RU2012119545A - Каучуковая композиция на основе глицерина и функционализированного эластомера и протектор пневматической шины - Google Patents
Каучуковая композиция на основе глицерина и функционализированного эластомера и протектор пневматической шины Download PDFInfo
- Publication number
- RU2012119545A RU2012119545A RU2012119545/04A RU2012119545A RU2012119545A RU 2012119545 A RU2012119545 A RU 2012119545A RU 2012119545/04 A RU2012119545/04 A RU 2012119545/04A RU 2012119545 A RU2012119545 A RU 2012119545A RU 2012119545 A RU2012119545 A RU 2012119545A
- Authority
- RU
- Russia
- Prior art keywords
- composition according
- chain
- elastomers
- denotes
- group
- Prior art date
Abstract
1. Усиленная каучуковая композиция на основе по меньшей мере:- (а) модифицированного диенового эластомера, несущего полярный сегмент, выбранного из диеновых эластомеров, функционализированных в конце цепи, связанных или звездообразных при помощи группы, содержащей полярную функциональную группу, содержащую по меньшей мере один атом кислорода, и диеновых блок-эластомеров, содержащих по меньшей мере один полярный блок,- (b) глицерина и- (с) усиливающего наполнителя, содержащего неорганический наполнитель.2. Композиция по п.1, отличающаяся тем, что полярная группа, содержащая по меньшей мере один атом кислорода, выбрана из группы, состоящей из силанола, алкоксисиланов, алкоксисиланов, несущих аминную группу, эпоксидов, простых эфиров, сложных эфиров, гидроксила, карбоновой кислоты.3. Композиция по п.2, отличающаяся тем, что модифицированный диеновый эластомер выбран из эластомеров, несущих силанольную группу, причем силанольная группа находится в конце цепи или в середине цепи.4. Композиция по п.2, отличающаяся тем, что модифицированный диеновый эластомер выбран из эластомеров, функционализированных в конце цепи, связанных или звездообразных, полученных функционализацией диеновых эластомеров агентом, соответствующим общей формуле:(Y)m-R-Si(OR)-Rnв которой:Y обозначает остатки,- Rобозначает алкильный, циклоалкильный или арильный остаток, содержащий от 1 до 10 атомов углерода,- Rобозначает алкильный, арильный, циклоалкильный алкарильный, аралкильный остаток, содержащий от 1 до 12 атомов углерода,- Rобозначает алкильный, арильный, алкарильный остаток, содержащий от 1 до 12 атомов углерода,- Rобозначает углеводородный остаток, соде
Claims (17)
1. Усиленная каучуковая композиция на основе по меньшей мере:
- (а) модифицированного диенового эластомера, несущего полярный сегмент, выбранного из диеновых эластомеров, функционализированных в конце цепи, связанных или звездообразных при помощи группы, содержащей полярную функциональную группу, содержащую по меньшей мере один атом кислорода, и диеновых блок-эластомеров, содержащих по меньшей мере один полярный блок,
- (b) глицерина и
- (с) усиливающего наполнителя, содержащего неорганический наполнитель.
2. Композиция по п.1, отличающаяся тем, что полярная группа, содержащая по меньшей мере один атом кислорода, выбрана из группы, состоящей из силанола, алкоксисиланов, алкоксисиланов, несущих аминную группу, эпоксидов, простых эфиров, сложных эфиров, гидроксила, карбоновой кислоты.
3. Композиция по п.2, отличающаяся тем, что модифицированный диеновый эластомер выбран из эластомеров, несущих силанольную группу, причем силанольная группа находится в конце цепи или в середине цепи.
4. Композиция по п.2, отличающаяся тем, что модифицированный диеновый эластомер выбран из эластомеров, функционализированных в конце цепи, связанных или звездообразных, полученных функционализацией диеновых эластомеров агентом, соответствующим общей формуле:
(Y)m-R1-Si(OR2)3-n-R3n
в которой:
- R1 обозначает алкильный, циклоалкильный или арильный остаток, содержащий от 1 до 10 атомов углерода,
- R2 обозначает алкильный, арильный, циклоалкильный алкарильный, аралкильный остаток, содержащий от 1 до 12 атомов углерода,
- R3 обозначает алкильный, арильный, алкарильный остаток, содержащий от 1 до 12 атомов углерода,
- R4 обозначает углеводородный остаток, содержащий от 1 до 6 атомов углерода и могущий содержать один или несколько атомов кислорода в углеводородной цепи,
- n обозначает целое число, выбранное из значений 0, 1,
- m обозначает целое число, выбранное из значений 1 или 2,
- р и q обозначают целые числа, выбранные из значений 0, 1, 2, 3 или 4, при условии, что сумма p+q должна являться целым числом между 2 и 5 включительно.
5. Композиция по п.2, отличающаяся тем, что модифицированный диеновый эластомер выбран из эластомеров, функционализированных в конце цепи или связанных, полученных функционализацией диеновых эластомеров агентом типа алкоксисилана, несущего циклическую или нециклическую, третичную, вторичную или первичную аминную группу.
6. Композиция по п.1, отличающаяся тем, что модифицированный диеновый эластомер выбран из блок-эластомеров, содержащих по меньшей мере блок-сополимер простого полиэфира в конце полимерной цепи или в середине цепи, и блок-эластомеров, содержащих по меньшей мере один центральный полярный блок, с которым связаны больше двух полимерных цепей.
7. Композиция по любому из п.1-6, отличающаяся тем, что модифицированный диеновый эластомер содержит также на конце цепи или на концах цепей, не связанной(-ых) с полярным сегментом, аминную группу.
8. Композиция по п.7, отличающаяся тем, что аминная группа является производной пирролидина или гексаметиленимина.
9. Композиция по п.1, отличающаяся тем, что модифицированный диеновый эластомер является модифицированным бутадиен-стирольным сополимером.
10. Композиция по п.1, отличающаяся тем, что глицерин присутствует в количестве от 1 до 10 мсэ.
11. Композиция по п.1, отличающаяся тем, что усиливающий наполнитель содержит главным образом неорганический усиливающий наполнитель.
12. Композиция по п.1, отличающаяся тем, что усиливающим неорганическим наполнителем является диоксид кремния.
13. Композиция по п.1, отличающаяся тем, что композиция также содержит традиционный диеновый эластомер.
14. Каучуковый полупродукт для пневматической шины, отличающийся тем, что содержит каучуковую композицию, сшиваемую или сшитую по любому из п.1-13.
15. Полупродукт по п.14, отличающийся тем, что указанное изделие является протектором.
16. Способ получения протектора пневматической шины по п.15, отличающийся тем, что включает в себя следующие стадии:
(i) осуществление при максимальной температуре между 130 и 200°С первой термомеханической стадии обработки (иногда называемой «непродуктивной») необходимых базовых компонентов, за исключением системы сшивки, композиции, определенной в п.1-13, содержащей функционализированный диеновый эластомер, глицерин и усиливающий наполнитель за исключением системы сшивки, затем
(ii) осуществление при температуре, ниже указанной максимальной температуры, указанной первой стадии, предпочтительно ниже 120°С, второй механической рабочей стадии, в процессе которой вводят указанную систему сшивки,
(iii) экструдирование или каландрирование каучуковой композиции, полученной таким образом, в виде протектора пневматической шины.
17. Пневматическая шина, отличающаяся тем, что содержит полупродукт по п.14 или 15.