RU2006114345A - Микрогели в сшиваемой органической среде, способ их получения и их применение - Google Patents
Микрогели в сшиваемой органической среде, способ их получения и их применение Download PDFInfo
- Publication number
- RU2006114345A RU2006114345A RU2006114345/04A RU2006114345A RU2006114345A RU 2006114345 A RU2006114345 A RU 2006114345A RU 2006114345/04 A RU2006114345/04 A RU 2006114345/04A RU 2006114345 A RU2006114345 A RU 2006114345A RU 2006114345 A RU2006114345 A RU 2006114345A
- Authority
- RU
- Russia
- Prior art keywords
- composition according
- microgel
- composition
- microgels
- organic medium
- Prior art date
Links
- 238000004519 manufacturing process Methods 0.000 title claims 3
- 239000000203 mixture Substances 0.000 claims 45
- YXFVVABEGXRONW-UHFFFAOYSA-N Toluene Chemical compound CC1=CC=CC=C1 YXFVVABEGXRONW-UHFFFAOYSA-N 0.000 claims 9
- 239000002245 particle Substances 0.000 claims 9
- 238000000034 method Methods 0.000 claims 8
- 229920000642 polymer Polymers 0.000 claims 5
- 238000000576 coating method Methods 0.000 claims 4
- 239000003431 cross linking reagent Substances 0.000 claims 3
- 238000005266 casting Methods 0.000 claims 2
- 150000002009 diols Chemical class 0.000 claims 2
- 125000000524 functional group Chemical group 0.000 claims 2
- 230000009477 glass transition Effects 0.000 claims 2
- 229920005862 polyol Polymers 0.000 claims 2
- 150000003077 polyols Chemical class 0.000 claims 2
- 238000002360 preparation method Methods 0.000 claims 2
- 230000008961 swelling Effects 0.000 claims 2
- 239000000654 additive Substances 0.000 claims 1
- 239000011248 coating agent Substances 0.000 claims 1
- 229920001577 copolymer Polymers 0.000 claims 1
- 238000004132 cross linking Methods 0.000 claims 1
- 125000005442 diisocyanate group Chemical group 0.000 claims 1
- 229920001971 elastomer Polymers 0.000 claims 1
- 239000000839 emulsion Substances 0.000 claims 1
- 239000000945 filler Substances 0.000 claims 1
- 125000005842 heteroatom Chemical group 0.000 claims 1
- 229920001519 homopolymer Polymers 0.000 claims 1
- 125000002887 hydroxy group Chemical group [H]O* 0.000 claims 1
- 238000000465 moulding Methods 0.000 claims 1
- 229920001228 polyisocyanate Polymers 0.000 claims 1
- 239000005056 polyisocyanate Substances 0.000 claims 1
- 238000006116 polymerization reaction Methods 0.000 claims 1
- 230000000379 polymerizing effect Effects 0.000 claims 1
- 230000005855 radiation Effects 0.000 claims 1
- 239000006254 rheological additive Substances 0.000 claims 1
- 229920002725 thermoplastic elastomer Polymers 0.000 claims 1
- 239000002562 thickening agent Substances 0.000 claims 1
- 239000013008 thixotropic agent Substances 0.000 claims 1
Classifications
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
- C08J3/00—Processes of treating or compounding macromolecular substances
- C08J3/02—Making solutions, dispersions, lattices or gels by other methods than by solution, emulsion or suspension polymerisation techniques
- C08J3/03—Making solutions, dispersions, lattices or gels by other methods than by solution, emulsion or suspension polymerisation techniques in aqueous media
- C08J3/075—Macromolecular gels
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
- C08L75/00—Compositions of polyureas or polyurethanes; Compositions of derivatives of such polymers
- C08L75/04—Polyurethanes
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
- C08G2220/00—Compositions for preparing gels other than hydrogels, aerogels and xerogels
Landscapes
- Chemical & Material Sciences (AREA)
- Dispersion Chemistry (AREA)
- Chemical Kinetics & Catalysis (AREA)
- Medicinal Chemistry (AREA)
- Polymers & Plastics (AREA)
- Organic Chemistry (AREA)
- Health & Medical Sciences (AREA)
- Compositions Of Macromolecular Compounds (AREA)
- Processes Of Treating Macromolecular Substances (AREA)
- Polyurethanes Or Polyureas (AREA)
- Addition Polymer Or Copolymer, Post-Treatments, Or Chemical Modifications (AREA)
- Polymerisation Methods In General (AREA)
- Paints Or Removers (AREA)
Claims (40)
1. Композиция, представляющая собой микрогель в сшиваемой органической среде, включающая по меньшей мере одну органическую среду (А), которая обладает вязкостью менее 30000 мПуаз при температуре 120°С, и по меньшей мере один микрогель (В), который не был сшит с помощью высокоэнергетического облучения.
2. Композиция по п.1, в которой сшиваемая органическая среда (А) имеет вязкость менее 10000 мПуаз при температуре 120°С.
3. Композиция по п.1, в которой сшиваемая органическая среда (А) имеет вязкость менее 1000 мПуаз при температуре 120°С.
4. Композиция по любому из пп.1-3, в которой исходные частицы микрогеля (В) имеют примерно сферическую форму.
5. Композиция по п.1, в которой диаметры индивидуальных исходных частиц микрогеля (В) определяются по формуле
[(d1-d2)/d2]·100,
где d1 и d2 являются любыми из двух диаметров исходной частицы и d1>d2, меньше, чем 250%.
6. Композиция по п.4, в которой диаметры индивидуальных исходных частиц микрогеля (В) определяются по формуле
[(d1-d2)/d2]·100,
где d1 и d2 являются любыми из двух диаметров исходной частицы и d1>d2, меньше, чем 250%.
7. Композиция по п.1, в которой исходные частицы микрогеля (В) имеют средний размер частиц от 5 до 500 нм.
8. Композиция по п.1, в которой исходные частицы микрогеля (В) имеют средний размер частиц менее 99 нм.
9. Композиция по п.1, в которой микрогели (В) содержат компоненты, которые не растворимы в толуоле при 23°С, и они составляют по меньшей мере около 70% от всей композиции.
10. Композиция по п.1, в которой микрогели (В) имеют индекс набухания в толуоле при 23°С менее чем примерно 80.
11. Композиция по п.1, в которой микрогели (В) имеют температуру стеклования в диапазоне от -100 до +120°С.
12. Композиция по п.1, в которой микрогели (В) имеют ширину области стеклования более чем примерно 5°С.
13. Композиция по п.1, в которой микрогели (В) могут быть получены полимеризацией эмульсии.
14. Композиция по п.1, в которой микрогели (В) основаны на резине.
15. Композиция по п.1, в которой микрогели (В) основаны на гомополимерах или неупорядоченных сополимерах.
16. Композиция по п.1, в которой микрогели (В) были модифицированы функциональными группами, реагирующими с С=С двойными связями.
17. Композиция по п.1, в которой сшиваемая органическая среда (А) является сшиваемой через функциональные группы, содержащие гетероатомы, или через С=С группы.
18. Композиция по п.1, которая включает от 1 до 60 вес.% микрогеля (В) по отношению к общему количеству композиции.
19. Композиция по п.1, которая включает от 10 до 99 вес.% сшиваемой органической среды (А) по отношению к общему количеству композиции.
20. Композиция по п.1, которая дополнительно включает наполнители или добавки.
21. Композиция по п.1, которая была приготовлена посредством смешивания сшиваемой среды (А) и микрогеля (В) в гомогенизаторе, шаровой мельнице, трехвалковой мельнице, одноканальном или многоканальном экструдере, тестомесильной машине и/или диссольвере (распускном танке).
22. Композиция по п.21, которая была приготовлена посредством гомогенизатора, шаровой мельницы или трехвалковой мельницы.
23. Композиция по п.1, которая имеет вязкость от 25 до 20000000 мПуаз при скорости 5 с-1, при определении в измерительной системе конус/пластина согласно DIN 53018 при 20°C.
24. Композиция по п.1, в которой микрогель (В) имеет индекс набухания в толуоле при 23°С менее чем примерно 80.
25. Композиция по п.1, в которой микрогель был модифицирован по гидроксильным группам.
26. Композиция по п.1, в которой сшиваемая среда представляет собой по меньшей мере один полиол, предпочтительно диол, или их смесь.
27. Использование композиции по п.1 для приготовления микрогельсодержащих полимеров.
28. Использование композиции согласно п.27 для приготовления микрогельсодержащих термопластичных эластомеров.
29. Использование композиции, заявленной по любому из пп.1-26 для производства формованных изделий или покрытий.
30. Способ приготовления микрогельсодержащих полимеров путем полимеризации композиции по любому из пп.1-26.
31. Композиция по пп.1-25, полученная способом по п.30.
32. Использование композиций, заявленных в п.31 в качестве форм для отливки или покрытий.
33. Способ производства формованных изделий или покрытий с помощью отливки (формовки) или нанесения покрытия с использованием композиций согласно любому из пп.1-26.
34. Способ приготовления композиции, заявленной по любому из пп.1-26, отличающийся тем, что компоненты (А) и (В) вместе подвергаются обработке в гомогенизаторе, шаровой мельнице, трехвалковой мельнице, одноканальном или многоканальном экструдере, тестомесильной машине и/или диссольвере (распускном танке).
35. Способ приготовления микрогельсодержащих полимерных композиций, отличающийся тем, что включает смешивание по меньшей мере одной сшиваемой органической среды (А), имеющей вязкость менее чем 30000 мПуаз при температуре 120°С, и по меньшей мере одного микрогеля (В), который не был сшит посредством высоко энергетического облучения, с добавлением сшивающего агента (С) для сшиваемой органической среды (А) и последующим сшиванием композиции.
36. Способ по п.35, отличающийся тем, что сшиваемая органическая среда (А) представляет собой по меньшей мере один полиол, предпочтительно диол, или их смесь, а сшивающий агент (С) представляет собой по меньшей мере один полиизоцианат, предпочтительно диизоцианат, или их смесь.
37. Способ по п.35 или 36, отличающийся тем, что компоненты (А) и (В) смешивают в гомогенизаторе, шаровой мельнице, трехвалковой мельнице, одноканальном или многоканальном экструдере, тестомесильной машине и/или диссольвере (распускном танке).
38. Полимерная композиция, полученная способом по любому из пп.35-37.
39. Двухсекционный набор, включающий в пространственно разделенных частях композицию по любому из пп.1-26 и полимерную композицию, полученную способом по пп.35-37, содержащую сшивающий агент (С) для сшиваемой органической среды (А).
40. Использование микрогелей в качестве реологических добавок, в частности в качестве загустителя или тиксотропного агента, в сшиваемой органической среде, имеющей вязкость менее чем 30000 мПуаз при температуре 120°С.