TW202124146A - 偏光板及使用該偏光板的圖像顯示裝置 - Google Patents
偏光板及使用該偏光板的圖像顯示裝置 Download PDFInfo
- Publication number
- TW202124146A TW202124146A TW109138637A TW109138637A TW202124146A TW 202124146 A TW202124146 A TW 202124146A TW 109138637 A TW109138637 A TW 109138637A TW 109138637 A TW109138637 A TW 109138637A TW 202124146 A TW202124146 A TW 202124146A
- Authority
- TW
- Taiwan
- Prior art keywords
- urea
- polarizing plate
- moisture content
- temperature
- relative humidity
- Prior art date
Abstract
本發明之目的在於提供一種偏光板,係即使在用於層間填充結構的圖像顯示裝置的情況,也會抑制高溫環境下之穿透率的降低。本發明提供一種具有碘吸附定向於聚乙烯醇系樹脂層所成的偏光元件及透明保護膜的偏光板,其中,該偏光板具有含尿素系化合物層,該含尿素系化合物層包含選自尿素、尿素衍生物、硫脲及硫脲衍生物所組成群組中的至少一種尿素系化合物;前述偏光元件的含水率係在溫度20℃、相對濕度30%的平衡含水率以上,而且在溫度20℃、相對濕度50%的平衡含水率以下。
Description
本發明係關於偏光板。再者,本發明關於一種圖像顯示裝置,其係該偏光板的一面與圖像顯示單元貼合,而另一面與觸控面板、前面板等透明構件貼合而成者。
液晶顯示裝置(LCD)不僅被使用於液晶電視,還廣泛使用於於個人電腦、行動電話等可攜裝置、汽車導航等車載用途等。通常來說,液晶顯示裝置係具有在液晶單元的兩側用黏著劑貼合有偏光板之液晶面板構件,並藉由以液晶面板構件調控源自背光構件的光而進行顯示。而且,近年來有機EL顯示裝置也與液晶顯示裝置同樣地被廣泛地用於電視、行動電話等可攜裝置、汽車導航等車載用途。於有機EL顯示裝置,為了抑制外部光被金屬電極(陰極)反射而如鏡面地被視認,係有在圖像顯示面板的視認側表面配置圓偏光板(包含偏光元件與λ/4板的積層體)的情形。
如上所述,偏光板作為液晶顯示裝置、有機EL顯示裝置的構件而裝載在車上的機會有所增加。與車用以外的電視、行動電話等可攜用途相比,使用於車用圖像顯示裝置之偏光板暴露在高溫環境下之情形較多,而要求
更高溫的特性變化小(高溫耐久性)。
另一方面,以防止來自外表面的衝擊所致之圖像顯示面板的破損等為目的,而在圖像顯示面板的較偏光板更靠近視認側予以設置透明樹脂板、玻璃板等前面板(亦稱為「窗層(window layer)」)的結構係有所增加。而且,於具備觸控面板的圖像顯示裝置中,係廣泛採用在較圖像顯示面板的偏光板更靠近視認側設置觸控面板,而在較觸控面板更靠近視認側具備前面板的結構。
於如此的結構中,當於圖像顯示面板與前面板和觸控面板等透明構件之間存在空氣層時,在空氣層界面的光的反射致使產生外部光的鏡面反射,畫面的視認性有降低的傾向。因此,開始廣為採用將配置於圖像顯示面板的視認側表面的偏光板與透明構件之間的空間以空氣層以外的層(以下有稱為「層間填充劑」的情況)來進行填充的結構(以下有稱為「層間填充結構」的情況),較佳為採用以折射率與該等材料接近的材料來進行填充的結構。作為層間填充劑,係能夠以在抑制因界面的反射造成的視認性的降低,同時將各構件之間進行接著固定為目的,而使用黏著劑、UV硬化型接著劑(例如參照專利文獻1)。
上述層間填充結構,被廣泛地採用於常在戶外使用的行動電話等可攜用途。而且,因於近年來對於視認性的要求提高,因此即使是導航裝置等的車載用途方面,也檢討採用在圖像顯示面板表面配置前面板,並在圖像顯示面板與前面板之間填充黏著劑層等的層間填充結構。
但是,就採用如此的結構的情況而言,有報告為加熱耐久測試(95℃、200小時等)的結果係觀察到在偏光板面內中央部穿透率顯著地降低,另一方面,偏光板即使單獨在95℃下1000小時,也未觀察到穿透率顯著地降低;還
有報告為依據該等結果,於高溫環境偏光板的穿透率顯著地降低,係採用「偏光板的一面與圖像顯示單元貼合,而另一面與觸控面板、前面板等透明構件貼合的層間填充結構」的圖像顯示裝置在暴露於高溫環境的情況下所特有的問題(專利文獻2)。
而且,於上述專利文獻2中為層間填充結構且穿透率顯著地降低的偏光板當以拉曼光譜測定時,因為係在1100cm-1附近(源自=C-C=鍵)以及1500cm-1附近(源自-C=C-鍵)具有譜峰,故咸認係形成聚烯構造(-C=C)n,而推測構成偏光元件的聚乙烯醇因脫水而產生聚烯化(專利文獻2、段落[0012])。
於專利文獻2中,作為該問題的解決策略,係提案將偏光板的每單位面積的水分量設為規定量以下,並且將鄰接於偏光元件的透明保護膜的飽和吸水量設為規定量以下,藉此抑制穿透率的降低。
然而,即便採用如此的方法,在高溫耐久測試之穿透率降低的抑制效果仍不充分。
[先前技術文獻]
[專利文獻]
[專利文獻1]日本特開平11-174417號公報
[專利文獻2]日本特開2014-102353號公報
本發明係提供以下的偏光板、圖像顯示裝置及偏光板的製造方法。
〔1〕一種偏光板,其係具有碘吸附定向於聚乙烯醇系樹脂層所成的偏光元件及透明保護膜,其中,
具有含尿素系化合物層,該含尿素系化合物層包含選自尿素、尿素衍生物、硫脲及硫脲衍生物所組成群組中的至少一種尿素系化合物;
前述偏光元件的含水率係在溫度20℃、相對濕度30%的平衡含水率以上,而且在溫度20℃、相對濕度50%的平衡含水率以下。
〔2〕一種偏光板,其係具有碘吸附定向於聚乙烯醇系樹脂層所成的偏光元件及透明保護膜,其中,
具有含尿素系化合物層,該含尿素系化合物層包含選自尿素、尿素衍生物、硫脲及硫脲衍生物所組成群組中的至少一種尿素系化合物;
前述偏光板的含水率係在溫度20℃、相對濕度30%的平衡含水率以上,而且在溫度20℃、相對濕度50%的平衡含水率以下。
〔3〕如〔1〕或〔2〕所記載的偏光板,其中,前述含尿素系化合物層係含有選自尿素衍生物及硫脲衍生物所組成群組中的至少一種尿素系化合物。
〔4〕如〔1〕至〔3〕中任一項所述的偏光板,其中,前述含尿素系化合物層接於前述偏光元件。
〔5〕如〔1〕至〔4〕中任一項所述的偏光板,其中,前述含尿素系化合物層為接著劑(pressure-sensitive adhesive)層。
〔6〕如〔5〕所述的偏光板,其中,前述含尿素系化合物層包含聚乙烯醇系樹脂。
〔7〕如〔6〕所述的偏光板,其中,於前述含尿素系化合物層中,相對於前述聚乙烯醇系樹脂100質量份,前述尿素系化合物的合計含量為0.1質量份以上400質量份以下。
〔8〕如〔5〕至〔7〕中任一項所述的偏光板,其中,前述含尿素系化合物層的厚度為0.01至7μm。
〔9〕一種偏光板,其係具有碘吸附定向於聚乙烯醇系樹脂層所成的偏光元件及透明保護膜,其中,
前述偏光元件包含選自尿素、尿素衍生物、硫脲及硫脲衍生物所組成群組中的至少一種尿素系化合物;
前述偏光元件的含水率係在溫度20℃、相對濕度30%的平衡含水率以上,而且在溫度20℃、相對濕度50%的平衡含水率以下。
〔10〕一種偏光板,其係具有碘吸附定向於聚乙烯醇系樹脂層所成的偏光元件及透明保護膜,其中,
前述偏光元件包含選自尿素、尿素衍生物、硫脲及硫脲衍生物所組成群組中的至少一種尿素系化合物;
前述偏光板的含水率係在溫度20℃、相對濕度30%的平衡含水率以上,而且在溫度20℃、相對濕度50%的平衡含水率以下。
〔11〕如〔1〕至〔10〕中任一項所述的偏光板,其中,前述偏光板係用於圖像顯示裝置,於前述圖像顯示裝置中,係於前述偏光板的兩面相接地設置空氣層以外的層。
〔12〕一種圖像顯示裝置,係具有:圖像顯示單元、積層於前述圖像顯示單元的視認側表面之第1黏著劑層、以及積層於前述第1黏著劑層的視認側表面之〔1〕至〔11〕中任一項所述的偏光板。
〔13〕如〔12〕所述的圖像顯示裝置,更具有:積層於前述偏光板的視認側表面的第2黏著劑層、以及積層於前述第2黏著劑層的視認側表面的透明構件。
〔14〕如〔13〕所述的圖像顯示裝置,其中,前述透明構件為玻璃板或透明樹脂板。
〔15〕如〔13〕所述的圖像顯示裝置,其中,前述透明構件為觸控面板。
〔16〕一種偏光板的製造方法,其係〔1〕或〔9〕所述的偏光板的製造方法;其中,
具有將前述偏光元件的含水率以成為在溫度20℃、相對濕度30%的平衡含水率以上,而且在溫度20℃、相對濕度50%的平衡含水率以下的方式進行調整的含水率調整步驟。
〔17〕一種偏光板的製造方法,其係〔2〕或〔10〕所述的偏光板的製造方法;其中,
具有將前述偏光板的含水率以成為在溫度20℃、相對濕度30%的平衡含水率以上,而且在溫度20℃、相對濕度50%的平衡含水率以下的方式進行調整之含水率調整步驟。
根據本發明,能夠提供一種偏光板,該偏光板即使在用於層間填充結構的圖像顯示裝置的情況,在高溫環境下的穿透率降低也為小,高溫耐
久性優異;又能夠提供一種圖像顯示裝置,其係藉由使用本發明的偏光板而抑制了高溫環境下的穿透率降低。
《第1實施態樣》
本發明的第1實施態樣的偏光板係具有:碘吸附定向於聚乙烯醇系樹脂層所成的偏光元件;包含選自尿素、尿素衍生物、硫脲及硫脲衍生物的至少一種尿素系化合物的含尿素系化合物層;以及透明保護膜。關於本實施態樣的偏光板係具有下述(a)及(b)中的至少一項特性。
(a)偏光元件的含水率係在溫度20℃、相對濕度30%的平衡含水率以上,而且在溫度20℃、相對濕度50%的平衡含水率以下。
(b)偏光板的含水率係在溫度20℃、相對濕度30%的平衡含水率以上,而且在溫度20℃、相對濕度50%的平衡含水率以下。
本實施態樣的偏光板具有上述(a)及(b)中的至少一項特性,更具有含尿素系化合物層,藉此,即使在作為層間填充結構的圖像顯示裝置的結構要件而長時間暴露在高溫環境下的情況下,也可以抑制單體穿透率的降低。
本實施態樣的偏光板係具有含尿素系化合物層,藉此,即使將偏光板暴露於高溫環境下,也可以抑制偏光度的降低。在將2個偏光板配置成正交偏光鏡(crossed nicol)的關係來使用的情況下,雖然當偏光板的偏光度降低時會變得容易產生漏光(以下也稱為「正交漏光」),惟若是藉由本發明,則即使暴露於高溫環境下偏光度亦不易降低,因此也變得容易抑制正交漏光。
[偏光元件]
作為本發明的碘吸附定向於聚乙烯醇(於後亦稱為PVA)系樹脂層所成的偏光元件,係可使用習知的偏光元件。如此的偏光元件,一般係使用PVA系樹脂膜,藉由將該PVA系樹脂膜用碘染色並進行單軸延伸而形成。
如前所述,PVA系樹脂一般係使用聚乙酸乙烯酯系樹脂進行皂化而得者。皂化度為約85莫耳%以上,較佳為約90莫耳%以上,更佳為約90莫耳%至100莫耳%。作為聚乙酸乙烯酯系樹脂,除了乙酸乙烯酯的均聚物之聚乙酸乙烯酯以外,可列舉乙酸乙烯酯及可與乙酸乙烯酯共聚合的其他單體的共聚物,例如乙烯-乙酸乙烯酯共聚物等。作為可與乙酸乙烯酯共聚合的單體,可列舉例如:不飽和羧酸類、烯烴類、乙烯醚類、不飽和磺酸類等。就PVA系樹脂的聚合度而言,為1000至10000,較佳為1500至5000。該PVA系樹脂可被改性,例如經醛類改性的聚乙烯醇縮甲醛(polyvinyl formal)、聚乙烯醇縮乙醛(polyvinyl acetal)、聚乙烯醇縮丁醛等。
偏光元件的製造方法並無特別限制,典型為:將預先捲成卷軸狀的聚乙烯醇系樹脂膜送出並進行延伸、染色、交聯等而製作之方法;和包含「製作出聚乙烯醇系樹脂與延伸用樹脂基材的積層體,並以積層體的狀態進行延伸」的步驟之方法。於本發明中係可使用任意方法。關於此等偏光元件的製造方法,係記載於日本特開2014-48497號公報的段落[0109]至[0128],而本實施態樣可使用此等方法。而且,本實施態樣的偏光元件的厚度較佳為3至35μm,更佳為4至30μm,又更佳為5至25μm。
(特性(a))
於具有特性(a)的情況下,偏光元件的含水率係在溫度20℃、相對濕度30%的平衡含水率以上,溫度20℃、相對濕度50%的平衡含水率以下。較佳為在溫度20℃、相對濕度45%的平衡含水率以下,又更佳為在溫度20℃、相對濕度42%的平衡含水率以下,最佳為在溫度20℃、相對濕度38%的平衡含水率以下。低於溫度20℃、相對濕度30%的平衡含水率時,偏光元件的操作性會降低,變得容易破裂。偏光元件的含水率若高於溫度20℃、相對濕度50%的平衡含水率時,偏光元件的穿透率會變得容易降低。推測是因為偏光子的含水率高時,PVA系樹脂的聚烯化會變得容易進行之故。偏光元件的上述含水率係偏光板中的偏光元件的含水率。
確認偏光元件的含水率是否在溫度20℃、相對濕度30%的平衡含水率以上,而且在溫度20℃、相對濕度50%的平衡含水率以下之範圍內的方法,係能夠例示以下的方法。將偏光元件保管於已調整為上述溫度及上述相對濕度的範圍之環境,並於一定時間無質量變化的情況下,可視為與該環境達成平衡。或者,可預先計算出經調整為上述溫度及上述相對濕度的範圍的環境之偏光元件的平衡含水率,並藉由將偏光元件的含水率與預先計算出的平衡含水率進行對比來確認。
就含水率在溫度20℃、相對濕度30%的平衡含水率以上,而且在溫度20℃、相對濕度50%的平衡含水率以下的偏光元件之製造方法而言,無特別限制,而可列舉例如:將偏光元件在經調整為上述溫度及上述相對濕度的範圍的環境中保管10分鐘以上3小時以下的方法;或者,以30℃以上90℃以下進行加熱處理的方法。
就製造為上述含水率的偏光元件之其他較佳的方法而言,係可
列舉將在偏光元件的至少單面積層有保護膜的積層體、或用偏光元件所構成的偏光板,於已調整為上述溫度及上述相對濕度的範圍的環境中保管10分鐘以上120小時以下的方法,或者以30℃以上90℃以下進行加熱處理的方法。於製作採用層間填充結構的圖像顯示裝置時,亦可在將於圖像顯示單元積層有偏光板的圖像顯示面板於已調整為上述溫度及上述相對濕度的範圍之環境中保管10分鐘以上3小時以下、或者以30℃以上90℃以下加熱之後,貼合前面板。
偏光元件的含水率,係以在為偏光元件單獨或為偏光元件與保護膜的積層體而構成偏光板用的材料之階段,便將含水率以成為上述數值範圍之方式進行調整為較佳。在構成偏光板之後調整含水率的情況下,翹曲會變得太大,而有在貼合至圖像顯示單元時容易產生不良之情形。藉由使用在構成偏光板之前的材料階段便將含水率調整成為上述含水率的偏光元件來構成偏光板,可容易地構成具備含水率滿足上述數值範圍的偏光元件之偏光板。也可以是在偏光板已貼合於圖像顯示單元的狀態下,將偏光板中的偏光元件的含水率以成為上述數值範圍之方式進行調整。於此情況下,因為偏光板貼合於圖像顯示單元,故不易產生翹曲。
(特性(b))
於具有特性(b)的情況下,偏光板的含水率係在溫度20℃、相對濕度30%的平衡含水率以上,而且在溫度20℃、相對濕度50%的平衡含水率以下。偏光板的含水率較佳為在溫度20℃、相對濕度45%的平衡含水率以下,更佳為在溫度20℃、相對濕度42%的平衡含水率以下,又更佳為在溫度20℃、相對濕度38%的平衡含水率以下。當偏光板的含水率低於溫度20℃、相對濕度30%的平衡含水率時,偏光板的操作性會降低,變得容易破裂。當偏光板的含
水率高於溫度20℃、相對濕度50%的平衡含水率時,偏光元件的穿透率會變得容易降低。推測此係因為當偏光板的含水率高時,PVA系樹脂的聚烯化更容易進行之故。
就確認偏光板的含水率是否在溫度20℃、相對濕度30%的平衡含水率以上,而且在溫度20℃、相對濕度50%的平衡含水率以下之範圍內的方法而言,係可例示以下的方法。保管在已調整為上述溫度及上述相對濕度的範圍的環境中,並於一定時間無質量變化的情況下,可視為與環境達到平衡。或者,預先計算出在調整成上述溫度及上述相對濕度的範圍的環境之偏光板的平衡含水率,並藉由將偏光板的含水率與預先計算出的平衡含水率進行對比而可確認。
就製造含水率在溫度20℃、相對濕度30%的平衡含水率以上,而且在溫度20℃、相對濕度50%的平衡含水率以下之偏光板的方法而言,並無特別限制,例如可列舉:將偏光板在已調整為上述溫度及上述相對濕度的範圍的環境中保管10分鐘以上3小時以下的方法,或者,以30℃以上90℃以下進行加熱處理的方法。
於製作採用層間填充結構的圖像顯示裝置時,亦可在將於圖像顯示單元積層有偏光板的圖像顯示面板於已調整為上述溫度及上述相對濕度的範圍之環境保管中10分鐘以上3小時以下、或者以30℃以上90℃以下進行加熱之後,貼合前面板。
[含尿素系化合物層]
本發明的偏光板具有含尿素系化合物層,此含尿素系化合物層係含有選自尿素、尿素衍生物、硫脲及硫脲衍生物的至少一種尿素系化合物。含尿素系化
合物層只要是含有尿素系化合物之層,即無特別限制,例如可列舉:接著劑層、硬化層。含尿素系化合物層可以接於偏光元件或不接於偏光元件,惟從可進一步抑制高溫環境下的穿透率降低之觀點來看,係以接於偏光元件為較佳。
從生產性之觀點來看,於本發明中,以接著劑層係含尿素系化合物層為較佳。接著劑層係由以下的接著劑形成。作為含尿素系化合物層之接著劑層,可例示貼合偏光元件與保護膜的接著劑層。再者,含尿素系化合物層為接著劑層以外之情況的結構係敘述於後。
〈接著劑層〉
構成用以將保護膜貼合於偏光元件用的接著劑層之接著劑,可使用任意之適合的接著劑。具體而言,接著劑係可使用水系接著劑、溶劑系接著劑、活性能量射線硬化型接著劑等,較佳為水系接著劑。
當接著劑層為含尿素系化合物層的情況下,接著劑係含有選自尿素、尿素衍生物、硫脲及硫脲衍生物的至少一種尿素系化合物。
上述接著劑之塗佈時的厚度,係能夠設定為任意之適合的值。例如以在硬化後或加熱(乾燥)後能夠得到具有所期望的厚度之接著劑層的方式進行設定。接著劑層的厚度較佳為0.01μm至7μm,更佳為0.01μm至5μm,又更佳為0.01μm至2μm,最佳為0.01μm至1μm。
(水系接著劑)
而且,上述水系接著劑能夠採用任意之適合的水系接著劑。其中,尤以使用包含PVA系樹脂的水系接著劑(PVA系接著劑)為較佳。就接著性之點而言,水系接著劑所包含的PVA系樹脂的平均聚合度較佳為100至5500左右,
更佳為1000至4500。就接著性之點而言,平均皂化度較佳為85莫耳%至100莫耳%左右,更佳為90莫耳%至100莫耳%。
作為上述水系接著劑所包含的PVA系樹脂,較佳為含有乙醯乙醯基者,其理由為:PVA系樹脂層與保護膜的黏合性佳、耐久性佳。含有乙醯乙醯基的PVA系樹脂係例如能夠藉由使PVA系樹脂與倍羰烯(diketene)以任意方法反應而得到。含有乙醯乙醯基的PVA系樹脂的乙醯乙醯基的改性度,一般而言為0.1莫耳%以上,較佳為0.1莫耳%至20莫耳%左右。
上述水系接著劑的樹脂濃度較佳為0.1重量%至15重量%,更佳為0.5重量%至10重量%。
(交聯劑、溶劑)
本發明可使用的較佳的水溶性PVA系接著劑,除了可含有上述PVA系樹脂、尿素系化合物之外,亦可依需要而含有交聯劑。作為交聯劑,可使用習知的交聯劑。例如可列舉:水溶性環氧化合物、二醛、異氰酸酯等。
當PVA系樹脂為含有乙醯乙醯基的PVA系樹脂時,交聯劑較佳為乙二醛(glyoxal)、乙醛酸鹽、羥甲基三聚氰胺中的任一種,更佳為乙二醛、乙酸酸鹽中的任一種,特別佳為乙二醛。
而且,本發明的水溶性PVA系接著劑也可以含有有機溶劑。於該情況下,就與水具有混合性之點而言,較佳為醇類,而更佳為醇類中的甲醇或乙醇。
再者,於本發明中,係有一部分的尿素衍生物對於水的溶解度低,但是對於醇的溶解度為充分者。於該情況下,「在溶解於醇而調製出尿素衍生物的醇
溶液之後,將尿素衍生物的醇溶液添加於PVA水溶液,調製接著劑」亦屬較佳態樣之一。
(活性能量射線硬化型接著劑)
作為上述活性能量射線硬化型接著劑,若為能夠藉由活性能量射線的照射而硬化的接著劑,即可使用任意適合的接著劑。活性能量射線硬化型接著劑例如可列舉:紫外線硬化型接著劑、電子射線硬化型接著劑等。活性能量射線硬化型接著劑之硬化型的具體例例如可列舉:自由基硬化型、陽離子硬化型、陰離子硬化型、該等的組合(例如自由基硬化型與陽離子硬化型的混合)。
上述活性能量射線硬化型接著劑係例如可列舉:含有具有(甲基)丙烯酸酯基、(甲基)丙烯醯胺基等自由基聚合性基的化合物(例如單體及/或寡聚物)作為硬化成分的接著劑。上述活性能量射線硬化型接著劑及其硬化方法的具體例,例如記載於日本特開2012-144690號公報。
(尿素系化合物)
當接著劑層為含尿素系化合物層時,接著劑層係含有選自尿素、尿素衍生物、硫脲及硫脲衍生物的至少一種尿素系化合物。
就使接著劑層含有尿素系化合物的方法而言,係以使上述接著劑含有尿素系化合物為較佳。再者,在從接著劑經由乾燥步驟等而形成接著劑層的過程中,尿素系化合物的一部分從接著劑層移動到偏光元件等亦無妨。
尿素系化合物有水溶性者及難水溶性者,任一種尿素系化合物都可用於本發明。當將難水溶性尿素系化合物使用於水溶性接著劑時,係以於形成接著劑層之後不發生霧度上升的方式在分散方法下功夫為較佳。
當接著劑含有PVA樹脂的水系接著劑時,相對於PVA 100質量
份,尿素系化合物的添加量係以0.1至400質量份為較佳,1至200質量份為更佳,3至100質量份為又更佳。
(尿素衍生物)
尿素衍生物為尿素分子的4個氫原子中的至少1個經取代基取代之化合物。於此情況下,取代基並無特別限制,較佳為由碳原子、氫原子及氧原子所成的取代基。
就尿素衍生物的具體例而言,單取代尿素可列舉:甲基脲、乙基脲、丙基脲、丁基脲、異丁基脲、N-十八基脲、2-羥基乙基脲、羥基脲、乙醯基脲、烯丙基脲、2-丙炔基脲、環己基脲、苯基脲、3-羥基苯基脲、(4-甲氧基苯基)脲、苯甲基脲、苯甲醯基脲、鄰甲苯基脲、對甲苯基脲。
二取代尿素可列舉:1,1-二甲基脲、1,3-二甲基脲、1,1-二乙基脲、1,3-二乙基脲、1,3-雙(羥基甲基)脲、1,3-第三丁基脲、1,3-二環己基脲、1,3-二苯基脲、1,3-雙(4-甲氧基苯基)脲、1-乙醯基-3-甲基脲、2-咪唑啉酮(乙烯脲)、四氫-2-嘧啶酮(丙烯脲)。
四取代尿素可列舉:四甲基脲、1,1,3,3-四乙基脲、1,1,3,3-四丁基脲、1,3-二甲氧基-1,3-二甲基脲、1,3-二甲基-2-咪唑啉酮、1,3-二甲基-3,4,5,6-四氫-2(1H)-嘧啶酮。
(硫脲衍生物)
硫脲衍生物為硫脲分子的4個氫原子中的至少1個經取代基取代的化合物。於此情況下,取代基並無特別限制,較佳為由碳原子、氫原子及氧原子所成的取代基。
就硫脲衍生物的具體例而言,單取代硫脲可列舉:N-甲基硫
脲、乙基硫脲、丙基硫脲、異丙基硫脲、1-丁基硫脲、環己基硫脲、N-乙醯基硫脲、N-烯丙基硫脲、(2-甲氧基乙基)硫脲、N-苯基硫脲、(4-甲氧基苯基)硫脲、N-(2-甲氧基苯基)硫脲、N-(1-萘基)硫脲、(2-吡啶基)硫脲、鄰甲苯基硫脲、對甲苯基硫脲。
二取代硫脲可列舉:1,1-二甲基硫脲、1,3-二甲基硫脲、1,1-二乙基硫脲、1,3-二乙基硫脲、1,3-二丁基硫脲、1,3-二異丙基硫脲、1,3-二環己基硫脲、N,N-二苯基硫脲、N,N’-二苯基硫脲、1,3-二(鄰甲苯基)硫脲、1,3-二(對甲苯基)硫脲、1-苯甲基-3-苯基硫脲、1-甲基-3-苯基硫脲、N-烯丙基-N,-(2-羥基乙基)硫脲、乙烯硫脲。
三取代硫脲可列舉三甲基硫脲,四取代硫脲可列舉:四甲基硫脲、1,1,3,3-四乙基硫脲。
就在使用於層間填充結構的圖像顯示裝置時,會抑制高溫環境下的穿透率的降低且偏光度的降低少之點(正交漏光受到抑制之點)而言,尿素系化合物當中,較佳為尿素衍生物或硫脲衍生物,更佳為尿素衍生物。尿素衍生物當中,尤以單取代尿素或二取代尿素為較佳,以單取代尿素為更佳。二取代尿素係有1,1-取代尿素及1,3-取代尿素,惟以1,3-取代尿素為更佳。
[透明保護膜]
本發明所使用的透明保護膜(於後,亦簡稱為「保護膜」),係隔著接著劑層而貼合於偏光元件的至少單面側。此透明保護膜可貼合於偏光元件的單面或兩面,而以貼合於兩面為更佳。於一態樣中,保護膜係隔著屬於含尿素系化合物層的接著劑層而貼合於偏光元件。
而且,於在偏光元件的兩面隔著接著劑層而貼合保護膜的結構中,偏光元件兩面的接著劑層當中,係只有單面的接著劑層為含尿素系化合物層亦無妨,惟更佳為兩面的接著劑層均為含尿素系化合物層。
近年來,為了因應偏光板的薄型化之需求,係開發只在偏光元件的單面具有保護膜之偏光板。於該結構中,亦以隔著本發明的含尿素系化合物層之接著劑層來積層保護膜為較佳。
作為只在偏光元件的單面具有保護膜之偏光板的製作方法,可考慮「先製作出在兩面隔著接著劑層而貼合有保護膜的偏光板之後,將一個保護膜剝離」的方法,而於使用如此的製造方法的情況下,僅某一接著劑層為本發明的含尿素系化合物層亦無妨,更佳為於偏光元件的兩面使用本發明的含尿素系化合物層。
而且,當本發明的含尿素系化合物層作為接著劑層而只施用於偏光元件的單面的情況下,較佳為不剝離的膜側之接著劑層為本發明的含尿素系化合物層。
保護膜可同時具有其他的光學功能,亦可形成積層有其他層的積層構造。
從光學特性之觀點來看,此時之保護膜的膜厚係以薄者為較佳,惟太薄時強度會降低,為加工性差者。適合的膜厚為5至100μm,較佳為10至80μm,更佳為15至70μm。
保護膜係可使用由醯化纖維素系樹脂膜、聚碳酸酯系樹脂所成的膜、由降莰烯等環烯烴系樹脂所成的膜、(甲基)丙烯酸系聚合物膜、聚對苯二甲酸乙二酯等聚酯系樹脂膜等膜。
當為於偏光元件的兩面具有保護膜的結構時,在使用PVA接著劑等水系接著劑進行貼合的情況下,就透濕度之點而言,以至少單側的保護膜係醯化纖維素系樹脂膜或(甲基)丙烯酸系聚合物膜中之任一者為較佳,其中尤以醯化纖維素系樹脂膜為較佳。
作為至少一側的保護膜,係可以視角補償等為目的而具備相位差功能,於該情況下,可為膜本身具有相位差功能,亦可為另外具有相位差層,也可以是兩者的組合。
再者,雖係就具備相位差功能的膜隔著接著劑而直接貼合於偏光元件知結構進行說明,但是若為隔著已貼合於偏光元件的另一保護膜而隔著黏著劑或接著劑來貼合的結構亦無妨。
[偏光板的製造方法]
本實施態樣的偏光板的製造方法係具有積層步驟與含水率調整步驟,前述積層步驟係積層偏光元件與含尿素系化合物層,而前述含尿素系化合物層係包含選自尿素、尿素衍生物、硫脲及硫脲衍生物所組成群組中的至少一種尿素系化合物者。當製造具有特性(a)的偏光板時,於含水率調整步驟中,係以使偏光元件的含水率成為在溫度20℃、相對濕度30%的平衡含水率以上而且在溫度20℃、相對濕度50%的平衡含水率以下的方式來調整偏光元件的含水率。偏光元件的含水率係可根據上述偏光元件的含水率之記載來進行調整。當製造具有特性(b)的偏光板時,於含水率調整步驟中,係以使偏光板的含水率成為在溫度20℃、相對濕度30%的平衡含水率以上而且在溫度20℃、相對濕度50%的平衡含水率以下的方式來調整偏光元件的含水率。偏光板的含水率
係可根據上述偏光板的含水率之記載來進行調整。積層步驟及含水率調整步驟的順序並沒有限制,亦可同時進行積層步驟與含水率調整步驟。
[圖像顯示裝置的結構]
本發明的偏光板可使用於液晶顯示裝置、有機EL顯示裝置等各種圖像顯示裝置。關於圖像顯示裝置,當為以偏光板的兩面與空氣層以外的層相接的結構之層間填充結構時,於高溫環境下的穿透率容易降低。在使用了本發明的偏光板之圖像顯示裝置中,即使為層間填充結構,也可以抑制於高溫環境下之偏光板的穿透率降低。作為圖像顯示裝置,可例示具有圖像顯示單元、積層於圖像顯示單元的視認側表面之第1黏著劑層、積層於第1黏著劑層的視認側表面之偏光板的結構。如此的圖像顯示裝置,可更具有積層於偏光板的視認側表面之第2黏著劑層、及積層於第2黏著劑層表面之透明構件。特別是本發明的偏光板,適合使用於具有層間填充結構的圖像顯示裝置,前述層間填充結構係於圖像顯示裝置的視認側配置透明構件,藉由第1黏著劑層貼合偏光板與圖像顯示單元,並藉由第2黏著劑層貼合偏光板與透明構件藉由第2黏著劑層而成者。於本說明書中,係有將第1黏著劑層及第2黏著劑層中之一者或兩者簡稱為「黏著劑層」的情況。再者,就偏光板與圖像顯示單元的貼合和偏光板與透明構件的貼合所使用之構件而言,並不限定於黏著劑層,亦可為接著劑層。
〈圖像顯示單元〉
作為圖像顯示單元,可列舉液晶單元和有機EL單元。作為液晶單元,係可使用「利用外部光的反射型液晶單元」、「利用源自背光等光源的光之穿透型液晶單元」、「利用源自外部的光及源自光源的光雙方之半穿透半反射型液晶單元」的任一種。當液晶單元係利用源自光源的光者時,圖像顯示裝置(液
晶顯示裝置)係於圖像顯示單元(液晶單元)的視認側與相反側均配置偏光板,並且配置光源。光源側的偏光板與液晶單元,係以隔著適合的黏著劑層貼合為較佳。就液晶單元的驅動方式而言,例如可使用為VA模式、IPS模式、TN模式、STN模式、彎曲定向(π型)等任意型式者。
作為有機EL單元,係適合使用於透明基板上依序積層透明電極、有機發光層及金屬電極而形成有發光體(有機電激發光的發光體)者等。有機發光層為各種有機薄膜的積層體,可採用各種層結構,例如:由三苯基胺衍生物等所成的電洞注入層與由蒽等螢光性的有機固體所成的發光層之積層體;該等發光層與由苝衍生物等所成的電子注入層之積層體;或電洞注入層、發光層及電子注入層之積層體等。
〈圖像顯示單元與偏光板的貼合〉
圖像顯示單元與偏光板的貼合係能夠適合使用黏著劑層(黏著片)。其中,從操作性等之觀點來看,尤以將在偏光板的一面附設有黏著劑層之附黏著劑層的偏光板與圖像顯示單元進行貼合的方法為較佳。對於偏光板附設黏著劑層,係可用適合的方法來進行。就其例子而言,例如可列舉:使基質聚合物或其組成物溶解或分散在甲苯、乙酸乙酯等適合的溶劑之單獨或混合物所成的溶劑中,調製10至40重量%左右的黏著劑溶液,並將該黏著劑溶液以流動方式、塗佈方式等適當地延展方式直接附設在偏光板上之方式;或者如前所述般地在分隔膜上形成黏著劑層之後,將黏著劑層轉移到偏光板之方式等。
〈黏著劑層〉
關於黏著劑層,係如日本特開2018-025765號公報的段落[0103]至[0143]所記載般,於本發明可使用該等黏著劑。
〈透明構件〉
作為配置於圖像顯示裝置的視認側的透明構件,可列舉前面板(窗層)、觸控面板等。前面板可使用具有適合的機械強度及厚度之前面板。如此的前面板例如可列舉如丙烯酸系樹脂和聚碳酸酯系樹脂的透明樹脂板、或玻璃板等。於前面板的視認側積層抗反射層等功能層亦無妨。而且,當前面板為透明樹脂板時,為了提高物理強度而積層硬塗層、為了降低透濕度而積層低透濕層亦無妨。
觸控面板係可使用電阻膜式、電容式、光學式、超音波式等的各種觸控面板,和具備觸控感測器功能的玻璃板、透明樹脂板等。當使用電容式的觸控面板來作為透明構件時,係以在較觸控面板更靠近視認側處設置由玻璃、透明樹脂板所成的前面板為較佳。
〈偏光板與透明構件的貼合〉
在偏光板與透明構件的貼合方面,係適合使用黏著劑或UV硬化型的接著劑。當使用黏著劑時,能夠用適合的方式進行黏著劑的設置。具體的設置方法例如可列舉:在前述圖像顯示單元與偏光板的貼合所使用之黏著劑層的設置方法。
當使用UV硬化型的接著劑時,在防止硬化前的接著劑溶液的擴散之目的下,係適合使用以圍繞圖像顯示面板上的周圍部之方式設置壩材(dam material),並在壩材上載置透明構件,而注入接著劑溶液的方法。在注入接著劑溶液之後,係依需要而進行對位及脫泡,之後照射UV光來進行硬化。
然後,說明接著劑層以外的含尿素系化合物層。
[含尿素系化合物層(接著劑層以外)]
含尿素系化合物層係以具有至少1種尿素系化合物及黏結劑為較佳。作為黏結劑,可列舉聚合物黏結劑、熱硬化型樹脂黏結劑、活性能量射線硬化型樹脂黏結劑等,於本發明中係可使用任意的黏結劑。
含尿素系化合物層的厚度係以0.1至20μm為較佳,0.5至15μm為更佳,1至10μm為又更佳。
含尿素系化合物層係直接積層於偏光元件或隔著其他層而積層均無妨,惟就容易抑制高溫環境下的穿透率降低之點而言,係以直接積層並接於偏光元件為較佳。
具有接著劑層以外的含尿素系化合物層之偏光板就提高偏光板的物理強度之點而言,係以於偏光元件的至少一面隔著接著劑層而具有透明保護膜為較佳。此時,接著劑層係含有尿素系化合物或不含有尿素系化合物均無妨,惟以含有尿素系化合物為更佳。
如保護膜的說明所記載的,近年來為了因應偏光板的薄型化之需求,係開發只在偏光元件的單面具有保護膜之偏光板(於後亦稱為「單面附保護膜的偏光板」)。
對於如此的結構,係以提高物理強度等為目的而嘗試了在偏光元件的不具保護膜的面積層硬化層(例如日本特開2011-221185號公報)。
於本實施態樣中,使如此的硬化層含有尿素系化合物而作為含尿素系化合物層之結構,亦屬於較佳的態樣之一。通常來說,如此的硬化層是由包含有機溶劑的硬化性組成物所形成,而於日本特開2017-075986號公報的段落[0020]至[0042]中,係記載了由活性能量射線硬化性高分子組成物的水性溶液來形成如此的硬化層之方法。因為尿素系化合物多為水溶性,故使如此的組
成物含有水溶性的尿素系化合物,並形成含尿素系化合物層者亦為本實施態樣的較佳態樣之一。
《第2實施態樣》
本發明的第2實施態樣的偏光板,係具有偏光元件以及透明保護膜,前述偏光元件係使碘吸附定向於聚乙烯醇系樹脂層所成者,其中包含選自尿素、尿素衍生物、硫脲及硫脲衍生物的至少一種尿素系化合物。關於本實施態樣的偏光板係具有下述(a)及(b)中的至少一項特性。
(a)偏光元件的含水率係在溫度20℃、相對濕度30%的平衡含水率以上,而且在溫度20℃、相對濕度50%的平衡含水率以下。
(b)偏光板的含水率係在溫度20℃、相對濕度30%的平衡含水率以上溫度20℃、相對濕度50%的平衡含水率以下。
本實施態樣的偏光板係具有上述(a)及(b)中的至少一項特性,而且於偏光元件含有尿素系化合物,藉此,即使在使用於層間填充結構的圖像顯示裝置,而且長時間暴露在高溫環境下之情況下,也可以抑制單體穿透率的降低。本實施態樣的偏光板,偏光元件係含有尿素系化合物,藉此,即使偏光板暴露於高溫環境下也可以抑制偏光度的降低,還變得容易抑制正交漏光。
上述(a)及(b)的特性係與第1實施態樣中的(a)及(b)特性相同。
本實施態樣的偏光元件的製作方法,係於第1實施態樣記載的偏光元件的製作方法中具有使偏光元件含有尿素系化合物的步驟。就使偏光元件含有尿素系化合物的方法而言,可係經由在偏光元件的至少單面過塗佈含有
尿素系化合物的溶液並乾燥的步驟來製作偏光元件,藉此得到含有尿素系化合物的偏光元件。也可於偏光元件的製造步驟中,藉由將PVA系樹脂層浸漬於含有尿素系化合物的處理溶液中之方法、或將處理溶液對PVA系樹脂層進行噴霧、流佈或滴加之方法等來使偏光元件含有尿素系化合物。其中,尤以使用將PVA系樹脂層浸漬於含有尿素系化合物的處理溶液中的方法為較佳。
將PVA系樹脂層浸漬於含有尿素系化合物的處理溶液中之步驟,係可與偏光元件的製造方法中之膨潤、延伸、染色、交聯、洗淨等步驟同時進行,亦可與該等步驟另行設置。使PVA系樹脂層含有尿素系化合物的步驟,係以在將PVA系樹脂層用碘染色後進行為較佳,而以與染色後的交聯步驟同時進行為更佳。藉由如此的方法,可使色調變化小,並使對偏光元件的光學特性造成的影響變小。
關於本實施態樣之偏光元件所包含的尿素系化合物的種類、含量,係能套用第1實施態樣之含尿素系化合物層的說明。再者,本實施態樣的偏光元件亦可使用作為第1實施態樣之偏光板的偏光元件。本實施態樣之偏光板的其他結構,除了第1實施態樣的含尿素系化合物層為任意的結構要素之點以外,係與第1實施態樣為相同結構。
[尿素系化合物溶液]
本實施態樣所使用的含有尿素系化合物之溶液的溶劑係以水、有機溶劑或該等的混合液為較佳,而以水或水與醇的混合溶劑中之任一者為更佳。而且,當為水與醇的混合溶劑時,係以醇為甲醇或乙醇中之任一者為較佳。關於尿素系化合物,係如第1實施態樣所說明,惟就乾燥後不易在偏光元件的表面析出尿素系化合物之點而言,以尿素系化合物係水溶性為較佳。
[偏光板的製造方法]
本實施態樣的偏光板的製造方法係具有含水率調整步驟。關於含水率調整步驟,係與第1實施態樣的偏光板之製造方法相同。
(實施例)
以下,係基於實施例而具體地說明本發明。以下的實施例所表示的材料、試劑、物質的量及其比例、操作等,係可在不脫離本發明的精神下適當地予以改變。因此,本發明並不侷限於以下的實施例。
(偏光元件1的製作)
將平均聚合度約2,400、皂化度99.9莫耳%以上之由聚乙烯醇所成的厚度40μm的聚乙烯醇膜以乾式進行約5倍的單軸延伸,再保持緊繃狀態而浸漬於60℃的純水中1分鐘後,在28℃浸漬於碘/碘化鉀/水的重量比為0.05/5/100的水溶液中60秒。然後,在72℃浸漬於碘化鉀/硼酸/水的重量比為8.5/8.5/100的水溶液中300秒。接著,以26℃的純水洗淨20秒後,以65℃乾燥,得到碘吸附定向於聚乙烯醇的厚度15μm的偏光元件。
(接著劑用PVA溶液的調製)
將含有乙醯乙醯基的改性PVA系樹脂(三菱化學(股份公司)公司製:Gohsenx Z-410)50g溶解於950g的純水中,在90℃加熱2小時後,冷卻至常溫,得到接著劑用PVA溶液。
(尿素系化合物溶液的調製)
在純水90g中添加尿素10g,得到尿素10重量%水溶液(溶液1)。同樣地,根據表1,用表1所記載的尿素系化合物取代尿素而調製出尿素溶液2至4。
上述之所使用的尿素、甲基尿素、乙基尿素、四氫-2-嘧啶酮皆係使用東京化成工業股份公司的試劑。
(偏光板用接著劑1的調製)
將上述所調製的接著劑用PVA溶液、尿素溶液1、純水及甲醇以成為PVA濃度3.0%、甲醇濃度20%、尿素濃度0.5%的方式進行調配,得到偏光板用接著劑1。
(偏光板用接著劑2的調製)
同樣地,將接著劑用PVA溶液、表1所記載的尿素溶液2、純水及甲醇以成為PVA濃度3.0%、甲醇濃度20%、甲基尿素濃度0.7%的方式進行調配,得到偏光板用接著劑2。
(偏光板用接著劑3的調製)
同樣地,將接著劑用PVA溶液、表1所記載的尿素溶液3、純水及甲醇以成為PVA濃度3.0%、甲醇濃度20%、乙基尿素濃度1.0%的方式進行調配,得到偏光板用接著劑3。
(偏光板用接著劑4的調製)
同樣地,將接著劑用PVA溶液、表1所記載的尿素溶液4、純水及甲醇以成為PVA濃度3.0%、甲醇濃度20%、四氫-2-嘧啶酮濃度1.5%的方式進行調配,得到偏光板用接著劑4。
(偏光板用接著劑5的調製)
同樣地,將接著劑用PVA溶液、純水及甲醇以成為PVA濃度3.0%、甲醇濃度20%的方式進行調配,得到偏光板用接著劑5。
(醯化纖維素膜的皂化)
將市售的醯化纖維素膜TD40(FUJI FILM(股份公司)公司製:膜厚40μm)浸漬於保持在55℃的1.5莫耳/升之NaOH水溶液(皂化液)中2分鐘後,將膜進行水洗,然後,浸漬於25℃的0.05莫耳/升的硫酸水溶液中30秒後,再將膜以水洗浴在流水下通過30秒,使膜成為中性的狀態。然後,以空氣刀重複除水3次,除去水後在70℃的乾燥區停留15秒進行乾燥,製作成經皂化處理的膜。
(偏光板1的製作)
於偏光元件1的兩面,將上述製作的皂化處理過的醯化纖維素膜隔著偏光板用接著劑1,以乾燥後的接著劑層的厚度成為兩面共為100nm的方式進行調整並使用滾輪貼合機貼合之後,以60℃乾燥10分鐘,得到兩面附醯化纖維素膜的偏光板1。
(偏光板2至5的製作)
除了以偏光板用接著劑2至5取代偏光板用接著劑1之外,係以與偏光板1同樣的方式製作偏光板2至5。
(偏光板(偏光元件)的含水率之調整)
將上述所得之偏光板1至5在溫度20℃且相對濕度30%、35%、40%、45%、50%或55%的條件下保管72小時。在保管66小時、69小時及72小時使用卡耳-費雪(Karl Fischer)法,測定出含水率。在所有的濕度條件下,於保管66小時、69小時及72小時之含水率的值均未改變。所以,可將偏光板1至5的含水率視為與本實驗例所採用的72小時的保管環境之平衡含水率相同。當偏光板的含水率在某保管環境下達成平衡時,則可將偏光板中的偏光元件之含水率也同樣地視為與該保管環境達成平衡。而且,當偏光板中的偏光元件的含水率與某保管環境達成平衡時,可將偏光板的含水率也同樣地視為與該保管環境達成平衡。
(光學積層體1的製作)
參考日本特開2018-025765號公報的實施例,在上述製作的偏光板1的兩面塗佈丙烯酸系黏著劑(製造者:LINTEC(股份公司)公司、產品編號:# 7),藉此製作出於兩面具有厚度25μm的黏著劑層(第1黏著劑層及第2黏著劑層)之光學積層體1。
(光學積層體2至5的製作)
與光學積層體1同樣地,除了係以偏光板2至5取代偏光板1之外,以同樣的方式製作光學積層體2至5。
[實施例1至9、比較例1至6]
實施例1至9、比較例1至6係使用表2所示的光學積層體,並以使所使用的光學積層體的含水率成為如表2所示之環境的平衡含水率的方式,在溫度20℃、相對濕度30%、35%、40%、45%、50%或55%的條件下保管72小
時。光學積層體的含水率可視為與保管環境的含水率達成平衡,而且光學積層體中的偏光板及偏光元件的含水率也可視為與光學積層體的含水率相同。
(檢查用偏光板1)
只在偏光板1的單面積層丙烯酸系黏著劑(製造者:LINTEC(股份公司)公司、產品編號:# 7),製作成檢查用偏光板1。將如此方式製作出的檢查用偏光板1以短邊與吸收軸呈平行的方式裁切成50mm×100mm的大小,並將前述黏著劑層的表面貼合於無鹼玻璃〔商品名”EAGLE XG”、康寧公司製〕,製作交叉評估用試樣1。
[高溫耐久測試後的單體穿透率評估(105℃)]
將上述製作的光學積層體1至5分別以長邊與吸收軸呈平行的方式裁切成50mm×100mm的大小,並將第1黏著劑層及第2黏著劑層的表面分別貼合於無鹼玻璃〔商品名”EAGLE XG”、康寧公司製〕,製作出評估用試樣。
將該評估試樣以溫度50℃、壓力5kgf/cm2(490.3kPa)實施1小時的高壓釜處理後,在溫度23℃、相對濕度55%的環境下放置24小時。然後,測定穿透率(初始值),在溫度105℃的加熱環境下保管,並於100至200小時為止每隔50小時測定穿透率。基於相對於初始值之穿透率的降低達到5%以上的時間,而用以下的基準進行評估。將所得之結果表示於表2。
200小時後穿透率的降低為5%以下者:A
150至200小時後穿透率的降低達到5%以上者:B
100至150小時後穿透率的降低達到5%以上者:C
100小時後穿透率的降低達到5%以上者:D
[高溫耐久測試後的正交漏光的評估]
在將高溫耐久測試後的單體穿透率評估試樣進行200小時後的評估之後,將上述光學積層體與未放入加熱環境下的交叉評估用試樣1配置成正交偏光鏡的狀態,並載置於在背光上。將周圍遮光,用目視方式根據以下標準評估正交漏光。再者,單體穿透率降低5%以上的試樣由於有聚烯化所致之著色,因此從正交漏光的評估對象中排除。
完全沒有觀察到正交漏光者:A
幾乎沒有觀察到正交漏光者:B
觀察到些許的正交漏光者:C
觀察到明顯的正交漏光者:D
Claims (17)
- 一種偏光板,其係具有碘吸附定向於聚乙烯醇系樹脂層所成的偏光元件及透明保護膜,其中,具有含尿素系化合物層,該含尿素系化合物層包含選自尿素、尿素衍生物、硫脲及硫脲衍生物所組成群組中的至少一種尿素系化合物;前述偏光元件的含水率係在溫度20℃、相對濕度30%的平衡含水率以上,而且在溫度20℃、相對濕度50%的平衡含水率以下。
- 一種偏光板,其係具有碘吸附定向於聚乙烯醇系樹脂層所成的偏光元件及透明保護膜,其中,具有含尿素系化合物層,該含尿素系化合物層包含選自尿素、尿素衍生物、硫脲及硫脲衍生物所組成群組中的至少一種尿素系化合物;前述偏光板的含水率係在溫度20℃、相對濕度30%的平衡含水率以上,而且在溫度20℃、相對濕度50%的平衡含水率以下。
- 如請求項1或2所述之偏光板,其中,前述含尿素系化合物層係含有選自尿素衍生物及硫脲衍生物所組成群組中的至少一種尿素系化合物。
- 如請求項1至3中任一項所述之偏光板,其中,前述含尿素系化合物層係接於前述偏光元件。
- 如請求項1至4中任一項所述之偏光板,其中,前述含尿素系化合物層為接著劑層。
- 如請求項5所述之偏光板,其中,前述含尿素系化合物層包含聚乙烯醇系樹脂。
- 如請求項6所述之偏光板,其中,於前述含尿素系化合物層中,相對於前述聚乙烯醇系樹脂100質量份,前述尿素系化合物的合計含量為0.1質量份以上400質量份以下。
- 如請求項5至7中任一項所述之偏光板,其中,前述含尿素系化合物層的厚度為0.01至7μm。
- 一種偏光板,其係具有碘吸附定向於聚乙烯醇系樹脂層所成的偏光元件及透明保護膜,其中,前述偏光元件包含選自尿素、尿素衍生物、硫脲及硫脲衍生物所組成群組中的至少一種尿素系化合物;前述偏光元件的含水率係在溫度20℃、相對濕度30%的平衡含水率以上,而且在溫度20℃、相對濕度50%的平衡含水率以下。
- 一種偏光板,其係具有碘吸附定向於聚乙烯醇系樹脂層所成的偏光元件及透明保護膜,其中,前述偏光元件包含選自尿素、尿素衍生物、硫脲及硫脲衍生物所組成群組中的至少一種尿素系化合物;前述偏光板的含水率係在溫度20℃、相對濕度30%的平衡含水率以上,而且在溫度20℃、相對濕度50%的平衡含水率以下。
- 如請求項1至10中任一項所述之偏光板,其中,前述偏光板係用於圖像顯示裝置,在前述圖像顯示裝置中,係於前述偏光板的兩面相接地設置空氣層以外的層。
- 一種圖像顯示裝置,係具備圖像顯示單元、積層於前述圖像顯示單元的視認側表面的第1黏著劑層、及積層於前述第1黏著劑層的視認側表面之請求項1至11中任一項所述之偏光板。
- 如請求項12所述之圖像顯示裝置,其中更具有:積層於前述偏光板的視認側表面之第2黏著劑層、及積層於前述第2黏著劑層的視認側表面之透明構件。
- 如請求項13所述之圖像顯示裝置,其中,前述透明構件為玻璃板或透明樹脂板。
- 如請求項13所述之圖像顯示裝置,其中,前述透明構件為觸控面板。
- 一種偏光板的製造方法,其係請求項1或9所述之偏光板的製造方法,其中,具有以使前述偏光元件的含水率成為在溫度20℃、相對濕度30%的平衡含水率以上,而且在溫度20℃、相對濕度50%的平衡含水率以下的方式來進行調整之含水率調整步驟。
- 一種偏光板的製造方法,其係請求項2或10所述之偏光板的製造方法,其中,具有以使前述偏光板的含水率成為在溫度20℃、相對濕度30%的平衡含水率以上,而且在溫度20℃、相對濕度50%的平衡含水率以下的方式來進行調整之含水率調整步驟。