RO107702B1 - Procedeu pentru obtinerea de corpuri de formare, din celuloza - Google Patents
Procedeu pentru obtinerea de corpuri de formare, din celuloza Download PDFInfo
- Publication number
- RO107702B1 RO107702B1 RO148885A RO14888591A RO107702B1 RO 107702 B1 RO107702 B1 RO 107702B1 RO 148885 A RO148885 A RO 148885A RO 14888591 A RO14888591 A RO 14888591A RO 107702 B1 RO107702 B1 RO 107702B1
- Authority
- RO
- Romania
- Prior art keywords
- nmmo
- precipitation bath
- cellulose
- water
- solution
- Prior art date
Description
Invenția de față se referă la un procedeu pentru obținerea de corpuri de forme din celuloză, dintr-o soluție de celuloză în N-metilmorfolin-N-oxid (NMMO) și apă în care soluția se supune formării și apoi se precipită' celuloza într-o baie de precipitare, care conține apă și NMMO.
Se cunoaște din US-PS 4196282, modul de obținere a unei soluții de celuloză în N-oxid de N-metilmorfolină (prescurtat în cele ce urmează prin notația NMMO) și apă. Soluțiile de celuloză sunt utilizate la obținerea de fibre din celuloză sau a altor corpuri de formare, pe bază de celuloză, în acest scop, soluția se extrudează prin duze de filare într-o baie de precipitare. Utilizarea unui amestec de NMMO și apă ca solvent are diferite avantaje: mai ales trebuie scos în evidență faptul, că este posibilă recircularea soluției, astfel că poluarea mediului ambiant se menține între limite foarte restrânse.
La procedeul NMMO, celuloza dizolvată în NMMO și apă se lasă să coaguleze într-o baie de precipitare conținând NMMO. Fibra se spală, apoi apa de spălare se recirculă în baia de precipitare și baia de precipitare se concentrează prin evaporare. Distilatul se utilizează pentru spălarea fibrei (vezi mai sus) și concentratul NMMO se utilizează la rândul său pentru o nouă obținere de soluție.
în baia de precipitare concentrația NMMO a fost limitată până acum de la circa 20% până la 25%, deoarece la concentrații mai ridicate s-au prejudiciat proprietățile textile și mecanice ale fibrei. Totuși ar fi de dorit, să se ridice concentrația NMMO în baia de precipitare, pentru ca apoi să trebuiască să se evapore mai puțină apă din baia de precipitare.
Problema, pe care o rezolvă invenția de față, este conducerea procedeului cunoscut, astfel încât și la concentrații ridicate de NMMO în baia de precipitare.
să se obțină proprietăți bune ale fibrei. Aceasta se realizează prin invenția de față, prin aceea că, temperatura băii de precipitare este de maximum 0°C.
Invenția prezintă următoarele avantaje:
- duce la obținerea unor fibre celulozice cu proprietăți mecanice superioare, chiar și la concentrații ridicate de NMMO în baia de precipitare;
- reduce timpul de lucru, precum și consumul de energie necesar conducerii procedeului prin micșorarea cantității de apă care trebuie evaporată;
- permite conducerea procedeului la concentrații de peste 40% NMMO în baia de precipitare.
Cu ajutorul exemplelor care urmează se compară invenția cu stadiul tehnicii, pentru a susține afirmațiile de mai sus.
Exemplele 1, până la 6:
2276 g celuloză (conținut de substanță solidă sau uscată 94%, DP 750. (DP = - grad de polimerizare mediu/, alfa - 98%) și 0,02% propilester al acidului galic se aduc în suspensie în 26139 g soluție apoasă 60% de N-oxid al N-metilmorfolinei; după aceea se elimină prin distilare timp de 2 h la 100°C și la un vid de 50 până la 300 mbar 9415 g apă. Soluția de filare formată în acest caz a avut următoarea compoziție: celuloză: 10%, apă: 12%, NMMO'. 78%. Ea s-a presat printr-o duză cu 589 găuri (diametrul orificiilor duzei 130 pm). Temperatura de filare a fost în acest caz de 75UC. Fibrele formate au fost precipitate - după laminare într-o fantă de aer - într-o baie de precipitare conținând NMMO. Titrul, concentrația NMMO în baia de precipitare și temperatura băii de precipitare. sunt indicate în tabel, pentru fiecare exemplu; din acest tabel rezultă și proprietățile fibrelor care se obțin. în acest tabel sunt următoarele notații: FFk - rezistența fibrei (condiționată). FDk = dilatarea fibrei. SF = rezistența la buclă.
Exemplul nr. | Finețea dtex | Concentrația băii de precipitare % | Temperatura băii de precipitare °C | EFk cN/tex | FDk % | SF cN/tex |
1 | ' 1,62 | 0 | 15 | 47,8 | 10,9 | 18,1 |
2 | 1,65 | 21 | 11 | 46,4 | 11,4 | 17,8 |
3 | 1,62 | 40 | 14 | 41,4 | 8,6 | 12 |
4 | 1,63 | 19,5 | 0 | 49 | 12,4 | 19,5 |
5 | 1,68 | 30 | - -2,1 | 47,1 | 11,8 | 19,5 |
6 | 1,85 | 40 | -E3 | 45,5 | 12,2 | 21,9 |
Exemplele 1 și 2, corespund stadiului tehnicii; se utilizează în baia de precipitare apă curată (exemplul 1), respectiv apă cu 20% NMMO (exemplul 2); temperaturile din baia de precipitare sunt relativ ridicate (15 respectiv 11°C). Fibrele de celuloză precipitate din aceste băi au proprietăți mulțumitoare. La exemplul 3, s-a încercat să se ridice concentrația NMMO în baia de precipitare la 40%; prin aceasta însă proprietățile fibrelor devin mai proaste.
Exemplele 4 până la 6. sunt exemple, conform invenției, adică temperaturile sunt de maximum 0,°C. Cum se vede, la aceste temperaturi mărirea concentrației NMMO în baia de precipitare are o influ ență mai mică asupra proprietăților fibrelor; astfel, de exemplu, fibra conform exemplului 5, este cu totul echivalentă, cu cea conform exemplului 1.
Claims (1)
- RevendicareProcedeu pentru obținerea de corpuri de formare din celuloză dintr-o soluție de 10 celuloză în N-metilmorfolin-N-oxid (NMMO) și apă, soluția este supusă formării și apoi celuloza se precipită dintr-o baie de precipitare care conține apa și (NMMO), caracterizat prin aceea că 15 temperatura băii de precipitare este de maximum 0°C.Președintele comisiei de invenții: dr. ing. Paraschiv Adriana Examinator: ins. lonescu Bucura