CN114746780A - 偏振板以及使用了该偏振板的图像显示装置 - Google Patents
偏振板以及使用了该偏振板的图像显示装置 Download PDFInfo
- Publication number
- CN114746780A CN114746780A CN202080078958.6A CN202080078958A CN114746780A CN 114746780 A CN114746780 A CN 114746780A CN 202080078958 A CN202080078958 A CN 202080078958A CN 114746780 A CN114746780 A CN 114746780A
- Authority
- CN
- China
- Prior art keywords
- polarizing plate
- urea
- water content
- relative humidity
- temperature
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明的目的在于,提供一种偏振板,其即使在用于层间填充构成的图像显示装置的情况下,也能够抑制高温环境下的透射率的降低。本发明提供一种偏振板,其具有使聚乙烯醇系树脂层吸附碘并使碘取向而成的偏振元件、和透明保护膜,所述偏振板具有包含选自脲、脲衍生物、硫脲及硫脲衍生物中的至少一种脲系化合物的含有脲系化合物的层,所述偏振元件的含水率为温度20℃且相对湿度30%的平衡含水率以上,并且为温度20℃相对湿度50%的平衡含水率以下。
Description
技术领域
本发明涉及一种偏振板。此外,本发明涉及该偏振板的一个面与图像显示单元贴合、另一个面与触控面板、前面板等透明构件贴合的图像显示装置。
背景技术
液晶显示装置(LCD)不仅用于液晶电视,而且还在个人电脑、手机等移动设备、导航仪等车载用途等中广泛地使用。通常,液晶显示装置具有在液晶单元的两侧利用粘合剂贴合有偏振板的液晶面板构件,通过利用液晶面板构件控制来自背光构件的光来进行显示。另外,近年来,有机EL显示装置也与液晶显示装置同样地在电视、手机等移动设备、导航仪等车载用途中广泛地使用。有机EL显示装置中,为了抑制外来光由金属电极(阴极)反射而被观察成镜面的情况,有时在图像显示面板的可视侧表面配置圆偏振板(包含偏振元件和λ/4板的层叠体)。
偏振板被如上所述地作为液晶显示装置、有机EL显示装置的构件搭载于车中的机会正在增加。车载用的图像显示装置中使用的偏振板与其以外的电视、手机等移动设备用途相比,暴露于高温环境下的情况更多,要求高温下的特性变化更小(高温耐久性)。
另一方面,出于防止来自外表面的冲击所致的图像显示面板的破损等目的,相对于图像显示面板的偏振板进一步在可视侧设置透明树脂板、玻璃板等前面板(也称作“窗层”等。)的构成增多起来。另外,具备触控面板的显示装置中,广泛地采用如下的构成,即,相对于图像显示面板的偏振板进一步在可视侧设置触控面板,相对于触控面板进一步在可视侧具备前面板。
此种构成中,若在图像显示面板与前面板、触控面板等透明构件之间存在空气层,则会产生空气层界面处的光的反射所致的外来光的反射眩光,画面的可视性有降低的趋势。因此,采用如下构成的做法正在推广开来,即,将配置于图像显示面板的可视侧表面的偏振板与透明构件之间的空间用空气层以外的层(以下有时称作“层间填充剂”)填充的构成(以下有时称作“层间填充构成”),优选采用以折射率与这些材料接近的材料来填充的构成。作为层间填充剂,出于抑制界面处的反射所致的可视性的降低、并且将各构件间粘接固定的目的,使用粘合剂、UV固化型粘接剂(例如参照专利文献1)。
上述的层间填充构成在经常在室外使用的手机等移动设备用途中的采用正在拓展。另外,由于近年来的对可视性的要求的提高,在汽车导航装置等车载用途中,也正在研究采用在图像显示面板表面配置前面板、将面板与前面板之间用粘合剂层等填充的层间填充构成。
但是有过报告,在采用此种构成的情况下,加热耐久试验(在95℃条件下200小时等)的结果是,在偏振板面内中央部可以观察到透射率的显著降低,另一方面,若是单独的偏振板,则即使在95℃条件下放置1000小时,也观察不到显著的透射率的降低。根据这些结果也有过报告,高温环境下的偏振板的透射率的显著降低是将采用层间填充构成的图像显示装置暴露于高温环境中的情况下特有的问题,所述层间填充构成是将偏振板的一面与图像显示单元贴合、将另一面与触控面板、前面板等透明构件贴合的构成(专利文献2)。
此外,上述专利文献2中,在层间填充构成中透射率显著地降低的偏振板在拉曼分光测定中在1100cm-1附近(来自于=C-C=键)及1500cm-1附近(来自于-C=C-键)具有峰,因此认为形成了多烯结构(-C=C)n-,推测是因为构成偏振元件的聚乙烯醇因脱水而被多烯化后产生(专利文献2、[0012]段)。
专利文献2中作为该问题的解决对策,提出如下的方法,即,将偏振板的每单位面积的水分量设为规定量以下,并且将与偏振元件相邻的透明保护膜的饱和吸水量设为规定量以下,由此来抑制透射率的降低。
然而,即使采用此种方法,高温耐久试验中的透射率降低的抑制效果也不充分。
现有技术文献
专利文献
专利文献1:日本特开平11-174417号公报
专利文献2:日本特开2014-102353号公报
发明内容
发明所要解决的课题
本发明提供以下的偏振板、图像显示装置、以及偏振板的制造方法。
〔1〕一种偏振板,其具有使聚乙烯醇系树脂层吸附碘并使碘取向而成的偏振元件、和透明保护膜,
所述偏振板具有包含选自脲、脲衍生物、硫脲及硫脲衍生物中的至少一种脲系化合物的含有脲系化合物的层,
所述偏振元件的含水率为温度20℃且相对湿度30%的平衡含水率以上,并且为温度20℃相对湿度50%的平衡含水率以下。
〔2〕一种偏振板,其具有使聚乙烯醇系树脂层吸附碘并使碘取向而成的偏振元件、和透明保护膜,
所述偏振板具有包含选自脲、脲衍生物、硫脲及硫脲衍生物中的至少一种脲系化合物的含有脲系化合物的层,
所述偏振板的含水率为温度20℃且相对湿度30%的平衡含水率以上,并且为温度20℃相对湿度50%的平衡含水率以下。
〔3〕根据〔1〕或〔2〕中记载的偏振板,其中,所述含有脲系化合物的层含有选自脲衍生物及硫脲衍生物中的至少一种脲系化合物。
〔4〕根据〔1〕~〔3〕中任一项记载的偏振板,其中,所述含有脲系化合物的层与所述偏振元件接触。
〔5〕根据〔1〕~〔4〕中任一项记载的偏振板,其中,所述含有脲系化合物的层为粘接剂层。
〔6〕根据〔5〕中记载的偏振板,其中,所述含有脲系化合物的层包含聚乙烯醇系树脂。
〔7〕根据〔6〕中记载的偏振板,其中,在所述含有脲系化合物的层中,所述脲系化合物的合计含量相对于所述聚乙烯醇系树脂100质量份为0.1质量份以上且400质量份以下。
〔8〕根据〔5〕~〔7〕中任一项记载的偏振板,其中,所述含有脲系化合物的层的厚度为0.01~7μm。
〔9〕一种偏振板,其具有使聚乙烯醇系树脂层吸附碘并使碘取向而成的偏振元件、和透明保护膜,
所述偏振元件包含选自脲、脲衍生物、硫脲及硫脲衍生物中的至少一种脲系化合物,
所述偏振元件的含水率为温度20℃且相对湿度30%的平衡含水率以上,并且为温度20℃相对湿度50%的平衡含水率以下。
〔10〕一种偏振板,其具有使聚乙烯醇系树脂层吸附碘并使碘取向而成的偏振元件、和透明保护膜,
所述偏振元件包含选自脲、脲衍生物、硫脲及硫脲衍生物中的至少一种脲系化合物,
所述偏振板的含水率为温度20℃且相对湿度30%的平衡含水率以上,并且为温度20℃相对湿度50%的平衡含水率以下。
〔11〕根据〔1〕~〔10〕中任一项记载的偏振板,其中,所述偏振板被用于图像显示装置,
在所述图像显示装置中,与所述偏振板的两面接触地设有空气层以外的层。
〔12〕一种图像显示装置,其具有图像显示单元、层叠于所述图像显示单元的可视侧表面的第1粘合剂层、和层叠于所述第1粘合剂层的可视侧表面的〔1〕~〔11〕中任一项记载的偏振板。
〔13〕根据〔12〕中记载的图像显示装置,其还具有层叠于所述偏振板的可视侧表面的第2粘合剂层、和层叠于所述第2粘合剂层的可视侧表面的透明构件。
〔14〕根据〔13〕中记载的图像显示装置,其中,所述透明构件为玻璃板或透明树脂板。
〔15〕根据〔13〕中记载的图像显示装置,其中,所述透明构件为触控面板。
〔16〕一种偏振板的制造方法,是〔1〕或〔9〕中记载的偏振板的制造方法,
所述制造方法具有含水率调整工序,将所述偏振元件的含水率调整为温度20℃且相对湿度30%的平衡含水率以上、并且为温度20℃相对湿度50%的平衡含水率以下。
〔17〕一种偏振板的制造方法,是〔2〕或〔10〕中记载的偏振板的制造方法,
所述制造方法具有含水率调整工序,将所述偏振板的含水率调整为温度20℃且相对湿度30%的平衡含水率以上、并且为温度20℃相对湿度50%的平衡含水率以下。
发明效果
根据本发明,能够提供一种偏振板,即使在用于层间填充构成的图像显示装置的情况下,高温环境下的透射率的降低也小,高温耐久性优异,此外,提供一种图像显示装置,通过使用本发明的偏振板,抑制了高温环境下的透射率降低。
具体实施方式
《第1实施方式》
本发明的第1实施方式的偏振板具有使聚乙烯醇系树脂层吸附碘并使碘取向而成的偏振元件、包含选自脲、脲衍生物、硫脲及硫脲衍生物中的至少一种脲系化合物的脲系化合物层、和透明保护膜。本实施方式的偏振板具有下述的(a)及(b)的至少一方的特征。
(a)偏振元件的含水率为温度20℃且相对湿度30%的平衡含水率以上,并且为温度20℃相对湿度50%的平衡含水率以下。
(b)偏振板的含水率为温度20℃且相对湿度30%的平衡含水率以上,并且为温度20℃相对湿度50%的平衡含水率以下。
通过使本实施方式的偏振板具有上述的(a)及(b)的至少一方的特征,而且具有含有脲系化合物的层,由此,即使在作为层间填充构成的图像显示装置的构成要素长时间暴露于高温环境下的情况下,也能够抑制单体透射率的降低。通过使本实施方式的偏振板具有含有脲系化合物的层,即使将偏振板暴露于高温环境下,也能够抑制偏振度的降低。在将两个偏振板以形成正交尼科尔棱镜的关系的方式配置使用的情况下,若偏振板的偏振度降低,则容易产生漏光(以下也称作“正交漏光(日文:ク口ス拔け)”),然而根据本发明,即使暴露于高温环境下,偏振度也不易降低,因此也易于抑制正交漏光。
[偏振元件]
作为本发明的使聚乙烯醇(以后也称作PVA)系树脂层吸附碘并使碘取向而成的偏振元件,可以使用公知的偏振元件。作为此种偏振元件,一般通过使用PVA系树脂膜、将该PVA系树脂膜用碘染色、并进行单轴拉伸而形成。
如前所述,PVA系树脂一般使用将聚乙酸乙烯酯系树脂皂化而得的树脂。皂化度为约85摩尔%以上,优选为约90摩尔%以上,更优选为约99摩尔%~100摩尔%。作为聚乙酸乙烯酯系树脂,除了可以举出作为乙酸乙烯酯的均聚物的聚乙酸乙烯酯以外,还可以举出乙酸乙烯酯与能够与之共聚的其他单体的共聚物,例如可以举出乙烯-乙酸乙烯酯共聚物等。作为能够共聚的其他单体,例如可以举出不饱和羧酸类、烯烃类、乙烯基醚类、不饱和磺酸类等。作为PVA系树脂的聚合度,为1000~10000,优选为1500~5000。该PVA系树脂可以被改性,例如可以为由醛类改性了的聚乙烯醇缩甲醛、聚乙烯醇缩乙醛、聚乙烯醇缩丁醛等。
偏振元件的制造方法没有特别限定,典型的方法是将预先卷绕成卷筒状的聚乙烯醇系树脂膜送出后进行拉伸、染色、交联等而制作的方法;包括制作聚乙烯醇系树脂与拉伸用树脂基材的层叠体、并在层叠体的状态下进行拉伸的工序的方法。本发明中,可以使用这些方法的任选的方法。对于这些偏振元件的制造方法,记载于日本特开2014-48497号公报的[0109]~[0128]段中,本实施方式中可以使用这些方法。另外,本实施方式的偏振元件的厚度优选为3~35μm,更优选为4~30μm,进一步优选为5~25μm。
(特征(a))
在具有特征(a)的情况下,偏振元件的含水率为温度20℃相对湿度30%的平衡含水率以上,并且为温度20℃相对湿度50%的平衡含水率以下。更优选为温度20℃相对湿度45%的平衡含水率以下,进一步优选为温度20℃相对湿度42%的平衡含水率以下,最优选为温度20℃相对湿度38%的平衡含水率以下。若小于温度20℃相对湿度30%的平衡含水率,则偏振元件的操作性降低,易于破裂。若偏振元件的含水率大于温度20℃相对湿度50%的平衡含水率,则偏振元件的透射率易于降低。推测是因为,若偏振片的含水率高,则PVA系树脂的多烯化易于推进。偏振元件的上述含水率是偏振板中的偏振元件的含水率。
作为确认偏振元件的含水率是否为温度20℃相对湿度30%的平衡含水率以上、并且为温度20℃相对湿度50%的平衡含水率以下的范围内的方法,可以例示出以下的方法。在调整为上述温度和上述相对湿度的范围的环境中保管偏振元件、在一定时间没有质量的变化时则视为与该环境达到平衡。或者预先计算出调整为上述温度和上述相对湿度的范围的环境的偏振元件的平衡含水率,并通过对比偏振元件的含水率与预先计算出的平衡含水率来进行确认。
作为制造含水率为温度20℃相对湿度30%的平衡含水率以上、并且为温度20℃相对湿度50%的平衡含水率以下的偏振元件的方法,没有特别限定,例如可以举出在调整为上述温度和上述相对湿度的范围的环境中将偏振元件保管10分钟以上且3小时以下的方法、或在30℃以上且90℃以下进行加热处理的方法。
作为制造上述含水率的偏振元件的其他的优选的方法,可以举出将在偏振元件的至少一面层叠有保护膜的层叠体、或使用偏振元件形成的偏振板在调整为上述温度和上述相对湿度的范围的环境中保管10分钟以上且120小时以下的方法;或者在30℃以上且90℃以下进行加热处理的方法。在制作采用层间填充构成的图像显示装置时,可以将在图像显示单元层叠有偏振板的图像显示面板在调整为上述温度和上述相对湿度的范围的环境中保管10分钟以上且3小时以下、或者在30℃以上且90℃以下进行加热后,贴合前面板。
对于偏振元件的含水率,优选在单独的偏振元件中或者是偏振元件与保护膜的层叠体、且在为了形成偏振板而使用的材料阶段,将含水率调整为上述数值范围。在形成偏振板后调整含水率的情况下,卷曲变得过大,在向图像显示单元贴合时有易于产生不佳状况的情况。通过使用在形成偏振板前的材料阶段调整为上述含水率的偏振元件来形成偏振板,可以容易地形成具备含水率满足上述数值范围的偏振元件的偏振板。也可以在将偏振板贴合于图像显示单元的状态下,将偏振板中的偏振元件的含水率调整为上述数值范围。该情况下,由于偏振板被贴合于图像显示单元,因此不易产生卷曲。
(特征(b))
在具有特征(b)的情况下,偏振板的含水率为温度20℃相对湿度30%的平衡含水率以上,并且为温度20℃相对湿度50%的平衡含水率以下。偏振板的含水率优选为温度20℃相对湿度45%的平衡含水率以下,更优选为温度20℃相对湿度42%的平衡含水率以下,进一步优选为温度20℃相对湿度38%的平衡含水率以下。若偏振板的含水率小于温度20℃相对湿度30%的平衡含水率,则偏振板的操作性降低,容易破裂。若偏振板的含水率大于温度20℃相对湿度50%的平衡含水率,则偏振元件的透射率容易降低。推测是因为,若偏振板的含水率高,则PVA系树脂的多烯化易于推进。
作为确认偏振板的含水率是否为温度20℃相对湿度30%的平衡含水率以上、并且为温度20℃相对湿度50%的平衡含水率以下的范围内的方法,可以例示出以下的方法。在调整为上述温度和上述相对湿度的范围的环境中保管,在一定时间没有质量的变化时视为与环境达到平衡。或者预先计算出调整为上述温度和上述相对湿度的范围的环境的偏振板的平衡含水率,通过对比偏振板的含水率与预先计算出的平衡含水率来确认。
作为制造含水率为温度20℃相对湿度30%的平衡含水率以上、并且为温度20℃相对湿度50%的平衡含水率以下的偏振板的方法,没有特别限定,例如可以举出在调整为上述温度和上述相对湿度的范围的环境中将偏振板保管10分钟以上且3小时以下的方法、或者在30℃以上且90℃以下进行加热处理的方法。
在制作采用层间填充构成的图像显示装置时,可以将偏振板层叠于图像显示单元,将所得的图像显示面板在调整为上述温度和上述相对湿度的范围的环境中保管10分钟以上且3小时以下、或者在30℃以上且90℃以下加热后,贴合前面板。
[含有脲系化合物的层]
本发明的偏振板具有含有选自脲、脲衍生物、硫脲及硫脲衍生物中的至少一种脲系化合物的含有脲系化合物的层。含有脲系化合物的层只要是含有着脲系化合物的层,就不受限定,然而例如可以举出粘接剂层、固化层。含有脲系化合物的层可以与偏振元件接触,也可以不接触,从能够进一步抑制高温环境下的透射率的降低的观点出发,优选与偏振元件接触。
本发明中,从生产率的观点考虑,优选粘接剂层为含有脲系化合物的层。粘接剂层由以下的粘接剂形成。作为属于含有脲系化合物的层的粘接剂层,可以例示出将偏振元件与保护膜贴合的粘接剂层。需要说明的是,对于含有脲系化合物的层为粘接剂层以外的情况的构成将在后面叙述。
<粘接剂层>
形成用于在偏振元件贴合保护膜的粘接剂层的粘接剂可以使用任选的恰当的粘接剂。具体而言,作为粘接剂,可以使用水系粘接剂、溶剂系粘接剂、活性能量射线固化型等,然而优选为水系粘接剂。
在粘接剂层为含有脲系化合物的层的情况下,在粘接剂中含有选自脲、脲衍生物、硫脲及硫脲衍生物中的至少一种脲系化合物。
上述粘接剂的涂布时的厚度可以设定为任选的恰当的值。例如,以在固化后或加热(干燥)后获得具有所期望的厚度的粘接剂层的方式设定。粘接剂层的厚度优选为0.01μm~7μm,更优选为0.01μm~5μm,进一步优选为0.01μm~2μm,最优选为0.01μm~1μm。
(水系粘接剂)
另外,作为上述水系粘接剂,可以采用任选的恰当的水系粘接剂。其中,优选使用包含PVA系树脂的水系粘接剂(PVA系粘接剂)。从粘接性的方面出发,水系粘接剂中含有的PVA系树脂的平均聚合度优选为100~5500左右,更优选为1000~4500。从粘接性的方面出发,平均皂化度优选为85摩尔%~100摩尔%左右,更优选为90摩尔%~100摩尔%。
作为上述水系粘接剂中含有的PVA系树脂,优选含有乙酰乙酰基的PVA系树脂,其理由是因为,PVA系树脂层与保护膜的密合性优异,耐久性优异。含有乙酰乙酰基的PVA系树脂例如可以通过利用任选的方法使PVA系树脂与双烯酮反应而得到。含有乙酰乙酰基的PVA系树脂的乙酰乙酰基改性度在代表性的情况下为0.1摩尔%以上,优选为0.1摩尔%~20摩尔%左右。
上述水系粘接剂的树脂浓度优选为0.1重量%~15重量%,更优选为0.5重量%~10重量%。
(交联剂、溶剂)
本发明中可以优选使用的水溶性PVA系粘接剂也可以在上述的PVA系树脂、脲系化合物以外还根据需要含有交联剂。可以使用公知的交联剂作为交联剂。例如可以举出水溶性环氧化合物、二醛、异氰酸酯等。
在PVA系树脂为含有乙酰乙酰基的PVA系树脂的情况下,作为交联剂优选为乙二醛、乙醛酸盐、羟甲基三聚氰胺中的任意者,更优选为乙二醛、乙醛酸盐的任意者,特别优选为乙二醛。
另外,本发明的水溶性PVA系粘接剂可以含有有机溶剂。该情况下,从与水具有混溶性的方面考虑优选醇类,在醇类中更优选为甲醇或乙醇。
另外,本发明中,脲衍生物的一部分相对于水的溶解度低,然而相对于醇的溶解度充分。该情况下,在溶解于醇中、制备出脲衍生物的醇溶液后,将脲衍生物的醇溶液添加到PVA水溶液中,制备粘接剂,该做法也是优选的方式之一。
(活性能量射线固化型粘接剂)
作为上述活性能量射线固化型粘接剂,只要是能够通过活性能量射线的照射而固化的粘接剂,则可以使用任选的恰当的粘接剂。作为活性能量射线固化型粘接剂,例如可以举出紫外线固化型粘接剂、电子束固化型粘接剂等。作为活性能量射线固化型粘接剂的固化型的具体例,可以举出自由基固化型、阳离子固化型、阴离子固化型、它们的组合(例如自由基固化型与阳离子固化型的共混)。
作为上述活性能量射线固化型粘接剂,例如可以举出含有具有(甲基)丙烯酸酯基、(甲基)丙烯酰胺基等自由基聚合性基团的化合物(例如单体和/或低聚物)作为固化成分的粘接剂。上述活性能量射线固化型粘接剂及其固化方法的具体例例如记载于日本特开2012-144690号公报中。
(脲系化合物)
在粘接剂层为含有脲系化合物的层的情况下,粘接剂层含有选自脲、脲衍生物、硫脲及硫脲衍生物中的至少1种脲系化合物。
作为使粘接剂层中含有脲系化合物的方法,优选使上述的粘接剂含有脲系化合物。需要说明的是,在从粘接剂经由干燥工序等形成粘接剂层的过程中,脲系化合物的一部分可以从粘接剂层移动到偏振元件等。
在脲系化合物中有水溶性的脲系化合物和难水溶性的脲系化合物,本发明中无论使用哪种脲系化合物都可以。在水溶性粘接剂中使用难水溶性脲系化合物的情况下,优选以在形成粘接剂层后不发生浊度升高等的方式来设计分散方法。
在粘接剂为含有PVA树脂的水系粘接剂的情况下,脲系化合物的添加量优选相对于100质量份的PVA为0.1~400质量份,更优选为1~200质量份,进一步优选为3~100质量份。
(脲衍生物)
脲衍生物是脲分子的4个氢原子的至少1个由取代基取代了的化合物。该情况下,对于取代基没有特别限制,优选为包含碳原子、氢原子及氧原子的取代基。
作为脲衍生物的具体例,就单取代脲而言,可以举出甲基脲、乙基脲、丙基脲、丁基脲、异丁基脲、N-十八烷基脲、2-羟基乙基脲、羟基脲、乙酰基脲、烯丙基脲、2-丙炔基脲、环己基脲、苯基脲、3-羟基苯基脲、(4-甲氧基苯基)脲、苄基脲、苯甲酰基脲、邻甲苯基脲、对甲苯基脲。
就二取代脲而言,可以举出1,1-二甲基脲、1,3-二甲基脲、1,1-二乙基脲、1,3-二乙基脲、1,3-二(羟基甲基)脲、1,3-叔丁基脲、1,3-二环己基脲、1,3-二苯基脲、1,3-二(4-甲氧基苯基)脲、1-乙酰基-3-甲基脲、2-咪唑烷酮(乙烯脲)、四氢-2-嘧啶酮(丙烯脲)。
就四取代脲而言,可以举出四甲基脲、1,1,3,3-四乙基脲、1,1,3,3-四丁基脲、1,3-二甲氧基-1,3-二甲基脲、1,3-二甲基-2-咪唑烷酮、1,3-二甲基-3,4,5,6-四氢-2(1H)-嘧啶酮。
(硫脲衍生物)
硫脲衍生物是硫脲分子的4个氢原子的至少1个由取代基取代了的化合物。该情况下,对于取代基没有特别限制,优选为包含碳原子、氢原子及氧原子的取代基。
作为硫脲衍生物的具体例,就单取代硫脲而言,可以举出N-甲基硫脲、乙基硫脲、丙基硫脲、异丙基硫脲、1-丁基硫脲、环己基硫脲、N-乙酰基硫脲、N-烯丙基硫脲、(2-甲氧基乙基)硫脲、N-苯基硫脲、(4-甲氧基苯基)硫脲、N-(2-甲氧基苯基)硫脲、N-(1-萘基)硫脲、(2-吡啶基)硫脲、邻甲苯基硫脲、对甲苯基硫脲。
就二取代硫脲而言,可以举出1,1-二甲基硫脲、1,3-二甲基硫脲、1,1-二乙基硫脲、1,3-二乙基硫脲、1,3-二丁基硫脲、1,3-二异丙基硫脲、1,3-二环己基硫脲、N,N-二苯基硫脲、N,N’-二苯基硫脲、1,3-二(邻甲苯基)硫脲、1,3-二(对甲苯基)硫脲、1-苄基-3-苯基硫脲、1-甲基-3-苯基硫脲、N-烯丙基-N’-(2-羟基乙基)硫脲、乙烯硫脲。
就三取代硫脲而言,可以举出三甲基硫脲,就四取代硫脲而言,可以举出四甲基硫脲、1,1,3,3-四乙基硫脲。
从用于层间填充构成的图像显示装置时能够抑制高温环境下的透射率的降低、并且偏振度的降低少的方面(正交漏光得到抑制的方面)考虑,在脲系化合物中,优选脲衍生物或硫脲衍生物,更优选脲衍生物。在脲衍生物中,优选为单取代脲或二取代脲,更优选为单取代体。二取代脲中有1,1-取代脲和1,3-取代脲,更优选1,3-取代脲。
[透明保护膜]
本发明中使用的透明保护膜(以后也简称为“保护膜”。)经由粘接剂层贴合于偏振元件的至少一面侧。该透明保护膜贴合于偏振元件的一面或两面,更优选贴合于两面。在一个方式中,保护膜经由作为含有脲系化合物的层的粘接剂层贴合于偏振元件。
另外,在偏振元件的两面经由粘接剂层贴合有透明保护膜的构成中,在偏振元件两面的粘接剂层当中,可以仅一面的粘接剂层为本发明的含有脲系化合物的层,然而更优选两面的粘接剂层均为本发明的含有脲系化合物的层。
近年来,为了响应偏振板的薄型化的要求,开发出了仅在偏振元件的一面具有保护膜的偏振板。在该构成中,也优选经由作为本发明的含有脲系化合物的层的粘接剂层层叠保护膜。
作为仅在偏振元件的一面具有保护膜的偏振板的制作方法,可以考虑首先制作出在两面经由粘接剂层贴合有保护膜的偏振板后、剥离一方的保护膜的方法,在使用此种制造方法的情况下,仅哪一方的粘接剂层为本发明的含有脲系化合物的层都可以,更优选在偏振元件的两面使用本发明的含有脲系化合物的层。
另外,在本发明的含有脲系化合物的层作为粘接剂层仅在偏振元件的一面使用的情况下,优选不进行剥离的膜侧的粘接剂层为本发明的含有脲系化合物的层。
保护膜可以同时具有其他的光学功能,也可以被制成还层叠有其他的层的层叠结构。
从光学特性的观点出发,优选此时的保护膜的膜厚薄,然而若过薄则强度降低,加工性差。作为恰当的膜厚,为5~100μm,优选为10~80μm,更优选为15~70μm。
保护膜可以使用纤维素酰化物系树脂膜、包含聚碳酸酯系树脂的膜、包含降冰片烯等环烯烃系树脂的膜、(甲基)丙烯酸系聚合物膜、聚对苯二甲酸乙二醇酯等聚酯系树脂膜等膜。
在偏振元件的两面具有保护膜的构成的情况下,在使用PVA粘接剂等水系粘接剂进行贴合时,从透湿度的方面考虑优选至少一侧的保护膜为纤维素酰化物系膜或(甲基)丙烯酸系聚合物膜的任意者,其中优选纤维素酰化物膜。
作为至少一方的保护膜,出于视角补偿等目的可以具备相位差功能,该情况下,可以膜本身具有相位差功能,也可以另行具有相位差层,也可以是两者的组合。
需要说明的是,虽然对将具备相位差功能的膜经由粘接剂直接贴合于偏振元件的构成进行了说明,然而也可以是夹隔着贴合于偏振元件的其他的保护膜经由粘合剂或粘接剂贴合的构成。
[偏振板的制造方法]
本实施方式的偏振板的制造方法具有层叠工序和含水率调整工序,所述层叠工序中,将偏振元件、与包含选自脲、脲衍生物、硫脲及硫脲衍生物中的至少一种脲系化合物的含有脲系化合物的层层叠的层叠工序。含水率调整工序中,在制造具有特征(a)的偏振板的情况下,调整偏振元件的含水率,使得偏振元件的含水率为温度20℃相对湿度30%的平衡含水率以上,并且为温度20℃相对湿度50%的平衡含水率以下。偏振元件的含水率可以依照上述的偏振元件的含水率的记载来调整。含水率调整工序中,在制造具有特征(b)的偏振板的情况下,调整偏振板的含水率,使得偏振板的含水率为温度20℃相对湿度30%的平衡含水率以上,并且为温度20℃相对湿度50%的平衡含水率以下。偏振板的含水率可以依照上述的偏振板的含水率的记载来调整。层叠工序及含水率调整工序的顺序没有限定,另外也可以并行地进行层叠工序和含水率调整工序。
[图像显示装置的构成]
本发明的偏振板用于液晶显示装置、有机EL显示装置等各种图像显示装置。对于图像显示装置,在为以使偏振板的两面接触空气层以外的层的方式构成的层间填充构成的情况下,在高温环境下透射率容易降低。在使用了本发明的偏振板的图像显示装置中,即使是层间填充构成,也能够抑制高温环境下的偏振板的透射率的降低。作为图像显示装置,可以例示出具有图像显示单元、层叠于图像显示单元的可视侧表面的第1粘合剂层、和层叠于第1粘合剂层的可视侧表面的偏振板的构成。该图像显示装置可以还具有层叠于偏振板的可视侧表面的第2粘合剂层、和层叠于第2粘合剂层的表面的透明构件。特别是,本发明的偏振板可以合适地用于具有如下的层间填充构成的图像显示装置,即,在图像显示装置的可视侧配置有透明构件,偏振板与图像显示单元由第1粘合剂层贴合,偏振板与透明构件由第2粘合剂层贴合。本说明书中,有时将第1粘合剂层及第2粘合剂层的任意一方或双方简称为“粘合剂层”。需要说明的是,作为偏振板与图像显示单元的贴合、偏振板与透明构件的贴合中使用的构件,并不限定于粘合剂层,也可以是粘接剂层。
<图像显示单元>
作为图像显示单元,可以举出液晶单元、有机EL单元。作为液晶单元,可以使用利用外来光的反射型液晶单元、利用来自背光等光源的光的透射型液晶单元、利用来自外部的光和来自光源的光两者的半透射半反射型液晶单元的任意者。在液晶单元为利用来自光源的光的液晶单元的情况下,图像显示装置(液晶显示装置)在图像显示单元(液晶单元)的与可视侧相反的一侧也配置偏振板,此外还配置光源。光源侧的偏振板与液晶单元优选经由恰当的粘合剂层贴合。作为液晶单元的驱动方式,例如可以使用VA模式、IPS模式、TN模式、STN模式、弯曲取向(π型)等任选类型的驱动方式。
作为有机EL单元,可以合适地使用在透明基板上依次层叠透明电极、有机发光层和金属电极而形成发光体(有机电致发光发光体)的有机EL单元等。有机发光层是各种有机薄膜的层叠体,例如可以采用包含三苯基胺衍生物等的空穴注入层与包含蒽等荧光性的有机固体的发光层的层叠体、这些发光层与包含苝衍生物等的电子注入层的层叠体、或者空穴注入层、发光层、以及电子注入层的层叠体等各种层构成。
<图像显示单元与偏振板的贴合>
在图像显示单元与偏振板的贴合中,可以合适地使用粘合剂层(粘合片)。其中,从操作性等观点出发,优选将在偏振板的一个面附设有粘合剂层的带有粘合剂层的偏振板与图像显示单元贴合的方法。粘合剂层向偏振板的附设可以利用恰当的方式进行。作为其例子,例如可以举出:制备在由甲苯、乙酸乙酯等恰当的溶剂的单独物或混合物形成的溶剂中溶解或分散有基础聚合物或其组合物的10~40重量%左右的粘合剂溶液、并将其利用流延方式、涂布方式等恰当的展开方式直接附设于偏振板上的方式;或者依照上文在隔片上形成粘合剂层并将其转印到偏振板的方式等。
<粘合剂层>
对于粘合剂层,记载于日本特开2018-025765号公报的[0103]~[0143]段中,本发明中可以使用这些粘合剂。
<透明构件>
作为配置于图像显示装置的可视侧的透明构件,可以举出前面板(窗层)、触控面板等。作为前面板,使用具有恰当的机械强度及厚度的前面板。作为此种前面板,例如可以举出丙烯酸系树脂、聚碳酸酯系树脂之类的透明树脂板、或玻璃板等。也可以在前面板的可视侧层叠防反射层等功能层。另外,在前面板为透明树脂板的情况下,可以为了提高物理强度而层叠硬涂层、为了降低透湿度而层叠低透湿层。
作为触控面板,可以使用电阻膜方式、静电电容方式、光学方式、超声波方式等各种触控面板、具备触摸传感器功能的玻璃板、透明树脂板等。在使用静电电容方式的触控面板作为透明构件的情况下,优选相对于触控面板进一步在可视侧设置由玻璃或透明树脂板形成的前面板。
<偏振板与透明构件的贴合>
在偏振板与透明构件的贴合中,可以合适地使用粘合剂或UV固化型的粘接剂。在使用粘合剂的情况下,可以利用恰当的方式进行粘合剂的附设。作为具体的附设方法,例如可以举出前述的图像显示单元与偏振板的贴合中使用的粘合剂层的附设方法。
在使用UV固化型的粘接剂的情况下,出于防止固化前的粘接剂溶液展开的目的,可以合适地使用如下的方法,即,以包围图像显示面板上的周缘部的方式设置围堰材料,在围堰材料上载放透明构件,注入粘接剂溶液。在粘接剂溶液的注入后,根据需要进行对准及脱泡,然后照射UV光而进行固化。
下面,对粘接剂层以外的含有脲系化合物的层进行说明。
[含有脲系化合物的层(粘接剂层以外)]
含有脲系化合物的层优选具有至少1种脲系化合物、和粘结剂。作为粘结剂,可以举出聚合物粘结剂、热固型树脂粘结剂、活性能量射线固化型树脂粘结剂等,本发明中可以优选使用任意的粘结剂。
含有脲系化合物的层的厚度优选为0.1~20μm,更优选为0.5~15μm,进一步优选为1~10μm。
含有脲系化合物的层可以直接层叠于偏振元件,也可以夹隔着其他层层叠,然而从易于抑制高温环境下的透射率降低的方面考虑,优选直接层叠于偏振元件地接触。
对于具有粘接剂层以外的含有脲系化合物的层的偏振板,从提高偏振板的物理强度的方面考虑,优选在偏振元件的至少一个面经由粘接剂层具有透明保护膜。此时,粘接剂层可以含有脲系化合物,也可以不含有,然而更优选含有。
如保护膜的说明中记载所示,近年来,为了响应偏振板的薄型化的要求,开发出了仅在偏振元件的一面具有保护膜的偏振板(以后也称作“单面带有保护膜的偏振板”。)。
此种构成中,出于提高物理强度等目的,进行过在偏振元件的不具有保护膜的面层叠固化层的尝试(例如日本特开2011-221185号公报)。
本实施方式中使此种固化层中含有脲系化合物而作为含有脲系化合物的层构成也是优选的方式之一。通常此种固化层由包含有机溶剂的固化性组合物形成,然而在日本特开2017-075986号公报的[0020]~[0042]段中记载有由活性能量射线固化性高分子组合物的水性溶液来形成此种固化层的方法。脲系化合物多为水溶性的,因此使此种组合物中含有水溶性的脲系化合物、形成含有脲系化合物的层也是本实施方式的优选的方式之一。
《第2实施方式》
本发明的第2实施方式的偏振板具有偏振元件和透明保护膜,所述偏振元件是使聚乙烯醇系树脂层吸附碘并使碘取向而成,并且包含选自脲、脲衍生物、硫脲及硫脲衍生物中的至少一种脲系化合物。本实施方式的偏振板具有下述的(a)及(b)的至少一方的特征。
(a)偏振元件的含水率为温度20℃且相对湿度30%的平衡含水率以上,并且为温度20℃相对湿度50%的平衡含水率以下。
(b)偏振板的含水率为温度20℃且相对湿度30%的平衡含水率以上,并且为温度20℃相对湿度50%的平衡含水率以下。
通过使本实施方式的偏振板具有上述的(a)及(b)的至少一方的特征,此外还使偏振元件含有脲系化合物,由此,即使在用于层间填充构成的图像显示装置、并且长时间暴露于高温环境下的情况下,也能够抑制单体透射率的降低。本实施方式的偏振板中,通过使偏振元件含有脲系化合物,即使将偏振板暴露于高温环境下,也能够抑制偏振度的降低,还易于抑制正交漏光。
上述的(a)及(b)的特征与第1实施方式的(a)及(b)的特征相同。
本实施方式的偏振元件的制作方法中,在第1实施方式中记载的偏振元件的制作方法中,具有使偏振元件中含有脲系化合物的工序。作为使偏振元件中含有脲系化合物的方法,通过经由在偏振元件的至少一面涂布含有脲系化合物的溶液并进行干燥的工序来制偏振元件,可以得到含有脲系化合物的偏振元件。在偏振元件的制造工序中,也可以利用将PVA系树脂层浸渍于含有脲系化合物的处理溶液中的方法、或者将处理溶液向PVA系树脂层喷雾、流下或滴下的方法等来使偏振元件中含有脲系化合物。其中,优选使用将PVA系树脂层浸渍于含有脲系化合物的处理溶液中的方法。
将PVA系树脂层浸渍于包含脲系化合物的处理溶液中的工序可以与偏振元件的制造方法中的溶胀、拉伸、染色、交联、清洗等工序同时地进行,也可以与这些工序分开地设置。使PVA系树脂层中含有脲系化合物的工序优选在将PVA系树脂层用碘染色后进行,更优选与染色后的交联工序同时地进行。根据此种方法,色调变化小,可以减小对偏振元件的光学特性的影响。
对于本实施方式的偏振元件中含有的脲系化合物的种类、含量,应用第1实施方式的含有脲系化合物的层中的说明。需要说明的是,也可以使用本实施方式的偏振元件作为第1实施方式的偏振板的偏振元件。对于本实施方式的偏振板的其他构成,除了第1实施方式的含有脲系化合物的层为任选的构成要素这一点以外,是与第1实施方式同样的构成。
[脲系化合物溶液]
本实施方式中使用的含有脲系化合物的溶液的溶剂优选为水、有机溶剂或它们的混合液,更优选为水或水与醇的混合溶剂的任意者。另外,在为水与醇的混合溶剂的情况下,优选醇为甲醇或乙醇的任意者。对于脲系化合物,如第1实施方式中说明所示,然而从干燥后脲系化合物不易在偏振元件的表面析出这一点考虑,优选脲系化合物为水溶性。
[偏振板的制造方法]
本实施方式的偏振板的制造方法具有含水率调整工序。对于含水率调整工序,与第1实施方式的偏振板的制造方法同样。
实施例
以下,基于实施例对本发明进行具体说明。以下的实施例中所示的材料、试剂、物质量及其比例、操作等只要不脱离本发明的主旨,就可以适当地进行变更。因而,本发明不受以下的实施例限定、限制。
(偏振元件1的制作)
将由平均聚合度约2400、皂化度99.9摩尔%以上的聚乙烯醇形成的厚度40μm的聚乙烯醇膜以干式方式单轴拉伸为约5倍,再保持张紧状态不变地在60℃的纯水中浸渍1分钟后,在碘/碘化钾/水的重量比为0.05/5/100的水溶液中在28℃浸渍60秒。其后,在碘化钾/硼酸/水的重量比为8.5/8.5/100的水溶液中在72℃浸渍300秒。接着,在用26℃的纯水清洗20秒后,在65℃干燥,得到在聚乙烯醇吸附有碘并使碘取向了的厚度15μm的偏振元件。
(粘接剂用PVA溶液的制备)
将含有乙酰乙酰基的改性PVA系树脂(三菱化学(株)制:GOHSENX Z-410)50g溶解于950g的纯水中,在90℃加热2小时后冷却到常温,得到粘接剂用PVA溶液。
(脲系化合物溶液的制备)
在纯水90g中添加脲10g,得到脲10重量%水溶液(溶液1)。同样地依照表1,将脲替换为表1中记载的脲系化合物,制备出脲溶液2~4。
[表1]
上文中使用的脲、甲基脲、乙基脲、四氢-2-嘧啶酮均使用东京化成工业株式会社的试剂。
(偏振板用粘接剂1的制备)
将上文中制备的粘接剂用PVA溶液、脲溶液1、纯水及甲醇配合,使得PVA浓度为3.0%、甲醇浓度为20%、脲浓度为0.5%,得到偏振板用粘接剂1。
(偏振板用粘接剂2的制备)
同样地将粘接剂用PVA溶液、表1中记载的脲溶液2、纯水及甲醇配合,使得PVA浓度为3.0%、甲醇浓度为20%、甲基脲浓度为0.7%,得到偏振板用粘接剂2。
(偏振板用粘接剂3的制备)
同样地将粘接剂用PVA溶液、表1中记载的脲溶液3、纯水及甲醇配合,使得PVA浓度为3.0%、甲醇浓度为20%、乙基脲浓度为1.0%,得到偏振板用粘接剂3。
(偏振板用粘接剂4的制备)
同样地将粘接剂用PVA溶液、表1中记载的脲溶液4、纯水及甲醇配合,使得PVA浓度为3.0%、甲醇浓度为20%、四氢-2-嘧啶酮浓度为1.5%,得到偏振板用粘接剂4。
(偏振板用粘接剂5的制备)
同样地将粘接剂用PVA溶液、纯水及甲醇配合,使得PVA浓度为3.0%、甲醇浓度为20%,得到偏振板用粘接剂5。
(纤维素酰化物膜的皂化)
将市售的纤维素酰化物膜TD40(富士胶片(株)制:膜厚40μm)在保持为55℃的1.5mol/L的NaOH水溶液(皂化液)中浸渍2分钟后,对膜进行水洗,其后,在25℃的0.05mol/L的硫酸水溶液中浸渍30秒后,再在流水下通过30秒而进行水洗浴,使膜为中性的状态。此后,反复进行3次利用气刀的除水,去掉水后在70℃的干燥区中滞留15秒而进行干燥,制作出进行了皂化处理的膜。
(偏振板1的制作)
在偏振元件1的两面经由偏振板用粘接剂1使用辊式贴合机贴合上文中制成的进行了皂化处理的纤维素酰化物膜,将干燥后的粘接剂层的厚度在两面都调整为100nm,然后在60℃干燥10分钟,得到两面带有纤维素酰化物膜的偏振板1。
(偏振板2~5的制作)
除了将偏振板用粘接剂1替换为偏振板用粘接剂2~5以外,与偏振板1同样地制作出偏振板2~5。
(偏振板(偏振元件)的含水率的调整)
将上文中得到的偏振板1~5在温度20℃、且相对湿度30%、35%、40%、45%、50%或55%的条件下保管72小时。在保管66小时、69小时及72小时时使用卡尔-费休法测定出含水率。在任意的湿度条件下,在保管66小时、69小时、72小时时含水率的值都没有变化。因而,可以将偏振板1~5的含水率视为与本实验例中使用的72小时的保管环境的平衡含水率相同。在偏振板的含水率在某个保管环境下达到平衡时,可以将偏振板中的偏振元件的含水率也同样地视为在该保管环境下达到平衡。另外,在偏振板中的偏振元件的含水率在某个保管环境下达到平衡时,可以将偏振板的含水率也同样地视为在该保管环境下达到平衡。
(光学层叠体1的制作)
以日本特开2018-025765号公报的实施例为参考,在上文中制作的偏振板1的两面涂布丙烯酸系粘合剂(制造商:LINTEC(株)、型号:#7),由此制作出在两面具有厚度为25μm的粘合剂层(第1粘合剂层和第2粘合剂层)的光学层叠体1。
(光学层叠体2~5的制作)
与光学层叠体1同样,除了将偏振板1替换为偏振板2~5以外,同样地制作出光学层叠体2~5。
[实施例1~9、比较例1~6]
实施例1~9、比较例1~6中,使用表2所示的光学层叠体,以使所用的光学层叠体的含水率为表2所示的环境的平衡含水率的方式,在温度20℃且相对湿度35%、40%、45%、50%或55%的条件下保管72小时。可以将光学层叠体的含水率视为与保管环境的含水率达到平衡,另外,可以将光学层叠体中的偏振板及偏振元件的含水率也视为与光学层叠体的含水率相同。
(检查用偏振板1)
仅在偏振板1的一面层叠丙烯酸系粘合剂(制造商:LINTEC(株)、型号:#7),制作出检查用偏振板1。将如此所述地制作的检查用偏振板1以使短边与吸收轴平行的方式裁割为50mm×100mm的大小,将所述粘合剂层的表面贴合于无碱玻璃〔商品名“EAGLE XG”、Corning公司制〕,制作出正交评价用样品1。
[高温耐久试验后的单体透射率评价(105℃)]
将上文中制作的光学层叠体1~5分别以使长边与吸收轴平行的方式裁割为50mm×100mm的大小,将第1粘合剂层及第2粘合剂层各自的表面贴合于无碱玻璃〔商品名“EAGLEXG”、Corning公司制〕,由此制作出评价样品。
对该评价样品在温度50℃、压力5kgf/cm2(490.3kPa)条件下实施1小时高压釜处理后,在温度23℃、相对湿度55%的环境下放置24小时。其后,测定透射率(初始值),在温度105℃的加热环境下保管,直至100~200小时为止地每隔50小时测定透射率。以透射率降低相对于初始值达到5%以上的时间为基础利用以下的基准进行评价。将所得的结果表示于表2中。
[高温耐久试验后的正交漏光的评价]
对高温耐久后的单体透射率评价样品进行200小时后的评价后,将上述光学层叠体和没有投入加热环境下的正交评价用样品1配置为正交尼科尔棱镜状态,载放在背光上。将周围遮光,利用目视,依照以下的基准评价正交漏光。需要说明的是,对于单体透射率降低5%以上的样品,由于有多烯化所致的着色,因此排除在正交漏光的评价对象之外。
[表2]
Claims (17)
1.一种偏振板,其具有使聚乙烯醇系树脂层吸附碘并使碘取向而成的偏振元件、和透明保护膜,
所述偏振板具有包含选自脲、脲衍生物、硫脲及硫脲衍生物中的至少一种脲系化合物的含有脲系化合物的层,
所述偏振元件的含水率为温度20℃且相对湿度30%的平衡含水率以上,并且为温度20℃相对湿度50%的平衡含水率以下。
2.一种偏振板,其具有使聚乙烯醇系树脂层吸附碘并使碘取向而成的偏振元件、和透明保护膜,
所述偏振板具有包含选自脲、脲衍生物、硫脲及硫脲衍生物中的至少一种脲系化合物的含有脲系化合物的层,
所述偏振板的含水率为温度20℃且相对湿度30%的平衡含水率以上,并且为温度20℃相对湿度50%的平衡含水率以下。
3.根据权利要求1或2所述的偏振板,其中,
所述含有脲系化合物的层含有选自脲衍生物及硫脲衍生物中的至少一种脲系化合物。
4.根据权利要求1~3中任一项所述的偏振板,其中,
所述含有脲系化合物的层与所述偏振元件接触。
5.根据权利要求1~4中任一项所述的偏振板,其中,
所述含有脲系化合物的层为粘接剂层。
6.根据权利要求5所述的偏振板,其中,
所述含有脲系化合物的层包含聚乙烯醇系树脂。
7.根据权利要求6所述的偏振板,其中,
在所述含有脲系化合物的层中,所述脲系化合物的合计含量相对于所述聚乙烯醇系树脂100质量份为0.1质量份以上且400质量份以下。
8.根据权利要求5~7中任一项所述的偏振板,其中,
所述含有脲系化合物的层的厚度为0.01μm~7μm。
9.一种偏振板,其具有使聚乙烯醇系树脂层吸附碘并使碘取向而成的偏振元件、和透明保护膜,
所述偏振元件包含选自脲、脲衍生物、硫脲及硫脲衍生物中的至少一种脲系化合物,
所述偏振元件的含水率为温度20℃且相对湿度30%的平衡含水率以上,并且为温度20℃相对湿度50%的平衡含水率以下。
10.一种偏振板,其具有使聚乙烯醇系树脂层吸附碘并使碘取向而成的偏振元件、和透明保护膜,
所述偏振元件包含选自脲、脲衍生物、硫脲及硫脲衍生物中的至少一种脲系化合物,
所述偏振板的含水率为温度20℃且相对湿度30%的平衡含水率以上,并且为温度20℃相对湿度50%的平衡含水率以下。
11.根据权利要求1~10中任一项所述的偏振板,其中,
所述偏振板被用于图像显示装置,
在所述图像显示装置中,与所述偏振板的两面接触地设有空气层以外的层。
12.一种图像显示装置,其具有图像显示单元、层叠于所述图像显示单元的可视侧表面的第1粘合剂层、和层叠于所述第1粘合剂层的可视侧表面的权利要求1~11中任一项所述的偏振板。
13.根据权利要求12所述的图像显示装置,其还具有层叠于所述偏振板的可视侧表面的第2粘合剂层、和层叠于所述第2粘合剂层的可视侧表面的透明构件。
14.根据权利要求13所述的图像显示装置,其中,
所述透明构件为玻璃板或透明树脂板。
15.根据权利要求13所述的图像显示装置,其中,
所述透明构件为触控面板。
16.一种偏振板的制造方法,是权利要求1或9所述的偏振板的制造方法,
所述制造方法具有含水率调整工序,将所述偏振元件的含水率调整为温度20℃且相对湿度30%的平衡含水率以上、并且为温度20℃相对湿度50%的平衡含水率以下。
17.一种偏振板的制造方法,是权利要求2或10所述的偏振板的制造方法,
所述制造方法具有含水率调整工序,将所述偏振板的含水率调整为温度20℃且相对湿度30%的平衡含水率以上、并且为温度20℃相对湿度50%的平衡含水率以下。