TWI362424B - Carbon steel sheet hiving high carburizing quenching property and manufacturing method thereof - Google Patents
Carbon steel sheet hiving high carburizing quenching property and manufacturing method thereof Download PDFInfo
- Publication number
- TWI362424B TWI362424B TW099106131A TW99106131A TWI362424B TW I362424 B TWI362424 B TW I362424B TW 099106131 A TW099106131 A TW 099106131A TW 99106131 A TW99106131 A TW 99106131A TW I362424 B TWI362424 B TW I362424B
- Authority
- TW
- Taiwan
- Prior art keywords
- annealing
- less
- mass
- steel sheet
- acl
- Prior art date
Links
Classifications
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/02—Ferrous alloys, e.g. steel alloys containing silicon
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D1/00—General methods or devices for heat treatment, e.g. annealing, hardening, quenching or tempering
- C21D1/06—Surface hardening
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
- C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
- C21D8/0221—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the working steps
- C21D8/0226—Hot rolling
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
- C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
- C21D8/0221—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the working steps
- C21D8/0236—Cold rolling
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
- C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
- C21D8/0247—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the heat treatment
- C21D8/0263—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the heat treatment following hot rolling
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
- C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
- C21D8/0247—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the heat treatment
- C21D8/0268—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the heat treatment between cold rolling steps
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
- C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
- C21D8/04—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips to produce plates or strips for deep-drawing
- C21D8/0421—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips to produce plates or strips for deep-drawing characterised by the working steps
- C21D8/0426—Hot rolling
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
- C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
- C21D8/04—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips to produce plates or strips for deep-drawing
- C21D8/0421—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips to produce plates or strips for deep-drawing characterised by the working steps
- C21D8/0436—Cold rolling
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
- C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
- C21D8/04—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips to produce plates or strips for deep-drawing
- C21D8/0447—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips to produce plates or strips for deep-drawing characterised by the heat treatment
- C21D8/0463—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips to produce plates or strips for deep-drawing characterised by the heat treatment following hot rolling
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
- C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
- C21D8/04—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips to produce plates or strips for deep-drawing
- C21D8/0447—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips to produce plates or strips for deep-drawing characterised by the heat treatment
- C21D8/0468—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips to produce plates or strips for deep-drawing characterised by the heat treatment between cold rolling steps
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D9/00—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
- C21D9/46—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for sheet metals
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D9/00—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
- C21D9/52—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for wires; for strips ; for rods of unlimited length
- C21D9/54—Furnaces for treating strips or wire
- C21D9/56—Continuous furnaces for strip or wire
- C21D9/561—Continuous furnaces for strip or wire with a controlled atmosphere or vacuum
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/001—Ferrous alloys, e.g. steel alloys containing N
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/008—Ferrous alloys, e.g. steel alloys containing tin
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/04—Ferrous alloys, e.g. steel alloys containing manganese
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/06—Ferrous alloys, e.g. steel alloys containing aluminium
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/14—Ferrous alloys, e.g. steel alloys containing titanium or zirconium
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
- C22C38/32—Ferrous alloys, e.g. steel alloys containing chromium with boron
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
- C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
- C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
- C22C38/42—Ferrous alloys, e.g. steel alloys containing chromium with nickel with copper
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
- C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
- C22C38/44—Ferrous alloys, e.g. steel alloys containing chromium with nickel with molybdenum or tungsten
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C8/00—Solid state diffusion of only non-metal elements into metallic material surfaces; Chemical surface treatment of metallic material by reaction of the surface with a reactive gas, leaving reaction products of surface material in the coating, e.g. conversion coatings, passivation of metals
- C23C8/06—Solid state diffusion of only non-metal elements into metallic material surfaces; Chemical surface treatment of metallic material by reaction of the surface with a reactive gas, leaving reaction products of surface material in the coating, e.g. conversion coatings, passivation of metals using gases
- C23C8/08—Solid state diffusion of only non-metal elements into metallic material surfaces; Chemical surface treatment of metallic material by reaction of the surface with a reactive gas, leaving reaction products of surface material in the coating, e.g. conversion coatings, passivation of metals using gases only one element being applied
- C23C8/20—Carburising
- C23C8/22—Carburising of ferrous surfaces
Landscapes
- Chemical & Material Sciences (AREA)
- Engineering & Computer Science (AREA)
- Mechanical Engineering (AREA)
- Materials Engineering (AREA)
- Metallurgy (AREA)
- Organic Chemistry (AREA)
- Physics & Mathematics (AREA)
- Thermal Sciences (AREA)
- Crystallography & Structural Chemistry (AREA)
- Chemical Kinetics & Catalysis (AREA)
- Heat Treatment Of Sheet Steel (AREA)
- Solid-Phase Diffusion Into Metallic Material Surfaces (AREA)
Applications Claiming Priority (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
JP2009079959 | 2009-03-27 |
Publications (2)
Publication Number | Publication Date |
---|---|
TW201038748A TW201038748A (en) | 2010-11-01 |
TWI362424B true TWI362424B (en) | 2012-04-21 |
Family
ID=42780478
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
TW099106131A TWI362424B (en) | 2009-03-27 | 2010-03-03 | Carbon steel sheet hiving high carburizing quenching property and manufacturing method thereof |
Country Status (7)
Country | Link |
---|---|
US (1) | US20120006451A1 (fr) |
JP (1) | JP4659142B2 (fr) |
KR (1) | KR101122840B1 (fr) |
CN (1) | CN102149839B (fr) |
CA (1) | CA2736374A1 (fr) |
TW (1) | TWI362424B (fr) |
WO (1) | WO2010109778A1 (fr) |
Families Citing this family (16)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JP5458649B2 (ja) * | 2009-04-28 | 2014-04-02 | Jfeスチール株式会社 | 高炭素熱延鋼板およびその製造方法 |
CN102695814B (zh) * | 2010-10-27 | 2014-10-29 | 新日铁住金株式会社 | 表面硬化用机械结构用钢、机械结构用钢部件及其制造方法 |
KR101617505B1 (ko) * | 2011-04-27 | 2016-05-02 | 신닛테츠스미킨 카부시키카이샤 | 핫 스탬프 부재용 강판 및 그 제조 방법 |
KR101382675B1 (ko) * | 2012-03-19 | 2014-04-07 | 주식회사 포스코 | 내마모성과 가공성이 우수한 저합금 열연 강판 및 그 제조방법 |
CN104583445B (zh) * | 2012-08-28 | 2016-10-19 | 新日铁住金株式会社 | 钢板 |
JP5862802B2 (ja) * | 2012-12-28 | 2016-02-16 | 新日鐵住金株式会社 | 浸炭用鋼 |
EP2984198B1 (fr) | 2013-04-10 | 2021-06-23 | Tata Steel IJmuiden B.V. | Produit formé par formage à chaud de tôle d'acier à revêtement métallique, procédé pour former le produit et bande d'acier |
US20160129489A1 (en) * | 2013-06-13 | 2016-05-12 | Nippon Steel & Sumitomo Metal Corporation | A WIRE ROD HAVING TENSILE STRENGTH OF 950 TO 1600MPa FOR MANUFACTURING A STEEL WIRE FOR A PEARLITE STRUCTURE BOLT, A STEEL WIRE HAVING TENSILE STRENGTH OF 950 TO 1600MPa FOR A PEARLITE STRUCTURE BOLT, A PEARLITE STRUCTURE BOLT, AND MANUFACTURING METHOD FOR THE SAME |
JP5812048B2 (ja) * | 2013-07-09 | 2015-11-11 | Jfeスチール株式会社 | 焼入れ性および加工性に優れる高炭素熱延鋼板およびその製造方法 |
EP3040437B1 (fr) * | 2013-08-30 | 2019-10-30 | JFE Steel Corporation | Composant structural mécanique et son procédé de fabrication |
CN104178695B (zh) * | 2014-07-10 | 2017-04-26 | 燕山大学 | 一种风电轴承用中碳硼微合金化钢的制备方法 |
CN107075625B (zh) * | 2014-10-16 | 2019-07-09 | 日本制铁株式会社 | 高碳钢板及其制造方法 |
JP6610067B2 (ja) * | 2015-08-05 | 2019-11-27 | 日本製鉄株式会社 | 冷延鋼板の製造方法及び冷延鋼板 |
KR101751530B1 (ko) | 2015-12-28 | 2017-06-27 | 주식회사 포스코 | 공구용 강판 및 그 제조방법 |
TWI665310B (zh) * | 2018-10-02 | 2019-07-11 | 日商新日鐵住金股份有限公司 | 滲碳用鋼板及滲碳用鋼板的製造方法 |
CN113549830B (zh) * | 2021-07-16 | 2022-05-20 | 鞍钢股份有限公司 | 高表面硬度折弯性能优异的中碳球化索氏体工具钢及其生产方法 |
Family Cites Families (7)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JPH075970B2 (ja) * | 1989-12-18 | 1995-01-25 | 住友金属工業株式会社 | 高炭素薄鋼板の製造方法 |
JP3511268B2 (ja) * | 1992-05-29 | 2004-03-29 | 日新製鋼株式会社 | 含b鋼板の焼鈍方法 |
JP3166652B2 (ja) * | 1997-03-14 | 2001-05-14 | 住友金属工業株式会社 | 成形性にすぐれた高炭素薄鋼板の製造方法 |
JP3869754B2 (ja) * | 2002-05-16 | 2007-01-17 | 新日本製鐵株式会社 | バーリング加工時のバラツキが少ない浸炭焼入れ用鋼板及びその製造方法 |
JP4445365B2 (ja) * | 2004-10-06 | 2010-04-07 | 新日本製鐵株式会社 | 伸びと穴拡げ性に優れた高強度薄鋼板の製造方法 |
JP4846308B2 (ja) * | 2005-09-09 | 2011-12-28 | 新日本製鐵株式会社 | 使用中の硬さ変化が少ない高靭性耐摩耗鋼およびその製造方法 |
AU2007273767B2 (en) * | 2006-07-14 | 2010-08-12 | Nippon Steel Corporation | High-strength steel sheet excellent in stretch flangeability and fatigue property |
-
2010
- 2010-03-03 CN CN201080002531.4A patent/CN102149839B/zh active Active
- 2010-03-03 KR KR1020117005139A patent/KR101122840B1/ko active IP Right Grant
- 2010-03-03 JP JP2010529172A patent/JP4659142B2/ja active Active
- 2010-03-03 US US12/998,035 patent/US20120006451A1/en not_active Abandoned
- 2010-03-03 WO PCT/JP2010/001456 patent/WO2010109778A1/fr active Application Filing
- 2010-03-03 CA CA2736374A patent/CA2736374A1/fr not_active Abandoned
- 2010-03-03 TW TW099106131A patent/TWI362424B/zh not_active IP Right Cessation
Also Published As
Publication number | Publication date |
---|---|
TW201038748A (en) | 2010-11-01 |
CN102149839B (zh) | 2015-06-03 |
CA2736374A1 (fr) | 2010-09-30 |
WO2010109778A1 (fr) | 2010-09-30 |
KR101122840B1 (ko) | 2012-03-21 |
KR20110038172A (ko) | 2011-04-13 |
JPWO2010109778A1 (ja) | 2012-09-27 |
US20120006451A1 (en) | 2012-01-12 |
JP4659142B2 (ja) | 2011-03-30 |
CN102149839A (zh) | 2011-08-10 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
TWI362424B (en) | Carbon steel sheet hiving high carburizing quenching property and manufacturing method thereof | |
TWI404808B (zh) | 淬火性優異之硼添加鋼板及製造方法 | |
KR101665783B1 (ko) | 상온 가공성 및 저온 충격인성이 우수한 중탄소강 비조질 선재 및 이의 제조방법 | |
KR20140117586A (ko) | 내열 페라이트계 스테인리스 냉연 강판, 냉연 소재용 페라이트계 스테인리스 열연 강판 및 그들의 제조 방법 | |
WO2015077932A1 (fr) | Acier au manganèse et son procédé de production | |
JP2011153364A (ja) | クランクシャフトおよびその製造方法 | |
EP3927858B1 (fr) | Acier haute résistance présentant des propriétés mécaniques améliorées | |
KR101674775B1 (ko) | 유정용 열연강판, 이의 제조 방법 및 이에 의해 제조된 강관의 제조 방법 | |
EP2623625B1 (fr) | Tôle d'acier pour tube de canalisation, présentant une excellente résistance à la fissuration sous hydrogène, et son procédé de préparation | |
JP3606024B2 (ja) | 高周波焼入部品およびその製造方法 | |
JP6691967B2 (ja) | 靭性及び耐切断割れ性に優れた高硬度耐摩耗鋼、並びにその製造方法 | |
JP2003147482A (ja) | 非調質高強度・高靭性鍛造品およびその製造方法 | |
JP2002047532A (ja) | 溶接性に優れた高張力鋼板およびその製造方法 | |
KR20160080314A (ko) | 페라이트계 스테인리스강 및 그 제조방법 | |
JP7304415B2 (ja) | 防振性及び成形性に優れた高マンガン鋼材の製造方法、並びにこの製造方法により製造された高マンガン鋼材 | |
JP4196766B2 (ja) | 耐遅れ破壊特性および疲労特性に優れた鋼材およびその製造方法 | |
JP2012153926A (ja) | フェライト系ステンレス鋼板の製造方法 | |
JP2002256376A (ja) | 歪時効による靭性劣化の少ない鋼板 | |
WO2021039499A1 (fr) | Tôle d'acier à faible résistance pour estampage à chaud, composant estampé à chaud, et procédé de fabrication d'un composant estampé à chaud | |
JP4088886B2 (ja) | 耐熱処理変形性および表面処理特性に優れた快削工具鋼と、それを用いた金型 | |
KR101461713B1 (ko) | 고인성 선재 및 그의 제조방법 | |
JP5515949B2 (ja) | 板厚方向の材質均一性に優れた低炭素鋼材の製造方法 | |
JP4231466B2 (ja) | 耐磨耗性に優れた軟窒化処理鋼 | |
JP5515948B2 (ja) | 板厚方向の材質均一性に優れた極低炭素鋼材の製造方法 | |
KR101641793B1 (ko) | 페라이트계 스테인리스강 및 그 제조방법 |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
MM4A | Annulment or lapse of patent due to non-payment of fees |