SU963963A1 - Способ получени кварцевого стекла - Google Patents

Способ получени кварцевого стекла Download PDF

Info

Publication number
SU963963A1
SU963963A1 SU813280227A SU3280227A SU963963A1 SU 963963 A1 SU963963 A1 SU 963963A1 SU 813280227 A SU813280227 A SU 813280227A SU 3280227 A SU3280227 A SU 3280227A SU 963963 A1 SU963963 A1 SU 963963A1
Authority
SU
USSR - Soviet Union
Prior art keywords
quartz glass
heating
stabilization
making quartz
carried out
Prior art date
Application number
SU813280227A
Other languages
English (en)
Inventor
Валентин Никифорович Шубин
Виктор Константинович Леко
Татьяна Ивановна Киселева
Юрий Анатольевич Опыхтин
Original Assignee
Государственный Научно-Исследовательский Институт Кварцевого Стекла
Гусевский Завод Особо Чистого Кварцевого Стекла
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Государственный Научно-Исследовательский Институт Кварцевого Стекла, Гусевский Завод Особо Чистого Кварцевого Стекла filed Critical Государственный Научно-Исследовательский Институт Кварцевого Стекла
Priority to SU813280227A priority Critical patent/SU963963A1/ru
Application granted granted Critical
Publication of SU963963A1 publication Critical patent/SU963963A1/ru

Description

В таблице приведены сравнительные данные по времени стабилизации по известному и предлагаемому способам.
Граничные услови  температуры и времени температурной стабилизации обусловлены особенностью сырь . Дл  горного
хрустал  и жильного кварца стабилизацию осуществл ют при 1300-1400° С в течение минимального времени 10 Z) с; дл  жильного кварца с большим количеством газожидких включений необходимы соответственно меньша  температура (1100- 1200° С) и больше времени (10 /)Ь9-1,эд с)..

Claims (1)

  1. Формула изобретения
    Способ получения кварцевого стекла, включающий нагрев сырья в графитовых тиглях 1100—1400° С, стабилизацию при: этой температуре, дальнейший нагрев до 1800° С в вакууме и охлаждение, отличающийся тем, что, с целью повышения производительности, нагрев и стабилизацию ведут при атмосферном давлении, причем радиальный температурный градиент нагрева составляет 1—1400° С-см-1, а стабилизацию ведут в течение 10 · О’·5-1·9 с, где D — внутренний диаметр тигля, см.
SU813280227A 1981-04-21 1981-04-21 Способ получени кварцевого стекла SU963963A1 (ru)