RU2014115694A - Бумага и способы производства бумаги - Google Patents
Бумага и способы производства бумаги Download PDFInfo
- Publication number
- RU2014115694A RU2014115694A RU2014115694/05A RU2014115694A RU2014115694A RU 2014115694 A RU2014115694 A RU 2014115694A RU 2014115694/05 A RU2014115694/05 A RU 2014115694/05A RU 2014115694 A RU2014115694 A RU 2014115694A RU 2014115694 A RU2014115694 A RU 2014115694A
- Authority
- RU
- Russia
- Prior art keywords
- resin
- paper
- aldehyde
- polyamidoaminoepihalohydrin
- functionalized
- Prior art date
Abstract
1. Бумага, изготовленная способом, включающим обработку водной суспензии волокнистой массы смолой функционализированного альдегидом полимера и полиамидоаминоэпигалогидриновой смолой, где соотношение смолы функционализированного альдегидом полимера к полиамидоаминоэпигалогидриновой смоле составляет приблизительно 1:1 или более, и где полиамидоаминоэпигалогидриновая смола имеет содержание азетидиния приблизительно 80% или менее.2. Бумага по п. 1, где смола функционализированного альдегидом полимера составляет приблизительно от 0,01 до 2,5 мас. % от массы водной суспензии волокнистой массы и полиамидоаминоэпигалогидриновая смола составляет приблизительно от 0,01 до 2,5 мас. % от массы водной суспензии волокнистой массы.3. Бумага по п. 1, где полиамидоаминоэпигалогидриновая смола имеет общий уровень АОГ (абсорбируемых органических галоген-производных) приблизительно 400 млнили менее.4. Бумага по п. 1, где смола функционализированного альдегидом полимера представляет собой глиоксилированную полиакриламидную смолу, и полиамидоаминоэпигалогидриновая смола представляет собой полиамидоаминоэпихлоргидриновую смолу.5. Бумага по п. 1, где содержание азетидиния составляет приблизительно 50% или менее.6. Бумага по п. 1, где соотношение смолы функционализированного альдегидом полимера к полиамидоаминоэпигалогидриновой смоле составляет приблизительно от 1:1 до 100:1.7. Бумага по п. 1, где полиамидоаминоэпигалогидриновая смола имеет общий уровень АОГ приблизительно 100 млнили менее, а содержание азетидиния составляет приблизительно 50% или менее.8. Бумага по п. 1, где бумага представляет собой бумажный продукт, выбранный из группы, �
Claims (31)
1. Бумага, изготовленная способом, включающим обработку водной суспензии волокнистой массы смолой функционализированного альдегидом полимера и полиамидоаминоэпигалогидриновой смолой, где соотношение смолы функционализированного альдегидом полимера к полиамидоаминоэпигалогидриновой смоле составляет приблизительно 1:1 или более, и где полиамидоаминоэпигалогидриновая смола имеет содержание азетидиния приблизительно 80% или менее.
2. Бумага по п. 1, где смола функционализированного альдегидом полимера составляет приблизительно от 0,01 до 2,5 мас. % от массы водной суспензии волокнистой массы и полиамидоаминоэпигалогидриновая смола составляет приблизительно от 0,01 до 2,5 мас. % от массы водной суспензии волокнистой массы.
3. Бумага по п. 1, где полиамидоаминоэпигалогидриновая смола имеет общий уровень АОГ (абсорбируемых органических галоген-производных) приблизительно 400 млн-1 или менее.
4. Бумага по п. 1, где смола функционализированного альдегидом полимера представляет собой глиоксилированную полиакриламидную смолу, и полиамидоаминоэпигалогидриновая смола представляет собой полиамидоаминоэпихлоргидриновую смолу.
5. Бумага по п. 1, где содержание азетидиния составляет приблизительно 50% или менее.
6. Бумага по п. 1, где соотношение смолы функционализированного альдегидом полимера к полиамидоаминоэпигалогидриновой смоле составляет приблизительно от 1:1 до 100:1.
7. Бумага по п. 1, где полиамидоаминоэпигалогидриновая смола имеет общий уровень АОГ приблизительно 100 млн-1 или менее, а содержание азетидиния составляет приблизительно 50% или менее.
8. Бумага по п. 1, где бумага представляет собой бумажный продукт, выбранный из группы, состоящей из сухого картона, тонкой бумаги, полотенца, бумаги тиссью и газетного продукта.
9. Бумага, изготовленная способом, включающим обработку водной суспензии волокнистой массы смолой функционализированного альдегидом полимера и полиамидоаминоэпигалогидриновой смолой, где соотношение смолы функционализированного альдегидом полимера к полиамидоаминоэпигалогидриновой смоле составляет приблизительно 1:1 или более, и где полиамидоаминоэпигалогидриновая смола имеет общий уровень АОГ приблизительно 400 млн-1 или менее.
10. Бумага по п. 9, где смола функционализированного альдегидом полимера составляет приблизительно от 0,01 до 2,5 мас. % от массы водной суспензии волокнистой массы и полиамидоаминоэпигалогидриновая смола составляет приблизительно от 0,01 до 2,5 мас. % от массы водной суспензии волокнистой массы
11. Бумага по п. 9, где полиамидоаминоэпигалогидриновая смола имеет общий уровень АОГ приблизительно 100 млн-1 или менее.
12. Бумага по п. 9, где смола функционализированного альдегидом полимера представляет собой глиоксилированную полиакриламидную смолу, и полиамидоаминоэпигалогидриновая смола представляет собой полиамидоаминоэпихлоргидриновую смолу.
13. Бумага по п. 9, где соотношение смолы функционализированного альдегидом полимера к полиамидоаминоэпигалогидриновой смоле составляет приблизительно от 1:1 до 100:1.
14. Бумага по п. 9, где бумага представляет собой бумажный продукт, выбранный из группы, состоящей из сухого картона, тонкой бумаги, полотенца, бумаги тиссью и газетного продукта.
15. Способ производства бумаги, включающий:
введение в водную суспензию волокнистой массы смолы функционализированного альдегидом полимера и полиамидоаминоэпигалогидриновой смолы, где соотношение смолы функционализированного альдегидом полимера к полиамидоаминоэпигалогидриновой смоле составляет приблизительно 1:1 или более, и где полиамидоаминоэпигалогидриновая смола имеет содержание азетидиния приблизительно 80% или менее.
16. Способ по п. 15, где смола функционализированного альдегидом полимера представляет собой глиоксилированную полиакриламидную смолу, и полиамидоаминоэпигалогидриновая смола представляет собой полиамидоаминоэпихлоргидриновую смолу.
17. Способ по п. 15, где содержание азетидиния составляет приблизительно 50% или менее.
18. Способ по п. 15, где соотношение смолы функционализированного альдегидом полимера к полиамидоаминоэпигалогидриновой смоле составляет приблизительно от 1:1 до 100:1.
19. Способ по п. 15, где полиамидоаминоэпигалогидриновая смола имеет общий уровень АОГ приблизительно 100 млн-1 или менее.
20. Способ по п. 15, где бумага представляет собой бумажный продукт, выбранный из группы, состоящей из сухого картона, тонкой бумаги, полотенца, бумаги тиссью и газетного продукта.
21. Способ по п. 15, где смолу функционализированного альдегидом полимера и полиамидоаминоэпигалогидриновую смолу смешивают вместе перед смешиванием с суспензией волокнистой массы.
22. Способ по п. 15, где смолу функционализированного альдегидом полимера и полиамидоаминоэпигалогидриновую смолу добавляют в суспензию волокнистой массы одновременно.
23. Способ по п. 15, где смолу функционализированного альдегидом полимера и полиамидоаминоэпигалогидриновую смолу добавляют в суспензию волокнистой массы последовательно.
24. Способ производства бумаги, включающий:
введение в суспензию волокнистой массы смолы функционализированного альдегидом полимера и полиамидоаминоэпигалогидриновой смолы, где соотношение смолы функционализированного альдегидом полимера к полиамидоаминоэпигалогидриновой смоле составляет более чем приблизительно 1:1, и где полиамидоаминоэпигалогидриновая смола имеет общий уровень АОГ приблизительно 400 млн-1 или менее.
25. Способ по п. 24, где смола функционализированного альдегидом полимера представляет собой глиоксилированную полиакриламидную смолу, и полиамидоаминоэпигалогидриновая смола представляет собой полиамидоаминоэпихлоргидриновую смолу.
26. Способ по п. 24, где соотношение смолы функционализированного альдегидом полимера к полиамидоаминоэпигалогидриновой смоле составляет приблизительно от 1:1 до 100:1.
27. Способ по п. 24, где полиамидоаминоэпигалогидриновая смола имеет общий уровень АОГ приблизительно 100 млн-1 или менее.
28. Способ по п. 24, где бумага представляет собой бумажный продукт, выбранный из группы, состоящей из сухого картона, тонкой бумаги, полотенца, бумаги тиссью и газетного продукта.
29. Способ по п. 24, где смолу функционализированного альдегидом полимера и полиамидоаминоэпигалогидриновую смолу смешивают вместе перед смешиванием с суспензией волокнистой массы.
30. Способ по п. 24, где смолу функционализированного альдегидом полимера и полиамидоаминоэпигалогидриновую смолу добавляют в суспензию волокнистой массы одновременно.
31. Способ по п. 24, где смолу функционализированного альдегидом полимера и полиамидоаминоэпигалогидриновую смолу добавляют в суспензию волокнистой массы последовательно.