RU2009100625A - Устойчивые к царапинам и износостойкие покрытия на полимерных поверхностях - Google Patents
Устойчивые к царапинам и износостойкие покрытия на полимерных поверхностях Download PDFInfo
- Publication number
- RU2009100625A RU2009100625A RU2009100625/05A RU2009100625A RU2009100625A RU 2009100625 A RU2009100625 A RU 2009100625A RU 2009100625/05 A RU2009100625/05 A RU 2009100625/05A RU 2009100625 A RU2009100625 A RU 2009100625A RU 2009100625 A RU2009100625 A RU 2009100625A
- Authority
- RU
- Russia
- Prior art keywords
- composition
- surface coating
- composition according
- component
- amount
- Prior art date
Abstract
1. Композиция, которая содержит ! а) по меньшей мере, один продукт превращения ! а1) силана общей формулы ! ! причем Y(1) = 3-глицидилоксипропил, и ! R1, R2, R3 = одинаковые или различные алкильные группы, имеющие от 1 до 6 атомов углерода, и ! а2) силана общей формулы ! ! причем Y(2) = N-2-аминоэтил-3-аминопропил или NH2(CH2)2NH(CH2)2NH(CH)3, ! и R'1, R'2, R'3 = одинаковые или различные алкильные группы, имеющие от 1 до 6 атомов углерода, и ! b) по меньшей мере, один неорганический наполнитель, и ! c) растворитель с температурой кипения меньшей или равной 85°С, и ! d) воду, и ! e) катализатор, выбираемый из неорганических или органических кислот. ! 2. Композиция по п.1, ! отличающаяся тем, ! что R1, R2, R3 и/или R'1, R'2, R'3 одинаковы, по меньшей мере, парами. ! 3. Композиция по п.1, ! отличающаяся тем, ! что неорганический наполнитель выбирают из SiO2, TiO2, ZnO, Al2O3, BaSO4, CeO2, ZrO2, или смеси данных наполнителей. ! 4. Композиция по п.1, ! отличающаяся тем, ! что неорганический наполнитель имеет средний размер частиц d50 от 10 до 200 нм. ! 5. Композиция по п.1, ! отличающаяся тем, ! что компонент с) выбирают из ряда спиртов общей формулы CnH2n+1OH, причем n=1-4, или смеси данных спиртов, или выбирают из кетонов, выбранных из ацетона, метилэтилкетона, или смеси данных кетонов. ! 6. Композиция по п.5, ! отличающаяся тем, ! что компонент с) выбирают из этанола, 1-пропанола, 2-пропанола, или смеси данных спиртов. ! 7. Композиция по п.1, ! отличающаяся тем, ! что компонент е) выбирают из водной азотной кислоты. ! 8. Композиция по одному из пп.1-7, ! отличающаяся тем, ! что композиция содержит следующий компонент ! а3), который является, по меньшей мере, одним продуктом превращения следующего силана ! ! причем Y(3) выбирают из фтора,
Claims (29)
1. Композиция, которая содержит
а) по меньшей мере, один продукт превращения
а1) силана общей формулы
причем Y(1) = 3-глицидилоксипропил, и
R1, R2, R3 = одинаковые или различные алкильные группы, имеющие от 1 до 6 атомов углерода, и
а2) силана общей формулы
причем Y(2) = N-2-аминоэтил-3-аминопропил или NH2(CH2)2NH(CH2)2NH(CH)3,
и R'1, R'2, R'3 = одинаковые или различные алкильные группы, имеющие от 1 до 6 атомов углерода, и
b) по меньшей мере, один неорганический наполнитель, и
c) растворитель с температурой кипения меньшей или равной 85°С, и
d) воду, и
e) катализатор, выбираемый из неорганических или органических кислот.
2. Композиция по п.1,
отличающаяся тем,
что R1, R2, R3 и/или R'1, R'2, R'3 одинаковы, по меньшей мере, парами.
3. Композиция по п.1,
отличающаяся тем,
что неорганический наполнитель выбирают из SiO2, TiO2, ZnO, Al2O3, BaSO4, CeO2, ZrO2, или смеси данных наполнителей.
4. Композиция по п.1,
отличающаяся тем,
что неорганический наполнитель имеет средний размер частиц d50 от 10 до 200 нм.
5. Композиция по п.1,
отличающаяся тем,
что компонент с) выбирают из ряда спиртов общей формулы CnH2n+1OH, причем n=1-4, или смеси данных спиртов, или выбирают из кетонов, выбранных из ацетона, метилэтилкетона, или смеси данных кетонов.
6. Композиция по п.5,
отличающаяся тем,
что компонент с) выбирают из этанола, 1-пропанола, 2-пропанола, или смеси данных спиртов.
7. Композиция по п.1,
отличающаяся тем,
что компонент е) выбирают из водной азотной кислоты.
8. Композиция по одному из пп.1-7,
отличающаяся тем,
что композиция содержит следующий компонент
а3), который является, по меньшей мере, одним продуктом превращения следующего силана
причем Y(3) выбирают из фтора, фторалкила, метакрила, винила, меркапто, и R''1, R''2, R''3 = одинаковые или различные алкильные группы, имеющие от 1 до 6 атомов углерода.
9. Способ получения поверхностного слоя на полимерной поверхности, отличающийся тем,
что композицию, по меньшей мере, по одному из пп.1-8 наносят на полимерную поверхность путем окунания, намазывания, нанесения ракелем, нанесения кистью, нанесение роликом, вальцевания или разбрызгивания, и там отверждают.
10. Способ по п.9,
отличающийся тем,
что к композиции подмешивают компоненты
а1) в количестве от 5 до 40 мас.%, и
а2) в количестве от 5 до 50 мас.%, и
b) в количестве от 2 до 20 мас.%, и
c) в количестве от 20 до 60 мас.%, и
d) в количестве от 0,5 до 5 мас.%, и
e) в количестве от 0,02 до 0,5 мас.%, и
причем количественные данные в каждом случае приведены в расчете на композицию, и при условии, что сумма массовых частей составляет 100%.
11. Способ по п.9,
отличающийся тем,
что к композиции добавляют компонент а1) и а2) в мольном соотношении от 1:3 до 3:1.
12. Способ по п.9,
отличающийся тем,
что к композиции подмешивают компонент а3) в количестве от 0,5 до 10 мас.%, причем количественные данные приведены в расчете на композицию, и при условии, что сумма массовых частей компонентов а1), а2), а3), и b)-е) составляет 100%.
13. Способ по п.9,
отличающийся тем,
что к композиции подмешивают в качестве следующих компонентов
i) пленкообразователь, выбираемый из меламиновой смолы, акрилата или смеси данных связующих, в количестве от 0,001 до 15 мас.% и/или
j) эпоксидную смолу в количестве от 0,001 до 15 мас.%,
причем количественные данные в каждом случае приведены в расчете на композицию, и при условии, что сумма массовых частей компонентов а)-g) составляет 100%.
14. Способ по п.9,
отличающийся тем,
что композицию нагревают при температуре от 60 до 150°С, вследствие этого композиция отверждается.
15. Способ по п.9,
отличающийся тем,
что композицию отверждают путем нагревания в течение от 1 до 300 с.
16. Способ по одному из пп.9-15,
отличающийся тем,
что к композиции в качестве следующих компонентов подмешивают
k) неорганический УФ-абсорбер, выбираемый из оксида цинка, оксида церия или диоксида титана, или смеси данных неорганических абсорберов, и/или органический абсорбер, выбираемый из гидроксифенилбензотриазола, гидроксибензофенона, HALS-стабилизаторов, или смеси данных органических абсорберов и композицию, нанесенную на поверхность отверждают УФ-облучением.
17. Способ по п.16,
отличающийся тем,
что компонент h) содержится в количестве от 0,5 до 5 мас.%, причем количественные данные приведены в расчете на композицию, и при условии, что сумма массовых частей компонентов а)-h) составляет 100%.
18. Поверхностное покрытие, содержащее кремний,
отличающееся тем,
что поверхностное покрытие имеет сопротивление царапанию от 3 до 20 Н.
19. Поверхностное покрытие по п.18,
отличающееся тем,
что поверхностное покрытие имеет износоустойчивость от 0,1 до 0,5 мас.%.
20. Поверхностное покрытие по п.18,
отличающееся тем,
что поверхностное покрытие имеет толщину слоя от 1 до 10 мкм.
21. Поверхностное покрытие по п.18,
отличающееся тем,
что поверхностное покрытие содержит неорганический наполнитель в форме частиц, которые имеют однородное распределение.
22. Поверхностное покрытие по п.18,
отличающееся тем,
что поверхностное покрытие имеет эластичность от 0,5 до 10%.
23. Поверхностное покрытие по п.18,
отличающееся тем,
что поверхностное покрытие обладает термической свариваемостью.
24. Поверхностное покрытие по одному из пп.18-23,
которое получают с помощью способа по одному из пп.9-17.
25. Изделие с, по меньшей мере, одной полимерной поверхностью, которое имеет поверхностное покрытие по одному из пп.18-24.
26. Изделие по п.25,
отличающееся тем,
что полимерную поверхность выбирают из ПВХ, ПЭТ, ПЭ, ПК, ПММА или комбинации данных полимерных поверхностей.
27. Применение изделия по одному из пп.25 или 26 для облицовки устройств, оборудования, инструментов, измерительных приборов, санитарно-технических приборов, кухонных приборов, бытовых приборов, интерьеров транспортных средств, кабин (кокпитов), дисплеев, обзорных окон или мебели.
28. Применение изделия по одному из пп.25 или 26 в виде пластин, оболочек, формованных деталей, кожухов, ручек, рычагов, ножек, дверей, крышек, полов, боковых стенок, грифов, декоративных элементов или брызговиков.
29. Применение изделия по одному из пп.25 или 26 в качестве предметов домашнего обихода, орудий труда для домашнего хозяйства, а также их частей, в качестве корпусов приборов или рамок приборов, посуды, столовых приборов для вечеринок, подносов, кухонного инвентаря, ваз для цветов, облицовок для стенных часов, стереофонических установок, корпусов для бытовых приборов, елочных шаров, браслетов, украшений, ламп и фонарей, отделочных материалов, приборов и вспомогательных средств для игр, спорта и досуга, садовой мебели, садово-огородного инвентаря, мест для сидения в парках или на игровых площадках, приборов, вспомогательных средств и устройств для медицинских целей и пациентов, оправ для очков, больничного оборудования или его частей.