RU2012143614A - Способ производства текстурованных листов из электротехнической стали - Google Patents
Способ производства текстурованных листов из электротехнической стали Download PDFInfo
- Publication number
- RU2012143614A RU2012143614A RU2012143614/02A RU2012143614A RU2012143614A RU 2012143614 A RU2012143614 A RU 2012143614A RU 2012143614/02 A RU2012143614/02 A RU 2012143614/02A RU 2012143614 A RU2012143614 A RU 2012143614A RU 2012143614 A RU2012143614 A RU 2012143614A
- Authority
- RU
- Russia
- Prior art keywords
- temperature
- rolling
- sheet
- steel
- subjected
- Prior art date
Abstract
1. Способ производства текстурованных листов из электротехнической стали, включающий последовательность стадий, на которых стальной сляб, содержащий:от 0,01 до 0,10 мас.% C,от 2,5 до 4,5 мас.% Si,от 0,02 до 0,12 мас.% Mn,от 0,005 до 0,10 мас.% Al иот 0,004 до 0,015 мас.% N,а также от 0,005 до 0,06 мас.% Se и/или от 0,005 до 0,06 мас.% S, нагревают до температуры не ниже 1280°C и подвергают горячей прокатке или дополнительно отжигают, и подвергают однократной холодной прокатке или холодной прокатке два или более раз с выполняемым между ними промежуточным отжигом до достижения конечной толщины листа, указанный холоднокатаный лист подвергают обезуглероживающему отжигу и окончательному отжигу,при этом способ включает контролирование температуры стального листа таким образом, чтобы после завершения чистовой прокатки при горячей прокатке в ходе охлаждения она удовлетворяла по всей длине рулона условиям приведенного ниже уравнения (1),где T(t) представляет температуру стального листа (°C), FDT является температурой конца прокатки (°C) и t - время (c) после завершения чистовой прокатки,и контролирование температуры концевого участка рулона стального листа, представляющего 10% длины рулона, с тем, чтобы по истечении 3 секунд от момента завершения горячей прокатки она составляла не менее 650°C:2. Способ по п.1, в котором стальной сляб в дополнение к перечисленным компонентам содержит, кроме того, один, или два, или более компонентов, выбираемых из от 0,01 до 0,15 мас.% Cu, от 0,01 до 0,15 мас.% Sn, от 0,005 до 0,1 мас.% Sb, от 0,005 до 0,1 мас.% Mo, от 0,005 до 0,1 мас.% Te и от 0,005 до 0,1 мас.% Bi.
Claims (2)
1. Способ производства текстурованных листов из электротехнической стали, включающий последовательность стадий, на которых стальной сляб, содержащий:
от 0,01 до 0,10 мас.% C,
от 2,5 до 4,5 мас.% Si,
от 0,02 до 0,12 мас.% Mn,
от 0,005 до 0,10 мас.% Al и
от 0,004 до 0,015 мас.% N,
а также от 0,005 до 0,06 мас.% Se и/или от 0,005 до 0,06 мас.% S, нагревают до температуры не ниже 1280°C и подвергают горячей прокатке или дополнительно отжигают, и подвергают однократной холодной прокатке или холодной прокатке два или более раз с выполняемым между ними промежуточным отжигом до достижения конечной толщины листа, указанный холоднокатаный лист подвергают обезуглероживающему отжигу и окончательному отжигу,
при этом способ включает контролирование температуры стального листа таким образом, чтобы после завершения чистовой прокатки при горячей прокатке в ходе охлаждения она удовлетворяла по всей длине рулона условиям приведенного ниже уравнения (1)
где T(t) представляет температуру стального листа (°C), FDT является температурой конца прокатки (°C) и t - время (c) после завершения чистовой прокатки,
и контролирование температуры концевого участка рулона стального листа, представляющего 10% длины рулона, с тем, чтобы по истечении 3 секунд от момента завершения горячей прокатки она составляла не менее 650°C:
2. Способ по п.1, в котором стальной сляб в дополнение к перечисленным компонентам содержит, кроме того, один, или два, или более компонентов, выбираемых из от 0,01 до 0,15 мас.% Cu, от 0,01 до 0,15 мас.% Sn, от 0,005 до 0,1 мас.% Sb, от 0,005 до 0,1 мас.% Mo, от 0,005 до 0,1 мас.% Te и от 0,005 до 0,1 мас.% Bi.