RU2015142283A - Способ обработки подложки из черного металла - Google Patents
Способ обработки подложки из черного металла Download PDFInfo
- Publication number
- RU2015142283A RU2015142283A RU2015142283A RU2015142283A RU2015142283A RU 2015142283 A RU2015142283 A RU 2015142283A RU 2015142283 A RU2015142283 A RU 2015142283A RU 2015142283 A RU2015142283 A RU 2015142283A RU 2015142283 A RU2015142283 A RU 2015142283A
- Authority
- RU
- Russia
- Prior art keywords
- pretreatment
- acid
- pretreatment bath
- bath
- phosphate ions
- Prior art date
Links
- 238000000034 method Methods 0.000 title claims 24
- 239000000758 substrate Substances 0.000 title 1
- 239000000203 mixture Substances 0.000 claims 10
- NBIIXXVUZAFLBC-UHFFFAOYSA-K phosphate Chemical compound [O-]P([O-])([O-])=O NBIIXXVUZAFLBC-UHFFFAOYSA-K 0.000 claims 8
- XEEYBQQBJWHFJM-UHFFFAOYSA-N Iron Chemical compound [Fe] XEEYBQQBJWHFJM-UHFFFAOYSA-N 0.000 claims 6
- 239000002253 acid Substances 0.000 claims 6
- 229910052751 metal Inorganic materials 0.000 claims 4
- 239000002184 metal Substances 0.000 claims 4
- 239000007800 oxidant agent Substances 0.000 claims 4
- 238000002203 pretreatment Methods 0.000 claims 4
- 229910052742 iron Inorganic materials 0.000 claims 3
- NBIIXXVUZAFLBC-UHFFFAOYSA-N Phosphoric acid Chemical compound OP(O)(O)=O NBIIXXVUZAFLBC-UHFFFAOYSA-N 0.000 claims 2
- QAOWNCQODCNURD-UHFFFAOYSA-N Sulfuric acid Chemical compound OS(O)(=O)=O QAOWNCQODCNURD-UHFFFAOYSA-N 0.000 claims 2
- 229910000403 monosodium phosphate Inorganic materials 0.000 claims 2
- 235000019799 monosodium phosphate Nutrition 0.000 claims 2
- -1 peroxide compounds Chemical class 0.000 claims 2
- AJPJDKMHJJGVTQ-UHFFFAOYSA-M sodium dihydrogen phosphate Chemical compound [Na+].OP(O)([O-])=O AJPJDKMHJJGVTQ-UHFFFAOYSA-M 0.000 claims 2
- 239000001488 sodium phosphate Substances 0.000 claims 2
- DXIGZHYPWYIZLM-UHFFFAOYSA-J tetrafluorozirconium;dihydrofluoride Chemical compound F.F.F[Zr](F)(F)F DXIGZHYPWYIZLM-UHFFFAOYSA-J 0.000 claims 2
- VTLYFUHAOXGGBS-UHFFFAOYSA-N Fe3+ Chemical compound [Fe+3] VTLYFUHAOXGGBS-UHFFFAOYSA-N 0.000 claims 1
- PXGOKWXKJXAPGV-UHFFFAOYSA-N Fluorine Chemical compound FF PXGOKWXKJXAPGV-UHFFFAOYSA-N 0.000 claims 1
- GRYLNZFGIOXLOG-UHFFFAOYSA-N Nitric acid Chemical compound O[N+]([O-])=O GRYLNZFGIOXLOG-UHFFFAOYSA-N 0.000 claims 1
- 229910019142 PO4 Inorganic materials 0.000 claims 1
- QCWXUUIWCKQGHC-UHFFFAOYSA-N Zirconium Chemical compound [Zr] QCWXUUIWCKQGHC-UHFFFAOYSA-N 0.000 claims 1
- 229910052783 alkali metal Inorganic materials 0.000 claims 1
- 150000001340 alkali metals Chemical class 0.000 claims 1
- 229910000147 aluminium phosphate Inorganic materials 0.000 claims 1
- ZRIUUUJAJJNDSS-UHFFFAOYSA-N ammonium phosphates Chemical class [NH4+].[NH4+].[NH4+].[O-]P([O-])([O-])=O ZRIUUUJAJJNDSS-UHFFFAOYSA-N 0.000 claims 1
- 229910001447 ferric ion Inorganic materials 0.000 claims 1
- 238000001914 filtration Methods 0.000 claims 1
- 239000011737 fluorine Substances 0.000 claims 1
- 229910052731 fluorine Inorganic materials 0.000 claims 1
- LNOPIUAQISRISI-UHFFFAOYSA-N n'-hydroxy-2-propan-2-ylsulfonylethanimidamide Chemical compound CC(C)S(=O)(=O)CC(N)=NO LNOPIUAQISRISI-UHFFFAOYSA-N 0.000 claims 1
- 229910017604 nitric acid Inorganic materials 0.000 claims 1
- 230000020477 pH reduction Effects 0.000 claims 1
- 239000010452 phosphate Substances 0.000 claims 1
- 229910052726 zirconium Inorganic materials 0.000 claims 1
Classifications
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C22/00—Chemical surface treatment of metallic material by reaction of the surface with a reactive liquid, leaving reaction products of surface material in the coating, e.g. conversion coatings, passivation of metals
- C23C22/05—Chemical surface treatment of metallic material by reaction of the surface with a reactive liquid, leaving reaction products of surface material in the coating, e.g. conversion coatings, passivation of metals using aqueous solutions
- C23C22/06—Chemical surface treatment of metallic material by reaction of the surface with a reactive liquid, leaving reaction products of surface material in the coating, e.g. conversion coatings, passivation of metals using aqueous solutions using aqueous acidic solutions with pH less than 6
- C23C22/34—Chemical surface treatment of metallic material by reaction of the surface with a reactive liquid, leaving reaction products of surface material in the coating, e.g. conversion coatings, passivation of metals using aqueous solutions using aqueous acidic solutions with pH less than 6 containing fluorides or complex fluorides
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C22/00—Chemical surface treatment of metallic material by reaction of the surface with a reactive liquid, leaving reaction products of surface material in the coating, e.g. conversion coatings, passivation of metals
- C23C22/05—Chemical surface treatment of metallic material by reaction of the surface with a reactive liquid, leaving reaction products of surface material in the coating, e.g. conversion coatings, passivation of metals using aqueous solutions
- C23C22/06—Chemical surface treatment of metallic material by reaction of the surface with a reactive liquid, leaving reaction products of surface material in the coating, e.g. conversion coatings, passivation of metals using aqueous solutions using aqueous acidic solutions with pH less than 6
- C23C22/34—Chemical surface treatment of metallic material by reaction of the surface with a reactive liquid, leaving reaction products of surface material in the coating, e.g. conversion coatings, passivation of metals using aqueous solutions using aqueous acidic solutions with pH less than 6 containing fluorides or complex fluorides
- C23C22/36—Chemical surface treatment of metallic material by reaction of the surface with a reactive liquid, leaving reaction products of surface material in the coating, e.g. conversion coatings, passivation of metals using aqueous solutions using aqueous acidic solutions with pH less than 6 containing fluorides or complex fluorides containing also phosphates
- C23C22/361—Chemical surface treatment of metallic material by reaction of the surface with a reactive liquid, leaving reaction products of surface material in the coating, e.g. conversion coatings, passivation of metals using aqueous solutions using aqueous acidic solutions with pH less than 6 containing fluorides or complex fluorides containing also phosphates containing titanium, zirconium or hafnium compounds
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C22/00—Chemical surface treatment of metallic material by reaction of the surface with a reactive liquid, leaving reaction products of surface material in the coating, e.g. conversion coatings, passivation of metals
- C23C22/86—Regeneration of coating baths
Landscapes
- Chemical & Material Sciences (AREA)
- General Chemical & Material Sciences (AREA)
- Chemical Kinetics & Catalysis (AREA)
- Engineering & Computer Science (AREA)
- Materials Engineering (AREA)
- Mechanical Engineering (AREA)
- Metallurgy (AREA)
- Organic Chemistry (AREA)
- Chemical Treatment Of Metals (AREA)
Claims (29)
1. Способ удаления железа из ванны предварительной обработки, содержащей композицию для предварительной обработки, содержащую металл Группы IIIB и/или Группы IV, в котором:
(a) уменьшают pH указанной ванны предварительной обработки на по меньшей мере 0,2;
(b) добавляют фосфат-ионы в указанную ванну предварительной обработки со стадии (а) и
(c) увеличивают pH указанной ванны предварительной обработки со стадии (b) на по меньшей мере 0,2.
2. Способ по п. 1, в котором pH указанной ванны предварительной обработки уменьшают на по меньшей мере 1,0.
3. Способ по п. 1, в котором указанное уменьшение pH включает добавление кислоты в указанную ванну предварительной обработки.
4. Способ по п. 3, в котором указанную кислоту выбирают из кислоты, содержащей фтор и металл Группы IVB, фосфорной кислоты, серной кислоты, сульфаминой кислоты, азотной кислоты и их смесей.
5. Способ по п. 3, в котором указанная кислота представляет собой гексафторциркониевую кислоту.
6. Способ по п. 1, в котором источник указанных фосфат-ионов включает ортофосфаты щелочных металлов, ортофосфаты аммония и их смеси.
7. Способ по п. 1, в котором источник указанных фосфат-ионов включает мононатрийфосфат.
8. Способ по п. 1, в котором указанная ванна предварительной обработки на стадии (с) по существу свободна от железа.
9. Способ по п. 1, в котором в указанную ванну предварительной обработки на стадии (b) дополнительно добавляют окисляющий агент.
10. Способ по п. 9, в котором указанный окисляющий агент содержит пероксидные соединения.
11. Способ по п. 1, в котором указанную ванну предварительной обработки со стадии (с) дополнительно подвергают фильтрованию.
12. Способ по п. 1, который осуществляют в отсутствие изделия, подлежащего покрытию указанной композицией для предварительной обработки.
13. Способ по п. 1, в котором указанный металл Группы IIIB и/или Группы IVB представляет собой цирконий.
14. Способ по п. 1, в котором указанная композиция для предварительной обработки дополнительно содержит фосфат-ионы.
15. Способ удаления железа из ванны предварительной обработки, содержащей композицию для предварительной обработки, содержащую металл Группы IIIB и/или Группы IVB, в котором:
(a) добавляют кислоту в указанную ванну предварительной обработки для уменьшения pH указанной композиции для предварительной обработки до величины менее 4,0;
(b) добавляют фосфат-ионы в указанную ванну предварительной обработки со стадии (а) и
(c) увеличивают pH указанной ванны предварительной обработки со стадии (b) до 4-5,5.
16. Способ по п. 15, в котором указанная кислота представляет собой гексафторциркониевую кислоту.
17. Способ по п. 15, в котором источник указанных фосфат-ионов представляет собой мононатрийфосфат.
18. Способ по п. 15, в котором в указанную ванну предварительной обработки на стадии (b) дополнительно добавляют окисляющий агент.
19. Способ по п. 18, в котором указанный окисляющий агент содержит пероксидные соединения.
20. Способ по п. 15, в котором указанную ванну предварительной обработки со стадии (с) дополнительно подвергают фильтрованию.
21. Способ по п. 15, в котором указанная композиция для предварительной обработки в указанной ванне предварительной обработки после стадии (с) имеет массовое соотношение фосфата к ионам трехвалентного железа в интервале от 1:1 до 1,7:1 массовых частей.
22. Способ по п. 15, который осуществляют в отсутствие изделия, подлежащего покрытию указанной композицией для предварительной обработки.
23. Способ по п. 15, в котором указанная композиция для предварительной обработки дополнительно содержит фосфат-ионы.