TW201833070A - 含有建基於環己烷１ ， ４ － 二酯之化合物的塑化劑組成物及含有彼之樹脂組成物 - Google Patents
含有建基於環己烷１ ， ４ － 二酯之化合物的塑化劑組成物及含有彼之樹脂組成物 Download PDFInfo
- Publication number
- TW201833070A TW201833070A TW106146000A TW106146000A TW201833070A TW 201833070 A TW201833070 A TW 201833070A TW 106146000 A TW106146000 A TW 106146000A TW 106146000 A TW106146000 A TW 106146000A TW 201833070 A TW201833070 A TW 201833070A
- Authority
- TW
- Taiwan
- Prior art keywords
- compound
- cyclohexane
- diester
- weight
- chemical formula
- Prior art date
Abstract
本發明係關於一種塑化劑組成物，於其中使經由轉酯化反應及氫化反應所製備的三種建基於環己烷1,4-二酯之化合物混合，其中二羧酸酯之烷基取代基為2-乙基己基及具有少於2-乙基己基之碳原子之丁基或異丁基，以致塑化劑組成物可就應力抗性、遷移抗性、塑化效率等而言展現優異性質，並同時在用於樹脂組成物時，維持優異水平的抗拉強度及伸長率。
Description
[0001] 相關申請案之交叉參照 [0002] 此申請案主張2017年1月04日提出申請之韓國專利申請案第10-2017-0001572號之優先權及權益，其揭示內容以引用彼之整體的方式併入本文中。 [0003] 本發明關於一種含有建基於環己烷1,4-二酯之化合物的塑化劑組成物及一種含有彼之樹脂組成物，且更特別關於一種含有衍生自具有一或多種組成之建基於對酞酸酯之化合物之經氫化化合物的塑化劑組成物及一種含有彼之樹脂組成物。
[0004] 傳統上，塑化劑經由醇及多羧酸(諸如鄰酞酸或己二酸)之間的反應形成酯。酯之商業上重要實例含有C8、C9、及C10醇之己二酸酯，諸如己二酸二(2-乙基己基)酯、己二酸二異壬基酯、及己二酸二異癸基酯；及C8、C9、及C10醇之鄰酞酸酯，諸如鄰酞酸二(2-乙基己基)酯、鄰酞酸二異壬基酯、及鄰酞酸二異癸基酯。 [0005] 具體地，鄰酞酸二(2-乙基己基)酯使用在經由乾混拌製造塑溶膠、玩具、膜、鞋子、塗料、地板材料、手套、壁紙、人造皮革、密封膠、篷布、汽車地板塗劑、家具、泡沫墊及隔音板，且也可用於生產用於PVC電纜及其他壓延塑料PVC產品的外部及絕緣材料。 [0006] 作為目前用作塑化劑的酯化合物，已主要使用鄰酞酸二(2-乙基己基)酯(DEHP)、鄰酞酸二異壬基酯(DINP)、鄰酞酸二(2-丙基庚基)酯(DPHP)、鄰酞酸二異癸基酯(DIDP)等。然而，這些化合物是破壞內分泌系統並且對人體有害的環境賀爾蒙，且取決於應用領域，也在改善產品性質，諸如樹脂的可加工性、吸收速度、揮發耗損、遷移耗損、熱安定性等上有限制。 [0007] 據此，有需要開發一種製備環境友善或非建基於鄰酞酸酯之化合物的方法，就各種性質而言，該化合物能充分改善現有產品性質，諸如樹脂的可加工性、吸收速度、硬度、抗拉強度(tensile strength)、伸長率、揮發耗損、遷移耗損、熱安定性等。
[0008] [技術問題] [0009] 因此，本發明的一目標為提供一種塑化劑組成物，其含有從一或多種建基於對酞酸酯組成物氫化而來之一或多種建基於環己烷1,4-二酯之化合物作為新穎化合物。本發明的另一目標為藉由使用含有建基於環己烷1,4-二酯之化合物的塑化劑組成物，提供一種樹脂產品，其中遷移抗性、塑化效率、應力抗性等以不犧牲機械性質(諸如抗拉強度及伸長率)之方式改善。 [0010] [技術手段] [0011] 根據本發明一具體實施例，提供了一種塑化劑組成物，其含有下列化學式1所示建基於環己烷1,4-二酯之化合物、下列化學式2所示建基於環己烷1,4-二酯之化合物、以及下列化學式3所示建基於環己烷1,4-二酯之化合物。 [0012][0013][0014][0015] 化學式1至3中，R1
為丁基或異丁基，及R2
為2-乙基己基。 [0016] 塑化劑組成物可含有，相對於塑化劑組成物的總重量，分別為0.5至70重量%、0.5至50重量%、及0.5至85重量%之化學式1所示建基於環己烷1,4-二酯之化合物、化學式2所示建基於環己烷1,4-二酯之化合物、以及化學式3所示建基於環己烷1,4-二酯之化合物。 [0017] 於塑化劑組成物中，化學式2所示建基於環己烷1,4-二酯之化合物與化學式3所示建基於環己烷1,4-二酯之化合物的總和與化學式1所示建基於環己烷1,4-二酯之化合物的重量比可為95:5至30:70。 [0018] 根據本發明另一具體實施例，提供了一種樹脂組成物，其含有100重量份的樹脂；以及5至150重量份的上述塑化劑組成物。 [0019] 樹脂可含有一或多種選自乙烯乙酸乙烯酯共聚物(ethylene vinyl acetate)、聚乙烯、聚丙烯、聚酮、聚氯乙烯、聚苯乙烯、聚胺甲酸酯、熱塑性彈性體及聚乳酸所組成群組者。 [0020] [有利效果] [0021] 根據本發明一具體實施例之經由轉酯化及氫化製備之塑化劑組成物，就抗拉強度、伸長率、遷移抗性、揮發抗性等而言可賦予優異性質，並在用於樹脂組成物時，提供具有優異應力抗性之樹脂產物。
[0022] [發明模式] [0023] 下文中，將更詳細描述本發明以幫助了解本發明。 [0024] 基於發明人已為了以最佳方式描述發明而適當地定義術語之概念的原則下，本說明書及申請專利範圍中所用術語及用語不應該被解釋為限於一般使用含義或字典中的含義，而應採與本發明的技術範疇一致的含義及概念來解釋。 [0025] 塑化劑組成物 [0026] 根據本發明一具體實施例，提供了一種塑化劑組成物，其含有下列化學式1所示建基於環己烷1,4-二酯之化合物。 [0027][0028] 化學式1中，R1
為丁基或異丁基，及R2
為2-乙基己基。 [0029] 如上所述，當塑化劑組成物含有其中丁基或異丁基鍵結至一側出現的酯基及2-乙基己基鍵結至另一側出現的酯基之建基於環己烷1,4-二酯之化合物時，施用塑化劑組成物之樹脂產物可具有改善之遷移能力及增加之塑化效率。 [0030] 為何如上所述可改善性質的理由是，鍵結至在與2-乙基己基相異側出現的酯基之烷基具有少於2-乙基己基之碳原子，而較佳的是鍵結至在與2-乙基己基相異側出現的酯基之烷基為具有四個碳原子的丁基或異丁基。因此，較佳的是，在塑化劑組成物中含有其中2-乙基己基鍵結至一側且丁基或異丁基鍵結至另一側之建基於環己烷1,4-二酯之化合物，諸如化學式1所示化合物。 [0031] 同時，當具有多於2-乙基己基之碳原子的烷基或芳族烴(諸如具有苯環之烴)而非脂族烴係鍵結至在與2-乙基己基相異側出現的酯基時，可能結果是，就壓縮下遷移、應力下遷移、塑化效率等而言，有不良性質，故而此情況可能是不佳的。 [0032] 此外，塑化劑組成物可進一步含有下列化學式2所示建基於環己烷1,4-二酯之化合物及下列化學式3所示建基於環己烷1,4-二酯之化合物。 [0033][0034][0035] 化學式2及3中，R1
為丁基或異丁基，及R2
為2-乙基己基。 [0036] 如上所述，當塑化劑組成物除含有化學式1所示建基於環己烷1,4-二酯之化合物外還含有化學式2及3所示建基於環己烷1,4-二酯之化合物時，可改善應力抗性，且也可改善塑化效率。 [0037] 塑化劑組成物可為含有一或多種建基於環己烷1,4-二酯之化合物(其中羧酸酯基鍵結至環己烷第1及第4位置的碳原子)之組成物。如上所述，將化學式1所示建基於環己烷1,4-二酯之化合物使用於塑化劑組成物得到改善之性質。然而，當化學式1所示化合物與化學式2及3所示化合物組合使用時，也可改善其他性質，並因此可達成具有普遍優異性質之塑化劑組成物。 [0038] 具體地，當塑化劑組成物含有一或多種化合物，例如三種建基於環己烷1,4-二酯之化合物時，塑化劑組成物可含有作為化學式1所示化合物之1,4-環己烷二羧酸丁基酯(2-乙基己基)酯(1,4-BEHCH)、作為化學式2所示化合物之1,4-環己烷二羧酸二丁基酯(1,4-DBCH)、及作為化學式3所示化合物之1,4-環己烷二羧酸二(2-乙基己基)酯(1,4-DEHCH)。 [0039] 替代地，塑化劑組成物可含有作為化學式1所示化合物之環己烷-1,4-二羧酸異丁基酯(2-乙基己基)酯(1,4-iBEHCH)、作為化學式2所示化合物之環己烷-1,4-二羧酸二異丁基酯(1,4-DiBCH)、及作為化學式3所示化合物之環己烷-1,4-二羧酸二(2-乙基己基)酯(1,4-DEHCH)。 [0040] 塑化劑組成物可含有，相對於塑化劑組成物的總重量，分別為0.5至70重量%、0.5至50重量%、及0.5至85重量%之化學式1所示建基於環己烷1,4-二酯之化合物、化學式2所示建基於環己烷1,4-二酯之化合物、及化學式3所示建基於環己烷1,4-二酯之化合物。 [0041] 較佳地，塑化劑組成物含有，相對於塑化劑組成物的總重量，分別為10至50重量%、0.5至50重量%、及35至80重量%之化學式1所示建基於環己烷1,4-二酯之化合物、化學式2所示建基於環己烷1,4-二酯之化合物、及化學式3所示建基於環己烷1,4-二酯之化合物。 [0042] 根據本發明之塑化劑組成物含有化學式1至3分別所示建基於環己烷1,4-二酯之化合物，如上所述。在此情況下，基於碳數及重量比測定之重量平均碳數可為約5.7至7.9，較佳6.2至7.7，且更佳6.4至7.5。當重量平均碳數在上述範圍內時，可獲製適當調整之吸收速度，可得到由於短熔融時間所致優異可加工性，且可改善塑化效率及遷移抗性同時機械強度(諸如抗拉強度及伸長率)維持在充分水平。 [0043] 文中所用術語「重量平均碳數」係指藉由使用各對酞酸酯組分之重量分率而將各對酞酸酯組分之鍵結到二酯基的兩個烷基之平均碳數平均所獲值。例如，重量平均碳數可藉下列方程式1界定。 [0044][0045] 於方程式1中，Nc
為重量平均碳數，Ci
為各對酞酸酯組分之鍵結到二酯基的兩個烷基的平均碳數，及wi
為各對酞酸酯組分之重量分率。 [0046] 具體地，當建基於對酞酸酯之化合物含有第1至第n組分，重量平均碳數可為藉由將第1組分的兩個烷基的平均碳數(C1
)乘上第1組分的重量分率(w1
)所獲值，第2組分的兩個烷基的平均碳數(C2
)乘上第2組分的重量分率(w2
)所獲值及將第n組分的兩個烷基的平均碳數(Cn
)乘上第n組分的重量分率(wn
)所獲值的和。 [0047] 例如，當分別以5重量%、40重量%及55重量%含有三種組分，即化學式2所示化合物、化學式1所示化合物、及化學式3所示化合物時，重量平均碳數為(0.05×4)+(0.4×6)+(0.55×8)=7。 [0048] 於塑化劑組成物中，化學式2所示建基於環己烷1,4-二酯之化合物與化學式3所示建基於環己烷1,4-二酯之化合物的總和與化學式1所示建基於環己烷1,4-二酯之化合物的重量比可為95:5至30:70。 [0049] 也就是說，化學式2所示化合物及化學式3所示化合物可為衍生自雙重攻擊酯化合物及轉酯化中反應殘質酯化合物之化合物，且可為非雜合型，這是因為相同烷基鍵結至環己烷的二羧酸酯基。化學式1所示化合物可為衍生自單一攻擊酯化合物之化合物，且可為雜合型。也就是說，可理解的是非雜合型化合物及雜合型化合物以重量比95:5至30:70含有。 [0050] 下面將描述雙重攻擊酯化合物、單一攻擊酯化合物及殘質酯化合物的詳細說明。 [0051] 當作為樹脂組成物的塑化劑使用時，塑化劑組成物可確保如傳統主要使用之塑化劑(諸如建基於鄰酞酸酯之化合物)所提供者相同水平的硬度、抗拉強度、及伸長率，且可得到減少之揮發耗損、顯著高遷移抗性、及優異應力抗性。 [0052] 製備塑化劑組成物的方法 [0053] 根據本發明一具體實施例，提供了一種製備塑化劑組成物之方法，其含有藉由以醇進行建基於二酯之化合物的轉酯化來製備建基於酯之組成物；以及藉由在金屬觸媒存在下進行建基於酯之組成物的氫化來製備建基於環己烷1,4-二酯之組成物，其中建基於二酯之化合物含有對酞酸二(2-乙基己基)酯(DEHTP)。 [0054] 製備塑化劑組成物的方法可含有，藉由以醇進行建基於二酯之化合物的轉酯化來製備建基於酯之組成物(其中混有三種建基於酯之化合物)。 [0055] 作為轉酯化中反應物使用之建基於二酯之化合物可為對酞酸二(2-乙基己基)酯，其中形成分支之2-乙基己基(它是其中乙基鍵結至在具有6個碳原子之己基的第2位置的碳之取代基)，可具有總共8個碳原子且於說明書中與「辛基」可互換使用。 [0056] 此外，醇可為任一種選自異丁醇及正丁醇所組成群組者。 [0057] 文中所用術語「轉酯化」是指如反應方案1所示醇與酯之間的反應，其中酯的R"與醇的R'互換： [0058][0059] 轉酯化可產生：藉由醇的烷氧基(alkoxide)攻擊出現於對酞酸二辛基酯中的兩個酯(RCOOR")基的羰基的兩個碳所形成之化合物(後文中，稱為「雙重攻擊酯化合物」)；藉由醇的烷氧基攻擊一個酯(RCOOR")基的一個碳所形成之化合物(後文中，稱為「單一攻擊酯化合物」)；及維持是未反應物之化合物(後文中，稱為「反應殘質酯化合物」)，其未參與反應。 [0060] 轉酯化可在無觸媒下進行。據此，不像酸–醇酯化，轉酯化不會引發水污染，並可解決因為使用酸性觸媒而引發的問題。 [0061] 上述轉酯化可產生三種化合物：相對於建基於酯之組成物的總重量，分別為0.5重量%至70重量%、0.5重量%至50重量%、及0.5重量%至85重量%，具體地10重量%至50重量%、0.5重量%至50重量%、及35重量%至80重量%之單一攻擊酯化合物，雙重攻擊酯化合物，及反應殘質酯化合物。 [0062] 當使用含有酯化合物在上述含量範圍內之建基於酯之組成物來製備樹脂組成物時，可達成具有高加工效率、優異可加工性及優異吸收速度之塑化劑組成物。 [0063] 經由轉酯化製備之建基於酯之組成物可含有三種酯化合物，即單一攻擊酯化合物，雙重攻擊酯化合物，及反應殘質酯化合物，且可根據醇的添加量來控制建基於酯之組成物的組成比。 [0064] 相對於100重量份的建基於二酯之化合物，也就是說對酞酸二辛基酯，醇的添加量可為0.1至89.9重量份，具體地3至50重量份，且更具體地5至40重量份。 [0065] 於製備建基於酯之組成物中，隨著使用越多醇，越高莫耳分率建基於二酯之化合物涉及轉酯化。據此，可能增加塑化劑組成物中單一攻擊酯化合物及雙重攻擊酯化合物的含量。 [0066] 另一方面，維持未反應之反應殘質酯化合物的含量可能傾向於減少。 [0067] 建基於二酯之化合物與醇的莫耳比可為，例如1:0.005至5.0、1:0.05至2.5、或1:0.1至1.0。在此範圍內，可獲得能提供具有高加工效率及高的改善可加工性效果的塑化劑組成物之建基於酯之組成物。 [0068] 轉酯化可在120至190℃，較佳135至180℃，及更佳141至179℃之溫度進行10分鐘至10小時，較佳30分鐘至8小時，且更佳1至6小時。在上面溫度與時間範圍內，可有效率獲得具有所欲組成比之建基於酯之組成物。在此情況下，反應時間可從提高反應物溫度而到達反應溫度的時間點起算。 [0069] 轉酯化可在無觸媒下進行，但在一些情況下，其可在酸性觸媒或金屬觸媒存在下進行，其提供減少反應時間之效果。 [0070] 酸性觸媒的實例含有硫酸、甲烷磺酸、對甲苯磺酸等，而金屬觸媒的實例含有有機金屬觸媒、金屬氧化物觸媒、金屬鹽觸媒及金屬本身。 [0071] 金屬觸媒的金屬組分可為例如，任一種選自錫、鈦及鋯所組成群組者或二或更多種選自錫、鈦及鋯所組成群組者之混合物。 [0072] 製備塑化劑組成物之方法可進一步含有轉酯化後經由蒸餾來移除未反應醇及反應副產物，例如建基於二酯之化合物。 [0073] 蒸餾可為，例如二步驟蒸餾，其中醇與反應副產物因為彼等之不同沸點而分離，或混合蒸餾。在此情況下，可相對精確確保建基於酯之組成物的所欲組成比。混合蒸餾是指一種同時蒸餾丁醇與副產物之程序。 [0074] 如上所述，轉酯化中建基於二酯之化合物可為對酞酸二(2-乙基己基)酯，且醇可為丁醇及/或異丁醇。 [0075] 所生產建基於酯之組成物中含有的酯化合物之種類可取決於轉酯化中建基於二酯之化合物及所用醇之組合變化。據此，在含有建基於環己烷1,4-二酯之化合物的最終製備塑化劑組成物中，化合物之特定組合可變化。 [0076] 製備塑化劑組成物之方法可含有藉由在金屬觸媒存在下進行建基於酯之組成物的氫化而將構成建基於酯之組成物的酯化合物轉化成組成物，該組成物為建基於環己烷1,4-二酯之化合物的混合物。 [0077] 氫化為藉由在金屬觸媒存在下添加氫來消除建基於酯之組成物中苯環芳香性之反應且可為一種還原反應。 [0078] 氫化為藉由在金屬觸媒存在下將建基於酯之組成物與氫反應來合成組成物之反應，該組成物為建基於環己烷1,4-二酯之化合物之混合物，且此反應之條件可含有僅氫化苯環同時不影響取代在苯環中之羰基的所有傳統反應條件。 [0079] 氫化可用額外有機溶劑諸如醇等進行，但本發明不限於此。金屬觸媒可為一般用於將苯環氫化之Rh/C觸媒、Pt觸媒、Pd觸媒等，且可使用任何一種可用於氫化者而無受限。 [0080] 當經由氫化而從建基於對酞酸酯之化合物製備了建基於環己烷1,4-二酯之化合物或其混合組成物時，則不論建基於對酞酸酯之化合物為單一化合物或複數種化合物之混合物，建基於對酞酸酯之化合物之組成比可維持幾乎在均等水平。 [0081] 根據本發明之製備塑化劑組成物之方法可進一步含有，經由在觸媒存在下以醇直接酯化建基於二羧酸之化合物來製備轉酯化中所用建基於二酯之化合物。 [0082] 於直接酯化中，建基於二羧酸之化合物可含有對酞酸，而醇可含有2-乙基己醇。 [0083] 直接酯化可在80至270℃，較佳150至250℃進行10分鐘至10小時，較佳30分鐘至8小時，且更佳1至6小時。在上面溫度與時間範圍內，可有效率獲得建基於二酯之組成物。 [0084] 直接酯化中所用觸媒可為有機金屬觸媒諸如建基於Sn或建基於Ti之觸媒，酸性觸媒諸如建基於磺酸或建基於硫酸之觸媒，或其組合，但觸媒種類不限於此。 [0085] 建基於二羧酸之化合物及醇係以1:1至7，較佳1:2至5的莫耳比使用。 [0086] 醇可藉由常見方法製備或可為市售產品。當使用市售產品時，醇可以與一或多種其之異構物組合含有。在此情況下，所用醇及其異構物可為，例如50至100重量份:0至50重量份，較佳70至100重量份:0至30重量份。 [0087] 根據本發明一具體實施例，當醇與其之異構物組合使用時，可製備建基於二酯之化合物及其異構物之混合物。據此，根據本發明一具體實施例之建基於酯之組成物可進一步含有各酯化合物的複數種異構物。 [0088] 經由製備根據本發明一具體實施例之建基於二酯之化合物之直接酯化，可製備約80%或更多產率之建基於二酯之化合物，且可進行以醇將如是製備之建基於二酯之化合物轉酯化，而容易地製備由所欲組分以所欲組成比混合所組成之建基於酯之組成物。 [0089] 作為另一實例，可改變製備塑化劑組成物之方法中酯化及氫化之順序；然而，在此情況下，可製備相同組成物。也就是說，藉由進行氫化建基於二酯之化合物來消除苯環雙鍵，以製備建基於環己烷1,4-二酯之化合物，並接著進行以醇轉酯化建基於環己烷1,4-二酯之化合物，而可製備含有雜合型化合物及非雜合型化合物之建基於環己烷1,4-二酯之化合物物質。 [0090] 替代地，建基於環己烷1,4-二酯之物質可藉由使用1,4-環己烷二羧酸而非對酞酸作為原料製備。在此情況下，為單一化合物之建基於環己烷1,4-二酯之物質可經由以一種醇直接酯化1,4-環己烷二羧酸製備，而為複數種化合物的混合物之建基於環己烷1,4-二酯之物質可經由以二或更多種醇直接酯化1,4-環己烷二羧酸製備，或經由以一種醇直接酯化1,4-環己烷二羧酸且之後以另一種醇轉酯化而製備。 [0091] 此外，可使用環己烷-1,4-二甲基酯而非1,4-環己烷二羧酸。在此情況下，為單一化合物或為複數種化合物的混合物之建基於環己烷1,4-二酯之物質，可經由就像使用二羧酸時般之酯化製備。 [0092] 如上所述，建基於環己烷1,4-二酯之物質可在不進行氫化下製備，且此方法可減少該程序中所涉及之風險或氫化所引發之高加工成本的門檻。 [0093] 然而，不特別限制製備建基於環己烷1,4-二酯之物質之方法，只要它製備含有化學式1所示化合物之建基於環己烷1,4-二酯之物質。 [0094] 根據本發明另一具體實施例，提供了一種樹脂組成物，其含有上述塑化劑組成物及樹脂。 [0095] 樹脂可為相關領域中已知之樹脂。例如，樹脂為一或多種選自乙烯乙酸乙烯酯共聚物、聚乙烯、聚丙烯、聚氯乙烯、聚酮、聚苯乙烯、聚胺甲酸酯、熱塑性彈性體、及聚乳酸之混合物，但本發明不限於此。 [0096] 相對於100重量份的樹脂，可以5至150重量份，較佳5至80重量份，且更佳10至60重量份的量含有塑化劑組成物。 [0097] 此外，有需要時，樹脂組成物可進一步含有各種添加劑，且可根據使用目的適當選擇添加劑。亦，塑化劑組成物可施用於製備一或多種選自電線、地板材料、汽車的內裝材料、膜、片材、壁紙及管所組成群組者。 [0098] 實施例 [0099] 下文中，將參照具體實施例詳細描述本發明。然而，本發明之具體實施例可有各種不同形式的修飾，且本發明之範疇不限於以下描述的具體實施例。提供本發明之具體實施例以使本揭露更透徹且完整，且將更充分傳達具體實施例的概念給所屬技術領域中具有通常知識者。 [0100] 實施例1 1) 酯化 將2,000 g的對酞酸二(2-乙基己基)酯(DEHTP)及340g (17重量份，相對於100重量份DEHTP)的正丁醇添加到配備攪拌器、冷凝器及傾析器的反應瓶中，並接著在氮氣氛下以160℃反應溫度進行轉酯化約2小時，進而獲得建基於酯之塑化劑組成物，其含有分別為4重量%、35重量%及61重量%之對酞酸二丁基酯(DBTP)、對酞酸丁基酯(2-乙基己基)酯(BEHTP)及對酞酸二(2-乙基己基)(DEHTP)。 [0101] 使建基於酯之塑化劑組成物歷經混合蒸餾，而移除丁醇及2-乙基己醇，進而最終製備混合組成物。 2) 氫化 [0102] 將1,000g經由酯化產生的組成物與20g的釕觸媒(N.E CHEMCAT)作為原料添加至1.5L高壓反應瓶，並在8MPa壓力下添加氫，以於150℃進行氫化3小時，接著完成反應。於反應完成後，過濾觸媒並進行傳統純化程序，進而製備99%產率之經氫化混合組成物。 [0103] 實施例2 1) 酯化 將498.0g經純化的對酞酸(PTA)、585g的2-乙基己醇(2-EH)(PTA:2-EH的莫耳比=1.0:1.5)、及333g的丁醇(BA)(PTA:BA的莫耳比=1.0:1.5)添加到配備冷卻器、冷凝器、傾析器、回流幫浦、溫度控制器、攪拌器等的4-頸3L反應瓶中。對其添加10g(2.0重量份，相對於100重量份的PTA)建基於磺酸之觸媒(甲烷磺酸(MSA))，並接著緩慢將反應瓶的溫度增溫至約150℃。於約130℃開始產生生成水，且在連續引入氮氣下，在大氣壓條件及約220℃的最終反應溫度下，進行酯化約4.5小時，且當酸值達6.0時中止反應。 [0104] 反應完成之後，在減壓下進行0.5至4小時的蒸餾萃取以移除未反應原料。為了藉由移除未反應原料而使未反應原料的水平降至預定含量水平或更低，使用蒸汽在減壓下進行0.5至3小時的蒸汽萃取。將反應溶液的溫度冷卻至約90℃，以及使用鹼溶液進行中和處理。在此情況下，可視需要進行清洗。之後，反應溶液經脫水以移除水。將過濾材料引入至經脫水的反應溶液中，攪拌預定時間段且接著過濾，進而最終獲得混合組成物。 [0105] 2) 氫化 以與實施例1相同之方式，藉由進行氫化混合組成物而製備經氫化之混合組成物。 [0106] 實施例3 [0107] 將516.0g的1,4-環己烷二羧酸(CHDA)、897g的2-乙基己醇(2-EH)(PTA:2-EH的莫耳比=1.0:2.3)、及155g的丁醇(BA)(PTA:BA的莫耳比=1.0:0.7)添加到配備冷卻器、冷凝器、傾析器、回流幫浦、溫度控制器、攪拌器等的4-頸3L反應瓶中。對其添加10g(2.0重量份，相對於100重量份的PTA)建基於磺酸之觸媒(MSA)，並接著緩慢將反應瓶的溫度增溫至約150℃。於約130℃開始產生生成水，且在連續引入氮氣下，在大氣壓條件及約220℃的最終反應溫度下，進行酯化約4.5小時，且當酸值達6.0時中止反應。 [0108] 反應完成之後，在減壓下進行0.5至4小時的蒸餾萃取以移除未反應原料。為了藉由移除未反應原料而使未反應原料的水平降至預定含量水平或更低，使用蒸汽在減壓下進行0.5至3小時的蒸汽萃取。將反應溶液的溫度冷卻至約90℃，以及使用鹼溶液進行中和處理。在此情況下，可視需要進行清洗。之後，反應溶液經脫水以移除水。將過濾材料引入至經脫水的反應溶液中，攪拌預定時間段且接著過濾，進而最終獲得混合組成物。 [0109] 比較例1 除了改用苯甲醇而非2-乙基己醇，以與實施例1相同之方式製備環己烷-1,4-二丁基酯、環己烷-1,4-丁基酯苯甲基酯及環己烷-1,4-二苯甲基酯之混合組成物。 [0110] 比較例2 除了改用異壬醇而非丁醇，以與實施例1相同之方式製備環己烷-1,4-二異壬基酯、環己烷-1,4-異壬基酯(2-乙基己基)酯及環己烷-1,4-二(2-乙基己基)酯之混合組成物。 [0111] 比較例3 藉由單獨使用環己烷-1,4-二(2-乙基己基)酯製備組成物。 [0112] 比較例4 藉由單獨使用環己烷-1,4-二丁基酯(LG化學)製備組成物。 [0113] 比較例5 除了改用鄰苯二甲酸酐而非對酞酸，以與實施例1相同之方式製備環己烷-1,2-二丁基酯、環己烷-1,2-丁基酯(2-乙基己基)酯及環己烷-1,2-二(2-乙基己基)酯之混合組成物。 [0114] 根據實施例1至3及比較例1至5之組成物的組成比顯示於下表1中。[0115] 實驗例1：試樣之製備及性能評估
將根據實施例1至3及比較例1至5之塑化劑用作為實驗試樣。針對試樣製備，參考ASTM D638，將40重量份的各塑化劑及3重量份的安定劑(LOX 912 NP)係與100重量份的PVC於混合機中混合，且所得混合物接著經歷170℃輥磨4分鐘，並利用壓製，於180℃壓製2.5分鐘(低壓)及2分鐘(高壓)，進而製備1T及3T片材。各試樣經歷下列性質之測試，其結果顯示於下表2。 [0116] ＜測試項目 ＞
硬度之量測 根據ASTM D2240，在25℃測量Shore硬度(Shore “A”)。 [0117] 拉伸強度之量測 根據ASTM D638，使用通用測試儀(UTM)(製造商；Instron，型號；4466)將各試樣以200mm/min的十字頭速度拉伸，並接著測出試樣斷裂時點。拉伸強度計算如下： 拉伸強度(kgf/mm2
)=負載值(kgf)∕厚度(mm)×寬度(mm) [0118] 伸長率之量測 根據ASTM D638，使用通用測試儀(UTM)將各試樣以200mm/min的十字頭速度拉伸，並接著測出試樣斷裂時點。伸長率計算如下： 伸長率(%)=拉長之後的長度∕初始長度×100 [0119] 遷移耗損之量測 根據KSM-3156獲得具有2mm或更大的厚度之試樣，將ABS板(自然色)附接於試樣的兩側，接著對其施加1kgf/cm2
的負載。試樣置於熱空氣對流烘箱(80℃)中72小時，接著從烘箱取出，並於室溫冷卻4小時。之後，在移除附接至試樣兩側的ABS板之後，測量將試樣置於烘箱中之前與之後的重量，故而藉以下的方程式計算遷移耗損。 [0120] 遷移耗損(%)={(試樣於室溫的初始重量–試樣置於烘箱中之後的重量)∕試樣於室溫的初始重量}×100 [0121] 揮發耗損之量測 所製備的試樣於100℃加工72小時，接著測量試樣的重量。 揮發耗損(%)=(初始試樣的重量–試樣於100℃加工72小時之後的重量)∕初始試樣的重量×100 [0122] 應力測試 藉由於室溫使試樣維持在彎折狀態下24小時，72小時及168小時而進行應力測試，並接著觀察且以數值表示遷移程度(滲漏程度)。於此測試中，越靠近0的值表示優異特性。[0123] 參考表2，可確認的是，與比較例1至5相比，實施例1至3都展現優異性質且具有均一優異之性質。 [0124] 具體地，可確認的是，對其施用具有大碳數之烷基的比較例2及對其施用芳族環的比較例1展現高硬度，故而塑化效率低於實施例1至3所具者。亦，可確認的是，比較例1及2展現顯著高度的應力下遷移，及就伸長率及抗拉強度而言相對不良機械性質。 [0125] 此外，可確認的是，對其施用單一化合物之比較例3及4的少數性質特別差。尤其，比較例3展現不良塑化效率(高硬度)及高度的應力下遷移，而比較例4展現就抗拉強度及伸長率而言顯著不良機械性質並展現高遷移遷移耗損及高揮發耗損。然而，可確認的是，與比較例3及4所具者相比，其中已彌補比較例3及4之弱點的實施例1至3於所有上述性質中展現改善，尤其就抗拉強度、伸長率及應力下遷移而言。 [0126] 額外地，可確認的是，與實施例1至3相比，比較例5(其中使用衍生自建基於對酞酸酯之化合物的經氫化物質)展現相對不良性質，更不用說於製備程序中無法避免引發環境問題。 [0127] 據此，可確認的是，當使用對其施用C4及C8烷基各者之經氫化物質作為塑化劑時，特別是在考慮其之重量平均碳數，如同在根據本發明之實施例1至3的情況時，可改善遷移能力及塑化效率，同時維持就抗拉強度及伸長率而言優異的機械性質，且特別是可顯著改善應力下遷移。
Claims (8)
- 一種塑化劑組成物，其包含： 下列化學式1所示建基於環己烷1,4-二酯之化合物； 下列化學式2所示建基於環己烷1,4-二酯之化合物；以及 下列化學式3所示建基於環己烷1,4-二酯之化合物， 其中，R1 為丁基或異丁基，及R2 為2-乙基己基。
- 如請求項1之塑化劑組成物，其中相對於該塑化劑組成物的總重量，該化學式1所示建基於環己烷1,4-二酯之化合物、該化學式2所示建基於環己烷1,4-二酯之化合物、以及該化學式3所示建基於環己烷1,4-二酯之化合物的含量分別為0.5至70重量%、0.5至50重量%、及0.5至85重量%。
- 如請求項1之塑化劑組成物，其中相對於該塑化劑組成物的總重量，該化學式1所示建基於環己烷1,4-二酯之化合物、該化學式2所示建基於環己烷1,4-二酯之化合物、以及該化學式3所示建基於環己烷1,4-二酯之化合物的含量分別為10至50重量%、0.5至50重量%、及35至80重量%。
- 如請求項1之塑化劑組成物，其中該化學式2所示建基於環己烷1,4-二酯之化合物與該化學式3所示建基於環己烷1,4-二酯之化合物的總和與該化學式1所示建基於環己烷1,4-二酯之化合物的重量比為95:5至30:70。
- 如請求項1之塑化劑組成物，其中該塑化劑組成物具有5.7至7.9之重量平均碳數。
- 一種樹脂組成物，其包含： 100重量份的樹脂；及 5至150重量份的如請求項1之塑化劑組成物。
- 如請求項6之樹脂組成物，其中該樹脂包含選自由乙烯-乙酸乙烯酯共聚物(ethylene vinyl acetate)、聚乙烯、聚酮、聚丙烯、聚氯乙烯、聚苯乙烯、聚胺甲酸酯、及熱塑性彈性體所組成群組者中之一或多者。
- 如請求項6之樹脂組成物，其中該樹脂組成物係應用於製備選自由電線、地板材料、汽車的內裝材料、膜、片材、壁紙及管所組成群組者中之一或多者。