TWI303639B - Multifunctional adhesive film and plasma display panel filter and plasma display panel using the same - Google Patents
Multifunctional adhesive film and plasma display panel filter and plasma display panel using the same Download PDFInfo
- Publication number
- TWI303639B TWI303639B TW094105487A TW94105487A TWI303639B TW I303639 B TWI303639 B TW I303639B TW 094105487 A TW094105487 A TW 094105487A TW 94105487 A TW94105487 A TW 94105487A TW I303639 B TWI303639 B TW I303639B
- Authority
- TW
- Taiwan
- Prior art keywords
- group
- substituted
- film
- chemical formula
- dye
- Prior art date
Description
1303639 九、發明說明: 相關申請案的交互參照 本案對2004年2月23日向韓國智慧財產局提出的第 10-2004-0011798 號和 2005 年 2 月 23 日提出的第 10-2005-0014754號韓國專利申請案主張擁有優先權,該等申請案揭 5 示的内容茲以參照併入本案。 【發明所屬之技術領域】 本發明係有關於一種具有像氖光切截(neon-cut)之類色 彩補償與近紅外線阻卻功能的膠膜,以及含有該膠膜之電 10漿顯示器濾光片。尤指一種在高溫高濕情況下透射率幾乎 不改變而具有優異耐久性、熱穩定性及黏合性的膠膜,以 及使用該膠膜的電漿顯示器濾光片。 【先前技術】 15 近來,電漿顯示面板(以下簡稱PDP)已被公認是寬螢幕 的主要顯示面板。 迄今,業已開發出螢幕寬度約為70吋的電漿顯示面 板。參閱第一圖,所示者係一電漿顯示面板一般結構的示 意圖。在第一圖中,數字11表示機殼,12表示驅動電路板, 20 13表示面板總成,14表示PDP濾光片,而15則表示蓋板。 PDP遽光片會對面板所射出之獨特橘色光譜而使紅色 光譜純度降低的情形予以補償,以及阻卻會使遙控器故障 的近紅外線和造成對人體有害之電磁輻射。為達成該等任 各,PDP攄光片包括若干功能層,例如抗反射層、用以補 -6- 1303639 償色彩純度的色_償層、近、 蔽層等。大體上,該等功心3 i及㈣1魏射< 堆疊並於彼此間般的㈣製成,再予 Ί:將具有色彩補償與近紅外線阻卻功 ;;題3:二省缸闲篁減少’就能降低與堆疊相關的品質 問通广T耗用的材料。舉例來說 ==t=使該薄膜具有三種功能,那麼就能讓 “ a 減半。或者,可採用一種能發揮該等功 Π占劑而,結構簡化。通常,染料會被用於阻卻近紅外 fit樹Γ?亥4染料的範例是可吸收特定波長區域之 光線的^切❹料與近紅外線阻卻染料…般說來,係 將含有黏結聚合物混合物的層面塗布在一透明基板上。於 此情況下,應制_將其上已㈣㈣ 入該PDP濾光片中。 15 20 為此目的而常使用的黏劑為橡膠、聚(乙烯峻)、丙烯 酸、石夕等。然而’橡膠黏劑的抗老化性不佳,聚(乙稀鍵) 黏劑的耐熱性不佳,而雜_黏合性不好。另一方面, 丙烯酸基黏劑因為具有優異的溶融性質,所以被廣泛用於 製備黏劑、喊,^且因為含有軸_聚合物分子為流體 狀態亚對壓力㈣’所以只要在室溫情訂對該黏劑施加 -點壓力,通常就可發揮優異的黏合性。但對於包含在該 黏劑中為改善色彩補償或近紅外線阻卻性能的染料來說, 這種流動性卻會減低該染料的耐熱性或财濕性。因此,選 用一種能耐高溫高濕的耐用染料,便相形重要。 -7- 1303639 兹將採用色彩補償染料和近紅外線染料的習用技藝說 明於後。 "" 曰本苐2001-248721號專利公報揭示一種在"ο至605 nm區域採用吖卟啉(azaporphyrin)染料的濾光片。這專利雖 5冒提及可加入一透明黏劑(丙烯酸黏劑)以增進黏合性,但卻 未詳細提及使用的黏劑結構,交聯劑與偶聯劑。此外,文 内雖曾提及584 nm處的初始透射率為15.9%,但卻未提及 耐久性測試之前和之後的透射率維持性。 4早國弟2002-0055410號專利公報揭示一種將花青染料 1〇和能對550至620 nm區域予以吸收之近紅外線染料施用到 一透明基板上而製備的近紅外線阻卻材料。韓國第 2004_0049280號專利公報揭示一種含有丙烯酸黏合樹脂。 近紅外線染料,紫外線吸收劑,和阻礙胺光穩定劑的壓感 黏劑組成。日本第2001-207142號專利公報揭示一種含有丙 I5烯酸黏合樹脂,花青紅外線吸收劑,與多功能丙烯酸共聚 物的紅外線吸收黏劑組成,另外日本第2004-107566號專利 公報也揭示一種含有具特定酸值之丙烯酸樹脂與聚次甲基 氖光切截染料的黏劑。 然而,韓國第2002-0055410號專利公報未提及黏劑結 2〇構與組成,韓國第2004-0049280號專利公報則未提出有關 近紅外線吸收薄膜的近紅外線阻卻效能。此外,日本第 2001-207142號專利公報未提出花青基近紅外線染料和花 青基氖光切截染料,但若只單獨使用花青染料時,即會發 生耐熱性與财濕性不良的情形。 -8- i3〇3639 再者,依習用方法製備的色彩補償薄膜與近紅外線阻 卻薄膜在尚溫高濕情況下,視黏結劑種類、塗布條件等而 .定’也都顯現出耐久性的差異。此外,堆疊這些薄膜來製 造PDP濾光片時,成本既高,效果也不佳。是以,有人曾 5試圖開發多功能黏合層’例如含有氖光切截層以及含有近 紅外線阻卻層的黏合層,惟’其在高溫高濕時的耐久性均 不符要求。 【發明内容】 本發明的-目的是提供一種具有色彩補償與近紅線阻 卻功能的多魏賴’其具有在高溫高濕時透射率幾乎不 改變的優異耐久性,具有優異熱穩定定,能長時間保持可 見光區域之透射率,以及具有良好的和近外線阻卻性能。 15 人右ΐίΓΓ—目的是提供—種電漿顯示面㈣光片及 二有4 W的顯示面板’該遽光片則包括一種不必 =黏劑層便具有色彩職與近紅外線阻卻㈣多 劑Μ,以致能簡化該薄膜。 ’ 板 功 20能膠膜 2達的,本發明提供—種適用於電漿顯示面 ^ 一丙城基黏劑與一近紅外線阻卻染料組成的多 臈宜包括-近紅外線阻卻染料。4力月匕膠膜。取好,該膠 本表月亦提供-種在基板的至少一側上包括前述至少 -9- 1303639 一種多功能膠膜的電漿顯示面板濾光片。 本發明另提供一種包括前述之電漿顯示面板濾光片的 電黎顯示面板。 5【圖式簡單說明】 第一圖係一示意圖,顯示出一電漿顯示面板的結構。 第二圖所示者係依本發明範例4製備之多功能膠膜的 光譜變化。 第三圖所示者係依本發明範例5製備之多功能膠膜的 10 光譜變化。 第四圖所示者係依本發明範例6製備之多功能膠膜的 光譜變化。 第五圖所示者係比較範例1所製備的膠膜在經高溫耐 久性測試後的光譜變化。 15 第六圖所示者係比較範例1所製備的膠膜在經高溫/高 濕測試後的光譜變化。 第七圖所不者係比較範例2所製備之膠膜的光譜變化。 第八圖所示者係依本發明含有範例7多功能黏劑的電 漿顯示濾光片結構。 20 帛九圖所示者係依本發明含有範例8多功能黏劑的電 漿顯示濾光片結構。 第十圖所示者係比較範例3的電聚顯示濃光片結構。 【實施方式】 -10- 1303639 兹將本發明詳予說明於後。 本發明提供一種具有良好耐久性及黏合性之用於電漿 顯示面板的多功能膠膜,該膠膜包括一具有優良黏合性及 耐久性且可供取代習用黏劑(pressure_senskive adhesive, 5 PSA)作為黏結樹脂的壓敏丙烯酸基黏劑,一色彩補償染 料,和一近紅外線染料。 本發明的膠膜包括一種能阻卻約為590 nm之氖光的氖 光切截(neon_cut)染料和一種能阻卻約850 nm和950 nm之 近紅外線的近紅外線染料,以符合電漿顯示器濾光片所需 ίο 的典型光學特性。 本發明的多功能膠膜可將PDP模組所產生、約為570 至600 nm的氖光峰值有效減低,並將800至1100 nm之近 紅外線(NIR)區域的光線阻卻到1〇%或以下。在高溫及高濕 條件下測試時’具體言之,在8〇〇c溫度下測試5〇()小時和 I5在60°C溫度及90%相對溼度(RH)條件下測試5〇()小時, 在可見光與NIR區域之染料濃度的變化為1〇%或更少。因 為一片膠膜可具有色彩補償或同時具有色彩補償與近紅外 線阻卻二種性能,所以能減低膠膜數量而使結構簡化。 現將本發明的膠膜詳予說明於後。 2〇 PDP具有-種設在吨前方並可發揮若干功能的薄膜 (滤光片),以便阻卻運作㈣所產生的電磁輻射,氖光輻 射’近紅外、線等。該薄骐係以一種黏劑(psA)形成。該黏劑 不但應具有優異的黏合性,而且在可見光區域(38〇〜78〇·) 也應具有極佳的透射率。 -11- 1303639 基此,本發明的薄膜包含有一丙烯酸基黏劑以及一近 紅外線件阻卻染料。而且,本發明的薄膜可包含有一丙烯 酸基黏劑以及一氖光切截染料,而且更包含有一近紅外線 阻卻染料。 5 作為本發明之黏結樹脂的黏劑,宜為一種玻璃化轉變 溫度(Tg)在0 °c或以下的丙烯酸基黏劑。對75至99.89 wt% (重量百分比)的一種具有CM2烷基的(甲基)丙烯酸酯單 體,〇·1至20 wt〇/◦的一種屬於功能性單體的α,β_不飽和羧酸 單體,和0.01至5 wt%的一種具有羥基的聚合單體加以共 10聚合’就可獲得這種丙烯酸基黏劑。嫻熟本技藝者均可進 行此共聚合。 最好’該丙烯酸基黏劑為一種丙烯酸丁酯(BA)/曱基丙 烯酸經乙基醋(HEMA)共聚物,或丙烯酸丁酯/丙烯酸(AA) 共聚物’因為相較於習用技藝的丙烯酸黏劑,它們在可見 15光區域和近紅外線區域具有優異的吸收能力。 該近紅外線阻卻染料可以是常用者,例如二亞銨 (dmnmonium)染料。必要時,也可跟金屬複合染料或酞青 (phthalocyanme)染料合用。該二亞銨染料可吸收9〇0至 1200nm這寬廣區域的近紅外線。 20 該近紅外線阻卻染料可以是下列構成之群組中選用的 至>、種。下列化學式4表示的二亞敍染料,下列化學式5 表不的醜青染料,下列化學式6表示的萘青 (naphthal〇cyanine)染料,和下列化學式7與8表示的金屬複 合物。 -12· 1303639
(化學式4)
(化學式5)
(化學式6) (化學式7) R1\^s S^/R1 Τ ;Μ; Τ R2/^S S 人 r2
L 」 (化學式8) 在化學式4中,心至R12各自分別是個氩原子,鹵原 子’以Ci_Ci6取代或未被取代的烧基,或以Ci_Ci6取代或 -13- 1303639 未被取代的芳基;x則是個單價或二價有機陰離子,單價 陰離子,或二價無機陰離子。 在化學式5和6中,R各自分別是個氫原子,鹵原子, 以CrC^取代或未被取代的烷基,取代或未被取代的笨 5基,具有C1-C5之取代或未被取代的烧氧基,取代或未被取 代的烯丙氧基’氟取代的燒氧基,或具有至少一個取代或 未被取代之氮原子的五角環;Μ則是從二個氫原子,二價 金屬原子’二彳貝或四彳貝取代之金屬原子,和氧化金屬 (oxy-metal)原子所構成之群組中選用的至少一種,並以錄 ίο (Ni)、鉑(Pt)、鈀(Pd)或銅(Cu)為宜。 在化學式7和8中’R和心至仏各自分別是個氫原子, 具有Ci-Cm的烷基,芳基,烷氧基,苯氧基,羥基,具有 的烧氨基’芳氨基’三氟曱基’具有Ci_Ci6的烧硫 基,芳硫基’硝基’氰基’鹵原子,苯基,或蔡基。 15 社學式4巾,該單财·離子可以是個有機紐 鲁料’有__子’有機硼_子#。該有機_離子 - 可以是醋酸鹽,乳酸鹽,三氟醋酸鹽,丙酸鹽,苯甲酸鹽, 。该有機續酸離子可以是
例如氟化物、氯化物、溴化物、碘化物、 硫氰化物、六氟 草酸鹽,丁二酸鹽,或硬脂酸鹽。該有機 金屬磺酸鹽,甲苯磺酸鹽,萘基單磺酸鹽 硝基苯續酸鹽,十二苯績酸鹽, (benzonesulfonate),乙烷磺酸鹽,或=惫 -14· 1303639 娣酸鹽、向氯酸鹽、高蛾酸鹽、硝酸鹽、四氟蝴酸鹽、六 氟磷酸鹽、鉬酸鹽、鎢酸鹽、鈦酸鹽、釩酸鹽、磷酸鹽、 和硼酸鹽。該二價無機陰離子則宜為萘—丨,孓二磺酸鹽,萘 -1,6-二磺酸鹽,萘二磺酸衍生物等。 该氖光切截染料的最大吸收波長為57〇至6〇〇 nm,半 :員寬:50 nm或以下。它宜具有—種分子内或分子間金
10 屬稷合物的結構。
舉例來說’該氖光城染料可以是從下列構成之 屬至少—種1有如下列化*式1表*之分子内金 屬^物的悄p。咖in)雜,和具有如下顺學式2鱼 表二分刊金屬複合物結構的花,㈣―最 子,该氖光切截染料係為卟琳染料。
(化學式2) -15- 1303639
(化學式3) 在化學式1中,Ri至Rs各自分別是個氫原子,齒原子’ 具有CrC16之取代或未被取代的烷基,具有crci6之取代 5或未被取代的烷氧基,取代或未被取代的苯基,取代或未 被取代的烯丙氧基,氟取代的烷氧基,或具有至少一個取 代或未被取代之氮原子的五角環;Μ則是氫原子,氧原子, 鹵原子,或配位的二價或四價金屬原子。 在化學式2和3中,R各自分別是個氫原子,具有1 ⑺至30碳原子之取代或未取代的脂族烴,具有1至8碳原子 之烧氧基’或具有6至30碳原子之芳基;X和Υ各自分別 是個函原子,硝基,羧基,具有2至8碳原子之烷氧基, 苯氧羰基,綾酸基,具有1至8碳原子之烷基,具有1至8 碳原子之烷氧基,或具有6至30碳原子之芳基。 15 在化學1的Μ中,該二價金屬原子可以是銅、辞、鐵、 鈷、鎳、釕、铑、鈀、錳、鍚、鎂、鈦等;該三價金屬原 子可以由鹵原子、經基、或諸如紹-氯、鎵-氯、銦氯、鐵-氣、釕-氯等之類的烷氧基取代;該四價原子則可由下列構 成之群組中選用的二個取代基予以取代··鹵原子,羥原子, 2〇和諸如二氣化矽、二氯化鎵、二氯化鈦、二氯化錫、氫氧 -16- 1303639 2亞:氫氧化亞鍺、氫氧化亞錳、氫氧化亞錫等之烷氧 二^ ’ M也可叹個與氧結合的氧化金屬,例如-氧 化叙、氧化鐘、氧化欽等。 5 10 15 以^量為準’該丙婦酸基黏劑對該近紅外線阻卻染料
的比例為10 : 1到10 〇〇〇 · 1 士 B ,觸.卜每重I比例因黏劑溶液t的 洛劑重虿份,黏劑溶液的# _ 糾减H外線阻㈣料的分子 沩先係數,和意欲的透射值而異。 』對於含有-氖光切截染料的_而言,該丙烯酸黏劑 對该風光切截染料的重量比例為1G : i至1(>,_ : !。這 量比例也因黏劑溶液中的溶劑重量份,黏·液的黏度, 氖光切截染料的分子消光係數,和意欲的透射值而里。又 本發明的多功能膠膜可進-步包括一溶劑。該溶劑可 以是常用的有機溶劑’且宜為丁酮(Mek) (THF)、醋酸乙醋、甲苯等。此溶劑的含量並未特別限南 本發明的膠膜尚可包括一交聯劑與—偶聯劑。 ° 該交聯劑可以是種多功能化合物,例如異氛酸龜 劑’環氧交聯劑"丫丙蚊聯劑,和金屬蟄合交聯劑: 宜者係異氰酸酯交聯劑,例如曱笨二異氰酸酯,二甲〜又 異氰酸酯,二苯基曱烷二異氰酸酯,六亞甲丄二異-^ 等,但並不以前述者為限。以重量為準,就每丨㈨份 丙烯酸共聚物而言,可用〇·〇1至2份的交聯劑。77、 該偶聯劑宜為石夕烧基偶聯劑。該矽酸基^聯劑可择系 合可靠性’尤其是任其在高溫與高濕度條件下長時間= 的情況下。該矽烷基偶聯劑可以是乙烯基矽烷,環氧 -17- 20 1303639 烷,甲基丙烯基矽烷等.舉 基三甲氧基魏,乙基三乙兒,可單獨或聯合使用乙 三甲翕其石々m 羊土發烧,Y-縮水甘油氧基丙基 5 15 20 至2份的魏基偶聯劑。μ丙知酸共聚物而言’可用讀 膠膜的製備方法並未特 法可以是將染料與黏結劑Μ,U例’其製備方 劑與偶聯劑,以獲得一種条匕冰加預疋數置的交聯 二=:可。所獲得的塗層宜具有至少— 二方::之塗布方法則可採取喷塗棒塗、旋 本舍明也提供-種用於—電襞顯示面板且包含有該多 :能膠膜的電漿顯示面板攄光片。藉由堆疊一片基底薄 邑衫補侦及近紅外線阻卻功能的 :二=膜,一片電磁干擾遮蔽薄膜(EMI薄膜)’和-片 …色螢幕處理薄膜等,即可製備該電漿顯示面減光片。 …將前述的各薄卿疊在1由玻璃或聚對苯二甲酸乙 ΠΕΤ)®成的透明基板,财製備電·顯㈣板遽光 ^本發明的濾光片可包括至少一片近紅外線薄膜,一片 色彩補償薄膜,和-片具有色彩補償與近紅外線阻卻功能 的缚膜。各該薄膜可於基板的上方或下方。該等多功能薄 版的至少-種若是被直接堆疊在基板上時,即不使用黏 ^如形成一道不包括該多功能薄膜的層面,便可用常見 -18- 1303639 的壓感黏劑(PSA)。也就是說,可採取習用黏劑來堆疊電磁 干擾遮蔽薄膜與黑色螢幕處理薄膜。 本發明另提供一種包括該電漿顯示面板濾光片的電聚 顯示面板。該面板可用本技藝熟知的方式予以製造,因而 5 在此不予詳述。 將包括本發明之膠膜的濾、光片用於一面板總成時,即 可獲付一種具有在咼溫及咼溫條件下透射率幾乎不改變的 優異耐久性,優異熱穩定性,和可見光區域之透射率良好 的電漿顯示面板。 15 20 如前所述,由一作為黏結樹脂且具有優異黏合性及耐 久性之丙烯酸基黏劑,與一色彩補償染料,或一色彩補償 染料和一近紅外線阻卻染料構成的電漿顯示面板用膠膜, 具有在高溫及高溫條件下透射率幾乎不改變的優異耐久 性’優異的熱穩定性,良好的可見光區域之透射率,和優 異的近紅外線阻卻性能。尤其,職本纽是軸,所以 ^製造電I顯示面域光片時不需另使用黏劑, 製程和減低濾光片的厚度。 舉若干制科㈣本㈣。_,下_各範例 僅供用以瞭解本發明,並非用以限制本發明。 [範例】 備及=翻職的乡魏_似如後職方式予以製 <薄膜的製備> 1.塗料溶液的製備:單獨以或藉由混合—丙埽酸丁醋 -19- 1303639 (BA)/甲基丙烯酸經乙基酿(HEMA)共聚物或_丙稀酸丁酿 (BA)/丙烯酸(AA)共聚物作為一黏合樹脂,和一氖光切截^ 料,-第-近紅外線阻卻染料,和一第二近紅外線阻卻; 料混合’據以製備-制於製财功能膠料塗料溶液。 2·塗布··將塗料溶液在一薄膜上塗布到15叫的厚 度。接著於12〇。(:溫度經3分鐘乾燥後,塗布表 一道薄膜。 理 3.熟成處理(aging):在室溫條件下進行3曰的熟成處 <耐久性測試> 時 高溫條件:於80 〇C溫度將薄膜置入一隔室内5〇〇小 比較其前與其後的透射率。 (範例1) 15 含有近紅外線阻卻染料之薄膜的製備 將溶解於84.5 ml的醋酸乙酯中刚重量份(15 5 w 的丙烯酸丁醋(BA)/甲基丙婦_乙基酿(hema)共聚物溶 液’ 〇.〇5重量份以化學式4表示和作為近紅外線阻卻染料 的二亞銨染料(lapan Carlit Co.公司供售的CIR1G81),〇〇5 20重量份作為異氛酸酯交聯劑的T_39M,和〇 〇7重量份作為 石夕炫偶聯劑的T-789J添加到45重量份的丁 g同(MEK)並予混 合而獲得-種塗料溶液。將這塗料溶液在一基底薄膜上塗 难到23 μιη的厚度,據以獲得一種多功 從事如前所述的财久性測試。下列表i所載者即為其 -20· 1303639 結果。 表1 可 見光區域的透射率(0/〇) NIR區域的 438nm 450nm 528nm 550nm 586nm 612nm 628nm 850nm 950nm 初始 70.4 68.0 71.0 81.4 86.5 87.0 85.3 2.3 3.0 500 小時 之後 70.3 67.7 71.7 82.1 87.3 87.4 85.5 2.4 3.1 如表1所示,經高溫測試後,該膠膜在可見光區域及 5近紅外線(NIR)區域均保持優異的透射率。 (範例2) 除了採用化學式5表示的欧青染料(Japan Catalyst Co. 公司供售的IP12)作為近紅外線阻卻染料外,其餘均以如同 ίο範例1的方式來製備膠膜。 (範例3) 除了改用丙烯酸丁酯/丙烯酸共聚物溶液取代丙烯酸丁 酯(BA)/曱基丙烯酸羥乙基酯(HEMA)共聚物溶液作為丙烯 15酸基黏劑外,其餘均以如同範例1的方式來製備膠膜。 (範例4) 將溶解於84.5 ml的醋酸乙S旨中100重量份(15.5 wt%) 的丙烯酸丁酯(BA)/曱基丙烯酸羥乙基酯(HEMA)共聚物溶 -21- 1303639 液,0.05重量份以化學式1表示的卟琳染料,〇·〇5重量份 作為異氰酸酯交聯劑的Τ-39Μ,和〇·〇7重量份作為矽烷偶 聯劑的T-789J添加到45重量份的丁酮(ΜΕΚ)並予混合而獲 得一種塗料溶液。將這塗料溶液在一基底薄膜上塗布到23 5 μπι的厚度,據以獲得一種多功能膠膜。 從事如前所述的耐久性測試。下列表2所載者即為其 結果。第二圖所示者係這膠膜的譜頻變化。 表2 可見光區域的透射率(%、 400nm 450nm 528nm 550nm 593nm 612nm 628nm 初始 68.8 70.3 60.9 52.5 27.9 53.6 74.0 500小 時後 68.7 70.5 60.5 52.3 28.0 54.1 74.2 ----— 10 如表2及第二圖所示,含有範例4之色彩補償染料的 膠膜顯示出在可見光區域保持優異的透射率。 (範例5) 15 將溶解於84.5 ml的醋酸乙酯中1〇〇重量份(14.5 ^力 的丙烯酸丁酯/丙烯酸共聚物溶液,0.05重量份以化學气i 表示的卟啉染料,〇·23重量份作為異氰酸酯交聯劑的 Τ-39Μ,和〇·〇3重量份作為矽烷偶聯劑的T-789J添加&衫 重量份的丁酮(ΜΕΚ)並予混合而獲得一種塗料溶液。將这 塗料溶液塗布在一基底薄膜上,據以獲得一種多功能膠 從事如前所述的耐久性測試。下列表3所載者即為其 -22- 20 1303639 結果。弟二圖所不者係這膠膜的譜頻變化。 表3 可見光區域的透射率 400nm 450nm 528nm 550nm 593nm 612nm 628nm 初始 67.9 69.8 60.7 52.3 27.4 53.0 73.6 500小 時後 67.0 69.6 60.5 52.4 28.0 53〇7 73.6 如表3及第三圖所示,含有範例5之色彩補償染料的 5膠膜顯示出在可見光區域保持優異的透射率。 (範例6) 除了另使用0.3重量份的卟啉染料,〇·3重量份的二亞 銨染料(第一近紅外線阻卻染料)(Japan Carlit C〇·公司供售 ίο的CIR1081),和0·1重量份的酜青(第二近紅外線阻卻染料) (Japan Catalyst Co公司供售的ΙΡ12),其餘均以如同範例4 的方式來製備膠膜。 從事如前所述的耐久性測試。下列表4所載者即為其 結果。第四圖所示者係這膠膜的譜頻變化。 15 表4 可 '見光區域的透射率(%) nir區域的 透射率(%) 400nm 450nm 528nm 550nm 586nm 612nm 628nm 850nm 950ππι 初始 23.4 583 52.2 48.6 24.3 45.9 63.4 4.2 2.7 500 小時 之後 23.6 655.3 52.3 48.5 24.4 45.4 62.9 5.0 4。0 -23- 1303639 如表4及第四圖所示,含有範例6之色彩補償染料的 膠膜不僅在可見光區域,而且在NIR區域均保持優異的透 射率。 5 (比較範例1) 將塗料溶液的組成更改成下列的組成,據以製備膠膜。 組成:作為氣光切截染料的花青(cyanine)染料 (0·0214g,TY102 ·· Asahi denka 公司),14BB (1 〇〇g,具有 _〇H 基的丙烯酸基),固化劑(〇.〇3g,T-39M),和偶聯劑(〇 〇7g, 10 T-789J)。 基板上的塗層:棒塗,乾燥厚度為25 μπι。 其後’從事如前所述的财久性測試。下列表5所載者 即為其結果。第五圖所示者係這膠膜的譜頻變化。 15 表5 NIR區域的透射率(%) 波長(nm) 450 550 587 628 耐久性測試前 57.6 38.7 11.5 66.5 在100 °c進行10分鐘耐久性測試 後 43.6 39.0 11.9 66.6 在问/皿(80 C)條件下進行500小時 耐久性測試後 43.0 44.3 16.1 67.3 另外’表6所載者為高溫高濕的測試結果,而第六圖 所示者係這膠臈的譜頻變化。 -24- 1303639 表6 NIR區域的透射率(%) 波長(nm) 450 550 587 628 财久性測試前 56.6 37.0 10.4 65.4 在100 °C進行10分鐘耐久性測試 兔 56.3 37.3 10.7 65.5 在向溫高濕(80 T,RH 90%)條件下 裏步500小時耐久性測試後 53.2 46.8 18.1 66.6 如前述結果所示,相較於本發明的各範例,含有比較 範例1之色彩補償染料的膠膜在可見光區域展示出不佳的 遷射維持性。 (比較範例2)
15 將塗料溶液的組成更改成下列的組成,據以製備膠膜。 組成:花青 NIR 吸收染料(O.Olg,TY102 : Asahi denka 公司),14BB (l〇〇g,具有_〇H基的丙烯酸基),固化劑 (〇.〇06g,T-39M),和偶聯劑(0.014g,T-789J)。 基板上的塗層:棒塗,乾燥厚度為20 μιη。 固化條件:室溫條件下經3日 其後,從事如前所述的耐久性測試。下列表7所載者 印為其結果。第七圖所示者係這膠膜的譜頻變化。 表7 測試前 NIR區域9透射率 450 550 586 628 854 在高溫(80 °C)條件下進行500小時 生測試後 80-9 81.2 84.8 85.1 84.3 84.7
80J 82.5 34.2 35.4 -25- 1303639 如前述結果所示,相較於本發明的各範例,比較範例2 的膠膜在可見光區域也展示出不佳的透射維持性。 (範例7) 電漿顯示面板濾光片的製備 在一玻璃基板上堆豐一抗反射薄膜(AR薄膜)3〇,一片 範例1製備的膠膜28, 一強化玻璃26, 一壓感黏劑層(PSA) 24,和一電磁干擾遮蔽薄膜(EMI薄膜)22,據以製備如第 八圖所示(五層結構)的電漿顯示面板濾光片。 10 (範例8) 電漿顯示面板濾光片的製備 在一玻璃基板上堆疊一抗反射薄膜(AR薄膜)30,^一片 範例4製備的膠膜28,一 NIR薄膜29,一強化玻璃26, 15 一 PSA24,和一電磁干擾遮蔽薄膜(EMI薄膜)22,據以製 備如第九圖所示(七層結構)的電聚顯示面板渡光片。 (比較範例3) 堆疊一抗反射薄膜30,一黏劑層24,一片比較範例1 20的色彩補償薄膜25,一黏劑層24,一片比較範例2的習用 近紅外線薄膜29,一黏劑層24,一強化玻璃26,一黏劑層 24 ’和一電磁干擾遮蔽薄膜22,據以製備電漿顯示面板滤 光片。所有該等薄膜係以一種橡膠黏劑(PSA)予以層合。第 十圖所不者係其結構。該比較範例3的滤光片具有九層多口 -26- 1303639 構。 從前述說明顯然可知,本發明的多功能膠膜因為以丙 烯k基黏劑作為黏結樹脂,並使用一色彩補償染料和一近 紅外線阻卻染料來發揮色彩補償與近紅外線阻卻性能,所 以增進了耐久性。此外,它還具有優異的近紅外 尤其因為膠膜本身便具有優異的黏合性,所以 劑:是以’它可簡化電賴示面板遽光片的結構而並 於製造電漿顯不面板濾光片和電漿顯示面板。 以上所舉實施例僅用以說明本發明而已 本發明之^。舉凡科本發_神賴㈣ ^ 變化,俱屬本發明申請專利範圍。 > 文或 -27· 1303639 【圖式簡單說明】 第一圖係一不意圖,顯示出一電漿顯示面板的結構。 第一圖所不者係依本發明範例4製備之多功能膠膜的 光譜變化。 5 第二圖所不者係依本發明範例5製備之多功能膠膜的 光譜變化。 第四圖所示者係依本發明範例6製備之多功能膠膜的 光譜變化。 第五圖所示者係比較範例1所製備的膠膜在經高溫耐 ίο 久性測試後的光譜變化。 第六圖所示者係比較範例1所製備的膠膜在經高溫/高 濕測試後的光譜變化。 第七圖所示者係比較範例2所製備之膠膜的光譜變化。 第八圖所示者係依本發明含有範例7多功能黏劑的電 15漿顯示遽光片結構。 第九圖所示者係依本發明含有範例8多功能黏劑的電 漿顯示濾光片結構。 第十圖所示者係比較範例3的電漿顯示濾光片結構。 -28- 1303639 【主要元件符號說明】 11機殼 13面板總成 15蓋板 5 24壓感黏劑層 26強化玻璃 29近紅外線薄膜 12驅動電路板 14電漿顯示面板濾光片 22電磁干擾遮蔽薄膜 25色彩補償薄膜 28膠膜 30抗反射薄膜 29-
Claims (1)
1303639 十、申請專利範圍: 1· 一種用於電漿顯示面板之多功能膠膜,其包含有一 丙烯酸基黏劑與一近紅外線阻卻染料; 其中该丙烯酸基黏劑係為一丙烯酸丁酯/曱基丙烯酸經 乙基酯共聚物’或者為一丙烯酸丁酯/丙烯酸共聚物; 其中以重量為準’對每100份之丙烯酸基黏劑而言, 該近紅外線^卩染_含量為。。。份。
近紅外利乾圍第1項所述之多功能膠膜’其中該 種:以下列從下列構成之族群中所選用的至少一 表示的❹染料的二亞銨染料、以下列化學式5 以下列化學式7或化幾^化學式6表示的萘青染料,以及 ffi 千式8所表示的金屬複合物;
R11
2X' R3 一 N R10 R4 r12
(化學式4) (化學式5) -30- 1303639
(化學式6) (化學式7) (化學式8) 5 ^化學式4中,Ri至Ri2各自分別是個氮原子函原 在化子 * d Ci-C16取代或 a Ci-C16取代或未被取代的烧基’或 , ’以 ^你劣嬙陰離子,或者 帔取代的芳基,且X是一單價或二價有械
一單價陰離子或二價無機陰離子; 在化學式5和6中,R各自分別是個氫原子’鹵原子’ 10
C,-Cl6取代或未被取代的烧基’取代或未被取代的本 基,具有CrC5之取代或未被取代的烷氧基,取代或未被取 代的烯丙氧基,氟取代的烷氧基,或具有至少一個取代戍 未被取代之氮原子的五角環,且Μ是從二個氫原子,二^ 金屬原子,三價或四價取代之金屬原子,和氧化金屬原子 所構成之群組中選用的至少一種,並以鎳、鉑、把或鋼為 -31- 15 1303639 宜; 在化學式7和8中,R和Ri至R4各自分別是個氣原 具有CpC!1的烷基,芳基,烷氧基,苯氧基,經基’ CrC!1的炫氨基,芳氨基,三氟甲基,具有具有 基,芳硫基,硝基,氰基,鹵原子,笨基,或蔡基1。、貌倚 3·如申請專利範圍第1項所述之多功能膠膜,发 重量為準,對每1〇〇份的該丙烯酸基黏劑而言,'更;=以 從0.01至2份的交聯劑與〇·〇1至2份的偶聯劑所構^含f 群中所選用的至少一種添加劑。 、 4· 一種電漿顯示面板濾光片,包含有一基板,且在該 基板的至少一面上具有如申請專利範圍第丨到3項其中任 何一項所述之多功能膠膜。 ,5.如申請專利範圍第4項所述之電漿顯示面板濾光 15 20 片更包含有一抗反射薄膜,一電磁干擾遮蔽薄膜,以及 黑色螢幕處理薄膜。 -32. 1 ·、一種電漿顯示面板,其包含有如申請專利範圍第4 工、所,之電漿顯示面板濾光片者。 光切多功能膠膜,其包含有一丙烯酸基黏劑與一氖 乙中ί丙烯酸基黏劑係為一丙烯酸丁酯2 3曱基丙烯酸羥 2 ^來物或者為一丙烯酸丁酯/丙烯酸共聚物; 其中以會蚤炎、、隹 里馬準,對每100份之丙烯酸基黏劑而言, ^8光域純的含量為G.G1至1〇份。 3 .如申請專利範圍第7項所述之多功能膠膜,其中該 1303639 氖光切截染料是從下列構成之族群中所選用的至少一種: 具有如下列化學式1所表示之分子内金屬複合物的卟琳 染料,以及具有如下列化學式2與3表示之分子間金屬複 合物結構的花青染料;
(化學式1)
其中 在化學式1中; -33- 1303639 R!至R8各自分別是個氫原子,鹵原子,具有CrCl6 之取代或未被取代的烷基,具有ci_Cl6之取代或未被取代 的烷氧基,取代或未被取代的苯基,取代或未被取代的烯 丙氧基,氟取代的烷氧基,或具有至少一個取代或未被取 5代之氮原子的五角環,且]V[係為氫原子,氧原子,鹵原子, 或配位的二價或四價金屬原子;以及 在化學式2和3中; R各自分別是個氫原子,具有1至30碳原子之取代或 未取代的脂族烴,具有1至8碳原子之烧氧基,或具有6 ίο至30碳原子之芳基,且X和γ各自分別是個鹵原子,硝 基’羧基,具有2至8碳原子之烷氧基,苯氧羰基,羧酸 基’具有1至8碳原子之烷基,具有1至8碳原子之烷氧 基’或具有6至30碳原子之芳基。 15
20 9·如申請專利範圍第7項所述之多功能膠膜,其中以 重畺為準,對每1〇〇份之丙烯酸基黏劑而言,更包含有〇·〇1 至10份的近紅外線阻卻染料。 、1〇·如申請專利範圍第7項所述之多功能膠膜,其中該 近紅外線阻卻染料係從下列構成之族群中所選用的至少一 ,一以下列化學式4表7F的二亞銨㈣、以下列化學式5 ==染料、以下列化學式6表示的蔡青染料,以及 化予式7或化學式8所表示的金屬複合物; -34- 1303639 R2—N
R11
R10 R12
N 2X L6
R n-R7 R8 (化學式4) R3-N r4 P
R (化學式5) R
(化學式6) μ; I —R (化學式7) as S (化學式8) 其中 鹵原 在化學式4中,&至R12各自分別是個氫原子 -35- 1303639 子,以Ci-Ci6取代或未被取代的烷基,或以CVCm取代或 未被取代的芳基’且x是一單價或二價有機陰離子,或者 係為一單價陰離子或二價無機陰離子; 在化學式5和6中,R各自分別是個氫原子,鹵原子, 5以取代或未被取代的烷基,取代或未被取代的苯 基,具有CrC5之取代或未被取代的烷氧基,取代或未被取 代的烯丙氧基,氟取代的烷氧基,或具有至少一個取代或 未被取代之氮原子的五角環,且Μ是從二個氫原子,二價 金屬原子,三價或四價取代之金屬原子,和氧化金屬原子 10所構成之群組中選用的至少一種,並以鎳、鉑、把或銅為 宜; 在化學式7和8中,R和心至^各自分別是個氫原子, 具有Ci_Ci6的烧基’芳基’烧氧基,苯氧基,經基,具有 CrCw的烷氨基,芳氨基,三氟甲基,具有CpCi6的燒硫 I5基’芳硫基,硝基,氰基,鹵原子,苯基,或萘基。 11·如申請專利範圍第7項所述之多功能膠膜,其中以 重篁為準’對每1〇〇份的該丙浠酸基黏劑而言,更包含有 從〇·〇1至2份的交聯劑與0·01至2份的偶聯劑所構成之姨 群中所選用的至少一種添加劑。 、 20 12· 一種電漿顯示面板濾光片,包含有一基板,且在該 基板的至少一面上具有如申請專利範圍第7到U項其中^ 何一項所述之多功能膠膜。 13·如申請專利範圍第12項所述之電漿顯示面板據光 片,更包含有一抗反射薄膜,一電磁干擾遮蔽薄膜,以及 -36- 1303639 一黑色螢幕處理薄膜。 14. 一種電漿顯示面板,其包含有如申請專利範圍第 12項所述之電漿顯示面板濾光片者。
-37· 1303639 七、指定代表圖: (一) 本案指定代表圖為:第(二)圖 (二) 本代表圖之元件符號簡單說明:無 八、本案若有化學式時,請揭示最能顯示發明特徵的化學式:無