KR950032678A - 고온 내식성 단결정 니켈계 초합금 - Google Patents
고온 내식성 단결정 니켈계 초합금 Download PDFInfo
- Publication number
- KR950032678A KR950032678A KR1019950010785A KR19950010785A KR950032678A KR 950032678 A KR950032678 A KR 950032678A KR 1019950010785 A KR1019950010785 A KR 1019950010785A KR 19950010785 A KR19950010785 A KR 19950010785A KR 950032678 A KR950032678 A KR 950032678A
- Authority
- KR
- South Korea
- Prior art keywords
- weight
- single crystal
- superalloy
- percent
- gas turbine
- Prior art date
Abstract
본 발명은 크롬 약 11.5 내지 약 13.5중량%, 코발트 약 5.5 내지 약 8.5중량%, 몰리브덴 약 0.40 내지 약 0.55중량%, 텅스텐 약 4.5 내지 약 5.5중량%, 텐탈 약 4.5 내지 약 5.8중량%, 나오브 약 0.05 내지 약 0.25중량%, 알루미늄 약 3.4 내지 약 3.8중량%, 티탄 약 4.0 내지 약 4.4중량%, 하프늄 약 0.01 내지 약 0.06중량%, 및 니켈 잔여량과 부수적인 불순물을 포함하고, 상 안정도 수 NV3B가 약 2.45 미만인 고온 내식성 니켈계 초합금에 관한 것이다. 단결정 제품은 본 발명의 초합금으로부터 적합하게 제조할수 있다. 제품은 가스 터빈 엔진용 부품, 보다 특히 가스 터빈 블레이드 또는 가스 터빈 베인일 수 있다.
Description
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음
제1도는 본 발명의 한 가지 양태 및 4가지의 다른 합금을 대상으로 3가지의 노출온도에서 수행한 고온 부식 시험결과 챠트이고, 제4도는 본 발명의 한가지 양태 및 6가시의 다른 합금을 대상으로 수행한 시험으로부터의 합금 강도 및 고온 부식 데이타를 비교한 그래프.
Claims (20)
- 하기 원소들을 포함하고 상 안정도 수(phasial stability number) NV3B가 약 2.45 미만인 고온 내식성 니켈계 초합금.크 롬 약 11.5 내지 13.5중량%코 발 트 약 5.5 내지 8.5중량%몰리브텐 약 0.40 내지 0.55중량%텅 스 텐 약 4.5 내지 5.5중량%탄 탈 약 4.5 내지 5.8중량%니 오 브 약 0.05 내지 0.25중량%알루미늄 약 3.4 내지 3.8중량%티 탄 약 4.0 내지 4.4중량%하 프 늄 약 0.01 내지 0.06중량%니켈+부수적불순물 잔여량
- 제1항에 있어서, 하기 원소들을 추가로 포함하는 초합금.탄 소 약 0 내지 0.05중량%붕 소 약 0 내지 0.03중량%지르코늄 약 0 내지 0.03중량%레 늄 약 0 내지 0.25중량%규 소 약 0 내지 0.10중량%망 간 약 0 내지 0.10중량%
- 제1항에 있어서, 니오브와 하푸늄의 합계가 0.06 내지 0.31중량%인 초합금.
- 제1항에 있어서, Ti : Al 비가 1 보다 큰 초합금.
- 제1항에 있어서, 알루미늄과 티탄의 합계가 7.4 내지 8.2중량%인 초합금.
- 제1항에 있어서, Ta : W 비가 1 보다 큰 초합금.
- 제1항에 있어서, 내산화성이 증가된 초합금.
- 제1항의 초합금으로부터 제조된 단결정 제품.
- 제8항에 있어서, 제품이 터빈 엔진용 부품인 단결정 제품.
- 제9항에 있어서, 부품이 가스 터빈 블레이드 또는 가스 터빈 베인인 제품.
- 하기 원소들을 포함하고 상 안정도수 NV3B가 약 2.45 미만인 니켈계 초합금으로부터 제조된, 고온 내식성이 증가됨을 특징으로 하는 단결정 주물.크 롬 약 12.0 내지 13.0중량%코 발 트 약 6.2 내지 6.8중량%몰리브텐 약 0.42 내지 0.48중량%텅 스 텐 약 4.7 내지 5.3중량%탄 탈 약 4.9 내지 5.5중량%니 오 브 약 0.05 내지 0.12중량%알루미늄 약 3.5 내지 3.7중량%티 탄 약 4.1 내지 4.3중량%하 프 늄 약 0.02 내지 0.05중량%니켈+부수적불순물 잔여량
- 제11항에 있어서, 하기 원소들을 추가로 포함하는 단결정 주물.탄 소 약 0 내지 0.05중량%붕 소 약 0 내지 0.03중량%지르코늄 약 0 내지 0.03중량%레 늄 약 0 내지 0.25중량%규 소 약 0 내지 0.10중량%망 간 약 0 내지 0.10중량%
- 제11항에 있어서, 니오브와 하프늄의 합계가 0.06 내지 0.31중량%인 단결정 주물.
- 제11항에 있어서, 알루미늄과 티탄의 합계가 7.4 내지 8.2중량%인 단결정 주물.
- 제11항에 있어서, Ti : Al 비와 Ta : W 비가 1 보다 큰 단결정 주물.
- 제11항에 있어서, 내산화성이 증가된 단결정 주형물.
- 제11항에 있어서, 크리프(creep)-파열강도가 증가된 단결정 주물.
- 제11항에 있어서, 가스 터빈 블레이드 또는 가스 터빈 베인인 단결정 주물.
- 하기 원소들을 포함하고 상 안정도수 NV3B가 약 2.45 미만인 니켈계 초합금으로부터 제조된, 고온 내식성이 증가됨을 특징으로 하는 단결정 주물.〔여기서, 니오브와 하프늄의 합계는 0.06내지 0.31중량%이고, 알루미늄과 티탄의 합계는 7.4내지 8.2중량%이며, Ti : Al 비는 1 보다 크고 Ta : W 비는 1 보다 크다〕.크 롬 약 12.5중량%코 발 트 약 6.5중량%몰리브텐 약 0.45중량%텅 스 텐 약 5.0중량%탄 탈 약 5.2중량%니 오 브 약 0.10중량%알루미늄 약 3.60중량%티 탄 약 4.2중량%하 프 늄 약 0.03중량%탄 소 약 0 내지 0.05중량%붕 소 약 0 내지 0.03중량%지르코늄 약 0 내지 0.03중량%레 늄 약 0 내지 0.25중량%규 소 약 0 내지 0.10중량%망 간 약 0 내지 0.10중량%니 켈 잔여량
- 제19항에 있어서, 터빈 블레이드 또는 가스 터빈 베인인 단결정 주물.※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.