RU2318773C1 - Ceramic mix - Google Patents
Ceramic mix Download PDFInfo
- Publication number
- RU2318773C1 RU2318773C1 RU2006121177/03A RU2006121177A RU2318773C1 RU 2318773 C1 RU2318773 C1 RU 2318773C1 RU 2006121177/03 A RU2006121177/03 A RU 2006121177/03A RU 2006121177 A RU2006121177 A RU 2006121177A RU 2318773 C1 RU2318773 C1 RU 2318773C1
- Authority
- RU
- Russia
- Prior art keywords
- clay
- nepheline
- ceramic
- caustic magnesite
- ceramic mix
- Prior art date
Abstract
Description
Изобретение относится к области технологии силикатов и касается составов керамических масс, используемых в производстве облицовочной плитки.The invention relates to the field of technology of silicates and relates to compositions of ceramic masses used in the manufacture of tiles.
Известна керамическая масса, содержащая, мас.%: глина 40,0-60,0; молотый стеклобой 40,0-60,0 (1).Known ceramic mass containing, wt.%: Clay 40,0-60,0; ground cullet 40.0-60.0 (1).
Задача изобретения состоит в повышении прочности изделий, полученных из керамической массы.The objective of the invention is to increase the strength of products obtained from ceramic mass.
Технический результат достигается тем, что керамическая масса, содержащая глину и молотый стеклобой, дополнительно включает нефелин и каустический магнезит при следующем соотношении компонентов, мас.%: глина 45,0-50,0; молотый стеклобой 20,0-25,0; нефелин 20,0-25,0; каустический магнезит 5,0-10,0.The technical result is achieved in that the ceramic mass containing clay and ground cullet additionally includes nepheline and caustic magnesite in the following ratio of components, wt.%: Clay 45.0-50.0; ground cullet 20.0-25.0; nepheline 20.0-25.0; caustic magnesite 5.0-10.0.
В таблице приведены составы керамической массы.The table shows the composition of the ceramic mass.
Стеклобой и нефелин размалывают до получения порошка с удельной поверхностью 2000-2500 см2/г, смешивают с каустическим магнезитом, добавляют глину и готовят керамическую массу с влажностью 18-22%. Массу тщательно перемешивают и формуют из нее пластическим способом плитку, которую сушат и обжигают при температуре 930-970°С.Cullet and nepheline are ground to obtain a powder with a specific surface of 2000-2500 cm 2 / g, mixed with caustic magnesite, clay is added and a ceramic mass with a moisture content of 18-22% is prepared. The mass is thoroughly mixed and molded from it in a plastic way, which is dried and fired at a temperature of 930-970 ° C.
Источники информацииInformation sources
1. SU 622789, С04В 33/00, 1978.1. SU 622789, C04B 33/00, 1978.
Claims (1)