KR900016482A - 내부식성 니켈-콜롬비움-몰리브멘 합금 - Google Patents
내부식성 니켈-콜롬비움-몰리브멘 합금 Download PDFInfo
- Publication number
- KR900016482A KR900016482A KR1019900005177A KR900005177A KR900016482A KR 900016482 A KR900016482 A KR 900016482A KR 1019900005177 A KR1019900005177 A KR 1019900005177A KR 900005177 A KR900005177 A KR 900005177A KR 900016482 A KR900016482 A KR 900016482A
- Authority
- KR
- South Korea
- Prior art keywords
- nickel
- alloy
- carbon
- hours
- molybdenum
- Prior art date
Abstract
내용 없음.
Description
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음
제1도는 본 발명에 따라 처리된 합금의 500배 현미경 사진의 재생사진,
제2도는 본 발명의 균질화 처리(homog enization treatment)를 사용하여 처리된 동일합금의 동일배율의 현미경 사진의 유사한 재생사진,
제3도와 제4도는 합금 6을 비-균질상태와 균질상태로 각기 묘사하는 도면.
Claims (15)
- 중량으로 약 19-23% 크롬, 약 14-17% 몰리브덴, 약 2-4% 텅스텐, 약 0-약0.1% 탄소, 약 0-0.25% 티탄니움, 약 0-약 10% 철을 함유하고 나머지가 기본적으로 니켈인 합금을 1149℃에서 약 1316℃까지의 온도범위 내에서 적어도 약 5시간의 기간동안 균질화처리(homogenization treatment)를 받게하여 유해한 량의 Mu상 (phase)의 형성을 최소화함에 의해, 여러가지 부식환경에서 크롬, 몰리브덴 및 텅스텐의 높은 결합비율의 니켈-베이스합금의 롬새 및 점부식 저항성을 향상시키기 위한 공정.
- 제1항에 있어서, 균질화 온도가 약 1190℃에서 약 1260℃까지이고 방치기간이 5에서 50시간인 공정.
- 제1항에 있어서, 균질화처리가 합금은 약 1773℃에서 1204℃까지 약5-50시간동안 가열하고 다음 이 합금은 5-72시간동안 약 1204℃에서 1316℃까지 가열하는 두단계로 실시되는 공정.
- 제3항에 있어서, 합금이 약 20- 약 23%의 크롬, 약 14.25- 약 16% 몰리브덴, 약 2.5- 약 4% 텅스텐, 최대 약 0.05% 탄소, 약 2- 약10% 철, 최대 약 0.5% 망간 및 외대 약 0.25% 규소를 함유하는 공정.
- 제1항에 있어서, 합금이 약 21.5- 약 23%의 크롬을 함유하고 몰리브덴이 약 14- 약 15%인 공정.
- 제1항에 있어서, 합금이 약 19.5- 약 21.5%의 크롬과 약 15- 약 16% 몰리브덴을 함유하는 공정.
- 19-25% 크롬, 약12- 약18% 몰리브덴, 최대 4% 텅스텐, 최대 0.1% 탄소를 함유하고 나머지가 기본적으로 니켈인 합금을 약 1149℃이상 약 1316℃까지의 온도범위에서 약 5-100시간의 기간동안 균질화처리를 받게하여 유해한 량의 Mu상의 형성을 최소화 함에 의해 여러가지 부식환경에서 크롬과 몰리브덴의 높은 결합비율의 니켈-베이스합금의 틈새 및 점부식 저항성을 향상시키기 위한 공정.
- 제7항에 있어서, 지속기간이 약 10-100 시간동안인 공정.
- 제7항에 있어서, 균질화 온도가 약 1190℃-약 1260℃이고 지속시간이 약 5-50 시간인 공정.
- 중량으로 약 19-23%크롬, 약 14-17% 몰리브덴, 약2-4% 텅스텐, 약0-약0.1% 탄소 약0-약0.25% 티탄니움, 약 0-약 10% 철을 함유하고, 나머지가 기본적으로 니켈인 합금이 얼간작업전에 적어도 5시간동안 1149℃-약 1316℃의 온도범위내에서 균질화하고 이어 통상의 처리를 함으로 인해 조절된 상태에 있어 최소량의 유해 Mu상의 가짐에 특징이 있고 틈새와 점부식에 향상된 저항성을 가지는 니켈-베이스합금.
- 제10항에 있어서, 1190℃-1260℃에서 5-50 시간동안 균질화시키고 열간작업후 통상의 처 리를 하여 조절된 상태에 있는 니켈-베이스합금.
- 제10항에 있어서, 1093-1204℃ 에서 5-50시간동안과 1204℃-1316℃ 에서 5-72 시간동안 균질화하고 열간가공하고 이어 통상의 처리를 하여 조절된 상태에 있는 니켈-베이스합금.
- 중량으로 약 19-23%크롬, 약 14-17%몰리브덴, 약2-4%텅스텐, 0-0.1%탄소, 탄소에 대한 티탄니움의 비율(탄소/티타니움)이 적어도 약 1이 되도록 하는 양내의 최대 0.25%까지의 티탄니움, 약 0-2.5%의 철을 함유하고, 나머지가 기본적으로 니켈이며 합금의 기본적이고 신규한 특성을 해롭게 변화시키고 않을 정도의 소량의 불가피한 불순물을 함유하고, 약 1149℃-약 1316℃의 온도범위내에서 약 5-100시간동안 균질화된 후에, 설사 760-982℃의 온도범위로 재가열가되었을 때라도 유해한 량의 Mu상이 없고, 내산화성, 틈새 및 점부식 저항성이 향상됨에 특징이 있는 니켈-베이스합금.
- 제13항에 있어서, 탄소를 0.02% 보다 적게 함유하는 니켈-베이스합금.
- 제13항에 있어서, 철이 2% 이하이고, 탄소가 0.01% 이하이며, 탄소에 대한 티탄니움의 중량비 (탄소/티탄니움)이 3보다 큰 니켈-베이스합금.※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.