RU2008140949A - Стальной лист для дуговой сварки под флюсом - Google Patents
Стальной лист для дуговой сварки под флюсом Download PDFInfo
- Publication number
- RU2008140949A RU2008140949A RU2008140949/02A RU2008140949A RU2008140949A RU 2008140949 A RU2008140949 A RU 2008140949A RU 2008140949/02 A RU2008140949/02 A RU 2008140949/02A RU 2008140949 A RU2008140949 A RU 2008140949A RU 2008140949 A RU2008140949 A RU 2008140949A
- Authority
- RU
- Russia
- Prior art keywords
- steel sheet
- arc welding
- submerged arc
- welding under
- under flux
- Prior art date
Abstract
1. Стальной лист для дуговой сварки под флюсом, содержащий по массе 0,03-0,09% C, 1,5-2,5% Mn, 0,005-0,025% Nb, 0,005-0,02% Ti, 0,01-0,06% Al, не более 0,0005% B, 0,001-0,008% N, не более 0,015% P, не более 0,015% S и не более 0,006% O, остальное составляют Fe и примесей. ! 2. Стальной лист для дуговой сварки под флюсом по п.1, дополнительно содержащий по меньшей мере одно из не более 0,6% Cu, не более 1,5% Ni, не более 0,04% V, не более 0,08% Mo и не более 0,5% Cr, при этом выполняются следующие выражения (1) и (2): ! (Mo/15+V/3+Nb/2) ≤ 0,015 (1) ! (Mn/20+Cu/20+Ni/60) ≥ 0,09 (2), ! где символы означают содержания элементов (мас.%). ! 3. Стальной лист для дуговой сварки под флюсом по п.1, дополнительно содержащий не более 0,3% Si. ! 4. Стальной лист для дуговой сварки под флюсом по п.2, дополнительно содержащий не более 0,3% Si. ! 5. Стальной лист для дуговой сварки под флюсом по любому из пп.1-4, дополнительно содержащий по меньшей мере одно из не более 0,005% Ca, не более 0,005% Zr, не более 0,005% Mg и не более 0,005% Ce.
Claims (5)
1. Стальной лист для дуговой сварки под флюсом, содержащий по массе 0,03-0,09% C, 1,5-2,5% Mn, 0,005-0,025% Nb, 0,005-0,02% Ti, 0,01-0,06% Al, не более 0,0005% B, 0,001-0,008% N, не более 0,015% P, не более 0,015% S и не более 0,006% O, остальное составляют Fe и примесей.
2. Стальной лист для дуговой сварки под флюсом по п.1, дополнительно содержащий по меньшей мере одно из не более 0,6% Cu, не более 1,5% Ni, не более 0,04% V, не более 0,08% Mo и не более 0,5% Cr, при этом выполняются следующие выражения (1) и (2):
(Mo/15+V/3+Nb/2) ≤ 0,015 (1)
(Mn/20+Cu/20+Ni/60) ≥ 0,09 (2),
где символы означают содержания элементов (мас.%).
3. Стальной лист для дуговой сварки под флюсом по п.1, дополнительно содержащий не более 0,3% Si.
4. Стальной лист для дуговой сварки под флюсом по п.2, дополнительно содержащий не более 0,3% Si.
5. Стальной лист для дуговой сварки под флюсом по любому из пп.1-4, дополнительно содержащий по меньшей мере одно из не более 0,005% Ca, не более 0,005% Zr, не более 0,005% Mg и не более 0,005% Ce.