KR950000785A - 난연 폴리스티렌계 수지 및 그 제조방법 - Google Patents
난연 폴리스티렌계 수지 및 그 제조방법 Download PDFInfo
- Publication number
- KR950000785A KR950000785A KR1019930011853A KR930011853A KR950000785A KR 950000785 A KR950000785 A KR 950000785A KR 1019930011853 A KR1019930011853 A KR 1019930011853A KR 930011853 A KR930011853 A KR 930011853A KR 950000785 A KR950000785 A KR 950000785A
- Authority
- KR
- South Korea
- Prior art keywords
- flame retardant
- amount
- flame
- polystyrene resin
- weight
- Prior art date
Abstract
본 발명은 강도를 저하시키지 않으면서 난연성을 중대시킨 난연 폴리스티렌계 수지 및 그의 제조방법에 관한 것이다.
본 발명의 난연 폴리스티렌계 수지는 폴리스티렌계 수지 100중량부에 대하여, 난연제로 염소화 파라핀, 산화안티몬과 열팽창성 흑연의 총 합계 사용량이 5∼40중량부, 그리고 수지 조성물 전체에 대한 총 염소량이 1∼20중량부, 염소화 파라핀 사용량과 열팽창성 흑연 사용량의 비가 4 : 1∼1 : 4, 염소화 파라핀 사용량과 열팽창성 흑연 사용량의 합계에 대한 산화안티몬 사용량의 비가 0.05∼2로 되는 것을 특징으로 하고 있다.
본 발명에 따르면 종래의 난연화 방법에 비하여 소량의 난연제를 첨가하여 기계적 물성이 저하되지 않고 우수한 난연성을 나타내게 함으로써, 일용품, 전기 전자제품, 포장재, 건축자재등 각종 산업분야에 유용하게 사용될 수 있는 난연 폴리스티렌계 수지가 제공되는 효과가 있다.
Description
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음
Claims (11)
- 난연제로서 염소화 파라핀, 산화 안티몬 및 열팽창성 흑연이 조합되어 사용되며, 그 사용량에 있어서 폴리스티렌계 수지 100중량부에 대하여 상기 3종의 산화제 총 합계 사용량이 5 내지 40중량부로 되고, 전체수지 조성물에 대한 총 염소 함량이 1 내지 20중량부, 염소화 파라핀 사용량과 열팽창성 흑연 사용량의 비율이 4 : 1 내지 1 : 4, 염소화 파라핀 사용량과 열팽창성 흑연 사용량의 합계에 대한 산화 안티몬 사용량의 비가 0.05 내지 2로 되는 것을 특징으로 하는 난연 폴리스티렌계 수지.
- 제 1 항에 있어서, 상기 염소화 파라핀의 염소함량이 35 내지 80%인 것을 특징으로 하는 상기 난연 폴리스티렌계 수지.
- 제 1 항에 있어서, 상기 3종의 산화제 총 합계 사용량이 폴리스티렌계 수지 100중량부에 대하여 10 내지 30중량부로 되는 것을 특징으로 하는 상기 난연 폴리스티렌계 수지.
- 제 1 항에 있어서, 상기 폴리스티렌계 수지가 스티렌, α-메틸 스티렌, 디메틸스티렌, 에틸스티렌, 클로로스티렌, 브로모스티렌, 비닐톨루엔으로부터 선택되는 단량체의 중합체 또는 이들 단량체 끼리의 공중합체 또는 이들 단량체와 부타디엔, 아크릴로니트릴, 메틸메타크릴레이트, 이소부틸렌, 염화비닐 또는 이소프렌과의 공중합체인 것을 특징으로 하는 상기 난연 폴리스티렌계 수지.
- 제 1 항에 있어서, 상기 염소화 파라핀이 염소함유량이 68 내지 75중량%이고, 연화온도가 100 내지 115℃, 유리전이 온도가 55 내지 70℃로 되는 고온 입자 상태인 것을 특징으로 하는 상기 난연 폴리스티렌계 수지.
- 제 1 항에 있어서, 상기 열팽창성 흑연이 98중량%의 진한 황산과 50중량%의 과산화 수소수 혼합액에 20 내지 100메쉬로 분쇄한 흑연을 45℃ 이하에서 10 내지 30분 동안 접촉시키고, 물로 세척한 후 건조시켜 제조되는 것을 특징으로 하는 상기 난연 폴리스티렌계 수지.
- 제 6 항에 있어서, 상기 분쇄된 흑연이 40 내지 80메쉬의 입도를 가지는 것을 특징으로 하는 상기 난연 폴리스티렌계 수지.
- 제 1 항에 있어서, 상기 난연제들 이외에 산화방지제, 자외선흡수제, 광보호제, 활제, 대전방지제, 무기 또는 유기충전재등의 기타 첨가제가 부가 되는 것을 특징으로 하는 상기 난연 폴리스티렌계 수지.
- 제 1 항의 조성비로 된 폴리스티렌계 수지 및 난연제 각 성분을 회전 교반수단을 구비한 혼합 수단을 이용하여 상온에서 500 내지 5000RPM으로 1분 내지 10분동안 혼합한 후 혼련 압출수단에 의해 170℃ 내지 220℃에서 스크류우 RPM을 200 내지 300으로 하여 혼련 압출하는 것을 특징으로 하는 상기 난연 폴리스티렌계 수지의 제조방법.
- 제 9 항에 있어서, 상기 혼합수단으로써 리본 블렌더(Ribbon Blender)나 V형 블렌더, 및 헨셀 믹서(Henchel Mixer)를 사용하는 것을 특징으로 하는 상기 난연 폴리스티렌계 수지의 제조방법.
- 제 9 항에 있어서, 상기 혼련 압출수단으로써 통상의 압출기, 브라벤더 플라스티코더(Brabender Plasticorder), 반바리 믹서(Banbury Mixer), 믹싱롤(Mixing Roll) 또는 니더(Kneader)를 사용하는 것을 특징으로 하는 상기 난연 폴리스티렌계 수지의 제조방법.※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.