KR930010436B1 - 방청성이 우수한 윤활처리 강철재 제조용 도료 조성물 - Google Patents

방청성이 우수한 윤활처리 강철재 제조용 도료 조성물 Download PDF

Info

Publication number
KR930010436B1
KR930010436B1 KR1019880002598A KR880002598A KR930010436B1 KR 930010436 B1 KR930010436 B1 KR 930010436B1 KR 1019880002598 A KR1019880002598 A KR 1019880002598A KR 880002598 A KR880002598 A KR 880002598A KR 930010436 B1 KR930010436 B1 KR 930010436B1
Authority
KR
South Korea
Prior art keywords
coating composition
weight
lubricated
steel
acrylic resin
Prior art date
Application number
KR1019880002598A
Other languages
English (en)
Other versions
KR880011290A (ko
Inventor
히로키 하나바다
히데오 가와구치
하로시 후쿠도메
료오이치 노오미
히로미 이자이쿠
고이치 고마이
기스케 요시다
Original Assignee
스미토모긴조쿠 고오교오 가부시기가이샤
신구우 야스오
닛뽕 유시 가부시기가이샤
오가와 데루쯔기
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 스미토모긴조쿠 고오교오 가부시기가이샤, 신구우 야스오, 닛뽕 유시 가부시기가이샤, 오가와 데루쯔기 filed Critical 스미토모긴조쿠 고오교오 가부시기가이샤
Publication of KR880011290A publication Critical patent/KR880011290A/ko
Application granted granted Critical
Publication of KR930010436B1 publication Critical patent/KR930010436B1/ko

Abstract

내용 없음.

Description

방청성이 우수한 윤활처리 강철재 제조용 도료 조성물
본 발명은 프레스가공 또는 유사한 가공(스탬핑등)이 수행되는 강철재, 즉 프레스 가공용 강철재의 윤활처리용 도료 조성물에 관한 것이다. 특히, 본 발명은 윤활처리 강철재의 제조에 유용함은 물론 윤활처리 강철재를 저장 또는 운송중에 코일링 또는 적층하는 경우에 우수한 방청성을 발휘하는 도료 조성물에 관한 것이다.
프레스 가공에 유용한 강철재에는 열간압연산세 강판, 냉간압연강판, 유전처리 강판등의 도금강판, 및 스테인레스강판 등의 강판은 물론 강판 등의 성형 강철재가 있다.
강판 또는 강판을 프레스 가공하는 경우에, 광물성 오일 및/또는 식물성 오일 및 각종 첨가제로 구성되는 윤활유를 다년간 사용하여 왔다 이러한 윤활유는 프레스기의 운전자와 같은 수요자에 의해 프레스 가공 되기전에 가공대상 강철재의 표면에 도포된다. 수요자가 윤활유를 취급할때 당면할 수 있는 환경문제를 제거하기 위해서, 최근, 각종 윤활제를 함유하는 윤활용 유기건조피막으로 강관 및 강판을 미리 피복하고 있다. 강철재를 제조한 후 수요자에게 판매하기전의 적당한 단계 윤활피막을 형성시킨다. 표면에 예비성형 윤활건조피막을 가지는 강판 및 강관(이하 ＂윤활처리 강철재＂라 약칭함)의 사용이 상당히 증가되었다.
윤활처리 강철재 제조시, 윤활건식피막의 제조에 유용한 도료 조성물은 아크릴수지, 에폭시수지, 멜라민수지, 또는 페놀수지와 같은 건조형 또는 역경화형의 도막형성수지로 구성되며, 윤활제로서 하나이상의 지방산, 지방에스테르, 지방산비누, 금속성비누, 알코올, 폴리에틸렌미분, 그래파이트, 몰리브덴디설파이드, 플루오르화수지미분등을 함유한다. 이러한 도료 조성물을 일본국 특공소 제60-250099호 (1985), 제59-204668호 (1984), 및 제57-65795호 (1982)에 개시되어 있다.
실제로 사용하기 위해서, 윤활처리 강철재 제조용 도료 조성물은 하기의 특성을 가지는 건조피막을 형성하는 것히 바람직하다 :
(a) 윤활처리 강철재의 프레스 가공시에 필요한 윤활성, (b) 윤활처리 강철재의 제조시, 프레스 가공후 탈지 세정하기 전의 방청성, (c) 탈지 세정용액에 의한 탈막성, 및 (d) 윤활처리 강철재의 코일링 또는 적충중의 내몰로킹성 또는 비점착성.
전술한 각종 도료 조성물의 대부분은 방청성이 손실되더라도 얻어지는 건조피막의 프레스성형성(윤활성)이 개량되도륵 제제화 하였다. 실제로, 종래의 도료 조성물로 피복된 윤활처리 강철재는 실제 사용중, 특허 저장중의 코일링 또는 적층시에 발청으로 인한 난점을 가진다. 따라서, 방청성이 개량된 윤활처리 강철재 제조용으로, 적합한 도료 조성물이 절실히 요망되고 있다.
본 발명의 목적은 우수한 윤활성과 더불어 방청성이 개량된 윤활처리 강철재 계조시에 유용한 도료 조성물을 제공하는데 있다.
본 발명의 다른 목적은 강철표면에 윤활성, 탈막성, 내블로킹성이 우수함과 동시에 방청성이 개량된 도막을 형성시킬 수 있는 윤활처리 강철재 제조용 도료 조성물을 제공하는데 있다.
본 발명의 또다른 목적 및 장점은 하기의 설명 및 실시예로부터 알 수 있다.
본 발명자들은 종래의 윤활처리 강철재에서 발생하는 발청현상을 연구 검토한 결과, 발청은 하기 메카니즘에 의한 것임을 밝혀내었다. 윤활처리 강판 또는 강관의 코일링 또는 적층시에, 대기중의 수중기가 인접강판 또는 강관 사이의 공간에 응축되어 이 공간내의 강철재의 윤활도막이 강판 또는 강판에 하중이 작용할때 응축된 수분의 작용에 의해 손상되는 것이다. 윤활도막이 손상되면, 물의 존재하에서 전기화학적 작용에 의해 윤활처리 강철재의 발청현상이 촉진된다.
따라서, 코일링 또는 적층시에 윤활처리 강철재의 발청현상을 방지하기 위해서는, 상기 메카니즘으로 인한 발청을 방지해야 하며, 이를 위해서, 강철표면과 대기사이의 장벽으로서 유기 윤활도막에 의해 강철표면을 보호하는 것만으로 항상 효과적인 것은 아니다.
상기 목적들은 기본수지로서 특정특성을 가지는 아크릴수지와 특정 방청제 및 방수제로 구성되는 도료 조성물에 의해 성취할 수 있다. 본 발명의 도료 조성물은 강철재를 상기 메카니즘에 의한 발청현상을 효과적으로 방지할 수 있다.
본 발명은 윤활처리 강철재 제조용으로 적합한 개량된 방청성을 가지는 도료 조성물을 제공하는데, 이것은 조성물중의 고형분 총량에 대하여, 산가가 20 내지 160이고 유리전이온도가 5 내지 100℃인 아크릴수지 75 내지 97.7중량%와, 방청제로서 설폰아미드카르복실산과 시클릭아민의 혼합물 0.3 내지 5중량%와, 방수 제2 내지 20중량%로 구성된다.
본 발명에 의한 도료 조성물은 미량, 예를들면 하술하는 바와 같이 총량이 조성물중 고형분 총량에 대하여 20중량%까지의 하나이상의 부가성분을 함유한다.
또한, 본 발명은 적어도 하나의 표면에 상기한 도료 조성물로 성형된 건조도막을 가지는 강판 또는 강판과 같은 윤활처리 강철재를 제공한다.
설폰아미드카르복실산과 시클릭아민의 혼합물인 본 발명에 사용된 방청제의 비율이 0.3중량% 미만인 경우에, 얻어지는 도료 조성물은 적합한 방청성을 가지는 도막을 형성하지 못한다. 또한, 방청제의 비율이 5중량%를 초과하는 경우에는, 방청성이 감소된다. 따라서, 방청제는 조성물중 고형분 총량에 대하여 0.3 내지 5중량%, 바람직하게는 0.5 내지 3중량%를 함유해야 한다.
방수제의 비율이 2중량% 미만인 경우, 제조되는 피막은 적합한 방수성을 발휘하지 못한다. 한편, 20중량% 이상의 방수제를 첨가하면 피막의 방수성이 더이상 증가하지 않기 때문에 경제성면에서 바람직하지 못하다. 따라서, 방수제는 조성물중 고형분 총량에 대하여 2 내지 20중량%, 바람직하게는 3 내지 15중량%를 함유해야 한다.
아크릴수지는 도료 조성물의 바란스를 구성하며, 조성물중 고형분 총량에 대하여 75 내지 97.7중량%, 바람직하게는 82 내지 96.5중량%를 구성한다.
본 발명의 도료 조성물에 유용한 아크릴수지는 20 내지 160, 바람직하게는 40 내지 120, 더욱 바람직하게는 50 내지 100의 산가(산수)를 가지며, 5 내지 100℃, 바람직하게는 10 내지 85℃의 유리전이온도를 가진다.
아크릴수지의 산가가 20미만인 경우에, 얻어지는 도료 조성물은 알카리성 탈지 세정용액 사용시에는 탈막성이 충분치 못하다. 탈막성은 가공 강철재를 패인팅과 같은 후속 단계에서 처리하기 위해 필요한 것이다. 160이상의 산가를 가지는 아크릴수지를 사용한 결과, 얻어지는 피막의 방청성이 상당히 감소되었다. 아크릴 수지의 산가는 수지제조시에 사용된 산단량체의 농도에 의해 변화시킬 수 있다.
아크릴수지의 유리전이온도(Tg)가 5℃ 미만인 경우에는, 수지의 점착성이 너무 높고 얻어지는 도료 조성물의 건조도막이 만족할만한 내블로킹성을 가지지 못하게 된다. 한편, 100℃ 이상인 경우에는 수지의 도막 형성성이 열화되어 피막의 방청성이 감소됨은 물론, 조성물의 탈막성이 감소된다. 아크릴수지의 유리전이온도는 조성물과 중합체의 분자량에 따라 다르다.
본 발명에 사용된 아크릴수지는 각종 도료 조성물에 통상 사용되는 열가소성 아크릴수지이며, 종래의 중합법, 예를들면 용액 또는 유화액 중합법에 의해 제조할 수 있다. 이러한 아크릴수지 및 그 제조방법은 공지되어 있다.
아크릴수지는 하나이상의 단량체, 일반적으로 α,β-에틸렌성 불포화카르복실산 및 그 에스테르에서 선택된 적어도 2개의 단량체를 1 내지 25개의 탄소원자를 가지는 알코올과 중합하여 제조한다.
유용한 단량체의 특정예에는 아크릴산, 메타크릴산, 소르빈산, 이타콘산, 말레인산, 푸마르산, 메틸(메트)아크릴레이트[＂(메트)아크릴레이트＂는 아크릴레이트 또는 메타크릴레이트를 나타냄], 에틸(메트)아크릴레이트, 프로필(메트)아크릴레이트, 이소프로필(메트)아크릴레이트, 부틸(메트)아크릴레이트, 이소부틸(메트)아크릴레이트, 2-에틸헥실(메트)아크릴레이트, 헥실(메트)아크릴레이트, 라우릴(메트)아크릴레이트, 수테아릴(메트)아크릴레이트, 2-히드록시에틸(메트)아크릴레이트, 2-히드록시프로필(메트)아크릴레이트, 글리시딜(메트)아크릴레이트, 및 디메틸 아미노에틸(메트)아크릴레이트가 있다.
본 발명에 사용된 아크릴수지는 20 내지 160의 산가를 가지기 때문에, α,β-에틸렌성 불포화카르복실산 및 그 에스테르에서 선택된 적어도 하나의 유리산단량체 및 적어도 하나의 에스테르단량체는 얻어지는 아크릴수지가 소정의 산가를 가지는 비율로 사용한다. 전술한 바와같이, 아크릴수지의 유리전이온도는 조성물과 수지의 분자량에 따라 다르다. 따라서, 단량체 및 중합도는 소정의 Tg를 가지는 아크릴수지를 형성할 수 있도록 선택해야 한다. 경우에 따라서, 2이상의 아크릴수지의 혼합물을 도료 조성물에 사용할 수 있다. 이경우에, 혼합물의 산가 및 Tg가 전술한 각 범위내에 드는한 각 아크릴단량체의 산가 및 Tg가 상기 범위내에 반드시 들필요는 없다. 본 발명에 유용한 아크릴수지의 수평균 분자량은 5,000 내지 1,000,000이며, 10,000 내지 500,000인 것이 바람직하다.
아크릴수지는 얻어지는 도료 조성물의 안정성 향상을 위해서 암모니아 또는 아민으로 부분 또는 완전 중화시킬 수 있다.
도료 조성물에 사용된 방청제는 설폰아미드카르복실산 및 시클릭아민의 혼합물이다. 시클릭아민의 사용량은 설폰아미드카르복실산의 각 당량에 대하여 0.5 내지 2.5당량이 바람직하고. 0.8 내지 1.2당량이 더욱 바람직하다. 경우에 따라서는, 종래의 방청제중에서 선택된 하나이상의 부가의 방청제, 예를들면 올레오일사르코신을 사용할 수 있다.
용액중에 존재하는 경우에는, 설폰아미드카르복실산과 시클릭아민이 반응하여 염을 형성한다. 그러나, 전술한 바와같이, 두성분의 단량이 반드시 상기 범위내에 들필요는 없으며, 이들중 하나가 화학양론적으로 과량 존재하여도 무방하다.
설폰아미드카르복실산의 예에는 하기 구조식의 화합물이 있다 :
RSO2NHCnH2nCOOH
식중, R은 포화 또는 불포화 지방족, 시클로지방족, 또는 방향족 탄화수소기이고, n은 1 내지 7의 정수이다.
상기 화합물의 특정예에는 메틸설폰아미드카르복실산. 에틸설폰아미드카르복실산, 프로필설폰아미드카르복실산, 알릴설폰아미드카르복실산, 부틸설폰아미드카르복실산, 벤젠설폰아미드타르복실산, 벤질설폰아미드카르복실산, 노닐페닐설폰아미드카르복실산, 옥틸페닐설폰아미드카르복실산 등이 있다. 이러한 화합물중 어떤 것은 유리산 또는 염의 형태로 HOECHST에 의해 Bohrmittel HOECHST 및 Hostacor H라는 상품명 으로 판매되고 있다(Hostacor은 등록 상표이다). 설폰아미드카르복실산은 유리산 또는 이들의 알칼리금속 또는 아민과의 염형태로 사용할 수 있다.
시클릭아민은 6원고리에 하나 이상의 고리질소원자를 함유하는 헤테로시클릭화합물이다. 시클릭아민의 예에는 피라진, 피리딘, 피페리딘, 피페라진, 모르폴린, 및 이들의 유도체가 있다. 시클릭아민의 특정예에는, 피리딘, 메틸피리딘, 디메틸피리딘, 에틸피리딘, 프로필피리딘, 시아노피리딘, 아미노피리딘, 아미노메틸피리딘, 피페리딘, N-메틸피페리딘, 메틸피페리딘, 디메틸피페리딘, N-에틸피페리딘, 에틸피페리딘, 피페라진, 모르폴린, N-메틸모르폴린, N-아미노에틸모르폴린, N-아미노프로필모르폴린, 피 라진, 메틸피라진, 디메틸피라진 등이 있다.
본 발명의 도료 조성물에는 아크릴수지의 도막성형성 또는 방청체의 효과에 역영향을 주지 않는 한 방수제로서 종래의 어떤 방수제를 사용하여도 무방하다. 이러한 관점에서 카르복실산에스테르, 금속성 비누, 폴리에틸렌미분, 및 플로오르화수지미분 등의 방수물질이 적합하다.
본 도료 조성물의 방수제로서 유용한 카르복실산에스테르에는 지방족 또는 방향족 포화모노카르복실산의 에스테르가 있으며, 디- 또는 트리카르복실산과 같은 지방족 방향족 포화 다작용성 카르복실산의 에스테르가 바람직하다. 이러한 카르복실산 에스테르의 특정예에는 부틸스테아레이트, 디-2-에틸헥실 프탈레이트, 디헵틸프탈레이트, 디-n-옥틸 프탈레이트, 디노닐 프탈레이트, 디이소데실 프탈레이트, 디트리데실 프탈레이트, 디-2-에틸헥실 아디페이트, 디-2-에틸헥실 세바케이트, 트리옥틸 트리멜리테이트, 에틸렌 글리코올 디스테아레이트, 글리세롤 트리카프릴레이트, 및 트리메틸올프로판 트리스테아레이트가 있다.
금속성 비누에는 알루미늄 스테아레이트, 칼슘 스테아레이트 아연 스테아레이트 및 마그네슘 스테아레이트가 있다.
플루오르화수지의 예에는 폴리테트라플루오로에틸렌 수지가 있다.
상기한 방수제 모두가 윤활효과를 가지는 것으로 공지되어 있으나, 본 발명에서는 윤활효과가 전혀 없는 다른 방사제를 사용하여도 된다.
필요에 따라서, 본 발명의 도료 조성물에는 극압첨가제, 방부제, 안료, 부가의 방청제, 및 윤활제등의 소량의 첨가제를 첨가할 수 있다. 이러한 임의 첨가제를 사용하는 경우에는, 총량이 도료 조성물의 20중량%이하가 되도록 첨가한다.
도료 조성물은 아크릴수지, 방청제, 방수제, 및 임의의 첨가제를 주위온도에서 단순혼합하여 제조할 수 있다. 희석제 또는 용매로서 물 또는 유기용매를 첨가할 수 있다. 아크릴수지가 용액 또는 유화핵 중합법에 의해 제조된 수용액 또는 유화액의 형태인 경우에, 도료 조성물은 아크릴수지의 용액 또는 유화액에 다른성분을 첨가하여 제조할 수 있다. 필요에 따라서는, 도료 조성물을 물 또는 유기용매로 희석하여 채택된 피복법에 의한 도포에 적합한 경점성을 가지도록 할 수 있다.
윤활처리 강철재의 제조방법에 있어서, 본 발명의 도료 조성물은 침지법, 로울피복법, 커어튼피복법, 스프레이피복법, 정전피복법 또는 전착피복법등의 통상의 피복법에 의해 강철재의 적어도 일면에 피복할 수 있다. 피복후, 습한 피막을 고온공기 또는 활성 방사선 조사에 의해 건조시켜 강철재 표면상에 건조한 윤활도막을 형성시킴으로써 소정의 윤활처리 강철재를 얻을 수 있다.
본 발명의 윤활처리 강철재는 도료 조성물중의 건조막의 피복량이 0.2 내지 6.Og/㎡인 것이 바람직하고, 0.5 내지 3.0g/㎡인 것이 바람직하다. 피복량이 0.2g/㎡ 미만이면, 윤활처리 강철재는 적합한 윤활성과 방청성을 가지지 못한다. 피복량이 6.0g/㎡ 이상이면, 윤활성 또는 방청성이 충분히 개량되지 못한다.
본 발명의 윤활처리 강철재에 의하면, 강철재의 표면에 형성된 아크릴수지 피막에서 방청제(설폰아미드카르복실산+시클릭아민)와 방수제가 충분히 보유된다. 피막은 강철재를 프레스 가공하는 경우에도 충분한 윤활성을 발휘한다. 윤활성은 대부분이 아크릴수지 피막자체에 의한 것이다. 피막에 존재하는 방수제에 의해 윤활성이 일층 향상된다.
본 발명의 윤활처리 강철재에 있어서, 윤활처리 강철재의 제조후는 물론 프레스 가공후 피막을 탈지 세정 용액으로 제거하기 전의 방청성, 알카리성 탈지 세정용액에 의한 탈막성, 및 내블로킹성 등의 필요 특성을 열화시키는 일없이 상기한 프레스 가공에 필요한 우수한 윤활성을 얻을 수 있다. 윤활처리 강철재의 방청성은 이들을 코일링 또는 적층시키는 경우에도 유지된다. 따라서, 윤활처리 강철재의 제조에서 윤활도막의 제거에 이르는 전단계, 즉 윤활처리 강철재의 저장, 이송, 및 프레스 가공단계를 통해서 윤활처리 강철재의 발청현상을 효과적으로 방지할 수 있다. 이에비해, 종래의 윤활처리강철재는 저장 또는 이송시의 적층상태 하에서 방청성이 현저하게 열화된다. 본 발명의 윤활처리강철재의 경우에는, 아크릴수지와 첨가제(방청제와 방수제)의 상승효과에 의해서 적층상태하에서도 우수한 방청성을 얻을 수 있으며, 이러한 특성은 상기한 첨가제중 하나가 윤활처리피막에 존재하지 않을 경우 또는 아크릴수지의 산가 또는 Tg가 상기한 범위를 벗어 나는 경우에는 적어도 부분적으로 손실될 수 있다.
다음은 실시예에 의거하여 본 발명을 일층 상세히 설명한다. 그러나, 하기의 실시예는 단지 설명을 위한 것이며, 본 발명이 이에 국한되는 것은 아니다.
[실시예]
아크릴산(AA), 메타크릴산(MAA), 메틸메타크릴레이트(MMA), 옥틸아크릴레이트(OA), 부틸 아크릴레이트(BA), 및 2-에틸헥실 메타크릴레이트(EHMA)에서 선택된 단량체로부터 종래의 유화액중합법에 의거하여 각종 아크릴수지를 제조하였다. 하기의 표 1에는 상기 단량체의 비율은 물론, 얻어진 아크릴수지의 산가(AV), 유리전이온도(Tg) 및 수평균분자량(
Figure kpo00001
)을 기재한다.
얻어진 수성유화액형태의 아크릴수지에 방수제(카르복실산염 또는 에스테르)와 방청제(설폰아미드 카르복실산과 시클릭아민의 혼합물)을 첨가하여 강교반하고, 필요한 경우에는 이 혼합물을 물로 희석하여 도표조성물을 제조하였다. 각 도료조성물에 사용된 아크릴수지와 첨가제는 하기 표 2에 기재한다. 각 도료조성물은 하기비율(%는 수분제거 상태, 즉 고형분총량애 대한 비율이다)의 각 성분을 포함하였으며, 이것의 pH는 트리에틸아민에 의해 8.0으로 조절하였다.
Figure kpo00002
표 2의 도료조성물중 어느것은 비교용으로서 방수제 또는 방청제를 포함하지 않으며, 이러한 경우에는 제외된 방수제 또는 방청제의 중량과 동량의 물을 부가로 첨가하였다.
얻어진 각 도료조성물을 탈지세정용액으로 처리하여 표면이 청결해진 0.8mm 두께의 냉간압연강판에 도포하였다. 도료조성물은 바피복기를 사용하여 건조피복량이 3g/㎡이 될정도외 두께로 피복하였다. 도포된 도료를 110℃의 고온공기중에서 10분동안 건조시켜서 일면에 건조윤활도막을 가지는 윤활처리 강판을 제조하였다.
윤활처리 강판을 하기의 시험법에 따라 윤활성의 척도인 커핑드로우잉성, 탈지세정 용액에 의한 탈막성, 내블로킹성. 및 적층상태 및 공기 또는 습기의 노출상태하에서의 방청성에 대하여 평가하였다.
[시 험 법]
(1) 커핑드로우잉성 :
종래의 커핑시험공정에 따라, 직경이 33.0mm인 펀치를 사용하여 1,000kg/㎠의 압력으로 다이에 대면한 윤활처리면을 원통형의 평저컵내로 펀칭하여 점차 큰 직경을 가지는 윤활처리 강판의 블랭크를 드로우잉 하고, 파열되는 일없이 드로우잉할 수 있는 최대 블랭크크기인 최대블랭크직경을 측정하였다. 윤활처리강판의 한계드로우잉비(LDR)은 하기식에 의해 계산하였다 :
Figure kpo00003
윤활처리피막을 가지지 않는 냉간압연강관(미윤활처리강판)의 LDR도 동일한 방법으로 계산하였다. 커핑드로우잉성은 윤활처리강판의 LDR(A)에 대한 미윤활처리강판의 LDR(B)의 비에 의해 평가하였으며, 다음과 같은 기준으로 평가하였다 :
× : A/B＜1.0 ;
△ : A/B=1.0-1.1 ;
O : A/B＞11 ;
A/B=윤활처리강판의 LDR/미윤활처리강판의 LDR.
(2) 탈막성 :
60-70℃의 Fine Cleaner FC 4326(Fine Cleaner는 Nippon Parkerizing Corp.Ltd.의 등록상표이다)의 2% 수용액을 1kg/㎠의 분무압으로 5초동안 윤활처리 강판시험편의 윤활처리면에 스프레이하여 표면을 탈지세정하였다. 이와 같은 처리표면의 방수정도에 의해 탈막성을 평가하였으며, 다음과 같은 기준으로 평가하였다 :
× : 표면전체가 방수성임.
△ : 표면일부가 방수성임
○ : 방수성이 아님
(3) 내블로킹성 :
크기가 70mm×150mm인 2매의 윤활처리 강판시험편을 윤활피막이 서로 대면하도록 중첩하였다. 중첩된 시험편을 67kg/㎠의 하중하에 50℃의 온도에서 1분동안 경시한후, 500g/㎡의 경하중하에 40℃의 온도에서 16시간동안 경시하고, 최종적으로 무하중하에 실온에서 50일동안 경시하였다. 이어서, 시험편의 윤활처리피막의 블로킹도를 관찰하면서 2개의 시험편을 분리하였다. 내블로킹성은 다음과 같은 기준으로 평가하였다:
×: 강블로킹성
△ : 약블로킹성
○ : 비블로킹성
(4) 방청성
4-1 적층상태하에서 : 시판되는 방청유를 윤활처리면, 즉 각 시험편의 윤활처리 피막에 0.5g/㎡을 도포 한후 크기가 70mm×150mm인 2매의 윤활처리 강판시험편을 윤활피막이 서로 대면하도록 중첩시켰다. 중첩된 시험편을 50kg/㎠의 하중하에 50℃의 온도에서 24시간동안 경시하였다.
4-2 공기의 노출상태하에서 : 윤활처리피막에 0.5g/㎡의 시판방청유를 도포한 70mm×150mm 크기의 시험편을 공기에 노출된 실내에서 30일동안 경시하였다.
4-3 습기의 노출상태하에서 : 크기가 70mm×150mm인 시험편의 윤활처리피막에 0.5g/㎡의 시판방청유를 도포한후, 습윤상자내의 49±1℃의 온도에서 10일 동안 습기(상대습도 : 97%)에 노출시켰다.
경시 또는 노출후 시험편의 윤활처리면에 나타나는 발청정도를 관찰하여 방청성을 평가하였으며, 다음과 같은 기준으로 평가하였다 :
× : 상당히 발청됨
△ : 약간 발청됨
○ : 발청되지 않음
이상의 시험결과는 하기의 표 3에 요약기재한다.
[표 1]
Figure kpo00004
(1) AA : 아크릴산, MAA : 메타크릴산,
MMA : 메틸메타크릴레이트, OA : 옥틸 아크릴레이트,
BA :부틸아크릴레이트, EHMA : 2-에틸헥실 메타크릴레이트.
(2) Tg : 유리전이온도 (℃ ),
AV : 산가,
Figure kpo00005
: 수평균분자량
* : 본 발명의 범위를 벗어남
[표 2]
Figure kpo00006
×: 본 발명의 범위를 벗어남.
(3) CaST : 칼슘 스테아레이트.
DOP : 디옥틸 프탈레이트.
(4) A : 알릴설폰 아미드-아세트산과 모르폴린의 동몰혼합물,
B : 알릴설폰 아미드-아세트산과 N-메틸모르폴린의 동몰혼합물,
C : 알릴설폰 아미드-아세트산과 트리에탄올아민의 동몰혼합물.
(5) 시판방청유
[표 3]
Figure kpo00007
표 3에서 알 수 있는 바와 같이, 본 발명의 범위를 벗어나는 산가 또는 Tg를 가지는 아크릴수지를 사용하는 비교예 6-9에서는, 윤활처리강판의 커핑드로우잉성과 공기노출 또는 습기노출상태하에서의 방청성은 충분히 유지되나, 탈막성, 내블로킹성 및 적층상태하에서의 방청성중의 적어도 하나는 열화된다. 아크릴수지의 산가 및 Tg가 본 발명의 범위내에 드는 경우에도, 도료조성물에 방청제 또는 방수제를 첨가하지 않으면, 적층상태하에서의 방청성이 현저하게 열화된다(비교예 10 및 12).
이에 비해, 본 발명에 의한 도료조성물을 강판에 도포한 실시예에 있어서는, 모든 특성에 대하여 만족한 결과를 얻었다.
이상, 본 발명을 대표적인 실시예에 의거하여 설명하였으나, 이것은 본 발명을 한정하기 위한 것이아니라 설명을 목적으로 하는 것이며, 본 발명의 요지를 벗어나지 않는 범위내에서 다양하게 변경실시할 수 있다.

Claims (8)

  1. 조성물중의 고형분총량에 대하여, 20 내지 160의 산가와 5 내지 100℃ 유리전이온도를 가지는 75 내지 97.7중량%의 아크릴수지와, 설폰아미드 카르복실산과 시클릭아민의 혼합물로 구성되는 0.3 내지 5중량%의 방청제와, 2 내지 20중량%의 방수제로 구성되는 것을, 특징으로 하는 방청성이 우수한 윤활처리 강철재 제조용 도료조성물.
  2. 제1항에 있어서, 상기 방수제가 카르복실산에스테르, 금속성비누, 폴리에틸렌미분, 및 플루오르화수지미분에서 선택되는 것을 특징으로하는 도료조성물.
  3. 제1항에 있어서, 상기 아크릴수지의 산가가 40 내지 120이고 유리전이 온도가 10 내지 85℃인 것을 특징으로 하는 도료조성물.
  4. 제1항에 있어서, 상기 방청제가 설폰아미드 카르복실산의 각 당량에 대하여 0.5 내지 2.5당량의 시클릭아민의 존재하는 설폰아미드 카르복실산과 시클릭아민의 혼합물인 것을 특징으로 하는 도료조성물.
  5. 제1항에 있어서, 82 내지 96.5중량%의 아크릴수지와, 0.5 내지 3중량%의 방청제와, 3 내지 15중량%의 방수제로 구성되는 것을 특징으로 하는 도료조성물.
  6. 적어도 일면에, 조성물중의 고형분 총량에 대하여, 20 내지 160의 산가와 5 내지 100℃의 유리전이온도를 75 내지 97.7중량%의 아크릴수지와, 설폰아미드 카르복실산과 시클릭아민의 혼합물로 구성되는 0.3 내지 5중량%의 방청제와, 2 내지 20중량%의 방수제로 구성되는 도료조성물로 성형된 피막을 가지는 것을 특징으로 하는 방청성이 우수한 윤활처리 강철재.
  7. 제6항에 있어서, 상기 강철재가 판 또는 관의 형태인 것을 특징으로 하는 윤활처리 강철재.
  8. 제6항에 있어서, 상기 건조 피막의 중량이 0.2 내지 6.0g/㎡인 것을 특징으로 하는 윤활처리 강철재.
KR1019880002598A 1987-03-12 1988-03-12 방청성이 우수한 윤활처리 강철재 제조용 도료 조성물 KR930010436B1 (ko)