TW201516104A - 包含含有氧化鈰之磨料粒子之cmp組成物 - Google Patents
包含含有氧化鈰之磨料粒子之cmp組成物 Download PDFInfo
- Publication number
- TW201516104A TW201516104A TW103124382A TW103124382A TW201516104A TW 201516104 A TW201516104 A TW 201516104A TW 103124382 A TW103124382 A TW 103124382A TW 103124382 A TW103124382 A TW 103124382A TW 201516104 A TW201516104 A TW 201516104A
- Authority
- TW
- Taiwan
- Prior art keywords
- group
- polymer
- cmp
- alkyl
- branched
- Prior art date
Abstract
本發明描述一種包含含有氧化鈰之磨料粒子之化學機械拋光(CMP)組成物。
Description
本發明係關於一種包含含有氧化鈰之磨料粒子之化學機械研磨(CMP)組成物;用於製備根據本發明之CMP組成物之方法;用於製造半導體裝置之方法,其包含在根據本發明之化學機械拋光(CMP)組成物存在下對基板進行化學機械拋光;係關於特定聚合物用於抑制分散於含水介質中之含有氧化鈰之粒子凝聚及/或調整該等粒子之ζ電位之用途;及係關於抑制分散於含水介質中之含有氧化鈰之粒子凝聚及/或調整該等粒子之ζ電位之方法。
在半導體工業中,化學機械拋光(縮寫為CMP)為應用於製造先進的光子、微機電及微電子材料及裝置(諸如半導體晶圓)中之熟知技術。
在製造用於半導體工業中之材料及裝置期間,採用CMP以使金屬及/或氧化物表面平坦化。CMP利用化學作用與機械作用之相互作用以使表面平坦化。藉由化學組成物(亦稱為CMP漿體或CMP組成物)提供化學作用。通常藉由經典型地按壓於待拋光表面上且安裝於移動壓板上之拋光墊及藉由分散於CMP組成物中之磨料粒子進行機械作用。壓板移動
通常為直線的、旋轉的或軌道的。在典型CMP製程步驟中,旋轉晶圓固持器使待拋光基板與拋光墊接觸。CMP組成物通常施用於基板待拋光之表面與拋光墊之間。
尤其在製造積體電路及微機電裝置中,在多層次結構之每一層次下進行之CMP製程步驟必須滿足極高要求。描述此等要求之一個重要參數為材料移除速率(MRR),亦即待拋光材料之移除速率。
CMP組成物典型地用於此含有充當磨料之無機材料之粒子及各種其他組分之領域。對於某些CMP應用,將膠狀含有氧化鈰之粒子用作研磨劑。基於氧化鈰之CMP組成物已在淺溝槽隔離(STI)應用中得到了廣泛關注,這是因為由於氧化鈰對於二氧化矽的高化學親和力(亦在此項技術中稱為氧化鈰之化學齒作用)其能夠實現相對較高氧化物對氮化物之選擇性。
藉由膠體粒子之ζ電位判定分散膠體之穩定性。粒子之ζ電位為假定相對於本體溶液出現剪切力之平面處的電位。此平面(名為剪切面)位於雙電層之擴散部分中且解釋為流體動力可動流體與固定流體之間的尖銳邊界(參見A.V.Delgado等人之Measurement and Interpretation of Electrokinetic Phenomena,Journal of Colloid and Interface Science 309(2007),第194-224頁)。ζ電位作為分散液之膠體穩定性的指標,可將其視為粒子之表面電荷之估值且視液體中之組成及pH值、溫度、離子強度及離子種類而定。
在僅包含一種粒子(例如氧化鈰粒子)之膠體中,在既定一組條件(液體中之pH值、溫度、離子強度及離子種類)下所有粒子之ζ電位具有相同跡象。因此當粒子帶有大量電荷時,靜電斥力防止其凝結(絮
凝)。
對於膠狀氧化物,ζ電位強有力地視液體之pH值而定。在酸性區域之pH值下,膠狀氧化物之粒子通常具有吸附於其表面上之H+離子。當pH值增加時,中和所吸附之H+離子,從而導致表面電荷降低直至達到等電點,此時各膠體氧化物粒子之總電荷為零。因此,粒子之間的靜電斥力停止,以致由於凡得瓦爾力(Van der Waals force)之作用使得該等粒子可凝結成較大粒子(凝聚粒子)。對於膠狀氧化鈰,在不存在穩定添加劑之情況下,在5.5或低於5.5之pH值下ζ電位明顯高於30mV,而當pH值上升高於6時明顯降低,從而導致粒子凝結。
另一問題為在介電質基板之情況下,待藉由CMP組成物拋光之基板表面亦帶電。若待拋光之基板的電荷與研磨粒子之電荷相反,則磨料粒子由於靜電引力吸附在帶相反電荷之表面上且在拋光之後幾乎不可移除。另一方面,若待拋光之材料的電荷符號與研磨粒子相同,則由於靜電斥力拋光受阻。因此,材料移除速率及選擇性強有力地視研磨劑之ζ電位與待拋光之材料的電荷之間的相互作用而定。出於此原因,磨料粒子較佳不帶有大量電荷。不幸的是,由於上述原因,降低磨料粒子之表面電荷的絕對值促進該等粒子凝結。
為了至少部分解決以上所說明之問題,已提出CMP組成物之若干添加劑,其將使磨料粒子之凝聚降至最低及/或改善各別CMP組成物之材料移除速率及選擇性。
在EP 1 844 122 B1中,揭示用於同時拋光像氮化矽之陽離子帶電材料及像二氧化矽之陰離子帶電材料的佐劑。假定該佐劑在陽離子
帶電材料上形成吸附層以便增加陰離子帶電材料優於陽離子帶電材料之拋光選擇性。該佐劑包含聚電解質鹽,其含有:(A)具有1,000至20,000之重量平均分子量且包含具有如EP 1 844 122 B1中所定義之特定結構之骨幹及側鏈的接枝型聚電解質及(B)鹼性材料。該佐劑亦將使磨料粒子之凝聚降至最低。然而,EP 1 844 122 B1之實例顯示採用所提出之佐劑未必總是達成該等目標。在一些情況下,與具有先前技術之佐劑的CMP組成物相比,二氧化矽優於氮化矽之材料移除選擇性並未提高。另外,在包含根據EP 1 844 122 B1之助劑的CMP組成物中,氧化鈰粒子之平均凝聚粒徑高於500nm,其對於複數個CMP應用而言不可接受。該佐劑對氧化鈰粒子之ζ電位之影響在EP 1 844 122 B1中並未論述。
US 7 381 251 B2揭示一種包含液體介質、礦物粒子之膠狀分散液及膦酸酯封端之聚(氧烯烴)聚合物之混合物的液體組成物。
本發明之一個目標為提供尤其對於介電質基板展示提高之拋光效能之一種化學機械拋光(CMP)組成物及一種CMP方法。更特定言之,本發明之一目的為提供展示如下性質之一種化學機械拋光(CMP)組成物及一種CMP方法(i)二氧化矽之高材料移除速率(MRR),或(ii)二氧化矽與氮化矽之間的可調整之選擇性,或(iii)二氧化矽與多晶矽之間的可調整之選擇性,(iv)拋光表面之高表面品質(v)較佳為(i)、(ii)、(iii)及(iv)之組合。
本發明之另一目的為提供一種包含氧化鈰粒子之化學機械拋光(CMP)組成物,其中氧化鈰粒子之凝聚在6及更高之pH值下,較佳在高達10之pH值下受到抑制。
本發明之另一目的為提供一種包含氧化鈰粒子之化學機械拋光(CMP)組成物,其中氧化鈰粒子帶有低電荷,亦即具有低ζ電位。
根據本發明之第一態樣,提供包含以下組分之化學機械拋光(CMP)組成物:
(A)含有氧化鈰之磨料粒子
(B)一或多種聚合物,其中該等聚合物(B)之各大分子包含(i)一或多個陰離子官能基及(ii)一或多個結構單元-(AO)a-R
其中在與每一其他結構單元-(AO)a-R獨立之各結構單元-(AO)a-R中A為CxH2x,其中對於該等結構單元-(AO)a-R中之每個A,x係(與每一其他x獨立地)選自2至4範圍內之整數,其中x較佳為2或3,進一步較佳地x=2
其中在各結構單元-(AO)a-R內,基團A為相同或不同
a為選自5至200,較佳8至150,最佳20至135範圍內之整數,R為氫或具有1至4個碳原子之分支鏈或直鏈烷基,其中在該聚合物(B)中,所有結構單元(ii)之莫耳質量總和至少為該聚合物(B)之莫耳質量的50%。
圖1展示根據本發明使用之聚合物(B)能夠針對電泳激發掩蔽含有氧化鈰之磨料粒子之電荷。
在以下【實施方式】及實施例中說明本發明之其他細節、修改及優點。
(A)含有氧化鈰之磨料粒子
根據本發明之CMP組成物包含含有氧化鈰之磨料粒子作為組分(A)。在CMP方法中,該等氧化鈰粒子使(A)充當研磨劑朝向待拋光之表面。
磨料粒子(A)較佳由氧化鈰組成。除含有氧化鈰或由氧化鈰組成之磨料粒子(A)外,根據本發明之化學機械拋光(CMP)組成物較佳不含有其他磨料粒子。
在本發明之CMP組成物內,氧化鈰粒子典型地以膠體狀態分散。
適合之含有氧化鈰之磨料粒子(A)市售可得,例如以商標名Rhodia。
適合之含有氧化鈰之磨料粒子(A)可例如藉由濕沈澱法或藉由電漿法獲得。在後者情況下氧化鈰亦稱為煙霧狀氧化鈰。在一些情況下,經濕沈澱之氧化鈰因其具有極好的分散特性所以為較佳的。在其他情況下,煙霧狀氧化鈰因其具有極強研磨作用所以為較佳的。
在本發明之CMP組成物中,含有氧化鈰之磨料粒子較佳具
有藉由500nm或更低之D50值,較佳250nm或更低之D50值,進一步較佳200nm或更低之D50值,尤其較佳180nm或更低之D50值,最佳150nm或更低之D50值特性化之粒徑分佈。例如可採用DLS(動態光散射)或SLS(靜態光散射)法量測粒徑分佈。此等方法及其他方法已為此項技術中所熟知,參見例如Kuntzsch,Timo;Witnik,Ulrike;Hollatz,Michael Stintz;Ripperger,Siegfried;Characterization of Slurries Used for Chemical-Mechanical Polishing(CMP)in the Semiconductor Industry;Chem.Eng.Technol;26(2003),第12卷,第1235頁。典型地使用Horiba LB550 V(DLS,動態光散射,根據手冊量測)或任何其他DLS儀器。通常在塑膠比色皿中在0.1%至1.0%固體濃度下量測氧化鈰分散體之粒徑分佈。必要時採用分散介質或超純水進行稀釋。將基於體積之粒徑分佈的D50值展示為粒徑分佈之表示。
含有氧化鈰之磨料粒子(A)之粒徑分佈可為單峰、雙峰或多峰。粒徑分佈較佳為單峰以便具有含有氧化鈰之磨料粒子(A)之可容易再現之特性曲線及本發明之製程期間可容易再現之條件。
另外,含有氧化鈰之磨料粒子(A)的粒徑分佈可為窄或寬。粒徑分佈較佳為窄,僅具有少量小粒子及大粒子以便具有含有氧化鈰之磨料粒子(A)之可容易再現之特性曲線及本發明之製程期間可容易再現之條件。
含有氧化鈰之磨料粒子(A)可具有各種形狀。因此,磨料粒子可為一種或基本上一種類型之形狀。然而,含有氧化鈰之磨料粒子(A)亦可能具有不同形狀。特定言之,兩種類型之不同形狀之含有氧化鈰的磨料粒子(A)可存在於本發明之既定組成物中。就形狀自身而言,其可為立
方體,具有削邊之立方體、八面體、二十面體、結節及具有或不具有突起或壓痕之球體。形狀最佳為不具有突起或壓痕或僅具有極少突起或壓痕之球體。此形狀通常為較佳的,因為其通常增加對CMP製程期間含有氧化鈰之磨料粒子(A)所暴露之機械力的抗性。
含有氧化鈰之磨料粒子(A)可含有少量其他稀土金屬氧化物。
由氧化鈰組成之磨料粒子(A)可具有六角形、立方形或面心立方體之晶格。
在某些特定情況下,含有氧化鈰之磨料粒子(A)為包含含有至少一種不同於氧化鈰之其他磨料粒狀物或由該磨料粒狀物組成之核心的複合粒子,該磨料粒狀物特定言之為氧化鋁、二氧化矽、二氧化鈦、氧化鋯、氧化鋅及其混合物。
該等複合粒子例如自WO 2005/035688 A1、US 6,110,396、US 6,238,469 B1、US 6,645,265 B1、K.S.Choi等人,Mat.Res.Soc.Symp.Proa,第671卷,2001 Materials Research Society,M5.8.1至M5.8.10、S.-H.Lee等人,J.Mater.Res.,第17卷,No.10(2002),第2744至2749頁、A.Jindal等人,Journal of the Electrochemical Society,150(5),G314-G318(2003)、Z.Lu,Journal of Materials Research,第18卷,第10期,2003年10月,Materials Research Society或S.Hedge等人,Electrochemical and Solid-State Letters,7(12),G316-G318(2004)已知。
複合粒子最佳為經樹莓式塗佈之粒子,其包含選自由氧化鋁、二氧化矽二氧化鈦、氧化鋯、氧化鋅及其混合物組成之群具有20至100
nm之核心尺寸的核心,其中該核心塗佈有粒徑小於10nm之氧化鈰粒子。
尤其較佳為根據本發明之化學機械拋光(CMP)組成物,其中含有氧化鈰之磨料粒子(A)的總量在0.01wt.-%至5wt.-%、較佳0.1wt.-%至1.0wt.-%範圍內,例如為0.5wt.-%,在每一種情況下均以各別CMP組成物之總重量計。
(B)聚合物
本發明之CMP組成物包含一或多種聚合物(B),其中該等聚合物(B)之每一大分子包含(i)一或多個陰離子官能基及(ii)一或多個結構單元-(AO)a-R
其中在與每一其他結構單元-(AO)a-R獨立之各結構單元-(AO)a-R中A為CxH2x,其中對於該等結構單元-(AO)a-R中之每個A,x(與每一其他x彼此獨立地)係選自2至4範圍內之整數,其中x較佳為2或3,進一步較佳地x=2
其中在各結構單元-(AO)a-R內,基團A為相同或不同
a為選自5至200,較佳8至150,最佳20至135範圍內之整數,R為氫或具有1至4個碳原子之分支鏈或直鏈烷基,其中在該聚合物(B)中,所有結構單元(ii)之莫耳質量總和至少為該聚合物(B)之莫耳質量的50%。
待根據本發明使用之聚合物(B)為水溶性的。
結構單元-(AO)a-R在下文中亦稱為結構單元(ii)。基團R較
佳選自由氫及甲基組成之群。
陰離子官能基為呈解離狀態時帶有負電荷之官能基。較佳地,在該聚合物(B)或該等聚合物(B)中之至少一種之大分子中,該或該等陰離子官能基係選自由羧酸基、磺酸基、硫酸基、磷酸基及膦酸基組成之群。
羧酸基具有呈未解離狀態之結構-COOM(其中M為H或一個陽離子等效物)及呈解離狀態之結構-COO-。
硫酸基具有呈未解離狀態之結構-O-SO3M(其中M為H或一個陽離子等效物)及呈解離狀態之結構-O-SO3-。
磺酸基具有呈未解離狀態之結構-SO3M(其中M為H或一個陽離子等效物)及呈解離狀態之結構-SO3-。
磷酸基具有呈未解離狀態之結構-O-PO3M2(其中M為H或一個陽離子等效物)、呈第一解離狀態之結構-O-PO3M-(其中M為H或一個陽離子等效物)及呈第二解離階段之結構-O-PO3 2-。
在本申請案之上下文中,術語磷酸基包括其中兩個羥基中之一個藉由醇Rx-OH酯化產生呈未解離狀態之結構-O-P(ORx)O2M(其中M為H或一個陽離子等效物)及呈解離狀態之結構-O-P(OR)O2 -的磷酸基。
膦酸基具有呈未解離狀態之結構-PO3M2(其中M為H或一個陽離子等效物)、呈第一解離狀態之結構-PO3M-(其中M為H或一個陽離子等效物)及呈完全解離階段之結構-PO3 2-。
在本申請案之上下文中,術語膦酸基包括其中兩個羥基中之一個藉由醇Rx-OH酯化產生呈未解離狀態之結構-P(ORx)O2M(其中M為H
或一個陽離子等效物)及呈解離狀態之結構-P(ORx)O2 -的膦酸基。
上文所定義之結構單元-AO-較佳選自由-O-CH2-CH2-、-O-CH2-CH(CH3)-、-O-CH(CH3)-CH2-及-O-CH2-CH2-CH2-CH2-組成之群,其中-O-CH2-CH2-(自環氧乙烷衍生之結構單元)為較佳。
較佳地,在待根據本發明使用之聚合物(B)中,該或該等結構單元(ii)-(AO)a-R中之每一者之莫耳質量為500g/mol或大於500g/mol,較佳1000g/mol或大於1000g/mol,更佳2000g/mol或大於2000g/mol,最佳3000g/mol或大於3000g/mol及/或所有該等結構單元(ii)-(AO)a-R之莫耳質量總和為該聚合物(B)之莫耳質量的60%或大於60%,較佳70%或大於70%,最佳80%或大於80%。
該聚合物(B)或該等聚合物(B)中之至少一種較佳係選自由梳形聚合物及嵌段共聚物組成之群。
嵌段共聚物為其大分子各自由結構上不同之相鄰嵌段(亦即在每一種情況下,該等相鄰嵌段包含衍生自不同種類單體之結構單元或衍生自相同種類單體但具有結構單元之不同組成或順序分佈的結構單元)組成的共聚物。
梳形聚合物為其大分子為梳形大分子之聚合物,該等梳形大分子各自包含具有複數個三官能性分支點之主鏈(典型地稱為骨幹),線性側鏈自該等分支點中之每一個發出。可藉由長鏈α-烯烴、烷基環氧乙烷、乙烯醚、乙烯酯、(甲基)丙烯酸烷酯或N-烷基(甲基)丙烯醯胺之均聚合或共聚合獲得梳形聚合物。長鏈單體亦稱為大分子單體。或者其可藉由接枝共聚合獲得。
在本發明之較佳CMP組成物中,該聚合物(B)或該等聚合物(B)中之至少一種(B)為包含以下之梳形聚合物(i)骨幹,一或多個陰離子官能基與其鍵聯及(ii)一或多個側鏈,各自包含結構單元-(AO)a-R(其中A、a及R具有上文所定義之含義)或由該結構單元組成
其中在該梳形聚合物中,所有該等結構單元(ii)-(AO)a-R之莫耳質量總和至少為該梳形聚合物之莫耳質量的50%。
在下文中,更詳細地描述特定類型之較佳聚合物(B),例如藉助於通式。在不同通式之範圍內,使用相同變數且該等變數在該各別式中具有不同含義,在每一種情況下結合對於各別式所特定定義之含義。
較佳梳形聚合物(B)包含- 構建單元,其各自包含一或多個陰離子官能基及- 側鏈,其各自包含結構單元(ii)-(AO)a-R,其中A為CxH2x,其中對於該等結構單元-(AO)a-R中之每個A,x(與每一其他x彼此獨立地)係選自2至4範圍內之整數,其中x較佳為2或3,進一步較佳地x=2
其中在各結構單元-(AO)a-R內,基團A為相同或不同
a為選自5至200,較佳8至150,最佳20至135範圍內之整數R為氫或具有1至4個碳原子之分支鏈或直鏈烷基,其中包含陰離子官能基之構建單元中之一或多個係選自通式(7.1)、
(7.2)、(7.3)及(7.4):
其中R1為H或未分支或分支鏈C1-C4烷基、CH2COOH或CH2CO-X-R2;R2為PO3M2、O-PO3M2、(C6H4)-PO3M2或(C6H4)-OPO3M2;X為NR7-(CnH2n)或O-(CnH2n),其中n=1、2、3或4,氮原子或氧原子分別與CO基團連接;R7為H、C1-C6烷基、(CnH2n)-OH、(CnH2n)-PO3M2、(CnH2n)-OPO3M2、(C6H4)-PO3M2、(C6H4)-OPO3M2或(CnH2n)-O-(A2O)α-R9,其中n=1、2、3或4A2為CzH2z(其中z=2、3、4或5)或為CH2CH(C6H5);α為1至350之整數;且R9為H或未分支或分支鏈C1-C4烷基;或X為化學鍵且R2為OM;
其中
R3為H或未分支或分支鏈C1-C4烷基;n為0、1、2、3或4;R4為PO3M2或O-PO3M2;
其中R5為H或未分支或分支鏈C1-C4烷基;Z為O或NR7;且R7為H、(CnH2n)-OH、(CnH2n)-PO3M2、(CnH2n)-OPO3M2、(C6H4)-PO3M2或(C6H4)-OPO3M2,其中n為1、2、3或4;
其中R6為H或未分支或分支鏈C1-C4烷基;Q為NR7或O;R7為H、(CnH2n)-OH、(CnH2n)-PO3M2、(CnH2n)-OPO3M2、(C6H4)-PO3M2)、
(C6H4)-OPO3M2或(CnH2n)-O-(A2O)α-R9,n為1、2、3或4;A2為CzH2z(其中z=2、3、4或5)或為CH2CH(C6H5);α為1至350之整數;R9為H或未分支或分支鏈C1-C4烷基;其中在式(7.1)、(7.2)、(7.3)及(7.4)中,獨立於任何其他M之每個M為H或一個陽離子等效物及/或其中包含結構單元(ii)-(AO)a-R之側鏈中之一或多個係選自通式(7.5)、(7.6)、(7.7)及(7.8):
其中R10、R11及R12彼此獨立地為H或未分支或分支鏈C1-C4烷基;n為0、1、2、3、4及/或5;E為未分支或分支鏈C1至C6伸烷基、伸環己基、CH2-C6H10、1,2-伸苯基、1,3-伸苯基或1,4-伸苯基;G為O、NH或CO-NH;或E及G一起為化學鍵;
其中R16、R17及R18彼此獨立地為H或未分支或分支鏈C1-C4烷基;n為0、1、2、3、4或5;E為未分支或分支鏈C1-C6伸烷基、伸環己基、CH2-C6H10、1,2-伸苯基、1,3-伸苯基或1,4-伸苯基或為化學鍵;L為CzH2z,其中z=2、3、4或5或為CH2-CH(C6H5);d為1至350之整數;R20為H或未分支C1-C4烷基;
其中R21、R22及R23彼此獨立地為H或未分支或分支鏈C1-C4烷基;W為O、NR25或N R25為H或未分支或分支鏈C1-C4烷基;若W=O或NR25,則Y為1,且若W=N,則Y為2;
其中R6為H或未分支或分支鏈C1-C4烷基;Q為NR10、N或O;R10為H或未分支或分支鏈C1-C4烷基;若Q=O或NR10,則Y為1,且若Q=N,則Y為2。
尤其較佳地,式(7.1)之構建單元為甲基丙烯酸或丙烯酸單元,式(7.3)之構建單元為順丁烯二酸酐單元且式(7.4)之構建單元為順丁烯二酸或順丁烯二酸單酯單元。
尤其較佳地,式(7.5)之構建單元為烷氧基化異戊二烯基單元、烷氧基化羥丁基乙烯醚單元、烷氧基化(甲基)烯丙醇單元或為乙烯基化甲基聚伸烷二醇單元。
在上文所定義梳形聚合物中,較佳地,式(7.1)、(7.2)、(7.3)及(7.4)之構建單元之總量與式(7.5)、(7.6)、(7.7)及(7.8)之構建單元之總量之間的莫耳比為1:4至15:1,較佳為1:1至10:1。
該等梳形聚合物可藉由選自由以下組成之群之單體的共聚合獲得:丙烯酸;丙烯酸羥基烷酯;甲基丙烯酸;甲基丙烯酸羥基烷酯;順丁烯二酸、衣康酸(itaconic acid)、2-丙烯醯胺基-2-甲基丙烷磺酸(AMPS);丙烯醯胺及甲基丙烯酸磷酸羥烷酯
其中,一或多個大分子單體選自由以下組成之群:烷醯基化乙烯醚(例如乙氧基化羥丁基乙烯酯)、烷氧基化烯丙醚、烷氧基化甲基烯丙醚、烷氧基化異戊二烯醚、聚烷醚單烷基醚之甲基丙烯酸酯、聚烷醚單烷基醚之丙烯酸酯、聚烷醚單烷基醚之順丁烯二酸酯。該等烷氧基化大分子單體各自包含結構單元-(AO)a-R,其中A為CxH2x,其中對於該等結構單元-(AO)a-R中之每個A,x(與每一其他x彼此獨立地)係選自2至4範圍內之整數,其中x較佳為2或3,進一步較佳地x=2。
較佳地,使富電子大分子單體與缺電子單體反應,亦即使乙烯醚單體與丙烯酸單體或順丁烯二酸單體反應。
用於獲得上文所定義之梳形聚合物之適合方式揭示於具有申請案號13156752.1之歐洲專利申請案中。
此類型之較佳梳形聚合物可以商標名MelPers 0045自BASF SE獲得。在該梳形聚合物中,骨幹係由丙烯酸單體及順丁烯二酸單體形成,結構單元-(AO)a-R各自具有5800g/mol之莫耳質量,A為-CH2-CH2-,R為H且所有該等結構單元-(AO)a-R之莫耳質量總和為該梳形聚合物之莫耳質量的94%。
適用於本發明之另一種類之聚合物(B)為可藉由以下單體之共聚合獲得之梳形聚合物(8.1)丙烯酸及(8.2)一或多個大分子單體,其各自包含可聚合雙鍵,較佳乙烯基、烯
丙基、異戊二烯基、丙烯酸酯基、甲基丙烯酸酯基或順丁烯二酸酯基之雙鍵,A為CxH2x,其中對於該等結構單元-(AO)a-R中之每個A,x(與每一其他x彼此獨立地)係選自2至4範圍內之整數,其中x較佳為2或3,進一步較佳地x=2
其中在各結構單元-(AO)a-R內,基團A為相同或不同
a為選自5至200,較佳8至150,最佳20至135範圍內之整數R為氫或具有1至4個碳原子之分支鏈或直鏈烷基,其中選擇單體(8.1)及(8.2)之量以便獲得梳形聚合物,其中在該梳形聚合物中,所有該等結構單元(ii)-(AO)a-R之莫耳質量總和至少為該梳形聚合物之莫耳質量的70%。
在此類型之較佳梳形聚合物中,骨幹係由聚丙烯酸形成,結構單元-(AO)a-R各自具有1100g/mol之莫耳質量,A為-CH2-CH2-,R為H且所有該等結構單元-(AO)a-R之莫耳質量總和為該梳形聚合物之莫耳質量的75%。
適用於本發明之另一種類之聚合物(B)為梳形聚合物,其為含有以下之聚縮合物
(9.1)至少一個構建單元,其包含芳族或雜芳族系統Ar1及包含結構單元(ii)-(AO)a-R或由結構單元(ii)-(AO)a-R組成之側鏈
其中在與每一其他構建單元(9.1)獨立之各構建單元(9.1)中A為CxH2x,其中對於該等結構單元-(AO)a-R中之每個A,x(與每一其他x獨立地)係選自2至4範圍內之整數,其中x較佳為2或3,進一步較
佳地x=2
其中在各結構單元-(AO)a-R內,基團A為相同或不同
a為選自5至200,較佳8至150,最佳20至135範圍內之整數R為氫或具有1至4個碳原子之分支鏈或直鏈烷基,其中該等構建單元(9.1)較佳由通式(9.1)表示
其中對於與每一其他式(9.1)之構建單元獨立之各式(9.1)之構建單元
在每一種情況下Ar1係選自由具有5至10個碳原子之未經取代的芳族或雜芳族系統組成之群E1係選自由N、NH及O組成之群,較佳為O若E1=N,則n=2且若E1=NH或O,則n=1 A、a及R係如上文所定義
(9.2)至少一個構建單元,其包含芳族或雜芳族系統Ar1及磷酸基其中構建單元(9.2)中之一或多個較佳由通式(9.2)表示
其中對於與每一其他式(9.2)之構建單元獨立之各式(9.2)之構建單
元
在每一種情況下Ar2係選自由具有5至10個碳原子之未經取代的芳族或雜芳族系統組成之群E2係選自由N、NH及O組成之群,較佳為O若E2=N,則m=2且若E2=NH或O,則m=1 A係如上文關於構建單元(9.1)所定義b為選自0至300,較佳1至5範圍內之整數
獨立於任何其他M之M為H或一個陽離子等效物,R26為M或Ar1-O-(AO)a-
(9.3)至少一個構建單元,其包含芳族或雜芳族系統Ar2,其中構建單元(9.3)不同於構建單元(9.2),僅僅在於構建單元(9.2)之膦酸基藉由構建單元(9.3)中之H置換,且構建單元(9.3)與構建單元(9.1)不同
其中構建單元(9.3)較佳由通式(9.3)表示
其中對於與每一其他式(9.3)之構建單元獨立之各式(9.3)之構建單元,Ar2、E2、m、A及b係如關於構建單元(9.2)所定義
在該等聚縮合物之構建單元(9.1)、(9.2)及(9.3)中,芳族或雜芳族系統Ar1及Ar2分別較佳係由以下基團表示或自該等基團衍生:苯基、2-羥苯基、3-羥苯基、4-羥苯基、2-甲氧基苯基、3-甲氧苯基、4-甲氧基苯基、萘基、2-羥萘基、4-羥萘基、2-甲氧基萘基、4-甲氧基萘基。芳族或雜芳族
系統Ar1及Ar2較佳為苯基。
以上所定義之聚縮合物較佳含有由下式表示之另一構建單元(9.4)
其中Y彼此獨立地為相同或不同且為構建單元(9.1)、(9.2)、(9.3)或聚縮合物之其他成分
其中R5為相同或不同且由H、CH3、COOH或具有5至10個C原子之經取代或未經取代之芳族或雜芳族系統表示
其中R6為相同或不同且由H、CH3、COOH或具有5至10個碳原子之經取代或未經取代之芳族或雜芳族系統表示。較佳地,構建單元(9.4)中之R5及R6彼此獨立地相同或不同且由H、COOH及/或甲基表示。
在該縮聚合物中,較佳地
構建單元[(9.1)+(9.2)+(9.3)]:(9.4)之莫耳比在1:0.8至3,較佳1:0.9至2且尤其較佳1:0.95至1.2範圍內。
及/或構建單元(9.1):[(9.2)+(9.3)]之莫耳比在1:10至10:1,較佳1:7至5:1且尤
其較佳1:5至3:1範圍內,及/或構建單元(9.2):(9.3)之莫耳比在1:0.005至1:10,較佳1:0.01至1:1,尤其1:0.01至1:0.2且尤其較佳1:0.01至1:0.1範圍內。
在用於製備該聚縮合物之方法中,聚縮合及引入磷酸基(磷酸化)較佳在反應混合物中進行。較佳地,用於此方法之反應混合物至少含有(9.1a)具有芳族或雜芳族系統Ar1及包含結構單元(ii)-(AO)a-R或由該結構單元組成之側鏈之單體(9.3a)具有芳族或雜芳族系統之單體,該單體(9.3a)在反應期間經部分磷化且由此形成單體(9.2a)及/或在聚縮合物中為構建單元(9.2),(9.4a)具有例如甲醛之醛基之單體,及磷化劑,例如聚磷酸及/或五氧化二磷。
用於獲得以上所定義之聚縮合物之適合方式揭示於WO2010/040612中。
此類型之較佳梳形聚合物可以商標名EPPR 312自BASF SE獲得。在該梳形聚合物中,結構單元-(AO)a-R各自具有5000g/mol之莫耳質量,A為-CH2-CH2-,R為H且所有該等結構單元(ii)-(AO)a-R之莫耳質量總和為該梳形聚合物之莫耳質量的83%,且構建單元(9.1):[(9.2)+(9.3)]之莫耳比為1:4。
適用於本發明之另一種類之聚合物(B)揭示於US 5,879,445中且具有式(10)之結構
其中- A為CxH2x,其中對於該等結構單元-(AO)a-R中之每個A,x(與每一其他x獨立地)係選自2至4範圍內之整數,其中x較佳為2或3,進一步較佳地x=2,其中在各結構單元-(AO)a-R內,基團A為相同或不同- a為選自5至200,較佳8至150,最佳20至135範圍內之整數- R為氫或具有1至4個碳原子之分支鏈或直鏈烷基,其中R較佳選自由氫及甲基組成之群,- Q1為包含2至18個碳原子及可能一或多個雜原子之烴基,- A1為包含1至5個碳原子之伸烷基,- Rj基團彼此獨立地選自由以下組成之群:- A1-PO3H2基團,其中A1具有以上所定義之含義,- 包含1至18個碳原子且能夠帶有-(AO)a-R基團之烷基及- 基團
其中B表示具有2至18個碳原子之伸烷基,
- r為藉由所有Rj基團帶有之結構單元-(AO)a-R的數目,- q為藉由Q所帶有之結構單元-(AO)a-R的數目,- 選擇「r+q」總和以便在該聚合物(B)中,所有該等結構單元-(AO)a-R之莫耳質量總和以該聚合物之莫耳質量計至少為該聚合物(B)之莫耳質量的50%,較佳為90%或大於90%- y為1至3範圍內之整數,其中當y>1時,基團
為相同或不同- Q1、N及Rj基團可在一起形成一或多個環,此環或此等環另外能夠含有一或多個其他雜原子。
用於獲得式(10)之聚合物(B)之適合方式揭示於US 5,879,445中。
基團Q1較佳具有2至12個碳原子(包括2及12)且其更佳具有2至6個碳原子(包括2及6)。有利地,Q1係選自於伸乙基、環己烯或正己烯中。
為一個二價碳原子之載體的伸烷基A1較佳具有1至3個碳原子(包括性)。A1為亞甲基尤其有利。
可能以鹽形式合併之Rj基團較佳選自於-CH2-PO3H2、甲基及-C2H4N(CH2-PO3H2)2基團中。Rj仍更佳表示-CH2-PO3H2基團。
「r+q」總和對應於聚氧烷基化鏈之總數。此總和較佳小於
3。其更佳等於1。
「y」為介於1與3之間(包括1及3)所包含之數目。其較佳等於1。
R較佳為H,A較佳為-CH2-CH2-且a較佳為50。
根據US 5,879,445,如上文所定義之較佳式(10)之化合物為
及
其中a較佳為50。
此類型之較佳聚合物下文稱為Stab 100。在該聚合物Stab 100中,結構單元-(AO)a-R各自具有3000g/mol之莫耳質量,A為-CH2-CH2-,R為H且所有該等結構單元-(AO)a-R之莫耳質量總和為該聚合物之莫耳質量的92%。
不希望受到任何特定理論約束,目前假定存在於聚合物(B)中之結構單元(ii)-(AO)a-R(其中A、a及R係如上文所定義)以非離子空間方式使含有氧化鈰之磨料粒子(A)穩定,同時帶負電陰離子官能基將聚合物(B)錨定至帶正電含有氧化鈰之磨料粒子(A)。假定空間穩定化因存在
於含有氧化鈰之磨料粒子(A)之表面上的結構單元-(AO)a-R之掩蔽(屏蔽)效應所致。因此,在待根據本發明使用的聚合物(B)中,各大分子中之大部分係由掩蔽結構單元-(AO)a-R形成為重要的。對於不具有掩蔽結構單元或不具有足夠部分之掩蔽結構單元之聚合物,可能無法達成此空間穩定化效應,例如其中大分子中之陰離子基團的部分明顯大於以上所定義之待根據本發明使用之聚合物的聚合物(例如形成具有大量負電荷之聚陰離子之羧酸均聚物,像聚丙烯酸及聚天冬胺酸)。至少出於此原因,在該聚合物(B)中提供掩蔽效應之結構單元-(AO)a-R之莫耳質量總和至少為該聚合物(B)之莫耳質量的50%為重要的。另一方面,有必要存在陰離子基團(i)以便使聚合物(B)能錨定至含有氧化鈰之磨料粒子(A)之帶正電表面。另外,為了提供可靠及有效藉由陰離子官能基(i)之錨定及藉由結構單元(ii)-(AO)a-R之掩蔽,在聚合物內不存在陰離子官能基(i)及結構單元(ii)-(AO)a-R之隨機分佈為重要的。
以此方式,即使在6至10範圍內,較佳高達10.8或至少在此pH值範圍之有效子範圍內的pH值下,使含有氧化鈰之磨料粒子(A)之電荷減至最少且同時抑制磨料粒子之凝聚(絮凝)。
帶有低電荷之磨料粒子特別較佳用於拋光像二氧化矽及氮化矽之介電材料的表面,因為當磨料粒子之電荷較低時,磨料粒子與待拋光介電質之帶電表面之間的靜電相互作用降低,該靜電相互作用對CMP製程有害(參見上文)。
尤其對於二氧化矽之化學機械拋光,需要具有大於6之pH值的CMP組成物,因為其允許二氧化矽之鹼性化學水解,該水解支持移除
機制且有助於防止在化學機械拋光製程之後出現可見刮痕。
因此,較佳在根據本發明之化學機械拋光(CMP)組成物中,選擇該或該等如上文所定義之聚合物(B)之濃度以便- 在6至10,較佳高達10.8之pH值範圍內,含有氧化鈰之粒子(A)未發生絮凝及/或- 在6至10範圍內之pH值下,含有氧化鈰之粒子之ζ電位在+30mV與-30mV,較佳+20mV與-20mV之間的範圍內。
尤其較佳為根據本發明之化學機械拋光(CMP)組成物,其
中如上文所定義之聚合物(B)之總量在0.0002wt.-%至1.0wt.-%,較佳0.001wt.-%至0.1wt.-%,更佳0.005wt.-%至0.025wt.-%,進一步較佳0.0075wt.-%至0.01wt.-%範圍內,在每一種情況下均以各別CMP組成物之總重量計。
就此而言,本發明之其他態樣係關於- 一種如上文所定義之聚合物(B)之用途,其用於抑制分散於水性介質中之含有氧化鈰之粒子凝聚及/或用於調整含有氧化鈰之粒子之ζ電位及- 一種用於抑制分散於水性介質中之含有氧化鈰之粒子凝聚及/或調整該等粒子之ζ電位的方法,該方法包含向其中分散含有氧化鈰之粒子之該水性介質中添加有效量之一或多種如上文所定義之聚合物(B)的步驟。
(C)多羥基化合物
對於某些應用,根據本發明之化學機械拋光(CMP)組成物較佳進一步包含
(C)一或多種多羥基化合物。
在較佳情況下,在本發明之CMP組成物中包括一或多種多羥基化合物(C)有助於改善拋光效能,尤其組合二氧化矽之高材料移除速率及氮化矽及/或多晶矽之低材料移除速率。
多羥基化合物(亦稱為多元醇)為每個分子包含兩個或兩個以上醇羥基之有機化合物。多羥基化合物之典型代表為二醇(例如二醇類,包括聚伸烷二醇)、甘油、碳水化合物及糖醇。
較佳多羥基化合物(C)係選自由以下組成之群:甘露糖醇、山梨糖醇、木糖醇、甘露糖、山梨糖、糊精、葡萄糖、明膠、刺雲豆膠、陽離子瓜爾豆膠、膠原蛋白、糊精、黃蓍、丙二醇海藻酸酯、環糊精、甲殼質、玻尿酸、卡梅林纖維素(carmelose)、澱粉、賽普洛膠(cyprogum)、蜂膠、普魯蘭(pullulan),「LAPONITE®(由Rockwood Additives有限公司製造)」、果膠、海藻糖、酪蛋白、蔗糖、麥芽糖、果糖、甘露糖、葡糖醛酸、葡糖胺、聚葡萄糖、陽離子纖維素、葡糖苷酶、葡萄糖苯脎、羥乙基纖維素、聚葡萄胺糖、磷酸澱粉、大豆卵磷脂、三仙膠、羅望子膠、刺槐豆膠、酸莢膠、阿拉伯膠、洋車前籽膠、角叉菜膠(caragynan)、結冷膠、瓜爾膠聚甘油脂肪酸酯、多醣(諸如澱粉、聚葡萄胺糖、褐藻酸、羧甲基纖維素、甲基纖維素、卡德蘭(curdlan)及其衍生物)、三仙膠、愈瘡膠、乳香膠及松香膠葡萄糖酸、葡萄糖(酸)δ內酯及醣苷,尤其烷基聚醣苷。
在較佳情況下,多羥基化合物(C)或多羥基化合物(C)中之一種為式1至6之醣苷
其中R1為烷基、芳基或烷芳基,R2為H、X1、X2、X3、X4、X5、X6、烷基、芳基或烷芳基,R3為H、X1、X2、X3、X4、X5、X6、烷基、芳基或烷芳基,R4為H、X1、X2、X3、X4、X5、X6、烷基、芳基或烷芳基,R5為H、X1、X2、X3、X4、X5、X6、烷基、芳基或烷芳基,醣苷中之單醣單元(X1、X2、X3、X4、X5或X6)之總數在1至20範圍內,且X1至X6為相對應的式1至6中之矩形中所指示的結構單元。
在式1至6之醣苷中,單醣單元(X1、X2、X3、X4、X5或X6)之總數較佳在1至5範圍內。
進一步較佳地,醣苷為式1之醣苷且其中R1為烷基、芳基或烷芳基,R2為H或X1,R3為H或X1,R4為H或X1,R5為H或X1。
尤其較佳地,醣苷為式1a之醣苷
其中R1為烷基、芳基或烷芳基,R12為H、烷基、芳基或烷芳基,較佳為H,R13為H、烷基、芳基或烷芳基,較佳為H,R14為H、烷基、芳基或烷芳基,較佳為H,R15為H、烷基、芳基或烷芳基,較佳為H,且k為1至20,較佳1至5之整數。
較佳地,在式(1a)中,R12、R13、R14及R15為H。
較佳地,在式(1a)中,R1為
其中R16為H、烷基、芳基或烷芳基,且R17為H、烷基、芳基或烷芳基,或R1為CH2R18,且R18為H、烷基、芳基或烷芳基。
尤其較佳為根據本發明之化學機械拋光(CMP)組成物,其中如上文所定義多羥基化合物(C)之總量在0.001wt.-%至2wt.-%,較佳0.01wt.-%至1wt.-%,例如0.02wt.-%至0.05wt.-%範圍內,在每一種情況下均以各別CMP組成物之總重量計。
(D)pH調節劑
進一步較佳地,根據本發明之化學機械拋光(CMP)組成物進一步包含(D)一或多種pH調節劑。
適合之pH調節劑係選自由以下組成之群:氨、KOH、NaOH;M2CO3、M(HCO3)2,其中在每一種情況下M係選自由以下組成之群:K、Na、NH4及四烷基銨、四烷基銨氫氧化物(像氫氧化四甲基銨(TMAH)及氫氧化四乙基銨(TEMH))、經烷基取代之胺(像三甲基胺、三乙基胺、二甲基胺、二乙基胺、甲基胺);乙基胺多胺(像二伸乙基三胺、六亞甲基三胺或優洛托品(urotropin))、聚合亞胺(像聚伸乙基亞胺)、硝酸、磷酸、硫酸、鹽酸、甲酸、膦酸、磺酸,其中氨、KOH、TMAH、TEAH;硝酸、甲酸為較佳。
根據本發明之CMP組成物之pH值在5至10.8,較佳6至10,更佳6.5至9.5,進一步較佳7至9,再進一步較佳7.5至8.5(例如8)範圍內。
尤其較佳為根據本發明之化學機械拋光(CMP)組成物,其中(A)含有氧化鈰之磨料粒子之總量在0.01wt.-%至5wt.-%,較佳0.1wt.-%至1.0wt.-%(例如0.5wt.-%)範圍內,在每一種情況下均以各別CMP組成物之總重量計,及(B)如上文所定義聚合物(B)之總量在0.0002wt.-%至1wt.-%,較佳
0.001wt.-%至0.1wt.-%,更佳0.005wt.-%至0.025wt.-%,進一步較佳0.0075wt.-%至0.01wt.-%範圍內,在每一種情況下均以各別CMP組成物之總重量計,及(C)多羥基化合物之總量在0.001wt.-%至2wt.-%,較佳0.01wt.-%至1wt.-%範圍內,在每一種情況下均以各別CMP組成物之總重量計。
CMP組成物之其他組分
必要時,根據本發明之CMP組成物可進一步含有各種其他組分,包括(但不限於)殺生物劑。殺生物劑不同於如上文所定義之組分(A)、(B)、(C)及(D)。一般而言,殺生物劑為藉由化學或生物方式阻止任何有害有機體、使任何有害有機體無害或對任何有害有機體施加控制作用之化合物。較佳地,殺生物劑為第四銨化合物、基於異噻唑啉酮之化合物、N-經取代之重氮二氧化物或N-羥基-重氮氧化物鹽。更佳地,殺生物劑為N-經取代之重氮二氧化物或N-羥基-重氮氧化物鹽。
製備根據本發明之CMP組成物
在另一態樣中,本發明係關於一種用於製備根據本發明之CMP組成物(如上文所定義)之方法。方法包含在水性介質中將以下組合之步驟
(A)含有氧化鈰之磨料粒子
(B)一或多種如上文所定義之聚合物。
製備CMP組成物之方法大體為已知的。此等方法可應用於製備根據本發明所使用之CMP組成物。此可藉由分散上述組分(A)且將
上述組分(B),且若適宜上述視情況選用之另一組分(C)溶解於水中,且視情況藉由經添加如上文或下文所定義之pH調節劑(D)調整pH值來進行。為達成此目的,可使用常用及標準混合方法及混合設備(諸如攪拌容器、高剪切葉輪、超音波混合器、均質器噴嘴或逆流混合器)。根據本發明之CMP組成物之pH值較佳在5至10.8,較佳6至10,更佳6.5至9.5,進一步較佳7至9,再進一步較佳7.5至8.5範圍內(例如8)調節。
較佳地,用於製備根據本發明之CMP組成物(如上文所定義)之方法包含向包含含有氧化鈰之磨料粒子(A)之水性懸浮液中添加一或多種如上文所定義之聚合物(B)的步驟。
使用本發明之CMP組成物進行化學機械拋光
在另一態樣中,本發明係關於一種用於製造半導體裝置之方法,其包含在如上文所定義之根據本發明之化學機械拋光(CMP)組成物存在下,化學機械拋光基板之步驟。在化學機械拋光步驟中,CMP組成物之pH值在5至10.8,較佳6至10,更佳6.5至9.5,進一步較佳7至9,再進一步較佳7.5至8.5範圍內(例如8)。
化學機械拋光步驟大體為已知的且可在製造具有積體電路之晶圓中通常用於CMP之條件下藉由該等方法及設備進行。
在根據本發明之較佳方法中,基板包含- 由二氧化矽組成之表面區域或層及- 由氮化矽或多晶矽組成之表面區域或層。
在較佳情況下,待藉由根據本發明之CMP組成物拋光之二氧化矽層為二氧化矽之基板層,其為淺溝槽隔離(STI)裝置或其部分。
實施例
在下文中進一步藉助於實施例及比較實施例說明本發明。製備CMP組成物:
向市售可得之膠狀氧化鈰溶液中添加如下文所定義之聚合物(B)及如下文所定義之視情況選用之多羥基化合物(C)。
使用以下聚合物(B)
為了比較,亦測試不含有任何聚合物(B)之CMP組成物。
藉由添加氨水溶液(0.1%)或HNO3(0.1%)來調節各組成物之pH值。用pH值組合電極(Schott,blue line 22 pH)量測pH值。
氧化鈰(濕沈澱,來自Rhodia之商標名HC 60或煙霧狀,來自NanoPhase之商標名NanoArc 6440)濃度在每一種情況下以各別CMP組成物之重量計均為0.5wt.-%。
自供應商獲得之濕沈澱氧化鈰粒子(例如Rhodia HC60)具有60nm之平均一次粒徑(如使用BET表面積量測所測定)及99nm之平均二次粒徑(d50值)(如經由Horiba儀器使用動態光散射技術所測定)。
自供應商獲得之煙霧狀氧化鈰粒子(例如NanoArc 6440)具有30nm之平均一次粒徑(如使用BET表面積量測所測定)及130nm之平
均二次粒徑(d50值)(如經由Horiba儀器使用動態光散射技術所測定)。
若不另外指示,則使用濕沈澱之氧化鈰。對於有關CMP組成物之組分之其他資訊,參見下文中「結果」部分中之表格。
CMP實驗
若干比較CMP組成物(參見結果部分中之表格)用於化學機械拋光直徑為200mm經二氧化矽、氮化矽及多晶矽塗佈之晶圓。
拋光參數如下:CMP裝置:Strasbaugh nSpire(型號6EC),ViPRR浮動扣環載體;向下壓力:2.0磅/平方吋(140毫巴);背面壓力:0.5磅/平方吋(34.5毫巴);扣環壓力:2.5磅/平方吋(172毫巴);拋光台/載體速度:95/85rpm;漿體流動速率:200ml/min;拋光時間:60s;襯墊調整:就地(4磅,17.8N);拋光墊:IC1000 A2疊層襯墊,x、yk或k開槽(R&H);襯底膜:Strasbaugh,DF200(136孔);調整盤:3M S60;為研究二氧化矽(SiO2)之材料移除,使用塗佈有藉由使用正矽酸四乙酯(TEOS)作為前驅體之電漿增強型化學氣相沈積獲得之二氧化矽層的基板。
為研究氮化矽(Si3N4)之材料移除,使用塗佈有藉由電漿增
強型化學氣相沈積獲得之氮化矽層之基板。
為研究多晶矽(poly-Si)之材料移除,使用塗佈有藉由化學氣相沈積獲得之多晶矽層之基板。
對於二氧化矽,基於1.9kg/l之SiO2密度,基於化學機械拋光之前及之後的重量差異測定材料移除。藉助於Sartorius LA310 S天平量測重量。對於氮化矽及多晶矽,基於化學機械拋光之前及之後基板之膜厚度差異測定材料移除。藉助於Filmmetrics F50反射計量測膜厚度(直徑掃描之平均厚度)。對於計算材料移除速率(MRR),用以上所測定之總材料移除除以主要拋光步驟之時間。
移除二氧化矽相對於氮化矽(SiO2/Si3N4)之選擇性為二氧化矽之材料移除速率與氮化矽之材料移除速率之間的比率。移除二氧化矽相對於多晶矽(SiO2/poly-Si)之選擇性為二氧化矽之材料移除速率與多晶矽之材料移除速率之間的比率。
CMP實驗結果
CMP實驗結果在下文表1-8中給出。
包含上述所指示量之EPPR312作為聚合物(B)的CMP組成物在表1中所給出之pH值下為穩定的。在一些情況下,在EPPR312存在
下提高SiO2/Si3N4及/或SiO2/poly-Si選擇性。
與不包含聚合物(B)或包含EPPR312作為聚合物(B)而無多羥基化合物(C)之CMP組成物相比,在表2中所列之pH值下將作為聚合物(B)之EPPR312與多羥基化合物(C)組合導致有效提高SiO2/Si3N4及SiO2/poly-Si之選擇性。
包含上述所指示量之Melpers 0045作為聚合物(B)的CMP組成物在表3中所給出之pH值下穩定。在Melpers 0045存在下,尤其在pH=9下明顯提高SiO2/Si3N4及/或SiO2/poly-Si之選擇性。
PEG為可自Aldrich獲得之具有10000g/mol之莫耳質量的聚乙二醇。在表4之最後兩種CMP組成物中,磨料粒子(A)為煙霧狀氧化鈰。
與不包含聚合物(B)之CMP組成物相比,在表4中所給出之pH值下將作為聚合物(B)之Melpers 0045與以上所列之多羥基化合物(C)組合產生適合之SiO2/Si3N4及SiO2/poly-Si之選擇性。
包含上述所指示量之Stab 100作為聚合物(B)的CMP組成物在pH=8下穩定,參見表5。在Stab 100存在下SiO2/Si3N4及SiO2/poly-Si之選擇性未明顯改變。
與不包含聚合物(B)或包含Stab 100作為聚合物(B)而無多羥基化合物(C)的CMP組成物相比,在pH=8下將作為聚合物(B)之Stab 100與表6中所列之多羥基化合物(C)組合導致提高SiO2/Si3N4及SiO2/poly-Si之選擇性。
包含上述所指示量之Stab 100作為聚合物(B)的CMP組成物在pH=8下穩定,參見表7。在Stab 100存在下SiO2/Si3N4及SiO2/poly-Si之選擇性明顯提高。
與不包含聚合物(B)或包含Stab 100作為聚合物(B)而無多羥基化合物(C)的CMP組成物相比,在pH=8下將作為聚合物(B)之Stab0557與表8中所列之多羥基化合物(C)組合導致提高SiO2/Si3N4及
SiO2/poly-Si之選擇性。
量測ζ電位
對於若干根據本發明之CMP組成物以及用於比較非根據本發明之CMP組成物,使用Zetasizer Nano(供應商:Malvern)隨4至10之pH值範圍內之pH值變化量測ζ電位。在10mmol/l KCl存在下在稀釋至0.1wt.-%之氧化鈰含量之後,在各別CMP組成物所具有之pH值下開始量測。為進行其他量測,藉由經NaOH或HCl自動滴定來調節各別CMP組成物之pH值。
所測試組成物中之聚合物濃度如下:
1. 無聚合物(比較組成物)
2. 0.002wt.-%聚天冬胺酸(比較組成物)
3. 0.002wt.-% Melpers 0045
4. 0.002wt.-% EPPR312
5. 0.001wt.-% EPPR312
6. 0.002wt.-% Stab 100。
結果(參見圖1)展示根據本發明所使用之聚合物(B)能夠針對電泳激發掩蔽含有氧化鈰之磨料粒子之電荷。因此,由電泳遷移率計算出之ζ電位之絕對值明顯低於不包含任何聚合物或包含聚陰離子而無大量具有該掩蔽效應之結構單元的CMP組成物中(就聚天冬胺酸之情況而言)。在聚天冬胺酸存在下,由於聚陰離子之大量負電荷,ζ電位之符號為負且ζ電位之絕對值較高。
儘管在6至10範圍內之pH值下根據本發明之CMP組成物
中之含有氧化鈰之粒子的低ζ電位,但由於氧化鈰粒子之空間穩定化,因此在此pH值範圍內或至少在此pH值範圍之有效子範圍內未發生氧化鈰凝結。
穩定性測試
如下製備包含(A)含有氧化鈰之粒子之CMP組成物:在攪拌下向100ml超純水中添加含有氧化鈰之粒子(Rhodia HC60)。含有氧化鈰之粒子(A)之終濃度為0.5wt.-%。pH值經氨調節至以下表9中所給出之值。
如下製備包含(A)含有氧化鈰之粒子及(B)聚合物Stab 100(參見上文)之CMP組成物:向100ml超純水中添加Stab 100以達到0.01wt.-%之濃度。在攪拌下添加含有氧化鈰之粒子(Rhodia HC 60)。含有氧化鈰之粒子(A)之終濃度為0.5wt.-%。pH值經氨調節至以下表9中所給出之值。
將CMP組成物儲存三天。每天在儲存之不同時間時使用Horiba LB 550 V(動態光散射DLS)量測粒徑分佈。結果在表9中給出。
對於不含聚合物(B),pH值經調節至10之CMP組成物,因為氧化鈰完全凝結所以在1天後可不再量測粒徑分佈。相比之下,含有0.01wt.-%之聚合物(B),pH值經調節至10之CMP組成物經三天保持穩定。上述情況適用於含有0.01wt.-%之聚合物(B)且pH值經調節至10.8之CMP組成物。
對於不含聚合物(B),pH值調節至9之CMP組成物,因為氧化鈰完全凝結所以在第三天時可不再量測粒徑分佈。相比之下,含有0.01
wt.-%之聚合物(B)且pH值經調節至9之CMP組成物經三天保持穩定。
長期穩定性測試
如下製備包含(A)含有氧化鈰之粒子之CMP組成物:在攪拌下向100ml超純水中添加含有氧化鈰之粒子(Rhodia HC 60)。含有氧化鈰之粒子(A)之終濃度為0.5wt.-%。pH值經氨調節至以下表10中所給出之值或pH值經KOH調節至以下表12中所給出之值。
如下製備包含(A)含有氧化鈰之粒子及(B)聚合物Stab 100(參見上文)之CMP組成物:向100ml超純水中添加Stab 100以達到0.01wt.-%之濃度。在攪拌下添加含有氧化鈰之粒子(Rhodia HC 60)。含有氧化鈰之粒子(A)之終濃度為0.5wt.-%。pH值經氨調節至以下表11中所給出之值或pH經值KOH調節至以下表13中所給出之值。
將CMP組成物儲存四十(40)天。在五(5)天、十二(12)天、二十六(26)天及四十(40)天後,在儲存之不同時間時使用Horiba LB 550 V(動態光散射DLS)量測粒徑分佈。結果在表10、11、12及13中給出。
如在以上實施例及表格中可見,就SiO2優於Si3N4及SiO2優於poly-Si之選擇性及材料移除速率而言,包含(A)含有氧化鈰之粒子及(B)一或多種聚合物之根據本發明的CMP組成物產生長期穩定分散液以及高拋光效能。
Claims (18)
- 一種化學機械拋光(CMP)組成物,其包含以下成分:(A)含有氧化鈰之磨料粒子(B)一或多種聚合物,其中該等聚合物(B)之各大分子包含(i)一或多個陰離子官能基(ii)及(iii)一或多個結構單元-(AO)a-R其中在與每一其他結構單元-(AO)a-R獨立之各結構單元-(AO)a-R中A為CxH2x,其中對於該等結構單元-(AO)a-R中之每個A,x與每一其他x獨立地選自2至4範圍內之整數,其中x較佳為2或3,進一步較佳地x=2其中在各結構單元-(AO)a-R內,基團A為相同或不同a為選自5至200,較佳8至150,最佳20至135範圍之整數,R為氫或具有1至4個碳原子之分支鏈或直鏈烷基,其中在該聚合物(B)中,所有結構單元(ii)之莫耳質量總和至少為該聚合物(B)之莫耳質量的50%。
- 如前述申請專利範圍任一項之化學機械拋光(CMP)組成物,其中選擇該或該等聚合物(B)之濃度以便- 在6至10之pH值範圍內未發生含有氧化鈰之粒子(A)絮凝-及/或 - 在6至10範圍內之pH值下,含有氧化鈰之粒子之ζ電位在+30mV與-30mV之間的範圍內。
- 如前述申請專利範圍任一項之化學機械拋光(CMP)組成物,其中在該聚合物(B)或該等聚合物(B)中之至少一種之該等大分子中,該或該等陰離子官能基選自由羧酸基、磺酸基、硫酸基、磷酸基及膦酸基組成之群。
- 如前述申請專利範圍任一項之化學機械拋光(CMP)組成物,其中在該聚合物(B)或該等聚合物(B)中之至少一種中該或該等結構單元(ii)-(AO)a-R中之每一者之莫耳質量為500g/mol或大於500g/mol,較佳1000g/mol或大於1000g/mol,更佳2000g/mol或大於2000g/mol,最佳3000g/mol或大於3000g/mol及/或所有該等結構單元(ii)-(AO)a-R之莫耳質量總和為該聚合物(B)之該莫耳質量的60%或大於60%,較佳70%或大於70%,最佳80%或大於80%。
- 如前述申請專利範圍任一項之化學機械拋光(CMP)組成物,其中該聚合物(B)或該等聚合物(B)中之至少一種係選自由梳形聚合物及嵌段共聚物組成之群。
- 如前述申請專利範圍任一項之化學機械拋光(CMP)組成物,其中該聚合物(B)或該等聚合物(B)中之至少一種為包含以下之梳形聚合物(i)骨幹,一或多個陰離子官能基與其鍵聯及 (ii)一或多個側鏈,其各自包含結構單元-(AO)a-R其中在該梳形聚合物中,所有該等結構單元(ii)-(AO)a-R之莫耳質量總和至少為該梳形聚合物之莫耳質量的50%。
- 如申請專利範圍第1項至第6項中任一項之化學機械拋光(CMP)組成物,其中該梳形聚合物包含- 構建單元,其各自包含一或多個陰離子官能基及- 側鏈,其各自包含結構單元(ii)-(AO)a-R,其中A為CxH2x,其中對於該等結構單元-(AO)a-R中之每個A,x與每一其他x獨立地選自2至4範圍內之整數,其中x較佳為2或3,進一步較佳地x=2其中在各結構單元-(AO)a-R內,該等基團A為相同或不同a為選自5至200,較佳8至150,最佳20至135範圍內之整數R為氫或具有1至4個碳原子之分支鏈或直鏈烷基,其中包含陰離子官能基之構建單元中之一或多個係選自通式(7.1)、(7.2)、(7.3)及(7.4):
- 如申請專利範圍第1項至第6項中任一項之化學機械拋光(CMP)組成物,其中該梳形聚合物(B)可藉由以下單體與結構單元(ii)-(AO)a-R之共聚合獲得(8.1)丙烯酸及(8.2)一或多個大分子單體,其各自包含可聚合雙鍵,較佳乙烯基、烯丙基、異戊二烯基、丙烯酸酯基、甲基丙烯酸酯基或順丁烯二酸酯基之雙鍵,在結構單元(ii)-(AO)a-R中A為CxH2x,其中對於該等結構單元-(AO)a-R中之每個A,x與每一其他x獨立地選自2至4範圍內之整數,其中x較佳為2或3,進一步較佳地x=2其中在各結構單元-(AO)a-R內,該等基團A為相同或不同a為選自5至200,較佳8至150,最佳20至135範圍內之整數R為氫或具有1至4個碳原子之分支鏈或直鏈烷基,其中選擇單體(8.1)及(8.2)之量以便獲得梳形聚合物,其中在該梳形聚合物中,所有該等結構單元(ii)-(AO)a-R之莫耳質量總和至少為該梳形聚合物之莫耳質量的70%。
- 如申請專利範圍第1項至第6項中任一項之化學機械拋光(CMP)組成物,其中該梳形聚合物(B)為含有以下之聚縮合物 (9.1)至少一個構建單元,其包含芳族或雜芳族系統Ar1及包含結構單元(ii)-(AO)a-R或由結構單元(ii)-(AO)a-R組成之側鏈其中在與每一其他構建單元(9.1)獨立之各構建單元(9.1)中A為CxH2x,其中對於該等結構單元-(AO)a-R中之每個A,x與每一其他x獨立地選自2至4範圍內之整數,其中x較佳為2或3,進一步較佳地x=2其中在各結構單元-(AO)a-R內,該等基團A為相同或不同a為選自5至200,較佳8至150,最佳20至135範圍內之整數R為氫或具有1至4個碳原子之分支鏈或直鏈烷基,其中該等構建單元(9.1)較佳由通式(9.1)表示
- 如申請專利範圍第1項至第4項中任一項之化學機械拋光(CMP)組成物,其中該聚合物(B)或該等聚合物(B)中之至少一種對應於式(10)
- 如前述申請專利範圍任一項之化學機械拋光(CMP)組成物,其進一步包含(C)一或多種多羥基化合物。
- 如前述申請專利範圍任一項之化學機械拋光(CMP)組成物,其進一步包含(D)一或多種pH調節劑。
- 如前述申請專利範圍任一項之化學機械拋光(CMP)組成物,其中該組成物具有5至10.8,較佳6至10範圍內之pH值。
- 如前述申請專利範圍任一項之化學機械拋光(CMP)組成物,其包含(A)以各別CMP組成物之總重量計,含有總量在0.01wt.-%至5wt.-%範圍內之氧化鈰之磨料粒子,及/或(B)以該各別CMP組成物之該總重量計,總量在0.0002wt.-%至1wt.-%範圍內如申請專利範圍第1項至第10項中所定義之聚合物(B),及/或(C)以該各別CMP組成物之該總重量計,總量在0.001wt.-%至2wt.-%範圍內之多羥基化合物。
- 一種用於製造半導體裝置之方法,其包含在如申請專利範圍第1項至第14項中任一項中所定義之化學機械拋光(CMP)組成物存在下,化學機械拋光基板。
- 如申請專利範圍第15項之方法,其中該基板包含- 由二氧化矽組成之表面區域或層及- 由氮化矽或多晶矽組成之表面區域或層。
- 一種如申請專利範圍第1項至第10項中所定義之聚合物(B)之用途其用於抑制分散於水性介質中之含有氧化鈰之粒子凝聚及/或用於調整含有氧化鈰之粒子之ζ電位。
- 一種用於抑制分散於水性介質中之含有氧化鈰之粒子凝聚及/或調整該等粒子之ζ電位的方法,該方法包含向其中分散該等含有氧化鈰之粒子之該水性介質中添加有效量之一或多種如申請專利範圍第1項至第10項中所定義之聚合物(B)的步驟。