。
本發明之主要目的在提供一種無鹵素樹脂組成物，其藉著包含特定之組成份及比例，以使可達到低介電常數、低介電損耗、高耐熱性及高耐燃性；可製作成半固化膠片或樹脂膜，進而達到可應用於銅箔基板及印刷電路板之目的。
為達上述目的，本發明提供一種無鹵素樹脂組成物，其包含：(A)100重量份之環氧樹脂(epoxy resin)；(B)10至100重量份之苯并噁嗪(benzoxazine)樹脂；(C)10至100重量份之苯乙烯馬來酸酐(styrene-maleic anhydride,SMA)共聚物；及(D)10至90重量份之雙環戊二烯(dicyclopentadiene,DCPD)酚醛樹脂。
上述之組成物的用途，其係用於製造半固化膠片、樹 脂膜、銅箔基板及印刷電路板。藉此，本發明之無鹵素樹脂組成物，其藉著包含特定之組成份及比例，以使可達到低介電常數、低介電損耗、高耐熱性及高耐燃性；可製作成半固化膠片或樹脂膜，進而達到可應用於銅箔基板及印刷電路板之目的。
本發明之無鹵素樹脂組成物中，該成分(A)環氧樹脂，係為下列其中一者或其組合：雙酚A(bisphenol A)環氧樹脂、雙酚F(bisphenol F)環氧樹脂、雙酚S(bisphenol S)環氧樹脂、雙酚AD(bisphenol AD)環氧樹脂、酚醛(phenol novolac)環氧樹脂、雙酚A酚醛(bisphenol A novolac)環氧樹脂、雙酚F酚醛(bisphenol F novolac)環氧樹脂、鄰甲酚(o-cresol novolac)環氧樹脂、三官能基(trifunctional)環氧樹脂、四官能基(tetrafunctional)環氧樹脂、多官能基(multifunctional)環氧樹脂、二環戊二烯(dicyclopentadiene,DCPD)環氧樹脂、含磷環氧樹脂、DOPO環氧樹脂、DOPO-HQ環氧樹脂、對二甲苯環氧樹脂(p-xylene epoxy resin)、萘型(naphthalene)環氧樹脂、苯并哌喃型(benzopyran)環氧樹脂、聯苯酚醛(biphenyl novolac)環氧樹脂、異氰酸酯改質(isocyanate modified)環氧樹脂、酚苯甲醛(phenol benzaldehyde epoxy)環氧樹脂及酚基苯烷基酚醛(phenol aralkyl novolac)環氧樹脂。其中，DOPO環氧樹脂可為DOPO-PN環氧樹脂、DOPO-CNE環氧樹脂、DOPO-BPN環氧樹脂，DOPO環氧樹脂可為DOPO-HQ-PN環氧樹脂、DOPO-HQ-CNE環氧樹脂、DOPO-HQ-BPN環氧樹脂。
本發明之無鹵素樹脂組成物中，該成分(B)苯并噁嗪樹脂，包含：雙酚A型苯并噁嗪樹脂、雙酚F型苯并噁嗪樹脂及酚酞型苯并噁嗪樹脂。更具體而言，其較佳係選自下列群組中之至少一者：
其中X1 及X2 係分別獨立為R或Ar或-SO2 -；R係選 自-C(CH3 )2 -、-CH(CH3 )-、-CH2 -及經取代或未經取代之二環戊二烯基；Ar係選自經取代或未經取代之苯、聯苯、萘、酚醛、雙酚A、雙酚A酚醛、雙酚F及雙酚F酚醛官能基。所述苯并噁嗪樹脂如Huntsman販賣之商品名LZ-8280或LZ-8290。本發明之無鹵素樹脂組成物中的苯并噁嗪樹脂，其添加種類可為上述之其中一者或其組合。
本發明之無鹵素樹脂組成物，以100重量份之環氧樹脂為基準，係添加10至100重量份之苯并噁嗪樹脂，於此添加範圍內之苯并噁嗪樹脂含量，可使該無鹵素樹脂組成物達到預期之低介電損耗值(Df)，若苯并噁嗪樹脂不足10重量份，則達不到預期之低介電損耗值要求，若超過100重量份，則該樹脂組成物製作之基板耐熱性變差。更具體的，本發明所述之無鹵素樹脂組成物，較佳係添加10至80重量份之苯并噁嗪樹脂。
本發明之無鹵素樹脂組成物中，該成分(C)苯乙烯馬來酸酐共聚物之苯乙烯(S)與馬來酸酐(MA)比例，可為1/1、2/1、3/1、4/1、6/1或8/1，如Sartomer販賣之商品名SMA-1000、SMA-2000、SMA-3000、EF-30、EF-40、EF-60及EF-80等之苯乙烯馬來酸酐共聚物。此外，所述苯乙烯馬來酸酐共聚物亦可為酯化之苯乙烯馬來酸酐共聚物，如商品名SMA1440、SMA17352、SMA2625、SMA3840及SMA31890。本發明之無鹵素樹脂組成物中的苯乙烯馬來酸酐共聚物，其添加種類可為上述之其中一者或其組合。
本發明之無鹵素樹脂組成物，以100重量份之環氧樹 脂為基準，係添加10至100重量份之苯乙烯馬來酸酐共聚物，於此添加範圍內之苯乙烯馬來酸酐共聚物含量，係可使該無鹵素樹脂組成物達到預期之低介電常數值(Dk)，若苯乙烯馬來酸酐共聚物之含量不足10重量份，則達不到預期之低介電常數要求，若超過100重量份，會造成該樹脂組成物製作之半固化膠片外觀不佳且易掉粉，造成半固化膠片之製程良率降低。更具體的，本發明之無鹵素樹脂組成物，較佳係添加10至50重量份之苯乙烯馬來酸酐共聚物。
本發明之無鹵素樹脂組成物中，該成分(D)雙環戊二烯酚醛樹脂係為具有雙環戊二烯結構之酚醛樹脂。如Momentive販賣之商品名SD-1806、SD-1809或SD-1819。
本發明之無鹵素樹脂組成物，以100重量份之環氧樹脂為基準，係添加10至90重量份之雙環戊二烯酚醛樹脂，於此添加範圍內之雙環戊二烯酚醛樹脂含量，係可使該無鹵素樹脂組成物達到良好的交聯性，並提升Tg及提升樹脂與銅箔之拉力值。若雙環戊二烯酚醛樹脂之含量不足10重量份，則該無鹵素樹脂組成物達不到預期之交聯性、Tg及銅箔拉力提升，若超過90重量份，會造成該樹脂組成物製作之基板耐熱性降低及吸水率上升，造成基板物性降低。更具體的，本發明之無鹵素樹脂組成物，較佳係添加15至50重量份之雙環戊二烯酚醛樹脂。
本發明之無鹵素樹脂組成物中，可進一步包含無鹵阻燃劑，該無鹵阻燃劑係可使用含氮阻燃劑或含磷阻燃劑， 所述無鹵阻燃劑係可選擇性添加下列至少一種化合物，但並不以此為限：雙酚聯苯磷酸鹽(bisphenol diphenyl phosphate)、聚磷酸銨(ammonium poly phosphate)、對苯二酚-雙-(聯苯基磷酸鹽)(hydroquinone bis-(diphenyl phosphate))、雙酚A-雙-(聯苯基磷酸鹽)(bisphenol A bis-(diphenylphosphate))、三(2-羧乙基)膦(tri(2-carboxyethyl)phosphine,TCEP)、三(異丙基氯)磷酸鹽、三甲基磷酸鹽(trimethyl phosphate,TMP)、二甲基-甲基磷酸鹽(dimethyl methyl phosphonate,DMMP)、間苯二酚雙二甲苯基磷酸鹽(resorcinol dixylenylphosphate,RDXP，如PX-200)、磷氮基化合物(phosphazene如SPB-100)、m-苯甲基膦(m-phenylene methylphosphonate,PMP)、聚磷酸三聚氰胺(melamine polyphosphate)、三聚氰胺氰尿酸酯(melamine cyanurate)及三-羥乙基異氰尿酸酯(tri-hydroxy ethyl isocyanurate)等，但並不以此為限。此外，無鹵阻燃劑亦可使用9,10-二氫-9-氧雜-10-磷菲-10-氧化物(9,10-dihydro-9-oxa-10-phosphaphenanthrene-10-oxide,DOPO)、含DOPO酚樹脂(如DOPO-HQ、DOPO-PN、DOPO-BPN)、含DOPO環氧樹脂、含DOPO-HQ環氧樹脂等，其中DOPO-BPN可為DOPO-BPAN、DOPO-BPFN、DOPO-BPSN等雙酚酚醛化合物。
本發明之無鹵素樹脂組成物，以100重量份之環氧樹脂為基準，係添加10至100重量份之無鹵阻燃劑，於此添加範圍內之無鹵阻燃劑含量，可使該無鹵素樹脂組成物達 到阻燃效果，若無鹵阻燃劑之含量不足10重量份，則達不到阻燃效果，若超過100重量份則吸水率上升且基板耐熱性變差。
本發明之無鹵素樹脂組成物，可再進一步包含無機填充物(filler)、硬化促進劑(curing accelerator)、矽氧烷偶合劑(silane coupling agent)、增韌劑(toughening agent)、溶劑(solvent)之其中一者或其組合。
本發明之無鹵素樹脂組成物進一步添加無機填充物之主要作用，在於增加樹脂組成物之熱傳導性、改良其熱膨脹性及機械強度等特性，且無機填充物較佳係均勻分佈於該樹脂組成物中。其中，無機填充物可包含二氧化矽(熔融態、非熔融態、多孔質或中空型)、氧化鋁、氫氧化鋁、氧化鎂、氫氧化鎂、碳酸鈣、氮化鋁、氮化硼、碳化鋁矽、碳化矽、二氧化鈦、氧化鋅、氧化鋯、雲母、勃姆石(boehmite,AlOOH)、煅燒滑石、滑石、氮化矽、煅燒高嶺土。且無機填充物可為球型、纖維狀、板狀、粒狀、片狀或針鬚狀，並可選擇性經由矽烷偶合劑預處理。
無機填充物可為粒徑100 μm以下之顆粒粉末，且較佳為粒徑1 nm至20 μm之顆粒粉末，最佳為粒徑1 μm以下之奈米尺寸顆粒粉末；針鬚狀無機填充物可為直徑50 μm以下且長度1至200 μm之粉末。
本發明之無鹵素樹脂組成物，以100重量份之環氧樹脂為基準，係添加10至1000重量份之無機填充物。若無機填充物之含量不足10重量份，則無顯著之熱傳導性，且 未改善熱膨脹性及機械強度等特性；若超過1000重量份，則該樹脂物組成物之填孔流動性變差，與銅箔之接著變差。
本發明所述之硬化促進劑係可包含路易士鹼或路易士酸等觸媒(catalyst)。其中，路易士鹼可包含咪唑(imidazole)、三氟化硼胺複合物、氯化乙基三苯基磷(ethyltriphenyl phosphonium chloride)、2-甲基咪唑(2-methylimidazole,2MI)、2-苯基咪唑(2-phenyl-1H-imidazole,2PZ)、2-乙基-4-甲基咪唑(2-ethyl-4-methylimidazole,2E4MI)、三苯基膦(triphenylphosphine,TPP)與4-二甲基胺基吡啶(4-dimethylaminopyridine,DMAP)中之一者或多者。路易士酸係可包含金屬鹽類化合物，如錳、鐵、鈷、鎳、銅、鋅等金屬鹽化合物，如辛酸鋅、辛酸鈷等金屬觸媒。
本發明所述之矽烷偶合劑，係可包含矽烷化合物(silane)及矽氧烷化合物(siloxane)，依官能基種類又可分為胺基矽烷化合物(amino silane)、胺基矽氧烷化合物(amino siloxane)、環氧基矽烷化合物(epoxy silane)及環氧基矽氧烷化合物(epoxy siloxane)。
本發明所述之所述增韌劑，係選自：橡膠(rubber)樹脂、聚丁二烯丙烯腈(carboxyl-terminated butadiene acrylonitrile rubber,CTBN)、核殼聚合物(core-shell rubber)等添加物。
本發明所述之溶劑係可選自甲醇、乙醇、乙二醇單甲醚、丙酮、丁酮(甲基乙基酮)、甲基異丁基酮、環己酮、甲 苯、二甲苯、甲氧基乙基乙酸酯、乙氧基乙基乙酸酯、丙氧基乙基乙酸酯、乙酸乙酯、二甲基甲醯胺、丙二醇甲基醚等溶劑或其混合溶劑。
本發明所述之無鹵素樹脂組成物，可再進一步包含下列樹脂之其一者或其組合：酚(phenol)樹脂、酚醛(phenol novolac)樹脂、聚苯醚(polyphenylene ether)樹脂、氰酸酯(cyanate ester)樹脂、異氰酸酯(isocyanate ester)樹脂、馬來醯亞胺(maleimide)樹脂、聚酯(polyester)樹脂、苯乙烯(styrene)樹脂、丁二烯(butadiene)樹脂、苯氧(phenoxy)樹脂、聚醯胺(polyamide)樹脂、聚醯亞胺(polyimide)樹脂。
本發明之再一目的在於揭露一半固化膠片(prepreg)，其具有低介電常數與低介電損耗、耐熱難燃性、低吸濕性及不含鹵素等特性。據此，本發明所揭露之半固化膠片可包含一補強材及前述之無鹵樹脂組成物，其中該無鹵樹脂組成物係以含浸等方式附著於該補強材上，並經由高溫加熱形成半固化態。其中，補強材係可為纖維材料、織布及不織布，如玻璃纖維布等，其係可增加該半固化膠片之機械強度。此外，該補強材可選擇性經由矽烷偶合劑或矽氧烷偶合劑進行預處理，如經矽烷偶合劑預處理之玻璃纖維布。
前述之半固化膠片經由高溫加熱或高溫且高壓下加熱可固化形成固化膠片或是固態絕緣層，其中無鹵樹脂組成物若含有溶劑，則該溶劑會於高溫加熱程序中揮發移除。
本發明之又一目的在於揭露一種銅箔基板(copper clad laminate)，其具有低介電特性、耐熱難燃性、低吸濕性及不含鹵素等特性，且特別適用於高速度高頻率訊號傳輸之電路板。據此，本發明提供一種銅箔基板，其包含兩個或兩個以上之銅箔及至少一絕緣層。其中，銅箔可進一步包含銅與鋁、鎳、鉑、銀、金等至少一種金屬之合金；絕緣層係由前述之半固化膠片於高溫高壓下固化而成，如將前述半固化膠片疊合於兩個銅箔之間且於高溫與高壓下進行壓合而成。
本發明所述之銅箔基板至少具有以下優點之一：低介電常數與低介電損耗、優良的耐熱性及難燃性、低吸濕性、較高的熱傳導率及不含鹵素之環保性。該銅箔基板進一步經由製作線路等製程加工後，可形成一電路板，且該電路板與電子元件接合後於高溫、高濕度等嚴苛環境下操作而並不影響其品質。
本發明之再一目的在於揭露一種印刷電路板(printed circuit board)，其具有低介電特性、耐熱難燃性、低吸濕性及不含鹵素等特性，且適用於高速度高頻率之訊號傳輸。其中，該電路板係包含至少一個前述之銅箔基板，且該電路板係可由習知之製程製作而成。
為進一步揭露本發明，以使本發明所屬技術領域者具有通常知識者可據以實施，以下謹以數個實施例進一步說明本發明。然應注意者，以下實施例僅係用以對本發明做進一步之說明，並非用以限制本發明之實施範圍，且任何本發明所屬技術領域者具有通常知識者在不違背本發明之 精神下所得以達成之修飾及變化，均屬於本發明之範圍。
為充分瞭解本發明之目的、特徵及功效，茲藉由下述具體之實施例，對本發明做一詳細說明，說明如後：分別將實施例1至7之樹脂組成物之組成列表於表一，比較例1至5之樹脂組成物之組成列表於表三。
實施例1(E1)
一種樹脂組成物，包含以下成份：(A)80重量份之二環戊二烯環氧樹脂(HP-7200)；(B)20重量份之聯苯環氧樹脂(NC-3000)；(C)35重量份之雙環戊二烯酚醛樹脂(SD-1809)；(D)50重量份之苯并噁嗪樹脂(LZ 8280)；(E)15重量份之苯乙烯馬來酸酐共聚物(EF-40)；(F)50重量份之磷腈化合物(SPB-100)；(G)50重量份之熔融二氧化矽(Fused silica)；(H)0.3重量份之觸媒(2E4MI)；及(I)60重量份之甲基乙基酮溶劑(MEK)。
實施例2(E2)
一種樹脂組成物，包含以下成份：(A)80重量份之二環戊二烯環氧樹脂(HP-7200)；(B)20重量份之聯苯環氧樹脂(NC-3000)；(C)36重量份之雙環戊二烯酚醛樹脂(SD-1809)；(D)50重量份之苯并噁嗪樹脂(LZ 8280)； (E)5重量份之苯乙烯馬來酸酐共聚物(EF-40)；(F)50重量份之磷腈化合物(SPB-100)；(G)50重量份之熔融二氧化矽；(H)0.3重量份之觸媒(2E4MI)；及(I)60重量份之甲基乙基酮溶劑(MEK)。
實施例3(E3)
一種樹脂組成物，包含以下成份：(A)80重量份之二環戊二烯環氧樹脂(HP-7200)；(B)20重量份之聯苯環氧樹脂(NC-3000)；(C)40重量份之雙環戊二烯酚醛樹脂(SD-1809)；(D)5重量份之苯并噁嗪樹脂(LZ 8280)；(E)40重量份之苯乙烯馬來酸酐共聚物(EF-40)；(F)50重量份之磷腈化合物(SPB-100)；(G)50重量份之熔融二氧化矽；(H)0.3重量份之觸媒(2E4MI)；(I)60重量份之甲基乙基酮溶劑(MEK)。
實施例4(E4)
一種樹脂組成物，包含以下成份：(A)80重量份之二環戊二烯環氧樹脂(HP-7200)；(B)20重量份之聯苯環氧樹脂(NC-3000)；(C)5重量份之雙環戊二烯酚醛樹脂(SD-1809)；(D)80重量份之苯并噁嗪樹脂(LZ 8280)；(E)25重量份之苯乙烯馬來酸酐共聚物(EF-40)；(F)50重量份之磷腈化合物(SPB-100)； (G)50重量份之熔融二氧化矽；(H)0.3重量份之觸媒(2E4MI)；及(I)60重量份之甲基乙基酮溶劑(MEK)。
實施例5(E5)
一種樹脂組成物，包含以下成份：(A)80重量份之二環戊二烯環氧樹脂(HP-7200)；(B)20重量份之聯苯環氧樹脂(NC-3000)；(C)95重量份之雙環戊二烯酚醛樹脂(SD-1809)；(D)10重量份之苯并噁嗪樹脂(LZ 8280)；(E)10重量份之苯乙烯馬來酸酐共聚物(EF-40)；(F)50重量份之磷腈化合物(SPB-100)；(G)50重量份之熔融二氧化矽；(H)0.3重量份之觸媒(2E4M1)；及(I)60重量份之甲基乙基酮溶劑(MEK)。
實施例6(E6)
一種樹脂組成物，包含以下成份：(A)80重量份之二環戊二烯環氧樹脂(HP-7200)；(B)20重量份之聯苯環氧樹脂(NC-3000)；(C)10重量份之雙環戊二烯酚醛樹脂(SD-1809)；(D)105重量份之苯并噁嗪樹脂(LZ 8280)；(E)10重量份之苯乙烯馬來酸酐共聚物(EF-40)；(F)50重量份之磷腈化合物(SPB-100)；(G)50重量份之熔融二氧化矽；(H)0.3重量份之觸媒(2E4MI)；及 (I)60重量份之甲基乙基酮溶劑(MEK)。
實施例7(E7)
一種樹脂組成物，包含以下成份：(A)80重量份之二環戊二烯環氧樹脂(HP-7200)；(B)20重量份之聯苯環氧樹脂(NC-3000)；(C)10重量份之雙環戊二烯酚醛樹脂(SD-1809)；(D)10重量份之苯并噁嗪樹脂(LZ 8280)；(E)105重量份之苯乙烯馬來酸酐共聚物(EF-40)；(F)50重量份之磷腈化合物(SPB-100)；(G)50重量份之熔融二氧化矽；(H)0.3重量份之觸媒(2E4MI)；及(I)60重量份之甲基乙基酮溶劑(MEK)。
比較例1(C1)
一種樹脂組成物，包含以下成份：(A)80重量份之二環戊二烯環氧樹脂(HP-7200)；(B)20重量份之聯苯環氧樹脂(NC-3000)；(C)60重量份之苯并噁嗪樹脂(LZ 8280)；(D)40重量份之苯乙烯馬來酸酐共聚物(EF-40)；(E)50重量份之磷腈化合物(SPB-100)；(F)50重量份之熔融二氧化矽；(G)0.3重量份之觸媒(2E4MI)；及(H)60重量份之甲基乙基酮溶劑(MEK)。
比較例2(C2)
一種樹脂組成物，包含以下成份： (A)80重量份之二環戊二烯環氧樹脂(HP-7200)；(B)20重量份之聯苯環氧樹脂(NC-3000)；(C)40重量份之雙環戊二烯酚醛樹脂(SD-1809)；(D)50重量份之苯并噁嗪樹脂(LZ 8280)；(E)50重量份之磷腈化合物(SPB-100)；(F)50重量份之熔融二氧化矽；(G)0.3重量份之觸媒(2E4MI)；及(H)60重量份之甲基乙基酮溶劑(MEK)。
比較例3(C3)
一種樹脂組成物，包含以下成份：(A)80重量份之二環戊二烯環氧樹脂(HP-7200)；(B)20重量份之聯苯環氧樹脂(NC-3000)；(C)50重量份之雙環戊二烯酚醛樹脂(SD-1809)；(D)40重量份之苯乙烯馬來酸酐共聚物(EF-40)；(E)50重量份之磷腈化合物(SPB-100)；(F)50重量份之熔融二氧化矽；(G)0.3重量份之觸媒(2E4MI)；及(H)60重量份之甲基乙基酮溶劑(MEK)。
比較例4(C4)
一種樹脂組成物，包含以下成份：(A)80重量份之二環戊二烯環氧樹脂(HP-7200)；(B)20重量份之聯苯環氧樹脂(NC-3000)；(C)10重量份之雙環戊二烯酚醛樹脂(SD-1809)；(D)10重量份之苯并噁嗪樹脂(LZ 8280)； (E)10重量份之苯乙烯馬來酸酐共聚物(EF-40)；(F)50重量份之磷腈化合物(SPB-100)；(G)50重量份之熔融二氧化矽；(H)0.3重量份之觸媒(2E4MI)；及(I)60重量份之甲基乙基酮溶劑(MEK)。
比較例5(C5)
一種樹脂組成物，包含以下成份：(A)80重量份之二環戊二烯環氧樹脂(HP-7200)；(B)20重量份之聯苯環氧樹脂(NC-3000)；(C)10重量份之苯并噁嗪樹脂(LZ 8280)；(D)10重量份之苯乙烯馬來酸酐共聚物(EF-40)；(E)50重量份之熔融二氧化矽；(F)0.3重量份之觸媒(2E4MI)；及(G)60重量份之甲基乙基酮溶劑(MEK)。
將上述實施例1至7及比較例1至5之樹脂組成物，分批於攪拌槽中混合均勻後置入一含浸槽中，再將玻璃纖維布通過上述含浸槽，使樹脂組成物附著於玻璃纖維布，再進行加熱烘烤成半固化態而得半固化膠片。
將上述分批製得的半固化膠片，取同一批之半固化膠片四張及兩張18 μm銅箔，依銅箔、四片半固化膠片、銅箔之順序進行疊合，再於真空條件下經由220℃壓合2小時形成銅箔基板，其中四片半固化膠片固化形成兩銅箔間之絕緣層。
分別將上述含銅箔基板及銅箔蝕刻後之不含銅基板做 物性量測，物性量測專案包含玻璃轉化溫度(Tg)、含銅基板耐熱性(T288)、含銅基板浸錫測試(solder dip 288℃，10秒，測耐熱回數，S/D)、不含銅基板PCT吸濕後浸錫測試(pressure cooking at 121℃，1小時後，測solder dip 288℃，20秒觀看有無爆板，PCT)、銅箔與基板間拉力(peeling strength,half ounce copper foil,P/S)、介電常數(Dk越低越佳)、介電損耗(Df越低越佳)及耐燃性(flaming test，UL94，其中等級優劣排列為V-0>V-1>V-2)。分別將實施例1至7之樹脂組成物之量測結果列表於表二，比較例1至5之樹脂組成物之量測結果列表於表四。
實施例1為本發明之無鹵素組成物，與實施例2及7相比較，實施例2之苯乙烯馬來酸酐共聚物不足，導致介電常數過高，而實施例7之苯乙烯馬來酸酐共聚物過多，導致PP外觀不佳，且物性及介電性質均較差。
實施例1與實施例3及6相比較，實施例3之苯并噁嗪樹脂不足，導致拉力過低且介電損耗較高，而實施例6之苯并噁嗪樹脂過多，導致耐熱性質不佳。
實施例1與實施例4及5相比較，實施例4之雙環戊二烯酚醛樹脂不足，導致拉力過低且耐熱性質不佳，而實施例5之雙環戊二烯酚醛樹脂過多，導致介電性質較差且耐熱性質不佳。
比較實施例1與比較例1至5，比較例1缺少雙環戊二烯酚醛樹脂，導致拉力較差且玻璃轉換溫度較低；比較例2缺少苯乙烯馬來酸酐共聚物，導致介電常數過高；比較例3缺少苯并噁嗪樹脂，導致介電損耗過高；比較例5缺少雙環戊二烯酚醛樹脂及阻燃劑，物性、耐熱性、耐燃性及介電性質均明顯較差。
如上所述，本發明完全符合專利三要件：新穎性、進步性和產業上的可利用性。以新穎性和進步性而言，本發明之無鹵素樹脂組成物，其藉著包含特定之組成份及比例，以使可達到低介電常數、低介電損耗、高耐熱性及高耐燃性；可製作成半固化膠片或樹脂膜，進而達到可應用於銅箔基板及印刷電路板之目的；就產業上的可利用性而言，利用本發明所衍生的產品，當可充分滿足目前市場的需求。
本發明在上文中已以較佳實施例揭露，然熟習本項技術者應理解的是，該實施例僅用於描繪本發明，而不應解 讀為限制本發明之範圍。應注意的是，舉凡與該實施例等效之變化與置換，均應設為涵蓋於本發明之範疇內。因此，本發明之保護範圍當以下文之申請專利範圍所界定者為準。

Claims (8)

  1. 一種無鹵素樹脂組成物，其包含：(A)100重量份之環氧樹脂；(B)10至100重量份之苯并噁嗪樹脂；(C)10至100重量份之苯乙烯馬來酸酐共聚物；以及(D)10至90重量份之雙環戊二烯酚醛樹脂；其中該苯并噁嗪樹脂係選自下列群組中之至少一者：雙酚A型苯并噁嗪樹脂、雙酚F型苯并噁嗪樹脂及酚酞型苯并噁嗪樹脂，該苯乙烯馬來酸酐共聚物之苯乙烯及馬來酸酐比例為1/1、2/1、3/1、4/1、6/1或8/1。
  2. 如申請專利範圍第1項所述之組成物，其中該環氧樹脂係選自下列群組中之至少一者：雙酚A環氧樹脂、雙酚F環氧樹脂、雙酚S環氧樹脂、雙酚AD環氧樹脂、酚醛環氧樹脂、雙酚A酚醛環氧樹脂、雙酚F酚醛環氧樹脂、鄰甲酚環氧樹脂、三官能基環氧樹脂、四官能基環氧樹脂、多官能基環氧樹脂、二環戊二烯環氧樹脂、含磷環氧樹脂、含DOPO環氧樹脂、含DOPO-HQ環氧樹脂、對二甲苯環氧樹脂、萘型環氧樹脂、苯并哌喃型環氧樹脂、聯苯酚醛環氧樹脂、異氰酸酯改質環氧樹脂、酚苯甲醛環氧樹脂及酚基苯烷基酚醛環氧樹脂。
  3. 如申請專利範圍第1項所述之組成物，其進一步包含無鹵阻燃劑，該無鹵阻燃劑係選自下列群組中之至少一者：雙酚聯苯磷酸鹽(bisphenol diphenyl phosphate)、聚磷酸銨(ammonium poly phosphate)、對苯二酚-雙-(聯苯基磷酸 鹽)(hydroquinone bis-(diphenyl phosphate))、雙酚A-雙-(聯苯基磷酸鹽)(bisphenol A bis-(diphenylphosphate))、三(2-羧乙基)膦(tri(2-carboxyethyl)phosphine,TCEP)、三(異丙基氯)磷酸鹽、三甲基磷酸鹽(trimethyl phosphate,TMP)、二甲基-甲基磷酸鹽(dimethyl methyl phosphonate,DMMP)、間苯二酚雙二甲苯基磷酸鹽(resorcinol dixylenyl phosphate,RDXP)、磷氮基化合物(phosphazene)、m-苯甲基膦(m-phenylene methylphosphonate,PMP)、聚磷酸三聚氰胺(melamine polyphosphate)、三聚氰胺氰尿酸酯(melamine cyanurate)及三-羥乙基異氰尿酸酯(tri-hydroxy ethyl isocyanurate)、9,10-二氫-9-氧雜-10-磷菲-10-氧化物(9,10-dihydro-9-oxa-10-phosphaphenanthrene-10-oxide,DOPO)、含DOPO酚樹脂、含DOPO環氧樹脂及含DOPO-HQ環氧樹脂。
  4. 如申請專利範圍第1至3項中任一項所述之組成物，其進一步包含選自下列群組中之至少一者：無機填充物、硬化促進劑、矽氧烷偶合劑、增韌劑及溶劑。
  5. 如申請專利範圍第1至3項中任一項所述之組成物，其進一步包含選自下列群組中之至少一者或其改質物：酚樹脂、酚醛樹脂、聚苯醚樹脂、氰酸酯樹脂、異氰酸酯樹脂、馬來醯亞胺、聚酯樹脂、苯乙烯樹脂、丁二烯樹脂、苯氧樹脂、聚醯胺及聚醯亞胺。
  6. 一種半固化膠片，其包含如申請專利範圍第1至5項中任一項所述之組成物。
  7. 一種銅箔基板，其包含如申請專利範圍第6項所述之半固化膠片。
  8. 一種印刷電路板，其包含如申請專利範圍第7項所述之銅箔基板。
TW101137677A 2012-05-22 2012-10-12 Halogen-free resin composition TWI476244B (zh)