RU2479505C1

RU2479505C1 - Mixture for making enamel coating

Info

Publication number: RU2479505C1
Application number: RU2011151130/03A
Authority: RU
Inventors: Юлия Алексеевна Щепочкина
Original assignee: Юлия Алексеевна Щепочкина
Priority date: 2011-12-14
Filing date: 2011-12-14
Publication date: 2013-04-20

Abstract

FIELD: chemistry.

SUBSTANCE: invention relates to compositions of mixtures for making enamel coating on ceramic articles. The mixture for making enamel coating contains the following, pts.wt: quartz 73.0-75.0; red lead 6.0-10.0; chalk 4.5-5.5; crystalline boric acid 4.5-5.5; bone ash 4.5-5.5; zinc oxide 2.5-3.5. The coating has water resistance not lower than hydrolytic class II. The prepared components are fed in the required amounts, mixed and melted at temperature of 1400-1450°C. The suspension is deposited on the surface of articles and fixed by firing at temperature of 1050-1150°C.

EFFECT: high water resistance of the coating.

1 tbl

Description

Изобретение относится к составам масс для получения эмалевого покрытия на керамических изделиях.The invention relates to compositions of the masses to obtain an enamel coating on ceramic products.

Известна масса для получения эмалевого покрытия следующего состава, вес. ч.: кварц 10,0; свинцовый сурик 20,0; мел 2,5; борная кислота кристаллическая 7,0 [1].Known mass to obtain an enamel coating of the following composition, weight. hours: quartz 10.0; lead minium 20.0; chalk 2.5; crystalline boric acid 7.0 [1].

Задачей изобретения является повышение водостойкости эмалевого покрытия.The objective of the invention is to increase the water resistance of the enamel coating.

Технический результат достигается тем, что масса для получения эмалевого покрытия, содержащая кварц, свинцовый сурик, мел, борную кислоту кристаллическую, дополнительно содержит костяную золу и оксид цинка при следующем соотношении компонентов, вес. ч.: кварц 73,0-75,0; свинцовый сурик 6,0-10,0; мел 4,5-5,5; борная кислота кристаллическая 4,5-5,5; костяная зола 4,5-5,5; оксид цинка 2,5-3,5.The technical result is achieved in that the mass to obtain an enamel coating containing quartz, lead red oxide, chalk, crystalline boric acid, additionally contains bone ash and zinc oxide in the following ratio of components, weight. hours: quartz 73.0-75.0; lead red lead 6.0-10.0; chalk 4.5-5.5; crystalline boric acid 4.5-5.5; bone ash 4.5-5.5; zinc oxide 2.5-3.5.

В таблице приведены составы массы для получения эмалевого покрытия.The table shows the composition of the mass to obtain an enamel coating.

СоставStructure Компонент, вес.ч.:Component parts by weight: КварцQuartz Свинцовый сурикRed lead Мелa piece of chalk Борная кислота кристаллическаяCrystalline boric acid Костяная золаBone ash Оксид цинкаZinc oxide 1one 75,075.0 6,06.0 5,55.5 5,55.5 4,54,5 3,53,5 22 74,074.0 8,08.0 5,05,0 5,05,0 5,05,0 3,03.0 33 73,073.0 10,010.0 4,54,5 4,54,5 5,55.5 2,52,5

Водостойкость эмалевого покрытия (для всех составов, приведенных в таблице) не ниже II гидролитического класса.The water resistance of the enamel coating (for all compositions listed in the table) is not lower than II hydrolytic class.

Подготовленные компоненты дозируют в требуемых количествах, смешивают и сплавляют при температуре 1400-1450°С. Расплав гранулируют в воду, гранулят размалывают до полного прохождения через сетку №0056 и готовят суспензию с влажностью 45-50%. Суспензию наносят на поверхность изделий и закрепляют обжигом при температуре 1050-1150°С.The prepared components are metered in the required quantities, mixed and alloyed at a temperature of 1400-1450 ° C. The melt is granulated into water, the granulate is milled until it passes through mesh No. 0056 and a suspension with a moisture content of 45-50% is prepared. The suspension is applied to the surface of the products and fixed by firing at a temperature of 1050-1150 ° C.

Источник информацииThe source of information

1. Новгородскiй М.П. Керамика. - СПб.: Издание В.И.Губинскаго, 1911. - С.29-30.1. Novgorodsky M.P. Ceramics. - SPb .: Edition of V.I. Gubinskago, 1911. - P.29-30.

Claims

A mass for producing an enamel coating containing quartz, lead minium, chalk, crystalline boric acid, characterized in that it further comprises bone ash and zinc oxide in the following ratio of components, parts by weight: quartz 73.0-75.0; lead red lead 6.0-10.0; chalk 4.5-5.5; crystalline boric acid 4.5-5.5; bone ash 4.5-5.5; zinc oxide 2.5-3.5.