RU2007107491A - Способ обработки диоксида титана и пигмент на его основе - Google Patents
Способ обработки диоксида титана и пигмент на его основе Download PDFInfo
- Publication number
- RU2007107491A RU2007107491A RU2007107491/15A RU2007107491A RU2007107491A RU 2007107491 A RU2007107491 A RU 2007107491A RU 2007107491/15 A RU2007107491/15 A RU 2007107491/15A RU 2007107491 A RU2007107491 A RU 2007107491A RU 2007107491 A RU2007107491 A RU 2007107491A
- Authority
- RU
- Russia
- Prior art keywords
- added
- zirconium
- titanium dioxide
- compounds
- tio
- Prior art date
Links
Classifications
-
- C—CHEMISTRY; METALLURGY
- C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
- C09C—TREATMENT OF INORGANIC MATERIALS, OTHER THAN FIBROUS FILLERS, TO ENHANCE THEIR PIGMENTING OR FILLING PROPERTIES ; PREPARATION OF CARBON BLACK ; PREPARATION OF INORGANIC MATERIALS WHICH ARE NO SINGLE CHEMICAL COMPOUNDS AND WHICH ARE MAINLY USED AS PIGMENTS OR FILLERS
- C09C1/00—Treatment of specific inorganic materials other than fibrous fillers; Preparation of carbon black
- C09C1/36—Compounds of titanium
-
- C—CHEMISTRY; METALLURGY
- C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
- C09C—TREATMENT OF INORGANIC MATERIALS, OTHER THAN FIBROUS FILLERS, TO ENHANCE THEIR PIGMENTING OR FILLING PROPERTIES ; PREPARATION OF CARBON BLACK ; PREPARATION OF INORGANIC MATERIALS WHICH ARE NO SINGLE CHEMICAL COMPOUNDS AND WHICH ARE MAINLY USED AS PIGMENTS OR FILLERS
- C09C1/00—Treatment of specific inorganic materials other than fibrous fillers; Preparation of carbon black
- C09C1/36—Compounds of titanium
- C09C1/3607—Titanium dioxide
- C09C1/3653—Treatment with inorganic compounds
- C09C1/3661—Coating
-
- C—CHEMISTRY; METALLURGY
- C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
- C09D—COATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
- C09D7/00—Features of coating compositions, not provided for in group C09D5/00; Processes for incorporating ingredients in coating compositions
- C09D7/40—Additives
- C09D7/60—Additives non-macromolecular
- C09D7/61—Additives non-macromolecular inorganic
- C09D7/62—Additives non-macromolecular inorganic modified by treatment with other compounds
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C16/00—Chemical coating by decomposition of gaseous compounds, without leaving reaction products of surface material in the coating, i.e. chemical vapour deposition [CVD] processes
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C16/00—Chemical coating by decomposition of gaseous compounds, without leaving reaction products of surface material in the coating, i.e. chemical vapour deposition [CVD] processes
- C23C16/06—Chemical coating by decomposition of gaseous compounds, without leaving reaction products of surface material in the coating, i.e. chemical vapour deposition [CVD] processes characterised by the deposition of metallic material
-
- C—CHEMISTRY; METALLURGY
- C01—INORGANIC CHEMISTRY
- C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
- C01P2002/00—Crystal-structural characteristics
- C01P2002/30—Three-dimensional structures
-
- C—CHEMISTRY; METALLURGY
- C01—INORGANIC CHEMISTRY
- C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
- C01P2004/00—Particle morphology
- C01P2004/80—Particles consisting of a mixture of two or more inorganic phases
- C01P2004/82—Particles consisting of a mixture of two or more inorganic phases two phases having the same anion, e.g. both oxidic phases
- C01P2004/84—Particles consisting of a mixture of two or more inorganic phases two phases having the same anion, e.g. both oxidic phases one phase coated with the other
-
- C—CHEMISTRY; METALLURGY
- C01—INORGANIC CHEMISTRY
- C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
- C01P2006/00—Physical properties of inorganic compounds
- C01P2006/60—Optical properties, e.g. expressed in CIELAB-values
- C01P2006/64—Optical properties, e.g. expressed in CIELAB-values b* (yellow-blue axis)
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
- C08K3/00—Use of inorganic substances as compounding ingredients
- C08K3/18—Oxygen-containing compounds, e.g. metal carbonyls
- C08K3/20—Oxides; Hydroxides
- C08K3/22—Oxides; Hydroxides of metals
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
- C08K9/00—Use of pretreated ingredients
- C08K9/02—Ingredients treated with inorganic substances
Landscapes
- Chemical & Material Sciences (AREA)
- Organic Chemistry (AREA)
- Engineering & Computer Science (AREA)
- Materials Engineering (AREA)
- Wood Science & Technology (AREA)
- Life Sciences & Earth Sciences (AREA)
- Inorganic Chemistry (AREA)
- General Chemical & Material Sciences (AREA)
- Chemical Kinetics & Catalysis (AREA)
- Mechanical Engineering (AREA)
- Metallurgy (AREA)
- Pigments, Carbon Blacks, Or Wood Stains (AREA)
- Inorganic Compounds Of Heavy Metals (AREA)
- Paints Or Removers (AREA)
- Compositions Of Macromolecular Compounds (AREA)
Claims (17)
1. Способ обработки диоксида титана, в частности, для производства пигментов, отличающийся тем, что сначала получают основу в виде водной суспензии диоксида титана при значении рН, равном не более 3, или при значении рН, равном по крайней мере 10, затем добавляют в нее водорастворимые соединения олова и циркония, а также водорастворимые соединения по крайней мере одного дополнительного элемента, выбранного из группы, включающей алюминий, кремний и титан, при рН, равном не более 3 или по крайней мере 10, и доводят получаемую смесь до величины рН от 6 до 8.
2. Способ по п.1, отличающийся тем, что добавляют соединения олова в количестве от 0,1 до 1,0 мас.%, предпочтительно от 0,2 до 0,5 мас.%, в перерасчете на SnO2, к основе TiO2.
3. Способ по п.1, отличающийся тем, что добавляют соединения циркония в количестве от 0,1 до 1,5 мас.%, предпочтительно от 0,2 до 1,0 мас.%, в перерасчете на ZrO2, к основе TiO2.
4. Способ по п.1, отличающийся тем, что добавляют соединения алюминия в количестве от 0,1 до 3,0 мас.%, предпочтительно от 0,2 до 1,5 мас.%, в перерасчете на Al2О3, к основе TiO2.
5. Способ по п.1, отличающийся тем, что добавляют соединения кремния в количестве от 0,1 до 1,5 мас.%, предпочтительно от 0,2 до 1,0 мас.%, в перерасчете на SiO2, к основе TiO2.
6. Способ по п.1, отличающийся тем, что добавляют соединения титана в количестве от 0,1 до 1,0 мас.%, в перерасчете на TiO2, к основе TiO2.
7. Способ по п.1, отличающийся тем, что дополнительно наносят внешний слой из водосодержащего оксида алюминия.
8. Способ по п.7, отличающийся тем, что после нанесения внешнего слоя рН смеси доводят до значения, равного 7, предпочтительно до значения, равного по крайней мере 7,5.
9. Способ по п.1 или 2, отличающийся тем, что добавляемое соединение олова выбирают из группы, включающей хлорид двухвалентного олова, сульфат двухвалентного олова, станнат калия и станнат натрия.
10. Способ по п.1 или 3, отличающийся тем, что добавляемое соединение циркония выбирают из группы, включающей сульфат циркония, оксихлорид циркония, нитрат циркония и карбонат циркония.
11. Способ по любому из пп.1, 4 и 7, отличающийся тем, что добавляемым соединением алюминия является алюминат щелочного металла, в частности, алюминат натрия или кислотное соединение алюминия, в частности, сульфат алюминия или хлорид алюминия.
12. Способ по п.1 или 5, отличающийся тем, что добавляемым соединением кремния является силикат щелочного металла, в частности, силикат натрия.
13. Способ по п.1 или 6, отличающийся тем, что добавляемым соединением титана является титанилпроизводное, в частности, титан илсульфат или титанилхлорид.
14. Способ по п.1, отличающийся тем, что при доведении получаемой смеси до величины рН от 6 до 8 или получении смеси добавляют щелочь или кислоту или их смеси.
15. Способ по п.1, отличающийся тем, что диоксид титана дополнительно обжигают при температуре от 125 до 500°С, предпочтительно при температуре приблизительно 160°С, в частности, при температуре приблизительно 250°С.
16. Пигмент на основе диоксида титана, полученный способом по любому из пп.1-15.
17. Применение пигмента на основе диоксида титана по п.16 в составе красок, лаков и пластмасс.