TW202129762A - 絕緣膜之形成方法 - Google Patents

絕緣膜之形成方法 Download PDF

Info

Publication number
TW202129762A
TW202129762A TW109122864A TW109122864A TW202129762A TW 202129762 A TW202129762 A TW 202129762A TW 109122864 A TW109122864 A TW 109122864A TW 109122864 A TW109122864 A TW 109122864A TW 202129762 A TW202129762 A TW 202129762A
Authority
TW
Taiwan
Prior art keywords
gas
forming
insulating film
film
substrate
Prior art date
Application number
TW109122864A
Other languages
English (en)
Other versions
TWI840581B (zh
Inventor
松木信雄
Original Assignee
日商東京威力科創股份有限公司
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 日商東京威力科創股份有限公司 filed Critical 日商東京威力科創股份有限公司
Publication of TW202129762A publication Critical patent/TW202129762A/zh
Application granted granted Critical
Publication of TWI840581B publication Critical patent/TWI840581B/zh

Abstract

在基板上形成絕緣膜的絕緣膜之形成方法具有：使作為成膜氣體的以下述(1)式表示的有機矽化合物氣體和非氧化性之含氫氣體，在至少將上述非氧化性之含氫氣體電漿化的狀態下予以反應，朝基板上成膜流動性之矽烷醇複合物之步驟；和之後對上述基板進行退火而使上述矽烷醇複合物成為絕緣膜之步驟， Siα Oβ (O-Cm Hn )Γ Cx Hy ･･･(1) 但是，m、n、α為1以上的任意整數，β、Γ、x、y為0以上的任意整數，β和Γ不同時成為0。

Description

絕緣膜之形成方法
本揭示係關於絕緣膜之形成方法。
在半導體裝置之製造工程中，存在將包含矽和氧的絕緣膜埋入基板上之微細的立體構造的工程。對於如此包含矽和氧的絕緣膜之埋入，自以往雖然使用塗佈技術，但是作為可以取得更良好的膜質之技術，提案有將原料氣體導入至腔室內，在腔室內增大原料氣體的分子量，使持有液體般之流動性而予以成膜的流動性CVD。
作為如此之技術的例，在專利文獻1記載藉由自由基CVD在基板上生成流動性之聚矽氮烷而堆積聚矽氮烷膜之後，藉由將聚矽氮烷膜曝露於濕氣等的氧化處理，變換成氧化矽的技術。 [先前技術文獻] [專利文獻]
[專利文獻1]日本特表2014-512687號公報
[發明所欲解決之課題]
本揭示係提供在基板上藉由流動性CVD，可以形成充分氧化且高密度的絕緣膜的絕緣膜之形成方法。 [用以解決課題之手段]
本揭示之一態樣所涉及的絕緣膜之形成方法係一種在基板上形成絕緣膜的絕緣膜之形成方法具有：使作為成膜氣體的以下述(1)式表示的含氧矽化合物氣體和非氧化性之含氫氣體，在至少將上述非氧化性之含氫氣體電漿化的狀態下予以反應，朝基板上成膜流動性之矽烷醇複合物之步驟；和之後對上述基板進行退火而使上述矽烷醇複合物成為絕緣膜之步驟， Siα Oβ (O-Cm Hn )Γ Cx Hy ･･･(1) 但是，m、n、α為1以上的任意整數，β、Γ、x、y為0以上的任意整數，β和Γ不同時成為0。 [發明之效果]
若藉由本揭示時，係提供在基板上藉由流動性CVD，可以形成充分氧化且高密度的絕緣膜的絕緣膜之形成方法。
以下，參照附件圖面針對實施型態予以具體性說明。
＜原委＞ 首先，針對原委說明。 於對基板上之微細的立體構造埋入包含矽和氧的絕緣膜之時，使用塗佈技術之情況，需要以溶劑或穩定劑使塗佈材料持有流動性及穩定性地進行塗佈，於塗佈後成為膜之時，因去除溶劑等，使得膜質劣化。另一方面，因在流動性CVD中，於腔室內，生成流動性之中間體而朝微細的立體構造埋入絕緣膜，故能獲得較塗佈技術更良質的膜。
但是，在使用專利文獻1之技術作為流動性CVD的情況，以電漿聚合生成流動性之聚矽氮烷寡聚物，堆積聚矽氮烷膜之後，進行氧化處理之時，首先表面被氧化固化，有成為內部之氧化不充分的情形。另一方面，雖然也考慮以在包含O2 或H2 O之氛圍下對含矽材料進行電漿聚合，而不需要後氧化之情形，但是為了防止藉由縮聚反應而固化，流動性被妨礙之情形，需要大量的水分。因此，在退火固化之階段，膜所含的水分被除去，產生膜的密度下降。
進行用以解決如此之問題點之檢討的結果，得到使特定的構造式之含氧矽化合物氣體和非氧化性之含氫氣體在至少將含氫氣體電漿化的狀態下予以反應，朝基板上成膜流動性的矽烷醇複合物，之後，對基板進行退火，依此形成絕緣膜的方法。
再者，發現鋁系之絕緣膜或鈦系的絕緣膜也可以同樣藉由流動性CVD所致的成膜，和之後的退火而形成。
＜第1實施型態＞ 接著，針對第1實施型態予以說明。
[絕緣膜之形成方法] 圖1為表示第1實施型態所涉及之絕緣膜之形成方法的流程圖。 在本實施型態中，包含在腔室內設置基板的工程(步驟1)，和在腔室內使作為成膜氣體的含氧矽化合物氣體和非氧化性之含氫氣體在至少將含氫氣體電漿化之狀態下予以反應，而朝基板上成膜流動性之矽烷醇複合物的工程(步驟2)，和之後對基板進行退火而使矽烷醇複合物成為絕緣膜的工程(步驟3)。
在步驟1中，雖然基板不特別被限定，但是例示矽等之半導體基板(半導體晶圓)。作為基板，能使用在表面具有微細的立體構造者。微細的立體構造可以舉出形成有微細圖案的構造。微細圖案具有間隙。間隙即使為例如溝槽或孔般的凹部亦可。圖2為形成有溝槽或孔般的凹部101之構造的基板100的例。用以形成絕緣膜之底層並不特別被限定。
作為在步驟2被使用之成膜氣體的含氧矽化合物氣體以下述(1)式的構造式表示。 Siα Oβ (O-Cm Hn )Γ Cx Hy ･･･(1) 但是，m、n、α為1以上的任意整數，β、Γ、x、y為0以上的任意整數，β和Γ不同時成為0。
作為如此的化合物，可以舉出例如β為0且Γ為1以上的烷氧基矽烷系化合物(烷氧基矽烷系單體)。作為烷氧基矽烷系化合物可以使用以(R1)a Si(-O-R2 )4-a (但是，R1為-CH3 、-C2 H5 、-C3 H7 、-C2 H3 、及-C2 H中之任一者，R2為-CH3 或-C2 H5 ，a為0、1、2或3)表示者。具體而言，可以舉出四甲氧基矽烷(TMOS；Si(OCH3 )4 )、甲基三甲氧基矽烷(MTMOS；Si(OCH3 )3 CH3 )、四乙氧基矽烷(TEOS；Si(OC2 H5 )4 )、二甲基二甲氧基矽烷(DMDMOS；Si(OCH3 ))2 (CH3 )2 )、三乙氧基矽烷(SiH(OC2 H5 )3 )、三甲氧基矽烷(SiH(OCH3 )3 )、三甲氧基二矽氧烷(Si(OCH3 )3 OSi(OCH3 )3 )等。該些化合物即使單獨使用亦可，即使組合2種以上使用亦可。
作為成膜氣體，即使在上述般的含氧矽化合物氣體中添加其他氣體者亦可。作為第1添加氣體，可以舉出具有Si-CH3 般之Si-Cm Hn 鍵結的化合物，例如甲基三甲氧基矽烷。再者，作為第2添加氣體，可以舉出不含氧的構造式以Sis Nt Cu Hv 表示的矽化合物(s、v為1以上之任意整數，t、u為0以上之任意整數)。第1添加氣體係為了將 -CH3 基般之-Cm Hn 基(碳化氫基)導入至電漿處理後被形成的矽烷醇複合物而被添加。再者，第2添加物氣體係為了減少藉由步驟2所形成的矽烷醇複合物之O而被添加。第1添加氣體和第2添加氣體可以因應所需，添加其中之一方或雙方。
作為非氧化性之含氫氣體，可以舉出H2 氣體、NH3 氣體、SiH4 氣體，即使該些單獨亦可，即使組合2以上亦可。
在步驟2中，除了含氧矽化合物氣體、因應所需而添加的第1添加氣體及/或第2添加氣體，及非氧化性之含氫氣體之外，即使對腔室內供給He、Ne、Ar、Kr、N2 般的惰性氣體亦可。
在步驟2中，雖然生成電漿，實施流動性CVD，但是不特別限定於電漿生成手法，可以使用電容耦合電漿、感應耦合電漿、微波電漿等之各種手法。再者，若電漿係至少含氫氣體被電漿化即可。即是，即使將成膜氣體和含氫氣體之雙方電漿化亦可，即使僅將含氫氣體電漿化亦可。在僅將含氫氣體電漿化之情況，若將含氫氣體在腔室外電漿化，作為遠端電漿而導入至腔室內，將成膜氣體原樣地供給至腔室即可。
藉由如此之電漿所致的反應，流動性之矽烷醇複合物朝基板被成膜。矽烷醇複合物係指具有Si-OH基的含矽單體及寡聚物(多量體)。
即是，烷氧基矽烷化合物般之含氧矽化合物係藉由與含氫氣體的電漿(氫基(H* ))之反應，-CH3 或-O-CH3 等之碳化氫基或烷氧基成為例如CH4 或CH4 OH而脫離，成為矽烷醇複合物之單體(例如，原矽酸和甲基三醇)。再者，藉由與電漿的反應，作為成膜氣體而導入的含氧矽化合物之一部分聚合而成為聚矽烷醇寡聚物，並且碳化氫基或烷氧基也同樣從聚矽烷醇寡聚物脫離，而成為矽烷醇複合物之寡聚物。如此地被生成在基板上的矽烷醇複合物係在單體狀態下具有流動性，被埋入至凹部等之間隙。再者，寡聚物狀態的矽烷醇複合物也具有流動性，被埋入至間隙。最終，成為矽烷醇複合物之寡聚物被填充於間隙(凹部)之狀態。
將此時的反應例表示於圖3。在此，作為構成成膜氣體的矽化合物，使用TMOS、MTMOS的情況。TMOS係藉由反應而成為原矽酸，MTMOS係藉由反應而成為甲基三醇。
此時的根據矽烷醇複合物所致的流動性CVD的埋入成為例如圖4所示般。即是，如(a)般地含氧矽化合物反應成含氫氣體的電漿時，則如(b)般地生成液體狀且具有流動性的矽烷醇複合物102，矽烷醇複合物102藉由表面張力流入至凹部101。此時，分子量越大，再者越低溫越容易成為液體。而且，如(c)般地矽烷醇複合物102被填充於凹部101內。之後，如(d)般地實施平坦化程式而被平坦化。
從確保矽烷醇複合物之流動性的觀點來看，步驟2係在低溫下進行為佳，以250℃以下為佳。當超過250℃時，則有矽烷醇複合物之流動性變得不充分之情形。較佳為-10～100℃，更佳為-10～50℃。再者，步驟2之壓力以130～2600Pa程度為佳。
因步驟2之流動性CVD所致的成膜係埋入液體狀之流動性矽烷醇複合物，故即使在長寬比為10以上之間隙(凹部)也不會於內部形成空洞，可以取得良好的埋入性。
作為成膜矽烷醇複合物之後進行步驟3之退火而被形成的絕緣膜，如後述般，可以舉出SiO膜及SiOCH膜(或SiOC膜)。在形成SiO膜之情況，作為在步驟2中被成膜的矽烷醇複合物，以O和Si之比亦即O/Si為1≦O/Si≦4之範圍者為佳。再者，在形成SiOCH膜(或是SiOC膜)之情況，作為在步驟2中被成膜的矽烷醇複合物，以O和Si之比亦即O/Si為0.5≦O/Si≦4者為佳。
步驟3之退火係藉由加熱進行步驟2之後的基板，被生成在基板上，使被埋入至間隙(凹部)之矽烷醇複合物變化成矽系的絕緣膜。例如，如圖5所示般，藉由退火在矽烷醇複合物之寡聚物產生脫水縮合反應而形成Si-O-Si鍵結，形成具有Si和O之網路構造的玻璃狀之SiO膜，作為絕緣膜。
另一方面，在當作成膜氣體使用的含氧矽化合物存在Si-Cm Hn 鍵結之情況，例如含氧矽化合物為MTMOS的情況，殘存-Cm Hn 之一部分，所形成的絕緣膜成為在Si和O之網路中含C和H之SiOCH膜(或是，在Si和O之網路中含C的SiOC膜)。SiOCH膜(或SiOC膜)可以作為例如低介電常數膜(Low-k膜)使用。但是，亦可以使用於Low-k膜以外的用途。藉由在含氧矽化合物氣體添加上述般的具有Si-Cm Hn 鍵結的第1添加氣體，可以使絕緣膜中之Cm Hn 基濃度成為期望的濃度。
再者，藉由在含氧矽化合物氣體中添加上述般的不含氧的矽化合物亦即第2添加氣體而減少矽烷醇複合物之O，可以於退火時減少H2 O之脫離量，可以使退火時的體積減少的情形變少。再者，藉由適當地調整第2添加氣體的量，可以使退火時之反應成為僅有脫氫反應。
步驟3之退火係以在與進行步驟2之腔室不同的腔室進行為佳。再者，退火係以高於步驟2之溫度的溫度並且80℃以上進行為佳，以850℃以下為佳。再者，雖然退火之氛圍並不特別限定，但是以在非氧化性氛圍下進行為佳。在氧化氛圍下形成SiOCH膜之情況，有在接近於表面之部分，含C基有可能消滅。在此，非氧化性氛圍係指不使底層氧化的氣體氛圍，若為不使底層氧化的範圍時，即使含氧亦可。作為非氧化性氛圍，以例如Ar、He、N2 等之惰性氣體氛圍為佳。
步驟3之退火的理想條件取決於底層而有所不同。每個底層之理想條件如同下述。 (1)以圖案製作工程在阻劑或SOC(旋塗碳)上成膜之情況 在90～350℃中的非氧化性氛圍中進行退火。 (2)在包含以金屬或Ge等之耐熱性低的材料形成的構造的底層上成膜之情況 (i)組合實施在100～250℃的第1步驟，和在250～450℃的第2步驟而予以實施(兩步驟皆為在非氧化性氛圍的退火)。 (ii)組合在100～250℃的第1步驟，和在250～450℃的第2步驟而予以實施，此外將紫外線(UV)照射組入至兩個步驟之至少一方(兩步驟皆為在非氧化性氛圍的退火)。 (3)在進行不含耐熱性低之材料之構造的淺溝槽隔離(STI)之埋入的情況 (i)組合實施在100～400℃的第1步驟，和在650～850℃的第2步驟而予以實施(兩步驟皆為在非氧化性氛圍的退火)。 (ii)組合在100～400℃的第1步驟，和在650～850℃的第2步驟而予以實施，此外將紫外線(UV)組入至第1步驟(兩步驟皆為在非氧化性氛圍的退火)。
雖然退火使用專用的退火裝置而進行亦可，即使在步驟2中，在基板上生成矽烷醇複合物之後，在接著進行的工程含有加熱處理之情況，即使藉由其工程進行本實施型態之退火亦可。
若藉由本實施型態時，使含氧矽化合物氣體和非氧化性之含氫氣體，在至少將含氫氣體電漿化的狀態下予以反應，朝基板上生成流動性的矽烷醇複合物。因所生成的矽烷醇複合物含氧，故僅藉由退火，可以形成SiO膜或SiOCH膜(或SiOC膜)等之絕緣膜，不需要專利文獻1般的後氧化處理。因此，不會有如專利文獻1般在後氧化處理之時氧化不充分之虞。再者，在專利文獻1之技術中，欲取得SiOCH膜之情況，在後氧化處理之時，受到接近於聚合膜之表面的部分之含C基消滅等的損傷，有可能無法獲得期望的膜，但是在本實施型態之方法中，不會有如此的情形，可以獲得良好的SiOCH膜。
再者，在本實施型態中，根據非氧化性之含氫氣體的電漿所致的處理(例如，H2 電漿處理)可以使堆積物不含有不必要的H2 O的純粹液體狀的矽烷醇複合物堆積於基板上。因此，由於去除了H2 O所致的膜之體積變化小，並且可以將獲得的絕緣膜的密度維持較高。再者，因可以堆積不含水分的矽烷醇複合物，故能獲得反應的穩定性。
[成膜裝置] 接著，針對進行步驟2之流動性CVD所致的成膜之成膜裝置予以說明。 圖6為表示成膜裝置之一例的剖面圖。如圖6所示般，成膜裝置1具有腔室2。腔室2被接地。在腔室2內設置用以將基板S載置成水平的載置台3。載置台3為金屬製，在內部設置進行基板S之調溫的調溫器4。載置台3係經由腔室2被接地。
在腔室2之底部連接排氣管5，在該排氣管5連接具有腔室2內之壓力控制功能的排氣裝置6。在腔室2之側壁，形成基板S被搬運的搬運口7，搬運口7藉由閘閥8被開關。
在腔室2之上部以與載置台3對向之方式，設置有氣體噴淋頭9。氣體噴淋頭9在內部具有氣體室9a，在底部具有複數氣體吐出孔9b。氣體噴淋頭9和腔室2之頂壁之間被絕緣構件14絕緣。
在氣體噴淋頭9經由氣體流路10而連接有氣體供給部11。氣體供給部11供給成膜氣體亦即含氧矽化合物氣體及非氧化性的含氫氣體。作為成膜氣體，即使添加上述第1添加氣體及第2添加氣體之至少一方亦可。再者，即使供給惰性氣體作為載體氣體、稀釋氣體、電漿生成氣體等亦可。該些氣體係從氣體供給部11經由氣體流路10而到達至氣體噴淋頭9之氣體室9a，經由氣體吐出孔9b而被吐出至腔室2內。
在氣體噴淋頭9經由匹配器12而連接高頻電源13。高頻電源13係對氣體噴淋頭9施加例如13.56MHz之高頻電力。藉由高頻電力被施加至氣體噴淋頭9，在氣體噴淋頭9和載置台3之間形成高頻電場，生成從氣體噴淋頭9被吐出之氣體所致的電容耦合電漿。
在如此的成膜裝置1中，在載置台3上載置基板S，藉由調溫器4將基板S之溫度控制成250℃以下，例如-10～100℃，將壓力控制成130～2600Pa。從氣體供給部11經由氣體噴淋頭9對腔室2內供給含氧矽化合物氣體和非氧化性之含氫氣體，並且從高頻電源13對氣體噴淋頭供給高頻電力。依此，生成含氧矽化合物及含氫氣體之電漿，藉由該些反應，朝基板S上成膜流動性的矽烷醇複合物，在被形成在基板S之間隙(凹部)埋入矽烷醇複合物。
另外，作為進行退火處理的退火裝置，例示具有例如腔室、被設置在腔室的載置台、加熱基板的加熱機構、對腔室內供給氣體的氣體供給機構，和將腔室內予以排氣的排氣機構的裝置。
[實驗例] 接著，針對實驗例予以說明。 (實施例1) 在此，使用圖6所示之構造的成膜裝置，使用TEOS作為含氧矽化合物，使用H2 作為含氫氣體，使用Ar氣體作為惰性氣體，藉由流動性CVD，對具有長寬比6.5之溝槽構造的基板進行矽烷醇複合物的成膜。膜厚為212.8nm。
此時的條件設為下述般。 載置台溫度：30℃ 壓力：4Torr(533Pa) TEOS氣體流量：30sccm H2 氣體流量：50sccm Ar氣體流量：50sccm 高頻電源 頻率：13.56MHz 功率：300W 處理時間：100sec
針對如此成膜的膜，在Ar氛圍進行200℃的退火。其結果，膜厚減少至210.0nm，膜厚減少率為1.3%。如此地退火所致的膜厚減少變少之結果，在狹窄的溝槽構造內形成無空乏的高密度的膜。在圖7示意性地表示剛成膜後和退火後之狀態。
為了比較，除了將H2 氣體變更成O2 氣體(50 sccm)之外，其他完全相同，藉由流動性CVD，同樣對具有長寬比6.5之溝槽構造的基板進行成膜。膜厚為190.1 nm。
針對如此成膜的膜，在Ar氛圍進行200℃的退火。其結果，膜厚減少至155.3nm，膜厚減少率為18 %。如此地藉由退火使得膜厚大幅度減少之結果，在狹窄的溝槽構造內，藉由膜收縮，形成密度低的多孔質構造的膜。在圖8示意性地表示剛成膜後和退火後之狀態。
(實施例2) 接著，使用以生成電漿的氣體予以變化而藉由流動性CVD進行成膜，確認在室溫放置2小時之後的膜之收縮。 在此，使用MTMOS作為含氧矽化合物，作為生成電漿之時的氣體，使用H2 氣體(狀況1)、O2 氣體(狀況2)、H2 O氣體(狀況3)、H2 O氣體+NH3 氣體(狀況4)之4種類的氣體，進行流動性CVD所致的成膜。在狀況1中，將H2 氣體流量設為50sccm，在狀況2中，將O2 氣體流量設為5sccm，在狀況3中，將H2 O氣體流量設為20sccm，在狀況4中，將H2 O氣體流量及NH3 氣體流量各設為20sccm及5sccm。其他條件除了將高頻功率設為50W之外，其他與實驗例1相同。
表1表示各狀況之剛成膜後的膜厚，在室溫放置2小時之後的膜厚，及收縮率。如表1所示般，依據本實施型態，使用非氧化性之含氫氣體亦即H2 氣體的狀況1中，收縮率為極小的1.2%。對此，在使用含氫氣體進行電漿處理的狀況2～4中，收縮率成為11～40%之較大的值。此被認為係在狀況2～4中，於成膜之時生成水分，在室溫放置後水分被釋放之故。在狀況1中，因幾乎不生成水分，故膜收縮非常小，認為退火後也成為高密度的膜。
Figure 02_image001
＜第2實施型態＞ 接著，針對第2實施型態予以說明。 在本實施型態中，形成鋁系之絕緣膜作為絕緣膜。
圖9為表示第2實施型態所涉及之絕緣膜之形成方法的流程圖。 在本實施型態中，在腔室內設置基板的工程(步驟11)，在腔室內，使作為成膜氣體的含鋁氣體和含氫氣體在將至少含氫氣體電漿化的狀態下予以反應，朝基板上成膜包含流動性之氧的鋁化合物的工程(步驟12)，和之後對基板進行退火而使含氧的鋁化合物成為絕緣膜的工程(步驟13)。
在步驟11中，可以使用與第1實施型態之步驟1相同的基板。
在步驟12中，作為成膜氣體使用的含鋁氣體，可以使用藉由以下述(2)式之構造式表示的鋁化合物。 Alα Oβ (O-Cm Hn )Γ Cx Hy ･･･(2) 但是，m、n、α為1以上的任意整數，β、Γ、x、y為0以上的任意整數。
作為如此的化合物，可以舉出β為0且Γ為1以上的烷氧化鋁系化合物，例如三甲氧基鋁(Al(OH3 )3 )、異丙醇鋁(Al(O-i-Pr)3 )、β及Γ為0的三甲基鋁(TMA；Al(CH3 )3 )。該些化合物即使單獨使用亦可，即使組合2種以上使用亦可。
再者，作為成膜氣體亦即含鋁氣體，其他即使使用AlCl3 NH3 、(NH4 )3 AlF6 、Al(i-Bu)3 (但是，Bu為丁基)亦可。
在作為成膜氣體使用的含鋁氣體含氧之情況，即使添加不含氧的鋁化合物作為添加氣體亦可。作為如此的添加氣體，可以舉出例如TMA、AlCl3 NH3 、(NH4 )3 AlF6 、Al(i-Bu)3 。如此的添加氣體係為了減少藉由步驟12被形成的鋁化合物之O而被添加。
作為含氫氣體，在作為成膜氣體使用的含鋁氣體中含O之情況，與第1實施型態相同，可以舉出H2 氣體、NH3 氣體、SiH4 氣體，即使該些單獨亦可，即使組合2以上亦可。在含鋁氣體不含O之情況，使用含O之氣體作為含氫氣體。例如，使用對H2 氣體、NH3 氣體及SiH4 氣體中之任一個以上，添加O2 氣體、NO、N2 O、CO2 及H2 O等之含氧氣體中之任一個以上的氣體。
在步驟12中，除了含鋁氣體，因應所需被添加的添加氣體及含氫氣體之外，即使對腔室內供給He、Ne、Ar、Kr、N2 般之惰性氣體亦可。
在步驟12中，雖然生成電漿，實施流動性CVD，但是與第1實施型態相同，不特別限定於電漿生成手段，可以使用電容耦合電漿、感應耦合電漿、微波電漿等之各種手法。再者，若電漿係至少含氫氣體被電漿化即可，即使將成膜氣體和含氫氣體之雙方電漿化亦可，即使僅將含氫氣體電漿化亦可。
藉由如此之電漿所致的反應，包含流動性之氧的鋁化合物被成膜在基板上。含氧的鋁化合物係例如具有Al-OH基的含鋁單體及寡聚物(多量體)。
此時，含鋁氣體與含氫氣體之電漿反應而成為流動性之含氧的鋁化合物。被成膜的含氧的鋁化合物在單體狀態下具有流動性，被埋入至凹部等之間隙。再者，藉由電漿所致的反應，鋁化合物成為具有流動性之寡聚物狀態的鋁化合物，被埋入至間隙。最終，成為含氧的鋁化合物之寡聚物被填充於間隙(凹部)之狀態。
此時，根據含氧的鋁化合物所致的流動性CVD的埋入，與第1實施型態相同，例如圖4所示般地被進行。
從確保被成膜之含氧的鋁化合物之流動性的觀點來看，步驟12係在低溫下進行為佳，以250℃以下為佳。較佳為-10～100℃，更佳為-10～50℃。再者，步驟12之壓力以130～2600Pa程度為佳。
因步驟12之流動性CVD所致的成膜係埋入液體狀且流動性的鋁化合物，故即使在長寬比為10以上之間隙(凹部)也不會於內部形成空洞，可以取得良好的埋入性。
步驟13之退火係藉由加熱進行步驟12之後的基板，被生成在基板上，使被埋入至間隙(凹部)之含氧的鋁化合物變化成鋁系的絕緣膜。例如，藉由退火在鋁化合物之寡聚物產生脫水縮合反應而形成AlO膜。
再者，藉由添加上述般的不含氧的鋁化合物作為添加氣體而減少所成膜之含氧的鋁化合物之O，可以於退火時減少H2 O之脫離量，可以使退火時的體積減少的情形變少。再者，藉由適當地調整添加氣體的量，可以使退火時之反應成為僅有脫氫反應。
步驟13之退火與第1實施型態之步驟3相同，以在與進行步驟12之腔室不同的腔室進行為佳。溫度係以高於步驟12之溫度的溫度並且80℃以上進行為佳，以850℃以下為佳。
在本實施型態中，使含鋁氣體和含氫氣體，在至少將含氫氣體電漿化的狀態下予以反應，朝基板上生成流動性之氧的鋁化合物。因所生成的鋁化合物含氧，故可以僅以退火形成AlO膜，不需要後氧化處理。再者，可以極力地減少H2 O之介入，縮小除去H2 O所致的膜的體積變化，可以將所獲得的絕緣膜之密度維持較高。
作為進行在步驟12中使用的流動性CVD的成膜裝置，可以使用在第1實施型態說明的圖6所示的裝置。
＜第3實施型態＞ 接著，針對第3實施型態予以說明。 在本實施型態中，形成鈦系之絕緣膜作為絕緣膜。
圖10為表示第3實施型態所涉及之絕緣膜之形成方法的流程圖。 在本實施型態中，在腔室內設置基板的工程(步驟21)，在腔室內，使作為成膜氣體的含鈦氣體和含氫氣體在將至少含氫氣體電漿化的狀態下予以反應，朝基板上成膜流動性之含氧的鈦化合物的工程(步驟22)，和之後對基板進行退火而使含氧的鈦化合物成為絕緣膜的工程(步驟23)。
在步驟21中，可以使用與第1實施型態之步驟1相同的基板。
在步驟22中，作為成膜氣體使用的含鈦氣體，可以使用藉由以下述(3)式之構造式表示的鈦化合物。 Ti(O-Cm Hn )α Cx Hy ･･･(3) 但是，m、n為1以上的任意整數，α、x、y為0以上的任意整數。
作為如此的化合物，可以舉出例如鈦酸四異丙酯(Ti(OCH(CH3 )2 )4 )、Ti(MeCp)(OMe)3 、Ti(Me5 Cp)(OMe)3 般之烷氧化鈦系化合物(但是，Me為甲基，Cp為環戊二烯基)。
再者，作為成膜氣體亦即含鈦氣體，即使其他使用四二甲基氨基鈦(TDMAT；Ti(N(CH3 )2 )4 )、TiCp(NMe2 )3 、TiMe5 Cp(NMe2 )3 ，或是四氯化鈦(TiCl4 )亦可。
在作為成膜氣體使用的含鈦氣體含氧之情況，即使添加不含氧的鈦化合物作為添加氣體亦可。作為如此的添加氣體，可以舉出例如TDMAT、TiCp(NMe2 )3 、TiMe5 Cp(NMe2 )3 、TiCl4 ，如此的添加氣體係為了減少藉由步驟22被形成的鈦化合物之O而被添加。
作為含氫氣體，在含鈦氣體中含O之情況，與第1實施型態相同，可以舉出H2 氣體、NH3 氣體、SiH4 氣體，即使該些單獨亦可，即使組合2以上亦可。在含鈦氣體不含O之情況，使用含O之氣體作為含氫氣體。例如，使用對H2 氣體、NH3 氣體及SiH4 氣體之至少一種，添加O2 氣體、NO、N2 O、CO2 及H2 O等之含氧氣體中之至少一種的氣體。
在步驟22中，除了含鈦氣體的成膜氣體及含氫氣體之外，即使對腔室內供給He、Ne、Ar、Kr、N2 般之惰性氣體亦可。
在步驟22中，雖然生成電漿，實施流動性CVD，但是與第1實施型態相同，不特別限定於電漿生成手段，可以使用電容耦合電漿、感應耦合電漿、微波電漿等之各種手法。再者，若電漿係至少含氫氣體被電漿化即可，即使將成膜氣體和含氫氣體之雙方電漿化亦可，即使僅將含氫氣體電漿化亦可。
藉由如此之電漿所致的反應，包含流動性之氧的鈦化合物被成膜在基板上。含氧的鈦化合物係例如具有例如Ti-OH基的含鈦單體及寡聚物(多量體)。
此時，含鈦氣體與含氫氣體之電漿反應而成為流動性之含氧的鈦化合物。含氧的鈦化合物在單體狀態下具有流動性，被埋入至凹部等之間隙。再者，藉由電漿所致的反應，鈦化合物成為具有流動性之寡聚物狀態的鈦化合物，被埋入至間隙。最終，成為含氧的鈦化合物之寡聚物被填充於間隙(凹部)之狀態。
此時，根據含氧之鈦化合物所致的流動性CVD的埋入，與第1實施型態相同，例如圖4所示般地被進行。
從確保被成膜之含氧的鈦化合物之流動性的觀點來看，步驟22係在低溫下進行為佳，以250℃以下為佳。較佳為-10～100℃，更佳為-10～50℃。再者，步驟22之壓力以130～2600Pa程度為佳。
因步驟22之流動性CVD所致的成膜係埋入液體狀之流動性的鈦化合物，故即使在長寬比為10以上之間隙(凹部)也不會於內部形成空洞，可以取得良好的埋入性。
步驟23之退火係藉由加熱進行步驟22之後的基板，被生成在基板上，使被埋入至間隙(凹部)之含氧的鈦化合物變化成鈦系的絕緣膜。例如，藉由退火在鈦化合物之寡聚物產生脫水縮合反應而形成TiO膜。
再者，藉由添加上述般的不含氧的鈦化合物作為添加氣體而減少含氧的鈦化合物之O，可以於退火時減少H2 O之脫離量，可以使退火時的體積減少的情形變少。再者，藉由適當地調整添加氣體的量，可以使退火時之反應成為僅有脫氫反應。
步驟23之退火與第1實施型態之步驟3相同，以在與進行步驟22之腔室不同的腔室進行為佳。溫度係以高於步驟22之溫度的溫度並且80℃以上進行為佳，以850℃以下為佳。再者，退火之氛圍並不特別限定，即使在非氧化性氛圍亦可，即使在氧化氛圍亦可。
在本實施型態中，使含鈦氣體和含氫氣體，在至少將含氫氣體電漿化的狀態下予以反應，朝基板上生成流動性之氧的鈦化合物。因所生成的鈦化合物含氧，故可以僅以退火形成TiO膜，不需要後氧化處理。再者，可以極力地減少H2 O之介入，縮小H2 O消除所致的膜的體積變化，可以將所獲得的絕緣膜之密度維持較高。
作為進行在步驟22中使用的流動性CVD的成膜裝置，可以使用在第1實施型態說明的圖6所示的裝置。
＜其他適用＞ 以上，雖然針對實施型態予以說明，但是此次揭示的實施型態所有方面都應視為例示而非限制性。即使上述實施型態不脫離附件的申請專利範圍及其要旨，以各種型態進行省略、置換、變更亦可。
例如，在上述實施型態具體性記載的成膜氣體只不為例示，可以使用滿足條件之其他氣體。再者，成膜裝置也只不過係例示，可以適用能進行電漿處理之各種構造的成膜裝置。並且，作為基板，雖然例示矽等之半導體基板(半導體晶圓)，但是不限定於此，可以使用其他各種基板。
1:成膜裝置 100:基板 101:凹部 102:矽烷醇複合物
[圖1]為表示第1實施型態所涉及之絕緣膜之形成方法的流程圖。 [圖2]為表示在表面具有微細的立體構造的基板之例的剖面圖。 [圖3]為表示成膜矽烷醇複合物之時之反應例的圖。 [圖4]為用以說明根據矽烷醇複合物所致的流動性CVD的埋入流程的圖。 [圖5]為表示對矽烷醇複合物進行退火之時之反應例的圖。 [圖6]為表示進行流動性CVD之成膜裝置之一例的剖面圖。 [圖7]為實驗例1中，依據第1實施型態，對具有溝槽構造的基板進行矽烷醇複合物之成膜之時之狀態和退火後之狀態的示意圖。 [圖8]為實驗例1中，為了進行比較，使用O2 氣體取代H2 氣體，對具有溝槽構造的基板進行矽烷醇複合物之成膜之時之狀態和退火後之狀態的示意圖。 [圖9]為表示第2實施型態所涉及之絕緣膜之形成方法的流程圖。 [圖10]為表示第3實施型態所涉及之絕緣膜之形成方法的流程圖。

Claims (17)

  1. 一種絕緣膜之形成方法，係在基板上形成絕緣膜的絕緣膜之形成方法，其特徵在於，具有：  　　使作為成膜氣體的以下述(1)式表示的含氧矽化合物氣體和非氧化性之含氫氣體，在至少將上述非氧化性之含氫氣體電漿化的狀態下予以反應，朝基板上成膜流動性之矽烷醇複合物之步驟，和 之後對上述基板進行退火而使上述矽烷醇複合物成為絕緣膜之步驟， Siα Oβ (O-Cm Hn )Γ Cx Hy ･･･(1) 但是，m、n、α為1以上的任意整數，β、Γ、x、y為0以上的任意整數，β和Γ不同時成為0。
  2. 如請求項1之絕緣膜之形成方法，其中 上述含氧矽化合物氣體為烷氧基矽烷系化合物氣體。
  3. 如請求項2之絕緣膜之形成方法，其中 上述烷氧基矽烷系化合物氣體係從四甲氧基矽烷、甲基三甲氧基矽烷、四乙氧基矽烷、二甲基二甲氧基矽烷、三乙氧基矽烷、三甲氧基矽烷、三甲氧基二矽氧烷被選擇出的至少一種。
  4. 如請求項1至3中之任一項之絕緣膜之形成方法，其中 作為成膜氣體，被添加具有Si-Cm Hn 鍵結之化合物的第1添加氣體。
  5. 如請求項1至4中之任一項之絕緣膜之形成方法，其中 作為成膜氣體，被添加構造式以Sis Nt Cu Hv 表示的矽化合物(但是，s、v為1以上之任意整數，t、u為0以上之任意整數)亦即第2添加氣體。
  6. 如請求項1至5中之任一項之絕緣膜之形成方法，其中 上述非氧化性之含氫氣體係從H2 氣體、NH3 氣體、SiH4 氣體被選擇出的至少一種。
  7. 如請求項1至6中之任一項之絕緣膜之形成方法，其中 上述矽烷醇複合物之成膜係使基板溫度成為250℃以下而進行。
  8. 如請求項7之絕緣膜之形成方法，其中 上述矽烷醇複合物之成膜係使基板溫度成為-10～100℃而進行。
  9. 一種絕緣膜之形成方法，係在基板上形成絕緣膜的絕緣膜之形成方法，其特徵在於，具有： 將作為成膜氣體的以下述(2)式表示的由鋁化合物、AlCl3 NH3 、(NH4 )3 AlF6 、Al(i-Bu)3 中之任一者構成的含鋁氣體和含氫氣體，在至少將上述含氫氣體電漿化的狀態下予以反應，朝基板上成膜流動性之含氧的鋁化合物之步驟，和 之後對上述基板進行退火而使上述含氧的鋁化合物成為絕緣膜之步驟， Alα Oβ (O-Cm Hn )Γ Cx Hy ･･･(2) 但是，m、n、α為1以上的任意整數，β、Γ、x、y為0以上的任意整數。
  10. 如請求項9之絕緣膜之形成方法，其中 上述(2)式之鋁化合物氣體係從三甲氧基鋁、異丙醇鋁、三甲基鋁被選擇出的至少一種。
  11. 如請求項9或10之絕緣膜之形成方法，其中 作為添加氣體，被添加三甲基鋁、AlCl3 NH3 、(NH4 )3 AlF6 、Al(i-Bu)3 之至少一種。
  12. 一種絕緣膜之形成方法，係在基板上形成絕緣膜的絕緣膜之形成方法，其特徵在於，具有： 將作為成膜氣體的以下述(3)式表示的由鈦化合物、四二甲基氨基鈦、TiCp(NMe2 )3 、TiMe5 Cp(NMe2 )3 、四氯化鈦中之任一者構成的含鈦氣體和含氫氣體，在至少將上述含氫氣體電漿化的狀態下予以反應，朝基板上成膜流動性之含氧的鈦化合物之步驟，和 之後對上述基板進行退火而使上述含氧的鈦化合物成為絕緣膜之步驟， Ti(O-Cm Hn )α Cx Hy ･･･(3) 但是，m、n為1以上的任意整數，α、x、y為0以上的任意整數。
  13. 如請求項12之絕緣膜之形成方法，其中 上述(3)式之鈦化合物係鈦酸四異丙酯、Ti(MeCp)(OMe)3 、Ti(Me5 Cp)(OMe)3 中之任一者。
  14. 如請求項12或13之絕緣膜之形成方法，其中 作為添加氣體，被添加四二甲基氨基鈦、TiCp(NMe2 )3 、TiMe5 Cp(NMe2 )3 、四氯化鈦之至少一種。
  15. 如請求項9至14中之任一項之絕緣膜之形成方法，其中 上述含氫氣體係從H2 氣體、NH3 氣體、SiH4 氣體被選擇出的至少一種，或對該些的至少一種，進一步添加O2 氣體、NO、N2 O、CO2 及H2 O等之含氧氣體的至少一種。
  16. 如請求項1至15中之任一項之絕緣膜之形成方法，其中 於上述退火之時的溫度係較上述成膜之時的溫度高溫，並且在80℃以上、850℃以下之溫度被進行。
  17. 如請求項1至16中之任一項之絕緣膜之形成方法，其中 上述退火係在非氧化性氛圍下被進行。
TW109122864A 2019-07-18 2020-07-07 絕緣膜之形成方法 TWI840581B (zh)