TW202409225A - 研磨用組合物及使用此的研磨方法 - Google Patents
研磨用組合物及使用此的研磨方法 Download PDFInfo
- Publication number
- TW202409225A TW202409225A TW112143196A TW112143196A TW202409225A TW 202409225 A TW202409225 A TW 202409225A TW 112143196 A TW112143196 A TW 112143196A TW 112143196 A TW112143196 A TW 112143196A TW 202409225 A TW202409225 A TW 202409225A
- Authority
- TW
- Taiwan
- Prior art keywords
- polishing
- acid
- oxide particles
- silicon oxide
- sioc
- Prior art date
Abstract
〔課題〕提供一種相對於氮化矽的研磨速度，能夠以較高的研磨速度研磨碳氧化矽(SiOC)之研磨用組合物(亦即，碳氧化矽/氮化矽的研磨選擇比高)。
〔解決手段〕提供一種研磨用組合物，其包括金平糖狀的氧化矽粒子及分散媒，且pH為小於5。
Description
本發明是有關於一種研磨用組合物及使用此的研磨方法。
近年，隨著半導體基板表面的多層線路化，在製造裝置時，利用將半導體基板物理性地研磨而平坦化的所謂化學機械研磨(chemical mechanical polishing；CMP)技術。CMP是使用包括氧化矽(silica)或氧化鋁(alumina)、氧化鈰(ceria)等的研磨粒、防蝕劑、界面活性劑等的研磨用組合物(漿料)，將半導體基板等的研磨對象物(被研磨物)的表面平坦化的方法，具體而言，其使用於淺溝隔離(STI)、層間絕緣膜(ILD膜)的平坦化、鎢插塞形成、由銅與低介電常數膜等所構成的多層線路的形成等的步驟。在如此的CMP，在STI步驟等的情況中，要求將第一絕緣膜(例如，碳氧化矽(SiOC)膜)與第二絕緣膜(例如，氮化矽膜)以高研磨選擇比研磨去除(亦即，以比氮化矽膜更高的研磨速度將SiOC膜去除。
作為如上述的技術，日本專利申請公開第2006-203188號揭示藉由使用包括甲磺酸、鹼金屬離子、氧化劑與氧化矽研磨材的化學機械研磨組合物，可提升絕緣膜(氮化矽膜、SiOC膜等)的研磨速度。
但是，使用日本專利申請公開第2006-203188號所述的研磨用組合物，研磨包括氮化矽及摻碳的氧化矽(SiOC)的研磨對象物時，由於SiOC及氮化矽都被以高速度研磨，因此無法得到SiOC與氮化矽的高研磨選擇比。
本發明是有鑑於上述課題而完成的，其目的在於提供一種相對於氮化矽的研磨速度具有足夠高的SiOC的研磨速度(亦即，SiOC/氮化矽的選擇比高)的研磨用組合物。
本發明的發明人有鑑於上述課題而進行了深入研究。結果發現，藉由使用包括金平糖狀的氧化矽粒子及分散媒且pH為小於5的研磨用組合物，能夠解決上述課題，而完成了本發明。
以下，說明本發明。再者，本發明並非限定於以下的實施形態。
再者，在本說明書中，化合物的具體名稱中所記載的「(甲基)丙烯酸」表示「丙烯酸」及「甲基丙烯酸」，「(甲基)丙烯酸酯」表示「丙烯酸酯」及「甲基丙烯酸酯」；表示範圍的「X至Y」，意指「X以上且Y以下」；「ppm」、「%」及「份」，分別意指「質量百萬分率」、質量「%」及「質量份」。此外，除非另有說明，否則操作及物性等的測定是在室溫(20-25℃)/相對濕度40-50%RH的條件下測定。
本發明相關的研磨用組合物，除了包括SiOC與氮化矽的研磨對象物之外，期待對於其它研磨對象物也是有效的。例如，期待對於包括以TEOS作為原料而成膜的氧化矽膜等的研磨對象物也是有效的。在此，就發揮本發明的效果之觀點而言，本發明的一實施形態相關的研磨用組合物，以被使用於研磨包括SiOC與氮化矽的研磨對象物的步驟為佳。如此的研磨對象物，推測是藉由後述的作用機制，而變得具有高研磨選擇比。
本發明的發明人，推定藉由本發明而能夠解決上述課題的機制如下。惟，下述機制僅為推測，本發明的範圍並非限定於此。
本發明相關的研磨用組合物包括金平糖狀的氧化矽粒子及分散媒，且pH為小於5。當pH為小於5時，氮化矽(等電點為小於約5)及氧化矽粒子的表面帶正電，而SiOC的表面帶負電。因此，SiOC與氧化矽粒子相互吸引，從而提高SiOC的研磨速度，另一方面，氮化矽與氧化矽粒子相互排斥，從而降低氮化矽的研磨速度，結果，認為能夠實現相對於氮化矽的研磨速度具有足夠高的SiOC研磨速度的研磨。此外，本發明相關的研磨用組合物，氧化矽粒子的表面形狀為金平糖狀是必須的。在使用金平糖狀的氧化矽粒子的情況中，雖然其機制是未知的，但是與使用表面光滑的氧化矽粒子的情況相比，對於SiOC的研磨速度得到提升的同時，對於氮化矽的研磨速度並未大幅變化，因此，能夠實現SiOC/氮化矽的高選擇比。亦即，依據本發明，可提供一種相對於氮化矽的研磨速度具有足夠高的SiOC研磨速度(亦即，SiOC/氮化矽的選擇比高)的研磨用組合物。
(金平糖狀的氧化矽粒子)
在本說明書中，所謂的「金平糖狀的氧化矽粒子」，是指在粒子表面上具有多個突起的氧化矽粒子。另外，在下文中，「金平糖狀的氧化矽粒子」可以僅稱為「氧化矽粒子」。在一個或多個實施形態中，金平糖狀的氧化矽粒子，是以最小的二氧化矽粒子的粒徑為基準，粒徑相差5倍以上的兩個以上的粒子凝集或熔融接著而成的形狀。較佳是粒徑相差5倍以上的兩個以上的粒子之中的較小粒子部分地埋入較大粒子中的狀態。在使用如此的氧化矽粒子的情況中，與使用表面光滑的氧化矽粒子的情況相比，對於SiOC的研磨速度得到提升的同時，對於氮化矽的研磨速度並未大幅變化，因此，能夠實現SiOC/氮化矽的高選擇比。
在此，作為金平糖狀的氧化矽粒子，可列舉金平糖狀的膠態氧化矽(colloidal silica)粒子、金平糖狀的氣相氧化矽(fumed silica)粒子。就抑制研磨損傷的發生之觀點而言，以金平糖狀的膠態氧化矽粒子為佳。
(金平糖狀的氧化矽粒子的製造方法)
在表面上具有多個突起的氧化矽粒子，亦即，金平糖狀的氧化矽粒子，能夠藉由，例如，以下的方法製造。
首先，將烷氧基矽烷連續地加入添加了氨水作為觸媒之甲醇與水的混合溶液中，而進行水解，藉此得到含有膠態氧化矽粒子的漿料。加熱所得到的漿料以蒸餾除去甲醇及氨。之後，將有機鹼作為觸媒添加到漿料中，然後在70℃以上的溫度再次連續添加烷氧基矽烷，而進行水解，藉此在膠態氧化矽粒子的表面上形成多個突起。作為在此可使用的有機鹼的具體例，可列舉三乙醇胺等的胺化合物、氫氧化四甲銨等的四級銨化合物等。依據此方法，能夠容易地得到金屬雜質含量為1質量ppm以下的在表面具有多個突起的氧化矽粒子。此外，在下文中，此製造方法可稱為製造方法A。
再者，藉由烷氧基矽烷水解而製造膠態氧化矽的一般方法，例如，記載於作花濟夫著「溶膠凝膠法的科學」(Agne 承風社出版)的第154至156頁。此外，在日本專利申請公開的平11-60232號公報中，揭示一種製造方法，其將矽酸甲酯或矽酸甲酯與甲醇的混合物滴入由水、甲醇及氨或氨與銨鹽的混合溶劑中，使矽酸甲酯與水反應，藉以製造繭形膠態氧化矽。日本專利申請公開2001-48520號公報中，揭示一種製造方法，其利用酸觸媒將矽酸烷基酯水解後，加入鹼觸媒並加熱，使矽酸的聚合進行並使粒子成長，藉以製造細長型狀的膠態氧化矽。日本專利申請公開2007-153732號公報中，揭示一種製造方法，其以特定量使用特定種類的水解觸媒，並使用易水解的有機矽酸鹽作為原料，而製備具有大量小突起的膠態氧化矽。日本專利申請公開2002-338232號公報中，揭示一種二次凝集膠態氧化矽的製造方法，其添加凝集劑到單分散的膠態氧化矽中，藉使其二次凝集為球狀。在日本專利申請公開的平07-118008號公報及國際公開WO 2007/018069號公報中，揭示為了得到細長等的特異形狀之膠態氧化矽，將鈣鹽或鎂鹽添加到由矽酸鈉得到的活性矽酸中。日本專利申請公開2001-11433號公報中，揭示將鈣鹽添加到由矽酸鈉得到的活性矽酸中，藉此得到念珠狀的膠態氧化矽。日本專利申請公開2008-169102號公報中，揭示在種子顆粒的表面上使微小粒子生成及生長，藉此可得到如金平糖般的具有大量小突起之膠態氧化矽。本發明相關的金平糖狀的氧化矽粒子，也可藉由單獨或組合使用這些文獻中描述的方法而製造。
再者，金平糖狀的氧化矽粒子的各個突起的有無，能夠藉由掃描式電子顯微鏡加以確認。
金平糖狀的氧化矽粒子在表面上所具有的突起數，每一個粒子平均3個以上為佳，以5個以上為更佳。
在此所謂的突起，是指相較於金平糖狀的氧化矽粒子的粒徑具有足夠小的高度及寬度者。進一步而言，是指符合以下條件的突起，在第1圖中通過點A及點B的曲線AB所示的部分之長度，不超過金平糖狀的氧化矽粒子的最大內接圓的圓周長，更正確而言，不超過內接於金平糖狀的氧化矽粒子的外形所投影的輪廓之最大的圓之圓周長的四分之一。再者，突起的寬度，是指突起之基部的寬度，在第1圖中，是以點A與點B之間的距離所表示者。此外，突起的高度，是指突起的基部與最遠離該基部的突起的部分之間的距離，在第1圖中，是以垂直於直線AB的線段CD的長度所表示者。
將金平糖狀的氧化矽粒子在表面上所具有的突起的高度各自除以相同突起的基部的寬度而得到的值(突起的高度/突起的寬度)的平均，以0.170以上為佳，更佳為0.200以上，進一步更佳為0.220以上。隨著該值的平均增加，因為突起的形狀相對尖銳，研磨用組合物的研磨速度提高。金平糖狀的氧化矽粒子的各個突起的高度及其基部的寬度，可藉由使用一般的影像分析軟體，分析由掃描式電子顯微鏡所得之金平糖狀的氧化矽粒子的影像而求取。
金平糖狀的氧化矽粒子在表面上所具有的突起的平均高度，以3.5 nm以上為佳，更佳為4.0 nm以上，進一步更佳為5.0 nm以上。隨著突起的平均高度增加，研磨用組合物對SiOC的研磨速度提高。
金平糖狀的氧化矽粒子的平均一次粒徑的下限，以10 nm以上為佳，以15 nm以上為更佳，以20 nm以上為進一步更佳。此外，金平糖狀的氧化矽粒子的平均一次粒徑的上限，以200 nm以下為佳，以150 nm以下為更佳，以100 nm以下為進一步更佳。若為如此的範圍，則由研磨用組合物所造成的研磨對象物(SiOC)的研磨速度進一步提高，此外，能夠進一步抑制在使用研磨用組合物研磨之後的研磨對象物表面所產生的缺陷。再者，金平糖狀的氧化矽粒子的平均一次粒徑，例如，可基於藉由BET法測量的金平糖狀的氧化矽粒子的比表面積而計算求出。
金平糖狀的氧化矽粒子的平均二次粒徑的下限，以15 nm以上為佳，以20 nm以上為更佳，以30 nm以上為進一步更佳。此外，金平糖狀的氧化矽粒子的平均二次粒徑的上限，以300 nm以下為佳，以260 nm以下為更佳，以220 nm以下為進一步更佳，以150 nm以下為特佳，以100 nm以下為特佳。若為如此的範圍，則由研磨用組合物所造成的研磨對象物(SiOC)的研磨速度進一步提高，此外，能夠進一步抑制在使用研磨用組合物研磨之後的研磨對象物表面所產生的缺陷。再者，在此所謂的「二次粒子」，是指金平糖狀的氧化矽粒子在研磨用組合物中結合而形成的粒子，此二次粒子的平均粒徑(平均二次粒徑)，能夠藉由，例如，動態光散射法而測定。
在本發明相關的研磨用組合物中，金平糖狀的氧化矽粒子的含量(濃度)沒有特別限制，相對於該研磨用組合物之金平糖狀的氧化矽粒子的含量，以1質量%以上為佳，以2質量%以上為更佳，以3質量%以上為進一步更佳。藉由增加金平糖狀的氧化矽粒子的含量，SiOC的研磨速度有變得更高的傾向。再者，就防止刮痕等的觀點而言，金平糖狀的氧化矽粒子的含量，通常以20質量%以下為適當，以15質量%以下為佳，以10質量%以下為更佳。就經濟性的觀點而言，也是以減少金平糖狀的氧化矽粒子的含量為佳。
(陽離子改質氧化矽粒子)
在本發明中，亦可對金平糖狀的氧化矽粒子進行陽離子改質。其理由在於，當pH為小於5時，SiOC在其表面上帶負電，並且一般的氧化矽粒子在其表面上帶正電，因此SiOC與氧化矽粒子相互吸引，而使SiOC的研磨速度變高。另一方面，由於氮化矽帶正電，氮化矽與氧化矽粒子相互排斥，因此氮化矽的研磨速度變低。在此，本案發明人為了提高金平糖狀的氧化矽粒子與研磨對象物之間的吸引力或排斥力，使金平糖狀的氧化矽粒子的表面陽離子改質而導入正(+)電荷，而得到在pH為小於5的條件下界面(Zeta)電位之正的絕對值較大的陽離子改質氧化矽粒子。亦即，在本發明中，以使用(金平糖狀的)陽離子改質氧化矽粒子為佳。在此所謂的陽離子改質，是指陽離子性基團(例如，胺基或四級陽離子基團)鍵結到氧化矽粒子的表面的狀態。並且，根據本發明的較佳實施形態，陽離子改質氧化矽粒子是胺基改質氧化矽粒子。根據這樣的實施形態，能夠更加提高SiOC/氮化矽的高選擇比之效果。
在此，所謂的「Zeta (ζ)電位」，是指當彼此接觸的固體與液體之間進行相對運動時兩者的界面所產生的電位差。當pH為小於5時，由於氮化矽與氧化矽粒子同樣帶正電，若氮化矽與氧化矽粒子之間的ζ電位的絕對值的差增加，則氮化矽與氧化矽粒子之間的排斥力很強而研磨率變低。氮化矽與氧化矽粒子之間的ζ電位的絕對值的差，沒有特別限制，以1 mV以上為佳，以5 mV以上為更佳，以10 mV以上為進一步更佳。另一方面，由於SiOC帶負電，隨著SiOC與氧化矽粒子之間的ζ電位絕對值的差增加，SiOC與氧化矽粒子變得更容易接觸，並且研磨速度變高。SiOC與二氧化矽粒子間的ζ電位的絕對值的差，沒有特別限定，以10 mV以上為佳，以15 mV以上為更佳，以20 mV以上為進一步更佳。
在此，為了使金平糖狀的氧化矽粒子進行陽離子改質，可對金平糖狀的氧化矽粒子加入具有陽離子性基團的矽烷偶合劑，並在所需的溫度下使其反應所需的時間。
此時，所使用的矽烷偶合劑沒有特別限制，可列舉，例如，N-(β-胺基乙基)-γ-胺基丙基甲基二甲氧基矽烷、N-(β-胺基乙基)-γ-胺基丙基三甲氧基矽烷、N-(β-胺基乙基)-γ-胺基丙基三乙氧基矽烷、γ-胺基丙基三乙氧基矽烷((3-胺基丙基)三乙氧基矽烷)、γ-胺基丙基三甲氧基矽烷、γ-三乙氧基矽基-N-(α,γ-二甲基-亞丁基)丙胺、N-苯基-γ-胺基丙基三甲氧基矽烷、N-(乙烯基芐基)-β-胺基乙基-γ-胺基丙基三乙氧基矽烷的鹽酸鹽、十八烷基二甲基-(γ-三甲氧基矽基丙基)-銨氯化物等。其中，就與膠態氧化矽的反應性良好的觀點而言，可適宜地使用N-(β-胺基乙基)-γ-胺基丙基三甲氧基矽烷、N-(β-胺基乙基)-γ-胺基丙基三乙氧基矽烷、γ-胺基丙基三乙氧基矽烷、γ-胺基丙基三甲氧基矽烷。再者，在本發明中，矽烷偶合劑，可僅單獨使用一種，亦可以組合使用兩種以上。
矽烷偶合劑，可維持原樣或是使用親水性有機溶劑稀釋，而加入氧化矽粒子中。藉由使用親水性有機溶劑稀釋，可以抑制凝集物的形成。當使用親水性有機溶劑稀釋矽烷偶合劑時，每1質量份矽烷偶合劑(包含兩種以上的情況時，是指其合計量)，較佳為稀釋於5質量份以上且50質量份以下的親水性有機溶劑中，更佳為稀釋於10質量份以上且20質量份以下的親水性有機溶劑中。作為親水性有機溶劑，沒有特別限制，可例示甲醇、乙醇、異丙醇及丁醇等的低級醇。
此外，認為藉由調節氧化矽原料的pH與矽烷偶合劑的添加量能夠調節導入氧化矽粒子表面的陽離子性基團的量。矽烷偶合劑的使用量沒有特別限制，相對於氧化矽粒子，以0.01質量%以上且3.0質量%以下為佳，以0.05質量%以上且1.0質量%以下為更佳。
藉由矽烷偶合劑對氧化矽粒子進行陽離子改質時的處理溫度沒有特別限制，可以是從室溫(例如，25℃)到約為分散氧化矽粒子的分散媒的沸點的溫度。具體而言，可為0℃以上且100℃以下，較佳為室溫(例如25°C)以上且約90℃以下。
(pH)
本發明相關的研磨用組合物的pH為小於5。如上所述，當pH為小於5時，氮化矽及氧化矽粒子的表面帶正電，而SiOC的表面帶負電，因此SiOC與氧化矽粒子相互吸引而SiOC的研磨速度變高，另一方面，氮化矽與氧化矽粒子相互排斥而氮化矽的研磨速度變低，結果，認為能夠實現相對於氮化矽的研磨速度具有足夠高的SiOC研磨速度的研磨。在較佳的一實施形態中，研磨用組合物的pH為4.5以下，更佳為4以下，進一步更佳為3.8以下。
研磨用組合物的pH的下限沒有特別限制，就易於處理及提高SiOC研磨速度‧SiOC/SiN選擇性的觀點而言，以1以上為佳，以1.5以上為更佳，以2以上為進一步更佳，以2.5以上為特佳，以3以上為最佳。
例如，在較佳的實施形態中，研磨用組合物的pH為2以上且4以下。
為了調整本發明的研磨用組合物的pH，可使用pH調整劑。
作為pH調整劑，可使用已知的酸、鹼或鹽。
可使用作為pH調整劑的酸的具體例，可列舉，例如，鹽酸、硫酸、硝酸、氫氟酸、硼酸、碳酸、次磷酸、亞磷酸及磷酸等的無機酸，甲酸、乙酸、丙酸、丁酸、戊酸、2-甲基丁酸、正己酸、3,3-二甲基丁酸、2-乙基丁酸、4-甲基戊酸、正庚酸、2-甲基己酸、正辛酸、2-乙基己酸、苯甲酸、乙醇酸、水楊酸、甘油酸、草酸、丙二酸、丁二酸、戊二酸、己二酸、庚二酸、順丁烯二酸、鄰苯二甲酸、蘋果酸、葡萄糖酸、伊康酸、酒石酸、檸檬酸、乳酸、二乙醇酸、2-呋喃甲酸、2,5-呋喃二甲酸、3-呋喃甲酸、2-四氫呋喃甲酸、甲氧基乙酸、甲氧基苯乙酸及苯氧基乙酸等的有機酸。當使用無機酸作為pH調整劑時，就提高研磨速度的觀點而言，特別是以硫酸、硝酸、磷酸等為佳，當使用有機酸作為pH調整劑時，以乙醇酸、丁二酸、順丁烯二酸、檸檬酸、酒石酸、蘋果酸、葡萄糖酸及伊康酸等為佳。
可使用作為pH調整劑的鹼的具體例，可列舉，例如，脂肪族胺、芳香族胺等的胺類，氫氧化四級銨等的有機鹼，氫氧化鉀等的鹼金屬之氫氧化物，鹼土金屬的氫氧化物、氫氧化四甲基銨及氨等。其中，就容易取得的觀點而言，以氫氧化鉀或氨為佳。
這些pH調整劑可單獨或混合兩種以上而使用。
pH調整劑的添加量沒有特別限制，可適當選擇添加量，以使pH成為本發明的目標pH範圍。
(分散媒)
本發明的研磨用組合物，可使用分散媒以分散構成研磨用組合物的組分。作為分散媒，可列舉有機溶劑、水，其中，以含有水為佳。
就抑制研磨對象物的污染、抑制其他成分的作用等的觀點而言，以盡可能不含雜質的水為佳。具體而言，以去離子水、純水等為佳。如此的水可藉由，例如，用離子交換樹脂除去雜質離子後通過過濾器除去雜質而得到。
(研磨方法)
在本發明中亦提供一種研磨方法，包括使用上述研磨用組合物研磨研磨對象物表面的步驟。前述研磨對象物，以含有SiOC與氮化矽為佳。藉由如此的研磨方法，能夠相對於氮化矽選擇性地研磨SiOC。
作為研磨裝置，沒有特別限制，例如，可使用一般的研磨裝置，其安裝有保持具有研磨對象物的基板等之保持座、與能夠變更轉數的馬達等，而且具有能夠貼附研磨墊(研磨布)的研磨轉盤。
作為前述研磨墊，沒有特別限制而可使用一般的不織布、聚氨酯、及多孔質氟樹脂等。
研磨條件亦沒有特別限制，例如，研磨轉盤的旋轉速度，以10 rpm以上且200 rpm以下為佳，載體(研磨頭)的旋轉速度，以10 rpm以上且200 rpm以下為佳，對具有研磨對象物的基板施加之壓力(研磨壓力)，以0.5 psi以上且10 psi以下為佳。將研磨用組合物供給至研磨墊之方法亦沒有特別限制，例如，能夠採用泵浦等連續地供給之方法(澆注)。此供給量沒有限制，以使本發明的研磨用組合物經常覆蓋研磨墊的表面為佳。
(半導體基板的製造方法)
在本發明中亦提供一種半導體基板的製造方法，包括藉由上述研磨方法研磨研磨對象物的步驟。本發明的半導體基板的製造方法，由於具有上述研磨方法，因此能夠相對於氮化矽選擇性地研磨SiOC，並且能夠根據目的而製造半導體基板。
[實施例]
使用以下的實施例與比較例進一步詳細說明本發明。然而，本發明的技術範圍並非僅限於以下的實施例。
(研磨用組合物的調製)
(實施例1)
使用純水作為分散媒，準備含有20質量%膠態氧化矽(金平糖狀，藉由上述製造方法A所製造者；一次粒徑48.4 nm；二次粒徑63.1 nm；突起的平均高度5.66 nm，突起的高度/突出的寬度 = 0.25)的膠態氧化矽分散液。之後，以使最終研磨用組合物中的膠態氧化矽的含量成為3.2質量%、pH為2.7之方式，而使用硝酸及純水調製研磨用組合物。
(實施例2)
將pH調整為3.4，除此之外，以與實施例1相同的方法調製研磨用組合物。
(實施例3)
使用純水作為分散媒，準備含有20質量%膠態氧化矽(金平糖狀，與實施例1相同之物)的膠態氧化矽分散液。對1kg的前述膠態氧化矽分散液緩慢(約5秒滴1滴，1滴約0.03g)加入0.11g的(3-胺基丙基)三乙氧基矽烷(APTES)。在添加期間，用攪拌機以300至400 rpm的速度攪拌膠態氧化矽分散液。在APTES的添加結束後，在室溫(25℃)下繼續攪拌5小時。攪拌結束後，用水稀釋膠態氧化矽與ATPES的混合物，用硝酸將pH值調整為2.6。此外，以使最終研磨用組合物中的膠態氧化矽的含量成為3.2質量%、ATPES的含量成為17.6 ppm之方式，而調製研磨用組合物。
(實施例4至8)
將pH調整為表1所記載的各個數值，除此之外，以與實施例3相同的方法調製實施例4至8的研磨用組合物。
(比較例1)
將pH調整為5.0，除此之外，以與實施例1相同的方法調製比較例1的研磨用組合物。
(比較例2至7)
將pH調整為表1所記載的各個數值，除此之外，以與實施例3相同的方法調製比較例2至7的研磨用組合物。
(比較例8至12)
使用表面平滑的膠態氧化矽(一次粒徑32 nm；二次粒徑61 nm)作為氧化矽粒子，並將pH調整為表1所記載的各個數值，除此之外，以與實施例1相同的方法調製比較例8至12的研磨用組合物。
(比較例13至18)
使用表面平滑的膠態氧化矽(一次粒徑32 nm；二次粒徑61 nm)作為氧化矽粒子，並將pH調整為表1所記載的各個數值，除此之外，以與實施例3相同的方法調製比較例13至18的研磨用組合物。
(CMP步驟)
針對SiOC晶圓與氮化矽晶圓，使用各研磨用組合物並在以下的條件下進行研磨。在此，SiOC晶圓及氮化矽晶圓，是使用300 mm晶圓。之後，為了收集研磨速度的數據，將SiOC晶圓及氮化矽晶圓切割成3 cm × 3 cm的正方形。
(研磨條件)
研磨設備：日本Engis股份有限公司製，EJ-380IN-CH
研磨墊：DOW公司製，IC1010
研磨壓力：1.4 psi (1 psi = 6894.76 Pa，以下相同)
研磨墊旋轉速度：100 rpm
研磨用組合物的供給：澆注
研磨用組合物供給量：100 mL / min
研磨時間：60秒。
具體而言，按照以下流程進行研磨：
1. 使用去離子水(DIW)沖洗研磨墊
2. DIW持續流動，並開始使用鑽石修整器在100 rpm的旋轉速度下修整研磨墊20秒
3. 將研磨用組合物滴在研磨墊的中心30秒(研磨墊持續旋轉的期間)，以將研磨用組合物均勻地分散在研磨墊上
4. 將SiOC晶圓或氮化矽晶圓放置在晶圓載體上，並將載體設置在研磨墊上
5. 按下研磨裝置的開始按鈕，並將研磨墊加速到100 rpm的旋轉速度以進行研磨
6. 從研磨裝置中取出晶圓，使用DIW洗淨，並用乾燥空氣使其乾燥
(研磨選擇比的評價)
首先，針對研磨後的各個研磨對象物，使用以下的公式1求取研磨速度。評價結果顯示於表1。
[公式1]
此外，在實施例中，分別使用SiOC晶圓及氮化矽晶圓進行評價，但是推測當使用同時包含SiOC及氮化矽的晶圓(基板)等時，也可得到與上述相同的結果。
然後，求取SiOC晶圓及氮化矽晶圓的研磨選擇比。就解決本發明的課題的觀點而言，較佳為研磨選擇比(SiOC/SiN)為15以上。
表1
| 氧化矽粒子的表面形態 | 偶合劑 | pH 調整劑 | pH | 研磨速率 [Å/min] | 選擇比 | ||
| SiOC | SiN | SiOC/SiN | |||||
| 實施例1 | 金平糖 | － | 硝酸 | 2.7 | 1204 | 56 | 21.6 |
| 實施例2 | 金平糖 | － | 硝酸 | 3.4 | 1586 | 67 | 23.5 |
| 實施例3 | 金平糖 | APTES | 硝酸 | 2.6 | 781 | 37 | 21.2 |
| 實施例4 | 金平糖 | APTES | 硝酸 | 2.9 | 1191 | 39 | 30.4 |
| 實施例5 | 金平糖 | APTES | 硝酸 | 3.2 | 1602 | 39 | 40.9 |
| 實施例6 | 金平糖 | APTES | 硝酸 | 3.4 | 1905 | 39 | 48.4 |
| 實施例7 | 金平糖 | APTES | 硝酸 | 3.6 | 2135 | 45 | 47.9 |
| 實施例8 | 金平糖 | APTES | 硝酸 | 3.9 | 1837 | 92 | 19.9 |
| 比較例1 | 金平糖 | － | 硝酸 | 5.0 | 305 | 370 | 0.8 |
| 比較例2 | 金平糖 | APTES | 硝酸 | 5.2 | 282 | 276 | 1.0 |
| 比較例3 | 金平糖 | APTES | 硝酸 | 6.3 | 205 | 160 | 1.3 |
| 比較例4 | 金平糖 | APTES | 硝酸 | 7.2 | 133 | 36 | 3.7 |
| 比較例5 | 金平糖 | APTES | NH 4OH | 9.2 | 18 | 2 | 11.5 |
| 比較例6 | 金平糖 | APTES | NH 4OH | 10.1 | 62 | 11 | 5.5 |
| 比較例7 | 金平糖 | APTES | NH 4OH | 11.0 | 74 | 16 | 4.6 |
| 比較例8 | 平滑 | － | 硝酸 | 1.5 | 209 | 150 | 1.4 |
| 比較例9 | 平滑 | － | 硝酸 | 2.7 | 329 | 45 | 7.3 |
| 比較例10 | 平滑 | － | 硝酸 | 3.5 | 401 | 75 | 5.3 |
| 比較例11 | 平滑 | － | 硝酸 | 4.1 | 332 | 292 | 1.1 |
| 比較例12 | 平滑 | － | 硝酸 | 6.1 | 75 | 195 | 0.4 |
| 比較例13 | 平滑 | APTES | 醋酸 | 2.4 | 245 | 30 | 8.2 |
| 比較例14 | 平滑 | APTES | 醋酸 | 3.4 | 179 | 20 | 9.0 |
| 比較例15 | 平滑 | APTES | 醋酸 | 4.4 | 531 | 80 | 6.6 |
| 比較例16 | 平滑 | APTES | 醋酸 | 5.4 | 182 | 107 | 1.7 |
| 比較例17 | 平滑 | APTES | 醋酸 | 6.4 | 51 | 56 | 0.9 |
| 比較例18 | 平滑 | APTES | 醋酸 | 7.4 | 37 | 20 | 1.9 |
從表1的結果可知，使用本發明的研磨用組合物的實施例1至8中，相對於氮化矽的研磨速度之SiOC的研磨速度(SiOC/SiN選擇比)是足夠高的。其中，從實施例2及6的比較可知，當使用陽離子改質的金平糖狀的氧化矽粒子時，可以得到更優異的選擇性。另一方面，在pH為5以上的比較例1至7中，雖然使用金平糖狀的氧化矽粒子，但是SiOC/SiN選擇比低。此外，在比較例8至18中，因為沒有使用金平糖狀的氧化矽粒子，不論pH值如何，SiOC/SiN選擇比皆低。
無
第1圖是顯示在本發明的一實施形態中之金平糖狀的氧化矽粒子的圖。
Claims (5)
- 一種研磨用組合物，包括金平糖狀的氧化矽粒子及分散媒，且pH為小於5，前述研磨用組合物的碳氧化矽相對於氮化矽的研磨選擇比(SiOC/SiN)為15以上，並且用於研磨包括碳氧化矽與氮化矽的研磨對象物的步驟。
- 如請求項1所述之研磨用組合物，其中前述氧化矽粒子為陽離子改質氧化矽粒子。
- 如請求項2所述之研磨用組合物，其中前述陽離子改質氧化矽粒子是胺基改質氧化矽粒子。
- 如請求項1至3中任一項所述之研磨用組合物，其中pH為2以上且4以下。
- 如請求項1至3中任一項所述之研磨用組合物，其中pH為2.9以上且3.6以下。