RU2016149096A - Химический состав для изготовления пустотелых сферических стеклянных частиц, отличающихся высокой прочностью на сжатие - Google Patents
Химический состав для изготовления пустотелых сферических стеклянных частиц, отличающихся высокой прочностью на сжатие Download PDFInfo
- Publication number
- RU2016149096A RU2016149096A RU2016149096A RU2016149096A RU2016149096A RU 2016149096 A RU2016149096 A RU 2016149096A RU 2016149096 A RU2016149096 A RU 2016149096A RU 2016149096 A RU2016149096 A RU 2016149096A RU 2016149096 A RU2016149096 A RU 2016149096A
- Authority
- RU
- Russia
- Prior art keywords
- spherical glass
- hollow spherical
- glass particle
- glass particles
- metal
- Prior art date
Links
Classifications
-
- C—CHEMISTRY; METALLURGY
- C03—GLASS; MINERAL OR SLAG WOOL
- C03B—MANUFACTURE, SHAPING, OR SUPPLEMENTARY PROCESSES
- C03B19/00—Other methods of shaping glass
- C03B19/08—Other methods of shaping glass by foaming
-
- C—CHEMISTRY; METALLURGY
- C03—GLASS; MINERAL OR SLAG WOOL
- C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
- C03C11/00—Multi-cellular glass ; Porous or hollow glass or glass particles
- C03C11/002—Hollow glass particles
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B22—CASTING; POWDER METALLURGY
- B22D—CASTING OF METALS; CASTING OF OTHER SUBSTANCES BY THE SAME PROCESSES OR DEVICES
- B22D25/00—Special casting characterised by the nature of the product
- B22D25/005—Casting metal foams
-
- C—CHEMISTRY; METALLURGY
- C03—GLASS; MINERAL OR SLAG WOOL
- C03B—MANUFACTURE, SHAPING, OR SUPPLEMENTARY PROCESSES
- C03B19/00—Other methods of shaping glass
- C03B19/10—Forming beads
- C03B19/107—Forming hollow beads
-
- C—CHEMISTRY; METALLURGY
- C03—GLASS; MINERAL OR SLAG WOOL
- C03B—MANUFACTURE, SHAPING, OR SUPPLEMENTARY PROCESSES
- C03B19/00—Other methods of shaping glass
- C03B19/10—Forming beads
- C03B19/108—Forming porous, sintered or foamed beads
-
- C—CHEMISTRY; METALLURGY
- C03—GLASS; MINERAL OR SLAG WOOL
- C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
- C03C3/00—Glass compositions
- C03C3/04—Glass compositions containing silica
- C03C3/076—Glass compositions containing silica with 40% to 90% silica, by weight
- C03C3/083—Glass compositions containing silica with 40% to 90% silica, by weight containing aluminium oxide or an iron compound
-
- C—CHEMISTRY; METALLURGY
- C03—GLASS; MINERAL OR SLAG WOOL
- C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
- C03C3/00—Glass compositions
- C03C3/04—Glass compositions containing silica
- C03C3/076—Glass compositions containing silica with 40% to 90% silica, by weight
- C03C3/083—Glass compositions containing silica with 40% to 90% silica, by weight containing aluminium oxide or an iron compound
- C03C3/085—Glass compositions containing silica with 40% to 90% silica, by weight containing aluminium oxide or an iron compound containing an oxide of a divalent metal
-
- Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y02—TECHNOLOGIES OR APPLICATIONS FOR MITIGATION OR ADAPTATION AGAINST CLIMATE CHANGE
- Y02P—CLIMATE CHANGE MITIGATION TECHNOLOGIES IN THE PRODUCTION OR PROCESSING OF GOODS
- Y02P40/00—Technologies relating to the processing of minerals
- Y02P40/10—Production of cement, e.g. improving or optimising the production methods; Cement grinding
Landscapes
- Chemical & Material Sciences (AREA)
- Engineering & Computer Science (AREA)
- Materials Engineering (AREA)
- Organic Chemistry (AREA)
- Life Sciences & Earth Sciences (AREA)
- Chemical Kinetics & Catalysis (AREA)
- General Chemical & Material Sciences (AREA)
- Geochemistry & Mineralogy (AREA)
- Manufacturing & Machinery (AREA)
- Mechanical Engineering (AREA)
- Glass Compositions (AREA)
- Curing Cements, Concrete, And Artificial Stone (AREA)
Claims (17)
1. Пустотелая сферическая стеклянная частица, состоящая из:
оксида алюминия Al2O3, диоксида кремния SiO2 и по меньшей мере одного оксида металла, причем этот оксид выбирается из группы, включающей оксиды щелочных и щелочноземельных металлов,
отличающаяся тем, что соотношение числа атомов алюминия к числу атомов щелочных металлов составляет около 1:1, а соотношение числа атомов алюминия к числу атомов щелочноземельных металлов составляет около 2:1,
причем пустотелая сферическая стеклянная частица не содержит бора.
2. Пустотелая сферическая стеклянная частица по п. 1, отличающаяся тем, что пустотелая сферическая стеклянная частица содержит примерно от 32 до примерно 40 мас.%, предпочтительно около 36 мас.%, Al2O3, примерно от 38 до примерно 46 мас.%, предпочтительно около 42 мас.%, SiO2 и от примерно 18 до примерно 26 мас.%, предпочтительно около 22 мас.%, оксида как минимум одного щелочного металла.
3. Пустотелая сферическая стеклянная частица по п. 2, отличающаяся тем, что пустотелая сферическая стеклянная частица содержит примерно от 18 до примерно 26 мас.%, предпочтительно около 22 мас.%, смеси K2O и Na2O.
4. Пустотелая сферическая стеклянная частица по пп. 1-3, отличающаяся тем, что диаметр получаемой пустотелой сферической стеклянной частицы составляет от примерно 10 до 600 микрометров, предпочтительно от примерно 90 до 500 микрометров.
5. Пустотелая сферическая стеклянная частица по п. 4, отличающаяся тем, что диаметр получаемой пустотелой сферической стеклянной частицы составляет от 100 до 400 микрометров.
6. Пустотелая сферическая стеклянная частица по пп. 1-5, отличающаяся тем, что пустотелые сферические стеклянные частицы обладают 80% прочностью на раздавливание не ниже 10 000 фунтов/кв. дюйм, желательно не менее 12 500 фунтов/кв. дюйм, предпочтительно 15 000 фунтов/кв. дюйм.
7. Пустотелая сферическая стеклянная частица по пп. 1-6, отличающаяся тем, что температура плавления получаемой пустотелой сферической стеклянной частицы составляет не менее 1200°C.
8. Множество пустотелых сферических стеклянных частиц по пп. 1-7.
9. Множество пустотелых сферических стеклянных частиц по п. 8, отличающихся тем, что сферические стеклянные частицы обладают истинной плотностью от около 0,4 г/см3 до 0,8 г/см3, преимущественно от около 0,45 г/см3 до 0,75 г/см3, предпочтительно от около 0,5 г/см3 до 0,6 г/см3.
10. Наполнитель, содержащий пустотелые сферические стеклянные частицы по пп. 1-7.
11. Использование наполнителя по п. 10 в металломатричных синтактических пенах.
12. Металломатричная синтактическая пена, содержащая наполнитель по п. 10 и металл и/или металлический сплав.
13. Металломатричная синтактическая пена по п. 12, в которой металл - алюминий.
14. Металломатричная синтактическая пена по п. 12 или 13, в которой металлический сплав - сплав алюминия.