RU2479501C1

RU2479501C1 - Mixture for making enamel coating

Info

Publication number: RU2479501C1
Application number: RU2011150991/03A
Authority: RU
Inventors: Юлия Алексеевна Щепочкина
Original assignee: Юлия Алексеевна Щепочкина
Priority date: 2011-12-14
Filing date: 2011-12-14
Publication date: 2013-04-20

Abstract

FIELD: chemistry.

SUBSTANCE: invention relates to compositions of mixtures for making enamel coating on ceramic articles. The mixture for making enamel coating contains the following, pts.wt: quartz 20.0-25.0; red lead 4.0-5.0; chalk 2.0-3.0; crystalline boric acid 2.0-3.0; volcanic ash 15.0-20.0. The coating has water resistance not lower than hydrolytic class III. The prepared components are fed in the required amounts, mixed and melted at temperature of 1500-1550°C. The melt is granulated in water. The granulated material is ground until complete passage through sieve No.0056 and a suspension with moisture content of 45-50% is prepared. The suspension is deposited onto the surface of articles and fixed by firing at temperature of 1150-1200°C.

EFFECT: high water resistance of the coating.

1 tbl

Description

Изобретение относится к составам масс для получения эмалевого покрытия на керамических изделиях.The invention relates to compositions of the masses to obtain an enamel coating on ceramic products.

Известна масса для получения эмалевого покрытия следующего состава, вес.ч.: кварц 10,0; свинцовый сурик 20,0; мел 2,5; борная кислота кристаллическая 7,0 [1].Known mass for the enamel coating of the following composition, parts by weight: quartz 10.0; lead minium 20.0; chalk 2.5; crystalline boric acid 7.0 [1].

Задачей изобретения является повышение водостойкости эмалевого покрытия.The objective of the invention is to increase the water resistance of the enamel coating.

Технический результат достигается тем, что масса для получения эмалевого покрытия, содержащая кварц, свинцовый сурик, мел, борную кислоту кристаллическую, дополнительно содержит вулканический пепел при следующем соотношении компонентов, вес.ч.: кварц 20,0-25,0; свинцовый сурик 4,0-5,0; мел 2,0-3,0; борная кислота кристаллическая 2,0-3,0; вулканический пепел 15,0-20,0.The technical result is achieved in that the mass to obtain an enamel coating containing quartz, lead red oxide, chalk, crystalline boric acid, additionally contains volcanic ash in the following ratio of components, parts by weight: quartz 20.0-25.0; lead red lead 4.0-5.0; chalk 2.0-3.0; crystalline boric acid 2.0-3.0; volcanic ash 15.0-20.0.

Вулканический пепел - это полиминеральная порода, представленная кварцем, полевым пшатом, биотитом, цеолитом, кристаллитом, вулканическим стеклом, графитом, магнетитом, обломками полиминеральных и окремненных пород. Химический состав пепла, мас.%: SiO₂ 71,6; TiO₂ 0,31; Al₂O₃ 14,29; Fе₂O₃ 2,26; MnO 0,04; CaO 1,8; MgO 0,7; K₂O 3,54; Na₂O 3,42; Р₂О₅ 0,08; SO₃ 0,05; п.п.п. 2,02; SiO_{2 аморф.} 4,8; SiO_{2 кварц.} 10,44.Volcanic ash is a polymineral rock represented by quartz, feldspar, biotite, zeolite, crystallite, volcanic glass, graphite, magnetite, fragments of polymineral and silicified rocks. The chemical composition of the ash, wt.%: SiO ₂ 71.6; TiO ₂ 0.31; Al ₂ O ₃ 14.29; Fe ₂ O ₃ 2.26; MnO 0.04; CaO 1.8; MgO 0.7; K ₂ O 3.54; Na ₂ O 3.42; P ₂ O ₅ 0.08; SO ₃ 0.05; p.p.p. 2.02; SiO _{2 amorph.} 4.8; SiO _{2 quartz.} 10.44.

В таблице приведены составы массы для получения эмалевого покрытия.The table shows the composition of the mass to obtain an enamel coating.

ТаблицаTable СоставStructure Компоненты, вес.ч.Components, parts by weight КварцQuartz Свинцовый сурикRed lead Мелa piece of chalk Борная кислота кристаллическаяCrystalline boric acid Вулканический пепелVolcanic ash 1one 25,025.0 4,04.0 2,02.0 3,03.0 15,015.0 22 22,522.5 4,54,5 2,52,5 2,52,5 17,517.5 33 20,020,0 5,05,0 3,03.0 2,02.0 20,020,0

Водостойкость эмалевого покрытия (дня всех составов, приведенных в таблице) - III гидролитический класс.Water resistance of enamel coating (day of all compounds listed in the table) - III hydrolytic class.

Подготовленные компоненты дозируют в требуемых количествах, смешивают и сплавляют при температуре 1500-1550°С. Расплав гранулируют в воду, гранулят размалывают до полного прохождения через сетку №0056 и готовят суспензию с влажностью 45-50%. Суспензию наносят на поверхность изделий и закрепляют обжигом при температуре 1150-1200°С.The prepared components are metered in the required quantities, mixed and alloyed at a temperature of 1500-1550 ° C. The melt is granulated into water, the granulate is milled until it passes through mesh No. 0056 and a suspension with a moisture content of 45-50% is prepared. The suspension is applied to the surface of the products and fixed by firing at a temperature of 1150-1200 ° C.

Источники информацииInformation sources

1. Новгородскiй М.П. Керамика. - СПб.: Изданiе В.И.Губинскаго, 1911. - С.29-30.1. Novgorodsky M.P. Ceramics. - St. Petersburg: Published by V.I. Gubinskago, 1911. - P.29-30.

Claims

A mass for obtaining an enamel coating containing quartz, lead minium, chalk, crystalline boric acid, characterized in that it further comprises volcanic ash in the following ratio of components, parts by weight: quartz 20.0-25.0; lead red lead 4.0-5.0; chalk 2.0-3.0; crystalline boric acid 2.0-3.0; volcanic ash 15.0-20.0.