RU2009139818A - Не требующий технического обслуживания подшипник скольжения и способ его изготовления - Google Patents
Не требующий технического обслуживания подшипник скольжения и способ его изготовления Download PDFInfo
- Publication number
- RU2009139818A RU2009139818A RU2009139818/02A RU2009139818A RU2009139818A RU 2009139818 A RU2009139818 A RU 2009139818A RU 2009139818/02 A RU2009139818/02 A RU 2009139818/02A RU 2009139818 A RU2009139818 A RU 2009139818A RU 2009139818 A RU2009139818 A RU 2009139818A
- Authority
- RU
- Russia
- Prior art keywords
- bearing according
- sliding bearing
- intermediate layer
- functional groups
- metal base
- Prior art date
Abstract
1. Не требующий технического обслуживания подшипник скольжения, который содержит металлическое основание, непосредственно нанесенный на него промежуточный слой и нанесенный на промежуточный слой антифрикционный слой, отличающийся тем, что промежуточный слой содержит, по меньшей мере, один термопластичный полимер, содержащий функциональные группы формулы , , , -COOH и/или -COOR, при этом R означает цикличные или линейные органические радикалы с 1-20 атомами углерода, при этом функциональные группы внедрены в термопластичный полимер путем добавления, по меньшей мере, одного модифицирующего агента, а именно малеиновой кислоты и ее производных, в частности ее ангидрида, и/или итаконовой кислоты и ее производных, в частности ее ангидрида, и/или цитраконовой кислоты и ее производных, в частности ее ангидрида. ! 2. Подшипник скольжения по п.1, отличающийся тем, что, по меньшей мере, один термопластичный полимер промежуточного слоя, содержащий функциональные группы, представляет собой термопластичный фторполимер, содержащий функциональные группы, в частности сополимер этилена-тетрафторэтилена (ETFE), перфторалкоксиэтилена (PFA) или сополимер тетрафторэтилена-перфторметилвинилэфира (MFA), преимущественно сополимер этилена-тетрафторэтилена (ETFE). ! 3. Подшипник скольжения по п.1 или 2, отличающийся тем, что промежуточный слой (2), содержащий, по меньшей мере, один термопластичный полимер, содержащий функциональные группы, дополнительно содержит сополимер перфторалкилвинилэфира формулы CF2=CF-O-R1, ! где R1 представляет собой радикал перфторэтила, перфтор-n-пропила или перфтор-n-бутила, и тетрафторэтилена. ! 4. Подшипник скольжения по п.1, о�
Claims (24)
1. Не требующий технического обслуживания подшипник скольжения, который содержит металлическое основание, непосредственно нанесенный на него промежуточный слой и нанесенный на промежуточный слой антифрикционный слой, отличающийся тем, что промежуточный слой содержит, по меньшей мере, один термопластичный полимер, содержащий функциональные группы формулы , , , -COOH и/или -COOR, при этом R означает цикличные или линейные органические радикалы с 1-20 атомами углерода, при этом функциональные группы внедрены в термопластичный полимер путем добавления, по меньшей мере, одного модифицирующего агента, а именно малеиновой кислоты и ее производных, в частности ее ангидрида, и/или итаконовой кислоты и ее производных, в частности ее ангидрида, и/или цитраконовой кислоты и ее производных, в частности ее ангидрида.
2. Подшипник скольжения по п.1, отличающийся тем, что, по меньшей мере, один термопластичный полимер промежуточного слоя, содержащий функциональные группы, представляет собой термопластичный фторполимер, содержащий функциональные группы, в частности сополимер этилена-тетрафторэтилена (ETFE), перфторалкоксиэтилена (PFA) или сополимер тетрафторэтилена-перфторметилвинилэфира (MFA), преимущественно сополимер этилена-тетрафторэтилена (ETFE).
3. Подшипник скольжения по п.1 или 2, отличающийся тем, что промежуточный слой (2), содержащий, по меньшей мере, один термопластичный полимер, содержащий функциональные группы, дополнительно содержит сополимер перфторалкилвинилэфира формулы CF2=CF-O-R1,
где R1 представляет собой радикал перфторэтила, перфтор-n-пропила или перфтор-n-бутила, и тетрафторэтилена.
4. Подшипник скольжения по п.1, отличающийся тем, что толщина промежуточного слоя соответствует шероховатости металлического основания (1), определенной как расстояние между максимальной высотой купола профиля и максимальной глубиной впадины профиля поверхности металлического основания (1).
6. Подшипник скольжения по п.5, отличающийся тем, что промежуточный металлический пласт выполнен в виде растянутого просечно-вытяжного листа.
7. Подшипник скольжения по п.5 или 6, отличающийся тем, что металлический промежуточный пласт выполнен из нержавеющей стали, алюминия или бронзы.
8. Подшипник скольжения по п.1, отличающийся тем, что промежуточный слой содержит наполнители для усиления и/или улучшения теплопроводности и/или характеристик износостойкости.
9. Подшипник скольжения по п.8, отличающийся тем, что промежуточный слой в качестве наполнителей содержит волокна, в частности стекловолокна, углеродные волокна или арамидные волокна, неорганические материалы, в частности керамические материалы, уголь, стекло, графит, оксид алюминия, сульфид молибдена, бронзу или карбид кремния в форме тканей, порошков, шариков или волокон, термопластичные материалы, в частности полиимид (PI), полиамидимид (PAI), полифениленсульфид (PPS), полифениленсульфон (PPSO2), жидкокристаллические полимеры (LCP), полиэфир эфиркетоны (РЕЕК) или ароматические полиэфиры (Эконол) или минеральные материалы, в частности волластонит или сульфат бария или их смеси.
10. Подшипник скольжения по одному из пп.8 или 9, отличающийся тем, что доля наполнителей составляет 1-40 об.%, в частности 5-30 об.%.
11. Подшипник скольжения по п.1, отличающийся тем, что промежуточный слой имеет толщину 0,01-0,1 мм, в частности 0,01-0,05 мм.
12. Подшипник скольжения по п.1, отличающийся тем, что металлическое основание имеет гладкую поверхность.
13. Подшипник скольжения по п.1, отличающийся тем, что металлическое основание имеет шероховатую поверхность.
14. Подшипник скольжения по п.1, отличающийся тем, что металлическое основание имеет улучшенную поверхность, в частности поверхность с гальваническим цинкованием.
15. Подшипник скольжения по п.1, отличающийся тем, что металлическое основание выполнено из стали, в частности холоднокатаной стали, в частности, с номером материала 1.0338 или 1.0347, или из матовой оцинкованной стали, высококачественной стали, предпочтительно с номером материала 1.4512 или 1.4720, или алюминия или их сплавов.
16. Подшипник скольжения по п.1, отличающийся тем, что нанесенный на промежуточный слой антифрикционный слой содержит политетрафторэтилен, полиамид, полиэфир эфиркетон или их смесь.
17. Подшипник скольжения по п.16, отличающийся тем, что антифрикционный слой выполнен в виде композиционного слоя PTFE (политетрафторэтилена).
18. Подшипник скольжения по п.1, отличающийся тем, что антифрикционный слой выполнен в виде перфорированной и/или воздухопроницаемой полимерной пленки.
19. Подшипник скольжения по п.1, отличающийся тем, что антифрикционный слой имеет толщину 0,01-1,5 мм, в частности 0,1-0,35 мм.
20. Подшипник скольжения по п.1, отличающийся тем, что антифрикционный слой содержит наполнители для усиления и/или улучшения теплопроводности и/или характеристик износостойкости.
21. Подшипник скольжения по п.20, отличающийся тем, что в качестве наполнителей содержит волокна, в частности стекловолокна, углеводные волокна или арамидные волокна, неорганические материалы, в частности керамические материалы, уголь, стекло, графит, оксид алюминия, сульфид молибдена, бронзу или карбид кремния в форме тканей, порошков, шариков или волокон, термопластичные материалы, в частности полиимид (PI), полиамидимид (PAI), полифениленсульфид (PPS), полифениленсульфон (PPSO2), жидкокристаллические полимеры (LCP), полиэфир эфиркетоны (PEEK) или ароматические полиэфиры (Эконол) или минеральные материалы, в частности волластонит или сульфат бария или их смеси.
22. Подшипник скольжения по п.20 или 21, отличающийся тем, что доля наполнителей составляет 1-40 об.%, в частности, 5-30 об.%.
23. Способ изготовления не требующего технического обслуживания подшипника скольжения по одному из пп.1-22, отличающийся тем, что функциональные группы в термопластичный полимер промежуточного слоя внедряют с помощью добавления, по меньшей мере, одного модифицирующего агента, а именно малеиновой кислоты и ее производных, в частности ее ангидрида, и/или итаконовой кислоты и ее производных, в частности ее ангидрида, и/или цитраконовой кислоты и ее производных, в частности ее ангидрида, и в заключение промежуточный слой и антифрикционный слой присоединяют по их поверхности к металлическому основанию под давлением с подводом тепла.
24. Способ по п.23, отличающийся тем, что перед нанесением промежуточного слоя поверхности металлического основания придают шероховатость и/или улучшают поверхность (например с помощью гальванического цинкования).