MA63900B1 - Tôle d'acier trempée et revêtue présentant une excellente aptitude au formage et son procédé de fabrication - Google Patents
Tôle d'acier trempée et revêtue présentant une excellente aptitude au formage et son procédé de fabricationInfo
- Publication number
- MA63900B1 MA63900B1 MA63900A MA63900A MA63900B1 MA 63900 B1 MA63900 B1 MA 63900B1 MA 63900 A MA63900 A MA 63900A MA 63900 A MA63900 A MA 63900A MA 63900 B1 MA63900 B1 MA 63900B1
- Authority
- MA
- Morocco
- Prior art keywords
- steel sheet
- coated steel
- hardened
- manufacturing same
- excellent formability
- Prior art date
Abstract
L'invention concerne une tôle d'acier trempée et revêtue ayant une composition comprenant les éléments suivants, exprimés en pourcentage en poids : 0,17 % = carbone = 0,25 %, 1,8 % = manganèse = 2,3 %, 0,5 % = silicium = 2,0 %, 0,03 % = aluminium = 1,2 %, soufre = 0,03 %, phosphore = 0,03 %, et pouvant contenir un ou plusieurs des éléments facultatifs suivants : chrome = 0,4 %, molybdène = 0,3 %, niobium = 0,04 %, titane = 0,1 %, la composition restante étant faite de fer et des inévitables impuretés provoquées par le traitement, la microstructure de ladite tôle d'acier comprenant en fraction de surface, 4 à 20 % d'austénite résiduelle, 0 à 15 % de ferrite, 40 à 85 % de bainite revenue et un minimum de 5 % de martensite revenue, les quantités cumulées de la martensite revenue et de l'austénite résiduelle allant de 10 à 30 %. L'invention concerne en outre le procédé de fabrication de ladite tôle d'acier.
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
PCT/IB2016/057907 WO2018115936A1 (fr) | 2016-12-21 | 2016-12-21 | Tôle d'acier revêtue et revenue présentant une excellente formabilité et son procédé de fabrication |
PCT/IB2017/057996 WO2018116099A1 (fr) | 2016-12-21 | 2017-12-15 | Tôle d'acier trempée et revêtue présentant une excellente aptitude au formage et son procédé de fabrication |
Publications (1)
Publication Number | Publication Date |
---|---|
MA63900B1 true MA63900B1 (fr) | 2024-02-29 |
Family
ID=57868289
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
MA63900A MA63900B1 (fr) | 2016-12-21 | 2017-12-15 | Tôle d'acier trempée et revêtue présentant une excellente aptitude au formage et son procédé de fabrication |
Country Status (15)
Country | Link |
---|---|
US (1) | US11655516B2 (fr) |
EP (1) | EP3559298B8 (fr) |
JP (2) | JP6992070B2 (fr) |
KR (1) | KR102325717B1 (fr) |
CN (1) | CN110088332B (fr) |
BR (1) | BR112019011142A2 (fr) |
CA (1) | CA3047690C (fr) |
FI (1) | FI3559298T3 (fr) |
MA (1) | MA63900B1 (fr) |
MX (1) | MX2019007169A (fr) |
PL (1) | PL3559298T3 (fr) |
RU (1) | RU2753173C2 (fr) |
UA (1) | UA124354C2 (fr) |
WO (2) | WO2018115936A1 (fr) |
ZA (1) | ZA201903329B (fr) |
Families Citing this family (17)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
WO2020058748A1 (fr) * | 2018-09-20 | 2020-03-26 | Arcelormittal | Tôle d'acier laminée à froid et revêtue et son procédé de fabrication |
KR102276740B1 (ko) * | 2018-12-18 | 2021-07-13 | 주식회사 포스코 | 연성 및 가공성이 우수한 고강도 강판 및 그 제조방법 |
WO2020245627A1 (fr) * | 2019-06-03 | 2020-12-10 | Arcelormittal | Tôle d'acier laminée à froid et revêtue et son procédé de fabrication |
PT3754034T (pt) * | 2019-06-17 | 2022-04-20 | Tata Steel Ijmuiden Bv | Tratamento térmico de tira de aço laminada a frio |
EP3754036B1 (fr) * | 2019-06-17 | 2022-03-02 | Tata Steel IJmuiden B.V. | Traitement thermique d'une bande d'acier laminée à froid à haute résistance |
EP3754035B1 (fr) * | 2019-06-17 | 2022-03-02 | Tata Steel IJmuiden B.V. | Procédé de traitement thermique d'une bande d'acier laminée à froid |
EP3754037B1 (fr) * | 2019-06-17 | 2022-03-02 | Tata Steel IJmuiden B.V. | Procédé de traitement thermique d'une bande d'acier laminée à froid à haute résistance |
CA3163376C (fr) * | 2019-12-13 | 2024-02-27 | Arcelormittal | Tole d'acier laminee a froid et traitee thermiquement et procede de fabrication de celle-ci |
WO2021123877A1 (fr) * | 2019-12-17 | 2021-06-24 | Arcelormittal | Tôle d'acier laminée à chaud et son procédé de fabrication |
CN111270160B (zh) * | 2020-03-25 | 2021-06-15 | 武汉钢铁有限公司 | 一种抗拉强度≥1200MPa的高延伸率热轧组织调控钢及生产方法 |
CN111334720B (zh) * | 2020-03-30 | 2022-03-25 | 邯郸钢铁集团有限责任公司 | 具有良好冷成型性能的高Al耐磨钢带及其生产方法 |
WO2022018501A1 (fr) * | 2020-07-24 | 2022-01-27 | Arcelormittal | Tôle d'acier laminée à froid recuite et son procédé de fabrication |
KR20230129244A (ko) * | 2020-12-23 | 2023-09-07 | 뵈스트알파인 스탈 게엠베하 | 개선된 아연 접착력을 갖는 아연 또는 아연-합금 코팅된스트립 또는 강 |
EP4339308A1 (fr) * | 2021-06-15 | 2024-03-20 | JFE Steel Corporation | Tôle d'acier galvanisé à et élément et procédé de fabrication associé |
WO2022264585A1 (fr) * | 2021-06-15 | 2022-12-22 | Jfeスチール株式会社 | Tôle d'acier galvanisé à et élément et procédé de fabrication associé |
DE102021119047A1 (de) * | 2021-07-22 | 2023-01-26 | Thyssenkrupp Steel Europe Ag | Verfahren zur Herstellung eines kaltgewalzten Stahlflachprodukts mit einem bainitischen Grundgefüge und kaltgewalztes Stahlflachprodukt mit einem bainitischen Grundgefüge |
CN115725900B (zh) * | 2022-11-14 | 2023-10-24 | 武汉科技大学 | 一种高强度高塑性贝氏体钢及生产方法 |
Family Cites Families (26)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JP3440894B2 (ja) * | 1998-08-05 | 2003-08-25 | Jfeスチール株式会社 | 伸びフランジ性に優れる高強度熱延鋼板およびその製造方法 |
US7090731B2 (en) | 2001-01-31 | 2006-08-15 | Kabushiki Kaisha Kobe Seiko Sho (Kobe Steel, Ltd.) | High strength steel sheet having excellent formability and method for production thereof |
JP4445365B2 (ja) * | 2004-10-06 | 2010-04-07 | 新日本製鐵株式会社 | 伸びと穴拡げ性に優れた高強度薄鋼板の製造方法 |
JP5223360B2 (ja) | 2007-03-22 | 2013-06-26 | Jfeスチール株式会社 | 成形性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法 |
EP1990431A1 (fr) | 2007-05-11 | 2008-11-12 | ArcelorMittal France | Procédé de fabrication de tôles d'acier laminées à froid et recuites à très haute résistance, et tôles ainsi produites |
UA112771C2 (uk) | 2011-05-10 | 2016-10-25 | Арселормітталь Інвестігасьон І Десароло Сл | Сталевий лист з високою механічною міцністю, пластичністю і формованістю, спосіб виготовлення та застосування таких листів |
KR101624057B1 (ko) | 2011-07-29 | 2016-05-24 | 신닛테츠스미킨 카부시키카이샤 | 성형성이 우수한 고강도 강판, 고강도 아연 도금 강판 및 그들의 제조 방법 |
MX2014003715A (es) | 2011-09-30 | 2014-07-09 | Nippon Steel & Sumitomo Metal Corp | Placa de acero galvanizado por inmersion en caliente, de alta resistencia, que tiene excelente resistencia al impacto y metodo para producir la misma, y lamina de acero galvanizado por inmersion en caliente, aleada, de alta resistencia y metodo para producir la misma. |
MX2014003718A (es) | 2011-09-30 | 2014-07-14 | Nippon Steel & Sumitomo Metal Corp | Lamina de acero galvanizado y recocido, de alta resistencia, de alta capacidad de templado por coccion, lamina de acero galvanizado y recocido, aleada, de alta resistencia y metodo para manufacturar la misma. |
CA2850045C (fr) | 2011-09-30 | 2016-04-12 | Nippon Steel & Sumitomo Metal Corporation | Feuille d'acier galvanisee et son procede de fabrication |
ES2614465T3 (es) * | 2012-07-10 | 2017-05-31 | Thyssenkrupp Steel Europe Ag | Producto plano de acero laminado en frío y procedimiento para su fabricación |
WO2015011511A1 (fr) * | 2013-07-24 | 2015-01-29 | Arcelormittal Investigación Y Desarrollo Sl | Tôle d'acier à très hautes caractéristiques mécaniques de résistance et de ductilité, procédé de fabrication et utilisation de telles tôles |
KR101814949B1 (ko) | 2013-11-29 | 2018-01-04 | 신닛테츠스미킨 카부시키카이샤 | 열간 성형 강판 부재 및 그 제조 방법 |
JP5862651B2 (ja) * | 2013-12-18 | 2016-02-16 | Jfeスチール株式会社 | 耐衝撃性および曲げ加工性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法 |
EP3101147B1 (fr) * | 2014-01-29 | 2018-08-15 | JFE Steel Corporation | Tôle d'acier laminée à froid à haute résistance, et son procédé de fabrication |
JP6398210B2 (ja) * | 2014-02-07 | 2018-10-03 | 新日鐵住金株式会社 | 冷延鋼板の製造方法 |
JP6237364B2 (ja) | 2014-03-17 | 2017-11-29 | 新日鐵住金株式会社 | 衝突特性に優れた高強度鋼板及びその製造方法 |
WO2016001702A1 (fr) * | 2014-07-03 | 2016-01-07 | Arcelormittal | Procédé de fabrication d'une tôle d'acier revêtue à haute résistance présentant une résistance, une ductilité et une formabilité améliorées |
WO2016020714A1 (fr) * | 2014-08-07 | 2016-02-11 | Arcelormittal | Procédé permettant de produire une tôle d'acier revêtue présentant une meilleure résistance, une meilleure ductilité et une meilleure aptitude au formage |
US10550446B2 (en) | 2014-10-30 | 2020-02-04 | Jfe Steel Corporation | High-strength steel sheet, high-strength hot-dip galvanized steel sheet, high-strength hot-dip aluminum-coated steel sheet, and high-strength electrogalvanized steel sheet, and methods for manufacturing same |
JP6282576B2 (ja) | 2014-11-21 | 2018-02-21 | 株式会社神戸製鋼所 | 高強度高延性鋼板 |
JP6282577B2 (ja) * | 2014-11-26 | 2018-02-21 | 株式会社神戸製鋼所 | 高強度高延性鋼板 |
WO2016139876A1 (fr) | 2015-03-03 | 2016-09-09 | Jfeスチール株式会社 | Tôle d'acier à haute résistance et son procédé de production |
JP6762797B2 (ja) * | 2016-08-03 | 2020-09-30 | 株式会社神戸製鋼所 | 高強度鋼板およびその製造方法 |
DE102016012321A1 (de) * | 2016-10-17 | 2018-04-19 | Fiona Gabriella Saygivar | Absturzsicherung für Personen |
WO2018115935A1 (fr) | 2016-12-21 | 2018-06-28 | Arcelormittal | Tôle d'acier revêtue et revenue présentant une excellente formabilité et son procédé de fabrication |
-
2016
- 2016-12-21 WO PCT/IB2016/057907 patent/WO2018115936A1/fr active Application Filing
-
2017
- 2017-12-15 KR KR1020197017845A patent/KR102325717B1/ko active IP Right Grant
- 2017-12-15 WO PCT/IB2017/057996 patent/WO2018116099A1/fr unknown
- 2017-12-15 CN CN201780078783.7A patent/CN110088332B/zh active Active
- 2017-12-15 MA MA63900A patent/MA63900B1/fr unknown
- 2017-12-15 UA UAA201908296A patent/UA124354C2/uk unknown
- 2017-12-15 MX MX2019007169A patent/MX2019007169A/es unknown
- 2017-12-15 BR BR112019011142A patent/BR112019011142A2/pt not_active Application Discontinuation
- 2017-12-15 RU RU2019122654A patent/RU2753173C2/ru active
- 2017-12-15 CA CA3047690A patent/CA3047690C/fr active Active
- 2017-12-15 FI FIEP17825618.6T patent/FI3559298T3/fi active
- 2017-12-15 PL PL17825618.6T patent/PL3559298T3/pl unknown
- 2017-12-15 JP JP2019533560A patent/JP6992070B2/ja active Active
- 2017-12-15 EP EP17825618.6A patent/EP3559298B8/fr active Active
- 2017-12-15 US US16/467,643 patent/US11655516B2/en active Active
-
2019
- 2019-05-27 ZA ZA2019/03329A patent/ZA201903329B/en unknown
-
2021
- 2021-07-21 JP JP2021120300A patent/JP2021176993A/ja active Pending
Also Published As
Publication number | Publication date |
---|---|
CN110088332B (zh) | 2022-03-01 |
RU2019122654A3 (fr) | 2021-01-22 |
JP2020503443A (ja) | 2020-01-30 |
JP2021176993A (ja) | 2021-11-11 |
CA3047690A1 (fr) | 2018-06-28 |
FI3559298T3 (fi) | 2024-03-18 |
CA3047690C (fr) | 2023-02-14 |
WO2018115936A1 (fr) | 2018-06-28 |
RU2019122654A (ru) | 2021-01-22 |
EP3559298A1 (fr) | 2019-10-30 |
BR112019011142A2 (pt) | 2019-10-01 |
KR20190089010A (ko) | 2019-07-29 |
US20190338388A1 (en) | 2019-11-07 |
UA124354C2 (uk) | 2021-09-01 |
EP3559298B8 (fr) | 2024-04-10 |
KR102325717B1 (ko) | 2021-11-15 |
CN110088332A (zh) | 2019-08-02 |
JP6992070B2 (ja) | 2022-01-13 |
ZA201903329B (en) | 2020-01-29 |
EP3559298B1 (fr) | 2024-01-24 |
US11655516B2 (en) | 2023-05-23 |
MX2019007169A (es) | 2019-08-29 |
WO2018116099A1 (fr) | 2018-06-28 |
PL3559298T3 (pl) | 2024-04-29 |
RU2753173C2 (ru) | 2021-08-12 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
MA63900B1 (fr) | Tôle d'acier trempée et revêtue présentant une excellente aptitude au formage et son procédé de fabrication | |
MA47078B1 (fr) | Tôle d'acier trempé revêtue douée d'une excellente aptitude au formage et son procédé de fabrication | |
MA50559B1 (fr) | Tôle d'acier laminée à froid et traitée thermiquement et son procédé de fabrication | |
MA47998B1 (fr) | Acier pour une trempe à la presse et pièce trempée à la presse fabriquée à partir d'un tel acier | |
MX2018008561A (es) | Lamina de acero de alta resistencia que tiene excelente conformabilidad y un metodo de fabricacion de la misma. | |
MX2020004769A (es) | Hoja de acero laminada en frio y un metodo para la fabricacion de la misma. | |
MX2019003282A (es) | Lamina de acero de alta resistencia y alta conformabilidad laminada en frio y tratada termicamente y metodo de fabricacion. | |
MA39075B1 (fr) | Acier à haute résistance et procédé de fabrication | |
MX2019007170A (es) | Hoja de acero enrollada en frio, de alta resistencia con alta capacidad de formacion y un metodo para fabricar la misma. | |
MX2018007347A (es) | Amina de acero galvanizada por inmersion en caliente de alta resistencia que tiene excelente calidad de superficie y soldabilidad por puntos, y metodo de manufactura para la misma. | |
MX2020004787A (es) | Hoja de acero tratada termicamente laminada en frio y un metodo de fabricacion de la misma. | |
MX2018009643A (es) | Lamina de acero de alta resistencia y metodo para la produccion de la misma. | |
MA50999B1 (fr) | Tôle d'acier laminée à froid et recuite et son procédé de fabrication | |
WO2019123240A3 (fr) | Tôle d'acier présentant une ténacité, une ductilité et une résistance excellentes, et son procédé de fabrication | |
BR112021021486A2 (pt) | Chapa de aço martensítico laminada a frio, método de produção de uma chapa de aço martensítico laminada a frio e uso de uma chapa de aço | |
MA45115B1 (fr) | Procédé de fabrication d'une tôle d'acier twip à microstructure austénitique | |
MA54523B1 (fr) | Tôle d'acier laminée à froid traitée thermiquement et son procédé de fabrication | |
MA39417B1 (fr) | Tôle d'acier doublement recuite a hautes caracteristiques mecaniques de resistance et de ductilite, procede de fabrication et utilisation de telles tôles | |
MA51270B1 (fr) | Tôle d'acier laminée à froid et traitée thermiquement et son procédé de fabrication | |
CA2908491A1 (fr) | Acier a haute resistance manifestant une bonne ductilite et son procede d'elaboration par traitement de trempe et de partitionnement en bain de zinc | |
MA51001B1 (fr) | Tôle d'acier laminée à froid recuite et son procédé de fabrication | |
MA50143B1 (fr) | Feuille d'acier à haute formabilité pour la fabrication de pièces structurelles légères et procédé de fabrication de la feuille | |
MX2020009802A (es) | Parte forjada de acero bainitico y un metodo de fabricacion del mismo. | |
MA53640B1 (fr) | Tôle d'acier laminée à froid et revêtue et son procédé de fabrication | |
MX2018002264A (es) | Hoja de acero galvanizada y recocida y metodo de produccion de la misma. |