RU1813077C - Стекло дл стекловолокна - Google Patents
Стекло дл стекловолокнаInfo
- Publication number
- RU1813077C RU1813077C SU904743944A SU4743944A RU1813077C RU 1813077 C RU1813077 C RU 1813077C SU 904743944 A SU904743944 A SU 904743944A SU 4743944 A SU4743944 A SU 4743944A RU 1813077 C RU1813077 C RU 1813077C
- Authority
- RU
- Russia
- Prior art keywords
- glass
- diameter
- microns
- mol
- fiberglass
- Prior art date
Abstract
Использование: дл изготовлени стекл нных войл.ока, ваты, холста и т.п, изделий. Стекло дл стекловолокна имеет следующий состав: оксид кремни 60,7 мас.% БФ SI02, оксид натри 15,4 мол,% БФ Na20; оксид кальци 16,5 мол. % БФ СаО; оксид кали 0,7 мол.% БФ К20; оксид магни 3,2 мол.% БФ МдО; оксид бора 3,3 мол.% БФ В20з; оксид железа 0,2 мол.% БФ Рез04, причем содержание волокон диаметром 0,1-3 мк составл ет 10-98%. Стекловолокна имеют меньшее врем пребывани в легких. 2 табл.
Description
Изобретение относитс к области неорганических волокон, в частности к стекловолокнам дл изготовлени стекл нных войлока, ваты, холста и т.п. изделий.
Целью изобретени вл етс повышение биологической переносимости изготовл емых изделий диаметром 0,1-8 мк,
Это достигаетс предлагаемыми стекловолокнами дл изготовлени стекл нных войлока, ваты, холста и т.п. изделий, содержащими двуокись кремни , окись бора, окись натри , окись кали , окись кальци , окись магни и окислы железа и имеющими диаметр 0,1-8 мк, за счет того, что указанные компоненты использованы в следующем соотношении, мол.%:
Двуокись кремни 60,7 Окись натри 15,4 Окись кальци 16,5 Окись кали 0,7 Окись магни . 3,2 Окись бора 3,3
Окислы железа0,2.
Содержание волокон диаметром OJ-3 мк предпочтительно составл ет 50-95%,
Кроме того, предлагаемые волокна могут содержать еще 0,1-3 мол.% окиси алюмини и/или 0,1-6 мол.% двуокиси титана и/или 0,1-2 мол.% фторида. Кроме того, предлагаемые волокна могут содержать окислы бари , цинка, стронци и циркони в максимальном общем количестве до 1 мол.%.
Предлагаемые стекловолокна изготовл ют общеизвестными способами.
Пример 1. Опыт 1. Изготовленные известным способом с использованием ло- дочки дл выт гивани стекловолокна А-В нижеследующей характеристики исследовались In vivo на их физиологическую переносимость .
Стекловолокна А (согласно изобретению ).
Химический состав (мол.%):
60,7 5(02,15,4 Na20,
16.5CaO. 3,ЗВ2Оз
3,2 MgO, 0,7 KaO, 0,2 окислов железа.
Распределение диаметров (определенного при помощи растрового электронного микроскопа): 0,1-8 мк, причем содержание волокон диаметром 0,1-3 мк составл ет 95%.
Стекловолокна Б (согласно изобретению ).
Химический состав соответствует стекловолокнам А. Распределение диаметров (определенное при помощи растрового электронного микроскопа): 0.1-8 мк, причем содержание волокон диаметром 0,1-3 мк составл ет 90%.
Стекловолокна В (известные - сравнительные ).
Рапределение диаметров (определенное при помощи растрового электронного микроскопа): 0,1-8 мк, причем содержание волокон диаметром 0,1-3 мк составл ет 90%.
Посредством шаровой мельницы стекловолокна А-В измельчают и по 2 мг волокон , суспендировэнных в 0,4 мл физиологического раствора поваренной соли , интратрахеально инстиллируют 35 самкам белых крыс. По истечении 1 дн , 1, 6,12. и 24 мес цев вскрывают по 5 животных на группу волокон, вынимают легкие, сушат и при температуре 300°С подвергают плазменному озолению. Дл отделени волокон от солевых компонентов суспендируют каждый раз часть золы легких в IN сол ной кислоты и подвергают ультразвуковой обработке в течение нескольких минут. Затем
0
волокна выдел ют на фильтре и определ ют их среднее количество в легких. Результаты опытов сведены в табл. 1.
Сравнение результатов опытов показывает , что предлагаемые стекловолокна А и Б имеют значительно меньшее врем пребывани в легких, чем сравнительные волокна В.
Опыт 2, Определение степени образовани опухолей. Стекловолокна А-В сначала размалывают в шаровой мельнице и затем в виде суспензии в 2 мл раствора поваренной соли интраперитонеально инъецируют белым крысам различными доза- 5 ми. По истечении 2 лет животных исследуют на образование опухолей. Проведение опытов и их результаты сведены в табл. 2.
Сравнение результатов опытов показывает , что предлагаемые стекловолокна А и Б практически не имеют никакого канцерогенного действи .
Ф о р м у л а и з о б р е т е н и Стекло дл стекловолокна, включающее Si02. NaaO. СаО, КаО, MgO, ВаОз, РезО/г, о т- л и ч а ю щ е е с и тем, что, с целью повышени биологической переносимости изготов; л емых изделий диаметром 0,1-8 мк, она содержит указанные компоненты в следующем соотношении, мол.%:
SI02 60,7 . №20 15,4 СаО 16.5 , К20 0,7 MgO 3,2 В20 3.3 Рез04 0,2.
0
5
0
5
40
Таблица 1
Продолжение табл. 1
Таблица 2